Patent Application
20220227810
Bacterial antibiotic resistance has become a critical threat to global health and the worldwide economy. According to the Center for Disease Control and Prevention (CDC), over 2 million cases of illness, and 23,000 deaths, are caused each year by bacterial drug-resistance in the United States [1]. Moreover, bacteria can develop resistance to a new antibiotic within a few years. Therefore, rather than continually developing new antibiotics that may be ineffective within a short time, there remains a need to develop novel antibacterial agents that target a broad range of bacteria without inducing bacterial drug-resistance.
In one aspect, the disclosure provides a polypeptide comprising an amphiphilic backbone and a cationic heparin-binding motif peptide.
In another aspect, the disclosure provides a method of antimicrobial treatment, comprising:
providing a sample comprising a plurality of microorganisms;
adding to the sample a polypeptide comprising an amphiphilic backbone and a cationic heparin-binding motif peptide;
thereby killing or inhibiting the growth of at least a portion of the plurality of microorganisms in the sample.
In another aspect, the disclosure provides a method of preventing or suppressing microbial growth on a surface, comprising:
applying to the surface a polypeptide comprising an amphiphilic backbone and a cationic heparin-binding motif peptide;
thereby preventing or suppressing microbial growth on the surface.
In another aspect, the disclosure provides a method of preparing self-assembled nanorods comprising the steps of:
dissolving a plurality of lyophilized polypeptides comprising an amphiphilic backbone and a cationic heparin-binding motif peptide in a solvent to form a mixture;
mixing the mixture; and
storing the mixture to allow for supramolecular self-assembly,
thereby preparing self-assembled nanorods.
There are four major pathways to the development of bacterial drug resistance: i) alteration in the target site of antimicrobial agents to reduce binding affinity; ii) reducing drug accessibility via increased efflux or decreased influx within the cell; iii) drug inactivation; and iv) tolerance that results in the survival of bacteria during inhibited bacteria growth [2].
Antibiotic-resistance continues to be one of the biggest threats to global health. Antimicrobial peptides (AMPs) have been explored as therapeutic agents to treat antibiotic resistant microbes. Naturally-occurring AMPs can be found in many living organisms, where they serve as defense components in the innate immune system against a broad range of pathogens, including bacteria, viruses, and fungi [3-5]. Unlike conventional antibiotics that mostly rely on receptor-specific pathways to display antibacterial activity, AMPs bind to negatively charged bacteria cell membranes by non-specific physical interactions with bacterial membranes, leading to cell death via membrane disruption. Moreover, AMPs possesses highly selective toxicity in bacteria compared to mammalian cells, which is ascribed to the considerable differences in lipid composition between prokaryotic and eukaryotic cells. In bacterial membranes, the negatively-charged hydroxylated phospholipids, such as phosphatidylglycerol (PG), cardiolipin (CL) and phosphatidylserine (PS), are abundantly present, while mammalian cell membranes are exclusively enriched by more electrically-neutral zwitterionic phospholipids and cholesterol that reduce peptide binding as well as membrane-thinning effects of AMPs [6]. Although some AMPs isolated from natural sources have shown early success as alternatives to antibiotics, their therapeutic applications are limited by their high costs due to long sequences, limited supply, low stability to enzymatic degradation in vivo, and off-target cytotoxicity [7, 8].
To overcome these challenges, sequence and structural features of naturally-occurring AMPs can be leveraged to develop strategies for the design of synthetic AMPs with wider therapeutic windows [9, 10]. Characteristics of natural AMPs (such as cationicity, amphipathicity, and the ability to fold into secondary structures) can be retained in synthetic AMPs, which are key factors for their membrane permeation and mechanisms of antibacterial action. Most AMPs carry a positive net charge from +2 to +9. Once the cationic domain of a peptide initiates attachment with the anionic membrane surface, the hydrophobic domain drives peptide partitioning into the non-polar regions of lipid bilayer to disrupt the membrane [6, 11]. Conjugation of cationic peptides with fatty acids [12] or hydrophobic amino acid residues [13] has been shown to meditate their antimicrobial activity. In addition, AMPs with β-sheet conformation can penetrate bacterial cell membranes via transmembrane channels and display potent antibacterial properties [7]. For instance, a series of short peptides that adopt β-sheet secondary structures on bacterial cell membranes have been shown to exhibit effective antibacterial properties against a broad range of clinically pathogenic bacteria strains, and possessed in vivo efficacy to treat fungal keratitis [9, 14]. β-sheet forming short peptides that can form highly packed nanorods showed enhanced antibacterial activity, which provides significant evidence for the future of self-assembled peptides and their clinical use [15].
A type of self-assembling peptide amphiphile (PA) has been designed to be effective against antibiotic-resistant bacteria. Self-assembly of these PA systems into high aspect ratio and highly organized nanostructures is driven by non-covalent intermolecular interactions [18]. Cylindrical supramolecular structures of PA can be constructed by oligopeptide building blocks containing hydrocarbon chains, β-sheet forming groups via hydrogen bonding, and charged amino acids. These self-assembled nanostructures can be engineered for specific biological functions with a short peptide sequence displayed on the surface. In recent decades, PA systems have been extensively studied for applications including regenerative medicines as well as drug delivery vehicles.
Nonetheless, few studies have investigated the potential use of self-assembling PA as therapeutics to treat drug-resistant bacteria. Here, amphiphilic Cardin-motif antimicrobial peptides (ACA-PA) were designed to self-assemble into cylindrical supramolecular structures. For example, this peptide self-assembly is driven by hydrophobic interactions of the hydrophobic palmitic (16 carbon) tail groups, and directed by the β-sheet forming V4K4 (SEQ ID NO: 1) peptide backbones into cylindrical shapes. The serial lysine groups act as a spacer and ensure water solubility of the peptide amphiphiles [19, 20]. The ACA-PA was functionalized with the heparin-binding (AKKARA)2 (SEQ ID NO: 2) Cardin-Weintraub motif [21] to initiate attachment with the anionic bacterial cell membranes (
Herein, self-assembling peptide amphiphiles (PAs) functionalized with heparin-binding Cardin-motifs (SEQ ID NO: 2, (AKKARA)2, where A, K, and R represent alanine, lysine and arginine, respectively) have been designed to combat the drug-resistance of both Gram-positive and Gram-negative bacteria. These cationic amphiphilic Cardin-motif antimicrobial (ACA) peptides could self-assemble in water into nanorods 10 nm in diameter. Unlike typical small molecule antibiotics, the self-assembled ACA nanorods were shown to damage the bacterial cell membrane and cause bacterial cell lysis. Such non-specific interactions can reduce the development of drug-resistance, as the entire bacterial cell membrane is the target site of the self-assembled ACA nanorods. In contrast, free (AKKARA)2 peptides (SEQ ID NO: 2, without the self-assembly property) showed little antibacterial activity. Therefore, the unique self-assembled ACA nanorods with heparin-binding Cardin-motif sequences are promising antibacterial agents to treat antibiotic-resistant bacteria.
In some embodiments, PAs functionalized with the Cardin-motif can self-assemble into nanorods. In some embodiments, PAs functionalized with the Cardin-motif can self-assemble into nanofibers. In some embodiments, PAs functionalized with the Cardin-motif can self-assemble into bundled and elongated nanofibers.
In some embodiments of the self-assembling peptide amphiphiles disclosed herein, the PA is a polypeptide comprising an amphiphilic backbone and a cationic heparin-binding motif peptide. In some embodiments, the amphiphilic backbone comprises a hydrophobic portion and a beta-sheet forming segment.
In some embodiments of the self-assembling peptide amphiphiles disclosed herein, the polypeptide is represented by:
R1-y1-y2
wherein
R1-y1 is an amphiphilic backbone; and
y2 is a cationic heparin-binding motif peptide.
In some embodiments, R1 is an alkyl group or an alkenyl group. In some embodiments, R1 is a C10-C22 alkyl group or a C10-C22 alkenyl group. In some embodiments, R1 is a C12-C22 alkyl group or a C12-C22 alkenyl group. In some embodiments, R1 is selected from the group consisting of C12, C14, C16, C16:1, C18, C18:1, C18:2, C18:3, C20, C20:1, C20:4, C20:5, C22, C22:1, and C22:6. In some embodiments, R1 is a C16 alkyl group.
In some embodiments, y1 is a hydrophilic polypeptide. In some embodiments, y1 has the following sequence (SEQ ID NO: 3):
—(Xn)—(Zn)-y3-
wherein, independently for each occurrence:
X is I, L, or V;
Z is K or R;
n is 2, 3, 4, 5, 6, 7, 8, 9, or 10; and
y3 is absent, A, or G.
In some embodiments of y1 disclosed herein, each X is I, L, or V. In some embodiments, X is I. In some embodiments, X is L. In some embodiments, X is V.
