Patent Grant
10821330
Not Applicable
The present invention generally relates to the use of graphene in layers of a golf ball with an embedded integrated circuit.
Typical process of synthesizing exfoliated graphite (individual sheets of exfoliated graphite are also known as graphene or graphene nanoplatelets) includes reacting graphite with acids such as nitric and or sulfuric acid followed by heat treatment and chemical reduction. Exfoliated graphite is a two dimensional planar sheet made of SP2-hybridized carbon. Graphene (individual sheets of reduced exfoliated graphite) sheets are typically few nanometers thick and few microns wide (aspect ratio of >1000). This high aspect ratio of graphene coupled with their high tensile strength (tensile strength in GPa compared to MPa for polymers) can lead to polymeric composite materials with very high tensile and flexural properties. Graphene's unusually high thermal conductivity (˜3000 W/mk compared to <1 W/mk for typical thermoplastic polymers; can be utilized in making thermally conductive composite materials. For thermally cured elastomeric products, this high thermal conductivity can mean shorter, more uniform curing cycles that can lead to higher production volumes.
Various examples of exfoliated graphite (also called graphene) based composites can be found in literature. Wang et al. describe expanded graphite polyethylene composite for electromagnetic radiation interference (EMI) shielding applications.
U.S. Pat. No. 4,946,892 describes synthesis of exfoliated graphene based composite by compression molding graphite with polyimide resin under high heat (200 C) and pressure (80 kPa).
Shioyama describes synthesis of polyisoprene and polystyrene based composite materials by in-situ polymerization of styrene and isoprene monomers in presence of exfoliated graphite.
U.S. Pat. No. 5,776,372 describes an electrically conductive nanocomposite made with expanded graphite and various polymers such as polypropylene, polytetrafluoroethylene, and phenolic resin. Pan et al. describe synthesis of nylon-6 expanded graphite nanocomposite by polymerization of ϵ-caprolactam in presence of expanded graphite.
Chen et al. describe in-situ polymerization of methyl methacrylate in presence of expanded graphite to obtain an electrically conductive nanocomposite.
Xiao et al. describe making exfoliated graphite composite with improved thermal stability by in-situ polymerization of styrene in presence of exfoliated graphene.
RFID chips (tags) are used in many applications to individually track products. There is prior IP around RFID chips being embedded in golf balls to be used in combination with a device to track the individual ball.
Quimby et al., U.S. Pat. No. 5,910,057 for a Golf Ball With Distance And Locating System discloses a golf ball having a transmitter therein which emits a signal at a frequency of 900 MegaHertz.
The prior art fails to even recognize this problem.
The primary purpose of the present invention is to improve durability of golf ball core by incorporation of graphene in the core to improve the impact strength of the ball. This benefit can be seen in either a ball with single piece core, or a dual core with an outer core firmer than the inner core. Improved durability of the core by using graphene can result in higher mean time to fail (MTTF) upon repeated impact in a high speed testing device, or with a golf club in normal play.
Another objective is to improve aging properties due to the incorporation of graphene in the core for better retention of compression and COR over time.
One aspect of the present invention is a golf ball comprising a center core comprising polybutadiene and a graphene material in an amount ranging from 0.1 to 5.0 weight percent of the center core, and a cover layer disposed over the center core.
In a more preferred embodiment, the graphene material ranges from 0.4 to 2.5 weight percent of the center core. In an even more preferred embodiment, the graphene material ranges from 0.6 to 1.5 weight percent of the center core.
Another aspect of the present invention is a golf ball comprising a center core, an outer core, an inner mantle layer, an outer mantle layer, and a cover. The center core comprises a polybutadiene material and a graphene material in an amount ranging from 0.1 to 5.0 weight percent of the center core. The outer core is disposed over the center core. The inner mantle layer is disposed over the outer core. The inner mantle layer has a thickness ranging from 0.03 inch to 0.09 inch. The inner mantle layer is composed of an ionomer material. The inner mantle layer material has a plaque Shore D hardness ranging from 34 to 55. The outer mantle layer is disposed over the inner mantle layer. The outer mantle layer has a thickness ranging from 0.025 inch to 0.050 inch. The cover layer is disposed over the outer mantle layer. The cover layer has a thickness ranging from 0.025 inch to 0.040 inch. The cover layer has a lower Shore D hardness than the outer mantle layer. The outer mantle layer has a higher Shore D hardness than the inner mantle layer. The outer core has a higher Shore D hardness than the inner mantle layer and the center core. An integrated circuit (“IC”) is embedded within the inner core.
Yet another aspect of the present invention is a golf ball comprising a center core, an outer core, an inner mantle layer, an outer mantle layer, and a cover. The center core comprises a polybutadiene material and a graphene material in an amount ranging from 0.1 to 5.0 weight percent of the center core. The outer core is disposed over the center core. The inner mantle layer is disposed over the outer core. The inner mantle layer has a thickness ranging from 0.03 inch to 0.09 inch. The inner mantle layer material has a plaque Shore D hardness ranging from 30 to 50. The outer mantle layer is disposed over the inner mantle layer. The outer mantle layer has a thickness ranging from 0.025 inch to 0.070 inch. The outer mantle layer material has a plaque Shore D hardness ranging from 50 to 71. The inner mantle is thicker than the outer mantle, and the outer mantle is harder than the inner mantle. The cover layer is disposed over the outer mantle layer. The cover layer has a thickness ranging from 0.025 inch to 0.050 inch. The cover layer has a Shore D hardness less than the hardness of the outer mantle layer. The outer mantle layer has a higher Shore D hardness than the inner mantle layer. The outer core has a higher Shore D hardness than the inner mantle layer and the center core. An IC is embedded within the center core.
