Claims
- 1. A fully aromatic polyester blend comprising 1 to 19 parts by weight of a polyester (a) comprising the following recurring moieties: ##STR18## wherein the sum of the number of units (II) and (III) is approximately equal to the number of unit (I); and unit (IV) ranges from about 0.18 to about 9.0 moles per each mole of unit (I); and which has a melting point in the range of from about 340.degree. to about 400.degree. C., a crystallization temperature of from about 300.degree. to about 340.degree. C., and a crystallization rate of at least 1,000 counts/minute; to one part by weight of a polyester (b) comprising recurring moieties: ##STR19## wherein the sum of the number of units (VI) and (VII) is approximately equal to the number of unit (V); and unit (VIII) ranges from about 1 to about 7 moles per each mole of unit (V); and said blend, when filled with 30 weight percent glass fibers has an heat distortion temperature of at least 240.degree. C. when measured under a load of 264 psi.
- 2. A blend comprising from about 1 to about 19 parts by weight of a first polyester polymer (a) comprising units (I), (II), (III) and (IV): ##STR20## where (I) is approximately equal to (II)+(III); q is in the range of from about 0.05 to about 0.76; r is in the range of from about 0.95 to about 0.24; s is in the range of from about 0.10 to about 9.0 moles per each mole of unit (I); per one part by weight of a second polyester polymer (b) comprising unit (IX), (X) and (XI): ##STR21## wherein e is approximately equal to f; e is 1; and g is in the range of from about 1.5 to about 5 moles per each mole of unit (IX).
- 3. A blend consisting essentially of about 1 to about 95 parts by weight of a first polyester (a) comprising units (I), (II), (III) and (IV): ##STR22## where (I) is approximately equal to (II)+(III); q is in the range of from about 0.05 to about 0.76; r is in the range of from about 0.95 to about 0.24; s is in the range of from about 0.10 to about 9.0 moles per each mole of unit (I); per one part by weight of a second polyester (b) comprising units (IX), (X) and (XI); ##STR23## wherein e is approximately equal to f, e is 1 mole; g is in the range of from about 1.5 moles to about 5 moles per each mole of e.
- 4. A blend as defined in claim 2 having a heat distortion temperature of at least about 200.degree. C. when measured under a load of 264 psi, and which yields fabricated articles having good surface characteristics.
- 5. A blend as defined in claim 2 wherein the component first and second polyesters are each prepared by reacting the aromatic dicarboxylic acid(s), the p-hydroxybenzoic acid, and the aromatic diol with an anhydride of a lower monocarboxylic acid to yield a prepolymer, followed by a solid state advancement of said prepolymer to a desired final molecular weight.
- 6. A blend as defined in claim 2 wherein s is about 0.25 mole to about 0.55 mole per each mole of unit (I); q is about 0.50 mole to about 0.70 mole; and r is about 0.30 mole to about 0.50 mole.
- 7. A blend as defined in claim 2 wherein s is about 0.55 mole to about 9.0 moles per each mole of unit (I); q is about 0.05 to about 0.80 mole; and r is about 0.95 mole to about 0.20 mole.
- 8. A blend as defined in claim 2 wherein when e is one mole g is in the range of from about 2 to about 4 moles.
- 9. A blend as defined in claim 2 wherein when unit (I) is one mole s is about 0.25 mole to about 0.55 mole per each mole of unit (I); q is about 0.50 mole to about 0.70 mole; r is about 0.30 mole to about 0.50 mole; e is 1 mole; and g is in the range of from about 2 to about 4 moles.
- 10. A blend as defined in claim 2 wherein when unit (I) is 1 mole s is about 0.55 mole to about 9.0 mole per each mole of unit (I); q is about 0.050 to about 0.80 mole; r is about 0.95 mole to about 0.20 mole; e is one mole; and g is in the range of from about 2 to about 4 moles.
- 11. A blend comprising from about 1 to about 19 parts by weight of a first polyester polymer comprising units (IX), (X), (XI), (XII): ##STR24## where n is 1 and 2; the number of moles of units (IX) is approximately equal to the number of moles of units (X)+(XI); to one part by weight of a second polyester polymer comprising at least one unit:
- --X.sub.1 -Ar-X.sub.2 -- (XIII)
- wherein Ar comprises at least one member selected from the group consisting of: ##STR25## X.sub.1 and X.sub.2 are independently selected from the group consisting of oxy and carbonyl.
- 12. The blend of claim 11 wherein the Ar group of the second polyester also comprises a divalent aromatic radical comprising at least one phenylene group.
