Gray and bronze glass composition

Abstract

The present invention is a bronze and gray glass composition. The composition comprises 68 to 75% SiO2, 10 to 18% Na2O, 5 to 15% CaO, 0 to 10% MgO, 0 to 5% Al2O3, and 0 to 5% K2O, where CaO+MgO is 6 to 15% and Na2O+K2O is 10 to 20%, and colorants comprising: 0.22 to 0.39 wt. % total iron as Fe2O3 wherein the ratio of FeO/total Fe as Fe2O3 is 0.35 to 0.64; 0.1 to 0.5 wt. % manganese compound as MnO2; 0 to 1.2 wt. % cerium oxide as CeO2; and 2 to 10 ppm selenium, and 0 to 20 ppm cobalt as cobalt oxide. The colored glass has the following spectral properties at 4.0 mm. thickness: 65 to 78% light transmittance using Illuminant A (LTA) and using Illuminant C has a dominant wavelength of 493 to 577 nanometers with an excitation purity up to 7%.

Description

TECHNICAL FIELD OF THE INVENTION

[0001] The invention is directed to gray and bronze glass compositions having a high transmittance and a high infrared absorption and method of producing the gray and bronze glass.

BACKGROUND OF THE INVENTION

[0002] It would be extremely advantageous to improve the infrared absorption of glass products while maintaining a high level of visible transmission and to also have a good absorption in the ultraviolet portion of the spectrum. Iron oxide exists in two chemical forms in the glass, an oxidized form which is yellow, Fe2O3, and a reduced form which is blue FeO. Advantageously, the oxidized form of iron oxide absorbs a portion of the ultraviolet light passing through the glass product and the reduced form of iron oxide absorbs a portion of the infrared light passing through the glass product. Under typical furnace firing conditions and batching conditions, when the total iron oxide in the glass product is within the range of about 0.2 to 1.2 wt. % as Fe2O3, the iron oxide equilibrium is such that the redox ratio of FeO/total Fe as Fe2O3 is about 0.18-0.26.

[0003] It is desirable to increase the proportion of reduced iron oxide (FeO) in the glass to improve its infrared absorption. In addition, by shifting the iron oxide away from the oxidized form (Fe2O3) the glass will change color from green to blue. It would be further desirable to shift the blue glass towards a gray or a bronze color and to simultaneously improve the ultra violet absorption as well as the infrared absorption.

[0004] One way commonly employed to shift the redox equilibrium of iron oxide in the glass, and hence its UV and IR properties, is by increasing the fuel to the furnace. Increasing the amount of fuel, however, has several undesirable consequences: the combustion heating of the furnace becomes inefficient and requires an air increase or the unburnt fuel will burn in the checker system of the furnace. Excess fuel can also reduce the glass to an amber color that sharply lowers the visible transmittance of the glass product.

[0005] An amber color arises when the iron reacts with sulfur that has been reduced to form iron sulfide. Amber colored glass containers are normally melted in like manner by using anthracite coal together with iron oxide and sulfate. The amber iron sulfide chromophore, once produced, significantly decreases the visible transmittance of the glass and the glass could not be used where a high transmittance is required.

[0006] Therefore, there is a need in the glass industry to produce gray or bronze glass that has high transmittance yet having an improved infrared light absorption and an ultra violet absorption.

SUMMARY OF THE INVENTION

[0007] In one aspect of the present invention a gray and a bronze glass having a base and a colorant is provided. The composition of the base comprises 68 to 75% SiO2, 10 to 18 wt. % Na2O, 5 to 15 wt. % CaO, 0 to 10 wt. % MgO, 0 to 5 wt. % Al2O3, and 0 to 5 wt. % K2O, where CaO+MgO is 6 to 15 wt. % and Na2O+K2O is 10 to 20 wt. % is provided. The composition of the colorants comprises: 0.22 to 0.39 wt. % total iron as Fe2O3 wherein the ratio of FeO/total Fe as Fe2O3 is 0.35 to 0.64; 0.1 to 0.5 wt. % manganese compound as MnO2; 0 to 1.2 wt. % cerium oxide as CeO2; and 2 to 10 ppm selenium, and 0 to 20 ppm cobalt as cobalt oxide.

[0008] In yet another aspect of the present invention glass products made according to the embodiment of the invention have the following spectral properties at 4.0 mm. thickness: 65 to 78% light transmittance using Illuminant A (LTA) and using Illuminant C has a dominant wavelength greater than 493 but less than or equal to 577 nanometers with an excitation purity less than 7%. Generally, as the quantities of the colorants increase, both the % LTA and % IR transmittance will go down. Similarly, as the glass thickness increases for a given glass composition, the transmittance of the thicker glass will decrease.

