The present invention refers to heat-sensitive coating compositions for marking substrates, to a process for the preparation of these compositions, to a process of coating substrates with these compositions, to substrates coated with these compositions, to a process for preparing marked substrates using these compositions, to marked substrates obtainable by the latter process, and to certain colour developers.
Heat sensitive coatings in which the mechanism of image formation is dependent on the thermal reaction between a colour-forming substance and a colour developer are well known.
Today, such heat-sensitive coatings have many diverse uses that include fax transmissions, Point of Sales (POS) receipts, bank statements, Automated Teller Machine (ATM) printouts, delivery and grocery labels, and transportation, lottery and entertainment tickets.
A common problem with typical heat-sensitive coating compositions used to prepare heat-sensitive coatings is that rapid discolouring occurs upon storage in the wet state at room temperature or slightly elevated temperature. Thus the heat-sensitive coating composition has either to be prepared immediately before use or one of the reactive components has to be modified in some way to render it less reactive, for example through microencapsulation.
It is an object of the present invention to provide heat-sensitive coating compositions, which are storage stable, i.e. only undergo minimal darkening (yellowing) upon storage in the wet state at room temperature or even slightly elevated temperature, and which also provide images of high contrast and of high stability towards heat, oil and light.
This object is solved by the composition of claim 1, the processes of claims 8, 9 and 11, the substrates of claims 10 and 13, and the colour developers of claims 14, 15 and 16.
The coating composition of the present invention comprises a colour developer of formula
or mixtures thereof
wherein
R1 can be hydrogen, C1-20-alkyl, C3-8-cycloalkyl, C2-10-alkenyl, aryl or SO3H, and
R2 and R3 can be the same or different and can be hydrogen, halogen, C1-20-alkyl, C3-8-cyclo-alkyl, C2-10-alkenyl, aryl, OR6, NR7R8, SR9, SO3H or COOR10 and
R4 and R5 can be the same or different, and can be hydrogen, halogen, C1-20-alkyl, C3-8-cyclo-alkyl, C2-10-alkenyl, aryl, OR6, NR7R8 or SR9,
R6, R7, R8, R9 and R10 can be the same or different and can be hydrogen, C1-30-alkyl, C3-8-cycloalkyl, C2-10-alkenyl or aryl,
wherein
C1-20-alkyl can be unsubstituted or substituted with one or more C3-8-cycloalkyl, C2-10-alkenyl, phenyl, halogen, OR11, NR12R13, SR14, SO3H or COOR15, and
aryl can be unsubstituted or substituted with one or more halogen, C1-10-alkyl, halogenated C1-10-alkyl, C3-8-cycloalkyl, C2-10-alkenyl, phenyl, OR11, NR12R13, SR14, SO3H or COOR15,
wherein
R11, R12, R13, R14 and R15 can be the same or different and can be hydrogen, C1-10-alkyl, C3-8-cycloalkyl or C2-10-alkenyl.
Examples of C1-10-alkyl are methyl, ethyl, propyl, isopropyl, butyl, isobutyl, sec-butyl, tert-butyl, pentyl, hexyl, heptyl, octyl, nonyl and decyl. Preferably, C1-10-alkyl is C1-4-alkyl. C1-4-alkyl can be methyl, ethyl, propyl, isopropyl, butyl, isobutyl, sec-butyl or tert-butyl.
An example of a halogenated C1-10-alkyl is trifluoromethyl.
Examples of C1-20-alkyl are methyl, ethyl, propyl, isopropyl, butyl, isobutyl, sec-butyl, tert-butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, dodecyl, tetradecyl, heptadecyl, octadecyl and eicosyl. Preferably, C1-20-alkyl is C1-6-alkyl. C1-6-alkyl can be methyl, ethyl, propyl, isopropyl, butyl, isobutyl, sec-butyl, tert-butyl, pentyl or hexyl.
Examples of C1-30-alkyl are methyl, ethyl, propyl, isopropyl, butyl, isobutyl, sec-butyl, tert-butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, dodecyl, tetradecyl, heptadecyl, octadecyl, eicosyl, heneicosyl, docosyl, tricosyl, pentacosyl, heptacosyl and triacontyl.
Examples of C3-8-cycloalkyl are cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl and cyclooctyl.
Examples of C2-10-alkenyl are allyl, 2-butenyl and 3-hexenyl.
Examples of aryl are phenyl, naphthyl, pyrrolyl and pyridyl. Preferred aryls are phenyl and pyrrolyl.
Halogen can be fluorine, chlorine or bromine.
