Patent Application
20140209308
The present invention generally relates to hydrocarbon exploration and production operations, such as subterranean cementing operations, and more particularly to compositions and methods that allow for greater control over the setting of fluids or slurries used during such operations.
Natural resources such as oil and gas located in a subterranean formation can be recovered by drilling a wellbore down to the subterranean formation, typically while circulating a drilling fluid in the wellbore. After the wellbore is drilled, a string of pipe, e.g., casing, can be run in the wellbore. The drilling fluid is then usually circulated downwardly through the interior of the pipe and upwardly through the annulus between the exterior of the pipe and the walls of the wellbore, although other methodologies are known in the art.
Hydraulic cement compositions are commonly employed in the drilling, completion and repair of oil and gas wells. For example, hydraulic cement compositions are utilized in primary cementing operations whereby strings of pipe such as casing or liners are cemented into wellbores. In performing primary cementing, a hydraulic cement composition is pumped into the annular space between the walls of a wellbore and the exterior surfaces of a pipe string disposed therein to harden. After the cement is placed within the wellbore, a period of time is needed for the cement to cure and obtain enough mechanical strength for drilling operations to resume. This down time is often referred to as “wait-on-cement”, or WOC. The WOC time ranges from a few hours to several days, depending on the difficulty and criticality of the cement job in question. It is desirable to reduce the WOC time, so that the crew can recommence the drilling operation, and thus reduce the total time and cost of operations. If operations are resumed prior to the cement obtaining sufficient mechanical strength, the structural integrity of the cement can be compromised. As such, systems generally are over-engineered to have very long setting (or thickening) times in order to ensure that the mix remains fluid until all of the cementitious material is in place, which can result in excessive WOC.
The present invention generally relates to hydrocarbon exploration and production operations, such as subterranean cementing operations, and more particularly to compositions and methods that allow for greater control over the setting of fluids or slurries used during such operations.
In some embodiments, the present invention provides a method comprising placing a sealant composition comprising a polymerizable additive into a wellbore penetrating a subterranean formation; and subjecting the sealant composition to a radiation dose of from about 1 to about 1000 grays, so as to form a seal therein.
In other embodiments, the present invention provides a method comprising preparing a cement composition comprising hydraulic cement, a polymerizable additive, and sufficient water to form a slurry; placing the cement composition into the wellbore; and subjecting the cement composition to a radiation dose of from about 1 to about 1000 grays to activate setting of the cement composition.
In still other embodiments, the present invention provides a cement composition comprising hydraulic cement; a polymerizable additive; and sufficient water to form a slurry. The cement composition is capable of setting when subjected to a radiation dose of from about 1 to about 1000 grays.
The features and advantages of the present invention will be readily apparent to those skilled in the art upon a reading of the description of the preferred embodiments that follows.
The following figures are included to illustrate certain aspects of the present invention, and should not be viewed as exclusive embodiments. The subject matter disclosed is capable of considerable modifications, alterations, combinations, and equivalents in form and function, as will occur to those skilled in the art and having the benefit of this disclosure.
The present invention generally relates to hydrocarbon exploration and production operations, such as subterranean cementing operations, and more particularly to compositions and methods that allow for greater control over the setting of fluids or slurries used during such operations by curing cement compositions with radiation.
The use of, for example, bremsstrahlung radiation in doses in the sub-1000 gray range generated by electron accelerators, has significant advantages. At 10-50%, the efficiency (E of photons out over electrical E in) of electron-to-bremsstrahlung photon production is much higher than that of most other ionizing particles, such as neutrons and protons. For many competing methods of high energy photon production, the efficiency of photon production is 2-4 orders of magnitude greater. As a result, the problems associated with excess heat production and large energy requirements are minimized.
Further, the use of electron accelerators to generate bremsstrahlung radiation does not require a supply of precursor fuel, such as deuterium or tritium due to the abundance of electrons in matter.