[0009] In yet another aspect of the present invention wherein the colored glass of the present invention exhibits an bronze color when the excitation purity is in the range of 2% to 7% and has a dominant wavelength in the range of 560 to 577 nanometers. In yet another aspect of the present invention the colored glass exhibits a gray color when the excitation purity is less than 2% and the dominant wavelength is in the range of 493 to 551 nanometers.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

[0010] Flat soda-lime-silica glass, used in the automotive and architectural industries and conveniently made by the float glass process, is generally characterized by the following basic composition, the amounts of the components being based on a weight percentage of the total glass composition:

	TABLE I
	Base Glass Components	Weight %
	SiO2	68 to	75
	Al2O3	0 to	5
	CaO	5 to	15
	MgO	0 to	10
	Na2O	10 to	18
	K2O	0 to	5

[0011] The gray and bronze glass composition of the present invention employs this basic soda-lime-silica glass composition wherein, additionally, CaO+MgO is 6 to 15 wt. % and Na2O+K2O is 10 to 20 wt. %. Preferably SO3 is present in an amount of 0.03 to 0.20 wt %, more preferably, 0.03 to 0.10 wt. % in the final glass product. In addition, the gray and bronze glass composition consists essentially of the following coloring components: iron oxide; selenium, manganese compound; and optionally one of cobalt oxide or cerium oxide or both.

[0012] The total iron as Fe2O3 is present in the invention composition in quantities of 0.22 to 0.39 wt. % Fe2O3. Typically, this ingredient is added with the batch ingredients in the oxide form, i.e. Fe2O3. The iron oxide incorporated in the composition lowers both the ultraviolet and the infrared transmittance of the glass products. When iron oxide is used in a glass composition in normal commercial production, the redox ratio defined as equal to FeO/total iron (Fe) as Fe2O3 In commercial glass products available today this redox ratio is in the range of is 0.18-0.26. On the other hand, the glass of the present invention has a high redox ratio, in the range of 0.35-0.64. If the redox ratio goes above 0.65, the undesirable amber chromophore may form and therefore the light transmittance of the glass will be reduced.

[0013] The glass of the invention is manufactured by one step batch admixing of the components to feed a conventional SIEMENS float glass furnace. Sodium sulfate is mixed in the batch together with anthracite coal to shift the iron oxide equilibrium toward the reduced form of iron (FeO). Manganese dioxide is necessary in the batch to prevent the formation of the amber iron sulfide and to aid in the retention of the selenium. All of the batch components are mixed together in a single step and then metered into the furnace. In glass product made with this method cerium oxide improves the ultra violet absorption of the glass. Selenium moves the color towards bronze and cobalt lowers the dominant wavelength and excitation purity.

[0014] When glass products made in this manner are used in vehicles, the bronze and gray glass absorbs solar heat and there is relatively less total heat build up in the vehicle. The load on vehicle air conditioners is reduced such that there is less heat build up to cool and comfort to the passengers occurs quickly. Glass made with the instant invention can also be used for architectural products and provides a similar reduction in air conditioner load.

[0015] A manganese compound is present in an amount of 0.1 to 0.5 wt. % based on MnO2 in the glass composition. The presence of manganese substantially prevents the formation of the amber color. This manganese compound can be added to the batch glass components in a variety forms, e.g., but not limited to MnO2, Mn3O4, MnO, MnCO3, MnSO4, MnF2, MnCl2, etc.

[0016] Table II discloses the amounts of raw material batch ingredients that are preferably used to form the gray and bronze glass compositions according to the present invention. The present invention uses identical amount of raw material to form both the gray glass and the bronze glass.

	TABLE II
	Batch Material	Range Mass (Lbs)
	Sand	1000
	Soda Ash	290 to	350
	Limestone	70 to	90
	Dolomite	215 to	260
	Salt cake	2.5 to	11
	Rouge (97% Fe2O3)	3.5 to	6.0
	Manganese Dioxide	1.3 to	7.0
	Selenium	0.05 to	0.50
	Cerium Oxide	0 to	16.0
	Cobalt Oxide	0 to	0.04
	Anthracite coal	0.9 to	2.5
	Nepheline Syenite	0 to	150

[0017] The anthracite coal is preferably bought under the trade-name CARBOCITE and is commercially available from the Shamokin Filler Company. Graphite could be used as a substitute for anthracite coal in an amount of about 70% that of anthracite coal because anthracite coal contains about 70-72% carbon. If graphite is used, the typical range would be from 0.7 to 2.1 pounds of graphite per 1000 pounds of sand. MELITE, a coal slag processed by Calumite Corporation could partially or wholly substitute for rouge in the batch up to about 55 pounds MELITE per 1000 pounds of sand. MELITE has about 80% of the total iron oxide in the reduced form and thus would require less anthracite coal to generate similar spectral properties.