Examples of colour developers of formula 1 are
In preferred colour developers of formula
R1 is hydrogen, C2-10-alkenyl, aryl or SO3H, and
R2 and R3 can be the same or different and are hydrogen, C1-20-alkyl, aryl, OR6, NR7R8, SR9, SO3H or COOR15 and
R4 and R5 can be the same or different, and are hydrogen, C1-20-alkyl, aryl, OR6, NR7R8 or SR9,
R6, R7, R8, R9 and R10 can be the same or different and are hydrogen, C1-30-alkyl or aryl,
wherein
C1-20-alkyl can be unsubstituted or substituted with one or more phenyl, OR11, NR12R13, SR14, SO3H or COOR15, and
aryl can be unsubstituted or substituted with one or more C1-10-alkyl, halogenated C1-10-alkyl, OR11, NR12R13, SR14, SO3H or COOR15,
wherein
R11, R12, R13, R14 and R15 can be the same or different and can be hydrogen or C1-10-alkyl.
In more preferred colour developers of formula
R1 is hydrogen and
R2 and R3 can be the same or different and are hydrogen, C1-20-alkyl, OR6 or SO3H and
R4 and R5 can be the same or different, and are C1-20-alkyl, aryl, OR6, NR7R9 or SR9,
R6, R7, R8 and R9 can be the same or different and are hydrogen, C1-30-alkyl or aryl,
wherein
C1-20-alkyl is unsubstituted and
aryl can be unsubstituted or substituted with one or more C1-10-alkyl, halogenated C1-10-alkyl, OR11, SO3H or COOR15,
wherein
R11 and R15 can be the same or different and can be hydrogen or C1-10-alkyl.
In even more preferred colour developers of formula
R1 is hydrogen and
R2 and R3 can be the same or different and are hydrogen and
R4 and R5 can be the same or different, and are aryl,
wherein
aryl can be unsubstituted or substituted with one or more OR11,
wherein
R11 is hydrogen.
The most preferred colour developer is the colour developer of formula 1p.
Most colour developers of formula 1 are known in the art and/or can be prepared by known methods.
2,4,6-Tris(2,4-dihydroxyphenyl)-s-triazine (1c), for example, can be prepared by reacting cyanuric chloride with resorcinol as outlined in example 1 of EP 0 941 989 A2. 1q can be prepared in analogy by reacting cyanuric chloride with 2,6-dimethylphenol. 1p can be prepared by the cyclotrimerization of 4-hydroxybenzonitrile according to the procedure of Ninagawa et al Makromol. Chem. 1979, 180, 2123.
2-(2,4-dihydroxyphenyl)-s-triazine derivatives such as 1a, 1b, 1d, 1o or 1y can be prepared from the corresponding 2-chloro-s-triazine derivative and resorcinol. 4,6-Diphenyl-2-(2,4-di-hydroxyphenyl)-s-triazine (1a), for example, can be prepared from 4,6-diphenyl-2-chloro-s-triazine and resorcinol as described in example 14 of EP 0941 989 A2; and 4,6-bis(2,4-di-methylphenyl)-2-(2,4-dihydroxyphenyl)-s-triazine (1b), for example, can be prepared from 4,6-bis(2,4-dimethylphenyl)-2-chloro-s-triazine and resorcinol as described in example 3 of EP 0 941 989 A2. The preparation of 10 is described in example 23 of DE 1 670 332.
2,4-Bis(2,4-dihydroxyphenyl)-s-triazine derivatives such as 1e, 1f, 1g, 1h, 1i, 1j, 1k, 1l, 1m, 1n, 1r, 1s or 1x can be prepared by reacting the corresponding 2,4-dichloro-s-triazine derivative or 2,4-diphenoxy-s-triazine derivative with resorcinol or substituted resorcinol. 2,4-Bis(2,4-dihydroxy-5-hexylphenyl)-6-phenyl-s-triazine (1g), for example, can be prepared from 2,4-dichloro-6-phenyl-s-triazine and 4-hexylresorcinol as described in example 62 of EP 0 704 437 A2; and 2,4-bis(2,4-di-hydroxyphenyl)-6-(2,4,6-trimethylphenyl)-s-triazine (1i), for example, can be prepared from 2,4-diphenoxy-6-(2,4,6-trimethylphenyl)-s-triazine and resorcinol as described in example 17 of EP 0 941 989 A2. 1s, for example, can be prepared as described in EP 0 165 608 A2 (compound 113, table 1). 1u, for example, can be prepared as described in example 2b of EP 0 949 251 A1. 1x, for example, can be prepared as described in example 2 of EP 0 165 608 A2.
1v can be prepared by as described in Ninagawa et al Makromol. Chem. 1979, 180, 2123.
1w can be prepared by reacting 1b with sulphuric acid at 65 to 70° C.
The coating composition can comprise further colour developers known in the art, but the coating composition can also not include further colour developers beside the colour developer of formula 1 or mixtures thereof.
Examples of further colour developers known in the art are N-(p-toluenesulfonyl)-N′-(3-p-toluenesulfonyloxy)phenyl)urea, 4-hydroxy-4′-isopropoxydiphenyl sulfone and 2,4′-di-hydroxydiphenyl sulfone.