In some embodiments, each Z is K or R. In some embodiments, Z is K. In some embodiments, Z is R.
In some embodiments, each n is 2, 3, 4, 5, 6, 7, 8, 9, or 10. In some embodiments, n is 2. In some embodiments, n is 3. In some embodiments, n is 4. In some embodiments, n is 5. In some embodiments, n is 6. In some embodiments, n is 7. In some embodiments, n is 8. In some embodiments, n is 9. In some embodiments, n is 10.
In some embodiments, y3 is absent, A, or G. In some embodiments, y3 is absent. In some embodiments, y3 is A. In some embodiments, y3 is G.
In some embodiments, y1 has the following sequence V4K4 (SEQ ID NO: 1) or V4K4G (SEQ ID NO: 4).
In some embodiments, y2 is a cationic heparin-binding motif peptide. In some embodiments, y2 has the following sequence (SEQ ID NO: 5):
-(WZZWZW)m
wherein, independently for each occurrence:
W is A or G;
Z is K or R; and
m is 2, 3, 4, 5, 6, 7, 8, 9, or 10.
In some embodiments of y2 disclosed herein, each W is A or G. In some embodiments, W is A. In some embodiments, W is G.
In some embodiments, each Z is K or R. In some embodiments, Z is K. In some embodiments, Z is R.
In some embodiments, m is 2, 3, 4, 5, 6, 7, 8, 9, or 10. In some embodiments, m is 2. In some embodiments, m is 3. In some embodiments, m is 4. In some embodiments, m is 5. In some embodiments, m is 6. In some embodiments, m is 7. In some embodiments, m is 8. In some embodiments, m is 9. In some embodiments, m is 10.
In some embodiments, y2 is -(AKKARA)m (SEQ ID NO: 6).
In some embodiments, each of these PAs contains a hydrophobic portion (e.g., a C16 hydrocarbon group), a beta-sheet forming segment (e.g., SEQ ID NO: 1, V4K4), and a cationic heparin-binding functional group (e.g., SEQ ID NO: 2, (AKKARA)2).
In some embodiments of the PAs disclosed herein, the PA has the following sequence C16-V4K4G(AKKARA)2 (SEQ ID NO: 7).
In some embodiments, the self-assembled nanorods are formed by non-covalent forces including hydrogen bonds and hydrophobic interactions, and display the cationic Cardin-motif on the surface.
In some embodiments of the polypeptides disclosed herein, the polypeptide is incorporated into an article. In some embodiments, for example, the article is selected from filters (e.g., hand-held water filters), membranes, packing materials (e.g., for foods, agriculture, paints, etc.), flow cells, filter gaskets, gloves, masks, garments, wound dressings, implants, catheters, and other medical devices. In some embodiments, the article is sterile.
In some embodiments, PAs exhibited promising antibacterial properties.
In some embodiments, the addition of self-assembling peptide amphiphilic backbones to cationic heparin-binding peptides significantly improves the antibacterial properties of the peptides, while the free heparin-binding peptides only have little antibacterial effects.
In some embodiments, self-assembly of the PAs is important to the antibacterial effects. For example, once the nanorods are self-assembled, the bactericidal effects towards Gram-negative bacteria are significantly more pronounced.
In some embodiments, the self-assembled ACA nanorods can be easily prepared by dissolving the lyophilized peptides in water. Since the self-assembly is driven by non-covalent intermolecular interactions, complex chemical synthesis is not required for the preparation of the nanorods.
In some embodiments, these self-assembled ACA nanorods can kill a broad range of bacteria including the antibiotic-resistant strains. In contrast, many current antibiotics are only effective to either Gram-negative or Gram-positive bacteria. For example, ciprofloxacin and ofloxacin specifically target the DNA enzyme in Gram-negative bacteria, and moxifloxacin and gatifloxacin are more effective against Gram-positive bacteria.
In some embodiments, the cationic self-assembled nanorods can attach on the negatively charged bacterial membranes by electrostatic interactions, so the target side of the nanorods is the whole bacterial membrane, which makes it more challenging for the bacteria to develop resistance.
In some embodiments, ACA nanorods may cause the formation of transmembrane pores on the surface of cell membranes, resulting in cytoplasmic leakage followed by cell lysis.
Since peptide-based self-assembled materials are biodegradable, these ACA nanorods can be degraded after displaying their antibacterial effects by proteolysis. Otherwise, undesirable retention of particles (such as synthetic polymeric and liposome materials) can cause systemic toxicity in liver, spleen and kidney.
In another aspect, the disclosure provides a method of antimicrobial treatment, comprising:
providing a sample comprising a plurality of microorganisms;
adding to the sample a plurality of polypeptides comprising an amphiphilic backbone and a cationic heparin-binding motif peptide, thereby killing or inhibiting the growth of at least a portion of the plurality of microorganisms in the sample.
In some embodiments, at least a portion of the plurality of microorganisms is killed. In some embodiments, the growth of at least a portion of the plurality of microorganisms is inhibited.
In another aspect, the disclosure provides a method of preventing or suppressing microbial growth on a surface, comprising:
applying to the surface a plurality of polypeptides comprising an amphiphilic backbone and a cationic heparin-binding motif peptide, thereby preventing or suppressing microbial growth on the surface.
In some embodiments, microbial growth on the surface is prevented. In some embodiments, microbial growth on the surface is suppressed.
In some embodiments of the methods disclosed herein, the surface coating is on an article. In some embodiments, for example, the article is selected from filters (e.g., hand-held water filters), membranes, packing materials (e.g., for foods, agriculture, paints, etc.), flow cells, filter gaskets, gloves, masks, garments, wound dressings, implants, catheters, and other medical devices. In some embodiments, the article is sterile.
In some embodiments of the methods disclosed herein, the sample further comprises water.
In some embodiments of the methods disclosed herein, the plurality of polypeptides comprising an amphiphilic backbone and a cationic heparin-binding motif peptide is any one of the self-assembling peptide amphiphiles disclosed herein. In some embodiments, the amphiphilic Cardin-motif antimicrobial (ACA) peptides self-assemble.
In some embodiments, the microorganism is a bacterium, a virus, a fungus, or a parasite. In some embodiments, the microorganism is antibiotic-resistant.
In some embodiments, the microorganism is a Gram-negative bacterium. In some embodiments, the microorganism is a Gram-positive bacterium. In some embodiments, for example, the microorganism is at least one bacterium selected from anthrax, Bacilli, Bordetella, Borrelia, botulism, Brucella, Burkholderia, Campylobacter, Chlamydia, cholera, Clostridium, Gonococcus, Corynebacterium, diptheria, Enterobacter, Enterococcus, Erwinia, Escherichia, Francisella, Haemophilus, Heliobacter, Klebsiella, Legionella, Leptospira, leptospirosis, Listeria, Lyme's disease, meningococcus, Mycobacterium, Mycoplasma, Neisseria, Pasteurella, Pelobacter, plague, Pneumonococcus, Proteus, Pseudomonas, Rickettsia, Salmonella, Serratia, Shigella, Staphylococcus, Streptococcus, tetanus, Treponema, Vibrio, Yersinia and Xanthomonas. In some embodiments, the microorganism is Staphylococcus aureus (S. aureus) or methicillin-resistant S. aureus (MRSA). In some embodiments, the microorganism is Escherichia coli (E. coli) or multidrug-resistant E. coli (MDR E. coli).
In some embodiments, for example, the microorganism is at least one virus selected from Adenoviridae, Papillomaviridae, Polyomaviridae, Herpesviridae, Poxviridae, Hepadnaviridae, Parvoviridae, Astroviridae, Caliciviridae, Picornaviridae, Coronoviridae, Flaviviridae, Retroviridae, Togaviridae, Arenaviridae, Bunyaviridae, Filoviridae, Orthomyxoviridae, Paramyxoviridae, Rhabdoviridae, and Reoviridae. In certain embodiments, the virus may be arboviral encephalitis virus, adenovirus, herpes simplex type I, herpes simplex type 2, Varicella-zoster virus, Epstein-burr virus, cytomegalovirus, herpesvirus type 8, papillomavirus, BK virus, coronavirus, echovirus, JC virus, smallpox, Hepatitis B, bocavirus, parvovirus B19, astrovirus, Norwalk virus, coxsackievirus, Hepatitis A, poliovirus, rhinovirus, severe acute respiratory syndrome virus, Hepatitis C, yellow fever, dengue virus, West Nile virus, rubella, Hepatitis E, human immunodeficiency virus (HIV), human T-cell lymphotropic virus (HTLV), influenza, guanarito virus, Junin virus, Lassa virus, Machupo virus, Sabia virus, Crimean-Congo hemorrhagic fever virus, ebola virus, Marburg virus, measles virus, molluscum virus, mumps virus, parainfluenza, respiratory syncytial virus, human metapneumovirus, Hendra virus, Nipah virus, rabies, Hepatitis D, rotavirus, orbivirus, coltivirus, vaccinia virus, and Banna virus.
