Guidewires having a vapor deposited primer coat

Information

  • Patent Grant
  • 6569107
  • Patent Number
    6,569,107
  • Date Filed
    Monday, January 29, 2001
    23 years ago
  • Date Issued
    Tuesday, May 27, 2003
    21 years ago
Abstract
An intraluminal device having an adhesive primer coat formed of a carbonaceous material and a lubricious top coat of a hydrophilic polymeric material. The invention also comprises the methods of making such intraluminal devices. The primer coat of the invention may comprise pure carbon, or a carbon based material such as a polymer. Preferably, the primer coat has a thickness of about 0.1 to about 2 μm. In a presently preferred embodiment, the primer coat is applied using chemical vapor deposition (CVD), but in certain embodiments, physical vapor deposition (PVD) may be suitable. The deposited primer coat forms an effective substrate for adhesion of the hydrophilic polymer top coat.
Description




BACKGROUND OF THE INVENTION




This invention is directed to the field of elongated intraluminal devices having lubricious coatings, and, in particular, to a guidewire having a thin carbonaceous primer coat and a hydrophilic polymer top coat.




In a typical coronary procedure a guiding catheter having a preformed distal tip is percutaneously introduced into a patient's peripheral artery, e.g. femoral or brachial artery, by means of a conventional Seldinger technique and advanced therein until the distal tip of the guiding catheter is seated in the ostium of a desired coronary artery. There are two basic techniques for advancing a guidewire into the desired location within the patient's coronary anatomy, the first is a preload technique which is used primarily for over-the-wire (OTW) devices and the bare wire technique which is used primarily for rail type systems. With the preload technique, a guidewire is positioned within an inner lumen of an OTW device such as a dilatation catheter or stent delivery catheter with the distal tip of the guidewire just proximal to the distal tip of the catheter and then both are advanced through the guiding catheter to the distal end thereof. The guidewire is first advanced out of the distal end of the guiding catheter into the patient's coronary vasculature until the distal end of the guidewire crosses the arterial location where the interventional procedure is to be performed, e.g. a lesion to be dilated or a dilated region where a stent is to be deployed. The catheter, which is slidably mounted onto the guidewire, is advanced out of the guiding catheter into the patient's coronary anatomy over the previously introduced guidewire until the operative portion of the intravascular device, e.g. the balloon of a dilatation or a stent delivery catheter, is properly positioned across the arterial location. Once the catheter is in position with the operative means located within the desired arterial location, the interventional procedure is performed. The catheter can then be removed from the patient over the guidewire. Usually, the guidewire is left in place for a period of time after the procedure is completed to ensure reaccess to the arterial location if it is necessary. For example, in the event of arterial blockage due to dissected lining collapse, a rapid exchange type perfusion balloon catheter such as described and claimed in U.S. Pat. No. 5,516,336 (McInnes et al.), can be advanced over the in-place guidewire so that the balloon can be inflated to open up the arterial passageway and allow blood to perfuse through the distal section of the catheter to a distal location until the dissection is reattached to the arterial wall by natural healing.




With the bare wire technique, the guidewire is first advanced by itself through the guiding catheter until the distal tip of the guidewire extends beyond the arterial location where the procedure is to be performed. Then a rail type catheter, such as described in U.S. Pat. No. 5,061,395 (Yock) and the previously discussed McInnes et al. which are incorporated herein by reference, is mounted onto the proximal portion of the guidewire which extends out of the proximal end of the guiding catheter which is outside of the patient. The catheter is advanced over the catheter, while the position of the guidewire is fixed, until the operative means on the rail type catheter is disposed within the arterial location where the procedure is to be performed. After the procedure the intravascular device may be withdrawn from the patient over the guidewire or the guidewire advanced further within the coronary anatomy for an additional procedure.




Conventional guidewires for angioplasty, stent delivery, atherectomy and other vascular procedures usually comprise an elongated core member with one or more tapered sections near the distal end thereof and a flexible body such as a helical coil or a tubular body of polymeric material disposed about the distal portion of the core member. A shapeable member, which may be the distal extremity of the core member or a separate shaping ribbon which is secured to the distal extremity of the core member extends through the flexible body and is secured to the distal end of the flexible body by soldering, brazing or welding which forms a rounded distal tip. Torquing means are provided on the proximal end of the core member to rotate, and thereby steer, the guidewire while it is being advanced through a patient's vascular system.




Further details of guidewires, and devices associated therewith for various interventional procedures can be found in U.S. Pat. No. 4,748,986 (Morrison et al.); U.S. Pat. No. 4,538,622 (Samson et al.): U.S. Pat. No. 5,135,503 (Abrams); U.S. Pat. No. 5,341,818 (Abrams et al.); and U.S. Pat. No. 5,345,945 (Hodgson et al.) which are hereby incorporated herein in their entirety by reference thereto.




