The present invention relates to a heavy-metal removal method and a heavy-metal removal device in a final neutralization step of a nickel oxide ore plant. The present application claims a priority based on Japanese Patent Application No. 2012-270722 filled on Dec. 11, 2012 in Japan, and the application is incorporated into the present application by reference.
Many kinds of heavy metals are contained in a nickel oxide ore, the nickel oxide ore is dissolved by using sulfuric acid under high temperature and pressure conditions, and then a chemical treatment is performed to remove impurities, subsequently, a required metal such as nickel is recovered.
In order to discharge a solution after nickel recovery, the heavy metals that have left in the solution are required to be removed in some way. As a method for removing a heavy metal from industrial wastewater, there are a coagulation sedimentation method, an ion exchange method, an adsorption method using an absorbent such as activated carbon, an electrical adsorption method, and a magnetic adsorption method, however, a coagulation sedimentation method using a neutralizing agent is used in many factories as a general method.
Specifically, a method in which pH is increased by the addition of a neutralizing agent, a heavy metal is solidified as a hydroxide, then the solid and the liquid are separated by an operation of a filtration treatment and the like, the liquid is discharged outside the factory, and the solid is treated in a dumping ground is used. Further, as the neutralizing agent, an inexpensive calcium-based neutralizing agent such as lime stone and slaked lime is frequently used.
In general, it has been known that a heavy metal forms a hydroxide by the increase of the pH, and can be removed from a solution, however, a heavy metal such as iron and manganese forms a more stable hydroxide by oxidation. As an oxidation method of a heavy metal, aeration is an extremely useful method in view of equipment cost and operation cost.
Herein, in a high pressure acid leaching (HPAL) method to obtain a nickel-cobalt mixed sulfide, as shown in
In the pretreatment step (1), a nickel oxide ore is ground and classified to obtain a slurry.
In a leaching step (2), sulfuric acid is added into the slurry obtained in the pretreatment step (1), the resultant mixture is stirred at a temperature of 220 to 280° C., and high temperature pressure acid leaching is performed to obtain a leach slurry.
In a solid-liquid separation step (3), a leach slurry obtained in the leaching step (2) is subjected to solid-liquid separation to obtain a leachate containing nickel and cobalt (hereinafter, referred to as “crude nickel sulfate aqueous solution”), and leach residues.
In a neutralization step (4), a crude nickel sulfate aqueous solution obtained in the solid-liquid separation step (3) is neutralized.
In a dezincification step (5), hydrogen sulfide gas is added into the crude nickel sulfate aqueous solution neutralized in the neutralization step (4), and zinc is precipitated and removed as a zinc sulfide.
In a sulfurization step (6), hydrogen sulfide gas is added into the dezincification final solution obtained in the dezincification step (5), and a nickel-cobalt complex sulfide and a nickel barren liquor are obtained. In a detoxification step (7), a leach residue generated in the solid-liquid separation step (3) and a nickel barren liquor generated in the sulfurization step (6) are detoxified.
By the above-described high temperature pressure leaching method (HPAL), for example, a leach slurry after the leaching of nickel from a nickel laterite ore, and an effluent (barren liquor) obtained after the recovery of Ni and Co is discarded to a dam, however, the slurry and the effluent have low pH as they are, therefore, are detoxified in the above-described detoxification step (7). Specifically, in the detoxification step (7), as shown in
At this time, in the neutralization treatment equipment, in order to oxidize a heavy metal ion contained in the process liquid (slurry), gas is discharged into the treatment tank so as to oxidize the heavy metal ion. Further, the slurry to be charged has around pH 2, and the slurry is subjected to neutralization by using CaCO3 in the initial stage in which the pH is low, and Ca(OH)2 in the latter half stage, and the pH is finally increased to around 9. In addition, in order to precipitate Mg, Mn, and other trace metals (Ni, Co, Fe, Al, and Cr), gas discharge (aeration) is performed to increase the valency number. Consequently, the metal content is reduced to from around 0.0 n to 0. ng/L to around 0.001 g/L (except for Mg).
In the detoxification treatment (final neutralization treatment), the required amount of the neutralizing agent varies depending on the flow rate and acidity of the process liquid to be subjected to the treatment, or on the concentration of the contained heavy metals, however, also in any process, it is desired to reduce the amount of a neutralizing agent to be used from the viewpoint of cost reduction.