[0018] The equilibrium reactions that occur in the glass melt which causes a shift in the forms of iron oxide are influenced by the sodium sulfate used as a refining agent and carbon used to react with sodium sulfate at lower furnace temperatures. Generally, increasing the quantity of sodium sulfate in the glass tends to shift the iron oxide equilibrium slightly toward oxidizing. On the other hand, increasing carbon concentration in the glass batch shifts the iron oxide equilibrium toward reducing form of iron. Increasing the amount of Manganese oxide shifts the iron oxide equilibrium again towards the oxide form. Another influence on the iron oxide equilibrium is the peak furnace temperature which, when increased will shift the iron oxide slightly toward the reduced state and lowering overall furnace temperature allows the iron oxide to shift back towards the oxidized state.

[0019] The colored glass obtained in accordance with the teachings of the present invention exhibits the following spectral properties at 4 mm. control thickness has a light transmittance using illuminant A in a range of 65% to 78%, an infrared transmittance in the range of 22% to 51% and an ultraviolet transmittance in the range of 35% to 62%.

[0020] Melts were made in the laboratory which demonstrate embodiments of this invention using the procedure as follows: batches were weighed, placed into a glass jar about 2″ high and 2″ inside diameter and dry mixed for 10 minutes each on a Turbula mixer, dry batch was placed into an 80% platinum/20% rhodium crucible that stands 2″ tall and has an inside diameter at the top of 2.5″ and is tapered to the base which has an inside diameter of 1.75″. An amount of 4.5 ml. of water is added to the dry batch in the crucible and mixed with a metal spoon. After such preparation, a group of six different batches is melted in a gas/air fired surface at the same time for 1 hour at 2600° F. and each crucible is removed in turn from the furnace and fritted. Fritting the glass involves coating the inside of the platinum/rhodium crucible by rolling the molten glass around the inside of the crucible and then plunging the crucible into cold water. After removing the crucible from the water and draining, the broken glass particles are removed from the sides of the crucible and mechanically mixed inside the crucible. All six samples are fritted in like manner and all crucibles are placed back into the furnace for another hour interval at 2600° F. and the fritting procedure is repeated. After the second fritting process, the crucibles are returned to the furnace for 4 hours at 2600° F. Each crucible is removed in turn from the furnace and each molten glass sample is poured into a graphite mold with an inside diameter of 2.5″. Each glass is cooled slowly, labeled, and placed into an annealing furnace where the temperature is quickly raised to 1050° F., held for 2 hours, and then slowly cooled by shutting off the furnace and removing the samples after 14 or more hours. The samples are ground and polished to about 4.0 mm. thickness and subsequently the spectral properties are measured for each sample.

[0021] All laboratory melts made with above procedure use a base composition of 100 grams sand, 32.22 grams soda ash, 8.81 grams limestone, 23.09 grams dolomite, 0.25 to 1.1 grams of sodium sulfate, 0.09 to 0.25 grams of CARBOCITE, 2.64 grams of nepheline syenite, and the remainder of the batch includes rouge, manganese dioxide, selenium and optionally cobalt oxide and cerium oxide if required.

[0022] In each of the following tables of examples with the glass composition includes spectral data at 4.0 mm, which is the control thickness. The % LTA is defined to be the % luminance transmittance measured under CIE standard illuminant A. The dominant wavelength and the % excitation purity are measured using CIE standard illuminant C. The % UV is the % ultra violet transmittance measured between 300 and 400 nanometers and % IR is the % infra red transmittance measured between 750 and 2100 nanometers.

[0023] Tables III to VI represent the bronze glass composition of the present invention. As can be seen from the Tables, the glass exhibits a bronze color when the excitation purity is in the range of 2% to 7%. Additionally, the dominant wavelength of the bronze glass is in the range of 560 nm to 575 nm.

[0024] As shown in Table III, as the amount of selenium is increased and the amount of FeO is decreased, results in increase in the % LTA of the glass. However, the UV transmittance and the IR transmittance also increases. All the spectral properties are listed at a control thickness of 4.0 mm.