In some embodiments, for example, the microorganism is at least one fungus selected from Aspergillus (fumigatus, niger, etc.), Basidiobolus (ranarum, etc.), Blastomyces dermatitidis, Candida (albicans, krusei, glabrata, tropicalis, etc.), Coccidioides immitis, Cryptococcus (neoformans, etc.), eumycetoma, Epidermophyton (floccosum, etc.), Histoplasma capsulatum, Hortaea werneckii, Lacazia loboi, Microsproum (audouinii, nanum etc.), Mucorales (mucor, absidia, rhizophus), Paracoccidioides brasiliensis, Rhinosporidium seeberi, Sporothrix schenkii, and Trichophyton (schoeleinii, mentagrophytes, rubrum, verrucosum, etc.).
In some embodiments, for example, the microorganism is at least one parasite selected from Acanthamoeba, Babesia microti, Balantidium coli, Entamoeba hystolytica, Giardia lamblia, Cryptosporidium muris, Trypanosomatida gambiense, Trypanosomatida rhodesiense, Trypanosoma brucei, Trypanosoma cruzi, Leishmania mexicana, Leishmania braziliensis, Leishmania tropica, Leishmania donovani, Toxoplasma gondii, Plasmodium vivax, Plasmodium ovale, Plasmodium malariae, Plasmodium falciparum, Pneumocystis carinii, Trichomonas vaginalis, Histomonas meleagridis, Secementea, Trichuris trichiura, Ascaris lumbricoides, Enterobius vermicularis, Ancylostoma duodenale, Naegleria fowleri, Necator americanus, Nippostrongylus brasiliensis, Strongyloides stercoralis, Wuchereria bancrofti, Dracunculus medinensis, blood flukes, liver flukes, intestinal flukes, lung flukes, Schistosoma mansoni, Schistosoma haematobium, Schistosoma japonicum, Fasciola hepatica, Fasciola gigantica, Heterophyes heterophyes, and Paragonimus westermani.
In another aspect, the disclosure provides a method of preparing self-assembled nanorods comprising the steps of:
dissolving a plurality of lyophilized polypeptides comprising an amphiphilic backbone and a cationic heparin-binding motif peptide in a solvent to form a mixture;
mixing the mixture; and
storing the mixture for a period of time to allow for supramolecular self-assembly, thereby preparing self-assembled nanorods.
In some embodiments, the solvent is selected from the group consisting of water, acetone, dimethylsulfoxide, ethanol, methanol, isopropanol, and mixtures thereof. In some embodiments, the solvent is water.
In some embodiments, the mixture is mixed by vortexing, shaking, or agitating. In some embodiments, the mixture is mixed by vortexing.
In some embodiments, the mixture is stored at a temperature below room temperature. In some embodiments, the mixture is stored at a temperature between about −5° C. and about 25° C. In some embodiments, the mixture is stored at a temperature between about 0° C. and about 20° C. In some embodiments, the mixture is stored at a temperature selected from the group consisting of about 20° C., about 19° C., about 18° C., about 17° C., about 16° C., about 15° C., about 14° C., about 13° C., about 12° C., about 11° C., about 10° C., about 9° C., about 8 ° C., about 7° C., about 6° C., about 5° C., about 4° C., about 3° C., about 2° C., about 1° C., and about 0° C. In some embodiments, the mixture is stored at a temperature of about 4° C.
In some embodiments, the mixture is stored for a period of time of at least 1 h. In some embodiments, the mixture is stored for a period of time of at least 5 h. In some embodiments, the mixture is stored for a period of time of at least 10 h. In some embodiments, the mixture is stored for a period of time of at least 15 h. In some embodiments, the mixture is stored for a period of time of at least 20 h. In some embodiments, the mixture is stored for a period of time of at least 24 h. In some embodiments, the mixture is stored for a period of time of at least 30 h. In some embodiments, the mixture is stored for a period of time of at least 36 h. In some embodiments, the mixture is stored for a period of time of at least 40 h. In some embodiments, the mixture is stored for a period of time of at least 45 h. In some embodiments, the mixture is stored for a period of time of at least 48 h. In some embodiments, the mixture is stored for a period of time selected from the group consisting of about 1 h, about 2 h, about 3 h, about 4 h, about 5 h, about 6 h, about 7 h, about 8 h, about 9 h, about 10 h, about 11 h, about 12 h, about 13 h, about 14 h, about 15 h, about 16 h, about 17 h, about 18 h, about 19 h, about 20 h, about 21 h, about 22 h, about 23 h, about 24 h, about 25 h, about 26 h, about 27 h, about 28 h, about 29 h, about 30 h, about 31 h, about 32 h, about 33 h, about 34 h, about 35 h, about 36 h, about 37 h, about 38 h, about 39 h, about 40 h, about 41 h, about 42 h, about 43 h, about 44 h, about 45 h, about 46 h, about 47 h, and about 48 h.
In some embodiments, the ACA nanorods in solution can be aimed to serve as antibacterial agents to treat eye infections. In some embodiments, the nanoparticles can be applied directly to the eye as eye drops in solution. In some embodiments, the nanoparticles in solution can be used as a rinsing solution for contact lenses.
The building block peptides of the ACA nanorods can be efficiently produced by a cGMP process at a large scale with low cost. Bioprocessing that produces peptides and proteins from recombinant DNA transfected mammalian cells and bacteria has been widely used by many industrial pharmaceutical companies. Since the peptide amphiphiles of ACA nanorods are short peptides, a gene that encodes this peptide sequence can be transfected into cells or bacteria, and the living organisms are incubated and able to generate the desired peptides exogenously.
Solid-phase peptide synthesis may also be used to produce large quantities of the peptides. Solid-phase peptide synthesis (SPPS), pioneered by Robert Bruce Merrifield, is the standard method for synthesizing peptides and proteins in the lab. SPPS allows for the synthesis of natural peptides which are difficult to express in bacteria, the incorporation of unnatural amino acids, peptide/protein backbone modification, and the synthesis of D-proteins, which consist of D-amino acids.
Small porous beads are treated with functional units ('linkers') on which peptide chains can be built. The peptide will remain covalently attached to the bead until cleaved from it by a reagent, such as anhydrous hydrogen fluoride or trifluoroacetic acid. The peptide is thus ‘immobilized’ on the solid-phase and can be retained during a filtration process while liquid-phase reagents and by-products of synthesis are flushed away.
The general principle of SPPS is one of repeated cycles of deprotection-wash-coupling-wash. The free N-terminal amine of a solid-phase attached peptide is coupled to a single N-protected amino acid unit. This unit is then deprotected, revealing a new N-terminal amine to which a further amino acid may be attached. The superiority of this technique partially lies in the ability to perform wash cycles after each reaction, removing excess reagent with all of the growing peptide of interest remaining covalently attached to the insoluble resin.
Liquid-phase peptide synthesis is a classical approach to peptide synthesis. It has been replaced in most labs by solid-phase synthesis; however, it retains usefulness in large-scale production of peptides for industrial purposes.
Unless otherwise defined herein, scientific and technical terms used in this application shall have the meanings that are commonly understood by those of ordinary skill in the art. Generally, nomenclature used in connection with, and techniques of, chemistry described herein, are those well-known and commonly used in the art.
The term “acyl” is art-recognized and refers to a group represented by the general formula hydrocarbylC(O)—, preferably alkylC(O)—.
The term “acyloxy” is art-recognized and refers to a group represented by the general formula hydrocarbylC(O)O—, preferably alkylC(O)O—.
The term “alkoxy” refers to an alkyl group, having an oxygen attached thereto. Representative alkoxy groups include methoxy, trifluoromethoxy, ethoxy, propoxy, tert-butoxy and the like.
The term “alkenyl”, as used herein, refers to an aliphatic group containing at least one double bond and is intended to include both “unsubstituted alkenyls” and “substituted alkenyls”, the latter of which refers to alkenyl moieties having substituents replacing a hydrogen on one or more carbons of the alkenyl group. Typically, a straight chained or branched alkenyl group has from 1 to about 20 carbon atoms, preferably from 1 to about 10 unless otherwise defined. Such substituents may occur on one or more carbons that are included or not included in one or more double bonds. Moreover, such substituents include all those contemplated for alkyl groups, as discussed below, except where stability is prohibitive. For example, substitution of alkenyl groups by one or more alkyl, carbocyclyl, aryl, heterocyclyl, or heteroaryl groups is contemplated.
