The present disclosure relates to alloy compositions for arc welding and more particularly to weld deposit compositions suitable for hard surfacing that reduce cracking and increase wear resistance and hardness.
The statements in this section merely provide background information related to the present disclosure and may not constitute prior art.
Hard-facing relates generally to techniques or methods of applying a hard, wear resistant alloy to the surface of a substrate, such as a softer metal, to reduce wear caused by abrasion, erosion, corrosion, and heat, among other operational or environmental conditions. A variety of methods are available to apply the wear resistant alloy to the substrate, among which includes welding, where a welding wire is deposited over the substrate surface to produce a weld deposit that is highly wear resistant. The welding wire may include a solid wire, metal-cored wire or a flux-cored wire, wherein the metal-cored wire generally comprises a metal sheath filled with a powdered metal alloy and the flux-cored wire generally comprises a mixture of powdered metal and fluxing ingredients. Accordingly, flux-cored and metal-cored wires offer additional versatility due to the wide variety of alloys that can be included within the powdered metal core in addition to the alloy content provided by the sheath.
One known welding wire material that is commonly used for hard-facing includes chromium carbides. While conventional chromium carbides provide good wear resistance, the weld deposits produced from chromium carbide welding wires can produce a cross-checking pattern in the hard weld deposit surface, which is undesirable due to an increased susceptibility to cracking from such patterns. Additionally, coarse chromium carbides contribute to check-cracking, which are cracks that develop perpendicular to a bead direction and accelerate abrasive wear.
In general, weld deposits with improved crack resistance, improved wear resistance, and improved hardness are provided by using nucleation sites to control matrix grain size and by balancing Titanium and/or Niobium with Carbon and/or Boron content. Additionally, the presence of coarse chromium carbides is drastically decreased to reduce the amount of check-cracking. Preferably, the weld deposit is produced from a flux-cored/metal-cored wire, however, it should be understood that other types of welding consumables such as a solid wires or coated shielded metal arc electrodes may also be employed. The weld deposit characteristics include a matrix having a fine grain size, small evenly dispersed carbides within the matrix, and a small amount of Carbon in the matrix. Additional alloying elements are provided for desired properties of the weld deposit and are described in greater detail herein.
In one form of the present disclosure, a weld deposit composition produced from a flux-cored or metal-cored welding wire is provided that comprises, by percent mass, between approximately 0.7% and approximately 2.0% Carbon, between approximately 0.2% and approximately 0.5% Manganese, between approximately 0.5% and approximately 1.1% Silicon, between approximately 2.0% and approximately 8.0% Chromium, between approximately 2.0% and approximately 6.0% Molybdenum, between approximately 2.0% and approximately 5.0% Tungsten, between approximately 2.0% and approximately 8.0% Niobium and Titanium, between approximately 1.0% and approximately 2.5% Vanadium, between approximately 0.2% and approximately 0.9% Boron, and a balance comprising Iron. In additional forms, the Carbon comprises approximately 1.1%, the Manganese comprises approximately 0.3%, the Silicon comprises approximately 0.8%, the Chromium comprises approximately 4.0%, the Molybdenum comprises approximately 4.0%, the Tungsten comprises approximately 3.5%, the Niobium and Titanium comprise approximately 3.2%, the Vanadium comprises approximately 1.8%, and the Boron comprises approximately 0.5%.
In another form, a weld deposit composition produced from a flux-cored or metal-cored welding wire is provided that comprises, by percent mass, between approximately 0.7% and approximately 2.0% Carbon, between approximately 0.1% and approximately 0.5% Manganese, between approximately 0.7% and approximately 1.4% Silicon, between approximately 6.0% and approximately 11.0% Chromium, between approximately 0.5% and approximately 2.0% Molybdenum, between approximately 2.0% and approximately 8.0% Niobium and Titanium, between approximately 0.2% and approximately 1.0% Vanadium, between approximately 0.2% and approximately 0.9% Boron, between approximately 0.4% and approximately 0.8% Copper, and a balance comprising Iron. In additional forms, the Carbon comprises approximately 1.1%, the Manganese comprises approximately 0.3%, the Silicon comprises approximately 0.8%, the Chromium comprises approximately 9.0%, the Molybdenum comprises approximately 0.8%, the Niobium and Titanium comprise approximately 3.5%, the Vanadium comprises approximately 0.3%, the Boron comprises approximately 0.5%, and the Copper comprises approximately 0.6%.
