High efficiency optical devices

Information

  • Patent Grant
  • 6210785
  • Patent Number
    6,210,785
  • Date Filed
    Wednesday, December 15, 1999
    24 years ago
  • Date Issued
    Tuesday, April 3, 2001
    23 years ago
Abstract
Optical devices such as light pipes which incorporate multilayer optical films in which the refractive indices of two adjacent layers in the thickness direction are substantially matched or are small relative to the difference in refractive indices of said two adjacent layers in an given in-plane direction which is at least 0.05. The multilayer optical film exhibits low absorptivity and can reflect light approaching at shallow angles as well as normal to the film.
Description




FIELD OF THE INVENTION




The present invention relates to the field of optical devices. More particularly, the present invention relates to optical devices employing multi-layer optical film as reflectors and/or polarizers.




BACKGROUND OF THE INVENTION




Optical devices employing reflectors are used, for example, in displays for laptop computers, hand-held calculators, digital watches and similar devices as well as illuminated signs, light pipes, backlight assemblies and many other devices.




Conventional reflectors, including pigmented surfaces, silvered mirrors, polished metallic or metallized surfaces, etc. suffer from a number of disadvantages in many applications. The conventional reflectors suffer from relatively high absorbance of light incident on their surfaces, typically absorbing about 4-10% of the light incident on them. As a result, the amount of light remaining after each reflection is less than that initially provided. In devices in which multiple reflections are encountered, the overall output of the optical device can be substantially limited. In addition, many of the conventional reflectors are too bulky and/or heavy for many of the applications, particularly in laptop computer displays and other portable devices.




Many optical devices use polarizers, either alone or in combination with reflectors, to provide light having substantially one plane of polarization. Polarized light is especially useful in conjunction with liquid crystal (LC) displays used in many portable devices such as laptop computers and watches, because the LC displays rely on polarized light passing through the LC to display information to a viewer.




Polarizers can be generally categorized as either absorptive or reflective. Typical absorptive polarizers are oriented dyed polymer films, while typical reflective polarizers are tilted thin film polarizers, also known as MacNeille polarizers. Absorptive polarizers do, of course, contribute to the absorptive losses of optical devices in which they are used, thereby limiting the output of those devices.




The absorptive losses of known reflectors and polarizers become much more important when the optical devices are used with a brightness enhancement film such as micro-replicated brightness enhancement film or any other type of reflective polarizer which causes light to typically travel through several reflections, thereby amplifying absorptive losses with every reflection. In the highest gain configurations, for, e.g., a single sheet of brightness enhancement film in combination with a reflective polarizer and back reflector, or two sheets of orthogonally crossed sheets of brightness enhancement film, the effective absorptive losses can reduce the total potential light output of an optical display by 10-30%.




This principle of absorptive losses also applies to optical devices employing non-totally internally reflecting surfaces. One example is an optical wedge in which light is directed into a structure having converging reflective surfaces. Optical wedges will typically reflect light many times before it exits the device. With each reflection, however, some of the light which entered the wedge is absorbed by conventional reflectors. As a result, the amount of light exiting the device is typically substantially less than the light entering the device.




Another optical device typically employing reflective surfaces is an illuminated sign which relies on a finite number of light sources and multiple reflections within an optical cavity to disperse the light to illuminate the surface of a sign in a generally uniform manner. To overcome the problems associated with absorptive losses, many signs typically employ numerous light sources, thereby increasing the cost to manufacture and operate the signs.




Yet another optical device which is limited by absorption losses is a light pipe in which light enters the pipe and is reflected along its length numerous times before exiting at a desired location. Each reflection results in some absorption when conventional reflectors are used, thereby limiting throughput of the light pipe.




To overcome some of the problems of weight, bulk and absorption of conventional reflectors, multi-layered polymer films have been used to reflect and/or polarize light. Such polymeric films are, however, subject to a number of other disadvantages including iridescence, as well as poor reflectivity when off-axis light approaches the surface of the film. The off-axis light is typically transmitted through the films, rather than being reflected, thereby resulting in transmissive losses rather than absorptive losses. Whether light is lost through absorption or transmission, however, the output of the optical device is limited.




Other problems with known multi-layer polymer films used to provide reflectors and/or polarizers is that the materials and methods used to manufacture the films presents serious problems due to poor optical transmission, extrudibility, and high costs.




SUMMARY OF THE INVENTION




Optical devices according to the present invention include a multilayer optical film. Optical devices incorporating multilayer optical film according to the present invention enjoy many advantages due to the low absorptivity of the film and its ability to reflect light approaching at shallow angles as well as normal to the film.




In those situations where complete reflectivity is desired, optical devices employing a multilayer optical film according to the present invention can reflect over 99% of the light striking the surface of the film.




If a reflective polarizer is desired, the optical devices can be constructed with a multilayer optical film which transmits a significant amount of light having one plane of polarization while reflecting a significant amount of light having an orthogonally oriented polarization. A further advantage is that the relative percentages of transmitted/reflected light can be largely controlled by the multilayer optical film used in the present invention.




As a result of the unique properties of the multilayer optical film, optical devices according to the present invention are highly efficient at reflecting and transporting light and/or transmitting light of one polarization, whether the light is incident normal to the film surface or off-axis.




Another advantage of optical devices employing multilayer optical film according to the present invention which rely on reflection to transport light is that the devices need not have symmetry to reduce the number of reflections needed to transmit light due to the low absorptivity of the multilayer optical film.




Yet another advantage of optical devices employing multilayer optical films according to the present invention is their relatively low weight as compared to many conventional reflectors and/or polarizers.




Still another advantage of optical devices employing multilayer optical films according to the present invention is that because the film is relatively thin as compared to many conventional reflectors and/or polarizers, the optical devices can be manufactured to occupy limited space in a system employing the device.




Additional features and advantages of optical devices according to the present invention will be apparent upon reading the detailed description of illustrative embodiments below.











BRIEF DESCRIPTION OF THE DRAWINGS





FIGS. 1



a


and


1




b


are diagrammatical views of the multilayer optical film of the present invention.





FIG. 2

depicts a two layer stack of films forming a single interface.





FIGS. 3-6

,


7


A and


7


B depict the optical performance of multilayer optical films described in Examples 1-5.





FIG. 8

is a graphical representation illustrating the relationship between the number of reflections experienced by a ray of light (x-axis) as compared to the relative intensity of the light ray (y-axis) for reflective surfaces made of multilayer optical film and a standard reflector.





FIG. 9

is schematic cross-sectional diagram of an alternate optical device according to the present invention.





FIG. 10

is a perspective view of the optical device of

FIG. 9

in which at least one surface of the device is intended to display a message.





FIG. 11

is a schematic cross-sectional diagram of a converging wedge optical device according to the present invention.





FIG. 12

is a schematic cross-sectional diagram of a diverging wedge optical device according to the present invention.





FIG. 13

is a schematic cross-sectional diagram of a light pipe employing multilayer optical films according to the present invention.





FIG. 14

is a schematic cross-sectional diagram of the device of

FIG. 13

, taken along a plane transverse to the longitudinal axis of the light pipe.





FIG. 15

is a perspective view of one illustrative optical device constructed using multilayer optical films according to the present invention.











DETAILED DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS OF THE INVENTION




I. Multilayer Optical Film




The optical devices described herein rely on the unique and advantageous properties of multilayer optical films. The advantages, characteristics and manufacturing of such films are most completely described in U.S. Pat. No. 5,882,774, which is incorporated herein by reference. The multilayer optical film is useful, for example, as highly efficient mirrors and/or polarizers. A relatively brief description of the properties and characteristics of the multilayer optical film is presented below followed by a description of illustrative embodiments of backlight systems using the multilayer optical film according to the present invention.




Multilayer optical films as used in conjunction with the present invention exhibit relatively low absorption of incident light, as well as high reflectivity for off-axis as well as normal light rays. These properties generally hold whether the films are used for pure reflection or reflective polarization of light. The unique properties and advantages of the multi-layer optical film provides an opportunity to design highly efficient backlight systems which exhibit low absorption losses when compared to known backlight systems.