An “alkyl” group or “alkane” is a straight chained or branched non-aromatic hydrocarbon which is completely saturated. Typically, a straight chained or branched alkyl group has from 1 to about 20 carbon atoms, preferably from 1 to about 10 unless otherwise defined. In some embodiments, the alkyl group has from 1 to 8 carbon atoms, from 1 to 6 carbon atoms, from 1 to 4 carbon atoms, or from 1 to 3 carbon atoms. Examples of straight chained and branched alkyl groups include methyl, ethyl, n-propyl, iso-propyl, n-butyl, sec-butyl, tert-butyl, pentyl, hexyl, pentyl and octyl.
Moreover, the term “alkyl” as used throughout the specification, examples, and claims is intended to include both “unsubstituted alkyls” and “substituted alkyls”, the latter of which refers to alkyl moieties having substituents replacing a hydrogen on one or more substitutable carbons of the hydrocarbon backbone. Such substituents, if not otherwise specified, can include, for example, a halogen (e.g., fluoro), a hydroxyl, a carbonyl (such as a carboxyl, an alkoxycarbonyl, a formyl, or an acyl), a thiocarbonyl (such as a thioester, a thioacetate, or a thioformate), an alkoxy, a phosphoryl, a phosphate, a phosphonate, a phosphinate, an amino, an amido, an amidine, an imine, a cyano, a nitro, an azido, a sulfhydryl, an alkylthio, a sulfate, a sulfonate, a sulfamoyl, a sulfonamido, a sulfonyl, a heterocyclyl, an aralkyl, or an aromatic or heteroaromatic moiety. In preferred embodiments, the substituents on substituted alkyls are selected from C1-6 alkyl, C3-6 cycloalkyl, halogen, carbonyl, cyano, or hydroxyl. In more preferred embodiments, the substituents on substituted alkyls are selected from fluoro, carbonyl, cyano, or hydroxyl. It will be understood by those skilled in the art that the moieties substituted on the hydrocarbon chain can themselves be substituted, if appropriate. For instance, the substituents of a substituted alkyl may include substituted and unsubstituted forms of amino, azido, imino, amido, phosphoryl (including phosphonate and phosphinate), sulfonyl (including sulfate, sulfonamido, sulfamoyl and sulfonate), and silyl groups, as well as ethers, alkylthios, carbonyls (including ketones, aldehydes, carboxylates, and esters), —CF3, —CN and the like. Exemplary substituted alkyls are described below. Cycloalkyls can be further substituted with alkyls, alkenyls, alkoxys, alkylthios, aminoalkyls, carbonyl-substituted alkyls, —CF3, —CN, and the like.
The term “Cx-y” when used in conjunction with a chemical moiety, such as, acyl, acyloxy, alkyl, alkenyl, alkynyl, or alkoxy is meant to include groups that contain from x to y carbons in the chain. For example, the term “Cx-y alkyl” refers to substituted or unsubstituted saturated hydrocarbon groups, including straight-chain alkyl and branched-chain alkyl groups that contain from x to y carbons in the chain, including haloalkyl groups. Preferred haloalkyl groups include tritluoromethyl, difluoromethyl, 2,2,2-trifluoroethyl, and pentafluoroethyl. C0 alkyl indicates a hydrogen where the group is in a terminal position, a bond if internal. The terms “C2-y alkenyl” and “C2-y alkynyl” refer to substituted or unsubstituted unsaturated aliphatic groups analogous in length and possible substitution to the alkyls described above, but that contain at least one double or triple bond respectively.
The term “alkylthio”, as used herein, refers to a thiol group substituted with an alkyl group and may be represented by the general formula alkylS—.
The term “amide”, as used herein, refers to a group
wherein each RA independently represent a hydrogen or hydrocarbyl group, or two RA are taken together with the N atom to which they are attached complete a heterocycle having from 4 to 8 atoms in the ring structure.
The terms “amine” and “amino” are art-recognized and refer to both unsubstituted and substituted amines and salts thereof, e.g., a moiety that can be represented by
wherein each RA independently represents a hydrogen or a hydrocarbyl group, or two RA are taken together with the N atom to which they are attached complete a heterocycle having from 4 to 8 atoms in the ring structure.
The term “aminoalkyl”, as used herein, refers to an alkyl group substituted with an amino group.
The term “aralkyl”, as used herein, refers to an alkyl group substituted with an aryl group.
The term “aryl” as used herein include substituted or unsubstituted single-ring aromatic groups in which each atom of the ring is carbon. Preferably the ring is a 6- or 20-membered ring, more preferably a 6-membered ring. The term “aryl” also includes polycyclic ring systems having two or more cyclic rings in which two or more carbons are common to two adjoining rings wherein at least one of the rings is aromatic, e.g., the other cyclic rings can be cycloalkyls, cycloalkenyls, cycloalkynyls, aryls, heteroaryls, and/or heterocyclyls. Aryl groups include benzene, naphthalene, phenanthrene, phenol, aniline, and the like.
The terms “carbocycle”, and “carbocyclic”, as used herein, refers to a saturated or unsaturated ring in which each atom of the ring is carbon. Preferably, a carbocylic group has from 3 to 20 carbon atoms. The term carbocycle includes both aromatic carbocycles and non-aromatic carbocycles. Non-aromatic carbocycles include both cycloalkane rings, in which all carbon atoms are saturated, and cycloalkane rings, which contain at least one double bond. “Carbocycle” includes 5-7 membered monocyclic and 8-12 membered bicyclic rings. Each ring of a bicyclic carbocycle may be selected from saturated, unsaturated and aromatic rings. Carbocycle includes bicyclic molecules in which one, two or three or more atoms are shared between the two rings. The term “fused carbocycle” refers to a bicyclic carbocycle in which each of the rings shares two adjacent atoms with the other ring. Each ring of a fused carbocycle may be selected from saturated, unsaturated and aromatic rings. In an exemplary embodiment, an aromatic ring, e.g., phenyl, may be fused to a saturated or unsaturated ring, e.g., cyclohexane, cyclopentane, or cyclohexene. Any combination of saturated, unsaturated and aromatic bicyclic rings, as valence permits, is included in the definition of carbocyclic. Exemplary “carbocycles” include cyclopentane, cyclohexane, bicyclo[2.2.1]heptane, 1,5-cyclooctadiene, 1,2,3,4-tetrahydronaphthalene, bicyclo[4.2.0]oct-3-ene, naphthalene and adamantane. Exemplary fused carbocycles include decalin, naphthalene, 1,2,3,4-tetrahydronaphthalene, bicyclo[4.2.0]octane, 4,5,6,7-tetrahydro-1H-indene and bicyclo[4.1.0]hept-3-ene. “Carbocycles” may be susbstituted at any one or more positions capable of bearing a hydrogen atom.
A “cycloalkyl” group is a cyclic hydrocarbon which is completely saturated. “Cycloalkyl” includes monocyclic and bicyclic rings. Preferably, a cycloalkyl group has from 3 to 20 carbon atoms. Typically, a monocyclic cycloalkyl group has from 3 to about 10 carbon atoms, more typically 3 to 8 carbon atoms unless otherwise defined. The second ring of a bicyclic cycloalkyl may be selected from saturated, unsaturated and aromatic rings. Cycloalkyl includes bicyclic molecules in which one, two or three or more atoms are shared between the two rings. The term “fused cycloalkyl” refers to a bicyclic cycloalkyl in which each of the rings shares two adjacent atoms with the other ring. The second ring of a fused bicyclic cycloalkyl may be selected from saturated, unsaturated and aromatic rings. A “cycloalkenyl” group is a cyclic hydrocarbon containing one or more double bonds.
The term “carboxy”, as used herein, refers to a group represented by the formula —CO2H.
The term “ester”, as used herein, refers to a group —C(O)ORA wherein RA represents a hydrocarbyl group.
The term “ether”, as used herein, refers to a hydrocarbyl group linked through an oxygen to another hydrocarbyl group. Accordingly, an ether substituent of a hydrocarbyl group may be hydrocarbyl-O—. Ethers may be either symmetrical or unsymmetrical. Examples of ethers include, but are not limited to, heterocycle-O-heterocycle and aryl-O-heterocycle. Ethers include “alkoxyalkyl” groups, which may be represented by the general formula alkyl-O-alkyl.
The terms “halo” and “halogen” as used herein means halogen and includes chloro, fluoro, bromo, and iodo.
The terms “heteroaryl” and “hetaryl” include substituted or unsubstituted aromatic single ring structures, preferably 5- to 20-membered rings, more preferably 5- to 6-membered rings, whose ring structures include at least one heteroatom, preferably one to four heteroatoms, more preferably one or two heteroatoms. The terms “heteroaryl” and “hetaryl” also include polycyclic ring systems having two or more cyclic rings in which two or more carbons are common to two adjoining rings wherein at least one of the rings is heteroaromatic, e.g., the other cyclic rings can be cycloalkyls, cycloalkenyls, cycloalkynyls, aryls, heteroaryls, and/or heterocyclyls. Heteroaryl groups include, for example, pyrrole, furan, thiophene, imidazole, oxazole, thiazole, pyrazole, pyridine, pyrazine, pyridazine, and pyrimidine, and the like.
