Patent Application
20150036240
In magnetic storage devices such as hard disk drives (HDD), read and write heads are used to magnetically read and write information to and from the storage media. In a HDD, data is stored on one or more disks in a series of adjacent concentric circles. A HDD comprises a rotary actuator, a suspension mounted on an arm of the rotary actuator, and a slider bonded to the suspension to form a head gimbal assembly. In a traditional HDD, the slider carries a read/write head, and radially floats over the recording surface of the disk under the control of a servo control system that selectively position the head over a specific track of the disk.
During read and write operations, the head moves adjacent to the recording surface of the disk at the Head Disk Interface (HDI) in preparation for performing read and write operations. During this movement, intermittent contact between the head and disk surface may occur at the HDI, particularly at low fly heights (FH) between the flying head and the rotating disk. The conventional disk includes a conventional carbon overcoat to protect the magnetic recording layer of the disk and a conventional lubrication layer on the carbon overcoat to prevent the head from crashing. More recently, the conventional read/write head also includes a dynamic flying height (DFH) adjust to control the FH. The DFH adjust acts by lowering the head portion of the slider to the disk by applying thermal actuation during read and write operations.
With areal recording densities rapidly increasing on the HDD, however, the FH continues to decrease, approaching sub 1 nm ranges. This decrease in FH decreases the available spacing margin for the slider. Even slight pitches or roll angles of the slider at this FH result in head-disk contacts. Accordingly, it is desirable to manufacture a hard disk with a lubrication layer that increases the DFH touch-down power by minimizing the spacing between the disk head and disk surface while maintaining good tribology performance.
The present application is illustrated by way of example, and not limitation, in the figures of the accompanying drawings in which:
FIGS. 2A through 2D-6 illustrate molecular structures for exemplary lubricants that may be used as the lubricant in the bonded lubrication layer of the hard disk of
FIGS. 3A through 3B-6 illustrate molecular structures for exemplary lubricants that may be used as the lubricant in the mobile lubrication layer of the hard disk of
In the following description, numerous specific details are set forth to provide a thorough understanding of various embodiment of the present disclosure. It will be apparent to one skilled in the art, however, that these specific details need not be employed to practice various embodiments of the present disclosure. In other instances, well known components or methods have not been described in detail to avoid unnecessarily obscuring various embodiments of the present disclosure.
The terms “over,” “under,” “between,” and “on” as used herein refer to a relative position of one media layer with respect to other layers. As such, for example, one layer disposed over or under another layer may be directly in contact with the other layer or may have one or more intervening layers. Moreover, one layer disposed between two layers may be directly in contact with the two layers or may have one or more intervening layers. By contrast, a first layer “on” a second layer is in contact with that second layer. Additionally, the relative position of one layer with respect to other layers is provided assuming operations are performed relative to a substrate without consideration of the absolute orientation of the substrate.
In accordance with the present disclosure, systems and methods are illustrated for manufacturing hard disks with double lubrication layers that allow minimization of the DFH touchdown point while maintaining good tribology performance for HDD reliability. These benefits are achieved by providing two lubrication layers comprising different lubricant materials to maximize the separate functions of: 1) conformity and 2) durability and mobility. The disclosed hard disks may be implemented in a high storage density HDD that includes a DFH adjust. In one embodiment, the disclosed hard disk may be implemented in a heat-assisted magnetic recording HDD.
In this exemplary embodiment, the two lubrication layers 103-104 comprise different lubricants. In one embodiment, the different lubricants are per-fluoro-poly-ether (PFPE) lubricants. Bonded lubrication layer 103 comprises a highly condensed and conformal lubricant for maximizing the available spacing margin and thereby lowering the DFH touch-down point. In one embodiment, the thickness of bonded lubrication layer 103 is between 5 Å and 10 Å. The thinness and uniformity of bonded lubrication layer 103 provides the benefit of allowing a close fly-by of the HDD head.
FIGS. 2A through 2D-6 illustrate molecular structures for exemplary PFPE lubricants that may be used in one embodiment of bonded lubrication layer 103. In this exemplary embodiment, the molecular structure 200 of bonded lubrication layer 103 comprises a functional end group 201, a center connection structure 202, and a fluorocarbon chain 203. These exemplary lubricants exhibit the property of a short branch length relative to conventional lubricants, thereby allowing for a smaller gyration diameter and lower physical thickness of bonded lubrication layer 103.
