Patent Grant
7241375
The invention relates to a heavy hydrocarbon composition useful as a heavy lubricant base stock, produced by isomerizing Fischer-Tropsch wax, to a heavy lubricant base stock and to a heavy lubricant formed from the base stock.
Heavy lubricants are used for high viscosity applications in which a lubricant based on a lighter oil will not provide sufficient lubrication between moving parts, such as heavy machine oils, gear boxes, deep drawing oils, and manual transmissions. A heavy lubricant is formed by combining a heavy lubricant base stock, which is a heavy oil possessing lubricating oil qualities, with one or more lubricant additives. Most heavy lubricant base stocks are derived from naturally occurring petroleum oil and contain aromatic unsaturates, including polynuclear aromatics, along with sulfur and nitrogen containing compounds. These compounds tend to reduce the viscosity and stability of the oil and the heavy lubricant. Refining the oil to remove these components results in a low yield of the product oil. Heavy paraffins can be refined to low levels of unsaturates and heteroatom compounds, but have unacceptably high pour and cloud points.
There is a need for a relatively pure or premium quality, heavy hydrocarbon composition that is a liquid at least at the temperature of use and that has utility as or in a heavy lubricant base stock.
U.S. Pat. No. 6,090,989 (Trewella et al) discloses a liquid hydrocarbon composition of paraffinic hydrocarbon components in which the extent of branching, as measured by the percentage of methyl hydrogens (BI), and the proximity of branching, as measured by the percentage of recurring methylene carbons which are four or more carbons removed from an end group or branch (CH2>4), are such that:
Also, there is always a need for hydrocarbon compositions which are useful, for example as a heavy white oil, a pharmaceutical oil, a carrier or base for medicinal formulations, in chemical and the pharmaceutical manufacturing and the like. Such applications generally require a pure and chemically inert material, which will for instance not cause allergies in medicinal applications. In other words, there is a need for a hydrocarbon composition which is very low in aromatics and heteroatom containing components.
The present invention provides for a heavy hydrocarbon composition which has both high viscosity and low pour and cloud points.
The invention relates to a relatively pure, premium quality, heavy hydrocarbon composition useful as or in a heavy lubricant base stock, to a heavy lubricant base stock, and to a heavy lubricant formed from the heavy lubricant base stock.
The heavy hydrocarbon composition comprises mostly (e.g. ≧98 wt %) saturated, paraffinic hydrocarbon molecules, is an oily liquid having a kinematic viscosity at 100° C. greater than 8 cSt (centistokes), with an initial (5%) boiling point of at least 850° F. (454° C.) and an end (95%) boiling point of at least 1,000° F. (538° C.). The heavy hydrocarbon composition comprises at least 95 wt % paraffin molecules, of which at least 90 wt % are isoparaffins. Isoparaffins make up for at least 90 wt. % of the paraffin molecules of the heavy hydrocarbon composition according to the invention. The heavy hydrocarbon composition contains hydrocarbon molecules having consecutive numbers of carbon atoms. The extent of branching of the isoparaffinic hydrocarbon molecules, as measured by the percentage of methyl hydrogens, hereinafter referred to as the branching index (BI), and the proximity of the branches (or branching proximity), as measured by the percentage of recurring methylene carbons which are four or more carbon atoms removed from an end group or branch (CH2>4), are such that:
The branching proximity (CH2>4) describes the n-paraffinic character of a paraffin molecule in the hydrocarbon. Generally, in order to obtain good lubricity, compositions are desired that contain paraffin molecules having a relatively high n-paraffinic character, i.e. a small number of branches and/or short branches. However, paraffins having a relatively high n-paraffinic character are expected to give undesired pour and cloud points, because n-paraffins tend to crystallize out from paraffin mixtures at a rather high temperature.
The branching index, as measured by the percentage of methyl hydrogens, is a measure of the number of branches attached to the backbone. If there is an abundance of branches and the branches are primarily methyl groups, the branching index will be large.
For instance, given a certain total number of carbon atoms, a paraffin molecule with a large number of branches and long branches on a relatively short backbone, i.e. a rather small n-paraffinic character, will have a branching proximity (CH2>4) which is relatively small. A paraffin molecule having the same total number of carbon atoms, but with a small number of branches and/or branches which have a larger distance to each other or to an end group, and with a relatively long backbone, i.e. a paraffin molecule with a more n-paraffinic character, will have a branching proximity (CH2>4) which is relatively large.
U.S. Pat. No. 6,090,989 relates to a liquid hydrocarbon composition in which BI−0.5(CH2>4)>15. It has now surprisingly been found that heavy hydrocarbon compositions with a relatively high viscosity, but low pour and cloud points may be obtained if (a) BI−0.5(CH2>4)<15. In other words, according to the invention, the branching proximity (CH2>4) is rather large, as compared to the compositions exemplified in U.S. Pat. No. 6,090,989. This finding was unexpected because the heavy hydrocarbon compositions according to the invention contain paraffin molecules with a more n-paraffinic character, as expressed by a relatively large branching proximity, and still have very low pour and cloud points. In fact, the finding is contrary to the common belief that low pour and cloud points require a small n-paraffinic and a relatively large isoparaffinic character.