In yet other forms of the present disclosure, a flux-cored or metal-cored welding wire capable of producing a weld deposit having the above-mentioned elements and a welded structure having a weld deposit with the above elements is provided by the teachings of the present disclosure.
Further areas of applicability will become apparent from the description provided herein. It should be understood that the description and specific examples are intended for purposes of illustration only and are not intended to limit the scope of the present disclosure.
The drawings described herein are for illustration purposes only and are not intended to limit the scope of the present disclosure in any way.
a is a photomicrograph of a weld deposit exhibiting a matrix having a fine grain size in accordance with the teachings of the present disclosure; and
b is a photomicrograph of a second weld deposit exhibiting a matrix having a fine grain size in accordance with the teachings of the present disclosure.
The following description is merely exemplary in nature and is not intended to limit the present disclosure, application, or uses. It should be understood that throughout the drawings, corresponding reference numerals indicate like or corresponding parts and features.
Weld deposits for use in hard-surfacing applications that produce improved crack resistance, improved wear resistance, and improved hardness are provided by controlling matrix grain size and balancing Titanium and/or Niobium with Carbon content according to the teachings of the present disclosure. Additionally, the presence of coarse chromium carbides is drastically reduced to reduce the amount of check-cracking. Preferably, the weld deposit is produced from a flux-cored wire, however, it should be understood that other types of welding consumables such as a solid wire or coated shielded metal arc electrodes may also be employed while remaining within the scope of the present disclosure. The weld deposit characteristics include a matrix having a fine grain size, small evenly dispersed carbides within the matrix, and a small amount of Carbon in the matrix. Additional alloying elements are provided for various properties of the weld deposit and are described in greater detail below.
Referring to
The specific alloy elements and their amounts that are present in the weld deposits according to the teachings of the present disclosure are now described in greater detail.
Referring to Table 1 below, two (2) weld deposit compositions (including both target percentages and ranges of percent elements by weight) according to the present disclosure are listed as “Weld Deposit A” and “Weld Deposit B,” along with typical M7 tool steel and martensitic hard-facing compositions for purposes of comparison. The M7 tool steel is a composition that is used quite frequently in applications involving significant wear and impact. With the compositional modifications to this M7 tool steel composition made with Weld Deposit A, there is significant improvement in the wear resistance. The martensitic hardfacing composition is a lower cost overlay that has significant usage in the hard-facing industry in applications requiring moderate resistance to wear and impact. Weld Deposit B is a modification of this martensitic hardfacing composition that results in a significant improvement in wear resistance.
Each element and its contribution to properties of the weld deposit are now described in greater detail.
Carbon (C) is an element that improves hardness and strength. The preferred amount of Carbon for both Weld Deposit A and Weld Deposit B is between approximately 0.7 and 2.0 percent, with a target value of approximately 1.1%.
Manganese (Mn) is an element that improves hardness, toughness and acts as a deoxidizer, in which the deoxidizer also acts as a grain refiner when fine oxides are not floated out of the metal or if the final grain boundary area is increased by final solidification of a manganese-silicon rich eutectic phase. The preferred amount of manganese for Weld Deposit A is between approximately 0.2 and 0.5 percent, with a target value of approximately 0.3%. The preferred amount of manganese for Weld Deposit B is between approximately 0.1 and 0.5 percent, with a target value of approximately 0.2%.
Silicon (Si) is an element that acts as a deoxidizer to improve corrosion resistance and which also acts as a grain refiner when fine oxides are not floated out of the metal or if the final grain boundary area is increased by final solidification of a manganese-silicon rich eutectic phase. The preferred amount of Silicon for Weld Deposit A is between approximately 0.5 and 1.1 percent, with a target value of approximately 0.8%. The preferred amount of Silicon for Weld Deposit B is between approximately 0.7 and 1.4 percent, with a target value of approximately 1.0%. Silicon is also added to the weld metal to improve fluidity.
