Patent Application
20070128925
The present invention relates to a heat-shrink jointing for an electrical power cable, in particular a medium voltage power cable operating at voltages typically between 12 kV and 42 kV inclusive.
Heat-shrink jointings for electrical power cables use heat-shrinkable polymeric technology to provide one or more heat recoverable sleeves having appropriate electrical characteristics which are shrunk into position around the ends of cables that have been electrically connected together. There are two main types of heat-shrink electrical cable jointing currently in use for medium voltage (MV) electrical power cables.
A first type of jointing, as shown in
This jointing is limited by the fact that it is not practical to manufacture sleeves comprising a thick wall of thermoplastic, heat-shrink material owing both to manufacturing difficulty, and to the problem posed in heating through the entire wall thickness of a thick tube sufficient to recover it, without over-heating the outer surface to the extent that damage occurs. This means that the maximum wall thickness of the insulating material is limited making it necessary to use multiple insulating sleeves 1 to create the required insulation thickness. Typically, two such sleeves are required for power cables operating at voltages up to around 24 kV. However, three or more insulating sleeves are required if a higher voltage rating is required for the joint. The use of multiple sleeves, however, causes its own problems not only because installation is prolonged but also because the increased number of interfaces between the multiple sleeves 1 can lead to electrical problems as a result of air entrapment, contamination of the joint and the like.
The second type of jointing, as shown in
This second type of jointing obviates the problems created by the use of multiple sleeves by replacing the inner thermoplastic insulating sleeve by an elastic layer 7 that can recover without needing heat. This elastic layer 7 is retained in an expanded form by the outer rigid conductive layer 6 that prevents recovery of the jointing 5 until the outer layer 6 is heated during installation. However, there are two main problems with this system. First, the elastomeric inner layer 7 is slower to recover than the heat-shrink materials used in the first system. Second, because the elastic layer 7 is not rigid, the only mechanism which prevents its recovery prior to installation is the rigid, conductive outer layer 6. This means that the outer layer 6 is usually thicker than would otherwise be required for electrical reasons, thus adding materials and therefore cost to the product.
The object of the present invention is to provide a heat-shrink jointing for an electrical power cable that overcomes or substantially mitigates the aforementioned problems of conventional jointing systems.
According to the present invention there is provided a heat-shrinkable jointing for an electrical power cable comprising a sleeve or other hollow article having an electrically insulating inner layer, an electrically conductive outer layer, and between the inner and outer layers a thermoplastic mid-layer which can be softened by application of heat to the said sleeve or article to cause and/or permit dimensional recovery thereof.
Preferably, the insulating inner layer is comprised of an elastomeric material, which may contribute to the recovery of the sleeve or article.
The thermoplastic mid-layer is preferably electrically insulating and/or preferably substantially rigid, by which is meant at least sufficiently rigid to retain the inner layer in a radially expanded state prior to recovery. When used with the preferred elastomeric inner layer, softening of the mid-layer by the application of heat may permit the elastomeric recovery force of the expanded inner layer to shrink the sleeve or article. It will often be preferred that the mid-layer itself be heat-shrinkable to cause or contribute to the dimensional recovery of the sleeve or article. The mid-layer accordingly may be made from heat-shrinkable thermoplastic materials known per se, for example semi-crystalline polyolefins or olefin co-polymers, which are well known and require no further explanation for those familiar with heat-shrink polymer technology. The usual cross-linking agents and other additives, for example colorings, fillers, antioxidants, may optionally be included in the usual quantities as known per se in all three layers.
The conductive outer layer of the sleeve or article is preferably formed of polymeric material, for example the thermoplastics mentioned above, containing appropriate amounts of electrically conductive carbon blacks and/or other suitable electrically conductive fillers, as known per se.