The BI is preferably less than 24 and the branching proximity, (CH2>4), is preferably greater than 17.
In another embodiment, the invention relates to a heavy lubricant formed by combining the heavy lubricant base stock of the invention with one or more lubricant additives. While the heavy hydrocarbon composition of the invention is useful as a heavy lubricant base stock, it will have other uses such as, for example, a heavy white oil, a pharmaceutical oil, as a carrier or base for medicinal formulations, in chemical and pharmaceutical manufacturing, and the like. Thus, in further embodiments the invention comprises one or more of the following, of or in which at least a portion uses or is based on the heavy hydrocarbon composition of the invention; a heavy white oil, a pharmaceutical oil, a carrier or base for medicinal formulations, chemical and pharmaceutical manufacturing processes.
In a further embodiment, the invention relates to a base stock comprising the heavy hydrocarbon composition according to the invention. In other words, this embodiment relates to the use of the heavy hydrocarbon composition in or as a base stock. Preferably, the base stock according to the invention consists of the heavy hydrocarbon composition.
The FIGURE is a graph plotting the BI and % CH2>4 values derived from NMR spectra of the heavy hydrocarbon compositions of the invention, the comparative examples of this application, and the data of U.S. Pat. No. 6,090,989 which includes other hydrocarbon compositions, as has been described above. The disclosure of U.S. Pat. No. 6,090,989 is incorporated herein in its entirety by reference. The shaded area on the plot defines the NMR parameter space of the heavy hydrocarbon compositions of the invention. Only the heavy hydrocarbon composition of this invention which are preferably derived from Fischer-Tropsch synthesized waxy hydrocarbons and PAO base stocks fall in this area of parameter space. The molecular composition of the PAO stocks are different from the heavy hydrocarbon compositions of the invention in that (i) they do not contain hydrocarbon molecules having consecutive numbers of carbon atoms, (ii) the percentage of hydrogen atoms from CH3 groups on the molecules is below 15, whereas those for the heavy hydrocarbon composition of the invention is preferably above 20, (iii) the percentage of hydrogen atoms from CH groups for the PAO stocks is preferably above 3, whereas for the heavy hydrocarbon compositions of the invention it is preferably less than 2.
The invention provides for a heavy hydrocarbon composition comprising at least 95 wt % paraffin molecules, of which at least 90 wt % are isoparaffin, containing hydrocarbon molecules having consecutive numbers of carbon atoms, is a liquid at 100° C., at which temperature its kinematic viscosity is above 8 cSt (ASTM D-445), has respective initial and end boiling points of at least 850 and 1000° F. (454 and 538° C.), wherein the branching index (BI), as measured by the percentage of methyl hydrogens, and the branching proximity (CH2>4), as measured by the percentage of recurring methylene carbons which are four or more carbon atoms removed from an end group or branch, of said isoparaffinic hydrocarbon molecules, are such that:
Preferably, the heavy hydrocarbon composition of the invention is produced from Fischer-Tropsch wax and comprises mostly (≧98 wt %) saturated, paraffinic hydrocarbons, of which at least 90 wt % are non-cyclic hydrocarbons and no more than 10 wt % cyclic hydrocarbons. At least 90 and preferably at least 95 wt %, more preferably at least 98 wt %, most preferably at least 99 wt % of the paraffinic hydrocarbon molecules are isoparaffins. While paraffinic cyclic hydrocarbons may be present in an amount of up to 5 wt %, more typically they will not exceed 1 wt %, if present.
The kinematic viscosity of the heavy hydrocarbon compositions of the invention at 100° C., as measured according to ASTM D-445, is greater than 8 cSt. The heavy hydrocarbon composition of the invention contains molecules having consecutive numbers of carbon atoms and preferably at least 95 wt °/C30+ hydrocarbon molecules. The initial boiling point is at least 850° F. (454° C.), preferably 900° F. (482° C.) and the end boiling point is at least 1,000° F. (538° C.). The heavy hydrocarbon composition is typically a liquid at the temperature and pressure conditions of use and typically, but not always, at ambient conditions of 75° F. (24° C.) and one atmosphere (101 kPa) pressure. The initial and end boiling points values referred to herein are nominal and refer to the T5 and T95 cut points (boiling temperatures) obtained by gas chromatograph simulated distillation (GCD), using the method set forth below.