Guidewires have been the subject of continual improvement. One direction of improvement has centered on reducing the surface friction of the guidewire to facilitate relative movement between the guidewire and a guiding catheter or a dilatation catheter within a patient's body lumen. Much of the innovation has centered on laminating low friction, polymeric materials onto the surface of the guidewire. However, it has proven difficult to obtain a tenacious bond between the lubricious polymer coating and the material of the guidewire. Further, achieving a uniform coat of polymer over the helical shapeable distal tip of most guidewires presents several difficulties. For example, bridging of the coat material between adjacent coils interferes with the designed flexibility of the distal tip and thereby effects performance of the guidewire.




In addition to guidewires, many intraluminal devices can benefit from a lubricious surface to facilitate insertion and guidance to the desired intraluminal destination. Reducing friction also minimizes luminal trauma caused by insertion of these devices, particularly in blood vessels such as coronary arteries. As with guidewires, much has been done with the prior art lubricious polymeric coatings to produce intraluminal devices having low friction surfaces. However, a number of drawbacks are associated with the use of polymeric coatings. Providing such devices with a uniform and tenacious coating is technically difficult and correspondingly expensive.




There remains a need for intraluminal devices having a lubricious polymeric coating which is thin and which is strongly adhered to the device. Further, there is a need for a process of applying such lubricious polymeric coatings in a repeatable, uniform and cost effective manner. This invention satisfies these and other needs.




SUMMARY OF THE INVENTION




This invention comprises an intraluminal device having a vapor deposited primer coat formed of a carbonaceous material and a lubricious top coat of a hydrophilic polymeric material. The invention also comprises the methods of making such intraluminal devices.




The vapor deposited primer coat of the invention may comprise substantially pure carbon, or a carbon-based material such as plasma polymerized hydrocarbons, polyurethane, or nylon, and preferably has a thickness of about 0.1 to about 2 μm. A variety of carbonaceous source materials may be used to form the primer coat depending on the composition of the primer coat and the coating method used. The primer coat is applied to the surface of the intraluminal device using chemical vapor deposition (CVD), or in certain embodiments as discussed below, physical vapor deposition (PVD). The deposited primer coat forms an effective substrate for adhesion of a later applied hydrophilic polymer top coat. The hydrophilic polymer top coat may be applied by a variety of methods, including CVD, PVD, dipping, spraying and the like.




In a presently preferred embodiment of the invention, the primer coat and the hydrophilic top coat are applied to the surface of a distal tip coil of a guidewire. The use of vapor deposition provides a thin primer coat which provides uniform coverage of the helical coil. In a presently preferred embodiment of the invention, at least a stretched section of the coil are coated such that the adjacent turns of the coated coils do not touch one another. A thicker, less uniform primer coat would likely bridge the adjacent coils, or significantly increase the diameter of the coils so that bridging would likely result in the lubricious top coat, which can interfere with guidewire performance.




The deposited primer coat of the invention has superior adhesion to the base material of an intraluminal device, and provides improved adhesion between a hydrophilic top coat and the device. Additionally, the deposited primer coat does not bridge the adjacent turns of guidewire tip coils, and does not significantly increase the thickness of the coating on the device. These and other advantages of the invention will become more apparent from the following detailed description and accompanying exemplary drawings.











BRIEF DESCRIPTION OF THE DRAWINGS





FIG. 1

illustrates guidewire of the invention with a shapeable coil tip and a distal portion having an adhesive primer coat and a hydrophilic polymer top coat.





FIG. 2

is a cross section of the intermediate coil of the guidewire of FIG.


1


.





FIG. 3

is a sectional detail of the shapeable coil showing the hydrophilic polymer top coat.





FIG. 4

is a further detail of

FIG. 3

, showing the hydrophilic polymer top coat and the adhesive primer coat.





FIG. 5

is schematic diagram of a CVD apparatus suitable for the practice of this invention.











DETAILED DESCRIPTION OF THE INVENTION





FIGS. 1-4

illustrate a guidewire


10


having features of this invention that generally include an elongated core member


12


and a distal tip


14


having a thin carbonaceous primer coat and a hydrophilic top coat on at least a portion thereof. The distal tip


14


, which may be shaped or shapeable, comprises a flexible helical coil


16


and a rounded member


18


on the distal extremity, preferably formed by a solder plug securing helical coil


16


to core member


12


.

FIG. 3

shows a detail of the distal portion


20


of the helical coil


16


which has a uniform hydrophilic polymer coating


22


. Various portions of the guidewire may be coated as desired. In a presently preferred embodiment, the distal 30 cm of guidewire


10


is coated, which includes the flexible helical coil


16


and a portion of the core member proximal to the intermediate coils. In other embodiments, only the coils


16


or only a distal portion of the coils, such as the distal 3 cm coils, may be coated, depending on the desired guidewire characteristics.





