Patent Application
20070128404
The present invention relates to synthetic polymeric filaments having a hexalobal cross-sectional shape with three major lobes and three minor lobes. The filaments are especially suitable for making carpets that exhibit low sheen, glitter-free subdued luster, high color yield, and excellent anti-soiling performance.
The present invention is a synthetic polymeric filament having a hexalobal cross-section comprising three major lobes positioned symmetrically about a central axis within a major radius (R1) relative to said central axis and three minor lobes each positioned symmetrically between a major lobe within a minor radius (R2) relative to said central axis wherein the ratio of major radius (R1) to minor radius (R2) defines an exterior modification ratio (R1/R2) greater than 1. Carpets comprised of synthetic polymeric filaments having a cross-section according to the invention exhibit low sheen, glitter-free subdued luster, high color yield, and excellent anti-soiling, i.e., soil hiding, performance
The invention will be more fully understood from the following detailed description, taken in connection with the accompanying drawings, which form a part of this application and in which:
Throughout the following detailed description of the invention, similar reference numerals have been used to refer to similar elements in all of the drawings.
The filaments of the present invention have a generally uniform solid hexalobal cross-section with three major lobes and three minor lobes. Each major lobal section has essentially straight side portions that extend outwardly and terminate in a generally convex tip. In one embodiment, the sides of the straight side portions are parallel. In another embodiment, the straight side portions can taper inwardly, from wide to narrow, moving away from the central axis in the direction of the convex tip. In yet another embodiment, the straight side portions can taper inwardly, from wide to narrow, moving toward the central axis in the direction from the convex tip to the central axis.
The major lobes of cross-section may be positioned symmetrically or asymmetrically in relation to the central axis of the filament cross-section. The length of each major lobe measuring from the central axis to the convex tip is greater than the corresponding length dimension of each minor lobe. The lobes are arranged having two sides being essentially mirror images of each other in embodiments where the lobes are symmetrical.
Referring now to
The distance from a respective center of generation 18A, 18B, 18C to the convex tip of each major lobe 16A, 16B, 16C is indicated by a major tip radius R3 (only one of which is illustrated in
Convex region 22 is disposed between each major lobe and each minor lobe as shown.
According to one embodiment, a filament 10 has an exterior modification ratio (R1/R2) greater than 1. In another words, the length of each major lobe (R1) measured from the central axis of the filament to the major lobe tip is greater than the corresponding length of each minor lobe (R2). According to another embodiment of the invention, the exterior modification ratio (R1/R2) is in the range of from 1.2 to about 3.5. In yet another embodiment, the exterior modification ratio (R1/R2) is in the range of from about 1.5 to about 2.5.
In addition, the ratio of major radius (R1) to major tip radius (R3) defines a “major tip ratio” (R1/R3) in the range of from about 2.0 to about 10.0. In another embodiment according to the invention the major tip ratio (R1/R3) is in the range of from about 2.5 to about 4.0.
The ratio of major radius (R1) to minor tip radius (R4) defines a “minor tip ratio” (R1/R4) in the range from about 2.0 to about 40.0. In another embodiment the minor tip ratio (R1/R4) is in range from about 3.75 to about 14.0.
A filament, i.e., a staple fiber or continuous filament, in accordance with the present invention is prepared using a synthetic, thermoplastic melt-spinnable polymer or copolymer. Suitable polymers and copolymers include polyamides, polyesters, polyolefins, and polyacrylonitrile. Hereinafter the term “polymer” is used to mean polymers, and random and block copolymers. The polymer composition is melted and then is extruded (i.e., “spun”) through a spinneret capillary opening 54 as shown in
The filaments are generally uniform in cross-section along their length and may be textured, also known as “bulked” or “crimped” according to know methods. They can be used for several different applications, including carpets, textile, or non-woven uses.
A plurality of bulked continuous filaments produced according to the invention can be gathered together to form a bulked continuous yarn. Owing to the particular desired properties of the filaments, a yarn formed there from is believed to be particularly advantageous for tufting (with or without other types of yarn(s), as desired) into carpet thereby resulting in especially desirable properties. If desired, the yarn can include other forms of filament(s).