The colour developer of formula 1 or mixtures thereof can be microencapsulated by techniques known in the art, but the colour developer of formula 1 or mixtures thereof can also not be microencapsulated as this is not necessary in order to prevent darkening (yellowing) upon storage in the wet state at room temperature or even slightly elevated temperature.
The coating composition of the present invention can also comprise a colour former or a mixture of colour formers.
The colour former can be any suitable colour former such as a phthalide, a fluoran, a triarylmethane, a benzoxazine, a quinazoline, a spiropyran, a quinone, a thiazine or an oxazine or mixtures thereof.
Examples of phthalides are crystal violet lactone (3,3-bis(ρ-dimethylaminophenyl)-6-dimethyl-aminophtalide), 3,3-bis(ρ-dimethylaminophenyl)phthalide, 3,3-bis(1-ethyl-2-methylindol-3-yl)phthalide, 3,3-bis(1-octyl-2-methylindol-3-yl)phthalide, 3-(4-diethylaminophenyl)-3-(1-ethyl-2-methylindol-3-yl)-phthalide, 7-(N-ethyl-N-isopentylamino)-3-methyl-1-phenyl-spiro[4H-chromeno[2,3-c]pyrazole-4(1H)-3′ phthalide, 3,6,6′-tris(dimethylamino)spiro-[fluorene-9,3′-phthalide], 3,6,6′-tris(diethylamino)spiro[fluorene-9,3′-phthalide], 3,3-bis-[2-(ρ-dimethylaminophenyl)-2-(ρ-methoxyphenyl)ethenyl-4,5,6,7-tetrabromophthalide, 3,3-bis[2-(ρ-dimethylaminophenyl)-2-(ρ-methoxyphenyl)ethenyl-4,5,6,7-tetrachlorophthalide, 3,3-bis[1,1-bis(4-pyrrolidinophenyl)ethylene-2-yl]-4,5,6,7-tetrabromophthalide, 3,3-bis-[1-(4-methoxyphenyl)-1-(4-pyrridinophenyl)ethylene-2-yl]-4,5,6,7-tetrachlorophthalide, 3-(4-diethylamino-2-ethoxyphenyl)-3-(1-ethyl-2-methylindol-3-yl)-4-azaphthalide, 3-(4-diethylamino-2-ethoxyphenyl)-3-(1-octyl-2-methylindol-3-yl)-4-azaphthalide and 3-(4-cyclo-hexylethylamino-2-methoxyphenyl)-3-(1-ethyl-2-methylindol-3-yl)-4-azaphthalide
The phthalides can be prepared by methods known in the art, for example crystal violet lactone can be prepared as described in GB 1,347,467, and 3,3-bis(1-ethyl-2-methylindol-3-yl)phthalide can be prepared as described in GB 1,389,716.
Examples of fluorans are 3-di(ethyl)amino-6-methyl-7-(tert-butoxycarbonyl)anilinofluoran, 3-diethylamino-7-dibenzylamino)fluoran, 3-dibutylamino-7-dibenzylaminofluoran, 3-diethylamino-6-methyl-7-(dibenzylamino)fluoran, 3-diethylamino-6-methylfluoran, 3-diethylamino-6-chloro-7-methylfluoran, 3-diethylamino-6-methyl-7-chlorofluoran, 3-diethylamino-7-tert-butylfluoran, 3-diethylamino-7-ethylcarboxyfluoran, 3-diethylamino-7-methylfluoran, 3-diethylamino-6,8-dimethylfluoran, 3-diethylamino-7-chlorofluoran, 3-dibutylamino-6-methylfluoran, 3-cyclohexylamino-6-chlorofluoran, 3-diethylamino-benzo[a]fluoran, 3-diethylamino-benzo[c]fluoran, 3-dimethylamino-6-methyl-7-anilinofluoran, 3-diethylamino-6-methyl-7-anilinofluoran, 3-diethylamino-6-methyl-7-(2,4-dimethylanilino)fluoran, 3-diethylamino-6-methyl-7-(3-trifluoromethylanilino)fluoran, 3-diethylamino-6-methyl-7-(2-chloroanilino)-fluoran, 3-diethylamino-6-methyl-7-(ρ-chloroanilino)fluoran, 3-diethylamino-6-methyl-7-(2-fluoroanilino)fluoran, 3-diethylamino-6-methyl-7-(ρ-octylanilino)fluoran, 3-diethylamino-7-(ρ-octylanilino)fluoran, 3-diethylamino-6-methyl-7-(ρ-methylanilino)fluoran, 3-diethylamino-6-ethoxyethyl-7-anilinofluoran, 3-diethylamino-6-methyl-7-(3-methylanilino)fluoran, 3-diethyl-amino-7-(3-trifluoromethylanilino)fluoran, 3-diethylamino-7-(2-chloroanilino)fluoran, 3-diethyl-amino-7-(2-fluoroanilino)fluoran, 