The present invention relates generally to wellbore operations involving fluids or slurries, and more particularly, to fluids or slurries that contain accelerating agents and/or retarders that can be released, activated and/or deactivated on command to provide thickening to the fluid or slurry. The fluids or slurries referred to herein can be any suitable for wellbore operations, drilling, completion, workover or production operations. The fluids may include various types of sealants, such as resins, cements, settable muds, lost circulation fluids, conformance fluids, and combinations thereof. One embodiment of the present invention relates to wellbore cementing operations, and more particularly, to methods of sealing in wellbores using cementitious compositions that contain polymerizable additives that can be subjected to radiation doses of from about 1 gray to about 1000 grays to form a seal.
Referring to
A cement composition can be pumped down the casing 8 and circulated up the annulus 10 while fluid returns are taken from the annulus 10 out annulus flow line 12, in a typical circulation direction. Alternately, the cement composition can be pumped into the annulus 10 from annulus flow line 12 while fluid returns are taken from the inner diameter of casing 8 through flow line 16. Thus, fluid flows through wellbore 2 in a reverse circulation direction.
In an alternate method a fluid composition, such as a cement slurry, can be placed within the wellbore 2 and a sealed or filled tubular, such as casing 8, can be lowered into the wellbore 2 such that the fluid composition is displaced into the annulus 10 area, thereby placing the fluid composition within the annulus 10 without pumping the fluid composition into the annulus 10. The above method can be referred to as puddle cementing. The fluid composition can be a drilling fluid placed within the wellbore after drilling operations are complete.
In some embodiments, the sealant is subjected to a dose of radiation from bremsstrahlung photons which result from decelerating electrons. Bremsstrahlung radiation, or simply bremsstrahlung, is electromagnetic radiation produced by a sudden slowing down or deflection of charged particles (specifically electrons in this embodiment) passing through matter in the vicinity of the strong electric fields of atomic nuclei. Bremsstrahlung produces a continuous X-ray spectra—i.e., the resulting photons cover a whole range of energy, from a maximum value downward through lower values all the way to zero. In generating bremsstrahlung, some electrons that collide with a material target are decelerated to zero kinetic energy by a single head-on collision with a nucleus, and thereby have all their energy of motion converted at once into photon radiation of maximum energy, Other electrons from the same incident beam come to rest after being decelerated many times by the positively charged nuclei. Each deflection and subsequent scattering of the electrons gives rise to a pulse of electromagnetic energy, or photon, of less than maximum energy. The maximum energy of any one bremsstrahlung photon is the original kinetic energy of the incoming charged particle, typically an electron in this embodiment.
To generate bremsstrahlung, an electron accelerator may be used. Electron beam bremsstrahlung-induced curing is a fast non-thermal process which utilizes highly energetic electrons at controlled doses to produce scattered photons that polymerize and crosslink polymeric materials. To produce electrons with resulting bremsstrahlung photons that are most effective at crosslinking, the electron accelerator in this embodiment should generate electrons having an energy of about 0.5 MeV to about 20 MeV. In other embodiments, the electrons have an energy of about 0.1 MeV to about 50 MeV. The maximum intensity of the electron accelerators which produce bremsstrahlung photons may be large, over 1014/s.
Further, the electron accelerators may be geometrically modified to be accessible downwell. For example, in some embodiments, a 5-6 MeV energy electron accelerator with an average current of 10s of microamps (>1014/s) and a tungsten target can induce bulk gelation in some slurries in a few seconds.
Various electron accelerators are suitable for use in the present invention. For example, on electron accelerator which includes a Cockcroft-Walton voltage multiplying system that can make use of extra linear space within a casing to amplify voltage up to the necessary several MeV level. This system, which has a long, narrow shape makes it amenable to downhole utility. Another suitable example of an electron accelerator is an RF cyclotron. Another example of an electron accelerator technology for use in the present invention is that of Wakefield technology. Wakefield technology exploits laser pulses to evacuate electrons from small volumes of crystals. This allows other particles to accelerate as the system returns to equilibrium.
One embodiment of the present invention is shown in
A tool wireline 401 supplies electrical power and communications from the accelerator 500 to the surface of the wellbore. The tool wireline 401 also bears the mass of the accelerator 500 during transit up and down the borehole.
The electron accelerator 500 comprises a housing 501 that houses all the accelerator components. The housing 501 may have any geometrical structure suitable for housing the components and for going downwell in any type of geological formation 301.