The term “heteroatom” as used herein means an atom of any element other than carbon or hydrogen. Preferred heteroatoms are nitrogen, oxygen, and sulfur.
The terms “heterocyclyl”, “heterocycle”, and “heterocyclic” refer to substituted or unsubstituted non-aromatic ring structures, preferably 3- to 20-membered rings, more preferably 3- to 7-membered rings, whose ring structures include at least one heteroatom, preferably one to four heteroatoms, more preferably one or two heteroatoms. The terms “heterocyclyl” and “heterocyclic” also include polycyclic ring systems having two or more cyclic rings in which two or more carbons are common to two adjoining rings wherein at least one of the rings is heterocyclic, e.g., the other cyclic rings can be cycloalkyls, cycloalkenyls, cycloalkynyls, aryls, heteroaryls, and/or heterocyclyls. Heterocyclyl groups include, for example, piperidine, piperazine, pyrrolidine, morpholine, lactones, lactams, and the like.
The terms “polycyclyl”, “polycycle”, and “polycyclic” refer to two or more rings (e.g., cycloalkyls, cycloalkenyls, cycloalkynyls, aryls, heteroaryls, and/or heterocyclyls) in which two or more atoms are common to two adjoining rings, e.g., the rings are “fused rings”. Each of the rings of the polycycle can be substituted or unsubstituted. In certain embodiments, each ring of the polycycle contains from 3 to 10 atoms in the ring, preferably from 5 to 7.
The term “substituted” refers to moieties having substituents replacing a hydrogen on one or more carbons of the backbone. It will be understood that “substitution” or “substituted with” includes the implicit proviso that such substitution is in accordance with permitted valence of the substituted atom and the substituent, and that the substitution results in a stable compound, e.g., which does not spontaneously undergo transformation such as by rearrangement, cyclization, elimination, etc. Moieties that may be substituted can include any appropriate substituents described herein, for example, acyl, acylamino, acyloxy, alkoxy, alkoxyalkyl, alkenyl, alkyl, alkylamino, alkylthio, arylthio, alkynyl, amide, amino, aminoalkyl, aralkyl, carbamate, carbocyclyl, cycloalkyl, carbocyclylalkyl, carbonate, ester, ether, heteroaralkyl, heterocyclyl, heterocyclylalkyl, hydrocarbyl, silyl, sulfone, or thioether. As used herein, the term “substituted” is contemplated to include all permissible substituents of organic compounds. In a broad aspect, the permissible substituents include acyclic and cyclic, branched and unbranched, carbocyclic and heterocyclic, aromatic and non-aromatic substituents of organic compounds. The permissible substituents can be one or more and the same or different for appropriate organic compounds. For purposes of this invention, the heteroatoms such as nitrogen may have hydrogen substituents and/or any permissible substituents of organic compounds described herein which satisfy the valences of the heteroatoms. Substituents can include any substituents described herein, for example, a halogen, a hydroxyl, a carbonyl (such as a carboxyl, an alkoxycarbonyl, a formyl, or an acyl), a thiocarbonyl (such as a thioester, a thioacetate, or a thioformate), an alkoxy, a phosphoryl, a phosphate, a phosphonate, a phosphinate, an amino, an amido, an amidine, an imine, a cyano, a nitro, an azido, a sulfhydryl, an alkylthio, a sulfate, a sulfonate, a sulfamoyl, a sulfonamido, a sulfonyl, a heterocyclyl, an aralkyl, or an aromatic or heteroaromatic moiety. In preferred embodiments, the substituents on substituted alkyls are selected from C1-6 alkyl, C3-6 cycloalkyl, halogen, carbonyl, cyano, or hydroxyl. In more preferred embodiments, the substituents on substituted alkyls are selected from fluoro, carbonyl, cyano, or hydroxyl. It will be understood by those skilled in the art that substituents can themselves be substituted, if appropriate. Unless specifically stated as “unsubstituted,” references to chemical moieties herein are understood to include substituted variants. For example, reference to an “aryl” group or moiety implicitly includes both substituted and unsubstituted variants.
The term “sulfonate” is art-recognized and refers to the group SO3H, or a pharmaceutically acceptable salt thereof.
The term “sulfone” is art-recognized and refers to the group —S(O)2—RA, wherein RA represents a hydrocarbyl.
The term “thioether”, as used herein, is equivalent to an ether, wherein the oxygen is replaced with a sulfur.
The invention now being generally described, it will be more readily understood by reference to the following, which is included merely for purposes of illustration of certain aspects and embodiments of the present invention, and is not intended to limit the invention.
All of the peptides were synthesized by and purchased from Biomatik (Ontario, Canada). The peptides had purity >95% by HPLC. The sequences of ACA peptide amphiphiles (ACA-PA) and Bi-Cardin peptides are listed in Table 1. For the self-assembling ACA-PAs, the self-assembly is understood to be driven by hydrophobic interactions of the hydrophobic palmitic (16 carbon) tail groups, and also directed by the β-sheet forming V3K3 peptide backbones into cylindrical shapes. With the rationally designed peptide backbones, the ACA-PAs can self-assemble into rod-like structures with cationic heparin-binding Cardin motifs exposed on the surface. ACA-PA contain palmitic tail groups and β-sheet forming sequence with hydrophobic oligopeptide blocks, thereby allowing the peptide amphiphiles to self-assemble into elongated structures with high aspect ratios. Heparin-binding Cardin motif peptide sequence was incorporated in the C-terminus of the peptide to potentiate antibacterial activities against a broad spectrum of bacteria.
To prepare the self-assembled supramolecules of the peptide amphiphiles, lyophilized ACA-PA powders were resuspended in deionized water (DI water, Milli-Q system). Peptide amphiphile solutions were vortexed, and then stored at 4° C. for at least 18 h to allow for supramolecular self-assembly. The solutions of the CVK peptide and Bi-Cardin peptide were also prepared by the same method. In all the experiments, the peptides were dissolved in autoclaved deionized water.
The self-assembled structure of each PA was observed by TEM. As
Morphology characterization using TEM indicated that the formation of long nanofibers for the CVK-PA measuring micrometers in length. The ACA-PA were also able to self-assemble into cylindrical supramolecular structures but with relatively shorter lengths. Without wishing to be bound by any theory, the addition of cationic Cardin-motif groups to the peptide backbone may have inhibited the formation of long nanofibers. Self-assembly is believed to be a result of a dynamic balance between the hydrophobic interactions of the alkyl tail groups and the opposing repulsive forces of the charged head groups. As the PAs aggregate and grow into cylindrical structures, the electrostatic repulsion between like-charged residues may limit the dimensions of the resulting supramolecular structures [17, 26, 27, 29]. Interestingly, the self-assembled structures of ACA-PA exhibited morphology transition from nanorod structures to bundle-like, longer fibers through the increase of concentration.
The self-assembled morphologies of peptide amphiphiles in water were observed by TEM (JEM-1010, Peabody, Mass.). Each sample was mounted on a 300-mesh copper-coated carbon grid (Electron Microscopy Sciences, Hatfield, Pa.), and then negatively stained with a 1.5% phosphotungstic acid solution (1.5% PTA). Before imaging, all the samples were air-dried for about 10 minutes. In all cases, samples were characterized at an accelerating voltage at 80 kV.
As the circular dichroism spectra showed, the self-assembly of these ACA nanorods was directed by the β-sheet secondary structure which resulted from the designed peptide backbones, which plays an important role in insertion of the nanorods into bacterial membranes.
In water, the CVK-PA adopted β-sheet secondary structure as
As characterized by CD measurements, spectra of the CVK-PA clearly indicated a well-ordered β-sheet secondary conformation, which can be exerted by the formation of packed hydrophobic cores and β-sheet forming intermolecular hydrogen bonds. Regarding the ACA-PA, functionalization of the cationic heparin-binding sequence caused a blue-shift on the CD spectra, leading to the spectra with 10 nm lower peak wavelengths and reduced ellipticity in the positive peak. Without wishing to be bound by any particular theory, this may be a consequence of increased positively charge and decreased peptide/peptide interactions [34]. The conformational contribution induced by the Cardin-motif groups may be excluded since: i) the Bi-Cardin peptide are unstructured in solution as measured by CD in this work, and ii) the free Cardin-motif peptide possesses low α-helix content [23]. Investigation of peptide secondary structures in lipidic environments suggests that both ACA-PA and CVK-PA can maintain their conformational characteristics in prokaryotic membranes. Interactions with the prokaryotic mimicking liposome vesicles also resulted in higher band intensity in the CD spectra of ACA-PA and CVK-PA, which can be attributed to peptide accumulation on the surface of anionic liposome vesicles [34]. It is also likely that the ACA-PA can exhibit transition to α-helix structure in a micelle-forming and membrane-mimetic SDS solution.