Yet another aspect of the present invention is a golf ball comprising a center core, an outer core, an inner mantle layer, an outer mantle layer, and a cover. The center core comprises a polybutadiene material and a graphene material in an amount ranging from 0.1 to 5.0 weight percent of the center core. The outer core is disposed over the center core. The inner mantle layer is disposed over the outer core. The inner mantle layer has a thickness ranging from 0.03 inch to 0.09 inch. The inner mantle layer material has a plaque Shore D hardness ranging from 36 to 44. The outer mantle layer is disposed over the inner mantle layer. The outer mantle layer has a thickness ranging from 0.025 inch to 0.070 inch. The outer mantle layer material has a plaque Shore D hardness ranging from 65 to 71. The inner mantle is thicker than the outer mantle, and the outer mantle is harder than the inner mantle. The cover layer is disposed over the outer mantle layer. The cover layer has a thickness ranging from 0.025 inch to 0.040 inch. The cover layer has a lower Shore D hardness than the outer mantle layer, the outer mantle layer has a higher Shore D hardness than the inner mantle layer, and the outer core has a higher Shore D hardness than the inner mantle layer and the center core. An IC is embedded within the center core.
Yet another aspect of the present invention is a golf ball comprising a center core, an inner mantle layer, a first center mantle layer, a second center mantle layer, an outer mantle layer, and a cover. The center core comprises a polybutadiene material and a graphene material in an amount ranging from 0.1 to 5.0 weight percent of the center core. The inner mantle layer is disposed over the center core. The inner mantle layer has a thickness ranging from 0.030 inch to 0.050 inch. The inner mantle layer material has a plaque Shore D hardness ranging from 30 to 40. The inner mantle layer is composed of a composed of an ionomer material. The first center mantle layer is disposed over the inner mantle layer. The first center mantle layer has a thickness ranging from 0.030 inch to 0.050 inch. The first center mantle layer material has a plaque Shore D hardness ranging from 40 to 55. The first center mantle layer is composed of a fully neutralized polymer material. The second center mantle layer is disposed over the second center mantle layer. The second center mantle layer has a thickness ranging from 0.030 inch to 0.050 inch. The second center mantle layer material has a plaque Shore D hardness ranging from 45 to 55. The second center mantle layer is composed of a fully neutralized polymer material. The outer mantle layer is disposed over the second center mantle layer. The outer mantle layer has a thickness ranging from 0.030 inch to 0.050 inch. The outer mantle layer is composed of an ionomer material. The outer mantle layer material has a plaque Shore D hardness ranging from 60 to 75. The cover layer is disposed over the outer mantle layer, and has a thickness ranging from 0.025 inch to 0.040 inch. An IC is embedded within the center core.
Yet another aspect of the present invention is a golf ball comprising a center core, an inner mantle layer, a first center mantle layer, a second center mantle layer, an outer mantle layer, and a cover. The center core comprises a polybutadiene material and a graphene material in an amount ranging from 0.1 to 5.0 weight percent of the center core. The inner mantle layer is disposed over the center core. The inner mantle layer has a thickness ranging from 0.030 inch to 0.050 inch. The inner mantle layer material has a plaque Shore D hardness ranging from 30 to 40. The inner mantle layer is composed of a composed of an ionomer material. The first center mantle layer is disposed over the inner mantle layer. The first center mantle layer has a thickness ranging from 0.030 inch to 0.050 inch. The first center mantle layer material has a plaque Shore D hardness ranging from 40 to 55. The first center mantle layer is composed of a fully neutralized polymer material. The second center mantle layer is disposed over the second center mantle layer. The second center mantle layer has a thickness ranging from 0.030 inch to 0.050 inch. The second center mantle layer material has a plaque Shore D hardness ranging from 45 to 55. The second center mantle layer is composed of a fully neutralized polymer material. The outer mantle layer is disposed over the second center mantle layer. The outer mantle layer has a thickness ranging from 0.030 inch to 0.050 inch. The outer mantle layer is composed of an ionomer material. The outer mantle layer material has a plaque Shore D hardness ranging from 60 to 75. The cover layer is disposed over the outer mantle layer, and has a thickness ranging from 0.025 inch to 0.040 inch. An IC is embedded within the center core.
A yet another aspect of the present invention is a method for forming a core for a golf ball. The method includes mixing a graphene material with a polybutadiene material to form a core mixture, wherein the graphene material ranges from 0.1 to 5.0 weight percent of the core mixture. The method also includes compression molding a core from the core mixture. The core preferably has a diameter ranging from 0.70 inch to 1.6 inch. The core mixture preferably comprises 40-90 weight percent of polybutadiene, 0.4 to 2.5 weight percent graphene material, 1-30 weight percent polyisoprene, 10-50 weight percent zinc diacrylate, 1-30 weight percent zinc oxide, 1-20 weight percent zinc stearate, and 0.1-10 weight percent peroxide initiator. An IC is embedded within the center core.
A more preferred embodiment of the method includes forming a cover over the core.
A more preferred embodiment of the method includes forming a mantle layer over the core.
