Claims
- 1. A turbine part which is formed of a heat-resisting chromium steel,
- said steel essentially consisting of:
- a carbon content of 0.13 percent to 0.25 percent by weight;
- a silicon content of over 0.2 percent to 1.0 percent by weight;
- a manganese content of 1.0 percent or less by weight;
- a nickel content of 0.3 percent to 2.0 percent by weight;
- a chromium content of 8.0 percent to 11.0 percent by weight;
- a molybdenum content of 0.5 percent to 2.0 percent by weight;
- a vanadium content of 0.1 percent to 0.3 percent by weight;
- niobium and/or tantalum contents of over 0.03 percent to 0.3 percent by weight in total;
- a nitrogen content of 0.01 percent to 0.2 percent by weight;
- a tungsten content of over 1.1 percent to 2.0 percent by weight; and
- an iron content basically constituting the remainder,
- the chromium equivalent given by the following expression being from 9 to 10: chromium equivalent=-40.times.[%C]-30.times.[%N]-2.times.[%Mn]-4.times.[%Ni]+[%Cr]+4.times.[%Mo]+6.times.[%Si]+11.times.[%V]+5.times.%Nb]+2.5.times.[%Ta]+1.5.times.[%W]; PG,21
- said steel substantially having a tempered martensitic structure; and
- said steel having an elongation of not less than 18% and a reduction in area of not less than 60% at room temperature and a creep rupture time of not less than 850 hours at 600.degree. C. with an applied stress of 30 kg/mm.sup.2.
- 2. The turbine part according to claim 1, wherein said carbon content ranges from 0.13 percent to 0.15 percent by weight, said silicon content from over 0.2 percent to 0.6 percent, said manganese content from 0.3 percent to 0.8 percent, said nickel content from over 0.5 percent to 1.5 percent, said chromium content from 9.5 percent to 11.0 percent, said molybdenum content from 0.7 percent to 1.5 percent, said vanadium content from 0.15 percent to 0.27 percent, said niobium and/or tantalum contents from 0.10 to 0.27 percent in total, said nitrogen content from 0.03 percent to 0.08 percent, and said tungsten content from over 1.1 percent to 1.5 percent.
- 3. The turbine part according to claim 2, wherein said nickel contents ranges from 0.6 percent to 1.2 percent.
- 4. The turbine part according to claim 1, which is a turbine blade.
- 5. The turbine part according to claim 1, which is a turbine bolt.
Priority Claims (1)
Number |
Date |
Country |
Kind |
59-126481 |
Jun 1984 |
JPX |
|
Parent Case Info
This application is a continuation of application Ser. No. 742,302 filed June 7, 1985, abandoned.
US Referenced Citations (4)
Foreign Referenced Citations (9)
Number |
Date |
Country |
073021 |
Feb 1983 |
EPX |
1001131 |
Feb 1952 |
FRX |
62425 |
Jul 1955 |
FRX |
1140573 |
Mar 1957 |
FRX |
404137 |
May 1962 |
JPX |
462741 |
Aug 1966 |
JPX |
53-140217 |
May 1977 |
JPX |
55-110758 |
Aug 1980 |
JPX |
741935 |
Dec 1955 |
GBX |
Continuations (1)
|
Number |
Date |
Country |
Parent |
742302 |
Jun 1985 |
|