The electron accelerator may include accelerator electrical power components 561. These components may include devices for properly allocating electrical power from the tool wireline 401 to the various power-using devices throughout the accelerator 500.
An accelerator RF electron acceleration component 581 may also be included in the electron accelerator 500. The accelerator type may be Cockcroft-Walton, radiofrequency, or Wakefield. The accelerator may also include lasers. In addition, the accelerator 500 may have a characteristic radius. The acceleration mechanism may involve plasma, RF induced electromagnetic fields, capacitors and diodes or other mechanisms suitable for downwell operations.
The accelerator 500 may also include cooling components 521. The cooling component 521 could include cryogenic liquid with insulation. The accelerator may also include communication components 541. These components may include devices used to assist with communicating signals to and from the tool wireline 401 to run the accelerator 500 properly.
Attached to the acceleration component 581 is an electron beam port 591. This location is where the accelerated electrons 601 are expelled from the acceleration electronics and put on a trajectory to impinge upon the high Z target 701. The accelerated electrons in the present disclosure may have a kinetic energy of from about 0.5 MeV and about 20 MeV. In other embodiments, the accelerated electrons have a kinetic energy of from about 0.1 MeV to about 50 MeV. The electrons may be accelerated in a direction parallel to the axis of the accelerator geometry.
An electron beam rastoring device 621 may be included to shape the trajectory of the electrons 601 to depart from straight lines, to impinge on the high Z target 701. The rastoring device 621 could include an electromagnet. In other embodiments, the electron accelerator 500 may forego the use of the rastoring device 621 and instead align the high Z target 701 with the electron beam port, or increase the size of the area of the high Z target 701. In order to optimize device utility, it is desirable to create a trajectory for the accelerated electrons whereby they impinge upon the high Z target 701 at angles that are as perpendicular to the casing 101 as feasible so as to minimize the path length of the bremsstrahlung photons 801 though the casing 101 and the material surrounding the accelerator such as mud, pressurized water and other materials. As such, the plane of the surface of the high Z target 701 might be angled with respect to the radial plane of the accelerator and borehole.
During use of the accelerator 500 in the borehole, the accelerator 500 may pass downward though the borehole in order to set the cement slurry. In the example shown in
Any cement suitable for use in subterranean applications may be suitable for use in the present invention. The cementitious compositions disclosed herein generally include water and a cement component such as hydraulic cement, which can include calcium, aluminum, silicon, oxygen, and/or sulfur that sets and hardens by reaction with the water. Examples of hydraulic cements include but are not limited to Portland cements (e.g., Classes A, C, G, and H Portland cements), pozzolana cements, gypsum cements, phosphate cements, high alumina content cements, silica cements, high alkalinity cements, and combinations thereof. Cements including shale, cement kiln dust or blast furnace slag also may be suitable for use in the present invention. In certain embodiments, the shale may include vitrified shale. In certain other embodiments, the shale may include raw shale (e.g., unfired shale), or a mixture of raw shale and vitrified shale.
The sealant may include a polymerizable additive capable of undergoing polymerization when subjected to radiation. The polymerizable additive may be present in an amount of about 0.01% to about 25% by weight of the cement composition. In other embodiments, the polymerizable additive is in an amount of about 1 to about 15%.
The polymerizable additive may include one selected from alkeneoxides, vinyl pyrrolidones, vinyl alcohols, acrylamides, vinyl methyl ethers, isobutylenes, fluoroelastomers, esters, tetrafluoroethylenes, acetals, propylenes, ethylenes, methylpentenes, methylmethacrylates, fluorinated ethylene propylenes, derivatives thereof and combinations thereof.
The sealant may also include a crosslinking agent capable of crosslinking a polymer formed by the polymerization of the polymerizable additive. For example, the crosslinking agent may include at least one selected from the group consisting of a poly(ethylene glycol) diacrylates, a poly(ethylene glycol) dimethacrylates, trimethylolpropane triacrylates (TM PTA), ethoxylated TM PTAs, trimethylolpropane trimethacrylates, trimethylolpropanetriacrylates, hexanediol diacrylates, N,N-methylene bisacrylam ides, hexanedioldivinylethers, triethyleneglycol diacrylates, pentaeritritoltriacrylates, tripropyleneglycol diacrylates, 1,3,5-triallyl-1,3,5-triazine-2,4,6(1H,3H,5H)-triones, 2,4,6-triallyloxy-1,3,5-triazines, alkoxylated bisphenol A diacrylates, derivatives thereof, and combinations thereof.