A more preferred embodiment of the method includes that the core mixture is molded over an inner core to produce a dual core with a diameter ranging from 0.7 inch to 1.6 inches.
A more preferred embodiment of the method includes compression molding a core from the core mixture comprises compression molding an outer core layer over a center core comprising a polybutadiene mixture.
A more preferred embodiment of the method includes compression molding a core from the core mixture comprises compression molding a center core and an outer core over the center core, and the center core and the outer core comprise the core mixture.
Yet another aspect of the invention is a golf ball comprising an inner core, an outer core comprising a polybutadiene and a graphene material in an amount ranging from 0.1 to 5.0 weight percent of the outer core, a mantle layer and a cover. An IC is embedded within the inner core.
Yet another aspect of the present invention is a method for manufacturing a graphene core golf ball with an embedded integrated circuit (“IC”). The method includes placing a first half-slug of core material in a mold half. The method also includes placing an IC on a surface of the first half-slug. The method also includes placing the second half slug on the IC. The method also includes molding the first half-slug, the IC and the second half slug using a hot cure compression process to form a golf ball core with an embedded IC. The method also includes molding a cover over the golf ball core to generate a golf ball with an embedded IC. The density of the core material is adjusted in relation to the mass of the IC. The golf ball with an embedded IC conforms to a mass limitation of the USGA.
Another aspect of the present invention is a method for manufacturing a graphene core golf ball with an embedded IC. The method includes placing a first half-slug of core material in a mold half. The method also includes placing an IC on a surface of the first half-slug. The method also includes placing the second half slug on the IC. The method also includes molding the first half-slug, the IC and the second half slug using a hot cure compression process to form a golf ball core with an embedded IC. The method also includes molding a boundary layer over the golf ball core to generate a golf ball precursor product with an embedded IC. The method also includes molding a cover over the golf ball precursor product with an embedded IC to generate a golf ball with an embedded IC. The density of the core material is adjusted in relation to the mass of the IC. The golf ball with an embedded IC conforms to a mass limitation of the USGA.
Yet another aspect of the present invention is a limited flight golf ball. The graphene core golf ball preferably includes an IC configured to transmit a radiofrequency signal, a core composed of a polybutadiene material, and a cover disposed over the core. The IC is disposed within the core. The density of the core material is adjusted in relation to the mass of the IC. The graphene core golf ball with an embedded IC conforms to a mass limitation of the USGA.
Yet another aspect of the invention is a golf ball comprising an inner core comprising a polybutadiene and a graphene material in an amount ranging from 0.1 to 5.0 weight percent of the inner core, an outer core comprising a polybutadiene and a graphene material in an amount ranging from 0.1 to 5.0 weight percent of the outer core, a mantle layer, and a cover. An IC is embedded within the core.
Having briefly described the present invention, the above and further objects, features and advantages thereof will be recognized by those skilled in the pertinent art from the following detailed description of the invention when taken in conjunction with the accompanying drawings.
One objective of the present invention is to improve durability of golf ball core by incorporation of graphene in either the core the impact strength of the ball. This benefit can be seen in either a ball designed to have a low compression single piece core, or a dual core with an outer core firmer than the inner core. Improved durability of the core or mantle composition by using graphene can result in higher mean time to fail (MTTF) upon repeated impact in a high speed testing device, or with a golf club in normal play.
Another objective of the present invention is to improve aging properties due to the incorporation of graphene in either the core or mantle layer for better retention of compression and COR over time.
Polybutadiene based cores were made using following materials. Corresponding levels (by % wt) is mentioned next to each material: Polybutadiene with more than 60% 1,4-cis structure—(40-90%); Polyisoprene—(1-30%); Zinc diacrylate—(10-50%); Zinc oxide—(1-30%); Zinc stearate—(1-20%); Peroxide initiator—(0.1-10%); Zinc pentachlorothiophenol—(0-10%); Color—(0-10%); Barium sulfate—(0-20%); Graphene A (0.01-6%)—is available from various suppliers such as Cheap Tubes Inc., Ad-Nano Technologies Private Limited, MKnano, XG Sciences Inc., Angstron Materials Inc. (graphene A may have an average surface area between 15-50 m2/g); Graphene B (0.01-6%)—is available from various suppliers such as Cheap Tubes Inc., Ad-Nano Technologies Private Limited, MKnano, XG Sciences Inc., Angstron Materials Inc. (graphene B may have an average surface area between 300-400 m2/g); Graphene C (0.01-6%)—is available from various suppliers such as Cheap Tubes Inc., Ad-Nano Technologies Private Limited, MKnano, XG Sciences Inc., Angstron Materials Inc. (graphene C has a higher surface average than either graphene A or graphene B, and graphene C may have an average surface area between 400-800 m2/g); Graphene masterbatch (a masterbatch of 90-99% polybutadiene or polyisoprene and 1-10% graphene)—(0.1-50%)—custom compounding can be done with the help of various suppliers such as Preferred Compounding Corp, Dyna-Mix, Alttran, Callaway (in house compounding).
Four different single cores (formula 1 to 4) were made as shown in recipe in Table 1. Control group (formula 1) had no graphene
Compression is measured by applying a 200 pound load to the core and measuring its deflection, in inches. Compression=180−(deflection*1000).
Durability Testing of Solid Cores
Cores were shot at 150 fps in a pneumatic testing machine (PTM).