The extent of branching of the isoparaffinic hydrocarbon components, as measured by the percentage of methyl (CH3) hydrogens or branching index (BI), and the proximity of the branches (or branching proximity), as measured by the percentage of recurring methylene carbons which are four or more carbon atoms removed from an end group or branch (CH2>4), are such that:
The heavy hydrocarbon composition of the invention is different from one derived from petroleum oil, slack wax, a PAO oil and the lubricant base stock disclosed in U.S. Pat. No. 6,090,989, which was obtained by isomerizing Fischer-Tropsch wax.
Sulfur, nitrogen and metals in the form of hydrocarbon compounds containing them are present in amounts of less than 50 wppm. Heavy hydrocarbon compositions of the invention that have been made from Fischer-Tropsch wax usually contain less than 1 wppm sulfur, nitrogen and metals. These were not detectable by X-ray or Antek Nitrogen tests.
While the heavy hydrocarbon composition of the invention is a mixture of various molecular weight paraffinic hydrocarbons, the residual normal paraffin content remaining after hydrodewaxing is less than 5 wt % and more typically less than 1 wt %, with at least 95% of the oil molecules containing at least one branch, at least half of which are methyl branches. At least half, and more preferably at least 75% of the remaining branches are ethyl, with less than 25% and preferably less than 15% of the total number of branches having three or more carbon atoms. The total number of branch carbon atoms is typically less than 25%, preferably less than 20% and more preferably no more than 15% (e.g., 10–15%) of the total number of carbon atoms comprising the hydrocarbon molecules.
PAO oils are an oligomerization product of even carbon numbered linear alpha olefins, typically 1-decene. The PAO oil molecules therefore comprise a mixture of even carbon numbered hydrocarbon molecules, differing from each other in the number of carbon atoms by multiples of the number of carbon atoms in the linear alpha olefin starting monomer. Even if a mixture of linear alpha olefin monomers having even numbers of carbon atoms (e.g., decene and dodecene) were oligomerized to form a heavy lubricant base stock oil, the number of carbon atoms in the resulting hydrocarbon molecules would still have even numbers of carbon atoms. This is different from the mixture of consecutive numbered hydrocarbon molecules of the heavy hydrocarbon composition of the invention, which comprise hydrocarbon molecules having both even and odd numbers of carbon atoms and which differ from each other by consecutive numbers of carbon atoms (e.g., 1, 2, 3, 4, 5, 6, 7 and more carbon atoms).
That hydrocarbon molecules of the heavy hydrocarbon composition of the invention differ from each other by consecutive numbers of carbon atoms is a consequence of the Fischer-Tropsch hydrocarbon synthesis reaction from which the wax feed, which was isomerized to form the heavy hydrocarbon composition of the invention may be produced. While a preferred heavy hydrocarbon composition is prepared from synthetic sources rather than sources on a mineral oil basis, and may thus be termed a synthetic heavy hydrocarbon composition, the heavy hydrocarbon composition of the invention is not limited to be based on synthetic sources. In a preferred embodiment, however, the heavy hydrocarbon composition is based on a synthetic source, and is more preferably based on a Fischer-Tropsch product.
In the Fischer-Tropsch hydrocarbon synthesis reaction the source of carbon atoms is CO and the hydrocarbon molecules are built up one carbon atom at a time. In contrast to an oil based on PAO, then hydrocarbon molecules of the heavy hydrocarbon composition of the invention have a more linear structure, comprising a relatively long backbone with short and few branches. The classic textbook description of a PAO is a star-shaped molecule, and in particular tridecane, which is illustrated as three decane molecules attached at a central point. While an ideal star-shaped molecule is theoretical, nevertheless PAO molecules have fewer and longer branches than the hydrocarbon molecules that make up the base stock of the invention.
Thus, the molecular make up of a heavy hydrocarbon composition of the invention preferably comprises at least 95 wt % isoparaffins (with no more than 5 wt % saturated cyclics) having a relatively linear molecular structure, with less than half the branches having two or more carbon atoms and less than 25% of the total number of carbon atoms present in the branches. In contrast to the present invention, in the molecular make-up of a PAO oil, more than half the branches contain two or more carbon atoms and more than 25°/ of the total number of carbon atoms are in the branches.
As those skilled in the art know, a lubricant base stock, sometimes also referred to as a lubricating or lube oil base stock, including a heavy lubricant base stock, is an oil boiling in the lubricating oil range, having a lubricating quality and is useful for preparing various lubricants such as lubricating oils and greases. In the present invention the heavy hydrocarbon composition boils in the heavy lubricant oil range. Fully formulated heavy lubricants or heavy lubricating oils are prepared by adding to the heavy lubricant base stock an effective amount of at least one additive or, more typically, an additive package containing more than one additive. Illustrative, but non-limiting examples of such additives include one or more of a detergent, a dispersant, an antioxidant, an antiwear additive, an extreme pressure additive, a pour point depressant, a VI improver, a friction modifier, a demulsifier, an antioxidant, an antifoamant, a corrosion inhibitor, and a seal swell control additive.