3-diethylamino-6-chloro-7-anilinofluoran, 3-dibutylamino-6-methyl-7-anilinofluoran, 3-dibutylamino-6-methyl-7-(2,4-dimethylanilino)fluoran, 3-dibutylamino-6-methyl-7-(2-chloroanilino)fluoran, 3-dibutylamino-6-methyl-7-(4-chloroanilino)-fluoran, 3-dibutylamino-6-methyl-7-(2-fluoroanilino)fluoran, 3-dibutylamino-6-methyl-7-(3-tri-fluoromethylanilino)fluoran, 3-dibutylamino-6-ethoxyethyl-7-anilinofluoran, 3-dibutylamino-6-chloro-anilinofluoran, 3-dibutylamino-6-methyl-7-(4-methylanilino)fluoran, 3-dibutylamino-7-(2-chloroanilino)fluoran, 3-dibutylamino-7-(2-fluoroanilino)fluoran, 3-dipentylamino-6-methyl-7-anilinofluoran, 3-dipentylamino-6-methyl-7-(4-2-chloroanilino)fluoran, 3-dipentylamino-7-(3-trifluoromethylanilino)fluoran, 3-dipentylamino-6-chloro-7-anilinofluoran, 3-dipentylamino-7-(4-chloroanilino)fluoran, 3-pyrrolidino-6-methyl-7-anilinofluoran, 3-piperidino-6-methyl-7-anilinofluoran, 3-(N-methyl-N-propylamino)-6-methyl-7-anilinofluoran, 3-(N-methyl-N-cyclohexylamino)-6-methyl-7-anilinofluoran, 3-(N-ethyl-N-cyclohexylamino)-6-methyl-7-anilinofluoran, 3-(N-ethyl-N-hexylamino)-7-anilinofluoran, 3-(N-ethyl-ρ-toluidino)-amino-6-methyl-7-anilinofluoran, 3-(N-ethyl-ρ-toluidino)amino-7-methylfluoran, 3-(N-ethyl-N-isoamylamino)-6-methyl-7-anilinofluoran, 3-(N-ethyl-N-isoamylamino)-7-(2-chloroanilino)-fluoran, 3-(N-ethyl-N-isoamylamino)-6-chloro-7-anilinofluoran, 3-(N-ethyl-N-tetrahydrofurfuryl-amino)-6-methyl-7-anilinofluoran, 3-(N-ethyl-N-isobutylamino)-6-methyl-7-anilinofluoran, 3-(N-butyl-N-isoamylamino)-6-methyl-7-anilinofluoran, 3-(N-isopropyl-N-3-pentylamino)-6-methyl-7-anilinofluoran, 3-(N-ethyl-N-ethoxypropylamino)-6-methyl-7-anilinofluoran, 2-methyl-6-ρ-(ρ-dimethylaminophenyl)aminoanilinofluoran, 2-methoxy-6-ρ-(ρ-dimethyl-aminophenyl)aminoanilinofluoran, 2-chloro-3-methyl-6-ρ-(ρ-phenylaminophenyl)aminoanilinofluoran, 2-diethylamino-6-ρ-(ρ-dimethylaminophenyl)aminoanilinofluoran, 2-phenyl-6-methyl-6-ρ-(ρ-phenylaminophenyl)aminoanilinofluoran, 2-benzyl-6-ρ-(ρ-phenylamino-phenyl)aminoanilinofluoran, 3-methyl-6-ρ-(ρ-dimethylaminophenyl)aminoanilinofluoran, 3-diethylamino-6-ρ-(ρ-diethylaminophenyl)aminoanilinofluoran, 3-diethylamino-6-ρ-(ρ-dibutyl-aminophenyl)aminoanilinofluoran and 2,4-dimethyl-6-[(4-dimethylamino)anilino]fluoran.
The fluorans can be prepared by methods known in the art, for example 3-diethylamino-7-di-benzylaminofluoran, 3-diethylamino-7-tert-butylfluoran, 3-diethylamino-6-methyl-7-anilinofluoran and 3-diethylamino-6-methyl-7-(2,4-dimethylanilino)fluoran and can be prepared as described in U.S. Pat. No. 5,166,350 A, 3-diethylamino-6-methyl-7-(3-methylanilino)fluoran can be prepared as described in EP 0 546 577 A1,3-diethylamino-6-chloro-7-anilinofluoran can be prepared as described in DE 2130845, 3-pyrrolidino-6-methyl-7-anilinofluoran and 3-piperidino-6-methyl-7-anilinofluoran can be prepared as described in U.S. Pat. No. 3,959,571 A, 3-(N-ethyl-N-isoamylamino)-6-methyl-7-anilinofluoran can be prepared as described in GB 2 002 801 A, and 3-(N-methyl-N-propylamino)-6-methyl-7-anilinofluoran can be prepared as described in GB 2 154 597 A.
Examples of benzoxazines are 2-phenyl-4-(4-diethylaminophenyl)-4-(4-methoxyphenyl)-6-methyl-7-dimethylamino-3,1-benzoxazine, which can be prepared as described in EP 0 187 329 A1, and 2-phenyl-4-(4-diethylaminophenyl)-4-(4-methoxyphenyl)-8-methyl-7-dimethylamino-3,1-benzoxazine.