For each formula mentioned in Table 1, twelve cores were tested. The number of shots after which each core cracked was recorded for each core, and the cracked core was removed from the remainder of the test. The data was reported using a Weibull plot, and the mean time to fail was reported as shown in Table 1. As seen in
Dual Cores with graphene A only in the outer core.
In this study graphene A was introduced to the outer core in a dual core construction. Dual cores were made by compression molding two outer core halves around an already molded inner core having a diameter of approximately 0.940″ and a soft compression of approximately 0.200 inches of deflection under a 200 lb load. Curing of the inner and outer core was done at temperatures ranging between 150-400° F. for times ranging from 1-30 minutes. After molding, the dual cores were spherically ground to approximately 1.554″ prior to testing.
Table 2 and 3 give details of recipe of inner and outer cores. Components from these recipes were mixed in an internal mixer. Optionally, additional mixing was done using a two roll mill.
Compression of the outer core is measured by first making a full size core separately, measuring its compression, and then molding two halves around the inner core to complete the dual core.
Compression differential describes the difference between the outer core compression (as molded independently) and inner core compression. A higher compression differential is more susceptible to crack durability upon impact.
Compression is measured by applying a 200 pound load to the core and measuring its deflection, in inches. Compression=180−(deflection*1000)
Durability Testing of Dual Cores
Cores were shot at 175 fps in a pneumatic testing machine (PTM).
For each formula mentioned in Table 3, twelve cores were tested. The number of shots after which each core cracked was recorded for each core, and the cracked core was removed from the remainder of the test. The data was reported using a Weibull plot, and the mean time to fail was reported as shown in Table 3. As seen in
Dual cores with Graphene-C in outer core only
In this study Graphene-C (0.01-6%, available from various suppliers such as Cheap Tubes Inc., Ad-Nano Technologies Private Limited, MKnano, XG Sciences Inc., Angstron Materials Inc., and has an average surface area between 400-800 m2/g) was introduced to the outer core in a dual core construction. Dual cores were made by compression molding two outer core halves around an already molded inner core having a diameter of approximately 0.940″ and a soft compression of approximately 0.200 inches of deflection under a 200 lb load. Curing of the inner and outer core was done at temperatures ranging between 150-400 F for times ranging from 1-30 minutes. After molding, the dual cores were spherically ground to approximately 1.554″ prior to testing.
Tables 4 and 5 give details of recipe of inner and outer cores. Components from these recipes were mixed in an internal mixer. Optionally, additional mixing was done using a two roll mill.
Compression of the outer core is measured by first making a full size core separately, measuring its compression, and then molding two halves around the inner core to complete the dual core. Compression differential describes the difference between the outer core compression (as molded independently) and inner core compression. A higher compression differential is more susceptible to crack durability upon impact.
Table 4. Inner core recipe
Compression is measured by applying a 200 pound load to the core and measuring its deflection, in inches. Compression=180−(deflection*1000).
Durability Testing of Dual Cores
Cores were shot at 175 fps in a pneumatic testing machine (PTM).
For each formula mentioned in Table 5, twelve cores were tested. The number of shots after which each core cracked was recorded for each core, and the cracked core was removed from the remainder of the test. The data was reported using a Weibull plot, and the mean time to fail was reported as shown in Table 5. Testing was stopped after 100 shots. As shown in
Dual Cores with Graphene A in the Inner Core and the Outer Core.
In this study graphene A was introduced to the inner and outer core in a dual core construction. Table 6 gives details of recipe of inner and outer cores of these dual cores. Components from these recipes were mixed in an internal mixer. Optionally, additional mixing was done using a two roll mill. Dual cores were made by compression molding two outer core halves around an already molded inner core having a diameter of approximately 0.940″ and a soft compression of approximately 0.200 inches of deflection under a 200 lb load. Curing of the inner and outer core was done at temperatures ranging between 150-400 F for times ranging from 1-30 minutes. After molding, the dual cores were spherically ground to approximately 1.554″ prior to testing.
Compression of the outer core was measured by first making a full size core separately, measuring its compression, and then molding two halves around the inner core to complete the dual core.
Table 6. Dual Core Recipes with Graphene A in the Inner Core and the Outer Core
Compression is measured by applying a 200 pound load to the core and measuring its deflection, in inches. Compression=180−(deflection*1000).
For each formula mentioned in Table 6, twelve cores were tested. The number of shots after which each core cracked was recorded for each core, and the cracked core was removed from the remainder of the test. The data was reported using a Weibull plot, and the mean time to fail was reported as shown in Table 6. As seen in
Dual Cores with Graphene B in the Outer Core Only
In this study Graphene-B was introduced to the outer core in a dual core construction. Dual cores were made by compression molding two outer core halves around an already molded inner core having a diameter of approximately 0.940″ and a soft compression of approximately 0.200 inches of deflection under a 200 lb load. Curing of the inner and outer core was done at temperatures ranging between 150-400 F for times ranging from 1-30 minutes. After molding, the dual cores were spherically ground to approximately 1.554″ prior to testing.
Tables 7 and 8 give details of recipe of inner and outer cores. Components from these recipes were mixed in an internal mixer. Optionally, additional mixing was done using a two roll mill.
Compression of the outer core is measured by first making a full size core separately, measuring its compression, and then molding two halves around the inner core to complete the dual core. Compression differential describes the difference between the outer core compression (as molded independently) and inner core compression. A higher compression differential is more susceptible to crack durability upon impact.