The secondary structures of the peptides were characterized by a J-715 spectropolarimeter (JASCO Analytical Instruments, Easton, Md., USA). The 0.4 mM solutions of each peptide were prepared in degassed DI water.
To study the secondary structures of peptides under membrane-mimetic conditions, each peptide was suspended in either prokaryotic membrane mimicking liposome vesicles or sodium dodecyl sulfate (SDS) solution (Thermo Fisher Scientific, Waltham, Mass., USA). Prokaryotic membrane mimicking liposome vesicles were prepared as previously described [12]. 1,2-Dilauroyl-sn-glycero-3-phosphoethanolamine (DLPE) and 1,2-dilauroyl-sn-glycero-3-[phosphor-rac-(1-glycerol)] (DLPG) were dissolved in chloroform to a molar ratio of 7:3. A thin film of lipids was formed by evaporating the solvent under vacuum at room temperature for 3 hours. The thin film was then rehydrated in DI water to a concentration of 2.4 mM, followed by extrusion for 21 times with a 100 nm Millipore polycarbonate filter. Structures of the resulting DLPE/DLPG liposome vesicles were confirmed by TEM characterization. Next, peptide solutions were diluted in liposome vesicle solution or SDS solution. The peptide concentrations were fixed at 0.4 mM, whereas the final concentration of liposome vesicles and SDS solution were 0.3 mM and 25 mM, respectively.
For CD measurements, 200 μL of each sample was transferred into a 1 mm path length quartz cuvette (Hellma, Germany). The CD spectra were collected between wavelengths of 190 nm to 240 nm at a scan rate of 10 nm/min, and expressed as the average of three scans. All the measurements were performed at room temperature.
First, the solvatochromic probe Nile Red was used to examine the threshold concentrations for the spontaneous aggregation induced by hydrophobic collapse of peptides. Once the supramolecular structures of PA self-assemble in water at their CMC, the Nile Red dye can be solubilized in the hydrophobic cores of the PA assemblies, displaying an enhanced fluorescent intensity [28, 29]. Consequently, the fluorescent intensity maxima of Nile Red were at the emission wavelength of 630 nm in the solutions of CVK-PA and ACA-PA, whereas the emission wavelength was located at 660 nm in the Bi-Cardin peptide solutions (
The solvatochromic Nile Red dye (9-diethylamino-5-benzo[a]-phenoxazinone, Thermofisher, Waltham, Mass., USA) was used to determine the CMC of each peptide. This dye is nearly non-fluorescent in polar solvents but undergoes a blue shift emission once incorporated into hydrophobic environments. Briefly, the stock solution of Nile Red (2.5 mM) was prepared in ethanol and then stored in −20° C. before use. 500 μL of the peptide solution ranging from 0.25 to 300 μM were prepared by serial dilution. The dye solution was diluted by 1,000-fold after 0.5 μL of the 2.5 mM Nile Red stock solution was placed into 500 μL of each peptide solution. The solutions were then mixed, and 100 μL of each solution were transferred onto a 96-well plate (each sample was triplicate). The emission spectra of Nile Red in samples was collected from 600 to 750 nm wavelengths at 5 nm intervals with an excitation wavelength of 550 nm using a spectrophotometer (SpectraMax M3, Molecular Devices, Molecular Devices, Sunnyvale, Calif., USA). To estimate the CMC of each peptide, the corrected fluorescent intensity (If,corrected) of Nile Red at its emission wavelength for each peptide solution was calculated using equation: If,corrected=If,sample−If,water, where If,sample is the average of the triplicate fluorescent intensity measurements in the sample and If,water is the fluorescent intensity of Nile Red in water without the peptide. The measurements of the corrected fluorescent intensity were plotted against the log 10 values of concentration of each peptide, then the CMC value was determined at the point of intersection of the plot of log peptide concentration and fluorescent intensity of Nile Red.
Gram-positive (S. aureus and MRSA) and Gram-negative (E. coli and MDR E. coli) bacteria were incubated with peptide concentrations ranging from 20 to 100 μM, and time-lapsed bacterial growth was monitored for 20 hours by determining the optical density at 562 nm (O.D. 562 nm). The ACA-PA remarkably inhibited the proliferation of both drug-susceptible and drug-resistant bacteria, but demonstrated different inhibitory effects between Gram-negative bacteria and Gram-positive bacteria (
On the other hand, peptide self-assembly was shown to be critical factor for bacteria growth inhibition against Gram-negative E. coli and MDR E. coli bacteria. At concentrations higher than the CMC (60 μM to 100 μM), bacterial proliferation was significantly suppressed by the ACA-PA (
ACA-PA achieved a significantly stronger antibacterial effect, as compared to CVK-PA with self-assembly backbone sequence and the non-self-assembling Bi-Cardin peptide. Without wishing to be bound by any theory, both heparin-binding groups and β-sheet forming self-assembly groups may be important to the antibacterial properties of the PA, which could be explained by the enhanced cationic charge, hydrophobicity and the formation of β-sheet structure of the ACA-PA. These physical and conformational characteristics of the amphiphilic peptide promote binding to the lipid acyl chains of the membrane and enhance membrane insertion [33]. Although the CVK-PA and Bi-Cardin peptide may interact with bacterial cell membranes via electrostatic interactions, the limited number of charged groups or hydrophobic residues may constrain their capability for membrane insertion.
Interestingly, the Gram-positive (S. aureus and MRSA) and Gram-negative (E. coli and MDR E. coli) strains responded differently to the ACA-PA treatment. Bacterial proliferation and the number of viable Gram-positive bacteria decreased proportionally to the increasing concentrations of ACA-PA. Even at concentrations below the CMC, the PA inhibited growth and promoted toxicity against the bacteria, which implied that the antibacterial property of the ACA-PA towards Gram-positive bacteria might not require peptide self-assembly. However, the results of bacterial studies towards Gram-negative bacteria indicated the low potency of ACA-PA at the concentrations lower than CMC. The dissociated PA had little antibacterial effect and, thus, peptide self-assembly was essential to kill Gram-negative bacteria. Once self-assembled, the ACA nanorods considerably suppressed Gram-negative bacterial growth and induced a remarkable reduction in cell viability.
This assay was performed to investigate the inhibitory effects of each peptide against Gram-positive Staphylococcus aureus (S. aureus, ATCC #25923) and methicillin-resistant S. aureus (MRSA, ATCC #43300), as well as Gram-negative Escherichia coli (E. coli, ATCC #25922), and multidrug-resistant E. coli (MDR E. coli, ATCC #BAA-2471). In all experiments, solutions of each peptide at the concentrations from 20 μM to 100 μM in 3% Tryptic Soy Broth (TSB) media were freshly prepared. A single colony of bacteria was isolated from a stock agar plate and cultured overnight in 4 mL of 3% TSB on a shaking incubator set at 200 rpm and 37° C. The bacteria culture was adjusted to an optical density at 562 nm (OD562) to about 0.52 (109 cells/mL), and the resulting bacteria suspension was subsequently diluted to about 106 colony forming units (CFU) per mL in each sample. The control samples were bacteria incubated in TSB media without peptides. The bacteria were incubated inside a spectrophotometer (Spectra-Max Paradigm, Molecular Devices, Sunnyvale, Calif.) at 37° C. under static conditions for 20 h, and the bacterial growth curves were measured in terms of turbidity at OD562 every 2 minutes [24]. The normalized OD562 values of samples were calculated by subtracting the experimental OD562 values from the corresponding blank samples without bacteria.
The minimum inhibitory concentration (MIC) of ACA-PA was tested against drug-resistant bacteria and compared with conventional penicillin-streptomycin (10,000 U/mL, Thermo Fisher Scientific, Waltham, Mass., USA) as well. Solutions of each antimicrobial agent at different concentrations were prepared by serial 2-fold dilutions in water. Bacteria (seeding density=106 CFU/mL) were then mixed with the antimicrobial solutions, and incubated for 24 h at 37° C. The OD562 was measured at the end of treatment. The MIC value was determined as the lowest concentration of each antimicrobial agent that induced no increase in OD562. All experiments were run in triplicate to demonstrate significance. Data are expressed as mean±standard error of the mean (S.E.M.) and a two-tailed Student t-test was used to evaluate differences between means, with p<0.005 being considered statistically significant.
