High energy density double layer energy storage devices

Abstract

The present invention relates to lignocellulosic-based carbon-containing double layer energy storage devices having improved electrical energy densities. In particular, the invention provides a double layer energy storage cell comprising a pair of electrodes, at least one of which is a carbon paste electrode, a porous ionically conductive separator, and an ion insulating collector, the improvement wherein said carbon paste electrode includes an activated lignocellulosic-based carbon having a pore volume of greater than about 0.45 cc/g, a median pore width of less than 2.0 nm, a specific surface area of greater than about 500 m.sup.2 /g, and a micropore content, based on the total particle volume of the activated carbon, of greater than about 75%.

Description

FIELD OF THE INVENTION

The present invention relates to double layer energy storage devices. In particular, the invention relates to lignocellulosic-based carbon-containing, double layer energy storage devices having improved electrical energy densities.

BACKGROUND OF THE INVENTION

Activated carbon is a microcrystalline, nongraphitic form of carbon which has been processed to increase internal porosity. Activated carbons are characterized by a large specific total surface area (typically in the range of 500-2500 m.sup.2 /g). Such large surface areas make activated carbons useful in a number of applications, including electrical energy storage devices.

The available surface area of activated carbon is dependent on its pore volume. Since the surface area per unit volume decreases as individual pore size increases, large surface area generally is maximized by maximizing the number of pores of very small dimensions and/or minimizing the number of pores of very large dimensions. Pore sizes are defined herein as micropores (pore width<2.0 nanometers or nm), mesopores (pore width=2.0 to 50.0 nm), and macropores (pore width>50.0 nm).

This invention relates to enhancing the energy densities in electrical energy storage devices of the general type disclosed in U.S. Pat. Nos. 3,536,963, 3,634,736, 3,648,126, 4,542,444, and 5,144,537 (which are hereby incorporated by reference) via the utilization of lignocellulosic-based activated carbons. These devices, which are commonly known as carbon double layer capacitors or CDLCs, are usually comprised of a pair of electrodes (at least one of which is a carbon paste electrode), a separator, and an ionic-insulating, electric current-conducting collector.

The carbon paste electrode in a CDLC is generally manufactured by mixing finely divided petroleum-derived carbon particles with an electrolyte to form a paste, and then subsequently forming an electrode from the paste. While the use of activated petroleum-derived carbons in CDLCs is well-known, the practical use of activated lignocellulosic-based carbons (particularly lignocellulosic-based carbons derived from wood) in CDLCs has, until now, only been the subject of theoretical speculation.

The use of carbon double layer capacitors in various applications is well established. Such capacitors can be described in terms of their energy density (kilowatt hour/kg) and power density (watts/kg) characteristics. High energy density capacitors store a relatively high capacitance which is discharged slowly over a period of minutes. In contrast, high power density capacitors can deliver their capacitance or energy quickly (in a few milliseconds). Various practical applications have different requirements in terms of energy and power. For example, memory back-up devices require a reasonably high energy density, but do not require that the energy be released quickly (low power, long discharge time). On the other hand, an application such as starting an automobile engine requires very high power and much of the energy must be released in a few milliseconds. Other applications require combinations of energy and power densities intermediate to these two extremes.

While activated carbons having high surface areas are employed in conventional carbon double layer capacitors, it has not been recognized that certain types of activated carbons have a large and demonstrable effect upon the energy and deliverable power densities of the devices. It has now been discovered that utilizing carbons with high microporosity in a CDLC can significantly increase the energy density while decreasing the discharge time of the device.

It is, therefore, an object of this invention to provide high energy carbon double layer capacitors with enhanced energy densities.

It is a further object of this invention to provide improved high energy density CDLCs which incorporate activated carbons derived from lignocellulosic materials which exhibit relatively specific pore volumes and mean pore radiuses.

SUMMARY OF THE INVENTION

The above objects of the invention are achieved, unexpectedly, by the activation of lignocellulosic material, with a chemical activation agent in a manner to effectively minimize the macropore and mesopore structure of the activated carbon while maximizing the micropore structure of the carbon. A final densification step is undertaken wherein the activated carbon is heated under an inert atmosphere at a temperature from about 900.degree. C. to about 1120.degree. C. This densification step produces carbons with improved characteristics which make these carbons more suitable for use in CDLCs than previously known lignocellulosic materials (particularly wood-based lignocellulosic materials). These improved characteristics include:

a) a decrease in the electrical resistance of the carbon, b) an increase in the capacitance of the carbon, c) an increase in the deliverable energy density of the carbon, d) an increase in the density of the carbon, and e) a decrease in the amount of oxygen bound on the surface of the carbon.

DESCRIPTION OF THE DRAWINGS

FIG. 1 is an exploded view of a single cell carbon double layer capacitor of the invention.