A bonded white yarn carpet comprising filaments according to the present invention can be passed under a jet-dye printer. Using design software, the jets shoot dye onto the carpet and form designs and patterns of infinite variety and color. The carpet is then steamed, followed by a thorough rinsing, and then it is spun dry. Both loop pile and cut pile carpets can be used to produce printed carpets.
A plurality of capillary openings extend through the spinneret plate from the recessed upper surface to the bottom surface. Each capillary opening 54 serves to form one filament. Only one such capillary opening 54 is illustrated in
As best seen in
Width dimensions of major legs 62A, 62B, and 62C are indicated by the respective reference characters B1, B2, B3. Width dimensions of minor legs 63A, 63B, 63C are indicated by the respective reference characters D1, D2, D3. Normally, the width of a major leg is greater than the width of a minor leg.
Length dimensions of major legs 62A, 62B, and 63C are indicated by the respective characters A1, A2, and A3 (only one of which is illustrated in
The sides of each leg are generally parallel and extend outwardly and terminate in a convex tip. Alternatively, the leg can taper in width, from wide to narrow, in the direction from central axis 68 to the circular tip. In yet another embodiment, the straight side portions can taper in width, from wide to narrow, in the direction from the circular tip to the central axis 68 of the cross-section.
The spinneret plate may be fabricated in any appropriate manner, as by using the laser technique described in U.S. Pat. No. 5,168,143.
The invention will now be described in greater detail in conjunction with the following, non-limiting examples.
Test Methods
Relative Viscosity
The relative viscosity (RV) was measured by dissolving 5.5 grams of nylon 6,6 polymer in fifty cubic centimeters (50 cc) of formic acid. The RV is the ratio of the absolute viscosity of the nylon 66/formic acid solution to the absolute viscosity of the formic acid. Both absolute viscosities were measured at twenty-five degrees Centigrade (25° C.).
Carpet Glitter
The degrees of glitter for different cut-pile carpet samples were visually compared in a side-by-side comparison without knowledge of which carpets were made with which yarns. The carpets were examined by a panel of five (5) experienced examiners each familiar with carpet construction and surface texture. The glitter value was measured by the examiners on a scale of “1” to “5”, with “5” being the most glitter. The glitter rating for each sample was averaged and the samples given a rating of low, medium or high glitter based on the average rating. Carpet bulk was rated in the same manner. The glitter results are reported in Table 3.
Lab Soiling Test
The soiling test was conducted on each carpet sample using a Vetterman drum. The base color of the sample was measured using the hand held color measurement instrument sold by Minolta Corporation as “Chromameter” model CR-210.
The carpet sample was placed in the Vetterman drum. Two hundred grams (200 g) of clean nylon 101 Zytel nylon beads and fifty grams (50 g) of dirty beads (by DuPont Canada, Mississauga, Ontario) were placed on the sample. The dirty beads were prepared by mixing ten grams (10 g) of AATCC TM-122 synthetic carpet soil (by Manufacturer Textile Innovators Corp. Windsor, N.C.) with one thousand grams (1000 g) of new Nylon 101 Zytel beads. Sixteen to seventeen hundred grams (1600-1700 g) of ceramic cylindrical shaped beads [110 to 130 ½″ diameter×½″ length small beads and twenty-five to thirty-five (25 to 35) ¾%″ diameter, ¾″ length (1.91 cm diameter, 1.91 cm length) large beads] were added into the Vetterman drum. The Vetterman drum was run for five hundred (500) cycles and the sample was removed.
The color of the sample was again measured and the color change versus the control value (delta E) owing to soiling was recorded. The sample was placed back in the drum, fifty grams (50 g) of soiled beads mixture was discarded and fifty grams (50 g) of new dirty beads were added into the drum. The procedure described above was repeated for three additional five hundred (500) cycle runs.
After a total of two thousand (2000) cycles, the color change versus the control value after vacuuming was measured and recorded. Samples with high number of delta E perform worse than samples with low delta E.
Soiling Test by Foot Traffic
Soiling performance test of foot traffic on loop carpets composed of the filaments of this invention was conducted. The test involved exposing the carpets to a significant amount of soil by an actual foot traffic test. Typical foot traffic levels ranged from 150,000 to 1,000,000 at a rate of about 100,000 to 200,000 traffics per week.