The bactericidal effects of the peptides were examined using a viable colony count assay as well as the live/dead staining assay. For the viable colony count assay, bacteria were treated with peptides for 4 h and the resulting viable bacterial density of each sample was expressed by log10[CFU/mL]. For the Gram-positive bacteria tested, the decrease in bacterial density was dependent on the concentration of the ACA-PA (
In addition, ACA-PA were mixed with heparin at various weight ratios (1:1, 1:2, and 1:3 ACA-PA to heparin ratios) to block the Cardin motif groups on the PA. The ACA-PA concentration used to treat bacteria (MRSA and MDR E. coli) was a constant 80 μM and only varied in the concentration of heparin. The results indicated that the number of viable bacteria colonies were positively proportional to the amount of heparin added to the ACA-PA, although the self-assembled structure of the ACA nanorods was not affected by the addition of heparin (
The viable count assay was performed to quantify the bactericidal activity of each peptide [25]. Stock solutions of peptides were diluted in 3% TSB media to concentrations ranging from 20 μM to 100 μM immediately before experiments. Heparin-ACA-PA were also prepared by mixing the ACA-PA stock solution with heparin (sodium salt from porcine intestinal mucosa, Sigma, St. Louis, Mo.) to 1:1, 1:2 and 1:3 weight ratios in water, and a final concentration of ACA-PA in the heparin-ACA-PA at each heparin weight ratio was adjusted to 80 μM for each experiment. The bacteria (106 CFU/mL) were incubated with peptides at 37° C. for 4 h. After incubation, serial dilutions of samples were plated on TSB agar and then incubated at 37° C. overnight. The colonies from each spot were manually counted, and the CFU number for each sample was determined. Experiments were conducted in triplicate and results were expressed as the log 10 values of the CFU number in each sample. Data were expressed by stand error of the mean (±S.E.M.) and N=3, *p<0.05 compared with control samples and #p<0.05 compared with bacteria treated with 40 μM of ACA-PA.
To further investigate bacteria viability after treatment with ACA-PA, the live/dead assay was used to confirm the antibacterial actions of ACA-PA. Dead bacteria with disrupted membrane were stained a first color, whereas live bacteria were stained with a second color fluorescence. A large amount of robust MRSA bacteria in the untreated control sample appeared a second color and in spherical shapes (
The live/dead bacterial viability assay was conducted to further assess the bactericidal efficacy of ACA-PA using the LIVE/DEAD BacLight Bacterial Viability Kits (Kits 71007, Molecular Probes, Eugene, Oreg., USA). MRSA and MDR E. coli bacteria (100 μl, 106 CFU/mL) were incubated with 80 μM and 40 μM of peptide in 3% TSB media at 37° C. for 4 h on a 96-well plate, and the control samples of bacteria were incubated in 3% TSB media only. At the end of treatment, the supernatant of each sample was carefully removed, and the bacteria on the bottom of the 96-well plate were stained with reagent solution that was prepared according to the manufacturer's instructions, and incubated at room temperature for 10 minutes Samples were observed in a fluorescent microscope using Alexa Fluor 488 (emission/excitation wavelength=500/519 nm) and PI (excitation emission=490/635 nm) filter sets. The live bacteria stained fluorescent a second color (SYTO9 nucleic acid stain), whereas the dead bacteria with disrupted membranes stained fluorescent a first color (propidium iodide, PI).
The binding of each peptide at various concentrations to LPS was determined by the capability of displacing the BC probes bound with LPS. The fluorescent BC probe was used as a probe to determine the level of peptide bound with LPS. BC probe binds to native LPS and particularly target the lipid A portion. The fluorescent intensity of BC probe decreases as it binds to LPS. Nonetheless, once the cationic peptides that that have competitively stronger interactions with LPS, BC probes on LPS are displaced and thus exhibit fluorescent enhancement [26, 27]. As
LPS is one of the major components in the outer membrane of most Gram-negative bacteria, which is considered the extra protection to bacteria. The core region of LPS can protect the organism from hydrophobic antibiotics, whereas the mutations in porins can decrease the entry of hydrophilic antimicrobial compounds and result in drug resistance. Thus, antibacterial agents that can penetrate and destabilize LPS barrier can possibly inhibit resistance of bacteria [35]. To further investigate the interactions with LPS and mechanisms of antibacterial actions towards Gram-negative bacteria, LPS binding affinity of each peptide was analyzed in this study. The results showed that both Bi-Cardin peptide and CVK-PA can associate with LPS, although these two peptides had low antibacterial activities as observed in the bacterial studies. Interestingly, the binding affmity of CVK-PA to LPS dramatically enhanced when it self-assembled into supramolecular nanofibers beyond the CMC at about 50 μM. These findings suggest that self-assembly of peptide amphiphiles monomers into highly organized nanostructures can play a crucial role in association with LPS layer in bacteria, and also indicate the potential applications of incorporating self-assembling properties in peptide-based antibiotics for improved LPS destabilization. In addition, the ACA-PA exhibited the most effective LPS binding actions over all the concentrations investigated, which may result from the electrostatic interactions of the positively charged peptide with anionic LPS. Since the ACA-PA showed to have high LPS binding affinity even at concentrations lower than CMC, the electrostatic interactions of the peptide seemed to dominate over the effects of peptide self-assembly on LPS binding. This can be explained by the “self-promoted uptake pathway” in the interactions of bacterial LPS with cationic peptides. Peptides with strong affinities to LPS can competitively displace divalent cations (i.e. Ca2+ and Mg2+), resulting in disruption in the outer membrane. The antimicrobial peptides can further perpetrate into the cytoplasm membrane as the damaged outer membrane passively internalizes more molecules from the exterior [3, 36]. In summary, we have found that the potent antibacterial properties of ACA-PA against Gram-negative bacteria can be ascribed to its strong LPS binding affinity, and the peptide self-assembly as well as the positive charge may participate in the interactions with LPS.
The LPS binding affinity of peptide was examined with the BODIPY TR cadaverine (BC) fluorescent probe displacement assay as previously described [26, 27]. Stock solution of each peptide was diluted to predetermined concentrations with 10 mM HEPES buffer (pH=7.5, Thermo Fisher Scientific, Waltham, Mass., USA). Peptide solutions were equilibrated for 10 minutes, and LPS (from Escherichia coli O111:B4, Sigma, St. Louis, Mo., USA) solution in 10 mM HEPES buffer was added. The final peptide concentrations ranged from 20 μM to 100 μM, and the LPS concentration was 100 μg/mL. LPS only samples were solutions that only contained the same amount of LPS without peptide. Peptides were allowed to interact with LPS in room temperature for 15 minutes, and the BC probe solution in 10 mM HEPES buffer was added to achieve a final concentration of 10 μM. Followed by incubation for 15 minutes in room temperature, the fluorescent intensity was measured using a spectrophotometer at an excitation wavelength of 580 nm and an emission wavelength of 620 nm. Finally, the LPS binding factor of each sample was calculated using the equation:
where Fp is the fluorescent intensity of BC probe in each peptide solution, Fp,LPS is the fluorescent intensity of BC probe in the mixture of peptide/LPS solution, FLPS represents the fluorescent intensity of BC probe in solution containing LPS only.
When peptides bind to LPS and displace the BC probe, fluorescence intensity of the probe is increased. LPS binding affinity of each peptide was then analyzed by the fluorescent intensity of the displaced BC probe. Data were expressed by stand error of the mean (±S.E.M.) and N=3, *p<0.05 compared with 0 μM samples and #p<0.05 compared with 40 μM samples of the same peptide.
TEM was used to reveal the damage in bacterial cell envelopes caused by ACA-PA treatment. Drug-resistant bacterial strains (MRSA and MDR E. coli) were exposed to ACA-PA at concentrations below (40 μM) and above (80 μM) the CMC, and ultrathin sections of the bacterial cultures were visualized by TEM.
