Graphene laminate structures

Abstract
Provided are methods of forming graphene laminate compositions and architectures. The method comprises: (i) contacting a graphene structure comprising one or more planar graphene sheets with a first interlayer material; (ii) depositing of a conductive material, where in the conductive material is deposited along an edge of the graphene and one end of the first interlayer; and (iii) contacting the graphene structure with a second interlayer material. Also provided are graphene laminates structures comprising doped graphene films having improved mechanical strength, electrical mobility and optical transparency.
Description
FIELD OF THE INVENTION

This present disclosure relates to graphene laminate compositions and architectures having improved mechanical strength, electrical mobility and optical transparency, and to methods of preparing the graphene laminate compositions and architectures.


BACKGROUND

Numerous applications require a laminate window material that is optically transparent (for visual clarity), strong (for protection, security, and long lifetime), and electrically conductive (for the reduction of electromagnetic interference, i.e. EMI shielding). For example, military and security applications often require optically transparent windows that are both ballistic and blast resistant and block the transmission of electromagnetic radiation. Windows capable of EMI shielding are typically composed with a thin film or grid of conductive metal or material (including, but not limited to copper or silver) on, or incorporated into, a transparent substrate (including, but not limited to glass, acrylic, and glass-polymer laminates).


EMI shielding films have an inherent tradeoff between the shielding effectiveness and the optical transparency. For a given material, the shielding effectiveness can be increased by making the material thicker, but at the expense of reduced optical transparency. New materials are desired that, relative to state of the art, yield higher optical transparency for a given shielding effectiveness.


Laminate glass architectures (for example, ballistic and/or blast resistant glass) suffer from a similar tradeoff: ballistic and blast protection can be improved by adding thicker or additional layers of glass or plastic, but at the expense of reduced optical transparency and physical weight. New materials are desired that, when incorporated into standard architectures, yield higher optical transparency for the same protection.


SUMMARY OF THE INVENTION

It is an object of the present invention to provide a method of forming graphene laminate structures that provide EMI shielding, for example, when incorporated into laminate windows. It is another object to provide graphene laminates and laminated window panels that provide EMI shielding. In another aspect, the invention provides a laminated window panel that provides EMI shielding and at least one or more of impact resistance, blast resistance and ballistic resistance.


The invention provides a method for producing a graphene laminate, the method comprising: (i) contacting a graphene structure comprising one or more planar graphene sheets with a first interlayer material; (ii) depositing of a conductive material, wherein the conductive material is deposited along an edge of the graphene and one end of the first interlayer; and (iii) contacting the graphene structure with a second interlayer material.


The invention further provides a graphene laminate structure that comprises: one or more layers of graphene between a first interlayer and a second interlayer; and a conductive material along an edge of the graphene and one end of the interlayers. The graphene laminate structure is incorporated into laminate window structures to provide EMI shielding and preferably at least one or more of impact resistance, blast resistance and ballistic resistance


A more complete understanding of the present invention, as well as further features and advantages of the present invention, will be obtained by reference to the following detailed description of drawings.





BRIEF DESCRIPTION OF THE FIGURES


FIG. 1 is a schematic view of a graphene laminate structure.



FIGS. 2A-2D are illustrations of exemplary spatial embodiments for conductive grounding material.



FIG. 3 is a schematic view of a laminated glass panel.



FIG. 4 is a schematic view of an alternative laminated glass panel.



FIG. 5 is a schematic view of an additional alternative laminated glass panel.





DETAILED DESCRIPTION OF THE INVENTION

Provided herein are graphene laminates structures comprising doped graphene films that have improved mechanical strength, electrical mobility and optical transparency. Further provided are methods of forming graphene laminates comprising doped graphene films.


Also provided are graphene laminate structures comprising:

    • one or more layers of graphene interposed between a first interlayer and a second interlayer; and a conductive material along at least one edge of the graphene layer.


Also provided are laminate windows comprising:

    • one or more layers of graphene interposed between a first interlayer and a second interlayer;
    • a conductive material along at least one edge of the graphene layer;
    • one or more glass or polycarbonate panels adjacent to the first interlayer and/or the second interlayer.