Mobile lubrication layer 104 comprises a low friction and high durability lubricant for improving tribology performance of the HDD, i.e. preventing dragging of a read/write head on disk 100. The high lubricity of mobile lubrication layer 104 provides the benefit of minimizing the wear of carbon overcoat layer 102, which protects the magnetic recording layer 101 of disk 100. Moreover, the high lubricity of mobile lubrication layer 104 provides the benefit of minimizing HDD head carbon overcoat wear. In one embodiment, the thickness of mobile lubrication layer 104 is between 2 Å to 4 Å.
FIGS. 3A through 3B-6 illustrate molecular structures for exemplary lubricants that may be used as the lubricant in the mobile lubrication layer 104 of the hard disk of
In one embodiment, bonded lubrication layer 103 and mobile layer 104 comprise the same PFPE lubricant but with different molecular weights (MW). For example, in one embodiment mobile layer 104 may comprise a higher MW version of the PFPE lubricant. This provides the benefit of preventing the loss of mobile lubrication by evaporation during drive operations at high temperatures. In this embodiment, bonded lubrication layer 103 may comprise a lower MW version of the PFPE lubricant for a thin and conformal lubrication layer structure.
At operation 404, a bonding treatment is applied to the disk to bond the first lubricant to the disk, thereby creating the first lubrication layer, bonded lubrication layer 103. The bonding treatment increases the bonding strength between the lubricant molecules and the carbon overcoat 102. In one embodiment, the bonding treatment comprises exposing the disk to ultraviolet (UV) light. For example, the disk may be exposed to a low-pressure Mercury UV lamp between 20 and 40 seconds. In an alternative embodiment, the bonding treatment comprises heating the disk in a chamber above a predetermined temperature, for example 100 C. The second lubrication layer may then be formed at operations 406-408.
Before coating the disk with a second lubricant after bonding operation 404, any non-bonding lubricant may be removed at operation 406. This removal process provides the benefit of preventing mixing of non-bonded first lubricant with the second lubricant, thereby maximizing the effect of the second lubricant. Moreover, operation 406 provides the benefit of keeping the subsequent coating process contamination free. In one embodiment, non-bonded lubricant is removed or stripped using a stripping solvent. For example, the disk may be soaked in fluorinated solvent for 5 to 10 minutes to dissolve un-bonded first lubricant material into the solvent. After soaking, the disk may be removed from the solvent at a predetermined speed, for example, 1 to 2 mm/second.
At operation 408, the disk is coated with a second solution comprising a second lubricant and a fluorosolvent. In exemplary dipping lubrication process 400, operation 408 is performed by dipping the disk in the second solution and removing the disk from the first solution at a predetermined speed (e.g. 1 to 2 mm/second), thereby creating a second lubrication layer, mobile layer 104. In one embodiment, the fluorosolvent has a concentration of 0.01-0.02 wt %.
At operation 506, prior to coating the disk with a second lubricant via a second vaporization process, any non-bonding first lubricant is removed using any suitable removal process such as for example, the strip removal process described above in operation 406. The disk is then coated with a second lubricant at operation 508 by applying a vapor lubrication process. In one exemplary implementation of the vapor lubrication process, a high lubricity lubricant is coated on the disk without solvent by vaporizing the lubricant via direct heating inside a vacuum chamber. A second lubrication layer, mobile layer 104, is thereby creating.
In alternative embodiments, a combination of dipping and vaporization processes may be implemented in the manufacture of the double lubrication layer (e.g. dipping to create first lubrication layer and vaporization to create second lubrication layer or vice-versa). In yet other embodiments, the disk may comprise more than two lubrication layers, whereby the plurality of lubrication layers improve the head touchdown point and overall HDI reliability.
In the foregoing specification, embodiments of the disclosure have been described with reference to specific exemplary features thereof. It will, however, be evident that various modifications and changes may be made thereto without departing from the broader spirit and scope of the disclosure. The specification and figures are, accordingly, to be regarded in an illustrative rather than a restrictive sense.
This application claims the benefit of U.S. Provisional Application Ser. No. 61/859,938 (Atty. Docket No. M6712.P), filed Jul. 30, 2013, which is incorporated herein by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 61859938 | Jul 2013 | US |