The present invention has been made in consideration of these circumstances, and an object of the present invention is to provide a heavy-metal removal method capable of reducing the amount of a neutralizing agent to be used, and a heavy-metal removal device used for the method.
Another object of the present invention and a specific advantage obtained by the present invention become more apparent from the explanation of an embodiment described below.
In the present invention, an annular aeration tube having a large number of air outlets is arranged to a bottom part of a vertical-type cylindrical reaction vessel, aeration is performed by using a simple aeration device for blowing gas for oxidation from a large number of air outlets of the annular aeration tube, while stirring an aqueous solution containing a heavy metal ion in the reaction vessel, and a neutralization treatment in which an aqueous solution containing a heavy metal ion is neutralized with a neutralizing agent is performed to solidify and remove the heavy metal as a hydroxide.
That is, the present invention is a heavy-metal removal method, and characterized in that in a neutralization tank provided with a vertical-type cylindrical reaction vessel, stirring blades arranged in the reaction vessel, and an annular aeration tube having a large number of air outlets and being arranged to the bottom part of the reaction vessel, aeration is performed by introducing gas for oxidation from a large number of air outlets of the aeration tube while stirring an aqueous solution containing at least one kind of ion of a divalent ferrous ion and a divalent manganese ion as a heavy metal element by rotation of the stirring blades, and into the aqueous solution, a neutralizing agent is added, the resultant mixture is subjected to a neutralization treatment to remove the heavy metal as a hydroxide.
Further, the present invention is a heavy-metal removal device, and characterized in that the heavy-metal removal device includes a neutralization tank provided with a vertical-type cylindrical reaction vessel, stirring blades arranged in the reaction vessel, and an annular aeration tube having a large number of air outlets and being arranged to a bottom part of the reaction vessel, and in the neutralization tank, aeration is performed by introducing gas for oxidation from a large number of air outlets of the aeration tube while stirring an aqueous solution containing at least one kind of ion of a divalent ferrous ion and a divalent manganese ion as a heavy metal element by rotation of the stirring blades, then into the aqueous solution, a neutralizing agent is added, the resultant mixture is subjected to a neutralization treatment to remove the heavy metal as a hydroxide.
In the present invention, in a final neutralization step in a hydrometallurgy plant for a nickel oxide ore, a neutralization treatment is performed by the neutralization tank, and the heavy metal is solidified and removed as a hydroxide.
Further, in the present invention, the gas for oxidation can be air.
In addition, in the present invention, the annular aeration tube can have a diameter size of 60 to 85% of that of the reaction vessel.
Further, in the present invention, the outlet can be circular and have a diameter size of 18 to 22 mm.
In addition, in the present invention, the outlet can be arranged at each position in an angle range of 45 degree to both sides from directly under the annular aeration tube and at equal intervals.
According to the present invention, an annular aeration tube having a large number of air outlets is arranged to bottom part of a vertical-type cylindrical reaction vessel, aeration is performed by using an aeration device for blowing gas for oxidation from the annular aeration tube to perform a neutralization treatment for an aqueous solution, while stirring an aqueous solution containing a heavy metal ion in the reaction vessel, as a result, the required amount of the neutralizing agent to be used for the neutralization of the heavy metals contained in the aqueous solution is reduced, and the heavy metals can efficiently be removed.
Hereinafter, a specific embodiment to which the present invention is applied will be described in detail with reference to the drawings.
A heavy-metal removal method according to the present embodiment is, for example, performed by a heavy-metal removal device with the constitution as illustrated in
The heavy-metal removal device 100 is an neutralization tank provided with a vertical-type cylindrical reaction vessel 110, stirring blades 120 arranged in the reaction vessel 110, and an annular aeration tube 130 having a large number of air outlets 131 and being arranged to bottom part of the reaction vessel 110. Further, in the vertical-type cylindrical reaction vessel 110, three plates of baffle plates 151 are arranged.