Graphene films combine mechanical strength, electrical mobility, and optical transparency (2.3% absorption per layer over all visible wavelengths) into one material. Graphene films have been shown to increase the strength of polymers. However, in order for graphene to serve as a high-performance EMI shielding material, it should have a sufficiently high electrical conductivity (proportional to the product of the graphene mobility and carrier concentration) in the plane of the film. Regarding mobility, the extremely high mobility values often quoted for graphene are under conditions where it is suspended, rather than in contact with a substrate. Achieving a high value of mobility when in contact with a substrate involves control over the scattering of graphene charge carriers through substrate interactions that can reduce mobility values. Regarding carrier concentration, intrinsic (undoped) graphene has a low carrier concentration. To achieve sufficiently high carrier concentrations to serve as high-performance EMI shielding can be improved by doping graphene (donating electrons to serve as charge carriers or borrowing electrons so that holes serve as charge carriers). Graphene can be doped to sufficiently high values of carrier concentration without altering the optical transmission of 2.3% per layer, thus opening up the possibility of highly optically transparent graphene films that provide strong EMI shielding. Intercalation compounds of alkali metals with multi-layer graphene (such as LiC6) can also be formed, which are so strongly doped that optical absorption is strongly decreased below 2.3% per layer due to the occupation of conduction band states by electrons.


The term “graphene” as used herein refers to a polycyclic aromatic molecule formed from a plurality of carbon atoms covalently bound to each other. The covalently bound carbon atoms may form a 6-membered ring as a repeating unit, or may further include at least one of a 5-membered ring and a 7-membered ring. Accordingly, in the graphene, the covalently bound carbon atoms (generally having sp2 hybridization) form a single layer. The graphene may have various structures which are determined according to the amount of the 5-membered rings and/or 7-membered rings which may be contained in the graphene. The graphene may have a single layer (single-layer graphene) or a plurality of layers (multi-layer graphene, also sometimes referred to as few-layer graphite). Graphene layers in multi-layer graphene each occupy about 340 μm, and so multi-layer graphene (1-50 layers) may have a thickness of about 0.3 nm to about 170 nm, or in other aspects from about 1 nm to about 30 nm. These layer spacings increase by about 10% (from 340 pm to 370 pm per layer) for LiC6 relative to unintercalated multi-layer graphene.


As used herein, the term “doping” refers to a process of providing charge-carriers by supplying electrons to, or removing electrons from, a part of a conjugated bonding it-orbit to provide conductivity to a conjugated compound, e.g., a polycyclic aromatic carbon compound, such as graphene. Here, the process of adding electrons or removing electrons is referred to as “doping”.


The term “dopant” as used herein refers an organic dopant, an inorganic dopant, or a combination including at least one of the foregoing.



FIG. 1, for example, provides an illustration of an exemplary graphene laminate structure comprising (i) a graphene structure comprising one or more planar graphene sheets adjacent to a first interlayer material; (ii) a conductive material along an edge of the graphene and one end of the first interlayer; and (iii) a second interlayer material.


The graphene laminate structure of FIG. 1 may be formed, for example, by (i) contacting a graphene structure comprising one or more planar graphene sheets with a first interlayer material; (ii) depositing of a conductive material, where in the conductive material is deposited along an edge of the graphene and one end of the first interlayer; and (iii) contacting the graphene structure with a second interlayer material. In an embodiment, steps (ii) and (iii) can be sequentially repeated 1-5 times.


According to an exemplary embodiment, the graphene laminate comprises a first interlayer 102, a graphene structure 104, a second interlayer 106, a conductive material 108, and optionally a conductive tab 110.