An exemplary multilayer optical film of the present invention as illustrated in

FIGS. 1A and 1B

includes a multilayer stack


10


having alternating layers of at least two materials


12


and


14


. At least one of the materials has the property of stress induced birefringence, such that the index of refraction (n) of the material is affected by the stretching process.

FIG. 1A

shows an exemplary multilayer stack before the stretching process in which both materials have the same index of refraction. Light ray


13


experiences no index of refraction change and passes through the stack. In

FIG. 1B

, the same stack has been stretched, thus increasing the index of refraction of material


12


. The difference in refractive index at each boundary between layers will cause part of ray


15


to be reflected. By stretching the multilayer stack over a range of uniaxial to biaxial orientation, a film is created with a range of reflectivities for differently oriented plane-polarized incident light. The multilayer stack can thus be made useful as reflective polarizers or mirrors.




Multilayer optical films constructed according to the present invention exhibit a Brewster angle (the angle at which reflectance goes to zero for light incident at any of the layer interfaces) which is very large or is nonexistent. In contrast, known multilayer polymer films exhibit relatively small Brewster angles at layer interfaces, resulting in transmission of light and/or undesirable iridescence. The multilayer optical films according to the present invention, however, allow for the construction of mirrors and polarizers whose reflectivity for p polarized light decrease slowly with angle of incidence, are independent of angle of incidence, or increase with angle of incidence away from the normal. As a result, multilayer stacks having high reflectivity for both s and p polarized light over a wide bandwidth, and over a wide range of angles can be achieved.





FIG. 2

shows two layers of a multilayer stack, and indicates the three dimensional indices of refraction for each layer. The indices of refraction for each layer are n1x, n1y, and n1z for layer


102


, and n2x, n2y, and n2z for layer


104


. The relationships between the indices of refraction in each film layer to each other and to those of the other layers in the film stack determine the reflectance behavior of the multilayer stack at any angle of incidence, from any azimuthal direction. The principles and design considerations described in U.S. Pat. No. 5,882,774 can be applied to create multilayer stacks having the desired optical effects for a wide variety of circumstances and applications. The indices of refraction of the layers in the multilayer stack can be manipulated and tailored to produce the desired optical properties.




Referring again to

FIG. 1B

, the multilayer stack


10


can include tens, hundreds or thousands of layers, and each layer can be made from any of a number of different materials. The characteristics which determine the choice of materials for a particular stack depend upon the desired optical performance of the stack. The stack can contain as many materials as there are layers in the stack. For ease of manufacture, preferred optical thin film stacks contain only a few different materials.




The boundaries between the materials, or chemically identical materials with different physical properties, can be abrupt or gradual. Except for some simple cases with analytical solutions, analysis of the latter type of stratified media with continuously varying index is usually treated as a much larger number of thinner uniform layers having abrupt boundaries but with only a small change in properties between adjacent layers.




The preferred multilayer stack is comprised of low/high index pairs of film layers, wherein each low/high index pair of layers has a combined optical thickness of ½ the center wavelength of the band it is designed to reflect. Stacks of such films are commonly referred to as quarterwave stacks. For multilayer optical films concerned with the visible and the near infrared wavelengths, a quarterwave stack design results in each of the layers in the multilayer stack having an average thickness of not more than 0.5 microns.




In those applications where reflective films (e.g. mirrors) are desired, the desired average transmission for light of each polarization and plane of incidence generally depends upon the intended use of the reflective film. One way to produce a multilayer mirror film is to biaxially stretch a multilayer stack which contains a birefringent material as the high index layer of the low/high index pair. For a high efficiency reflective film, average transmission along each stretch direction at normal incidence over the visible spectrum (400-700nm) is desirably less than 10% (reflectance greater than 90%), preferably less than 5% (reflectance greater than 95%), more preferably less than 2% (reflectance greater than 98%), and even more preferably less than 1% (reflectance greater than 99%). The average transmission at 60 degrees from the normal from 400-700 nm is desirably less than 20% (reflectance greater than 80%), preferably less than 10% (reflectance greater than 90%), more preferably less than 5% (reflectance greater than 95%), and even more preferably less than 2% (reflectance greater than 98%), and even more preferably less than 1% (reflectance greater than 99%).




In addition, asymmetric reflective films may be desirable for certain applications. In that case, average transmission along one stretch direction may be desirably less than, for example, 50%, while the average transmission along the other stretch direction may be desirably less than, for example 20%, over a bandwidth of, for example, the visible spectrum (400-700 nm), or over the visible spectrum and into the near infrared (e.g, 400-850 nm).




Multilayer optical films can also be designed to operate as reflective polarizers. One way to produce a multilayer reflective polarizer is to uniaxially stretch a multilayer stack which contains a birefringent material as the high index layer of the low/high index pair. The resulting reflective polarizers have high reflectivity for light with its plane of polarization parallel to one axis (in the stretch direction) for a broad range of angles of incidence, and simultaneously have low reflectivity and high transmissivity for light with its plane of polarization parallel to the other axis (in the non-stretch direction) for a broad range of angles of incidence. By controlling the three indices of refraction of each film, nx, ny and nz, the desired polarizer behavior can be obtained.




For many applications, the ideal reflecting polarizer has high reflectance along one axis (the so-called extinction axis) and zero reflectance along the other (the so-called transmission axis), at all angles of incidence. For the transmission axis of a polarizer, it generally desirable to maximize transmission of light polarized in the direction of the transmission axis over the bandwidth of interest and also over the range of angles of interest.




The average transmission at normal incidence for a polarizer in the transmission axis across the visible spectrum (400-700 nm for a bandwidth of 300 nm) is desirably at least 50%, preferably at least 70%, more preferably at least 85%, and even more preferably at least 90%. The average transmission at 60 degrees from the normal (measured along the transmission axis for p-polarized light) for a polarizer from 400-700 nm is desirably at least 50%, preferably at least 70%, more preferably at least 80%, and even more preferably at least 90%.




The average transmission for a multilayer reflective polarizer at normal incidence for light polarized in the direction of the extinction axis across the visible spectrum (400-700 nm for a bandwidth of 300 nm) is desirably at less than 50%, preferably less than 30%, more preferably less than 15%, and even more preferably less than 5%. The average transmission at 60 degrees from the normal (measured along the transmission axis for p-polarized light) for a polarizer for light polarized in the direction of the extinction axis from 400-700 nm is desirably less than 50%, preferably less than 30%, more preferably less than 15%, and even more preferably less than 5%.




For certain applications, high reflectivity for p-polarized light with its plane of polarization parallel to the transmission axis at off-normal angles are preferred. The average reflectivity for light polarized along the transmission axis should be more than 20% at an angle of at least 30 degrees from the normal.




In addition, although reflective polarizing films and asymmetric reflective films are discussed separately herein, it should be understood that two or more of such films could be provided to reflect substantially all light incident on them (provided they are properly oriented with respect to each other to do so). This construction is typically desired when the multilayer optical film is used as a reflector in a backlight system according to the present invention.




If some reflectivity occurs along the transmission axis, the efficiency of the polarizer at off-normal angles may be reduced. If the reflectivity along the transmission axis is different for various wavelengths, color may be introduced into the transmitted light. One way to measure the color is to determine the root mean square (RMS) value of the transmissivity at a selected angle or angles over the wavelength range of interest.







C
RMS

=




λ1
λ2





(


(

T
-

T
_


)

2

)


1
/
2









λ





T
_



(

λ2
-
λ1

)













where the range λ1 to λ2 is the wavelength range, or bandwidth, of interest, T is the transmissivity along the transmission axis, and T is the average transmissivity along the transmission axis in the wavelength range of interest. For applications where a low color polarizer is desirable, the % RMS color should be less than 10%, preferably less than 8%, more preferably less than 3.5%, and even more preferably less than 2% at an angle of at least 30 degrees from the normal, preferably at least 45 degrees from the normal, and even more preferably at least 60 degrees from the normal.