The compression of Formula 17 is 64.3, the compression of Formula 18 is 68.0, and the compression of Formula 19 is 67.1. The compression of a dual core built from the inner core and the outer core is 42.1 for Formula 17, 45.8 for Formula 18 and 48.7 for Formula 19. Compression is measured by applying a 200 pound load to the core and measuring its deflection, in inches. Compression=180−(deflection*1000).
Durability Testing of Dual Cores
Cores were shot at 175 fps in a pneumatic testing machine (PTM).
For each formula mentioned in Table 8, twelve cores were tested. The number of shots after which each core cracked was recorded for each core, and the cracked core was removed from the remainder of the test. The data was reported using a Weibull plot, and the mean time to fail was reported as shown in Table 8. Testing was stopped after 100 shots. As seen in
Effect of Average Surface Area on Durability of Dual Core.
As seen in Table 9 and
Improvement in Curing by Addition of Graphene
To test if graphene helps reduce the time required to cure a given rubber core, temperature/time experiment was conducted. Controlled cores had no graphene whereas modified cores contained 1.6% graphene in an outer core. Inner cores did not have any graphene. A thermocouple was attached to an outer core of the dual core. Temperature of outer core was recorded while curing the dual core. Temperature inside outer core of a dual core was recorded as a function of time as shown in
Novelty of this process: Durability of the dual core with a high compression differential is greatly enhanced by incorporation of graphene in inner and outer core. The graphene reinforcement to the inner and outer core helps resist the high stresses experienced by the core when struck at high club speeds. Addition of graphene to the core recipe is very simple and it can be dispersed into the polybutadiene mixture during two roll milling process. Due to high thermal conductivity of graphene, overall thermal conductivity of cores can be increased with incorporation of graphene. With higher thermal conductivity of graphene reinforced cores, curing cycles can be made shorter. Shorter curing cycles can lead to higher output in production. Optionally, graphene can be introduced as a masterbatch in polybutadiene or polyisoprene, making its dispersion into polybutadiene rubber much easier and dust free.
Dual Core
As our experiment has shown, incorporating graphene into the inner and outer core recipe reinforces the strength of the outer core and provides greater crack durability protection in the design of a dual core golf ball, which is more susceptible to crack durability failures if the outer core is much firmer than the soft inner core.
In general, this is applicable when the inner core is softer than the outer core. More specifically, when the inner core has more than 0.200″ deflection under a 200 lb load, and the dual core is 40 compression or greater.
This is particularly crucial if the ball is a 4-piece construction with a single mantle layer with thickness less than 0.050″, or more specifically thinner than 0.040″, with 0.036″ being the target in this study.
The mantle component is preferably composed of the inner mantle layer and the outer mantle layer. The mantle component preferably has a thickness ranging from 0.05 inch to 0.15 inch, and more preferably from 0.06 inch to 0.08 inch. The outer mantle layer is preferably composed of a blend of ionomer materials. One preferred embodiment comprises SURLYN 9150 material, SURLYN 8940 material, a SURLYN AD1022 material, and a masterbatch. The SURLYN 9150 material is preferably present in an amount ranging from 20 to 45 weight percent of the cover, and more preferably 30 to 40 weight percent. The SURLYN 8945 is preferably present in an amount ranging from 15 to 35 weight percent of the cover, more preferably 20 to 30 weight percent, and most preferably 26 weight percent. The SURLYN 9945 is preferably present in an amount ranging from 30 to 50 weight percent of the cover, more preferably 35 to 45 weight percent, and most preferably 41 weight percent. The SURLYN 8940 is preferably present in an amount ranging from 5 to 15 weight percent of the cover, more preferably 7 to 12 weight percent, and most preferably 10 weight percent.
SURLYN 8320, from DuPont, is a very-low modulus ethylene/methacrylic acid copolymer with partial neutralization of the acid groups with sodium ions. SURLYN 8945, also from DuPont, is a high acid ethylene/methacrylic acid copolymer with partial neutralization of the acid groups with sodium ions. SURLYN 9945, also from DuPont, is a high acid ethylene/methacrylic acid copolymer with partial neutralization of the acid groups with zinc ions. SURLYN 8940, also from DuPont, is an ethylene/methacrylic acid copolymer with partial neutralization of the acid groups with sodium ions.
The inner mantle layer is preferably composed of a blend of ionomers, preferably comprising a terpolymer and at least two high acid (greater than 18 weight percent) ionomers neutralized with sodium, zinc, magnesium, or other metal ions. The material for the inner mantle layer preferably has a Shore D plaque hardness ranging preferably from 35 to 77, more preferably from 36 to 44, a most preferably approximately 40. The thickness of the outer mantle layer preferably ranges from 0.025 inch to 0.050 inch, and is more preferably approximately 0.037 inch. The mass of an insert including the dual core and the inner mantle layer preferably ranges from 32 grams to 40 grams, more preferably from 34 to 38 grams, and is most preferably approximately 36 grams. The inner mantle layer is alternatively composed of a HPF material available from DuPont. Alternatively, the inner mantle layer 14b is composed of a material such as disclosed in Kennedy, III et al., U.S. Pat. No. 7,361,101 for a Golf Ball And Thermoplastic Material, which is hereby incorporated by reference in its entirety.