The first and second interlayer materials can be the same or different materials. The interlayers are preferable made of polymers, for example polyamides, polyimides, polychloroethylenes, polyurethanes, polyvinylethers, polythioureas, polyacrylates, polycarbonates, polyesters, polyethylenes, polypropylenes, polysytrenes, PTFE, polyethylacetates, polyvinylacetates and fluoropolymers. Preferred polymers include poly(methylmethacrylate), polyvinyl butyral, ethylene-vinyl acetate, thermoplastic polyurethane, polyethylene terephthalate, thermoset ethylene-vinyl acetate, polycarbonate and polyethylene.


In one aspect, one or more of the interlayers further comprises a dopant that increases the conductivity of the adjacent graphene. The dopant in the interlayer serves to increase the concentration of charge carriers in the adjacent graphene layer. In a further embodiment, the dopant may be an alkali-metal salt. The alkali metal of the salt may be selected from Na, Cs, Li, K, and Rb. In a further aspect, the anion in the alkali metal salt can be perchlorate, iodide, and carbonate. In one aspect, the alkali metal salt is MClO4 or MI, where M can be Li, Na or K. The concentration of alkali metal is in the range of about 2% to about 45% by weight (w/w). In an embodiment, the alkali metal ions intercalate in between the layers of the multi-layer graphene to form MC72, MC36, MC18, MC12, and/or MC6 (i.e., LiC72, LiC36, LiC18, LiC12, and/or LiC6).


In another aspect, the alkali metal dopant is intercalated into the graphene structure 104 prior to its incorporation into a graphene laminate structure. The alkali metal dopant may be Na, Cs, Li, K, and Rb, with Li, Na and K being preferred. The graphene may be doped with the alkali metal dopant by, for example, contacting the graphene with a suitable electrolyte solution. The counterion to the alkali metal may be any anion that is unreactive and stable under the conditions of the graphene structure fabrication and use. Preferred counterions include ClO4 and PF6. The electrolyte solution further comprises a solvent for the alkali metal salt. Preferred solvents include ethylene carbonate (EC), diethyl carbonate (DEC), dimethyl carbonate (DMC), ethyl methyl carbonate (EMC), and mixtures thereof. The alkali metal salt may present in the electrolyte solution in a concentration from 0.5 to 2 M, or in a concentration sufficient to form MC72, MC36, MC18, MC12, and/or MC6 (i.e., LiC72, LiC36, LiC18, LiC12, and/or LiC6), and preferably MC6. The electrolyte solution may further be in contact with a metal source, such as a metal foil, which maintains a high concentration of alkali metal in the electrolyte solution. In one embodiment, the multilayer graphene is contacted with 1-1.2 M LiPF6 in 1:1 wt ratio of EC/DEC (Lithium hexafluorophosphate solution in ethylene carbonate and diethyl carbonate, while the electrolyte is contacted with Li metal foil. The alkali metal ions are intercalated into the multilayer graphene (for example, forming LiC72, LiC36, LiC18, LiC12, and/or LiC6). The intercalated graphene is then used to form the laminate structure as provided herein. In this case, the interlayers preferably do not include additional alkali metal ions.


In an embodiment, a liquid adhesive solution is applied between the graphene structure 104 and at least one of the first interlayer 102 and second interlayer 106. The liquid adhesive preferably comprises a solvent and one or more polymers. The polymers include, for example, polyamides, polyimides, polychloroethylenes, polyurethanes, polyvinylethers, polythioureas, polyacrylates, polycarbonates, polyesters, polyethylenes, polypropylenes, polysytrenes, PTFE, polyethylacetates, polyvinylacetates and fluoropolymers. Preferred polymers include poly(methylmethacrylate), polyvinyl butyral, ethylene-vinyl acetate, thermoplastic polyurethane, polyethylene terephthalate, thermoset ethylene-vinyl acetate, polycarbonate and polyethylene. Preferred solvents include water, chlorobenzene, acetone, methanol, N-methyl-2-pyrrolidone, tetrahydrofuran, dimethylformamide, hexane, toluene, isopropyl alcohol, acetonitrile, chloroform, acetic acid, 2-methoxyethanol, n-butylamine, or combinations thereof. The liquid adhesive solution can be cured with heat. In an embodiment, the liquid adhesive solution is cured to a final temperature in the range of about 130° C. to about 160° C., and the final temperature can be held or about 5 minutes to about 4 hours. The adhesive may further comprise a dopant that increases the conductivity of the adjacent graphene, as described above.