Preferably, a reflective polarizer combines the desired % RMS color along the transmission axis for the particular application with the desired amount of reflectivity along the extinction axis across the bandwidth of interest. For polarizers having a bandwidth in the visible range (400-700 nm, or a bandwidth of 300 nm), average transmission along the extinction axis at normal incidence is desirably less than 40%, more desirably less than 25%, preferably less than 15%, more preferably less than 5% and even more preferably less than 3%.




Materials Selection and Processing




With the design considerations described in the above mentioned U.S. Pat. No. 5,882,774, one of ordinary skill will readily appreciate that a wide variety of materials can be used to form multilayer reflective films or polarizers according to the invention when processed under conditions selected to yield the desired refractive index relationships. The desired refractive index relationships can be achieved in a variety of ways, including stretching during or after film formation (e.g., in the case of organic polymers), extruding (e.g., in the case of liquid crystalline materials), or coating. In addition, it is preferred that the two materials have similar rheological properties (e.g., melt viscosities) such that they can be co-extruded.




In general, appropriate combinations may be achieved by selecting, as the first material, a crystalline or semi-crystalline material, preferably a polymer. The second material, in turn, may be crystalline, semi-crystalline, or amorphous. The second material may have a birefringence opposite of the first material. Or, the second material may have no birefringence, or less birefringence than the first material.




Specific examples of suitable materials include polyethylene naphthalate (PEN) and isomers thereof (e.g., 2,6-, 1,4-, 1,5-, 2,7-, and 2,3-PEN), polyalkylene terephthalates (e.g., polyethylene terephthalate, polybutylene terephthalate, and poly-1,4-cyclohexanedimethylene terephthalate), polyimides (e.g., polyacrylic imides), polyetherimides, atactic polystyrene, polycarbonates, polymethacrylates (e.g., polyisobutyl methacrylate, polypropylmethacrylate, polyethylmethacrylate, and polymethylmethacrylate), polyacrylates (e.g., polybutylacrylate and polymethylacrylate), syndiotactic polystyrene (sPS), syndiotactic poly-alpha-methyl styrene, syndiotactic polydichlorostyrene, copolymers and blends of any of these polystyrenes, cellulose derivatives (e.g., ethyl cellulose, cellulose acetate, cellulose propionate, cellulose acetate butyrate, and cellulose nitrate), polyalkylene polymers (e.g., polyethylene, polypropylene, polybutylene, polyisobutylene, and poly(4-methyl)pentene), fluorinated polymers (e.g., perfluoroalkoxy resins, polytetrafluoroethylene, fluorinated ethylene-propylene copolymers, polyvinylidene fluoride, and polychlorotrifluoroethylene), chlorinated polymers (e.g., polyvinylidene chloride and polyvinylchloride), polysulfones, polyethersulfones, polyacrylonitrile, polyamides, silicone resins, epoxy resins, polyvinylacetate, polyether-amides, ionomeric resins, elastomers (e.g., polybutadiene, polyisoprene, and neoprene), and polyurethanes. Also suitable are copolymers, e.g., copolymers of PEN (e.g., copolymers of 2,6-, 1,4-, 1,5-, 2,7-, and/or 2,3-naphthalene dicarboxylic acid, or esters thereof, with (a) terephthalic acid, or esters thereof; (b) isophthalic acid, or esters thereof; (c) phthalic acid, or esters thereof; (d) alkane glycols; (e) cycloalkane glycols (e.g., -cyclohexane dimethane diol); (f) alkane dicarboxylic acids; and/or (g) cycloalkane dicarboxylic acids (e.g., cyclohexane dicarboxylic acid)), copolymers of polyalkylene terephthalates (e.g., copolymers of terephthalic acid, or esters thereof, with (a) naphthalene dicarboxylic acid, or esters thereof; (b) isophthalic acid, or esters thereof; (c) phthalic acid, or esters thereof; (d) alkane glycols; (e) cycloalkane glycols (e.g., cyclohexane dimethane diol); (f) alkane dicarboxylic acids; and/or (g) cycloalkane dicarboxylic acids (e.g., cyclohexane dicarboxylic acid)), and styrene copolymers (e.g., styrene-butadiene copolymers and styrene-acrylonitrile copolymers), 4,4′-bibenzoic acid and ethylene glycol. In addition, each individual layer may include blends of two or more of the above-described polymers or copolymers (e.g., blends of sPS and atactic polystyrene). The coPEN described may also be a blend of pellets where at least one component is a polymer based on naphthalene dicarboxylic acid and other components are other polyesters or polycarbonates, such as a PET, a PEN or a co-PEN.




Particularly preferred combinations of layers in the case of polarizers include PEN/co-PEN, polyethylene terephthalate (PET)/co-PEN, PEN/sPS, PET/sPS, PEN/EASTAR, and PET/EASTAR, where “co-PEN” refers to a copolymer or blend based upon naphthalene dicarboxylic acid (as described above) and EASTAR is polycyclohexanedimethylene terephthalate commercially available from Eastman Chemical Co.




Particularly preferred combinations of layers in the case of reflective films include PET/ECDEL, PEN/ECDEL, PEN/sPS, PEN/THV, PEN/co-PET, and PET/sPS, where “co-PET” refers to a copolymer or blend based upon terephthalic acid (as described above), ECDEL is a thermoplastic polyester commercially available from Eastman Chemical Co., and THV is a fluoropolymer commercially available from Minnesota Mining and Manufacturing Company, St. Paul, Minn.




The number of layers in the film is selected to achieve the desired optical properties using the minimum number of layers for reasons of film thickness, flexibility and economy. In the case of both polarizers and reflective films, the number of layers is preferably less than 10,000, more preferably less than 5,000, and even more preferably less than 2,000.




As discussed above, the ability to achieve the desired relationships among the various indices of refraction (and thus the optical properties of the multilayer film) is influenced by the processing conditions used to prepare the multilayer film. In the case of organic polymers which can be oriented by stretching, the films are generally prepared by co-extruding the individual polymers to form a multilayer film and then orienting the film by stretching at a selected temperature, optionally followed by heat-setting at a selected temperature. Alternatively, the extrusion and orientation steps may be performed simultaneously. In the case of polarizers, the film is stretched substantially in one direction (uniaxial orientation), while in the case of reflective films the film is stretched substantially in two directions (biaxial orientation).




The film may be allowed to dimensionally relax in the cross-stretch direction from the natural reduction in cross-stretch (equal to the square root of the stretch ratio); it may simply be constrained to limit any substantial change in cross-stretch dimension; or it may be actively stretched in the cross-stretch dimension. The film may be stretched in the machine direction, as with a length orienter, or in width using a tenter.




The pre-stretch temperature, stretch temperature, stretch rate, stretch ratio, heat set temperature, heat set time, heat set relaxation, and cross-stretch relaxation are selected to yield a multilayer film having the desired refractive index relationship. These variables are inter-dependent; thus, for example, a relatively low stretch rate could be used if coupled with, e.g., a relatively low stretch temperature. It will be apparent to one of ordinary skill how to select the appropriate combination of these variables to achieve the desired multilayer film. In general, however, a stretch ratios in the range from 1:2 to 1:10 (more preferably 1:3 to 1:7) in the stretch direction and from 1:0.2 to 1:10 (more preferably from 1:0.3 to 1:7) orthogonal to the stretch direction is preferred.




Suitable multilayer films may also be prepared using techniques such as spin coating (e.g., as described in Boese et al., J. Polym. Sci.: Part B, 30:1321 (1992) for birefringent polyimides, and vacuum deposition (e.g., as described by Zang et. al., Appl. Phys. Letters, 59:823 (1991) for crystalline organic compounds; the latter technique is particularly useful for certain combinations of crystalline organic compounds and inorganic materials. Exemplary multilayer reflective mirror films and multilayer reflective polarizers will now be described in the following examples.