An example of a quinazoline is 4,4′41-methylethylidene)bis(4,1-phenyleneoxy-4,2-quina-zolinediyl)]bis[N,N-diethylbenzeneamine]. An example of a triarylmethane is bis(N-methyldi-phenylamine)-4-yl-(N-butylcarbazole)-3-yl-methane, which can be prepared as described in GB 1,548,059.
Examples of spiropyrans are 1′,3′,3′-trimethylspiro[2H-1-benzopyran-2,2′-indoline], 1,3,3-tri-methylspiro[indoline-2,3′-[3H]naphth[2,1-b][1,4]oxazine] and 1′,3′,3′-trimethylspiro-[2H-1-benzothiopyran-2,2′-indoline].
An example of a quinone is hematoxyline. An example of an oxazine is 3,7-bis(dimethyl-amino)-10-benzoylphenoxazine. An example of a thiazine is 3,7-bis(dimethylamino)-10-benzoylphenothiazine.
Preferably, the colour former is a phthalide or a fluoran or mixtures thereof.
More preferably, the colour former is 3,3-bis(1-octyl-2-methylindol-3-yl)phthalide as sold for example under the tradename Ciba® Pergascript® Red 1-6B, 3-dibutylamino-6-methyl-7-anilinofluoran as sold for example under the tradename Ciba® Pergascript® Black T-2R or 3-diethylamino-7-ethylcarboxyfluoran as sold for example under the tradename Ciba® Pergascript® Black I-R.
The coating composition can also comprise a binder or a mixture of binders.
Examples of binders are polyvinyl alcohol (fully or partially hydrolysed), sulfonated-polyvinyl alcohol, carboxy-modified polyvinyl alcohol, acetoacetyl-modified polyvinyl alcohol, diacetone-modified polyvinyl alcohol, silicon-modified polyvinyl alcohol, oxidised starch, gelatine, caesin, derivatives of cellulose such as hydroxyethyl cellulose, methyl cellulose, ethyl cellulose, carboxymethyl cellulose and acetyl cellulose, starch-vinyl acetate graft copolymers, styrene-maleic anhydride copolymers, methyl vinyl ether-maleic anhydride copolymers, isopropylene-maleic anhydride copolymers and like water-soluble resins, styrene-butadiene latex, acrylic latex, urethane latex and like water-dispersible resins and mixtures thereof.
Preferred binders are polyvinyl alcohol (fully or partially hydrolysed), sulfonated-polyvinyl alcohol and acrylic latex and mixtures thereof. More preferably, the binder is polyvinyl alcohol.
The coating composition can comprise an aqueous medium. Usually the aqueous medium is water or a mixture of water and a water-miscible organic solvent. Preferably, the aqueous medium is water.
Examples of water-miscible organic solvents are C1-4-alkanols, C2-4-polyols, C3-6-ketones, C4-6-ethers, C2-3-nitriles, nitromethane, dimethylsulfoxide, dimethylformamide, dimethyl-acetamide, N-methylpyrolidone and sulfolane, whereby C1-4-alkanols and C2-4-polyols may be substituted with C1-4-alkoxy. Examples of C1-4-alkanols are methanol, ethanol, propanol, isopropanol, butanol, isobutanol, sec-butanol and tert-butanol. Examples of C1-4-alkoxy-derivatives thereof are 2-ethoxyethanol and 1-methoxy-2-propanol. Examples of C2-4-polyols are glycol and glycerol. Examples of C3-6-ketones are acetone and methyl ethyl ketone. Examples of C4-6-ethers are dimethoxyethane, diisopropylether and tetrahydrofurane. An example of a C2-3-nitrile is acetonitrile. Ethanol and isopropanol are preferred water-miscible organic solvents.
The coating composition can comprise a dispersing agent. Example of a dispersing agent are sodium naphthalene sulfonate, polymer with formaldehyde, and polyacrylic acid, sodium salt as sold for example under the tradename Ciba® Dispex® N40.
The coating composition can comprise a surfactant. Examples of surfactants are sodium dioctylsulfosuccinate, sodium dodecybenzenesulfonate, sodium lauryl sulfate, fatty acid metal salts and 2,4,7,9-tetramethyl-dec-5-in-4,7-diol (sold for example under the tradename Surfynol® 104).
The coating composition can also comprise additional components such as sensitizers, lubricants, pigments, stabilizers, insolubilisers, fluorescent whitening agents, wetting agents, IR absorbers, UV absorbers, antifoaming agents, fluorescent dyes, fluorescent pigment and tinting dyes.