After treatment with 40 μM of ACA-PA, the thick layer of the peptidoglycan envelope of MRSA was partially damaged and the inner cytoplasmic membrane was no longer attached to the outer membrane, leading to cytoplasmic leakage (
Bacterial membrane disruption was observed from the ultrathin sectioned sample using TEM. The ACA-PA caused localized membrane disintegration on Gram-positive MRSA at both 40 and 80 μM, further indicating that the membrane disruption effects were independent of peptide self-assembly. Nonetheless, ACA-PA at 40 μM (below the CMC) only caused preliminary blisters on the outer membrane of Gram-negative bacteria and were inadequate to induce complete membrane disruption as the cell membranes were still able to enclose the cytoplasm. After treatment with 80 μM ACA nanorods, bacterial cell membranes were severely damaged with complete cytoplasm leakage. Both outer and inner membranes demonstrated disorganized structures throughout the bacterium. On the damaged membranes, blisters appeared to originate from the pores. This explains the reason for the different antibacterial activity of ACA-PA on Gram-negative bacteria compared to the concentration-dependent toxicity on Gram-positive bacteria. The cell envelope of Gram-positive has a cytoplasmic membrane surrounded by a thick peptidoglycan layer with lipoteichoic acid. The antibacterial ACA-PA could penetrate the Gram-positive bacterial membrane by charge and hydrophobicity, although the PA were in a dispersed, non-assembled form. However, such dispersed PA were not able to penetrate the outer membrane of Gram-negative bacteria. Without wishing to be bound by any theory, it is proposed that at concentrations higher than the CMC, ACA-PA induced bacterial cell lysis possibly by the formation of transmembrane pores through the outer and inner membranes, which can be supported by the toroidal model. In the toroidal model, insertion of antibacterial peptides induces a local bending in the membrane leaflets through the pores, resulting in unfavorable elastic tension and ultimately lead to membrane disintegration [9]. Since the formation of self-assembled peptide nanoparticles can increase the local density of the cationic charge [10], once the self-assembly occurred at concentrations over CMC, it is likely that the self-assembled nanorods with localized charge and their β-sheet structure can insert into the cell wall layers perpendicularly and form transmembrane pores, initiating membrane disintegration and cytoplasmic leakage.
To observe the effects of ACA-PA on the bacteria cell membranes, the treated drug-resistant bacteria (MRSA and MDR E. coli) were fixed, sectioned and visualized by TEM using methods previously described [25]. Briefly, MRSA and MDR E. coli bacteria (107 CFU/mL) were treated by ACA nanorods at 40 μM and 80 μM in TSB media for 4 h at 37° C. (the control samples were bacteria grown in TSB media at the same condition). The bacteria were centrifuged and then fixed with 2.5% glutaraldehyde in 0.1M sodium cacodylate buffer overnight at 4° C. After rinsing with the sodium cacodylate buffer three times, bacteria pellets were post-fixed with 1% osmium tetroxide for 2 h and dehydrated by gradient ethanol solutions (30%, 50%, 70%, 85%, 90% and 100%). Samples were infiltrated with squetol resin. The resins were polymerized at 55° C. for 24 h and thin-sectioned using an ultra-microtome (Reichert-Jung Ultracut E, Reichert Technologies, Buffalo, N.Y.). The sectioned samples were mounted on 200-hex mesh copper-coated carbon grids and stained by 1.5% uranyl acetate before imaging.
To evaluate the cytotoxicity of the peptides, human dermal fibroblasts (HDF) were treated for 24 h, and cell viability was determined via MTS assays (
However, given that CVK-PA as well as ACA-PA showed noticeable toxicity towards HDF cells, biocompatibility of these peptide amphiphiles should be taken into consideration for their potential applications in clinical trials. Similar observation was also demonstrated by Newcomb et al. that nanofiber-forming peptide amphiphiles bearing β-sheet and serial lysine residues can have strong cytotoxicity [37]. The disclosed peptides showed toxicity and inhibitory effects towards drug-resistant bacteria.
Furthermore, although the self-assembled ACA-PA also had a moderate cytotoxicity at high concentrations, it was also significantly more effective against bacteria at concentrations from 60 to 100 μM than HDF cells. At this concentration range, the ACA nanorods induced about a 100-fold decrease in Gram-positive bacteria density, and a 10,000-fold decrease in Gram-negative bacteria density, but caused comparatively lower percentages of reduction (48%) in HDF cell viability. The Bi-Cardin peptide was shown to be non-cytotoxic at all the concentrations tested. The CVK-PA critically decreased the cell viability at concentrations higher than 20 μM, which induced over 40% of cell death.
Human dermal fibroblast cells (HDF, Detroit 551, ATCC #CCL-110) were cultured in Dulbecco's modified Eagle medium (DMEM; Fisher, Pittsburgh, Pa.) supplemented with 10% fetal bovine serum (FBS) and 1% penicillin/streptomycin for 24 h. All cells were cultured to 90% confluence in a 37° C., humidified, 5% CO2/95% air environment. Cells at passage numbers of 4-7 were used in these experiments.
The MTS cell viability assay kit (Promega, Madison, Wis., USA) was used to determine cytotoxicity of the peptides. First, HDF cells were seeded on a 96-well plate at a cell density of 5,000 cells/well (equal to 15,385 cells/cm2), and were incubated overnight for cell adhesion. After overnight incubation, the cell medium in each well was replaced by 100 μL of cell culture medium containing various concentrations of peptides (20 μM to 100 μM). The control samples were cells incubated in cell culture medium only. After 24 h, the treatment medium in each well was removed. The cells were washed with phosphate buffered saline (PBS, pH=7.4, Fisher, PA, USA) and 100 μL of fresh cell culture medium was added to each well, followed by the addition of 20 μL of the MTS reagent. After the cells were incubated for 2.5 h, the absorbance was measured at a wavelength of 490 nm by a spectrophotometer (SpectraMax M3, Molecular Devices, Molecular Devices, Sunnyvale, Calif., USA). To estimate the cell numbers in each well, a standard curve expressing the linear correlation between different cell densities and optical densities (R2>0.95) was plotted, and the cell numbers were determined with this standard curve from the OD490 value recorded in each sample. The cell viability of each sample was calculated by: Cell viability=[(cell density per mL of treated sample)/(cell density per mL of control sample)]×100%. Data were expressed by standard error of the mean (±S.E.M.) and N=3, *p<0.05 compared with control samples.
A self-assembled ACA-PA functionalized with a heparin-binding (AKKARA)2 (SEQ ID NO: 2) Cardin-motif sequence was designed to form nanoparticles with cylindrical shapes. At concentrations above the CMC (45 μM), the ACA-PA were found to self-assemble into nanorods about 7 to 10 nm in diameter. The ACA-PA was shown to have excellent antibacterial properties against both Gram-negative and Gram-positive bacteria in contrast to the CVK-PA and Bi-Cardin peptide. Antibacterial results demonstrated for the first time that ACA-PA had a concentration-dependent toxicity against Gram-positive bacteria (S. aureus and MRSA). For Gram-negative bacteria (E. coli and MDR E. coli), the ACA-PA possessed bactericidal effects only in self-assembled form, which indicated that self-assembly played a crucial role in antibacterial activity against Gram-negative bacteria. In all cases, the CVK-PA and Bi-Cardin peptide showed minimal antibacterial effect. With its strong interactions with LPS layer and formation of secondary structure on the prokaryotic membrane, the ACA-PA could target bacteria membranes and result in localized membrane disintegration against Gram-positive bacteria and blisters on the surface of Gram-negative bacteria, causing bacterial cytoplasmic leakage. Functionalization with a self-assembled PA effectively enhanced the antibacterial activity of the cationic Cardin-motif peptide sequence, and the resulting self-assembled nanorods are promising agents to combat infectious diseases caused by bacteria drug-resistance.
The contents of the articles, patents, and patent applications, and all other documents and electronically available information mentioned or cited herein, are hereby incorporated by reference in their entirety to the same extent as if each individual publication was specifically and individually indicated to be incorporated by reference. Applicants reserve the right to physically incorporate into this application any and all materials and information from any such articles, patents, patent applications, or other physical and electronic documents.
The invention has been described broadly and generically herein. Those of ordinary skill in the art will readily envision a variety of other means and/or structures for performing the functions and/or obtaining the results and/or one or more of the advantages described herein, and each of such variations and/or modifications is deemed to be within the scope of the present invention. More generally, those skilled in the art will readily appreciate that all parameters, dimensions, materials, and configurations described herein are meant to be exemplary and that the actual parameters, dimensions, materials, and/or configurations will depend upon the specific application or applications for which the teachings of the present invention is/are used. Those skilled in the art will recognize, or be able to ascertain using no more than routine experimentation, many equivalents to the specific embodiments of the invention described herein. It is, therefore, to be understood that the foregoing embodiments are presented by way of example only and that, within the scope of the appended claims and equivalents thereto, the invention may be practiced otherwise than as specifically described and claimed. The present invention is directed to each individual feature, system, article, material, kit, and/or method described herein. In addition, any combination of two or more such features, systems, articles, materials, kits, and/or methods, if such features, systems, articles, materials, kits, and/or methods are not mutually inconsistent, is included within the scope of the present invention. Further, each of the narrower species and subgeneric groupings falling within the generic disclosure also form part of the invention. This includes the generic description of the invention with a proviso or negative limitation removing any subject matter from the genus, regardless of whether or not the excised material is specifically recited herein.
This application claims the benefit of priority to U.S. Provisional Application for Patent Ser. No. 62/430,906, filed Dec. 6, 2016.
| Number | Date | Country | |
|---|---|---|---|
| 62430906 | Dec 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15832194 | Dec 2017 | US |
| Child | 17525354 | US |