EXAMPLE 1




(PEN:THV 500, 449, Mirror)




A coextruded film containing 449 layers was made by extruding the cast web in one operation and later orienting the film in a laboratory film-stretching apparatus. A Polyethylene naphthalate (PEN) with an Intrinsic Viscosity of 0.53 dVg (60 wt. % phenoV40 wt. % dichlorobenzene) was delivered by one extruder at a rate of 56 pounds per hour and THV 500 (a fluoropolymer available from Minnesota Mining and Manufacturing Company) was delivered by another extruder at a rate of 11 pounds per hour. The PEN was on the skin layers and 50% of the PEN was present in the two skin layers. The feedblock method was used to generate 57 layers which was passed through three multipliers producing an extrudate of 449 layers. The cast web was 20 mils thick and 12 inches wide. The web was later biaxially oriented using a laboratory stretching device that uses a pantograph to grip a square section of film and simultaneously stretch it in both directions at a uniform rate. A 7.46 cm square of web was loaded into the stretcher at about 100° C. and heated to 140° C. in 60 seconds. Stretching then commenced at 10%/sec (based on original dimensions) until the sample was stretched to about 3.5×3.5. Immediately after the stretching the sample was cooled by blowing room temperature air at it.





FIG. 3

shows the transmission of this multilayer film. Curve (a) shows the response at normal incidence, while curve (b) shows the response at 60 degrees for p-polarized light.




EXAMPLE 2




(PEN:PMMA 601, Mirror)




A coextruded film containing 601 layers was made on a sequential flat-film-making line via a coextrusion process. Polyethylene Naphthalate (PEN) with an Intrinsic Viscosity of 0.57 dl/g (60 wt. % phenoV40 wt. % dichlorobenzene) was delivered by extruder A at a rate of 114 pounds per hour with 64 pounds per hour going to the feedblock and the rest going to skin layers described below. PMMA (CP-82 from ICI of Americas) was delivered by extruder B at a rate of 61 pounds per hour with all of it going to the feedblock. PEN was on the skin layers of the feedblock. The feedblock method was used to generate 151 layers using the feedblock such as those described in U.S. Pat. No. 3,801,429, after the feedblock two symmetric skin layers were coextruded using extruder C metering about 30 pounds per hour of the same type of PEN delivered by extruder A. This extrudate passed through two multipliers producing an extrudate of about 601 layers. U.S. Pat. No. 3,565,985 describes similar coextrusion multipliers. The extrudate passed through another device that coextruded skin layers at a total rate of 50 pounds per hour of PEN from extruder A. The web was length oriented to a draw ratio of about 3.2 with the web temperature at about 280° F. The film was subsequently preheated to about 310° F. in about 38 seconds and drawn in the transverse direction to a draw ratio of about 4.5 at a rate of about 11% per second. The film was then heat-set at 440° F. with no relaxation allowed. The finished film thickness was about 3 mil.




As seen in

FIG. 4

, curve (a), the bandwidth at normal incidence is about 350 nm with an average in-band extinction of greater than 99%. The amount of optical absorption is difficult to measure because of its low value, but is less than 1%. At an incidence angle of 50° from the normal both s (curve (b)) and p-polarized (curve (c)) light showed similar extinctions, and the bands were shifted to shorter wavelengths as expected. The red band-edge for s-polarized light is not shifted to the blue as much as for p-polarized light due to the expected larger bandwidth for s-polarized light, an due to the lower index seen by the p-polarized light in the PEN layers.




EXAMPLE 3




(PEN:PCTG, 449, Polarizer)




A coextruded film containing 481 layers was made by extruding the cast web in one operation and later orienting the film in a laboratory film-stretching apparatus. The feedblock method was used with a 61 layer feedblock and three (2×) multipliers. Thick skin layers were added between the final multiplier and the die. Polyethylene naphthalate (PEN) with an intrinsic viscosity of 0.47 dl/g (60 wt. % phenol/40 wt. % dichlorobenzene) was delivered to the feedblock by one extruder at a rate of 25.0 pounds per hour. Glycol modified polyethylene dimethyl cyclohexane terephthalate (PCTG 5445 from Eastman) was delivered by another extruder at a rate of 25.0 pounds per hour. Another stream of PEN from the above extruder was added as skin layers after the multipliers at a rate of 25.0 pounds per hour. The cast web was 0.007 inches thick and 12 inches wide. The web was layer uniaxially oriented using a laboratory stretching device that uses a pantograph to grip a section of film and stretch it in one direction at a uniform rate while it is allowed to freely relax in the other direction. The sample of web loaded was about 5.40 cm wide (the unconstrained direction) and 7.45 cm long between the grippers of the pantograph. The web was loaded into the stretcher at about 100° C. and heated to 135° C. for 45 seconds. Stretching was then commenced at 20%/second (based on original dimensions) until the sample was stretched to about 6:1 (based on gripper to gripper measurements). Immediately after stretching, the sample was cooled by blowing room temperature air at it. In the center, the sample was found to relax by a factor of 2.0.





FIG. 5

shows the transmission of this multilayer film where curve a shows transmission of light polarized in the non-stretch direction at normal incidence, curve b shows transmission of p-polarized light polarized in the non-stretched direction at 60° incidence, and curve c shows the transmission of light polarized in the stretch direction at normal incidence. Average transmission for curve a from 400-700nm is 89.7%, average transmission for curve b from 400-700nm is 96.9%, and average transmission for curve c from 400-700nm is 4.0%. % RMS color for curve a is 1.05%, and %RMS color for curve b is 1.44%.




EXAMPLE 4




(PEN:CoPEN, 601, Polarizer)




A coextruded film containing 601 layers was made on a sequential flat-film-making line via a coextrusion process. A Polyethylene naphthalate (PEN) with an intrinsic viscosity of 0.54 dl/g (60 wt % Phenol plus 40 wt % dichlorobenzene) was delivered by on extruder at a rate of 75 pounds per hour and the coPEN was delivered by another extruder at 65 pounds per hour. The coPEN was a copolymer of 70 mole % 2,6 naphthalene dicarboxylate methyl ester, 15% dimethyl isophthalate and 15% dimethyl terephthalate with ethylene glycol. The feedblock method was used to generate 151 layers. The feedblock was designed to produce a stack of films having a thickness gradient from top to bottom, with a thickness ratio of 1.22 from the thinnest layers to the thickest layers. The PEN skin layers were coextruded on the outside of the optical stack with a total thickness of 8% of the coextruded layers. The optical stack was multiplied by two sequential multipliers. The nominal multiplication ratio of the multipliers were 1.2 and 1.27, respectively. The film was subsequently preheated to 310° F. in about 40 seconds and drawn in the transverse direction to a draw ratio of about 5.0 at a rate of 6% per second. The finished film thickness was about 2 mils.





FIG. 6

shows the transmission for this multilayer film. Curve a shows transmission of light polarized in the non-stretch direction at normal incidence, curve b shows transmission of p-polarized light at 60° incidence, and curve c shows transmission of light polarized in the stretch direction at normal incidence. Note the very high transmission of p-polarized light in the non-stretch direction at both normal and 60° incidence (80-100%). Also note the very high reflectance of light polarized in the stretched direction in the visible range (400-700nm) shown by curve c. Reflectance is nearly 99% between 500 and 650nm.




EXAMPLE 5




(PEN:sPS, 481, Polarizer)




A 481 layer multilayer film was made from a polyethylene naphthalate (PEN) with an intrinsic viscosity of 0.56 dl/g measured in 60 wt. % phenol and 40 wt % dichlorobenzene purchased from Eastman Chemicals and a syndiotactic polystyrene (sPS) homopolymer (weight average molecular weight 200,000 Daltons, sampled from Dow Corporation). The PEN was on the outer layers and was extruded at 26 pounds per hour and the sPS at 23 pounds per hour. The feedblock used produced 61 layers with each of the 61 being approximately the same thickness. After the feedblock three (2×) multipliers were used. Equal thickness skin layers containing the same PEN fed to the feedblock were added after the final multiplier at a total rate of 22 pounds per hour. The web was extruded through a 12″ wide die to a thickness of about 0.011 inches (0.276 mm). The extrusion temperature was 290° C.