- 13. A blend consisting essentially of from about 1 to 19 parts by weight of a first polyester comprising units (IX), (X), (XI), (XII): ##STR26## where n is 1 and 2; the number of moles of units (IX) is approximately equal to the number of mole of units (X) and (XI); to one part by weight of a second polyester comprising at least one unit:
- --X.sub.1 -Ar-X.sub.2 -- (XIII)
- wherein Ar comprises at least one member selected from the group consisting of: ##STR27## X.sub.1 and X.sub.2 are independently selected from the group consisting of oxy and carbonyl.
- 14. The blend of claim 13 wherein the Ar group of the second polyester also comprises a divalent aromatic radical comprising at least one phenylene group.
- 15. A blend as defined in claim 11 comprising from about 1 to 19 parts by weight of a first polyester comprising units (IX), (X), (XI), (XII): ##STR28## where n is 1; (IX) is approximately equal to (X)+(XI); (X) is in the range of from about 0.05 to about 0.76; (XI) is in the range of from about 0.95 to about 0.24; (XII) is in the range of from about 0.10 to about 9.0 moles per each mole of unit (IX); to one part by weight of a second polyester comprising at least one unit:
- --X.sub.1 -Ar-X.sub.2 -- (XIII)
- wherein Ar, X.sub.1 and X.sub.2 are as previously defined in claims 11 and 12.
- 16. The blend of claim 15 wherein the Ar group of the second polyester also comprises a divalent aromatic radical comprising at least one phenylene group.
- 17. A blend as defined in claim 11 consisting essentially of from about 5 to about 95 parts by weight of a first polyester comprising units (IX), (X), (XI), (XII): ##STR29## where n is 1; (IX) is approximately equal to (X)+(XI); (X) is in the range of from about 0.05 to about 0.76; (XI) is in the range of from about 0.95 to about 0.24; (XII) is in the range of from about 0.10 to about 9.0 moles per each mole of unit (IX); and from about 95 to about 5 parts by weight of a second polyester comprising at least one unit:
- --X.sub.1 -Ar-X.sub.2 -- (XIII)
- wherein Ar, X.sub.1 and X.sub.2 are as previously defined in claims 11 and 12.
- 18. The blend of claim 17 wherein the Ar group of the second polyester also comprises a divalent aromatic radical comprising at least one phenylene group.
- 19. A blend as defined in claim 11 comprising from about 5 to about 95 parts by weight of a first polyester comprising units (IXb), (IXc), (Xa), (XIa), (XIIa): ##STR30## wherein e'+e" is approximately equal to f+g; the ratio of e' to e" is from about 3:1 to about 99:1; the ratio of f to g is from about 0.42:1 to about 10:1; and the ratio of h to f+g is in the range of from about 0.15:1 to about 8.0:1 moles per one mole of monomers corresponding to the sum of units (IXb)+(IXc); and from about 95 to about 5 parts by weight of a second polyester comprising at least one unit:
- --X.sub.1 -Ar-X.sub.2 -- (XIII)
- wherein Ar, X.sub.1 and X.sub.2 are as previously defined in claims 11 and 12.
- 20. The blend of claim 19 wherein the Ar group of the second polyester also comprises a divalent aromatic radical comprising at least one phenylene group.
- 21. A blend as defined in claim 11 consisting essentially of from about 5 to about 95 parts by weight of a first polyester comprising units (IXb), (IXc), (Xa), (XIa), (XIIa): ##STR31## wherein e'+e" is approximately equal to f+g; the ratio of e' to e" is from about 3:1 to about 99:1; the ratio of f to g is from about 0.42:1 to about 10:1; and the ratio of h to f+g is in the range of from about 0.15:1 to about 8.0:1 moles and from about 95 to about 5 parts by weight of a second polyester comprising at least one unit:
- --X.sub.1 -Ar-X.sub.2 -- (XIII)
- wherein Ar, X.sub.1 and X.sub.2 are as previously defined in claims 11 and 12.
- 22. The blend of claim 21 wherein the Ar group of the second polyester also comprises a divalent aromatic radical comprising at least one phenylene group.
- 23. A blend as defined in claim 11 having heat distortion temperature of at least 175.degree. C. when measured under a load of 264 psi.
- 24. A blend as defined in claim 11 having heat distortion temperature of at least 200.degree. C. when measured under a load of 264 psi.
- 25. A blend as defined in claim 11 wherein the first polyester is comprised of units (IX), (X), (XI), (XII): ##STR32## where n is 1; (IX) is approximately equal to (X)+(XI) is from about 0.50 to about 0.70; (XI) is from about 0.30 to about 0.50; and (XII) is from about 0.25 to about 0.55 mole per each mole of unit (IX).