Examples of sensitiser are benzyloxynaphthylene, stearamide, methylol stearamide, p-benzylbiphenyl, m-terphenyl, benzyl-2-naphthyl ether, 4-methoxybiphenyl, dibenzyl oxalate, di(4-methylbenzyl) oxalate, di(4-chlorobenzyl) oxalate, dimethyl terephthalate, dibenzyl terephthalate, dibenzyl isophthalate, 1,2-diphenoxyethane, 1,2-bis(4-methyl-phenoxy)ethane, 1,2-bis(3-methylphenoxy)ethane, 4,4′-dimethylbiphenyl, phenyl-1-hydroxy-2-naphthoate, 4-methylphenyl biphenyl ether, 1,2-bis(3,4-dimethylphenyl)ethane, 1,4-di-ethoxynaphthalene, o-xylylene-bis(phenyl ether), 4-(m-methylphenoxymethyl) biphenyl, p-hydroxyacetanilide, p-hydroxybutyranilide, p-hydroxynonananilide, p-hydroxylauranilide, p-hydroxyoctadecananilide, N-phenyl-phenylsulfonamide and 2-phenoxyethyl-N-phenyl-carbamate. A preferred sensitizer is benzyloxynaphthylene.
Examples of lubricants are stearamide, methylene bis stearamide, polyethylene wax, carnauba wax, paraffin wax, zinc stearate, calcium stearate and mixtures thereof. A preferred lubricant is zinc stearate.
Examples of pigments are ground calcium carbonate, precipitated calcium carbonate, kaolin, calcined kaolin, aluminium hydroxide, talc, titanium dioxide, zinc oxide, amorphous silica, barium sulfate, polystyrene resin, urea-formaldehyde resin, hollow plastic pigment and mixtures thereof. Preferred pigments are ground calcium carbonate, precipitated calcium carbonate, amorphous silica and aluminium hydroxide. Calcium carbonate is the preferred pigment.
Examples of stabilisers are 2,2′-methylene-bis(4-methyl-6-tert-butylphenol), 2,2′-methylene-bis(4-ethyl-6-tert-butylphenol), 4,4′-butylidene-bis(3-methyl-6-tert-butylphenol), 4,4′-thio-bis(2-tert-butyl-5-methylphenol), 1,1,3-tris(2-methyl-4-hydroxy-5-tert-butylphenyl) butane, 1,1,3-tris(2-methyl-4-hydroxy-5-cyclohexylphenyl) butane, bis(3-tert-butyl-4-hydroxy-6-methylphenyl) sulfone, bis(3,5-dibromo-4-hydroxyphenyl) sulfone, 4,4′-sulfinyl bis(2-tert-butyl-5-methylphenol), 2,2′-methylene bis(4,6-di-tert-butylphenyl) phosphate and alkali metal, ammonium and polyvalent metal salts thereof, 4-benzyloxy-4′-(2-methylglycidyloxy) diphenyl sulfone, 4,4′-diglycidyloxydiphenyl sulfone, 1,4-diglycidyloxybenzene, 4[α-(hydroxylmethyl)benzyloxy]-4-hydroxydiphenyl sulfone, metal salts of p-nitrobenzoic acid, metal salts of phthalic acid mono benzyl ester, metal salts of cinnamic acid and mixtures thereof.
Examples of insolubilisers are glyoxal, urea-formaldehyde resins, melamine-formaldehyde resins, polyamide resins, polyamido-epichlorohydrin resins, adipic acid dihydrazide, boric acid, borax, ammonium zirconium carbonate, potassium zirconium carbonate and ammonium zirconium lactate.
Examples of fluorescent whitening agents are stilbene derivatives such as sold, for example, under the tradenames Ciba® Tinopal® SPP-Z or Ciba® Tinopal® ABP-Z.
An example of a wetting agent is Ciba® Irgaclear® D, a sorbitol based clarifying agent.
Examples of IR absorbers are alkylated triphenyl phosphorothionates, for example as sold under the trade name Ciba® Irgalube® 211. Examples of a UV absorber are Ciba® Tinuvin® 900 and Ciba® Tinuvin® 1130, which are UV absorbers of the hydroxyphenyl benzotriazole class and Ciba® Tinuvin® 400 and Ciba® Tinuvin® 1577, which are UV absorbers of the triaryltriazine class.
Examples of tinting colorants are Ciba® Pergasol® Violet BN and Ciba® Irgalite® Violet M.
The coating composition can comprise the colour developer of formula 1 or mixtures thereof from 0.1 to 25% by weight based on the weight of the coating composition, preferably from 0.5 to 15% by weight, more preferably from 1 to 10% by weight.
The coating composition can comprise the colour former or mixtures thereof from 0.1 to 25% by weight based on the weight of the coating composition, preferably from 0.5 to 15% by weight, more preferably from 1 to 10% by weight.
The coating composition can comprise the binder or mixtures thereof from 1 to 60% by weight based on the weight of the coating composition, preferably from 5 to 30% by weight, more preferably from 8 to 25% by weight.
The coating composition can comprise the aqueous medium from 1 to 99% by weight based on the weight of the coating composition, preferably from 25 to 95% by weight, more preferably from 40 to 90% by weight.