FIG. 4

is a further sectional detail of helical coil


16


, showing the base material


24


of the coil, adhesive primer coat


26


and hydrophilic polymer top coat


22


. Generally, base material


24


of guidewire


10


is stainless steel, but it may comprise a shape memory material such as nickel-titanium alloys or other materials. Primer coat


26


is either substantially pure carbon, or a carbon-based material.




In the embodiment in which the primer coat


26


is substantially pure carbon, a variety of source materials may be used to form the carbon primer coat, including graphite and pyrolytic carbon. The presently preferred coating method for applying a substantially pure carbon primer coating


26


from a graphite or pyrolytic carbon source is physical vapor deposition.




The presently preferred coating method for applying a carbon-based primer coating


26


is chemical vapor deposition. It should be understood that the carbon-based primer coating


26


applied by CVD comprises a plasma polymerized coating, so that the resulting polymer comprises an amorphous structure having groups in the structure other than the monomer groups of the source materials. For example, plasma polymerized polyethylene may include a variety of functional groups, such as vinyl, in addition to the methylene groups. The presently preferred carbon-based primer coating


26


is plasma polymerized nylon or plasma polymerized polyethylene. However, a variety of suitable carbon-based polymeric primer coatings may be used including plasma polymerized polypropylene, plasma polymerized polyurethane, and the like. A variety of suitable carbon based source materials may be used to form the carbon-based primer coating


26


. For example, vapor reactants having the carbonyl and amine functional groups characteristic of nylon, such as adipic acid and hexanediamine, may be used to form a plasma polymerized nylon primer coat. Additionally, hydrocarbons such as methane, ethane, hexane and the like, may be used as source materials. Primer coat


26


is very thin, generally about 0.1 to about 2 μm depending on the type of material.




Any suitable hydrophilic polymer may be used as top coat


22


, including poly(N-vinylpyrrolidone) (PVP), polyethylene oxide (PEO), Hydro Gel™, methacrylates and the like. Generally, the thickness of top coat


22


is about 0.0025 mm (0.1 mil) to about 0.015 mm (0.5 mil), but may vary depending on the application. Any suitable means of applying top coat


22


may be employed, including vapor deposition, dipping, spraying and the like.




The length of the guidewire


10


may be about 160 cm to about 310 cm. The OD of the guidewire and distal tip coil is about 0.025 cm to about 0.05 cm. The distal tip coil is formed from wire having a diameter of about 0.002 in (0.05 mm) to about 0.0055 in (0.14 mm). The spacing between adjacent turns of the helically wound coils varies along the length of the device, from substantially stacked coils having substantially space between adjacent coils, to stretched coils having a spacing of about 15% to about 30% of the wire diameter.




CVD typically involves vaporized compounds flowing over a substrate. A plasma can be generated via RF energy or the like to activate the deposition reactions. The reaction of the compounds in the plasma state and at the substrate surface results in a film coating. CVD should be performed at low pressures to enhance the quality of the coating. The use of a CVD process allows the application of very thin, uniform and repeatable primer coats, without causing bridging between adjacent coils on the guidewire.





FIG. 5

is a schematic diagram of a suitable CVD apparatus


28


, having a reaction chamber


30


, gas/vapor source


31


, gas/vapor inlet


32


, an electronic pressure regulator system


33


, a pressure sensor,


34


, a vacuum pump


35


, a RF power supply and regulator


36


, and RF induction coils


37


around the outside of the chamber. As an alternative to induction coils, plasma can be generated via capacitor plates (not shown), typically located inside the chamber


30


. Before deposition of the primer coat


26


, the guidewire is typically cleaned using well known procedures, such as washing with a solvent such as 1,1,1, trichloroethane, or exposure to ultrasonication or the plasma gas in the CVD chamber. Generally, the guidewire is suitably masked and placed in reaction chamber


30


. A nonreactive gas such as argon is used to purge the chamber atmosphere and the pressure is reduced to less than about 50 mtorr. RF power supply


36


and induction coils


37


are used to generate a plasma from the chamber gas. Desired gases or vapors are introduced through inlets


32


, which in the presence of the plasma, polymerize and deposit on the substrate. The reaction is allowed to continue until a sufficiently thick layer of primer coat is deposited, then the plasma is turned off and the chamber purged again with nonreactive gas. In general, the plasma power is about 5 to 50 Watts and the gas/vapor flow is less than about 20 sccm. Under these parameters, a suitable primer coat is applied in about 1 to 10 minutes. A plasma polymerized polyethylene coating was applied using hexane vapor as a source material, at a power of 50W and a flow rate of 5 sccm for 10 minutes.