The outer mantle layer is preferably composed of a blend of ionomers, preferably comprising at least two high acid (greater than 18 weight percent) ionomers neutralized with sodium, zinc, or other metal ions. The blend of ionomers also preferably includes a masterbatch. The material of the outer mantle layer preferably has a Shore D plaque hardness ranging preferably from 55 to 75, more preferably from 65 to 71, and most preferably approximately 67. The thickness of the outer mantle layer preferably ranges from 0.025 inch to 0.040 inch, and is more preferably approximately 0.030 inch. The mass of the entire insert including the core, the inner mantle layer and the outer mantle layer preferably ranges from 38 grams to 43 grams, more preferably from 39 to 41 grams, and is most preferably approximately 41 grams.
In an alternative embodiment, the inner mantle layer is preferably composed of a blend of ionomers, preferably comprising at least two high acid (greater than 18 weight percent) ionomers neutralized with sodium, zinc, or other metal ions. The blend of ionomers also preferably includes a masterbatch. In this embodiment, the material of the inner mantle layer has a Shore D plaque hardness ranging preferably from 55 to 75, more preferably from 65 to 71, and most preferably approximately 67. The thickness of the outer mantle layer preferably ranges from 0.025 inch to 0.040 inch, and is more preferably approximately 0.030 inch. Also in this embodiment, the outer mantle layer 14b is composed of a blend of ionomers, preferably comprising a terpolymer and at least two high acid (greater than 18 weight percent) ionomers neutralized with sodium, zinc, magnesium, or other metal ions. In this embodiment, the material for the outer mantle layer 14b preferably has a Shore D plaque hardness ranging preferably from 35 to 77, more preferably from 36 to 44, a most preferably approximately 40. The thickness of the outer mantle layer preferably ranges from 0.025 inch to 0.100 inch, and more preferably ranges from 0.070 inch to 0.090 inch.
In yet another embodiment wherein the inner mantle layer is thicker than the outer mantle layer and the outer mantle layer is harder than the inner mantle layer, the inner mantle layer is composed of a blend of ionomers, preferably comprising a terpolymer and at least two high acid (greater than 18 weight percent) ionomers neutralized with sodium, zinc, magnesium, or other metal ions. In this embodiment, the material for the inner mantle layer has a Shore D plaque hardness ranging preferably from 30 to 77, more preferably from 30 to 50, and most preferably approximately 40. In this embodiment, the material for the outer mantle layer has a Shore D plaque hardness ranging preferably from 40 to 77, more preferably from 50 to 71, and most preferably approximately 67. In this embodiment, the thickness of the inner mantle layer preferably ranges from 0.030 inch to 0.090 inch, and the thickness of the outer mantle layer ranges from 0.025 inch to 0.070 inch.
Preferably the inner core has a diameter ranging from 0.75 inch to 1.20 inches, more preferably from 0.85 inch to 1.05 inch, and most preferably approximately 0.95 inch. Preferably the inner core 12a has a Shore D hardness ranging from 20 to 50, more preferably from 25 to 40, and most preferably approximately 35. Preferably the inner core has a mass ranging from 5 grams to 15 grams, 7 grams to 10 grams and most preferably approximately 8 grams.
Preferably the outer core has a diameter ranging from 1.25 inch to 1.55 inches, more preferably from 1.40 inch to 1.5 inch, and most preferably approximately 1.5 inch. Preferably the outer core has a Shore D surface hardness ranging from 40 to 65, more preferably from 50 to 60, and most preferably approximately 56. Preferably the outer core is formed from a polybutadiene, zinc diacrylate, zinc oxide, zinc stearate, a peptizer and peroxide. Preferably the combined inner core and outer core have a mass ranging from 25 grams to 35 grams, 30 grams to 34 grams and most preferably approximately 32 grams.
Preferably the inner core has a deflection of at least 0.230 inch under a load of 220 pounds, and the core has a deflection of at least 0.080 inch under a load of 200 pounds. As shown in
In an alternative embodiment of the golf ball shown in
In one embodiment, the golf ball comprises a core, a mantle layer and a cover layer. The core comprises an inner core sphere, an intermediate core layer and an outer core layer. The intermediate core layer is composed of a highly neutralized ionomer and has a Shore D hardness less than 40. The outer core layer is composed of a highly neutralized ionomer and has a Shore D hardness less than 45. A thickness of the intermediate core layer is greater than a thickness of the outer core layer. The mantle layer is disposed over the core, comprises an ionomer material and has a Shore D hardness greater than 55. The cover layer is disposed over the mantle layer comprises a thermoplastic polyurethane material and has a Shore A hardness less than 100. The golf ball has a diameter of at least 1.68 inches. The mantle layer is harder than the outer core layer, the outer core layer is harder than the intermediate core layer, the intermediate core layer is harder than the inner core sphere, and the cover layer is softer than the mantle layer.
In another embodiment, shown in
In a particularly preferred embodiment of the invention, the golf ball preferably has an aerodynamic pattern such as disclosed in Simonds et al., U.S. Pat. No. 7,419,443 for a Low Volume Cover For A Golf Ball, which is hereby incorporated by reference in its entirety. Alternatively, the golf ball has an aerodynamic pattern such as disclosed in Simonds et al., U.S. Pat. No. 7,338,392 for An Aerodynamic Surface Geometry For A Golf Ball, which is hereby incorporated by reference in its entirety.
Various aspects of the present invention golf balls have been described in terms of certain tests or measuring procedures. These are described in greater detail as follows.