The sealant or cement compositions used in the present invention can further include a set retarder. Set retarding admixtures lengthen the time at which the fluid or slurry composition remains a fluid. These retarding admixtures consequently allow a fluid or slurry, such as cement, to be pumped along long distances without the effect of premature setting. A broad variety of set retarders may be suitable for use in the fluid or slurry compositions used in the present invention. For example, the set retarder may include, inter alia, phosphonic acid, phosphonic acid derivatives, lignosulfonates, salts, sugars, carbohydrate compounds, organic acids, carboxymethylated hydroxyethylated celluloses, synthetic co- or ter-polymers including sulfonate and carboxylic acid groups, and/or borate compounds. In certain embodiments, the set retarders used in the present invention are phosphonic acid derivatives, such as those described in U.S. Pat. No. 4,676,832, the entire disclosure of which is incorporated herein. Examples of suitable borate compounds include, but are not limited to, sodium tetraborate and potassium pentaborate. Examples of suitable organic acids include, inter alia, gluconic acid and tartaric acid. Generally, the set retarder is present in the fluid or slurry compositions used in the present invention in an amount sufficient to delay the setting of the fluid or slurry composition in a subterranean formation for a desired time. More particularly, the set retarder may be present in the fluid or slurry compositions used in the present invention in an amount of from about 0.1% to about 10% bwoc. In certain embodiments, the set retarder is present in the fluid or slurry compositions used in the present invention in an amount of from about 0.5% to about 4% bwoc.
The set retarders of the current invention may include a sensitizer-containing retarder, such as a boron-containing retarder. The sensitizer can be made from a material having a strong radiation absorption property. The sensitizer can also be a scintillator material. The sensitizer can be any material that increases the capture efficiency of the ionizing radiation within the slurry. This sensitizer-containing retarder, also referred to as a sensitized retarder, can be a boron-containing retarder, also referred to as a boronated retarder, may include a wide variety of set retarders, including the set retarders disclosed herein, wherein the selected set retarder, or combination or set retarders, additionally includes at least one boron atom. As discussed in the immediately preceding paragraph, sugars and/or carbohydrates can be used as a retarder in the setting of a cement composition. In an embodiment, the retarder is a sensitized sugar or carbohydrate. In a more specific embodiment, the sensitized retarder is boronated glucose. In an even more specific embodiment, the boronated glucose is represented by 3-O-(o-Carborany-1-ylmethyl)-D-glucose, as presented in U.S. Pat. No. 5,466,679, to Soloway et al.
The compositions of the present invention may also include a set accelerator. The accelerator aids in overcoming possible delays caused by the set retarders by shortening the setting time of the fluid or slurry composition. A broad variety of set accelerators may be suitable for use in the fluid or slurry compositions used in the present invention, the set accelerator may include any component that reduces the setting time of a cement composition. For example, the set accelerator may include alkali and alkali earth metal salts, silicate salts, aluminates and amines, such as triethanolamine. In an embodiment, the set accelerator is a calcium salt. The calcium salt may be selected from the group consisting of calcium formate, calcium nitrate, calcium nitrite and calcium chloride. In a specific embodiment, the set accelerator is calcium chloride. The set accelerator may be present in the fluid or slurry compositions used in the present invention in an amount of from about 0.1% to about 20% bwoc. In certain embodiments, the set accelerator is present in the cement compositions used in the present invention in an amount of from about 4% to about 12% bwoc.
Methods of this invention for isolating a wellbore or a portion of a wellbore may include placing a sealant composition including a polymerizable additive, pumping the sealant composition containing the polymerizable additive into a wellbore penetrating a subterranean formation, and subjecting the sealant composition to a radiation dose of from about 1 gray to about 1000 grays, so as to form a seal therein. In other embodiments, the sealant composition may be subjected to a radiation dose of from about 5 grays to about 500 grays.