A heavy hydrocarbon composition of the invention preferably comprises a dewaxed oil, and has low temperature properties able to meet target specifications or requirements and will be a clear and bright, oily liquid at the temperature and pressure conditions under which it is used. Typically, but not always, it will be an oily liquid at room temperature and pressure conditions of 75° F. (24° C.) and one atmosphere (101 kPa) pressure and is an oily liquid at this pressure and a temperature of 100° C. In some cases the cloud point may be higher than 75° F. (24° C.). A heavy hydrocarbon composition of the invention, having an end boiling point above 1,250° F. (677° C.), with respective cloud and pour points of 1° C. and −31° C., has been made according to the invention. Low temperature property requirements of both a heavy lubricant base stock and a finished heavy lubricant will vary and can depend on both the application for which they are is intended and the geographical location in which they will be used. A heavy lubricant composition is prepared by forming a mixture of a heavy lubricant base stock of the invention and an effective amount of at least one additive or, more typically, an additive package containing more than one additive, as mentioned above. The heavy lubricant base stock of the invention used in forming the mixture will typically have been mildly hydrofinished and/or dehazed after hydrodewaxing to improve its color, appearance and stability.
As is known, haze is cloudiness or a lack of clarity, and is an appearance factor. Dehazing is typically achieved by either catalytic or absorptive methods to remove those constituents that result in haziness. Hydrofinishing is a very mild, relatively cold hydrogenating process, which employs a catalyst, hydrogen and mild reaction conditions to remove trace amounts of heteroatom compounds, aromatics and olefins, to improve oxidation stability and color. Hydrofinishing reaction conditions include a temperature of from 302 to 662° F. (150 to 350° C.) and preferably from 302 to 482° F. (150 to 250° C.), a total pressure of from 400 to 3000 psig (2859 to 20786 kPa), a liquid hourly space velocity ranging from 0.1 to 5 LHSV (hr−1) and preferably 0.5 to 3 hr−1. The hydrogen treat gas rate will range from 2550 to 10000 scf/B (44.5 to 1780 m3/m3). The catalyst will comprise a support component and one or catalytic metal components of metal from Groups VIB (Mo, W, Cr) and/or iron group (Ni, Co) and noble metals (Pt, Pd) of Group VIII. The Groups VIB and VIII referred to herein, refers to Groups VIB and VIII as found in the Sargent-Welch Periodic Table of the Elements copyrighted in 1968 by the Sargent-Welch Scientific Company. The metal or metals may be present from as little as 0.1 wt % for noble metals, to as high as 30 wt % of the catalyst composition for non-noble metals. Preferred support materials are low in acid and include, for example, amorphous or crystalline metal oxides such as alumina, silica, silica alumina and ultra large pore crystalline materials known as mesoporous crystalline materials, of which MCM-41 is a preferred support component. The preparation and use of MCM-41 is disclosed, for example, in U.S. Pat. Nos. 5,098,684, 5,227,353 and 5,573,657.
The waxy feed or Fischer-Tropsch wax comprises the waxy hydrocarbon fraction produced in a Fischer-Tropsch hydrocarbon synthesis reactor, which is liquid at the reaction conditions. It is referred to as wax, because it is solid at 75° F. (24° C.) and one atmosphere (101 kPa) pressure. It must contain sufficient waxy material boiling above 1000° F. (538° C.) to produce the heavy hydrocarbon composition of the invention. The waxy feed is typically dewaxed in one or more catalytic dewaxing steps in which the feed is contacted with hydrogen and a dewaxing catalyst under dewaxing conditions. The iso- to normal paraffin ratio is measured by performing GC-FID for a composition containing molecules with up to 20 carbon atoms and a combination of GC-FID with 13C-NMR for a composition containing molecules with ≧20 carbon atoms. Aromatics are determined by X-Ray Fluorescence (XRF), as described in ASTM Standard D-2622. Sulfur is measured by XRF as per ASTM standard D-2622 and nitrogen by syringe/inlet oxidative combustion with chemiluminescence detection per ASTM standard D-4629.
The catalyst useful in the hydrodewaxing step comprises a solid acid component, a hydrogenation component and a binder. Illustrative, but nonlimiting examples of suitable catalyst components useful for hydrodewaxing include, for example, ZSM-23, ZSM-35, ZSM-48, ZSM-57, ZSM-22 also known as theta one or TON, and the silica aluminophosphates known as SAPO's (e.g., SAPO-11, 31 and 41), SSZ-32, zeolite beta, mordenite and rare earth ion exchanged ferrierite. Also useful are alumina and amorphous silica aluminas.