As used herein, “Shore D hardness” of the golf ball layers is measured generally in accordance with ASTM D-2240 type D, except the measurements may be made on the curved surface of a component of the golf ball, rather than on a plaque. If measured on the ball, the measurement will indicate that the measurement was made on the ball. In referring to a hardness of a material of a layer of the golf ball, the measurement will be made on a plaque in accordance with ASTM D-2240. Furthermore, the Shore D hardness of the cover is measured while the cover remains over the mantles and cores. When a hardness measurement is made on the golf ball, the Shore D hardness is preferably measured at a land area of the cover.
As used herein, “Shore A hardness” of a cover is measured generally in accordance with ASTM D-2240 type A, except the measurements may be made on the curved surface of a component of the golf ball, rather than on a plaque. If measured on the ball, the measurement will indicate that the measurement was made on the ball. In referring to a hardness of a material of a layer of the golf ball, the measurement will be made on a plaque in accordance with ASTM D-2240. Furthermore, the Shore A hardness of the cover is measured while the cover remains over the mantles and cores. When a hardness measurement is made on the golf ball, Shore A hardness is preferably measured at a land area of the cover
The resilience or coefficient of restitution (COR) of a golf ball is the constant “e,” which is the ratio of the relative velocity of an elastic sphere after direct impact to that before impact. As a result, the COR (“e”) can vary from 0 to 1, with 1 being equivalent to a perfectly or completely elastic collision and 0 being equivalent to a perfectly or completely inelastic collision.
COR, along with additional factors such as club head speed, club head mass, ball weight, ball size and density, spin rate, angle of trajectory and surface configuration as well as environmental conditions (e.g. temperature, moisture, atmospheric pressure, wind, etc.) generally determine the distance a ball will travel when hit. Along this line, the distance a golf ball will travel under controlled environmental conditions is a function of the speed and mass of the club and size, density and resilience (COR) of the ball and other factors. The initial velocity of the club, the mass of the club and the angle of the ball's departure are essentially provided by the golfer upon striking. Since club head speed, club head mass, the angle of trajectory and environmental conditions are not determinants controllable by golf ball producers and the ball size and weight are set by the U.S.G.A., these are not factors of concern among golf ball manufacturers. The factors or determinants of interest with respect to improved distance are generally the COR and the surface configuration of the ball.
The coefficient of restitution is the ratio of the outgoing velocity to the incoming velocity. In the examples of this application, the coefficient of restitution of a golf ball was measured by propelling a ball horizontally at a speed of 125+/−5 feet per second (fps) and corrected to 125 fps against a generally vertical, hard, flat steel plate and measuring the ball's incoming and outgoing velocity electronically. Speeds were measured with a pair of ballistic screens, which provide a timing pulse when an object passes through them. The screens were separated by 36 inches and are located 25.25 inches and 61.25 inches from the rebound wall. The ball speed was measured by timing the pulses from screen 1 to screen 2 on the way into the rebound wall (as the average speed of the ball over 36 inches), and then the exit speed was timed from screen 2 to screen 1 over the same distance. The rebound wall was tilted 2 degrees from a vertical plane to allow the ball to rebound slightly downward in order to miss the edge of the cannon that fired it. The rebound wall is solid steel.
As indicated above, the incoming speed should be 125±5 fps but corrected to 125 fps. The correlation between COR and forward or incoming speed has been studied and a correction has been made over the ±5 fps range so that the COR is reported as if the ball had an incoming speed of exactly 125.0 fps.
The measurements for deflection, compression, hardness, and the like are preferably performed on a finished golf ball as opposed to performing the measurement on each layer during manufacturing.
Preferably, in a five layer golf ball comprising an inner core, an outer core, an inner mantle layer, an outer mantle layer and a cover, the hardness/compression of layers involve an inner core with the greatest deflection (lowest hardness), an outer core (combined with the inner core) with a deflection less than the inner core, an inner mantle layer with a hardness less than the hardness of the combined outer core and inner core, an outer mantle layer with the hardness layer of the golf ball, and a cover with a hardness less than the hardness of the outer mantle layer. These measurements are preferably made on a finished golf ball that has been torn down for the measurements.
Preferably the inner mantle layer is thicker than the outer mantle layer or the cover layer. The dual core and dual mantle golf ball creates an optimized velocity-initial velocity ratio (Vi/IV), and allows for spin manipulation. The dual core provides for increased core compression differential resulting in a high spin for short game shots and a low spin for driver shots. A discussion of the USGA initial velocity test is disclosed in Yagley et al., U.S. Pat. No. 6,595,872 for a Golf Ball With High Coefficient Of Restitution, which is hereby incorporated by reference in its entirety. Another example is Bartels et al., U.S. Pat. No. 6,648,775 for a Golf Ball With High Coefficient Of Restitution, which is hereby incorporated by reference in its entirety.
A method 100 for manufacturing a graphene core golf ball with an embedded IC is shown in
As shown in
As shown in
As shown in
As shown in
The present invention takes an IC 40 smaller than ¾″×½″×¼″ and sandwiches it between two half slugs 35a and 35b of core material. One half slug 35a is placed in the mold half 30a, the IC 40 is placed on top, the second half slug 35b is placed on top “sandwiching” the IC 40 between the two halves 35a and 35b which are then molded together in a hot cure compression molding process to form the core 25 of the golf ball 20.
The cover 26 is then molded onto the core 25 either by an injection molding or compression molding process. This type of ball can be comprised of multiple cover layers.