In a heavy-metal removal method according to the present embodiment, using the heavy-metal removal device 100, in a vertical-type cylindrical reaction vessel 110, aeration is performed by introducing gas for oxidation from a large number of air outlets 131 of the aeration tube 130 while stirring an aqueous solution containing at least one kind of ion of a divalent ferrous ion and a divalent manganese ion as a heavy metal element by rotation of the stirring blades 120, and into the aqueous solution, a neutralizing agent is added, the resultant mixture is subjected to a neutralization treatment to solidify and remove the heavy metal as a hydroxide.
For example, in a hydrometallurgy plant for a nickel oxide ore, as described above, in a detoxification step, a heavy metal is solidified and removed as a hydroxide by a final neutralization treatment, and a leach residue generated in a solid-liquid separation step and a nickel barren liquor generated in a sulfurization step are detoxified and discarded. At this time, in the present embodiment, for example, as shown in the process chart of
Specifically, in the final neutralization step, a barren liquor that is a process liquid discharged in a sulfurization step is charged into a vertical-type cylindrical reaction vessel 110 of a heavy-metal removal device 100, and a neutralization treatment is performed.
In a barren liquor discharged in a hydrometallurgy plant for a nickel oxide ore, mainly a pure metal such as iron and manganese is contained. These heavy metals can be separated from the process liquid as precipitates (neutralized precipitates) of a hydroxide by the performing of a neutralization treatment in which pH of the barren liquor is adjusted.
Herein, in the final neutralization step, as the pH required for maintaining the concentration of a heavy metal in a solution to 1 mg/L or less, as shown in
That is, as to the heavy metal ion in a solution, a trivalent heavy metal ion can be precipitated with a lower pH as compared with the pH used for a divalent heavy metal ion. The process liquid to be charged into the final neutralization step is originally a solution on acidic side, therefore, when the pH is adjusted to low pH, the amount of a neutralizing agent to be used can be reduced.
In a final neutralization step in a hydrometallurgy plant for a nickel oxide ore, conventionally, a reaction tank with stirring blades is used. The reaction tank generally has a vertical-type cylindrical shape, and in which it is common not to generate stirring unevenness. At this time, in the present embodiment, further, gas for oxidation is blown into the reaction tank and a barren liquor is aerated.
Specifically, in the present embodiment, in a final neutralization step of a hydrometallurgy plant for a nickel oxide ore, a heavy-metal removal device 100 in which an annular aeration tube 130 having a large number of air outlets 131 and being arranged to a bottom part of the vertical-type cylindrical reaction vessel 110 is used. In addition, aeration by the blowing of gas for oxidation from outlets 131 of the aeration tube 130 is performed while stirring a process liquid containing a heavy metal ion in the reaction vessel 110, and the process liquid containing a heavy metal ion is subjected to a neutralization treatment. Heavy metals in the process liquid are solidified as hydroxides, and the solid and the liquid are subjected to gravity separation. The solid obtained by the gravity separation is discarded into a dumping ground, and on the other hand, the liquid is returned to the solid-liquid separation step and used as washing water, or discarded.
That is, the heavy-metal removal device 100 used in the heavy-metal removal method according to the above-described present embodiment includes a neutralization tank provided with a vertical-type cylindrical reaction vessel 110, stirring blades 120 arranged in the reaction vessel 110, and an annular aeration tube 130 having a large number of air outlets 131 and being arranged to bottom part of the reaction vessel 110. Further, in a vertical-type cylindrical reaction vessel 110, that is, in a neutralization tank, aeration is performed by introducing gas for oxidation from air outlets 131 of the aeration tube 130 while stirring a process liquid in a final neutralization step, that is, an aqueous solution containing at least one kind of ion of a divalent ferrous ion and a divalent manganese ion as a heavy metal element by rotation of the stirring blades 120, and the aqueous solution containing a heavy metal ion is subjected to a neutralization treatment in which neutralization is performed by a neutralizing agent.
As described above, aeration is performed via an annular aeration tube 130 having a large number of air outlets 131 and being arranged to bottom part in the reaction vessel 110, and bubbles to flow into the reaction vessel 110 are allowed to be split into small bubbles, and the total area of bubbles can be increased. In addition, an aqueous solution containing a heavy metal ion is uniformly stirred in the reaction vessel 110, as a result, the abundance of bubbles can be brought into contact with the aqueous solution, and a high aeration effect can be obtained. That is, the gas for oxidation fed into the reaction vessel 110 becomes in the state of being dispersed on the bottom of the neutralization tank from immediately after the feeding, therefore, the oxidation can efficiently be performed over the entire aqueous solution containing a heavy metal ion.