The coating composition can comprise the dispersing agent from 0.001 to 10% by weight based on the weight of the coating composition, preferably from 0.01 to 5% by weight, more preferably from 0.05 to 1% by weight.
The coating composition can comprise the surfactant from 0.001 to 10% by weight based on the weight of the coating composition, preferably from 0.01 to 5% by weight, more preferably from 0.01 to 1% by weight.
The coating composition can comprise additional components from 0 to 50% by weight of all additional components based on the weight of the coating composition, preferably from 0 to 25% by weight.
Preferably, the coating composition essentially consists of a colour developer of formula 1 or mixtures thereof, a colour former or mixtures thereof, a binder or mixtures thereof and an aqueous medium.
Generally, the weight ratio of colour developer to colour former is chosen in the range of from 1:5 to 5:1, preferably from 3:1 to 1:3.
Also part of the invention is a process for preparing the coating composition of the present invention. This process comprises mixing the colour developer 1 or mixtures thereof with a colour former or mixtures thereof, and optionally a binder or mixtures thereof, an aqueous medium, a dispersing agent, a surfactant and additional components. For example, the colour developer 1 and the colour former are milled separately in an aqueous medium and/or a binder by means of e.g. a ball mill, an attritor, a sand mill, a bead mill or like device to form dispersions with an average particle diameter preferably in the range of 0.2 to 2.0 μm. The fine particle dispersions thus obtained can be combined and then optionally mixed with binder, aqueous medium, a dispersing agent, a surfactant and additional components. The resulting mixture is thoroughly stirred to obtain the heat sensitive coating composition.
A process for preparing a substrate coated with the coating composition of the present invention is also part of the invention. This process comprises coating a substrate with the coating composition of the present invention.
The substrate can be a sheet or any other three dimensional object, it can be transparent or opaque and it can have an even or uneven surface. The substrate can be paper, cardboard, metal, wood, textiles, glass, ceramics and/or polymers. Examples of paper are wood-free paper made from non-chlorine bleached pulp and base paper containing waste paper. Examples of polymers are polyethylene terephthalate, low density-polyethylene, polypropylene, biaxially orientated polypropylene, polyether sulfone, polyvinyl chloride, polyester and polystyrene. Preferably, the substrate is paper, cardboard or polymer. More preferably, it is paper.
The substrate can be coated with the composition of the present invention by using a standard coating application such as a bar coater application, rotation application, spray application, curtain application, dip application, air application, knife application, blade application or roll application. The composition can also be applied to the substrate by various printing methods such as silk screen printing, gravure printing, offset printing and flexo printing. If the substrate is paper, the composition can also be applied in the size press or at the wet-end of the paper machine.
The coating composition can be dried, for example at ambient or elevated temperature. The elevated temperature is ideally chosen to avoid image formation before exposure to heat. The coating can have a weight of 1 to 10 g/m2, preferably from 2 to 7 g/m2 on a dry weight basis.
Also part of the invention is the substrate coated with the coating composition of the present invention.
Also part of the invention is a process for preparing a marked substrate, which comprises the steps of i) coating a substrate with the coating composition of the present invention, and ii) exposing those parts of the coated substrate, where a marking is intended, to heat in order to generate a marking.
The heat can be applied using a thermal printer or electromagnetic irradiation such as UV, IR, visible or microwave irradiation. UV, visible and IR irradiation can be applied by using a UV, visible or IR laser. Examples of IR lasers are CO2 lasers, Nd:YAG (neodym-yttrium-aluminum garnet) lasers and IR semicoductor lasers.
Preferably, the heat is applied by using a thermal printer or a laser. More preferably, the heat is applied using a thermal printer or an IR laser having a wavelength in the range of 780 to 1'000'000 nm. Even more preferably, the heat is applied using a thermal printer or a CO2 laser.
Typically the exact power of the IR laser and the line speed is determined by the application and chosen to be sufficient to generate the image, for example, when the wavelength of the IR laser is 10'600 nm and the diameter of the laser beam is 0.35 mm, the power is typically 0.1 to 4 W, and the line speed is typically 500 to 2'000 mm/s.
Yet another aspect of the invention is the marked substrate, which is obtained by above process.
Also parts of the present invention are the colour developers of formulae
The coating compositions of the present invention have the advantage that they are storage stable, i.e. only undergo minimal darkening (yellowing) upon storage in the wet state at room temperature or even slightly elevated temperature, and which also provide images of high contrast and of high stability towards heat, oil and light.
The following dispersions A to D are prepared by milling the compositions shown below in an attritor until a particle size of ˜1.0 micron is obtained.
A coating composition is prepared containing the following components:
The coating composition is applied to a base paper using a drawdown coater, dried and calendered to provide coatweights of 5.6 to 6.0 g/m2. The papers are printed with an Atlantek thermal printer to provide black images of good stability. The optical density of the papers and resulting images are measured with a GretagMacbeth SpectroEye spectrometer.