The dimensions of the carpet samples can vary. The width of the carpet sample is typically about six (6) feet in order to cover the width of corridor. The length of the carpet is typically in the range about twelve (12) to eighteen (18) inches, depending upon available number of samples. In this example, commercial level loop carpet measured twelve (12) inches×six (6) feet. The carpets were vacuumed prior to each measurement.
At every twelve (12) hours, reflectance measurements were made on the different carpet samples using a Minolta Chromagraph Meter CR-210 measuring device. The CR-210 is a compact tristimulus color analyzer for measuring reflected subject color. Color readings are taken at three (3) different areas on the carpet sample. The Chromagraph Meter calculates ΔE, color difference, for each reading.
ΔE color deviation represents total color difference. The equation assumes that color space is Euclides (three-dimensional) and calculated ΔE as the square root of the sum of the squares of the three components representing the difference between coordinates of the sample and the standard, as shown by the equation below:
ΔE=√{square root over ((ΔL*)2+(Δa*)2+(Δb*)2)}
where L* is a brightness variable, and a* and b* are chromaticity coordinates. When conducting soiling performance comparison test, it is important to test all of the samples at the same time and try to maintain the same floor location. Walk off mates are also used to prevent carpet samples closest to the corridor entrance from receiving an unduly amount of soil. This prevented bias in the testing. Test samples with low ΔE after foot traffic are considered to have better performances than the samples with high ΔE.
Spinning Process
In the following examples, Nylon 6,6 filaments having various cross-sections were produced. The nylon 6,6 filaments were spun from different spinnerets of the type shown in
The nylon 6,6 polymer used for all of the examples was a delustered polymer, meaning the polymer spin dope contained 0.15 weight percent of TiO2, and had a relative viscosity (RV) of sixty-eight plus/minus approximately three units (68, +/−˜3 units). The polymer temperature before the spinning pack was controlled at about two hundred eighty-five plus/minus one degree Centigrade (285, +/−1° C.). The spinning throughput was seventy pounds (70 lbs; 31.8 kg) per hour.
The polymer was extruded through the different spinnerets and divided into two (2) eighty filament (80) segments. The capillary dimensions for the spinnerets are described below. The molten fibers were then rapidly quenched in a chimney, where cooling air at about nine degrees Centigrade (˜9° C.) was blown past the filaments at three hundred cubic feet per minute (300 cfm; 8.49 cubic meter/min) through the quench zone. The filaments were then coated with a lubricant at eight hundred yards per minute (800 yds./min; 731.52 m/min) for drawing and crimping. The coated yarns were drawn at 2197 yards per minute (2009 m/min and 2.75× draw ratio) using a pair of heated draw rolls. The draw roll temperature was one hundred ninety degrees Centigrade (190° C.). The filaments were then forwarded into a dual-impingement bulking jet (210° C. hot air) similar to that described in U.S. Pat. No. 3,525,134 to form two (2) nine hundred and ninety-five denier (995 denier; 1106 decitex), and 12.5 denier per filament (dpf) yarns (13.9 decitex per filament).
The spun, drawn, and crimped bulked continuous filament (BCF) yarns were cable-twisted to 5.0 turns per inch (tpi) on a cable twister and heat-set on a Superba heat-setting machine at setting temperature of two hundred sixty-five degrees Farenheit (265° F.; 129.4° C.).
The test yarns were then tufted into fifty-five ounce per square yard (55 oz/sq.yd; 1865 g/sq.meter) having 0.625 inch (⅝″; 1.59 cm) pile height cut pile carpets on a 1/10 inch gauge (0.254 cm) tufting machine. The tufted carpets were dyed on a continuous range dyer into wool-beige color carpets. The carpet aesthetics were assessed by a panel of experts. They were also subjected to soling tests in Vetterman drum.
Filaments having a wavy trilobal cross-section (U.S. Pat. No. 5,108,838), as shown in
Filaments having a hexalobal cross section according to the invention, as shown in
Table 1 presents the magnitudes of the various dimensions A1, A2, A3, B1, B2, B3, and D of major legs shown in
Filaments having a hexalobal cross section according to the invention, as shown in
The carpets produced using the above filaments were subjected to soiling test in a Vetterman drum as described earlier. The soiling performance was judged by delta E measurements. Carpet samples with low delta E are considered to be better soiling performers, i.e., having better anti-soiling performance, than high delta E carpets. Reducing delta E by one or more unit is considered to be a significant improvement.