As in the case of many other zeolite catalysts, it may be desired to incorporate the solid acid component with a matrix material also known as a binder, which is resistant to the temperatures and other conditions employed in the dewaxing process herein. Such matrix materials include active and inactive materials and synthetic or naturally occurring zeolites as well as inorganic materials such as clays, silica and/or metal oxides e.g., alumina. The latter may be either naturally occurring or in the form of gelatinous precipitates, sols or gels including mixtures of silica and metal oxides. Use of a material in conjunction with the solid acid component, i.e., combined therewith, which is active, may enhance the conversion and/or selectivity of the catalyst herein. Inactive materials suitably serve as diluents to control the amount of conversion in a given process so that products can be obtained economically and orderly without employing other means for controlling the rate or reaction. Frequently, crystalline silicate materials have been incorporated into naturally occurring clays, e.g., bentonite and kaolin. These materials, i.e., clays, oxides, etc., function, in part, as binders for the catalyst. It is desirable to provide a catalyst having good crush strength since in a petroleum refinery the catalyst is often subject to rough handling which tends to break the catalyst down into powder-like materials which cause problems in processing.
Naturally occurring clays which can be composited with the solid acid component include the montmorillonite and kaolin families which include the sub-bentonites, and the kaolins commonly known as Dixie, McNamee, Georgia and Florida clays, or others in which the main mineral constituent is halloysite, kaolinite, dickite, nacrite or anauxite. Such clays can be used in the raw state as originally mined or initially subjected to calcination, acid treatment or chemical modification.
In addition to the foregoing materials, the solid acid component can be composited with a porous matrix material such as silica-alumina, silica-magnesia, silica-zirconia, silica-thoria, silica-beryllia, silica-titania, as well as ternary compositions such as silica-alumina-thoria, silica-alumina-zirconia, silica-alumina-magnesia and silica-magnesia-zirconia. The matrix can be in the form of a cogel. Mixtures of these components can also be used. The relative proportions of finely divided solid acid component and inorganic oxide gel matrix vary widely with the crystalline silicate content ranging from about 1 to about 90 percent by weight, and more usually in the range of about 2 to about 80 percent by weight, of the composite. ZSM-48 is preferably used.
The hydrogenation component will comprise at least one Group VIII metal component and preferably at least one noble Group VIII metal component, as in Pt and Pd. Noble metal concentrations will range from about 0.1–5 wt % of the metal, and more typically from about 0.2–1 wt %, based on the total catalyst weight, including the ZSM-48 zeolite component and any binder used in the catalyst composite. The Group VIII referred to herein refers to Group VIII as found in the Sargent-Welch Periodic Table of the Elements copyrighted in 1968 by the Sargent-Welch Scientific Company.
The preparation of ZSM-48 (ZSM-48 zeolites include EU-2, EU-11 and ZBM-30 which are structurally equivalent) is well known and is disclosed, for example, in U.S. Pat. Nos. 4,397,827; 4,585,747 and 5,075,269, and EP 0 142 317, the disclosures of which are incorporated herein by reference. Other hydrodewaxing catalysts useful in the practice of the invention, include any of the well known catalysts that dewax mostly by isomerization and not by cracking or hydrocracking. Zeolites comprising ten and twelve membered ring structures are useful as dewaxing catalysts, particularly when combined with a catalytic metal hydrogenating component. Hydrodewaxing reaction conditions employed to produce a hydrocarbon or heavy lubricant composition of the invention include a respective temperature, hydrogen partial pressure and space velocity broadly ranging from 450–750° F. (232–399° C.), 10–2,000 psig (69–13790 kPa), and 0.1–5.0 LHSV. These conditions will more generally range from 500–700° F. (260–371° C.), 100–1000 psig (690–6895 kPa) and 0.5–3.0 LHSV, a pressure of from 200–700 psig (1379–4827 kPa) more typical.
In this example, the wax feed comprised the entire 430° F.+ (221° C.) waxy hydrocarbon fraction produced in a slurry Fischer-Tropsch hydrocarbon synthesis reactor, that contained a titania supported, rhenium-promoted, non-shifting cobalt hydrocarbon synthesis catalyst. The wax comprised at least 90 wt % normal paraffinic hydrocarbons and 26.2 wt % of a 1000° F.+ (538° C.) fraction. It was hydrodewaxed with hydrogen in the presence of a ZSM-48 hydrodewaxing catalyst with a Pt noble metal component to form an isomerate. The isomerate was fractionated to remove the 700° F.− (371° C.−) hydrocarbons and the remaining 700° F.+ (371° C.+) fraction then fractionated to remove and recover a 950° F.+ (510° C.+) heavy lubricant isomerate fraction. This heavy isomerate fraction was then further hydrodewaxed with hydrogen, over the same ZSM-48 hydrodewaxing catalyst in a separate reactor, to form heavy hydrocarbon compositions or heavy lubricant base stocks of the invention. The hydrodewaxing conditions in the first and second reactors included respective temperatures of 586° F. (308° C.) and 616° F. (324° C.) and a low hydrogen pressure of 250 psi (1724 kPa). These compositions, the properties of which are shown in the Table, had kinematic viscosities of 13 and 15 cSt at 100° C.