This web was stored at ambient conditions for nine days and then uniaxially oriented on a tenter. The film was preheated to about 320° F. (160° C.) in about 25 seconds and drawn in the transverse direction to a draw ratio of about 6:1 at a rate of about 28% per second. No relaxation was allowed in the stretched direction. The finished film thickness was about 0.0018 inches (0.046 mm).





FIG. 7

shows the optical performance of this PEN:sPS reflective polarizer containing 481 layers. Curve a shows transmission of light polarized in the non-stretch direction at normal incidence, curve b shows transmission of p-polarized light at 60° incidence, and curve c shows transmission of light polarized in the stretch direction at normal incidence. Note the very high transmission of p-polarized light at both normal and 60° incidence. Average transmission for curve a over 400-700 nm is 86.2%, the average transmission for curve b over 400-700 nm is 79.7%. Also note the very high reflectance of light polarized in the stretched direction in the visible range (400-700nm) shown by curve c. The film has an average transmission of 1.6% for curve c between 400 and 700 nm. The % RMS color for curve a is 3.2%, while the % RMS color for curve b is 18.2%.




EXAMPLE 6




(PEN:coPEN, 603, Polarizer)




A reflecting polarizer comprising 603 layers was made on a sequential flat-film making line via a coextrusion process. A polyethylene naphthalate (PEN) with an intrinsic viscosity of 0.47 dl/g (in 60 wt % phenol plus 40 wt % dichlorobenzene) was delivered by an extruder at a rate of 83 pounds (38 kg) per hour and the CoPEN was delivered by another extruder at 75 pounds (34 kg) per hour. The CoPEN was a copolymer of 70 mole %, 2,6 naphthalene dicarboxylate methyl ester, 15 mole % dimethyl terephthalate, and 15 mole % dimethyl isophthalate with ethylene glycol. The feedblock method was used to generate 151 layers. The feedblock was designed to produce a stack of films having a thickness gradient from top to bottom, with a thickness ratio of 1.22 from the thinnest layers to the thickest layers. This optical stack was multiplied by two sequential multipliers. The nominal multiplication ratio of the multipliers was 1.2 and 1.4, respectively. Between the final multiplier and the die, skin layers were added composed of the same CoPEN described above, delivered by a third extruder at a total rate of 106 pounds (48 kg) per hour. The film was subsequently preheated to 300° F. (150° C.) in about 30 seconds and drawn in the transverse direction to a draw ratio of approximately 6 at an initial rate of about 20% per second. The finished film thickness was approximately 0.0035 inch (0.089 mm).





FIG. 7B

shows the optical performance of the polarizer of Example 6. Curve a shows transmission of light polarized in the non-stretch direction at normal incidence, curve b shows transmission of p-polarized light in the nonstretch direciton at 50 degree angle of incidence, and curve c shows transmission of light polarized in the stretch direction at normal incidence. Note the very high transmission of light polarized in the non-stretch direction. Average transmission for curve a over 400-700 nm is 87%. Also note the very high reflectance of light polarized in the stretched direction in the visible range (400-700nm) shown by curve c. The film has an average transmission of 2.5% for curve c between 400 and 700 nm. The % RMS color for curve b is 5%.




II. Optical Devices Using Multilayer Optical Films




Optical devices according to the present invention use multilayer optical films to polarize and/or reflect light. The advantages of using multilayer optical film in optical devices involving reflection of light are graphically illustrated in FIG.


8


. Curve a shows the total reflectivity as a function of the number of reflections for convention reflector that has 96% reflectivity (i.e., about 4% of the light is absorbed at each reflection). As shown by curve a, the intensity of light which has been reflected decreases significantly after a relatively low number of reflections when the surface reflecting the light absorbs only about 4% of the light. In contrast, curve b shows the total reflectivity for a multilayer mirror film having a reflectivity of about 99.4%. Curve b clearly shows a much smaller decrease in total reflectivity. The difference becomes especially pronounced after only 2-4 reflections.




For example, for five reflections, the intensity of light is about 97% for light reflected from multilayer optical films according to the present invention, while the intensity drops to about 81.5% for light reflected from a conventional reflector which is only about 3.5% less efficient. Although it is difficult to determine the average number of reflections experienced by light in a backlight system, the number of reflections can be expected to increase as aspect ratio (defined more completely below) increase in any given backlight system. Those increased reflections would cause a significant loss in efficiency for backlight systems using conventional reflectors which would not be experienced in backlight systems employing multilayer optical film reflectors according to the present invention.




The practical value of this characteristic is that the efficiency of the present optical device is greatly enhanced as compared to systems employing conventional reflectors. Stated another way, the number of acceptable reflections for a given light ray in optical devices employing multilayer optical film according to the present invention can be significantly increased without substantially impairing the overall output of the device as compared to optical devices employing known reflectors/polarizers. This means that the present optical devices can be used to transmit and transport light over greater distances with better efficiency than presently known conventional reflectors.




Optical devices which incorporate the multilayer optical film can be most generally described as devices in which at least a portion of the light entering and/or exiting the device is reflected from an optical surface comprising the multilayer optical film. For the purpose of this invention, an “optical surface” will be defined as a surface, planar or otherwise, which reflects at least a portion of randomly polarized light incident upon it. More preferably, at least a portion of the light traveling through the optical devices will be reflected from an optical surface more than once, thereby exploiting the advantages of the multilayer optical film.




A subset of optical devices incorporating multilayer optical film according to the present invention will comprise two or more optical surfaces and can generally be categorized into devices in which the optical surfaces are arranged in a parallel or a non-parallel opposing arrangement.




Optical devices with substantially parallel optical surfaces include, but are not limited to: light pipes, light boxes, rectangular light guides, etc. For those devices designed to transmit light from one location to another, such as a light pipe, it is desirable that the optical surfaces absorb and transmit a minimal amount of light incident upon them while reflecting substantially all of the light. In other devices such as light boxes and light guides, it may be desirable to deliver light to a selected area using generally reflective optical surfaces and to then allow for transmission of light out of the device in a known, predetermined manner. In such devices, it may be desirable to provide a portion of the optical surface as partially reflective to allow light to exit the device in a predetermined manner. Examples of such devices will be described more completely below.




Another class of optical devices which include two or more reflective optical surfaces are devices in which the reflective optical surfaces converge towards each other as distance from a light source (or point of entry into the device) increases. This construction is especially useful in optical devices where it is desired to return light emitted from an optical source towards the direction from which the light entered the device. Optical devices with converging reflective optical surfaces will typically reflect a majority of light in a direction generally towards the source of the light.




Yet another class of optical devices which include two or more optical surfaces are devices in which the reflective optical surfaces diverge as distance from a light source (or point of entry into the device) increases. Optical devices with diverging reflective optical surfaces will typically tend to collimate light. The amount and degree of collimation will depend on the location of the light source relative to the narrow end of the device and the rate of divergence of the multilayer reflective optical film surfaces.




In a preferred embodiment, the optical devices are hollow as this will tend to decrease the amount of absorption at each reflection as light is transported by the optical devices.




In the effort to direct light towards a specific target, such as in task lighting, solar collectors, or otherwise, it may be preferred that the diverging optical surfaces form a parabola or cone. If a parabolic shape is used, collimation is best accomplished for light passing through or emanating from the focal point of the parabola. The specifics of designing the shape of such devices will be well known to those skilled in the art and will not be discussed herein.




Turning now to the figures in which illustrative examples of optical devices according to the present invention are depicted,

FIGS. 9 and 10

depict one illustrative optical device


110


in a cross-sectional schematic view in

FIG. 9 and a

perspective view in FIG.


10


. Optical device


110


is commonly referred to as a light box and can be substantially rectangular as shown or it can take any other shape desired based on aesthetics or functional considerations. Light boxes are typically substantially enclosed volumes in which one or more light sources are located. The volume is preferably lined with a reflective surface and includes either partially reflective areas or voids which allow light to escape from the light box in a predetermined pattern or manner.