In an embodiment, the graphene laminate can include one or more spacer layers between one or more of the graphene layers.


The graphene structure 104 can be prepared by chemical vapor deposition (CVD). In this process, graphene is formed on a catalytic metal substrate through the decomposition of hydrocarbon precursors such as methane, commonly mixed with hydrogen, at suitable temperatures (˜1000 C-1100 C) and pressures (˜1 mTorr-10 Torr). (G. Deokar et al., Towards high quality CVD graphene growth and transfer, Carbon, 89, 82-92 (2015); N. C. Bartelt and K. F. McCarty, Graphene growth on metal surfaces, MRS Bulletin, 37, 1158-1165 (2012)). Suitable metal substrates may be copper, nickel, platinum, or iridium. To achieve uniform single-layer graphene sheets, most often a copper substrate is used. For multi-layer graphene, either copper or, more commonly, nickel is selected. These specific metals are chosen as they both act as a catalyst for graphene growth and due to the similar lattice spacing to that of graphene, provide minimal lattice mismatch between the materials.


The graphene structure 104 comprises 1-50 planar graphene sheets. The 1-50 graphene sheets can be applied to the interlayer material individually or as a growth of multi-layer graphene. In one aspect, the graphene sheets are intercalated with alkali metal ions.


Conductive material 108 provides a ground source. In an embodiment, the conductive material 108 may be a metal or adhesive tape. Representative metals include copper, silver and aluminum. The conductive material may be deposited by physical vapor deposition, thermal evaporation, sputtering or plating. The conductive material 108 can be deposited along an edge of the graphene in numerous spatial orientations. Examples of possible spatial orientations of the conductive material are illustrated in FIGS. 2A-D. For example, the conductive material can be present around the border of the graphene or along one edge, or on one spot along the edge, however the invention is not limited to these exemplary patterns. A small overlap between the conductive material and graphene is preferred to allow for sufficient electrical contact. In the embodiment shown in 2D, the graphene may not be one continuous sheet over the entire area of the interlayer, but may be tiled, with the conductive material connecting tiles along their adjacent edges.


The described methods can be used to prepare a graphene laminate that provides EMI shielding, wherein the graphene laminate comprises one or more layers of graphene between a first interlayer and a second interlayer; and a conductive material along an edge of the graphene and one end of the interlayers.


In an embodiment, the invention provides a laminated window panel that provides EMI shielding and at least one or more of impact resistance, blast resistance, and ballistic resistance, wherein the laminated window panel comprises two or more sheets of glass and/or polycarbonate bonded between one or more sheets of the graphene laminate structure of FIG. 1. As shown in FIG. 3, the laminated window panel comprises one or more layers of glass or polycarbonate 302, wherein the laminate can comprise layers of glass, or layers of polycarbonate, or both glass and polycarbonate. The laminated glass panel further comprises one or more interlayers 304, as previously defined. The laminated glass panel further comprises one or more graphene structure(s) 306, and a conductive material 308. The graphene structure may comprise from 1-50 layers of graphene. In preferred embodiments of the laminate window of FIG. 3, each of the graphene structures 306 are comprised of a film of multi-layer graphene having from 1-50 graphene layers, which is preferably intercalated with alkali metal ions. The graphene structure 306 may further comprise multiple laminates of interlayer/multilayer graphene (i.e., interlayer/multilayer graphene/interlayer/multilayer graphene/interlayer/ . . . , etc.).


The particular orientation of the various embodiments in the drawings is for illustrative purposes only, and the embodiments may be rotated relative to the shown orientations in some applications. An example of this is shown in FIG. 4, where the graphene structures are angled in a sawtooth pattern. Since the graphene structures largely provide EMI shielding via reflection of incoming RF radiation, the sawtooth pattern reflects the rejected power to the edge of the laminate structure, rather than creating cavities between adjacent graphene structures where radiation may be trapped, for example by reflecting back and forth.