Chromium (Cr) is an element that provides depth of hardenability, corrosion resistance, carbide/boride formation, and improved high temperature creep strength. The preferred amount of Chromium for Weld Deposit A is between approximately 2.0 and approximately 8.0 percent, with a target value of approximately 4.0%. The preferred amount of Chromium for Weld Deposit B is between approximately 6.0 and approximately 11.0 percent, with a target value of approximately 9.0%.
Molybdenum (Mo) is an element that provides improved tensile strength of the weld deposit as carbide, boride, or a solid-solution strengthener. Tungsten and molybdenum act as solid-solution strengtheners. Tungsten and molybdenum can be substituted for each other in many cases, but the molybdenum is more effective at increasing matrix strength and hardness. The preferred amount of molybdenum for Weld Deposit A is between approximately 2.0 and approximately 6.0 percent, with a target value of approximately 4.0%. The preferred amount of molybdenum for Weld Deposit B is between approximately 0.1 and approximately 2.0 percent, with a target value of approximately 0.8%.
Tungsten (W) is an element that provides improved creep strength of the weld deposit. The preferred amount of tungsten for Weld Deposit A is between approximately 2.0 and approximately 5.0 percent, with a target value of approximately 3.5%. Tungsten is not present in Weld Deposit B due to cost considerations and the presence of molybdenum.
Titanium (Ti) and Niobium (Nb) act as grain refiners, deoxidizers, and primary carbide/boride formers. The amounts of Titanium and Niobium are balanced with the amount of Carbon/Boron as set forth above in order to reduce the amount of Carbon/boron in the weld metal matrix and grain boundaries, which reduces the possibility of cracking and improves the toughness of the hard-facing surface. The ratios of the elements are based on the atomic weights and the type of intermetallic carbide/boride desired. The Titanium is generally 4 times the mass of Carbon, and the niobium is generally 8 times the mass of Carbon. Any excess Carbon is left to the secondary carbide formers and the matrix. The ratio of the Titanium to Boron is 4.4 for Titanium Boride and 2.2 for Titanium Diboride. The Niobium/Boron ratio is 8.6 for Niobium Boride and 4.3 for Niobium Diboride. The Titanium/Niobium and the Carbon/Boron pairs are substitutional in nature, and thus deviations from these ratios can be tolerated and should be construed as falling within the scope of the present disclosure. Additionally, particles of these elements freeze at a very high temperature and are therefore considered primary carbides/borides.
Vanadium (V) is secondary carbide former and a grain refiner and thus increases toughness of the weld deposit. The preferred amount of Vanadium for Weld Deposit A is between approximately 1.0 and approximately 2.5 percent, with a target value of approximately 1.8%. The preferred amount of Vanadium for Weld Deposit B is between approximately 0.2 and approximately 1.0 percent, with a target value of approximately 0.3%.
The Titanium and Niobium when combined with Carbon and/or Boron will act as grain refiners to provide nucleation sites for the formation of many small grains, which contribute to improved crack resistance. Additionally, the small grains improve ductility and reduce hot tearing by increasing the grain boundary area and reducing the average distance that the grains have to slide against each other to accommodate the local strain induced by shrinkage due to cooling. The grain boundary sliding is known as shear, which is generally responsible for hot-tearing in the grain boundaries.
Boron (B) is an element that provides interstitial hardening in the matrix, strengthens the grain boundaries by accommodating mismatches due to incident lattice angles of neighboring grains with respect to the common grain boundary, and by itself or in combination with Carbon, form nucleation sites as intermetallics with Titanium and/or Niobium. The preferred amount of Boron for Weld Deposit A is between approximately 0.2 and approximately 0.9 percent, with a target value of approximately 0.5%. The preferred amount of Boron for Weld Deposit B is between approximately 0.2 and approximately 0.9 percent, with a target value of approximately 0.5%.
Copper (Cu) is an alloying element that can be used in steels to modify the structure by providing a secondary phase to partition/refine grains or by depressing the freezing point of the austenite phase for a shorter freezing range. The shorter freezing range means that less shear strain is exerted on the phase due to the coefficient of thermal expansion/contraction. In effect, there is less strain due to the contraction that occurs upon cooling because the austenite is cooled through only half of its normal freezing range. Since austenite is prone to hot tearing, targeting this phase to avoid any excess shear stresses greatly reduces this failure mechanism in the alloy. The preferred amount of Copper for Weld Deposit B is between approximately 0.4% and approximately 0.8%, with a target value of approximately 0.6%. Preferably, there is no Copper in Weld Deposit A.