	TABLE III
	Example
	1	2	3	4	5	6	7	8
Wt. % Fe2O3	0.353	0.352	0.251	0.301	0.301	0.301	0.25	.03
Wt. % FeO	0.198	0.195	0.148	0.156	0.158	0.164	0.159	0.174
Redox Ratio	0.561	0.554	0.590	0.518	0.525	0.545	0.636	0.580
Wt. % MnO2	0.151	0.151	0.151	0.151	0.151	0.151	0.101	0.451
PPM SE	2	3	3	4	4	4	6	6
% LTA	67.66	66.82	74.03	69.36	69.9	68.87	72.44	71.68
% LTC	67.85	66.9	74.35	69.26	69.8	68.75	72.55	71.94
% UV	41.17	49.99	52.75	52.13	53.08	51.89	55.78	53.61
% INFRA RED	26.25	26.71	35.57	33.9	33.5	32.4	34.18	30.61
% TOTAL	43.99	44.5	52.24	49.65	49.65	48.59	52.15	48.83
SOLAR
Dominant	564	565.1	561.7	568.6	568.7	569.7	562.7	561
Wavelength
% Excitation	6.4	4.5	5.4	4.5	4.7	5.1	2.3	3.9
Purity

[0025] Table IV shows the effect of cobalt on the excitation purity and the % LTA. As seen from the examples, as the amount of cobalt is increased at constant amount of selenium and manganese oxide, the % excitation purity decreases and the % LTA significantly increases. The increase in the amount of cobalt lowers the UV transmittance, however increases the IR transmittance.

	TABLE IV
	Example
	9	10	11	12	13	14	15	16	17
Wt. % Fe2O3	0.354	0.354	0.377	0.303	0.302	0.303	0.303	0.304	0.302
Wt. % FeO	0.165	0.164	0.224	0.117	0.141	0.128	0.117	0.099	0.136
Redox Ratio	0.466	0.463	0.594	0.386	0.467	0.422	0.386	0.326	0.450
Wt. % MnO2	0.151	0.152	0.151	0.151	0.151	0.15	0.152	0.151	0.151
PPM SE	3	4	2	2	4	4	4	2	4
PPM CO*	1	1	3	12	12	12	12	13	13
Dominant	564.8	565.9	561.4	562.3	561.8	570.9	573.5	574.4	563.9
Wavelength
% Excitation	3.6	3.8	5.7	2.1	2.2	3.8	4.6	4.9	2.4
Purity
% LTA	69.69	69.09	65.33	70.35	67.3	66.34	67.06	67.08	67.85
% LTC	69.77	69.112	65.65	70.46	67.43	66.17	66.73	66.67	67.93
% UV	51.15	50.37	47.24	45.87	49.29	43.76	42.4	39.48	47.73
% INFRA	32.21	32.34	22.58	43.29	37.18	40.16	43	48.09	38.33
RED
% TOTAL	48.94	48.71	41.25	55.46	50.84	51.8	53.57	56.1	51.71
SOLAR

[0026] Table V shows that both selenium and cerium oxide increase the dominant wavelength of the glass. On the other hand as seen from the examples, increasing the amount of manganese oxide and cerium oxide lowers the ultra violet transmittance, in other words, the ultra violet absorption can be improved.

	TABLE V
	Example
	18	19	20	21	22	23
Wt. % Fe2O3	0.25	0.3	0.352	0.351	0.351	0.351
Wt. % FeO	0.159	0.174	0.195	0.141	0.123	0.125
Redox Ratio	0.636	0.580	0.554	0.402	0.350	0.356
Wt. % MnO2	0.101	0.451	0.151	0.15	0.151	0.151
Wt. % CeO2	0	0	0	0.504	1.009	1.009
PPM SE	6	6	3	8	5	8
Dominant	562.7	561	565.1	569.2	570.8	573.3
Wavelength
% Excitation	2.3	3.9	4.5	4.7	5.2	6.6
Purity
% LTA	72.44	71.68	66.82	71.43	72.71	71.61
% LTC	72.55	71.94	66.82	71.43	72.71	71.61
% UV	55.78	53.61	49.99	42.48	38.85	37.89
% INFRA	34.18	30.61	26.71	37.31	41.53	41.26
RED
TOTAL	52.15	48.83	44.5	52.12	54.8	54.06
SOLAR

[0027] Table VI below indicates the impact of cerium oxide on glass compositions to improve the % LTA of the glass. Increasing the cerium oxide helps to oxidize the iron oxide and that increases the transmittance in the visible portion of the spectrum and that is critical when the finished glass product is to be used in automotive applications. Examples 25 and 26 clearly indicate that an increase in the amount of cerium oxide, when all other components of the composition are constant, results in % LTA to increase from 66.42 to 70.45. The presence of cerium oxide also lowers the ultra violet transmittance.