The illustrative light box


110


depicted in

FIGS. 9 and 10

includes at least two opposing reflective and/or partially reflective optical surfaces


112


and


114


comprised of the multilayer optical film. It is most preferred that all of the interior reflective surfaces of the light box


110


are covered by the multilayer optical film. By using the multilayer optical film according to the present invention for all of the reflective surfaces within the light box


110


, absorption losses can be greatly reduced as compared to devices using conventional reflectors and/or polarizers. In some instances, however, all or a portion of either or both optical surfaces


112


and


114


can be constructed from other materials.




Where multilayer optical film is used in any optical device, it will be understood that it can be laminated to a support (which itself may be transparent, opaque reflective or any combination thereof) or it can be otherwise supported using any suitable frame or other support structure because in some instances the multilayer optical film itself may not be rigid enough to be self-supporting in an optical device such as illustrative device


110


.




The optical device


110


illustrated in

FIG. 9

includes two light sources


118




a


and


118




b


, referred to commonly as


118


, which emit light into the interior of the device


110


. Light emitted from the sources


118


will typically reflect between surfaces


112


and


114


numerous times before exiting the device


110


through a partially reflective area or transmissive void located in surface


112


, denoted by reference number


130


in FIG.


10


.




For illustration purposes, light rays


120


and


122


are shown as emanating from source


118




a


and reflecting within the optical device


110


until they exit from areas such as


130


in layer


112


. In an illuminated sign depicted as the illustrative optical device


110


, areas


130


will typically comprise advertising or other informational messages or, alternatively, may comprise a decorative display of some type. Although only areas


130


are depicted as transmitting light through optical surface


112


, it will be understood that all or any portion of both surfaces


112


and


114


may transmit light out of device


110


.




Areas


130


which transmit light can be provided of many different materials or constructions. The areas


130


can be made of multilayer optical film or any other transmissive or partially transmissive materials. One way to allow for light transmission through areas


130


is to provide areas in optical surface


112


which are partially reflective and partially transmissive. Partial reflectivity can be imparted to multilayer optical films in areas


130


according to the present invention by a variety of means.




In one aspect, areas


130


may comprise multi-layered optical film which is uniaxially stretched to allow transmission of light having one plane of polarization while reflecting light having a plane of polarization orthogonal to the transmitted light. Rays


120




a


and


120




b


of light as depicted in

FIG. 9

illustrate such a situation in which light having one polarization direction is transmitted through multi-layered optical film


130


while light having the orthogonal polarization direction is reflected back into optical device


110


.




When areas


130


are provided from a multilayer reflective polarizing film, it is preferable that the optical device


110


include some mechanism for randomizing polarization orientation of the light reflected back into the interior of the device


110


. One mechanism for randomizing polarization orientation would be to provide a thin pigmented coating on optical surface


114


to randomize polarization and scatter light reflected from the areas


130


. Another mechanism is to add a birefringent polymer film, or to have a birefringent skin layer on the MOF mirror. Any mechanism, however, by which the polarization orientation of returned light


120




b


can be modified after reflection from the reflective polarizing areas


130


is desirable as it can then be returned to areas


130


and, theoretically, a portion of the light will then have the proper polarization orientation to allow transmission through areas


130


and out of optical device


110


.




Light ray


122


depicts the effect of an alternate means of providing for transmission of light through areas


130


in an optical device


110


according to the present invention. Light ray


122


is transmitted through areas


130


without reflection through a void formed in the optical surface


112


. As a result, there is no partial reflection of light ray


122


as opposed to light ray


120


as described above. In this situation, optical surface


112


is itself substantially completely reflective, except for those voids in areas


130


which transmit light without substantial reflection.




It will be understood that the term “void” can be used to describe an actual physical aperture through optical surface


112


as well as clear or transparent areas formed in the optical surface


112


which do not substantially reflect light. The number and size of multiple apertures in area


130


of optical surface


112


may be varied to control the amount of light transmitted through the areas


130


. At one extreme, areas


130


may even constitute complete voids in optical surface


112


, although large voids are typically undesirable to protect the interior of the device


110


from debris, dust, etc.




An alternate embodiment of an optical device


110


can be provided where at least the areas


130


in optical surface


112


do not comprise a multilayer optical film at all, but rather comprise a different class of partially reflective films, such as a structured partially reflective film. Exemplary micro-replicated structured partially reflective films are marketed as Optical Lighting Film, and Brightness Enhancement Film, available from Minnesota Mining and Manufacturing Company, St. Paul, Minn.




In those instances where a less efficient multilayer optical film is used (i.e., some of the light incident upon the multilayer optical film surfaces is lost through transmission), it may be advantageous to provide the back surfaces of the multilayer optical film, i.e., the surface facing the exterior of the device


110


, with a thin metal or other reflective coating to reflect light that would otherwise be lost to transmission, thereby improving the reflectivity of the multilayer optical film. It will of course, be understood that the metallic or other reflective coating may suffer from some absorption losses, but the fraction of light transmitted through the film will typically be less than 5% (more preferably less than 1%) of the total light incident on the film. The metallic or other reflective coating may also be useful to reduce visible iridescence if leakage of narrow bands of wavelengths occurs in the multilayer optical film. In general, however, the high efficiency multilayer reflective films are preferred.




Due to the high efficiency of the multilayer optical film in reflecting light in optical devices


110


, the number and intensity of light sources


118


needed to provide uniform illumination over the areas


130


can be reduced. Any optical device design can be less concerned about the number of reflections a light ray will make within device


110


before exiting as illustrated in FIG.


10


and described above.




Aspect ratio in a device


110


is typically determined by comparing the depth of the light box, indicated as D in

FIG. 10

to the length and height of the device


110


, indicated as L and H, respectively. In some instances, aspect ratio may be the ratio of depth D as compared to the area which is defined by the length times the height of optical device


110


.





FIG. 11

is a schematic cross-sectional representation of a converging wedge optical device


210


, according to the present invention, incorporating multilayer optical film. In any optical device employing a converging wedge design, the optical surfaces


212


and


214


are arranged in a converging relationship in which the optical surfaces converge towards each other as distance from the opening


211


into the device


210


increases. In the preferred embodiment, the surfaces


212


and


214


are comprised of a multilayer optical film. Also, the optical device


210


is preferably hollow to minimize absorption losses.




It will be understood that the optical device


210


could comprise two generally planar optical surfaces


212


and


214


. One specific example of a converging wedge design would be a light guide used in a backlight assembly for a liquid crystal display device. Another specific example of an optical device represented in

FIG. 11

could comprise a generally conical device having a cross-section taken along the longitudinal axis of the device


210


. In a conical device, optical surfaces


212


and


214


may actually be portions of a continuous surface which appears discontinuous due to the cross-sectional nature of the view in FIG.


11


.




A light ray


220


is depicted as entering the optical device


210


through opening


211


as shown and is reflected numerous times before exiting in generally the same direction from which it entered the device


210


. Optical surfaces


212


and


214


could be comprised of many different materials. For example both surfaces


212


and


214


could be comprised of multilayer optical films according to the present invention and a portion or all of either or both surfaces


212


and


214


could be completely reflective or partially reflective.




If a less efficient multilayer optical film is used for reflective optical surfaces


212


and


214


and it is desired that both surfaces prevent transmission of light, they can be coated on their “exterior” surfaces with a reflective coating such as a thin metallic layer or other reflective coating. That additional layer will help to ensure that layers


212


and


214


do not transmit light. In some instances, however, it may be desirable to provide one or both of the multi-layered optical films


212


and


214


as partially reflective to allow some leakage of light, polarized or not, through surfaces


212


and/or


214


in a uniform or other controlled manner.




One specific example of a device


210


where uniform distribution of light is desired is a light guide backlight assembly for a liquid crystal display.





FIG. 12

is a schematic cross-sectional representation of a diverging wedge optical device


310


according to the present invention. In any optical device employing a diverging wedge design, the optical surfaces


312


and


314


are arranged in a diverging relationship in which the surfaces diverge as distance from the light source


318


increases. In a preferred embodiment, the surfaces


312


and


314


are comprised of a multilayer optical film. Also, the optical device


310


is preferably hollow to minimize absorption losses. It will be understood that, like the converging wedge device


210


, the diverging wedge depicted in

FIG. 12

could comprise two generally planar optical surfaces


312


and


314


or that device


310


could comprise a generally conical, parabolic or other shape in which the depicted cross-section is taken along the longitudinal axis of device


310


. In such an optical device, optical surfaces


312


and


314


may actually be portions of a continuous surface which appears discontinuous due to the cross-sectional nature of the view in FIG.