Methods of this invention may include preparing a cement composition comprising: hydraulic cement, a polymerizable additive, and sufficient water to form a slurry; placing the cement composition into the wellbore; and subjecting the cement composition to a radiation dose of from about 1 gray to about 1000 grays to activate setting of the cement composition. In other embodiments, the cement composition may be subjected to a radiation dose of from about 5 grays to about 500 grays.
In an embodiment, a set retarder and/or a set accelerator or oxidizing agent are/is added to the cement mixture before water is added to the mixture. In another embodiment, the set retarder and/or the set accelerator or oxidizing agent are/is added to the cement mixture after water has been added to the mixture. In yet another embodiment, set retarder is added before the set accelerator or oxidizing agent. In yet another embodiment, the set accelerator is added before the set retarder. In a further embodiment, the set accelerator and/or set retarder is/are added during the mixing of the cement and water.
In an embodiment, once the cementitious composition containing the set retarder and/or set accelerator or oxidizing agent is obtained, the slurry is then placed in the wellbore, such as in a wellbore/casing annulus. Upon the placement of the slurry containing the set retarder and/or set accelerator or oxidizing agent in the wellbore, the cement particles and the set retarder and/or set accelerator or oxidizing agent should be substantially uniformly mixed with the cement particles in the cement slurry.
In a further embodiment, a set retarder as well as both a set accelerator and oxidizer are added to the fluid or slurry. Upon being exposed to the ionizing radiation, both the set accelerator and oxidizer are released. The simultaneous destruction of the retarder by the oxidizer and the acceleration of cement hydration by the set accelerator provide rapid set.
In an embodiment, the ionizing radiation is introduced by an ionizing radiation emitter located at a point within the wellbore. In another embodiment, an ionizing radiation emitter located at the surface introduces the ionizing radiation directed downward into the wellbore. In another embodiment, a radiation source is lowered into the wellbore, such as on a wireline, and the ionizing radiation is emitted. The radiation source can be shielded to not emit the ionizing radiation other than when the shielding is removed. For example, a radiation source can be shielded at the surface when personnel could otherwise be exposed. Once the ionizing radiation source is placed in the wellbore and radiation can safely be emitted, the shield can be removed or opened, such as by an electronically activated signal transmitted from the surface down the wireline to the shield. In an embodiment, the radiation emitter can emit ionizing radiation as it is lowered down the wellbore and as it is pulled up the length of the wellbore. In a further embodiment, two or more ionizing radiation emitters are separately lowered to two or more depths, such that two or more depths of the wellbore may be subject to the ionizing radiation simultaneously.
In an embodiment, the ionizing radiation is introduced under the control of a technician in the field. The technician, engineer, or other on-site employee, can have the control over the emission of the ionizing radiation by imputing a signal that causes a release of the ionizing radiation from an emitter. In this embodiment, the ionizing radiation is released on demand from the technician in the field. The ionizing radiation can be released by a control system having parameters such as timer, flow meter, temperature sensor, or the like. In another embodiment, the lowering and/or emitting of the ionizing radiation source is triggered by a timing mechanism. In a further embodiment, the lowering and/or emitting of the radiation source is triggered by a flow meter that detects the amount of the cement mixture delivered into the wellbore.
As mentioned above, the ionizing radiation of the current invention can be under the control of technicians in the field. The release of the ionizing radiation emissions act as a trigger in the sense that the radiation can destroy the sensitized retarder, thus allowing the setting of the cement slurry to proceed. The release of the ionizing radiation may also act as a trigger when the ionizing radiation emissions act to release the set accelerator or oxidizing agent, or both, into the cement slurry. Once the set accelerator or oxidizing agent is released, it is dispersed into the cement slurry and reacts with the slurry or retarder, resulting in the acceleration of the setting process. Therefore, technicians in the field can trigger the thickening of the cement slurry. This triggering process puts the thickening of the cement slurry under the control of technicians in the field and can result in a decrease in the time needed to wait on cement (WOC) in the drilling and completion of a wellbore.