The density of the core 25 should be adjusted to account for the density of the IC so that the total ball weight falls with USGA conformance guidelines.
From the foregoing it is believed that those skilled in the pertinent art will recognize the meritorious advancement of this invention and will readily understand that while the present invention has been described in association with a preferred embodiment thereof, and other embodiments illustrated in the accompanying drawings, numerous changes, modifications and substitutions of equivalents may be made therein without departing from the spirit and scope of this invention which is intended to be unlimited by the foregoing except as may appear in the following appended claims. Therefore, the embodiments of the invention in which an exclusive property or privilege is claimed are defined in the following appended claims.
The Present Application is a continuation application of U.S. patent application Ser. No. 16/273,494, filed on Feb. 12, 2019, which is a divisional application of U.S. patent application Ser. No. 15/785,163, filed on Oct. 16, 2017, now U.S. patent Ser. No. 10/252,117, issued on Apr. 9, 2019, which is a continuation-in-part application of U.S. patent application Ser. No. 15/436,169, filed on Feb. 17, 2017, now U.S. Pat. No. 9,789,366, issued on Oct. 17, 2017, which claims priority to U.S. Provisional Patent Application No. 62/401,034, filed on Sep. 28, 2016, and U.S. patent application Ser. No. 15/785,163 is also a continuation-in-part application of U.S. patent application Ser. No. 15/649,172 filed on Jul. 13, 2017, now U.S. Pat. No. 1,001,660, issued on Jul. 10, 2018, which is a continuation application of U.S. patent application Ser. No. 14/921,243, filed on Oct. 23, 2015, now U.S. Pat. No. 9,707,454, issued on Jul. 18, 2017, which claims priority to U.S. Provisional Patent Application No. 62/068,489, filed on Oct. 24, 2014, each of which is hereby incorporated by reference in its entirety each of which is hereby incorporated by reference in its entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3351347 | Smith | Nov 1967 | A |
| 3458205 | Douglas | Jul 1969 | A |
| 3782730 | Horchler | Jan 1974 | A |
| 4660039 | Barricks | Apr 1987 | A |
| 5423549 | Englmeier | Jun 1995 | A |
| 5447314 | Yamazaki | Sep 1995 | A |
| 5626531 | Little | May 1997 | A |
| 6011466 | Goldman | Jan 2000 | A |
| 6042487 | Schrimmer | Mar 2000 | A |
| 6113504 | Kuesters | Sep 2000 | A |
| 6634959 | Kuesters | Oct 2003 | B2 |
| 6712487 | Liou | Mar 2004 | B2 |
| 6742449 | Sosin | Jun 2004 | B2 |
| 6783468 | Sullivan | Aug 2004 | B2 |
| 7207902 | Hamlin | Apr 2007 | B1 |
| 7220191 | Onoda | May 2007 | B2 |
| 7691009 | Savarese | Apr 2010 | B2 |
| 7724145 | Batra | May 2010 | B2 |
| 7766766 | Savarese | Aug 2010 | B2 |
| 7785215 | Kohnen, II | Aug 2010 | B2 |
| 7791982 | Karr | Sep 2010 | B2 |
| 7811163 | Ratcliffe | Oct 2010 | B2 |
| 7883428 | Balardeta | Feb 2011 | B1 |
| 7946926 | Balardeta | May 2011 | B1 |
| 8519906 | Richards | Aug 2013 | B2 |
| 9370694 | Luciano, Jr. | Jun 2016 | B2 |
| 9393462 | Farrell | Jul 2016 | B2 |
| 9498680 | Luciano, Jr. | Nov 2016 | B2 |
| 9498682 | Luciano, Jr. | Nov 2016 | B2 |
| 9630063 | Thompson | Apr 2017 | B1 |
| 9643056 | Luciano, Jr. | May 2017 | B2 |
| 9789366 | Chavan | Oct 2017 | B1 |
| 10039959 | Chavan | Aug 2018 | B2 |
| 10052524 | Chavan | Aug 2018 | B1 |
| 10062027 | Komatsu | Aug 2018 | B2 |
| 10086237 | Chavan | Oct 2018 | B1 |
| 10252114 | Petrich | Apr 2019 | B1 |
| 10252117 | Simonds | Apr 2019 | B1 |
| 10315077 | Komatsu | Jun 2019 | B2 |
| 10376744 | Petrich | Aug 2019 | B1 |
| 10441850 | Petrich | Oct 2019 | B1 |
| 10456629 | Chavan | Oct 2019 | B1 |
| 10500445 | Chavan | Dec 2019 | B1 |
| 10507362 | Chavan | Dec 2019 | B1 |
| 10688366 | Petrich | Jun 2020 | B1 |
| 10709937 | Jeon | Jul 2020 | B1 |
| 10722755 | Chavan | Jul 2020 | B1 |
| 10729939 | Chavan | Aug 2020 | B2 |
| 20160279482 | DuFaux | Sep 2016 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 62401034 | Sep 2016 | US | |
| 62068489 | Oct 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15785163 | Oct 2017 | US |
| Child | 16273494 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16273494 | Feb 2019 | US |
| Child | 16595099 | US | |
| Parent | 14921243 | Oct 2015 | US |
| Child | 15649172 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15436169 | Feb 2017 | US |
| Child | 15785163 | US | |
| Parent | 15649172 | Jul 2017 | US |
| Child | 15436169 | US |