FIG. 4 also shows an optional RF absorbing layer 309 to absorb the RF radiation that is reflected to the edge of the structure. The radiation-absorbent material is a material which has been specially designed and shaped to absorb incident RF radiation. The optional RF absorbing layer may be composed and any suitable material(s) that absorb RF radiation, such as carbon foam, silicon carbide and or carbon nanotubes. The carbon foam radiation-absorbent material may consist of a fireproofed urethane foam loaded with conductive carbon black (carbonyl iron spherical particles and/or crystalline graphite particles) in mixtures between 0.05% and 0.1%.


This same effect of shunting reflected power to the edge of the structure may also be accomplished by structuring the surface of the graphene structures, as shown in FIG. 5, rather than (or in tandem with) angling the entire layer. These structures may be hierarchical, with patterning as small as few micron on top of patterning at tens of microns and so on, up to cm-scale patterns. FIG. 5 shows a schematic view of a glass panel in which the graphene structure 306 has structured (or patterned) 310. These structures may be formed by stamping or etching the patterning into the interlayer. When the graphene structure is contacted with the interlayer, it conformally coats the interlayer, assuming the underlying spatial structure of the interlayer. While FIG. 5 shows square patterning, the patterning may be any shape including sawtooth, triangular, hemispherical, etc.


The description provided herein, and the claims that follow, pertain to any structures that have the described relationships between various features, regardless of whether the structures are in the particular orientation of the drawings, or are rotated relative to such orientation.


The cross-sectional views of the accompanying illustrations only show features within the planes of the cross-sections, and do not show materials behind the planes of the cross-sections in order to simplify the drawings.