That is, a heavy metal ion in an aqueous solution can efficiently be oxidized from divalent to trivalent. Further, as described above, since the heavy metal ion can be oxidized to a trivalent heavy metal ion, a precipitate of a hydroxide can be formed with a low pH, therefore, the required amount of a neutralizing agent to be used for a neutralization treatment can effectively be reduced.
Herein, the gas for oxidation is not particularly limited as long as being gas that maintains the bubbles in a liquid, that is, being gas that is not easily dissolved into a liquid, however, air is preferably used in view of cost.
Herein, in order to stabilize the flow in a reaction vessel 110 of a heavy-metal removal device 100, the air is required to be gone up along the vessel wall. In this respect, the aeration tube 130 in the heavy-metal removal device 100 is preferably formed in an annular shape having a diameter size of 60 to 85% of that of the reaction vessel 110.
The diameter of the aeration tube 130 for the diameter of the reaction vessel 110 is changed, and the aeration effect is observed. As a result, when an aeration tube 130 is formed in an annular shape having a diameter size of 60 to 85% of that of the reaction vessel 110, the degree of dispersion of the gas is increased, and a high aeration effect could be obtained.
Further, in a heavy-metal removal device 100, the shape of a large number of air outlets 131 formed to an aeration tube 130 is circular and has a diameter size of 18 to 22 mm.
When the air outlets 131 are formed to be circular, strength reduction of the aeration tube 130 can be the least as compared with the case where the air outlets are formed in another shape having the same opening area. Further, when the diameter is 18 mm to 22 mm, an effect of oxidizing a heavy metal ion can be enhanced, therefore, this is preferred.
It is noted that it is considered that there is a bubble size optimal for the density and flow characteristics of the process liquid to be subjected to a neutralization treatment, and when the diameter of an air outlet is smaller than 18 mm, the rising speed of bubbles in a liquid is extremely slow, and it takes a long time. On the other hand, when the diameter of an air outlet is larger than 22 mm, the rising speed is extremely fast, and there may be a case where air is not sufficiently brought into contact with the aqueous solution.
In addition, as to the air outlets 131, one outlet is arranged directly under the annular aeration tube 130, and each of other outlets is arranged at each of both positions at an angle of 45° to both sides from the one outlet arranged directly under the annular aeration tube, the total three outlets are made to be a set. The set is preferably arranged to the annular aeration tube 130 at equal intervals.
Hereinafter, Examples of the present invention will be described, however, the present invention is not limited to the following Examples.
In the present Examples, in a final neutralization step in a hydrometallurgy plant for a nickel oxide ore, a barren liquor that is a process liquid discharged from a sulfurization step was subjected to a detoxification treatment in which a heavy metal ion in the solution is removed by using the above-described heavy-metal removal device 100.
In the heavy-metal removal device 100, an aeration tube 130 was arranged to the bottom part at a position where the distance from the center of a cylindrical reaction vessel 110 is 72% of the diameter of the reaction vessel 110, and 189 outlets of air outlets 131 having a diameter of 20 mm was arranged to the bottom surface part of the aeration tube 130. At this time, as to a case where aeration was performed using the aeration tube 130 and a case where aeration was performed from a conventional simple blowing tube (three blowing tubes), the results of the hold-up amount of air were compared with each other. The measurement results are shown in Table 2.
As shown in
Next, in a final neutralization step in a hydrometallurgy plant for a nickel oxide ore, a barren liquor that is a process liquid discharged from a sulfurization step was subjected to a neutralization treatment in which a neutralizing agent is added, by using the same heavy-metal removal device 100 as that used in Example 1, the used amount of the slaked lime required for the neutralization treatment was compared with that in a conventional final neutralization step. The measurement results are shown in Table 3.
As shown in
100 heavy-metal removal device; 110 reaction vessel; 120 stirring blade; 130 aeration tube; 131 air outlet; 151 baffle plate
| Number | Date | Country | Kind |
|---|---|---|---|
| 2012-270722 | Dec 2012 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2013/081472 | 11/22/2013 | WO | 00 |