	TABLE VI
	Example
	24	25	26	27	28	29	30	31
Wt. % Fe2O3	0.301	0.301	0.301	0.302	0.302	0.301	0.301	0.302
Wt. % FeO	0.136	0.143	0.108	0.118	0.121	0.109	0.092	0.11
Redox Ratio	0.452	0.475	0.359	0.391	0.401	0.362	0.306	0.364
Wt. % MnO2	0.151	0.151	0.151	0.151	0.15	0.15	0.15	0.151
Wt. % CEO2	0.202	0.203	0.403	0.404	0.405	0.606	0.606	0.606
PPM SE	4	4	4	4	4	4	4	4
PPM CO	13	12	12	12	13	12	12	12
Dominant	568.8	563.9	562.1	575.1	571.6	565.6	572.9	576.7
Wavelength
% Excitation	3.3	2.5	2.1	5.9	3.9	2.5	4	7
Purity
% LTA	66.1	66.42	70.45	65.6	66.61	70.14	69.69	65.56
% LTC	66.03	66.5	70.56	65.08	66.4	70.17	69.4	64.83
% UV	45.65	46.66	44.88	40.29	42.45	42.96	41.13	38.34
% IR	38.21	36.63	45.57	42.71	42.08	45.34	50.32	44.95
% TOTAL	50.74	50.12	56.61	52.55	52.89	56.31	58.59	53.61
SOLAR

[0028] Tables VII to XIV are examples of the gray glass composition of the present invention. The gray glass is also manufactures using the same colorants as the bronze glass. The gray glass is characterized by a low excitation purity of less than 2%.

[0029] As demonstrated in Tables VII and VIII, increase in the amount of selenium and a decrease in the amount of FeO increases the light transmittance in the visible spectrum. It also lowers the amount of ultra violet transmittance however, has an undesirable effect of increasing the infra red transmittance. The increase in selenium also has the effect of increasing the excitation purity. The dominant wavelength and excitation purity are important because they define the color of the glass.

TABLE VII
Example
	32	33	34	35	36	37	38	39
Wt. % Fe2O3	0.352	0.352	0.301	0.301	0.353	0.354	0.352	0.351
Wt. % FeO	0.166	0.186	0.167	0.167	0.181	0.189	0.172	0.153
Redox Ratio	0.472	0.528	0.555	0.555	0.513	0.534	0.489	0.436
Wt. % MnO2	0.151	0.151	0.451	0.451	0.151	0.152	0.152	0.151
PPM SE	7	2	4	4	2	2	2	2
Dominant	499.7	530	536	536	503	503.2	505.4	506.9
Wavelength
% Excitation	1.9	1.4	1.6	1.6	1.7	1.8	1.4	1.2
Purity
% LTA	74.63	71.27	73.9	73.9	72.69	72.37	73.52	74.75
% LTC	75.55	71.88	74.49	74.49	73.59	73.33	74.3	75.48
% UV	52.55	55.5	57.23	57.23	48.31	46.56	57.25	57.07
% IR	31.92	28.31	31.88	31.88	29.04	27.7	30.96	34.55
% TOTAL	51.29	47.77	50.9	50.9	48.7	47.75	50.36	52.88
SOLAR

[0030]

	TABLE VIII
	Example
	40	41	42	43	44	45	46
Wt. % Fe2O3	0.352	0.351	0.353	0.352	0.352	0.351	0.301
Wt. % FeO	0.184	0.148	0.205	0.185	0.153	0.152	0.139
Redox Ratio	0.523	0.422	0.581	0.526	0.435	0.433	0.462
Wt. % MnO2	0.151	0.151	0.151	0.151	0.151	0.151	0.151
PPM SE	2	3	1	3	4	3	2
Dominant	525.4	525.9	526.1	529.5	536.3	538.6	545.9
Wavelength
% Excitation	1.3	1.1	1.8	1.4	1.4	1.5	1.6
Purity
% LTA	71.23	73.14	71.09	70.89	72.65	72.25	74.2
% LTC	71.86	73.7	71.94	71.51	73.15	72.75	74.62
% UV	55.36	54.96	49.01	54.47	54.72	53.4	56.96
% IR	28.66	35.46	25.36	28.41	34.62	34.63	37.53
% TOTAL SOLAR	47.95	52.51	45.73	47.65	51.81	51.61	54.09