The term “cementitious composition” as may be used herein includes pastes (or slurries), mortars, and grouts, such as oil well cementing grouts, shotcrete, and concrete compositions including a hydraulic cement binder. The terms “paste”, “mortar” and “concrete” are terms of art: pastes are mixtures composed of a hydratable (or hydraulic) cement binder (usually, but not exclusively, Portland cement, Masonry cement, Mortar cement, and/or gypsum, and may also include limestone, hydrated lime, fly ash, granulated blast furnace slag, and silica fume or other materials commonly included in such cements) and water; “mortars” are pastes additionally including fine aggregate (e.g., sand), and “concretes” are mortars additionally including coarse aggregate (e.g., crushed rock or gravel). The cement compositions described in this invention are formed by mixing required amounts of certain materials, e.g., a hydraulic cement, water, and fine and/or coarse aggregate, as may be required for making a particular cementitious composition.
The term “set accelerator” can include any component, which reduces the setting time of a cement composition. For example, the set accelerator may include alkali and alkali earth metal salts, such as a calcium salt. The calcium salt may include calcium formate, calcium nitrate, calcium nitrite or calcium chloride.
The term “encapsulating layer” as used herein can mean any form of coating or binding wherein most of the material being encapsulated is enclosed within the layer and that the dissipation of the material is substantially restricted by the layer. It does not mean that all of the material being encapsulated is enclosed within the layer or that the material being encapsulated cannot leak through the encapsulating layer.
The term oxidizer can include any component which is capable of degrading the retarder present. These include, but are not limited to alkaline earth and zinc salts of peroxide, perphosphate, perborate, percarbonate; calcium peroxide, calcium perphosphate, calcium perborate, magnesium peroxide, magnesium perphosphate, zinc perphosphate; calcium hypochlorite, magnesium hypochlorite, chloramine T, trichloroisocyanuric acid, trichloromelamine, dichloroisocynaurate dihydrate, anhydrous dichloroisocynaurate; and mixtures thereof.
The term “radiation tolerance” as used herein is the amount of ionizing radiation that a material can withstand without noticeable or measurable degradation.
The term “retarder” or “set retarder” can include boronated or non-boronated forms of phosphonic acid, phosphonic acid derivatives, lignosulfonates, salts, sugars, carbohydrate compounds, organic acids, carboxymethylated hydroxyethylated celluloses, synthetic co- or ter-polymers including sulfonate and carboxylic acid groups, and/or borate compounds.
The term “set” as used herein refers to an increase in mechanical strength of a fluid or slurry sufficient to perform a desired result, such as to restrict movement of an item or impede fluid flow or pressure transfer through a fluid. A cement may be referred to as set when it can restrict the movement of a pipe, or impede fluid flow or pressure transfer, regardless of whether the cement has cured to a fully solid composition. A fluid or slurry can be referred to as set when it has thickened to a sufficient level that it achieves the desired result, such as the isolation of a particular zone or the restriction of fluid flow or pressure transfer, regardless of whether it has reached its final consistency.
The present invention may also be useful for cement or concrete in other applications, including infrastructure and building materials, where a quick setting time can be obtained with the polymer system. Some specific examples include rapid hardening of pre-cast units such as pipes, panels, and beams, cast in-situ structures for bridges, dams, or roads, quick-set grout, increased adhesion in cement, addition of water-resistant properties to cement, decorative concrete, rapid concrete repair, production of cement board. Other advantages over typical polymer-enhanced concrete systems include the ability to use a wider variety of polymer species, including oligomers which are significantly less volatile, combustible and toxic, and the elimination of initiators, which are also toxic to humans and the environment.
To facilitate a better understanding of the present invention, the following examples of preferred or representative embodiments are given. In no way should the following examples be read to limit, or to define, the scope of the invention.
Cement slurry samples were prepared by mixing the following ingredients: 400 grams of a class H cement (Lafarge, Joppa Ill.), 160 grams of water (w/c=0.40), 8.0% by weight of solids (bwos) acrylamide, 0.42% bwos N,N-methylene-bis-acrylamide as a crosslinker, 0.50% bwos maltodextrin as a set retarder, 0.50% bwos HR-25 as a set retarder, 0.20% bwos Diutan gum as a rheology modifier, 0.10% bwos SnCl2 as an oxygen scavenger, and 1.0% bwos SYLOID® RAD 2105 silica gel (Grace Performance Chemicals, USA).