The primer coat


26


may be applied using physical vapor deposition (PVD). In general, PVD involves generation of the coating, transport of the coating to the substrate and growth of the coating on the substrate. Generation of the coating may be achieved either by evaporation or sputtering. In evaporative schemes, thermal energy from resistance, induction, electron-beam or laser beam sources is used to vaporize the coating. Sputtering, on the other hand uses plasma ions generated by direct current or radio frequency to energize and eject species of the coating material towards the substrate. Generating species with greater energies can improve adhesion with the substrate. Transport of the vaporized coating generally depends on the partial pressure of the vaporized coating; for example molecular flow occurs at low partial pressures while viscous flow occurs at higher partial pressures. Depending on the technique, the substrate may also be biased. Finally, growth of the coating depends on the energy of the vaporized coating and substrate temperature. One of skill in the art will be able to tailor the conditions to the type of coating being applied and the substrate material.




While the invention has been described herein primarily with reference to presently preferred embodiments comprising an adhesive primer coat applied to a guidewire through vapor deposition, various modifications and improvements can be made to the invention without departing from the scope thereof. For example, while the carbon-based primer coatings were primarily described as a CVD polymerized coating, PVD may also be used to apply the primer coat. The coatings may be applied to a variety of intraluminal products including electrophysiology devices, atherectomy catheters, stents and the like without departing from the scope thereof.



Claims
  • 1. An intraluminal stent having a primer coat formed of a carbonaceous material and vapor deposited on at least a portion of the device, and a hydrophilic polymer top coat on at least a portion of the primer coat.
  • 2. The intraluminal stent of claim 1, wherein the primer coat has a uniform thickness of not more than about 2 μm.
  • 3. The intraluminal stent of claim 1, wherein the primer coat is selected from the group consisting of carbon, plasma polymerized nylon, plasma polymerized polyurethane, plasma polymerized polyethylene, and plasma polymerized hydrocarbons.
  • 4. The intraluminal stent of claim 1, wherein the top coat is selected from the group consisting of poly(N-vinylpyrrolidone), and polyethylene oxide.
  • 5. The intraluminal stent of claim 1, wherein the top coat has a thickness of about 0.0025 mm to about 0.015 mm.
Parent Case Info

This application is a divisional application of copending application Ser. No. 09/092,229, filed Jun. 5, 1998, which is hereby incorporated herein by reference.

US Referenced Citations (45)
Number Name Date Kind
4538622 Samson et al. Sep 1985 A
4748986 Morrison et al. Jun 1988 A
4952357 Euteneuer Aug 1990 A
5061273 Yock Oct 1991 A
5084151 Vallana et al. Jan 1992 A
5135503 Abrams Aug 1992 A
5272012 Opolski Dec 1993 A
5295978 Fan et al. Mar 1994 A
5341818 Abrams et al. Aug 1994 A
5345945 Hodgson et al. Sep 1994 A
5350395 Yock Sep 1994 A
5356433 Rowland et al. Oct 1994 A
5387247 Vallana et al. Feb 1995 A
5423886 Arru et al. Jun 1995 A
5443455 Hergenrother et al. Aug 1995 A
5455072 Bension et al. Oct 1995 A
5477864 Davidson Dec 1995 A
5506059 Robbins et al. Apr 1996 A
5516336 McInnes et al. May 1996 A
5520664 Bricault, Jr. et al. May 1996 A
5552027 Birkle et al. Sep 1996 A
5562730 Davidson Oct 1996 A
5588443 Davidson Dec 1996 A
5607463 Schwartz et al. Mar 1997 A
5630840 Mayer May 1997 A
5647858 Davidson Jul 1997 A
5648127 Turchan et al. Jul 1997 A
5662622 Gore et al. Sep 1997 A
5665062 Houster Sep 1997 A
5681344 Kelly Oct 1997 A
5718678 Fleming, III Feb 1998 A
5722424 Engelson Mar 1998 A
5733400 Gore et al. Mar 1998 A
5735896 Amon et al. Apr 1998 A
5750206 Hergenrother et al. May 1998 A
5857997 Cimino et al. Jan 1999 A
5865721 Andrews et al. Feb 1999 A
5876369 Houser Mar 1999 A
5924998 Cornelius et al. Jul 1999 A
5971975 Mills et al. Oct 1999 A
5984878 Engelson Nov 1999 A
6090072 Kratoska et al. Jul 2000 A
6183443 Kratoska et al. Feb 2001 B1
6203534 Schoenholtz Apr 2001 B1
6240616 Yan Jun 2001 B1
Foreign Referenced Citations (5)
Number Date Country
4112936 Apr 1991 DE
747069 Jun 1996 EP
747069 Jun 1996 EP
769306 Sep 1996 EP
769306 Sep 1996 EP
Non-Patent Literature Citations (1)
Entry
Alexis T. Bell, “Review of lecture on plasma polymerization and structure of plasma films and oils”, The First Annual International Conference of Plasma Chemistry and Technology, 11/14-17/82.