- 26. A blend as defined in claim 11 wherein the first polyester is comprised of units (IX), (X), (XI), (XII): ##STR33## where n is 1; (IX) is approximately equal to (X)+(XI); (X) is from about 0.05 to about 0.80; (XI) is from about 0.20 to about 0.95; and (XII) is from about 0.55 to about 9.0 moles per each mole of unit (IX).
- 27. A blend as defined in claim 11 wherein the first polyester is comprised of units (IXb), (IXc), (Xa), (XIa), (XIIa): ##STR34## wherein e'+e" is approximately equal to f+g; the ratio of e' to e" is from about 3.0:1 to about 99.1; the ratio of f to g is from about 0.42:1 to about 10:1; and the ratio of h to f+g is from about 0.15:1 to about 8.0:1 moles.
- 28. A blend as defined in claim 11 wherein the second polyester consists essentially of the recurring units (XIX) and (XX) which may be substituted by one or more C.sub.1 to C.sub.4 alkyl groups, C.sub.1 to C.sub.4 alkoxy groups or halogen atoms; and wherein said second polyester comprises from about 10 to about 90 mole percent of units (XIX) and from about 90 to about 10 mole percent of units (XX) ##STR35##
- 29. A blend as defined in claim 11 wherein the second polyester consists essentially of the recurring units (XX), (XXI), (XXII): ##STR36## and wherein said second polyester comprises from about 40 to about 60 mole percent of units (XX); from about 20 to about 30 mole percent of units (XXI); and from about 20 to about 30 mole percent of units (XXII).
- 30. A blend as described in claim 29 wherein the second polyester consists essentially of the recurring units (XIX), (XXIII), (XXIV): ##STR37## which may be substituted by one or more C.sub.1 to C.sub.4 alkyl groups, C.sub.1 to C.sub.4 alkoxy groups, halogen atoms, or phenyl groups; wherein the group Ar.sub.1 is as previously defined in claims 11 and 12; and wherein said second polyester comprises from about 10 to about 90 mole percent of units (XIX); from about 5 to about 45 mole percent of units (XXIII); and from about 5 to about 45 mole percent of units (XXIV).
- 31. A molding compound comprising the blends of claim 2 and from about 1 to about 50 percent by weight, based upon the total weight of the molding compound, of at least one material selected from the group consisting of glass fibers, asbestos, graphitic carbon fibers, amorphous carbon fibers, synthetic polymeric fibers, aluminum, fibers, aluminum silicate fibers, oxide of aluminum fibers, titanium fibers, magnesium fibers, rock wool fibers, steel fibers, tungsten fibers, cotton, wool, and wood cellulose fibers, calcium silicate, silica, clays, talc, mica, carbon black, titanium dioxide, wollastonite, polytetrafluoroethylene, graphite, alumina trihydrate, sodium aluminum carbonate, barium ferrite, and glass beads.
- 32. A molding compound comprising the blends of claim 2 and from about 1 to about 50 percent by weight, based upon the total weight of the molding compound, of at least one material selected from the group consisting of glass fibers, asbestos, graphicit carbon fibers, amorphous carbon fibers, synthetic polymeric fibers, aluminum fibers, aluminum silicate fibers, oxide of aluminum fibers, titanium fibers, magnesium fibers, rock wool fibers, steel fibers, tungsten fibers, cotton, wool, and wood cellulose fibers, calcium silicate, silica, clays, talc, mica, carbon black, titanium dioxide, woolastonite, polytetrafluoroethylene, graphite, alumina trihydrate, sodium aluminum carbonate, barium ferrite, and glass beads.
- 33. An ovenware article comprising the molding compound of claim 31.
- 34. An ovenware article comprising the molding compound of claim 32.
Parent Case Info
This is a division of application Ser. No. 07/499,482, now U.S. Pat. No. 5,079,289, filed Jun. 4, 1990 which in turn is a continuation-in-part of Ser. No. 255,670, filed Oct. 11, 1988, now abandoned, and a continuation-in-part of Ser. No. 255,632 filed Oct. 11, 1988, now abandoned.
US Referenced Citations (4)
Non-Patent Literature Citations (1)
Entry |
"The Chemistry of Cellulose and Wood" Aca. of Sci. USSR., Nikitin, pp. 62-71 (1966). |
Divisions (1)
|
Number |
Date |
Country |
Parent |
499482 |
Jun 1990 |
|
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
255670 |
Oct 1988 |
|