The ZSM-48 hydrodewaxing catalyst in both reactors comprised 0.6 wt % Pt as the hydrogenating component, on a composite of the hydrogen form of a ZSM-48 zeolite and an alumina binder. The hydrogen form of the ZSM-48 zeolite was prepared according to the procedure in U.S. Pat. No. 5,075,269, the disclosure of which is incorporated herein by reference. The Pt component was added by impregnation, followed by calcining and reduction, using known procedures.
Gas chromatograph distillations (GCD) were conducted using a high temperature GCD method modification of ASTM D-5307. The column consisted of a single capillary column with a thin liquid phase, less than 0.2 microns. External standards were used, consisting of a boiling point calibrant ranging from 5 to 100 carbons. A temperature programmed injector was used and, prior to injection, the samples were gently warmed using hot water. Boiling ranges were determined using this method and the T5 and T95 GCD results. Cloud point values were measured using ASTM D-5773 for Phase Two Tec Instruments, under the lubricant procedure method. Pour point was measured according to ASTM D-5950 for ISL Auto Pour Point measurement. Cloud and pour points in the Table below are given in ° C. Viscosity and viscosity index were measured according to the ASTM protocols D-445 and D-2270, respectively.
In this example, the wax feed was Paraflint C-80, a commercally available, hydrotreated Fischer-Tropsch wax produced by Sasol in a fixed bed Fischer-Tropsch reactor from a shifting iron catalyst. The untreated raw wax contains relatively high levels of aromatic and aliphatic unsaturates, and heteroatom compounds, which is hydrotreated to produce the Paraflint C-80 wax. This solid wax is a distillate fraction having a viscosity ranging from 6–10 cSt at 100° C. and a nominal T5 boiling point of about 850° F. (454° C.). It was hydrodewaxed with hydrogen in a single reactor, in the presence of a Pt/ZSM-48 catalyst similar to that used above, but which had been sulfided. The hydro-dewaxing reaction pressure was 1000 psi (6895 kPa). The hydrodewaxing product was fractionated by distillation to give a heavy hydrocarbon composition of the invention with a viscosity of 11 cSt at 100° C., and its properties are also shown in the Table.
This run was similar to that of Example 1, except that the nominally 700–950° F. (371–510° C.) isomerate was then further hydrodewaxed with hydrogen, over the same ZSM-48 hydrodewaxing catalyst in a separate reactor, to form a composition not of the invention, which had a viscosity of 4 cSt at 100° C. The hydrodewaxing conditions in the first and second reactors included respective temperatures of 586° F. (308° C.) and 597° F. (314° C.) and a low hydrogen pressure of 250 psi (1724 kPa). This comparative composition is shown in the Table.
This was similar to Example 2 regarding the feed, catalyst and a single hydrodewaxing reactor. Two compositions, having viscosities of 6 and 8 cSt at 100° C., were produced by fractionating the hydrodewaxed product by distillation. Neither of these two compositions are compositions of the invention and are included in the Table below for comparative purposes.
1H NMR*
13C NMR**
The microstructure of the compositions in the Table was analyzed by carbon-13 NMR spectroscopy. Samples were prepared at w/w concentration of 20–25% in chloroform d-doped with 7.5 mg/ml Cr(acac)3. Chemical shift referencing was performed with TMS set to 0.0 ppm. Spectra were acquired on a Varian Unity Plus 500, at a carbon Larmor frequency of 125.7 MHz, with 8000 coaveraged transients per spectrum. All spectra were acquired with a 90° excitation pulse on carbon, inverse gated WALTZ-16 decoupling on protons (during the 0.8 second acquisition time), and a recycle delay of 6 seconds. Sample preparation and data acquisition were performed at 50° C. The data acquisition parameters (chromium doping, relaxation decay, inverse gated decoupling) were chosen to insure accurate and quantitative integrals. With regard to the NMR techniques, the data acquisition and calculations, reference is also made to U.S. Pat. No. 6,090,989.
Proton NMR analysis of the samples was performed in a 5 mm switchable probe, with approximately 80 mg samples dissolved in 1 gm chloroform-d. Sample preparation and data acquisition were performed at 50° C. on a Varian Unity Plus 500. Free induction decays of 64 coaveraged transients were acquired, employing a 90° excitation pulse, a relaxation decay of 8.4 seconds, and an acquisition time of 3.2 seconds. No relaxation agent was used in the proton NMR.