11


.




An optical device which includes diverging optical surfaces will tend to collimate light exiting it as light rays


320


and


322


illustrate. The device


310


depicted in

FIG. 12

includes a light source


318


located at the entry into device


310


. It will, however, be understood that a diverging optical device may include a plurality of sources


318


. If device


310


were formed in a roughly parabolic shape, that collimation would be more pronounced if the light source


318


was located proximate the focal point of the parabola. Alternatively, a diverging optical device


310


could also rely on a light generated from a source or sources located away from the actual opening into the diverging optical device


310


.




In general, the degree and amount of collimation of light exiting such a device


310


is dependent on a number of factors including the angle of light rays entering the device, the location of the light source, and the shape and/or angular relationship between the optical surfaces


312


and


314


.





FIG. 13

is a cross-sectional schematic view of another illustrative optical device


410


formed using the multilayer optical film according to the present invention. The cross-section of device


410


as depicted in

FIG. 13

is taken along a longitudinal axis which shows two generally parallel optical surfaces


412


and


414


. An additional view is depicted in

FIG. 14

, which shows a cross-section of device


410


taken transverse to the longitudinal axis. As depicted, device


410


has a generally circular shape.




Optical devices such as device


410


are typically used to transmit light between two locations and are commonly referred to as “light pipes.” Such devices have a longitudinal axis and a cross-section transverse to that axis which forms a closed plane figure. Examples of some typical cross-section figures include circles (such as that shown in FIG.


14


), ellipses, polygons, closed irregular curves, triangles, squares, rectangles or other polygonal shapes. Any device


410


having a closed plane figure transverse cross-section appears as two surfaces in a longitudinal cross-section as shown in

FIG. 13

even though the device


410


may actually be formed from a single continuous optical surface.




Because the multilayer optical film according to the present invention used absorbs substantially none of the light incident upon it, light pipes constructed of multilayer optical film according to the present invention can extend for a relatively large distances without significant loss of throughput. It is particularly advantageous to use the multilayer optical film with devices such as light pipes in which a large portion of the light travelling through the device approaches the surfaces of the device at shallow angles. Known multilayered polymer reflective films are not efficient at reflecting light approaching them at shallow angles and, therefore, would suffer from large transmissive losses. The present multilayer optical film, however, is able to reflect such light with the much the same efficiency as light approaching the film normal to the surfaces.




Alternately, it will be understood that a device such as light pipe


410


may include sections which are partially transmissive, thus allowing light to escape from the device. The transmission mechanisms may include multilayer reflective polarizing sections, voids or any other mechanism as described with respect to the illustrative embodiments above. Such designs do, however, start to resemble light boxes or guides depicted and described in conjunction with

FIGS. 9 and 10

, above.

FIG. 15

illustrates another optical device according to the present invention. The optical device


505


depicted in

FIG. 15

could be used, for example, in a decorative application such as a flower or a bow. Device


505


is constructed of a plurality of multilayer optical film layers (such as layers


510


and


520


) connected generally in their centers by a post or some other mechanism. Although the layers are depicted as generally circular, it will be understood that many different shapes could be provided.




The layers can be wrinkled or otherwise manipulated to give the device


505


volume. The wrinkling of multilayer optical film layers also provides device


510


with multiple converging wedges arranged generally vertically to return light incident on the device


505


to a viewer.




Although not required, leakage or transmission of light through the layers of multilayer optical film in device


505


is not a great concern as transmitted light can be reflected out of the device


505


by the adjacent diverging wedge formed by the next layer of film. Because of the adjacent diverging wedges in device


505


, it makes highly efficient use of leakage between the vertically arranged converging wedges because light escaping one wedge could be reflected back out of the adjacent wedge into which the light is transmitted. As a result, device


505


has an unusually brilliant appearance.




The multilayer optical film may also be provided in the form of elongated strips. Such strips of film can be advantageously used to form other configurations of optical devices which can be used, for example, as decorative bows, such as any of those described in U.S. Pat. No. 3,637,455 (Pearson et al.); U.S. Pat. No. 4,329,382 (Truskolaski et al.); U.S. Pat. No. 4,476,168 (Aoyama); and U.S. Pat. No. 4,515,837 (Chong); and in U.S. patent application Ser. No. 08/031,560 (Huss), abandoned, and Ser. No. 08/153,373 (Huss) U.S. Pat. No. 5,468,523; the entire disclosures of all of which are incorporated herein by reference.




Optical device


505


illustrates another significant advantage of the optical devices incorporating multilayer optical film according to the present invention, i.e., that the devices need not exhibit symmetry to be effective. In fact, optical devices according to the present invention need not exhibit symmetry in any plane or about any line but can still function effectively and efficiently due to the low absorbance and high reflectance both at normal angles and at high angles away from the normal of the multilayer optical films.




Symmetry in optical devices is provided in many instances to reduce or minimize the number of reflections experienced by light travelling through the devices. Minimizing reflections is particularly important when using conventional reflectors because of their relatively high absorptivities (see FIG.


8


and the accompanying description above). Because optical devices using multilayer optical film according to the present invention experience significantly reduced absorption, it is much less important to minimize the number of reflections and, consequently, symmetry is not as important to maintain the efficiency of the optical devices.




As a result, although the illustrative optical devices described above do generally exhibit symmetry about at least one axis, the present invention should not be limited to optical devices having an axis of symmetry. Furthermore, the present invention has been described above with respect to illustrative examples to which modifications may be made without departing from the scope of the invention as defined by the appended claims.



Claims
  • 1. An optical device comprising a body having at least two opposing optical surfaces, at least a portion of each of the optical surfaces comprising a reflective film that reflects incident light of at least one polarization orientation over an intended bandwidth,wherein the reflective film of each of the optical surfaces comprises a plurality of layers, wherein a refractive index difference between at least two adjacent layers in a first in-plane direction is greater than or equal to a refractive index difference between the at least two adjacent layers in a second in-plane direction for the reflective film, and further wherein the refractive index difference in the first in-plane direction is greater than a refractive index difference between the at least two adjacent layers in a third out-of-plane direction for the reflective film.
  • 2. The optical device of claim 1, wherein the device comprises a light guide.
  • 3. The optical device of claim 1, wherein the optical surfaces define a volume.
  • 4. The optical device of claim 1, wherein at least one of the optical surfaces comprises a transmissive area.
  • 5. The optical device of claim 4, wherein the transmissive area comprises a void in the optical surface.
  • 6. The optical device of claim 4, wherein the transmissive area transmits light having a first polarization orientation and reflects light having a second polarization orientation.
  • 7. The optical device of claim 1, wherein one of the at least two opposing optical surfaces comprises a mirror and the other optical surface comprises a reflective polarizer.
  • 8. The optical device of claim 1, wherein the reflective film transmits less than 2% of incident light with a first polarization orientation over an intended bandwidth, and wherein the optical device absorbs less than about 10% of the incident light after five reflections from the reflective film of the opposing optical surfaces.
  • 9. The optical device of claim 8, wherein the device comprises a light guide.
  • 10. The optical device of claim 8, wherein at least one of the optical surfaces comprises a transmissive area in which the incident light with the first polarization orientation over the intended bandwidth is transmitted through the surface.
  • 11. An optical device comprising:a plurality of diverging wedges, each diverging wedge of the plurality of diverging wedges comprising two opposing optical surfaces, wherein each of the optical surfaces comprise a multilayer optical film, wherein the multilayer optical film comprises a plurality of layers, wherein a refractive index difference between at least two adjacent layers in a first in-plane direction is greater than or equal to a refractive index difference between the at least two adjacent layers in a second in-plane direction, and further wherein the refractive index difference in the first in-plane direction is greater than a refractive index difference between the at least two adjacent layers in a third out-of-plane direction.
  • 12. The optical device of claim 11, wherein the plurality of diverging wedges are connected to each other.
  • 13. The optical device of claim 11, wherein the plurality of diverging wedges comprise a plurality of adjacent diverging wedges.
  • 14. A decorative article comprising:a plurality of diverging wedges, each diverging wedge of the plurality of diverging wedges comprising two opposing optical surfaces, wherein each of the optical surfaces comprise a multilayer optical film, wherein the multilayer optical film comprises a plurality of layers, wherein a refractive index difference between at least two adjacent layers in a first in-plane direction is greater than or equal to a refractive index difference between the at least two adjacent layers in a second in-plane direction, and further wherein the refractive index difference in the first in-plane direction is greater than a refractive index difference between the at least two adjacent layers in a third out-of-plane direction.
  • 15. The decorative article of claim 14, wherein the plurality of diverging wedges are connected to each other.
  • 16. The decorative article of claim 14, wherein the plurality of diverging wedges comprise a plurality of adjacent diverging wedges.
  • 17. The decorative article of claim 14, wherein the article comprises a bow.
  • 18. The decorative article of claim 14, wherein the article comprises a flower.
Parent Case Info