FIG. 2 is a level sectional view schematically showing an assembled single cell carbon double layer capacitor of the type shown in FIG. 1 with a partial showing in section of a housing and contact arrangement.

In FIGS. 1 and 2, the single cell carbon double layer capacitor 5 depicted consists of a pair of electrode subassemblies 10 and 11. Each electrode subassembly includes an electric conducting and ionic insulating collector member 12, a gasket 14, and a carbon paste electrode 13. The collector member 12 can be made of virtually any impervious conducting material. The primary functions of collector member 12 are as a current collector and an inter-cell ionic insulator. Accordingly, collector member 12 is characterized by its electrical conducting property and its chemical inertness to the particular electrolyte employed at the potential impressed upon it.

Annular means or gasket 14 is preferably sealingly bonded by an adhesive to collector member 12. Since electrode 13 is not a rigid mass (but is to some extent flexible), the primary function of gasket 14 is to confine the expansion and contractions of electrode 13. It is preferred that gasket 14 be made of a flexible, insulating material.

A separator 15 is positioned between subassemblies 10 and 11.

Carbon paste electrode 13 consists of an activated, high surface area, lignocellulosic-based carbon and an electrolyte associated therewith.

In FIG. 2 there is a partial showing of one embodiment of a housing and contact structure for the single cell capacitor 5. A metal housing 18 is crimped about the cell 5 and associated contact arrangement. The contact arrangement comprises a first contact plate 19 and its terminal 24 in electrical contact with one collector 12. A second contact plate 21 having a terminal 25 and a bore 28 there through is insulated from contact plate 19 by non-conductive member 22; but is in electrical contact with the other collector 12 through contact with the conductive metal housing 18 which physically and electrically contacts the other collector 12. Terminal 24 extends through non-conductive member 22 and centrally through bore 28 without touching the wall thereof (thereby avoiding shorting contact).

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The double layer energy storage cell with improved energy density is comprised of a pair of electrodes wherein at least one of said electrodes being a carbon paste electrode, a porous ionically conductive separator, and an ion insulating collector, the improvement wherein said carbon paste electrode comprises an activated lignocellulosic-based carbon having a pore volume of greater than about 0.45 cc/g, a median pore width of less than 2.0 nm, a specific surface area of greater than about 500 m.sup.2 /g, a micropore content, based on the total particle volume, of greater than about 75%, and a total combined mesopore and macropore content, based on the total particle volume, of less than about 25%.

As noted, the novel high energy density CDLCs incorporate lignocellulosic-based activated carbons characterized by having a pore volume of greater than about 0.45 cc/g (based on pores having a diameter of less than 1000 angstroms), a median pore width of less than 2.0 nm, and a specific surface area of greater than about 500 m.sup.2 /g. Preferably, the carbons exhibit a pore volume of greater than 0.50 cc/g and a specific surface area of about 1,000 to about 2,500 m.sup.2 /g.

These activated carbons also exhibit (based on the total pore volume) a micropore content of greater than about 75%, preferably greater than about 90%, and more preferably greater than about 99%. Correspondingly, such activated carbons would also exhibit a total combined mesopore and macropore content of less than 25%, preferably less than 10%, and more preferably less than 1% (based on the total pore volume).

In order to increase the surface areas of natural occurring carbonaceous material these carbons are subjected to an activation process. Such activation of the raw material is commonly accomplished via either chemical or thermal activation processes. Examples of such activation processes are taught in commonly assigned U.S. Pat. Nos. 4,107,084, 4,155,878, 5,212,144, and 5,270,017; which are hereby incorporated by reference.

The effective porosity of activated carbon produced by thermal activation is the result of gasification of the carbon at relatively high temperatures (after an initial carbonization of the raw material), while the porosity of chemically activated products generally is formed by chemical dehydration/condensation reactions occurring at significantly lower temperatures. Chemical activation typically is carried out commercially in a single kiln. The raw material precursor is impregnated with a chemical activation agent, and the blend is heated to a temperature of 450-700.degree. C. Chemical activation agents reduce the formation of tar and other by-products, thereby increasing yield.

Suitable raw lignocellulosic material precursors for use during chemical activation in the invention include hardwood, softwood, lignin, nut shells, nut pits, and the like, and various combinations thereof. Wood-based materials are preferred precursors; with the more preferred precursors being wood-based materials such as wood chips, wood flour, wood dust, sawdust, and combinations thereof.

Suitable chemical activation agents include alkali metal hydroxides, carbonates, sulfides, and sulfates; alkaline earth carbonates, chlorides, sulfates, and phosphates; phosphoric acid; polyphosphoric acid; pyrophosphoric acid; zinc chloride; sulfuric acid; oleum; and combinations thereof. Preferred among these agents are phosphoric acid and zinc chloride. Most preferred is phosphoric acid.