[0031] As seen from the experiments shown in Table IX, increasing the amount of cobalt and decreasing the amount of FeO, results in lowering the excitation purity as seen in examples 52 and 54. As can be seen from the above examples it does not significantly change the % LTA. Similarly as can been seen in examples 59 and 60 in Table X, increasing the amount of cobalt and selenium, results in increase in excitation purity from 1.1 to 1.6. Although there is an increase in the excitation purity, since the excitation purity is less than 2%, the color of the glass remains gray. The increase in both selenium and cobalt also results in increase in UV transmittance and a increase in % LTA.

	TABLE IX
	Example
	47	48	49	50	51	52	53	54
Wt. % Fe2O3	0.354	0.355	0.355	0.355	0.355	0.251	0.271	0.291
Wt. % FeO	0.166	0.155	0.14	0.139	0.14	0.112	0.135	0.159
Redox Ratio	0.469	0.437	0.394	0.392	0.394	0.446	0.498	0.546
Wt. % MnO2	0.151	0.151	0.151	0.151	0.151	0.151	0.151	0.151
PPM SE	2	3	2	3	4	3	3	3
PPM CO	1	2	2	2	2	3	4	5
Dominant	519.5	520.8	523.3	541.3	544.1	494.7	500	505
Wavelength
% Excitation	1.1	1.1	1.1	1.5	1.6	1.5	1.5	0.5
Purity
% LTA	72.79	72.28	73.98	73.49	72.3	72.62	74.88	72.67
% LTC	73.41	72.87	74.54	73.95	72.73	73.22	75.64	73.51
% UV	55.55	54.44	54.68	53.68	52.59	60.18	60.87	58.05
% IR	32.04	34.03	37.42	37.64	37.26	44.33	38.49	33.24
% TOTAL	50.57	51.41	54.01	53.79	53.02	57.64	55.27	51.27
SOLAR

[0032]

	TABLE X
	Example
	55	56	57	58	59	60	61	62
Wt. % Fe2O3	0.311	0.29	0.271	0.302	0.303	0.271	0.25	0.291
Wt. % FeO	0.178	0.14	0.121	0.137	0.128	0.127	0.112	0.147
Redox Ratio	0.572	0.483	0.446	0.454	0.422	0.469	0.448	0.505
Wt. % MnO2	0.151	0.151	0.15	0.151	0.152	0.151	0.151	0.151
PPM SE	3	3	3	2	2	3	4	5
PPM CO	5	8	9	12	12	13	15	16
Dominant	533	497	503.6	525.6	544	495.5	493.3	496.4
Wavelength
% Excitation	1.9	1.8	1	0.8	1.1	1.6	1.6	1.6
Purity
% LTA	70.75	73.55	74.44	69.73	69.8	71.43	72.28	67.82
% LTC	71.51	74.33	75.02	70.13	70.1	72.1	72.87	68.46
% UV	54.66	59.79	59.8	49.68	47.95	58.8	60.68	56.35
% IR	29.62	37.35	42.09	38.16	40.14	40.47	44.53	35.82
% TOTAL	48.12	54.17	57.07	52.62	53.62	54.95	57.69	50.86
SOLAR

[0033]

	TABLE XI
	Example
	63	64	65	66	67
Wt. % Fe2O3	0.331	0.331	0.251	0.271	0.331
Wt. % FeO	0.131	0.149	0.13	0.118	0.154
Redox Ratio	0.396	0.450	0.518	0.435	0.465
Wt. % MnO2	0.151	0.151	0.151	0.151	0.151
PPM SE	4	5	5	4	5
PPM CO	16	16	16	17	19
Dominant	499.8	500	512.1	495.9	498
Wavelength
% Excitation	1.1	1.3	0.7	1.3	1.5
Purity
% LTA	68.29	67.8	68.14	70.61	65.18
% LTC	68.79	68.4	68.53	71.15	65.78
% UV	56.58	54.27	56.67	58.04	52.16
% IR	39.34	35.4	39.78	42.91	34.17
% TOTAL	52.93	50.5	53.06	55.98	48.68
SOLAR

[0034] Table XI above represents the importance of cobalt to obtain the gray glass of the present invention having desired properties. As can be seen from examples 63 and 64, increasing the amount of selenium at constant cobalt, Fe2O3 and MnO2 results in lowering the % LTA, increasing the excitation purity and decreasing the UV and IR transmittance. On the other hand, as seen from examples 65 and 66 increasing the amount of cobalt and decreasing the amount of selenium and FeO results in increasing the % LTA.