Claims
  • 1. A method of forming a graphene laminate, the method comprising: (i) contacting a graphene structure comprising one or more planar graphene sheets with a first interlayer material;(ii) depositing of a conductive material, wherein the conductive material is deposited along an edge of the graphene structure and one end of the first interlayer material, and provides a ground source; and(iii) contacting the graphene structure with a second interlayer material,wherein the interlayer materials comprise one or more polymers, andwherein one or both of the interlayer materials further comprises an alkali metal salt.
  • 2. The method of claim 1, further comprising a liquid adhesive solution between the graphene structure and at least one of the first and second interlayer material.
  • 3. The method of claim 2, wherein the liquid adhesive solution is cured with heat.
  • 4. The method of claim 3, wherein the liquid adhesive solution is cured to a final temperature in the range of 130° C. to 160° C.
  • 5. The method of claim 4, wherein the final temperature is held for about 5 minutes to about 4 hours.
  • 6. The method of claim 2, wherein the liquid adhesive solution comprises a solvent and a polymer.
  • 7. The method of claim 6, wherein the polymer is selected from the group consisting of polyamides, polyimides, polychloroethylenes, polyurethanes, polyvinylethers, polythioureas, polyacrylates, polycarbonates, polyesters, polyethylenes, polypropylenes, polysytrenes, polyvinylacetates, polyvinyl butyral and fluoropolymers.
  • 8. The method of claim 7, wherein the polymer is selected from the group consisting of PTFE, poly(methyl methacrylate), ethylene vinyl acetate, thermoplastic polyurethane, polyethylene terephthalate, polycarbonate and polyethylene.
  • 9. The method of claim 1, further comprising one or more spacer layers between the one or more planar graphene sheets.
  • 10. The method of claim 1, wherein the polymer is selected from the group consisting of polyamides, polyimides, polychloroethylenes, polyurethanes, polyvinylethers, polythioureas, polyacrylates, polycarbonates, polyesters, polyethylenes, polypropylenes, polysytrenes, polyvinylacetates, polyvinyl butyral and fluoropolymers.
  • 11. The method of claim 10, wherein the polymer is selected from the group consisting of PTFE, poly(methyl methacrylate), ethylene vinyl acetate, thermoplastic polyurethane, polyethylene terephthalate, polycarbonate and polyethylene.
  • 12. The method of claim 1, wherein the cation in the alkali metal salt is selected from the group consisting of Na, Cs, Li, K, and Rb.
  • 13. The method of claim 12, wherein the anion in the alkali metal salt is selected from the group consisting of a perchlorate, iodide, and carbonate.
  • 14. The method of claim 1, wherein the one or more planar graphene sheets are intercalated with alkali metal ions.
  • 15. The method of claim 14 wherein compounds formed from the one or more planar graphene sheets and alkali metal ions are selected from the group consisting of LiC72, LiC36, LiC18, LiC12, and/or LiC6.
  • 16. The method of claim 1, wherein the graphene structure comprises 1-50 planar graphene sheets.
  • 17. The method of claim 1, wherein the one or more planar graphene sheets are applied to the interlayer materials individually.
  • 18. The method of claim 1, wherein the one or more planar graphene sheets are applied to the interlayers as a growth of multi-layer graphene, wherein the multi-layer graphene comprises 1-50 planar graphene sheets.
  • 19. The method of claim 1, wherein steps (ii) and (iii) are both sequentially repeated 1-5 times.
  • 20. The method of claim 1, wherein the conductive material is selected from the group consisting of a metal or adhesive tape.
  • 21. The method of claim 20, wherein the metal is selected from the group consisting of copper, silver or aluminum.
  • 22. The method of claim 1, wherein the depositing of a conductive material is selected from physical vapor deposition, thermal evaporation, sputtering and plating.
  • 23. A graphene laminate that provides EMI shielding wherein the graphene laminate comprises: one or more layers of graphene between a first interlayer material and a second interlayer material; anda conductive material along an edge of the graphene and one end of the interlayer materials,