The slurry was mixed for 45 seconds on a Waring blade mixer as per the API mixing schedule. The slurry was split into two samples. One sample was exposed for 20 seconds to bremsstrahlung radiation produced by focusing an electron beam of 5-6 MeV energy onto a tungsten target and placing the sample in a vial at the other end of the tungsten target and thereby exposing the sample to the bremsstrahlung photons. The other sample was not irradiated and kept as a control. The control sample remained fluid. The irradiated sample had been crosslinked and displayed a freestanding solid-like behavior.
A cement/sand slurry was prepared similar to that of Example 1, except that the 1% SYLOID RAD particles were not included, and 200 grams of the class H cement was replaced with 200 mesh sand for a 50:50 mixture of cement and silica flour.
The slurry was mixed for 45 seconds on a Waring blade mixer as per the API mixing schedule. The slurry was split into two samples. One sample was exposed for 30 seconds to bremsstrahlung radiation produced by focusing an electron beam of 5-6 MeV energy onto a tungsten target and placing the sample in a vial at the other end of the tungsten target and thereby exposing the sample to the bremsstrahlung photons. The other sample was not irradiated and kept as a control. The control sample remained fluid. The irradiated sample had been crosslinked and displayed a freestanding solid-like behavior.
Silica flour slurry samples were prepared by mixing the following ingredients: 400 grams of SSA-1 silica flour (Halliburton, Houston, Tex.) 168 grams of water (w/c=0.42), 0.18wt % Ca(OH)2 per 100 grams water, 8.0% by weight of solids (bwos) acrylamide, 0.42% bwos N,N-methylene-bis-acrylamide as a crosslinker, 0.20% bwos Diutan gum as a rheology modifier, 0.10% bwos SnCl2 as an oxygen scavenger.
The slurry was mixed for 45 seconds on a Waring blade mixer as per the API mixing schedule. The slurry was split into two samples. One sample was exposed for 30 seconds to bremsstrahlung radiation produced by focusing an electron beam of 5-6 MeV energy onto a tungsten target and placing the sample in a vial at the other end of the tungsten target and thereby exposing the sample to the bremsstrahlung photons. The other sample was not irradiated and kept as a control. The control sample remained fluid. The irradiated sample had been crosslinked and displayed a freestanding solid-like behavior.
The samples demonstrate that bremsstrahlung radiation may be utilized to solidify cement by irradiating a sample of polymerizable additive contained in the cement.
Therefore, the present invention is well adapted to attain the ends and advantages mentioned as well as those that are inherent therein. The particular embodiments disclosed above are illustrative only, as the present invention may be modified and practiced in different but equivalent manners apparent to those skilled in the art having the benefit of the teachings herein. Furthermore, no limitations are intended to the details of construction or design herein shown, other than as described in the claims below. It is therefore evident that the particular illustrative embodiments disclosed above may be altered, combined, or modified and all such variations are considered within the scope and spirit of the present invention. The invention illustratively disclosed herein suitably may be practiced in the absence of any element that is not specifically disclosed herein and/or any optional element disclosed herein. While compositions and methods are described in terms of “comprising,” “containing,” or “including” various components or steps, the compositions and methods can also “consist essentially of” or “consist of” the various components and steps. All numbers and ranges disclosed above may vary by some amount. Whenever a numerical range with a lower limit and an upper limit is disclosed, any number and any included range falling within the range is specifically disclosed. In particular, every range of values (of the form, “from about a to about b,” or, equivalently, “from approximately a to b,” or, equivalently, “from approximately a-b”) disclosed herein is to be understood to set forth every number and range encompassed within the broader range of values. Also, the terms in the claims have their plain, ordinary meaning unless otherwise explicitly and clearly defined by the patentee. Moreover, the indefinite articles “a” or “an,” as used in the claims, are defined herein to mean one or more than one of the element that it introduces. If there is any conflict in the usages of a word or term in this specification and one or more patent or other documents that may be incorporated herein by reference, the definitions that are consistent with this specification should be adopted.