This is a continuation of application Ser. No. 08/494,366 filed Jun. 26, 1995, U.S. Pat. No. 6,080,467.

US Referenced Citations (85)
Number Name Date Kind
0540768 Western Jun 1895
3124639 Kahn Mar 1964
3535016 Malifaud Oct 1970
3610729 Rogers Oct 1971
3637455 Pearson et al. Jan 1972
3647612 Schrenk et al. Mar 1972
3711176 Alfrey Jr. et al. Jan 1973
3759647 Schrenk et al. Sep 1973
3773882 Schrenk Nov 1973
3801429 Schrenk et al. Apr 1974
3860036 Newman, Jr. Jan 1975
4025688 Nagy et al. May 1977
4094947 Alfrey, Jr. et al. Jun 1978
4268127 Oshima et al. May 1981
4310584 Cooper et al. Jan 1982
4315258 McKnight et al. Feb 1982
4329382 Truskolaski et al. May 1982
4446305 Rogers et al. May 1984
4476168 Aoyama Oct 1984
4500173 Leibowitz et al. Feb 1985
4515441 Wentz May 1985
4515837 Cheng May 1985
4520189 Rogers et al. May 1985
4521588 Rogers et al. Jun 1985
4525413 Rogers et al. Jun 1985
4540623 Im et al. Sep 1985
4688897 Grinberg et al. Aug 1987
4720426 Englert et al. Jan 1988
4805984 Cobb, Jr. Feb 1989
4813765 Negishi Mar 1989
4937134 Schrenk et al. Jun 1990
5089318 Shetty et al. Feb 1992
5094788 Schrenk et al. Mar 1992
5094793 Schrenk et al. Mar 1992
5095210 Wheatley et al. Mar 1992
5103337 Schrenk et al. Apr 1992
5122905 Wheatley et al. Jun 1992
5122906 Wheatley Jun 1992
5126880 Wheatley et al. Jun 1992
5149578 Wheatley et al. Sep 1992
5188760 Hikmet et al. Feb 1993
5202074 Schrenk et al. Apr 1993
5211878 Reiffenrath et al. May 1993
5217794 Schrenk Jun 1993
5233465 Wheatley et al. Aug 1993
5234729 Wheatley et al. Aug 1993
5235443 Barnik et al. Aug 1993
5269995 Ramanathan et al. Dec 1993
5278694 Wheatley et al. Jan 1994
5294657 Melendy et al. Mar 1994
5316703 Schrenk May 1994
5319478 Fijnfschilling et al. Jun 1994
5339198 Wheatley et al. Aug 1994
5360659 Arends et al. Nov 1994
5389324 Lewis et al. Feb 1995
5422756 Weber Jun 1995
5424119 Phillips et al. Jun 1995
5448404 Schrenk et al. Sep 1995
5451449 Shetty et al. Sep 1995
5481445 Sitzema et al. Jan 1996
5486884 De Vaan Jan 1996
5486935 Kalmanash Jan 1996
5486949 Schrenk et al. Jan 1996
5540978 Schrenk Jul 1996
5550660 Yang Aug 1996
5552927 Wheatly et al. Sep 1996
5568316 Schrenk et al. Oct 1996
5612820 Schrenk et al. Mar 1997
5629055 Revol et al. May 1997
5686979 Weber et al. Nov 1997
5699188 Gilbert et al. Dec 1997
5721603 De Vaan et al. Feb 1998
5744534 Ishiharada et al. Apr 1998
5751388 Larson May 1998
5767935 Ueda et al. Jun 1998
5770306 Suzuki et al. Jun 1998
5783120 Ouderkirk et al. Jul 1998
5793456 Broer et al. Aug 1998
5808794 Weber et al. Sep 1998
5825542 Cobb, Jr. et al. Oct 1998
5825543 Ouderkirk et al. Oct 1998
5882774 Jonza et al. Mar 1999
5940149 Vanderwerf Aug 1999
5962114 Jonza et al. Oct 1999
5965247 Jonza et al. Oct 1999
Foreign Referenced Citations (16)
Number Date Country
1327286 Mar 1994 CA
5-288910 Nov 1993 JP
6-11607 Jan 1994 JP
WO 9109719 Jul 1991 WO
WO 9527919 Apr 1995 WO
WO 9517691 Jun 1995 WO
WO 9517692 Jun 1995 WO
WO 9517699 Jun 1995 WO
WO 9517303 Jun 1995 WO
WO 9619347 Jun 1996 WO
WO 9631794 Oct 1996 WO
WO 9701440 Jan 1997 WO
WO 9701774 Jan 1997 WO
WO 9732226 Sep 1997 WO
WO 9936248 Jul 1999 WO
WO 9936262 Jul 1999 WO
Non-Patent Literature Citations (11)
Entry
Alfrey, Jr. et al., Physical Optics of Iridescent Multilayered Plastic Films, Polymer Engineering and Science, vol. 9, No. 6, Nov. 1969.
Hodgkinson et al., Effective principal refractive indices and column angles for periodic stacks of thin birefringent films, Optical Society of America, vol. 10, No. 9, p. 2065-2071, Sep. 1993.
Im, J. et al., Coextruded Microlayer Film and Sheet, Journal of Plastic Film and Sheeting, vol. 4, p. 104-15 (Apr., 1988).
Radford et al., Reflectivity of Iridescent Coextruded Multilayered Plastic Films, Polymer Engineering and Science, vol. 13, No. 3, (May 1973); Dow Chemical Co., American Chemical Society Symposium on “Coextruded Plastic Films, Fibers, Composites”, Apr. 9-14, 1972.
Schrenk et al., Interfacial Flow Instability in Multilayer Coextrusion, Polymer Engineering and Science, vol. 18(8), p. 620-3 (Jun. 1978).
Schrenk et al., Coextruded Multilayer Polymer Films and Sheet, Chapt. 15, Polymer Blends, vol. 2, 129, Academic Press, Inc. (1978).
Schrenk et al., Coextruded Elastomeric Optical Interference Films, SPE Annual Technical Conference, Atlanta, Georgia, 1703 (1988).
Schrenk et al., Nanolayer polymeric optical films, Tappi Journal, pp. 169-174, Jun., 1992.
Schrenk, W., New Developments in Coextrusion, International Conference on Advances In Polymer Processing, New Orleans, Louisiana, (Apr., 1991).
Schrenk, W. et al., Coextruded Iridescent Film, TAPPI Paper Synthetics Conference, Atlanta, Georgia, p. 141-5 (Sep. 27-29, 1976).
Schrenk, W. et al., Coextruded Infrared Reflecting Films, 7th Annual Meeting Polymer Processing Society, Hamilton, Ontario, Canada, p. 222-3 (Apr. 1991).
Continuations (1)
Number Date Country
Parent 08/494366 Jun 1995 US
Child 09/461245 US