[0035] Table XII below shows the effect of CeO2, MnO2, and selenium on the excitation purity and the spectral properties of the glass of the present invention. As can be seen from examples 68 and 70, increasing the amounts of selenium and CeO2 at constant Fe2O3 results in significance increase the % LTA and the dominant wavelength. It also decreases the amount of UV transmittance. On the other hand, as seen from examples 71 and 72 increasing the amount of CeO2 at constant MnO2, selenium and Fe2O3, results in decrease in the excitation purity and the dominant wavelength. As can be seen it does not significantly affect the other spectral properties of the glass.

	TABLE XII
	Example
	68	69	70	71	72	73
Wt. % Fe2O3	0.352	0.351	0.351	0.351	0.351	0.301
Wt. % FeO	0.186	0.157	0.186	0.144	0.167	0.167
Redox Ratio	0.528	0.447	0.530	0.410	0.476	0.555
Wt. % MnO2	0.151	0.151	0.151	0.151	0.151	0.451
Wt. % CeO2	0	0.101	0.203	0.303	0.403	0
PPM SE	2	3	2	3	3	4
Dominant	530	511.2	508.9	542.6	525.4	536
Wavelength
% Excitation	1.4	1.1	1.7	1.6	1.2	1.6
Purity
% LTA	71.27	73.88	72.09	74.62	73.03	73.9
% LTC	71.88	74.58	72.89	75.09	73.65	74.49
% UV	55.5	52.96	50.49	48.41	47.58	57.23
% IR	28.31	33.65	28.32	36.55	31.75	31.88
% TOTAL	47.77	51.85	48.06	53.54	50.24	50.9
SOLAR

[0036] Table XIII demonstrates the effect of MnO2, CeO2, selenium and cobalt on the spectral properties of the glass. As seen from examples 76 and 77, increasing the amount of cobalt results in decrease in UV and IR transmittance, however results in decrease in % LTA.

	TABLE XIII
	Example
	74	75	76	77	78
Wt. % Fe2O3	0.351	0.351	0.351	0.352	0.351
Wt. % FeO	0.168	0.173	0.178	0.2	0.19
Redox Ratio	0.479	0.493	0.507	0.568	0.541
Wt. % MnO2	0.151	0.15	0.15	0.151	0.15
Wt. % CEO2	0.202	0.404	0.403	0.605	0.403
PPM SE	3	3	3	2	3
PPM CO	2	2	6	9	11
Dominant	503.6	504.2	513.5	525.5	504.3
Wavelength
% Excitation Purity	1.5	1.4	1.1	1.5	1.5
% LTA	72.62	71.81	68.62	65.61	67.04
% LTC	73.4	72.59	69.25	66.28	67.78
% UV	51.15	48.07	45.64	42.16	45.68
% IR	31.73	30.58	29.59	25.86	27.69
% TOTAL SOLAR	50.28	49.2	47.2	43.64	45.58

[0037] As seen from the above, lowering the % UV below 50% requires greater than 0.2 wt. % MnO2 and CEO2 or the total of the MnO2 and CEO2 to be 0.45 wt. % or greater.

	TABLE XIV
	Example
	79	80	81	82	83	84
Wt. % Fe2O3	0.301	0.301	0.301	0.377	0.377	0.377
Wt. % FeO	0.137	0.138	0.121	0.167	0.172	0.178
Redox Ratio	0.455	0.458	0.402	0.443	0.456	0.472
Wt. % MnO2	0.151	0.151	0.15	0.151	0.15	0.151
Wt. % CEO2	0.202	0.203	0.404	0.505	0.607	0.405
PPM SE	4	4	4	2	2	2
PPM CO	12	12	12	12	12	13
Dominant	509.6	501.2	551.1	517.4	505.1	501.7
Wavelength
% Excitation	0.8	1.2	1.4	1	1.3	1.5
Purity
% LTA	69.75	70.42	69.47	66.73	67.25	66.51
% LTC	70.23	71	69.72	67.28	67.91	67.21
% UV	49.77	50.38	45.52	42.53	42.84	44.4
% IR	37.88	37.77	41.95	31.65	30.74	29.55
% TOTAL	52.49	52.82	54.34	47.48	47.3	46.39
SOLAR