These data show that the heavy hydrocarbon compositions of the invention (those having viscosities of 11, 13 and 15 cSt) have molecules in which the branching index (BI), and the proximity of branching or branching proximity (CH2>4), are such that:
The FIGURE is a graph plotting the BI and % CH2>4 values derived from NMR spectra of the heavy hydrocarbon compositions of the invention, the comparative examples of this application, and the data of U.S. Pat. No. 6,090,989 which includes other hydrocarbon compositions. The disclosure of U.S. Pat. No. 6,090,989 is incorporated herein in its entirety by reference. The shaded area on the plot defines the NMR parameter space of the heavy hydrocarbon compositions of the invention. Only the heavy hydrocarbon compositions of this invention, which are preferably derived from Fischer-Tropsch synthesized waxy hydrocarbons, and PAO base stocks fall in this area of parameter space. The molecular composition of the PAO stocks are different from the heavy hydrocarbon compositions of the invention in that (i) they do not contain hydrocarbon molecules having consecutive numbers of carbon atoms, (ii) the percentage of hydrogen atoms from CH3 groups on the molecules is below 15, whereas those for the composition of the invention are typically above 20, (ii) the percentage of hydrogens from CH groups for the PAO stocks is above 3, whereas for the compositions of the invention it is typically less than 2.
This application is a Continuation-In-Part of U.S. Ser. No. 10/266,344 filed Oct. 8, 2002 now U.S. Pat. No. 6,846,778.
| Number | Name | Date | Kind |
|---|---|---|---|
| 2250410 | van Peski | Jul 1941 | A |
| 3711399 | Estes et al. | Jan 1973 | A |
| 4181597 | Yan et al. | Jan 1980 | A |
| 4335019 | Bowes et al. | Jun 1982 | A |
| 4377469 | Shihabi | Mar 1983 | A |
| 4388177 | Bowes et al. | Jun 1983 | A |
| 4402866 | Shihabi | Sep 1983 | A |
| 4431516 | Baird et al. | Feb 1984 | A |
| 4431517 | Nevitt et al. | Feb 1984 | A |
| 4436614 | Olbrich et al. | Mar 1984 | A |
| 4510045 | Dessau | Apr 1985 | A |
| 4568449 | Angmorter et al. | Feb 1986 | A |
| 4594146 | Chester et al. | Jun 1986 | A |
| 4684756 | Derr, Jr. | Aug 1987 | A |
| 4784747 | Shihabi | Nov 1988 | A |
| 4808296 | Chen et al. | Feb 1989 | A |
| 4908120 | Bowes et al. | Mar 1990 | A |
| 4919788 | Chen et al. | Apr 1990 | A |
| 4921593 | Smith | May 1990 | A |
| 4954325 | Rubin et al. | Sep 1990 | A |
| 4975177 | Garwood et al. | Dec 1990 | A |
| 5015361 | Anthes et al. | May 1991 | A |
| 5017535 | Schoonhoven et al. | May 1991 | A |
| 5037528 | Garwood et al. | Aug 1991 | A |
| 5059299 | Cody et al. | Oct 1991 | A |
| 5075269 | Degnan et al. | Dec 1991 | A |
| 5110445 | Chen et al. | May 1992 | A |
| 5110573 | Johnson | May 1992 | A |
| 5146022 | Buchanan et al. | Sep 1992 | A |
| 5164169 | Rubin | Nov 1992 | A |
| 5164170 | Rubn | Nov 1992 | A |
| 5208403 | Buchanan et al. | May 1993 | A |
| 5232579 | Absil et al. | Aug 1993 | A |
| 5275719 | Baker, Jr. et al. | Jan 1994 | A |
| 5276229 | Buchanan et al. | Jan 1994 | A |
| 5284985 | Girgis et al. | Feb 1994 | A |
| 5288395 | Marler et al. | Feb 1994 | A |
| 5358628 | Apelian et al. | Oct 1994 | A |
| 5362378 | Borghard et al. | Nov 1994 | A |
| 5399337 | Schmitt | Mar 1995 | A |
| 5405596 | Moini et al. | Apr 1995 | A |
| 5419830 | Chou et al. | May 1995 | A |
| 5456820 | Forbus, Jr. et al. | Oct 1995 | A |
| 5475178 | Del Rossi et al. | Dec 1995 | A |
| 5488191 | Chu et al. | Jan 1996 | A |