The carpet samples were also assessed by a panel of experts for luster and glitter. Carpets without any glitter are more desirable than carpets with high glitter. All natural fibers have no objectionable glitter. The test results are summarized below in Table 3.
Spinning Process
In the following examples, Nylon 6,6 filaments having various cross-sections were produced. The nylon 6,6 filaments were spun from different spinnerets as shown in
The nylon 6,6 polymer used for all of the examples was a delustered polymer, meaning that the polymer contained 0.2 weight percent of TiO2, and had a relative viscosity (RV) of sixty-eight plus/minus approximately three units (68, +/−˜3 units). The polymer temperature before the spinning pack was controlled at about two hundred eighty-six plus/minus one degree Centigrade (286, +/−1° C.). The spinning throughput was seventy pounds five (75 lbs; 34.1 kg) per hour.
The polymer was extruded through the different spinnerets and divided into two (2) sixty-four filament (64) segments. The molten fibers were then rapidly quenched in a chimney, where cooling air at about nine degrees Centigrade (˜9° C.) was blown past the filaments at three hundred cubic feet per minute (300 cfm; 8.49 cubic meter/min) through the quench zone. The filaments were then coated with a lubricant at seven hundred and fifteen yards per minute (715 yds./min; 654 m/min) for drawing and crimping. The coated yarns were drawn at 1930 yards per minute (111 m/min and 2.75× draw ratio) using a pair of heated draw rolls. The draw roll temperature was one hundred ninety degrees Centigrade (190° C.). The filaments were then forwarded into a dual-impingement bulking jet (230° C. hot air) similar to that described in Coon, U.S. Pat. No. 3,525,134, to form two (2) twelve hundred and forty-five denier (1245 denier; 1385 decitex), and 19 denier per filament (dpf) yarns (21.1 decitex per filament).
Carpet for the anti-soiling test were prepared by cable-twisting to 4.5 turns per inch (tpi) on a cable twister and heat-set on a Supreba heat-setting machine at setting temperature of two hundred sixty-five Fahrenheit (265° F.; 129.4° C.).
These test yarns were then tufted into thirty-two ounces per square yard (32 oz/sq.yd; 1085 g/sq.meter) having 0.25 inch ( 8/32″; 0.635 cm) pile height cut pile carpets on a 1/10 inch gauge (0.254 cm) tufting machine. The tufted carpets were dyed in a beck dyer into beige color carpets of approximately L*=71.
Carpet samples for the printing test were prepared by cable-twisting to 4.8 turns per inch (tpi) on a cable twister and heat-set on a Supreba heat-setting machine at setting temperature of two hundred sixty-five Fahrenheit (265° F.; 129.4° C.).
These test yarns were then tufted into thirty-six ounces per square yard (36 oz/sq.yd; 1221 g/sq.meter) having 0.31 inch ( 5/16″; 0.794 cm) pile height cut pile carpets on a 1/10 inch gauge (0.254 cm) tufting machine.
Filaments having a trilobal cross section as shown in
Filaments having a hexalobal cross section according to the invention as shown in
Filaments having a hexalobal cross section according to the invention as shown in
Filaments having a trilobal cross section as shown in
Examples 4-6 were converted into 1/10 inch gauge, ¼ inch pile height, 32 ounces loop pile carpets and dyed individually to a light beige (L*≈71) color. Anti-soiling tests were performed on these samples using foot traffic. The soiling data are listed in Table 4.
Examples 5-7 were converted into 1/10 inch gauge, 5/16 inch pile height, 36 ounces per square yard cut piles carpets. The carpet samples were treated with steam and printed on a Chromojet printer into multicolor patterned carpet. All carpet samples received the same amount of dyes. The printed carpets were then treated with steam to fix the dyes, and rinsed thoroughly with water to remove unused dyes. A Minolta colorimeter was used to measure the color depth (L* value) of carpet (beige section only). Carpet with low L* value have darker color than carpets with print quality. The rest results are listed in Table 5.
This application claims the benefit of U.S. Provisional Application No. 60/742,706 filed 6 Dec. 2005.
| Number | Date | Country | |
|---|---|---|---|
| 60742706 | Dec 2005 | US |