Examples of suitable compositions for the three layers of articles according to the present invention include the following, using known materials of the kinds indicated in proportions by weight selected within the specified ranges to total 100%:
Conductive Outer Layer
60-70% wt EVA (Ethylene/Vinyl Acetate copolymer)
10-20% wt HDPE (High Density Polyethylene)
15-25% wt Conductive carbon black
1-2% wt Aromatic amine antioxidant
Insulating Thermoplastic Mid-Layer
60-70% wt LLDPE (Linear Low Density Polyethylene)
30-40% wt Filler
1-2% wt Stabilizer
Insulating Elastomeric Inner Layer
40-50% wt EPDM (Ethylene Propylene Diene Monomer rubber)
10-20% wt PIB (Polyisobutylene)
25-40% wt Filler
2-5% wt Process aids
3-7% wt Stabilizers
3-5% wt Crosslinking agent
The three-layered sleeve or article of the jointing according to this invention is preferably of tubular, one-piece construction. The term “tubular” is used to indicate an elongate hollow article, which may be a substantially straight sleeve of substantially uniform round or oval cross-section, but is not necessarily limited to any particular longitudinal outline or uniformity of transverse dimensions.
The sleeve or article, especially sleeves of regular cross-sectional shape, may be manufactured efficiently by extrusion. However, layered moldings are not excluded and will often be preferable for articles of more complex shape.
As the thermoplastic mid-layer is substantially rigid prior to its recovery and therefore during storage conditions, the thickness of the conductive outer layer can be made thinner as compared to the previously known product. This is because the conductive outer layer now only has to perform an electrical function and is no longer required also to provide the hold-out mechanism, which is separately provided by the mid-layer. In addition, because the mid-layer need not carry the high loading of electrically conductive filler required in the outer layer, adequate hold-out performance can be achieved with a relatively thin mid-layer. Furthermore, an insulating mid-layer may be used to contribute to the total insulation thickness, thus allowing reduction of the inner insulation layer thickness. With the preferred elastomeric inner insulation, reduction in thickness reduces the elastomeric recovery force which the hold-out mid-layer must bear during storage, enabling further reduction in the hold-out thickness. Some or all of these reductions may accordingly be used to provide a sleeve or article whose total wall thickness is significantly less than that of the previously known jointings, thus usefully reducing bulk and weight, and importantly allowing heat to penetrate more quickly and bring about faster recovery, which is a considerable advantage in commercial use of the jointing according to the present invention.
The present invention will now be described by way of example with reference to the accompanying drawings, in which
a and 1b are respectively transverse sectional views of the pieces of a first, conventional two-piece heat-shrink jointing as described above;
A heat-shrink jointing as shown in
As aforementioned, because the thermoplastic mid-layer 12 is rigid prior to its recovery and therefore during storage conditions, the thickness of the conductive outer layer can be made thinner, for example 0.5 mm as compared to 4 mm in the prior art described above. The mid-layer may provide adequate hold-out performance at a thickness of only 5 mm, allowing a reduction in the elastomeric inner layer thickness, for example from the previously known 11 mm to only 6 mm, thus maintaining a total 11 mm insulation thickness. The resulting wall thickness of all three layers combined may thus be only 11.5 mm, which is significantly less than the total 15 mm thickness of the previously known sleeves having the dual-function conductive-and-hold-out layer.
A further advantage arises from the fact that as the insulation layer of the jointing 10 is made up of the inner layer 11 and mid-layer 12, the mid-layer 12 does not need to be thick-walled as in the prior art described above with reference to
Also, as the thermoplastic mid-layer 12 has a faster installation speed than the elastomeric insulation material, the replacement of some of the elastomeric material by an insulating thermoplastic material in the mid-layer 12 of the present invention improves the recovery speed of the jointing as compared with the prior art.
It will thus be appreciated that the jointing of the invention comprises a hybrid jointing that combines both thermoplastic and elastomeric layers to alleviate the weaknesses of purely elastomeric jointing sleeves and of those elastomeric jointings which only comprise two layers.
In view of the foregoing advantages, it is estimated that there will be potential installation speed improvements of around 30%, perhaps as much as 50%, compared to the elastomeric insulating jointing 5 described with reference to
| Number | Date | Country | Kind |
|---|---|---|---|
| 0327000.6 | Nov 2003 | GB | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/GB04/04811 | 11/12/2004 | WO | 5/19/2006 |