Claims
- 1. A rock bit hard facing comprising:
- steel in the range of from 18% to 32% by weight; and
- filler in the range of from 68% to 82% by weight, the filler comprising:
- from 20% to 65% by weight single crystal monotungsten carbide particles;
- from 35% to 80% by weight cemented tungsten carbide particles; and
- a balance of steel deoxidizer.
- 2. A rock bit hard facing as recited in claim 1 wherein the particle size of the single crystal monotungsten carbide is primarily between 40 and 80 mesh.
- 3. A rock bit hard facing as recited in claim 1 wherein the particle size of the cemented tungsten carbide is primarily between 20 and 30 mesh.
- 4. A rock bit hard facing as recited in claim 1 wherein the cemented tungsten carbide comprises particles of monotungsten carbide having an average particle size in the range of from one to fifteen microns bonded together by cobalt in the range of from 6% to 8% by weight.
- 5. A rock bit hard facing as recited in claim 1 wherein the particle size of the cemented tungsten carbide is larger than the particle size of the single crystal monotungsten carbide.
- 6. A rock bit as recited in claim 1 wherein the particle size of the cemented tungsten carbide particles is from two to five times larger than the particle size of the single crystal monotungsten carbide particles.
- 7. A rock bit hard facing as recited in claim 6 wherein the particle size of the cemented tungsten carbide is three times larger than the particle size of the single crystal monotungsten carbide.
- 8. A rock bit hard facing as recited in claim 1 wherein the filler comprises from 20% to 35% by weight single crystal monotungsten carbide particles, from 65% to 80% cemented tungsten carbide particles, and up to 5% steel deoxidizer.
- 9. A rock bit hard facing as recited in claim 8 wherein the particle size of the cemented tungsten carbide particles is from two to five times larger than the particle size of the single crystal monotungsten carbide particles.
- 10. A rock bit hard facing comprising:
- at least 65% particles primarily of tungsten carbide and a balance of alloy steel, the particles comprising:
- a first set of relatively larger cemented tungsten carbide particles and a second set of relatively smaller single crystal monotungsten carbide particles, the particle size in the first set being from two to five times the particle size in the second set and wherein the weight percentage of the cemented tungsten carbide particles is two to five times the weight percentage of single crystal monotungsten carbide.
- 11. A rock bit hard facing as recited in claim 10 wherein the particle size of the first set is primarily in the range of from 20 to 30 mesh and the particle size in the second set is primarily in the range of from 40 to 80 mesh.
- 12. A rock bit hard facing as recited in claim 11 wherein the weight percentage of 20 to 30 mesh particles is about three times the weight percentage of 40 to 80 mesh particles.
- 13. A rock bit hard facing as recited in claim 10 wherein the first set of particles consists essentially of cemented tungsten carbide primarily in the range of from 20 to 30 mesh and the second set comprises single crystal monotungsten carbide primarily in the range of from 40 to 80 mesh.
- 14. A rock bit hard facing as recited in claim 13 wherein the weight percentage of cemented tungsten carbide is three times the weight percentage of single crystal monotungsten carbide.
- 15. A rock bit hard facing comprising:
- steel in the range of from 18% to 32% by weight; and
- filler in the range of from 68% to 82% by weight, the filler consisting essentially of:
- from 20% to 65% by weight single crystal monotungsten carbide particles;
- from 35% to 80% by weight cemented tungsten carbide particles; and
- a balance of steel deoxidizer.
- 16. A rock bit hard facing as recited in claim 15 wherein the particle size of the single crystal monotungsten carbide is primarily between 40 and 80 mesh.
- 17. A rock bit hard facing as recited in claim 15 wherein the particle size of the cemented tungsten carbide is primarily between 20 and 30 mesh.
- 18. A rock bit hard facing as recited in claim 15 wherein the cemented tungsten carbide comprises particles of monotungsten carbide having an average particle size in the range of from one to fifteen microns bonded together by cobalt in the range of from 6% to 8% by weight.
- 19. A rock bit hard facing as recited in claim 15 wherein the particle size of the cemented tungsten carbide is larger than the particle size of the single crystal monotungsten carbide.
- 20. A rock bit as recited in claim 15 wherein the particle size of the cemented tungsten carbide particles is from two to five times larger than the particle size of the single crystal monotungsten carbide particles.
- 21. A rock bit hard facing as recited in claim 20 wherein the particle size of the cemented tungsten carbide is three times larger than the particle size of the single crystal monotungsten carbide.
- 22. A rock bit hard facing as recited in claim 15 wherein the filler comprises from 20% to 35% by weight single crystal monotungsten carbide particles, from 65% to 80% cemented tungsten carbide particles, and up to 5% steel deoxidizer.
- 23. A rock bit hard facing as recited in claim 22 wherein the particle size of the cemented tungsten carbide particles is from two to five times larger than the particle size of the single crystal monotungsten carbide particles.
CROSS-REFERENCE TO RELATED APPLICATIONS
This is a division of application Ser. No. 07/139,602 filed Dec. 29, 1987.
US Referenced Citations (16)
Foreign Referenced Citations (3)
Number |
Date |
Country |
0288775 |
Nov 1988 |
EPX |
8702711 |
May 1987 |
WOX |
8804649 |
Jun 1988 |
WOX |
Divisions (1)
|
Number |
Date |
Country |
Parent |
139602 |
Dec 1987 |
|