[0038] All of the examples are made using the batch only with no cullet (the broken pieces of glass that are added to the batch feed in production). There are two types of cullet that can be added to the batch to produce glass of the invention: reduced iron glass from glass of the invention and oxidized iron glass. The reduced iron glass cullet has a redox ratio of about 0.5 to 0.6 while the oxidized iron glass has a redox ratio of about 0.18 to 0.26. The redox ratio is defined as the ratio of wt. % FeO/total Fe as wt. % Fe2O3. For example, if the desired glass of the invention in the examples above uses 2 pounds of anthracite coal for 1000 pounds of sand, then an additional 1.5 pounds of anthracite coal must be added to the batch when the reduced iron glass cullet is added to make 50% of the batch feed to the furnace for a total of 3.5 pounds of anthracite coal per 1000 pounds of sand. For other cullet levels, the anthracite coal is increased or decreased proportionately. If the oxidized iron glass cullet is used, more anthracite coal must be added to drive the oxidized cullet toward the reduced iron to make a grey or bronze glass color. For example, if the desired glass of the invention in the examples above uses 2 pounds of anthracite coal for 1000 pounds of sand, then an additional 2.5 pounds of anthracite coal must be added to the batch when the oxidized iron glass cullet is added to make 50% of the batch feed to the furnace for a total of 4.5 pounds of anthracite coal per 1000 pounds of sand.

[0039] As can be seen from the examples above, the glass in accordance with the present invention provides for high transmittance, an improved infrared light absorption and an improved ultra violet absorption.

[0040] As any person skilled in the art will recognize from the previous description and from the figures and claims, modifications and changes can be made to the preferred embodiment of the invention without departing from the scope of the invention as defined in the following claims.

Claims

1. A colored glass having a base and a colorant, wherein composition of the colorant by weight of the colored glass comprises: 0.22 to 0.39 wt. % of total iron as Fe2 03, wherein ratio of FeO to total iron as Fe2O3 is in a range of 0.35 to 0.64; 0.1 to 0.5 wt. % of manganese oxide as MnO2; 2 to 10 ppm of selenium; and 0 to 20 ppm of cobalt; wherein the colored glass at 4 mm. control thickness has a light transmittance using illuminant A in a range of 65% to 78%, an infrared transmittance in the range of 22% to 51%, a dominant wavelength using illuminant C in a range of 493 to 577 nanometers and an excitation purity up to 7%.

2. The colored glass of claim 1, wherein the composition of the colorant further comprises up to 1.2 wt. % cerium oxide as CeO2.

3. The colored glass of claim 1, wherein the color of the colored glass is bronze when the excitation purity is in the range of 2% to 7%.

4. The colored glass of claim 3, wherein the dominant wavelength of the bronze colored glass is in the range of 561 to 577 nanometers.

5. The colored glass of claim 3, wherein the amount of selenium to obtain the bronze colored glass is in the range of 3 to 8 ppm.

6. The colored glass of claim 3, wherein the amount of cerium oxide to obtain the bronze colored glass is in the range of 0.5 to 1.0 wt. %.

7. The colored glass of claim 1, wherein the color of the colored glass is gray when the excitation purity is less than 2%.

8. The colored glass of claim 7, wherein the dominant wavelength of the gray colored glass is in the range of 493 to 551 nanometers.

9. The colored glass of claim 7, wherein the amount of cerium oxide to obtain the gray colored glass is in the range of 0.2 to 0.8 wt. %.

10. The colored glass of claim 7, wherein the amount of cobalt to obtain the gray colored glass is in the range of 2 to 12 ppm.

11. The colored glass of claim 1, wherein the amount of total iron expressed as Fe2O3 is in the range of 0.25 to 0.36 wt. %.

12. The colored glass of claim 1, wherein the amount of manganese oxide as MnO2 is in the range of 0.15 to 0.45 wt. %.

13. The colored glass of claim 1, wherein the infra red transmittance is in the range of 22% to 35%.

14. The colored glass of claim 1, wherein the colored glass at 4 mm. control thickness has an ultra violet transmittance in the range of 35% to 62%.

15. The colored glass of claim 1, wherein the composition of the base by weight of the colored glass is: 68 to 75 wt. % SiO2; 0 to 18 wt. % Na2O; 0 to 15 wt. % CaO; 0 to 10 wt. % MgO; 0 to 5 wt. % Al2O3; and 0 to 5 wt. % K2O; wherein the total amount of CaO and MgO is in a range of 6 to 15 wt. % and the total amount of Na2O and K2O is in a range of 10 to 20 wt. %.