The compositions of the weld deposits according to the teachings of the present disclosure are formulated to reduce the amount of cross-checking as compared with other martensitic and tool steel welding wire deposits while improving wear resistance. In exemplary testing, the composition of Weld Deposit A has shown improved hardness and weight loss when compared to other weld deposit compositions as shown below in Table 2.
Referring to
By controlling the matrix grain size and balancing the Titanium and/or Niobium with the Carbon/Boron content, weld deposits having improved crack resistance are produced according to the teachings of the present disclosure. Additionally, the weld deposits according to the present disclosure do not contain coarse chromium carbides. The absence of the coarse chromium carbide phases will reduce the presence of check-cracking.
By way of example,
The description of the disclosure is merely exemplary in nature and, thus, variations that do not depart from the gist of the disclosure are intended to be within the scope of the disclosure. For example, the weld deposit according to the teachings of the present disclosure may be produced from welding wire types other than flux-cored/metal-cored wires, such as solid wires, while remaining within the scope of the present disclosure. Such variations are not to be regarded as a departure from the spirit and scope of the disclosure.
This application is a division of U.S. application Ser. No. 11/356,409 filed on Feb. 16, 2006. The disclosure of the above application is incorporated herein by reference.
Number | Name | Date | Kind |
---|---|---|---|
3368887 | Enis et al. | Feb 1968 | A |
3575737 | Carlen et al. | Apr 1971 | A |
3876475 | Ramqvist | Apr 1975 | A |
4116684 | Uchida et al. | Sep 1978 | A |
4122238 | Frantzerb, Sr. | Oct 1978 | A |
4331857 | Crisci et al. | May 1982 | A |
4396822 | Kishida et al. | Aug 1983 | A |
4423119 | Brown et al. | Dec 1983 | A |
4800131 | Marshall et al. | Jan 1989 | A |
4810850 | Tenkula et al. | Mar 1989 | A |
4822415 | Dorfman et al. | Apr 1989 | A |
4897519 | Clark et al. | Jan 1990 | A |
4987288 | Yonker, Jr. | Jan 1991 | A |
5095191 | Bushey et al. | Mar 1992 | A |
5192016 | Araki et al. | Mar 1993 | A |
5250355 | Newman et al. | Oct 1993 | A |
5348212 | Galanes | Sep 1994 | A |
5525779 | Santella et al. | Jun 1996 | A |
5744782 | Sampath et al. | Apr 1998 | A |
6124569 | Bonnet et al. | Sep 2000 | A |
6228183 | Bangaru et al. | May 2001 | B1 |
6521060 | Kurata et al. | Feb 2003 | B1 |
6521867 | Bonnet et al. | Feb 2003 | B2 |
6702905 | Qiao et al. | Mar 2004 | B1 |
6841246 | Shimizu et al. | Jan 2005 | B2 |
6866816 | Liang et al. | Mar 2005 | B2 |
6899772 | Morando | May 2005 | B1 |
6908589 | Kitudo et al. | Jun 2005 | B2 |
6940042 | Hara et al. | Sep 2005 | B2 |
6953508 | Ikeda et al. | Oct 2005 | B2 |
7459041 | Beguinot et al. | Dec 2008 | B2 |
7794651 | Beguinot et al. | Sep 2010 | B2 |
20060283526 | Liang | Dec 2006 | A1 |
20070187369 | Menon et al. | Aug 2007 | A1 |
Number | Date | Country |
---|---|---|
1745184 | Aug 2006 | CN |
2754437 | Jul 1979 | DE |
3543601 | Jun 1986 | DE |
WO 2004067793 | Aug 2004 | WO |
WO 2007-097946 | Aug 2007 | WO |
Entry |
---|
International Search Report and Written Opinion of the International Searching Authority, dated May 29, 2008, pp. 1-15, International Application No. PCT/US2007/03744, European Patent Office, Rijswijk. |
Number | Date | Country | |
---|---|---|---|
20130294819 A1 | Nov 2013 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 11356409 | Feb 2006 | US |
Child | 13932681 | US |