  • 24. The graphene laminate of claim 23, further comprising a liquid adhesive solution between the graphene structure and at least one of the first and second interlayer material.
  • 25. The graphene laminate of claim 24, wherein the liquid adhesive solution is a liquid solution comprising a solvent and a polymer.
  • 26. The graphene laminate of claim 25, wherein the polymer is selected from the group consisting of polyamides, polyimides, polychloroethylenes, polyurethanes, polyvinylethers, polythioureas, polyacrylates, polycarbonates, polyesters, polyethylenes, polypropylenes, polysytrenes, polyvinylacetates, polyvinyl butyral and fluoropolymers.
  • 27. The graphene laminate of claim 26, wherein the polymer is selected from the group consisting of PTFE, poly(methyl methacrylate), ethylene vinyl acetate, thermoplastic polyurethane, polyethylene terephthalate, polycarbonate and polyethylene.
  • 28. The graphene laminate of claim 23, wherein the liquid adhesive solution is cured with heat.
  • 29. The graphene laminate of claim 23, further comprising one or more spacer layers between one or more layers of graphene.
  • 30. The graphene laminate of claim 23 wherein the interlayer materials are comprised of one or more polymers.
  • 31. The graphene laminate of claim 30, wherein the polymer is selected from the group consisting of polyamides, polyimides, polychloroethylenes, polyurethanes, polyvinylethers, polythioureas, polyacrylates, polycarbonates, polyesters, polyethylenes, polypropylenes, polysytrenes, polyvinylacetates, polyvinyl butyral and fluoropolymers.
  • 32. The graphene laminate of claim 31, wherein the polymer is selected from the group consisting of PTFE, poly(methyl methacrylate), ethylene vinyl acetate, thermoplastic polyurethane, polyethylene terephthalate, polycarbonate and polyethylene.
  • 33. The graphene laminate of claim 23, wherein the cation in the alkali metal salt is selected from the group consisting of Na, Cs, Li, K, Rb.
  • 34. The graphene laminate of claim 23, wherein the anion in the alkali metal salt is selected from the group consisting of a perchlorate, iodide, and carbonate.
  • 35. The graphene laminate of claim 23, wherein the one or more graphene layers are intercalated with alkali metal ions.
  • 36. The graphene laminate of claim 35, wherein the one or more graphene layers comprise 1-50 planar graphene layers intercalated with alkali metal ions.
  • 37. The graphene laminate of claim 36, wherein compounds formed from the one or more graphene layers and alkali metal ions are selected from the group consisting of such as LiC72, LiC36, LiC18, LiC12, and/or LiC6.
  • 38. The graphene laminate of claim 23, wherein the conductive material is selected from the group consisting of a metal or an adhesive tape.
  • 39. The graphene laminate of claim 38, wherein the metal is selected from the group consisting of copper, silver or aluminum.
  • 40. A method of forming a graphene laminate, the method comprising: (i) contacting a graphene structure comprising one or more planar graphene sheets with a first interlayer material;(ii) depositing of a conductive material, wherein the conductive material is deposited along an edge of the graphene structure and one end of the first interlayer material, and provides a ground source; and(iii) contacting the graphene structure with a second interlayer material,wherein the one or more planar graphene sheets are intercalated with alkali metal ions, andwherein compounds formed from the one or more planar graphene sheets and alkali metal ions are selected from the group consisting of LiC72, LiC36, LiC18, LiC12, and/or LiC6.
  • 41. A graphene laminate that provides EMI shielding wherein the graphene laminate comprises: one or more layers of graphene between a first interlayer material and a second interlayer material; anda conductive material along an edge of the graphene and one end of the interlayer materials,
PCT Information
Filing Document Filing Date Country Kind
PCT/US2019/063869 11/29/2019 WO
Publishing Document Publishing Date Country Kind
WO2020/113176 6/4/2020 WO A
US Referenced Citations (43)
Number Name Date Kind
8227685 Choi Jul 2012 B2
8945772 Kawakami et al. Feb 2015 B2
8946903 Sandhu Feb 2015 B2
9768443 Kawakami et al. Sep 2017 B2
9779882 Zhamu et al. Oct 2017 B2
9847184 Zhamu et al. Dec 2017 B2
9899672 Zhamu et al. Feb 2018 B2
9905373 Zhamu et al. Feb 2018 B2
9922775 Zhamu et al. Mar 2018 B2
9997611 Miyazaki et al. Jun 2018 B2
