Claims
- 1. A powder of hexagonal boron nitride with excellent sinterability having a purity of at least 95% by weight as boron nitride and containing an alkaline earth metal compound in an amount from 0.0001 to 0.1 mole calculated as alkaline earth metal per mole of boron, of which the crystallites (Lc) have a size in the range from 8 to 50 nm.
- 2. A powder of hexagonal boron nitride with excellent sinterability having a purity of at least 95% by weight as boron nitride and containing a calcium oxide or a barium oxide in an amount from 0.0001 to 0.1 mole calculated as calcium or barium per mole of boron, of which the crystallites (L.sub.c) have a size in the range from 8 to 50 nm.
- 3. A method for the preparation of a powder of hexagonal boron nitride having excellent sinterability which comprises the steps of:
- (a) mixing boric acid, dehydrated boric acid, ammonium borate and a nitrogen compound selected from the group consisting of urea, melamine, dicyandiamide, cyanuric acid and ammonium chloride to produce a powdery mixture;
- (b) admixing the powdery mixture with 0.005 to 0.1 moles of a carbonaceous powder calculated as carbon per mole of boron in the powdery mixture and 2.5 to 30% by weight of borax or anhydrous borax calculated as anhydrous borax based on the boric acid, dehydrated boric acid and ammonium borate in the powdery mixture; and
- (c) subjecting the powdery mixture to a heat treatment in a non-oxidizing atmosphere.
- 4. A method for the preparation of a powder of hexagonal boron nitride having excellent sinterability which comprises the steps of:
- (a) mixing boric acid, dehydrated boric acid, ammonium borate and a nitrogen compound selected from the group consisting of urea, melamine, dicyandiamide, cyanuric acid and ammonium chloride to produce a powdery mixture;
- (b) admixing the powdery mixture with 0.0001 to 0.1 mole of a calcium oxide or a barium oxide calculated as calcium or barium per mole of boron in the powdery mixture;
- (c) admixing the powdery mixture with a carbonaceous powder and at least one member selected from the group consisting of borax and anhydrous borax, the amount of the carbonaceous powder being in the range from 0.005 to 0.1 mole calculated as carbon per mole of boron in the powdery mixture and the amount of borax or anhydrous borax being in the range from 2.5 to 30% by weight calculated as anhydrous borax based on boric acid, dehydrated boric acid and ammonium borate in the powdery mixture; and
- (d) subjecting the powdery mixture to a heat treatment in a non-oxidizing atmosphere.
- 5. A method for the preparation of a powdery composition of hexagonal boron nitride having excellent sinterability which comprises the steps of:
- (a) mixing boric acid, dehydrated boric acid, ammonium borate and a nitrogen compound selected from the group consisting of urea, melamine, dicyandiamide, cyanuric acid and ammonium chloride to produce a powdery mixture;
- (b) admixing the powdery mixture with 0.005 to 0.1 mole of a carbonaceous powder calculated as carbon per mole of boron in the powdery mixture;
- (c) subjecting the powdery mixture to a heat treatment in a non-oxidizing atmosphere to obtain a powder of hexagonal boron nitride; and
- (d) admixing the powder of hexagonal boron nitride with 0.0001 to 0.1 mole of a calcium oxide or a barium oxide calculated as calcium or barium per mole of boron in the powder of hexagonal boron nitride.
- 6. A method for the preparation of a powdery composition of hexagonal boron nitride having excellent sinterability which comprises the steps of:
- (a) mixing boric acid, dehydrated boric acid, ammonium borate and a nitrogen compound selected from the group consisting of urea, melamine, dicyandiamide, cyanuric acid and ammonium chloride to produce a powdery mixture;
- (b) admixing the powdery mixture with 0.005 to 0.1 mole of a carbonaceous powder calculated as carbon per mole of boron in the powdery mixture and 2.5 to 30% by weight of borax or anhydrous borax calculated as anhydrous borax based on boric acid, dehydrated boric acid and ammonium borate in the powdery mixture;
- (c) subjecting the powdery mixture to a heat treatment in a non-oxidizing atmosphere to obtain a powder of hexagonal boron nitride; and
- (d) admixing the powder of hexagonal boron nitride with 0.0001 to 0.1 mole of a calcium oxide or a barium oxide calculated as calcium or barium per mole of boron in the powder of hexagonal boron nitride.
- 7. A method for the preparation of a powder of hexagonal boron nitride having excellent sinterability which comprises the steps of:
- (a) mixing boric acid, dehydrated boric acid, ammonium borate and a nitrogen compound selected from the group consisting of urea, melamine, dicyandiamide, cyanuric acid and ammonium chloride to produce a powdery mixture;
- (b) admixing the powdery mixture with 0.005 to 0.1 mole of a carbonaceous powder calculated as carbon per mole of boron in the powdery mixture;
- (c) admixing the powdery mixture with 0.0001 to 0.1 mole of a calcium oxide or barium oxide calculated as calcium or barium per mole of boron in the powdery mixture and 2.5 to 30% by weight of borax or anhydrous borax calculated as anhydrous borax based on boric acid, dehydrated boric acid and ammonium borate;
- (d) subjecting the powdery mixture to a heat treatment in a non-oxidizing atmosphere at a temperature of 900.degree. to 1300.degree. C. to obtain a crude powder of hexagonal boron nitride; and
- (e) washing the crude powder of hexagonal boron nitride followed by drying.
- 8. A method for the preparation of a powdery composition of hexagonal boron nitride having excellent sinterability which comprises the steps of:
- (a) mixing boric acid, dehydrated boric acid, ammonium borate and a nitrogen compound selected from the group consisting of urea, melamine, dicyandiamide, cyanuric acid and ammonium chloride to produce a powdery mixture;
- (b) admixing the powdery mixture with 0.005 to 0.1 mole of a carbonaceous powder calculated as carbon per mole of boron in the powdery mixture;
- (c) admixing the powdery mixture with 2.5 to 30% by weight of borax or anhydrous borax calculated as anhydrous borax based on the boric acid, dehydrated boric acid and ammonium borate in the powdery mixture;
- (d) subjecting the powdery mixture to a heat treatment in a non-oxidizing atmosphere at a temperature of 900.degree. C. to 1300.degree. C. to obtain a crude powder of hexagonal boron nitride;
- (e) washing the crude powder of hexagonal boron nitride followed by drying; and
- (f) admixing the dried powder of hexagonal boron nitride with 0.0001 to 0.1 mole of a calcium oxide or barium oxide calculated as calcium or barium per mole of boron in the dried powder.
Priority Claims (2)
Number |
Date |
Country |
Kind |
59-117375 |
Jun 1984 |
JPX |
|
59-182379 |
Aug 1984 |
JPX |
|
Parent Case Info
This is a continuation-in-part application from a copending U.S. patent application Ser. No. 741,288 filed June 4, 1985, now abandoned.
US Referenced Citations (4)
Foreign Referenced Citations (4)
Number |
Date |
Country |
0811644 |
Apr 1969 |
CAX |
2461821 |
Dec 1974 |
DEX |
0155507 |
Aug 1985 |
JPX |
1179156 |
Mar 1967 |
GBX |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
741288 |
Jun 1985 |
|