Claims
- 1. A coated substrate product comprised of
- (1) a substrate selected from the group consisting of titanium and titanium alloy, which substrate has been treated with a mild abrasive to remove oxides from its surface,
- (2) a thin, non-reactive noble metal interlayer deposited by an electroless plating technique after the treatment with said mild abrasive, said noble metal coated substrate is then subjected to a heat treatment by heating the substrate and the noble metal interlayer to a temperature in the range of about 200.degree. to about 300.degree. C. in the presence of air or a temperature in the range of about 200.degree. to about 475.degree. C. in the presence of an inert gas selected from the group consisting of argon, helium and mixtures thereof, and
- (3) a hard outer coating selected from the group consisting of a ceramic, a hard metal, a hard metal compound and a carbon having a hardness of greater than 1,000 Vickers.
- 2. A coated substrate product according to claim 1 wherein the non-reactive noble metal interlayer is consisting of a noble metal selected from the group comprised of cobalt, rhodium, iridium, nickel, palladium, platinum, copper, silver and gold, alloys thereof and mixtures thereof.
- 3. A coated substrate product according to claim 1 wherein said hard outer coating is selected from the group consisting of oxides, carbides, nitrides, carbonitrides, borides and silicides of the Group IIIB or Group IVB elements of the Periodic Table; transition element metals; oxides, carbides, nitrides, carbonitrides, silicides and borides of transition element metals; a carbon having a hardness of greater than 1,000 Vickers; and mixtures thereof.
- 4. A coated substrate product according to claim 1 wherein the noble metal interlayer is from about 0.5 microns to about 15 microns in thickness.
- 5. A coated substrate produce according to claim 1 wherein said hard outer coating has a hardness of at least 350 Vickers.
- 6. A coated substrate product comprised of:
- (1) a substrate selected from the group consisting of titanium and titanium alloys, which substrate has been treated with a mild abrasive to remove oxides from its surfaces,
- (2) two thin, non-reactive noble metal interlayers herein at least the non-reactive noble metal interlayer which is immediately adjacent to the substrate is deposited on the substrate by means of an electroless plating technique after treatment with said mild abrasive to remove oxides from its surface, said noble metal coated substrate is then subjected to a heat treatment by heating the substrate and the noble metal interlayers to a temperature in the range of about 200.degree. to about 300.degree. C. in the presence of air or a temperature in the range of about 200.degree. to about 475.degree. C. in the presence of an inert gas selected from the group consisting of argon, helium and mixtures thereof, and
- (3) a hard outer coating selected from the group consisting of a ceramic, a hard metal, a hard metal compound and a carbon having a hardness of greater than 1,000 Vickers onto the noble metal interlayers.
- 7. A coated substrate product according to claim 6 wherein the thin noble metal interlayers are selected from the group consisting of cobalt, rhodium, iridium, nickel, palladium, platinum, copper, silver and gold, alloys thereof and mixtures thereof.
- 8. A coated substrate product according to claim 6 wherein the two thin noble metal interlayers together are about 0.5 microns to about 15 microns in thickness.
- 9. A coated substrate product according to claim 6 wherein the noble metal interlayer which is not immediately adjacent to the titanium or titanium alloy substrate is deposited onto the interlayer which is immediately adjacent to the substrate by means of an electrochemical plating technique.
- 10. A coated substrate product according to claim 6 wherein said hard outer coating has a hardness of at least 350 Vickers.
- 11. A coated substrate product comprised of: (1) a titanium or titanium alloy substrate which has been treated with a mild abrasive to remove oxides from its surface, (2) a thin nickel interlayer which was deposited onto the substrate by means of an electroless plating technique, after treatment with said mild abrasive, said nickel coated substrate is then subjected to a heat treatment by heating the substrate and the nickel interlayer to a temperature in the range of about 200.degree. to about 475.degree. C. in the presence of an inert gas selected from the group comprising argon, helium and mixtures thereof and (3) an outer coating of tungsten and/or tungsten carbide.
- 12. A coated substrate product according to claim 11 wherein the nickel interlayer is from about 0.5 microns to about 15 microns in thickness.
- 13. A coated substrate product comprised of:
- (1) a titanium or titanium alloy substrate which has been treated with a mild abrasive to remove oxides from its surface,
- (2) a first noble metal interlayer comprised of a thin nickel interlayer which was deposited onto the titanium substrate by means of an electroless plating technique, and a second noble metal interlayer comprised of a thin layer of copper which is deposited onto the nickel interlayer by means of an electrochemical plating technique, said noble metal coated substrate is then subjected to a heat treatment by heating the substrate and the noble metal interlayers to a temperature in the range of about 200.degree. to about 300.degree. C. in the presence of air or a temperature in the range of about 200.degree. to about 475.degree. C. in the presence of an inert gas selected from the group comprising argon, helium and mixtures thereof, and
- (3) an outer coating of tungsten and/or tungsten carbide.
- 14. A coated substrate product according to claim 13 wherein the first nickel interlayer is about one micron thick and the second copper interlayer is about 4 microns thick.
Parent Case Info
This is a division of application Ser. No. 139,891, filed Dec. 31, 1989, now U.S. Pat. No. 4,902,535.
US Referenced Citations (23)
Foreign Referenced Citations (4)
Number |
Date |
Country |
186266 |
Jul 1986 |
EPX |
188057 |
Jul 1986 |
EPX |
1209347 |
Jan 1968 |
GBX |
1540718 |
Mar 1975 |
GBX |
Non-Patent Literature Citations (4)
Entry |
ASTM-B481-68 (Reapproved 1985) Standard Practice for "Preparation of Titanium and Titanium Alloys for Electroplating". |
A. Brenner & G. Riddell U.S. Dept. of Comm.-NBOS-"Deposition of Nickel and Cobalt by Chemical Reduction" Research Paper RP1835. |
ASTM-Sp. Tech. Publn. No. 265 1959 "Electroless Nickel Plating". |
1987 Am. Vacuum Society "Characterization of Diamondlike Carbon Films and Their Application as Overcoats on Thin-Film Media for Magnetic Recording," pp. 3287-3311, vol. A5(6) Nov.-Dec. 87. |
Divisions (1)
|
Number |
Date |
Country |
Parent |
139891 |
Dec 1987 |
|