9997784 Su et al. Jun 2018 B2
10415143 Dryfe et al. Sep 2019 B2
10774195 Hamidinejad et al. Sep 2020 B2
10784516 Ochiai et al. Sep 2020 B2
10850496 Zhamu et al. Dec 2020 B2
10903020 Zhamu et al. Jan 2021 B2
11127941 Lanning et al. Sep 2021 B2
11133495 Gazda et al. Sep 2021 B2
11168404 Zhamu et al. Nov 2021 B2
11296243 Ghidiu et al. Apr 2022 B2
11299397 Lanning et al. Apr 2022 B2
11539074 Rogojina et al. Dec 2022 B2
11631893 Rogojina et al. Apr 2023 B2
11760640 Nosker et al. Sep 2023 B2
20050075412 Hishida Apr 2005 A1
20100261058 Lopatin et al. Oct 2010 A1
20110011639 Visser Jan 2011 A1
20110123776 Shin et al. May 2011 A1
20120070612 Lee et al. Mar 2012 A1
20120328956 Oguni et al. Dec 2012 A1
20130154994 Yang Jun 2013 A1
20130228365 Uprety et al. Sep 2013 A1
20130270119 Wada et al. Oct 2013 A1
20140023920 Yamazaki et al. Jan 2014 A1
20160288459 Keller et al. Oct 2016 A1
20170156215 Lai et al. Jun 2017 A1
20170170012 Ko et al. Jun 2017 A1
20170179477 Walters et al. Jun 2017 A1
20180012846 Miyazaki et al. Jan 2018 A1
20180019072 Zhamu et al. Jan 2018 A1
20190372093 Zhamu et al. Dec 2019 A1
20210126243 Lanning et al. Apr 2021 A1
20220013788 Zhamu et al. Jan 2022 A1
Foreign Referenced Citations (24)
Number Date Country
2827793 Jul 2012 CA
103692735 Apr 2014 CN
104934108 Sep 2015 CN
105722679 Jun 2016 CN
105985019 Oct 2016 CN
106413360 Feb 2017 CN
107418045 Dec 2017 CN
107667071 Feb 2018 CN
106413363 Mar 2021 CN
2556066 Aug 2019 GB
2012076958 Apr 2012 JP
2012096937 May 2012 JP
2013239385 Nov 2013 JP
2015082374 Apr 2015 JP
20110079469 Jul 2011 KR
20110095751 Aug 2011 KR
101196820 Nov 2012 KR
20130019169 Feb 2013 KR
101655941 Sep 2016 KR
101830781 Feb 2018 KR
20200008368 Jan 2020 KR
2011081268 Jul 2011 WO
2019182624 Sep 2019 WO
2019182652 Sep 2019 WO
Non-Patent Literature Citations (13)
Entry
Song, W. et al., “Flexible Graphene/Polymer Composite Films in Sandwich Structues for Effective Electromagnetic Interference Shielding”; Carbon (2014); p. 67-76.
Chen, Y. et al., “Eectromagnetic Interfernce Shielding Efficiency of Polyaniline Composites Filled with Graphene Decorated with Metallic Nanapaticles”; Composites Sciences and Tecnhology (2013); vol. 80; pp. 80-86.
Lakshmi, N.V., et al, “EMI Shielding Effectiveness of Graphene Decorated with Graphene Quantum Dots and Silver Nanoparticles Reinforced PVDF Nanocomposities”; Composite Interfaces (2017); vol. 24:9; pp. 861-882.
Lin, S., et al., “Electromagnetic Interference Shieding Performance of Waterborne Polyurethane Composites filled with Silver Nanoparticles on Functionalized Graphene”; Appliced Surface Science (2016); vol. 385; pp. 436-444.
D'Aloia, A. G. et al., “Optimal Terahertz Shielding Performances of Flexible Multilayer Screens Based on Chemically Doped Graphene on Polymer Substrate”, IEEE (2015) pp. 1030-1035.
D'Aloia, A. G. et al., “Terahertz Shielding Effectiveness of Graphene-Based Multilayer Screens Controlled by Electric Field Bias in a Reverberating Environment”, IEEE (2015), vol. 5:4, pp. 628-636.
De Arco, L. W. et al., “Synthesis, Transfer and Devices of Single-and Few-Layer Graphene by Chemical Vapor Deposition”, IEEE Transactions of Nanotechnology (2009), vol. 8:2, pp. 135-138.
Du, X. et al., “Graphene/Epoxy Interleaves for Delamination Toughening and Monitoring of Crack Damage in Carbon Fibre/Epoxy Composite Laminates”, Composities Science and Technology (2017), vol. 140, pp. 123-133.
Kasry, A. et al., “Chemical Doping of Large-Area Stacked Graphene Films for Use as Transparent, Conducting Electrodes”, ACS Nano (2010), vol. 4:7, pp. 3839-3844.
Kim, K.K., et al., “Enhancing the Conductivity of Transparent Graphene Films via Doping”, Nanotechnology (2010), vol. 21, 7 pgs.
Kim, S. eta l., “Electromagnetic Interference (EMI) Transparent Shielding of Reduced Graphene Oxide (RGO) Interleaved Structure Fabricated by Electrophoretic Deposition”, ACS Applied Materials and Interfaces (2014), vol. 6, p. 17647-17653.
Wan, Y. et al., “Graphene Paper for Exceptional EMI Shielding Performance Using Large-Sized Graphene Oxide Sheets and Doping Strategy”, Carbon (2017), 8 pgs.
Wu, T. et al., “Facile Synthesis of Ag Interlayer Doped Graphene by Chemical Vapor Deposition Using Polystyrene as Solid Carbon Source”, ACS Applied Materials and Interfaces (2012), vol. 4, pp. 2041-2047.
Related Publications (1)
Number Date Country
20220022350 A1 Jan 2022 US
Provisional Applications (1)
Number Date Country
62773693 Nov 2018 US