| 5498821 | Ryan et al. | Mar 1996 | A |
| 5516736 | Chang et al. | May 1996 | A |
| 5603822 | Forbus, Jr. et al. | Feb 1997 | A |
| 5603824 | Kyan et al. | Feb 1997 | A |
| 5611192 | Weder | Mar 1997 | A |
| 5612270 | Beck et al. | Mar 1997 | A |
| 5637784 | Chu et al. | Jun 1997 | A |
| 5643440 | Borghard et al. | Jul 1997 | A |
| 5689031 | Berlowitz et al. | Nov 1997 | A |
| 5730858 | Olivier et al. | Mar 1998 | A |
| 5779882 | Chester et al. | Jul 1998 | A |
| 5780382 | Chang et al. | Jul 1998 | A |
| 5780703 | Chang et al. | Jul 1998 | A |
| 5827491 | Emerson et al. | Oct 1998 | A |
| 5833840 | Absil et al. | Nov 1998 | A |
| 5849968 | Beck et al. | Dec 1998 | A |
| 5854170 | Chang et al. | Dec 1998 | A |
| 5885438 | Apelian et al. | Mar 1999 | A |
| 5911874 | Cody et al. | Jun 1999 | A |
| 5935417 | Cody et al. | Aug 1999 | A |
| 5961951 | Kennedy et al. | Oct 1999 | A |
| 5976201 | Barry et al. | Nov 1999 | A |
| 5976351 | Apelian et al. | Nov 1999 | A |
| 5993644 | Xiao et al. | Nov 1999 | A |
| 6008164 | Aldrich et al. | Dec 1999 | A |
| 6013171 | Cook et al. | Jan 2000 | A |
| 6051129 | Harris et al. | Apr 2000 | A |
| 6063973 | Sen et al. | May 2000 | A |
| 6080301 | Berlowitz et al. | Jun 2000 | A |
| 6080904 | Chang et al. | Jun 2000 | A |
| 6090989 | Trewella et al. | Jul 2000 | A |
| 6096189 | Cody et al. | Aug 2000 | A |
| 6150576 | Jiang et al. | Nov 2000 | A |
| 6179994 | Clark et al. | Jan 2001 | B1 |
| 6180068 | Boyd et al. | Jan 2001 | B1 |
| 6180575 | Nipe | Jan 2001 | B1 |
| 6190532 | Degnan et al. | Feb 2001 | B1 |
| 6210563 | Tsao et al. | Apr 2001 | B1 |
| 6217747 | Chang et al. | Apr 2001 | B1 |
| 6231749 | Degnan et al. | May 2001 | B1 |
| 6261441 | Gentry et al. | Jul 2001 | B1 |
| 6264826 | Xiao et al. | Jul 2001 | B1 |
| 6277355 | Kennedy et al. | Aug 2001 | B1 |
| 6287454 | Forbus, Jr. et al. | Sep 2001 | B1 |
| 6294077 | Dougherty et al. | Sep 2001 | B1 |
| 6306362 | Han et al. | Oct 2001 | B1 |
| 6310265 | Chester et al. | Oct 2001 | B1 |
| 6319487 | Liu et al. | Nov 2001 | B1 |
| 6322692 | Cody et al. | Nov 2001 | B1 |
| 6337010 | Hofer | Jan 2002 | B1 |
| 6339051 | Carey et al. | Jan 2002 | B1 |
| 6346498 | Chang et al. | Feb 2002 | B1 |
| 6362123 | Tsao et al. | Mar 2002 | B1 |
| 6375830 | Clark et al. | Apr 2002 | B1 |
| 6416654 | Chou et al. | Jul 2002 | B1 |
| 6420063 | Ozin et al. | Jul 2002 | B1 |
| 6504075 | Beck et al. | Jan 2003 | B2 |
| 6506703 | Kao et al. | Jan 2003 | B1 |
| 6627779 | O'Rear | Sep 2003 | B2 |
| 6833065 | O'Rear | Dec 2004 | B2 |
| 6846778 | Johnson et al. | Jan 2005 | B2 |
| 7018525 | Miller et al. | Mar 2006 | B2 |
| 20010001449 | Kiliany et al. | May 2001 | A1 |
| 20010004972 | Miller et al. | Jun 2001 | A1 |
| 20010006154 | Krug et al. | Jul 2001 | A1 |
| 20020003102 | O'Rear et al. | Jan 2002 | A1 |
| Number | Date | Country |
|---|---|---|
| 0147873 | Mar 1988 | EP |
| 0635557 | Jan 1995 | EP |
| 0707057 | Apr 1996 | EP |
| 0909304 | Apr 1999 | EP |
| 0668342 | Aug 1999 | EP |
| 772478 | Apr 1957 | GB |
| 1582789 | Jan 1981 | GB |
| 2109402 | Jun 1983 | GB |
| 2311789 | Oct 1997 | GB |
| WO 9613563 | May 1996 | WO |
| WO 9626993 | Sep 1996 | WO |
| WO 9634930 | Nov 1996 | WO |
| WO 9718278 | May 1997 | WO |
| WO 9818883 | May 1998 | WO |
| WO 9935087 | Jul 1999 | WO |
| WO 0157166 | Aug 2001 | WO |
| WO 02070627 | Sep 2002 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20050150815 A1 | Jul 2005 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10266344 | Oct 2002 | US |
| Child | 10652389 | US |