A coating composition based on Dispersion A (1b) is prepared as described in example 2, but with varying amounts of Dispersion C. The coating compositions are applied to a base paper using a drawdown coater, dried and calendered to provide coatweights of 5.6 to 6.0 g/m2. The papers are printed with an Atlantek thermal printer to provide black images of good stability. The optical density of the papers and resulting images are measured with a GretagMacbeth SpectroEye spectrometer.
The same samples are then irradiated with a carbon dioxide laser (0.2 W/1000 mm/s) to provide images whose optical densities are also measured with the GretagMacbeth SpectroEye spectrometer.
A coating composition based on Dispersion A (1b) and Dispersion B (2a to 2c) is prepared as described in example 2, but no Dispersion C is present. The coating compositions are applied to a base paper using a drawdown coater, dried and calendered to provide coatweights of 5.6 to 6.0 g/m2. The papers are printed with an Atlantek thermal printer to provide black images of good stability. The optical density of the papers and resulting images is measured with a GretagMacbeth SpectroEye spectrometer.
The same samples are then irradiated with a carbon dioxide laser (0.2 W/1000 mm/s) to provide images whose optical density is also measured with the GretagMacbeth SpectroEye spectrometer.
A coating composition is prepared containing the following components:
The coating composition is applied to a base paper using a drawdown coater, dried and calendered to provide coatweights of 5.6 to 6.0 g/m2. The papers are then irradiated with a carbon dioxide laser (0.2 W/1000 mm/s) to provide images whose optical density is measured with the GretagMacbeth SpectroEye spectrometer.
Coating compositions based on Dispersion A (1a, 1b, 1d to 1y, 1/1 (weight/weight) mixture of 1a and 1p) and Dispersion B (2a) are prepared as described in example 5. The coating compositions are applied to paper and irradiated as described in example 5. The coating compositions are applied to the paper immediately after preparation, unless indicated otherwise (see footnotes to table 9).
1The composition is stored for one week at room temperature before application to paper and laser irradiation.
2The composition is stored for one week at 40° C. before application to paper and laser irradiation.
3Only one third of the amount specified added to coating.
As can be seen, the coating compositions of the present invention can be stored under various conditions without significant change in activity. Images of high stability against dry and moist heat, oil and light are obtained. A control coating composition containing methyl 2,4-dihydroxybenzoate instead of colour developer of formulae 1 is prepared in analogy to the samples of example 6. The control coating composition discolors immediately and the coated sheets obtained are gray in color.
Coating compositions based on Dispersion A (1p) and Dispersion B (2a to 2h) are prepared as described in example 5. The coating compositions are applied to paper and irradiated with a carbon dioxide laser (1.0 W/1000 mm/s) to provide images whose optical densities are also measured with the GretagMacbeth SpectroEye spectrometer. The coating compositions are applied to the paper immediately after preparation, unless indicated otherwise (see footnotes to table 10).
1The composition is stored for one week at room temperature before application to paper and laser irradiation.
2The composition is stored for one week at 40° C. before application to paper and laser irradiation.
3The composition is stored for four weeks at room temperature before application to paper and laser irradiation.
4The composition is stored for four weeks at 40° C. before application to paper and laser irradiation.
As can be seen, the coating compositions of the present invention comprising colour developer 1 p are extraordinary storage stable.
Coating compositions based on Dispersion A (1b) and Dispersion B (2a) are prepared as described in example 5, In addition, the coating compositions contain 0.55 g of the fluorescent whitening agent Ciba® Tinopal® ABP-Z and either 1.56 g of the UV absorbers Ciba® Tinuvin® 900 or Ciba® Tinuvin® 1130. The coating compositions are applied to paper and irradiated as described in example 5.
Coating compositions based on Dispersion A (1p) and Dispersion B (2a) are prepared as described in example 5, except that the acrylic binder is replaced with either a styrene butadiene latex or polyvinylalcohol. The coating compositions are applied to paper and irradiated as described in example 5. The coating compositions are applied to the paper immediately after preparation, unless indicated otherwise (see footnotes to table 9).
1Ciba ® Latexia ® 304 is a styrene butadiene latex (solids content 50%, particle size 0.15 μm, glass transition temperature Tg 20° C.).
2Ciba ® Latexia ® 318 is a styrene butadiene latex (solids content 50%, particle size 0.12 μm, glass transition temperature Tg 22° C.).
3Ciba ® Latexia ® 319 is a styrene butadiene latex (solids content 50%, particle size 0.12 μm, glass transition temperature Tg 28° C.).
4Mowiol 26-88 is a partially hydrolysed polyvinyl alcohol sold by Kuraray.
| Number | Date | Country | Kind |
|---|---|---|---|
| 07104184.2 | Mar 2007 | EP | regional |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2008/052637 | 3/5/2008 | WO | 00 | 9/2/2011 |