It is known in the art how to manipulate the activation processes to obtain carbons having a general preponderance of a desired pore volume (see, generally: U.S. Pat. Nos. 4,677,086, 5,204,310, 5,206,207, 5,250,491, 5,276,000, and 5,304,527; which are hereby incorporated by reference). However, the carbons produced via the methods taught in these references have proven to be unsuitable for use in CDLCs. Indeed, it has now been discovered that such carbons must undergo the additional densification step taught herein in order to acquire the characteristics necessary for successful incorporation into CDLCs.

The present method for producing the carbons can be described generally by the following sequence of steps:

A. Activating agent/lignocellulose material blending, B. Activation, and C. Heat treatment (densification).

The amounts of activating agent and lignocellulose material to be blended together in Step A will, of course, depend upon the actual types of agents and materials utilized. The blending of Step A is generally conducted at from about 35.degree. C. to about 95.degree. C. for a period of up to one hour. Suitable activating agent to lignocellulose material weight ratios are in the range of 1.2:1 to 0.3:1, respectively. The preferred activating agent to lignocellulose material ratios are in the range of about 0.9:1 to about 0.5:1, respectively.

The activation of Step B is generally to a temperature of about 480.degree. C.

As noted above, during the heat treatment (or densification) of Step C the activated carbon is heated under an inert atmosphere (or flue gas) at a temperature from about 900.degree. C. to about 1120.degree. C.; with the preferred temperature range being from about 990.degree. C. to about 1120.degree. C., and the most preferred temperature range being from about 1065.degree. C. to about 1120.degree. C. This densification step is generally conducted for a period greater than about 20 minutes (preferably between about 20 to about 60 minutes).

While the carbons having the capability of delivering enhanced energy densities are useful in producing the carbon paste utilized in CDLCs of the type generally disclosed in the above-noted U.S. patents, these carbons may also be useful in other types of electrical devices which employ carbons as electrodes (such as batteries, fuel cells, etc.). A typical CDLC is comprised of: (1) a pair of electrodes where at least one of the electrodes (and preferably both electrodes) is a carbon paste electrode, (2) a porous ionically conductive separator, and (3) an ion-insulating collector to electrically contact the electrodes. A single cell or a plurality of cells can comprise an energy storage device.

Electrolytes suitable for use in producing improved high energy density CDLCs containing the carbons having the capability of delivering enhanced power densities consist of any highly ionically conductive medium such as an aqueous solution of an acid, salt, or a base. If desired, non-aqueous electrolytes (wherein water is not utilized as a solvent) can also be used.

The electrolyte in the electrode structure serves three general functions: (1) as a promoter of ion conductivity, (2) as a source of ions, and (3) as a binder for the carbon particles. Sufficient electrolyte should be used to accommodate these functions (although a separate binder can be used to perform the binding functions).

While higher energy densities are obtained when the novel carbon is employed in both cell electrodes, enhanced energy density can be achieved even where one electrode is composed of other materials known in the art. The preparation and use of such non-carbon electrodes are described in U.S. Pat. Nos. 3,634,736 and 3,648,126.

The ion-insulating, electric current collector can be any conducting material which is impervious to ionic conductivity. Suitable materials for use in producing these collectors include: carbon, copper, lead, aluminum, gold, silver, iron, nickel, tantalum, conducting polymers, non-conductive polymers filled with conducting material so as to make the polymer electrically conductive, and the like. Preferred are carbon or graphite loaded butyl rubbers or carbon filled polycarbonates. The collector should be electrically connected to an electrode.

Between the electrodes is a separator generally made of a highly porous material which functions as an electronic insulator between the electrodes while affording free and unobstructed movement to the ions in the electrolyte. The pores of the separator must be small enough to prevent electrode-to-electrode contact between the opposing electrodes (as such a condition would result in a short circuit and consequent rapid depletion of the charges accumulated on the electrode). Generally, any conventional battery separator is suitable for use in the high energy density CDLC. The separator can also be an ion-permeable membrane which allows ions to pass there through, but prevents electrons from passing there through.

The invention method for producing the improved high energy density CDLCs is disclosed in the following examples. These examples are provided to further illustrate the present invention and are not to be construed as limiting the invention in any manner.

EXAMPLE 1

Multiple batches of the novel activated carbons were prepared by repeatedly mixing 1,177 g of concentrated phosphoric acid solution (85-86% concentration) with 1,950 g of sawdust (43% moisture) for an acid:sawdust ratio of 0.9:1 (by dry weight of their respective solids) and stirring for 30 minutes at 80-95.degree. C., after which the mixture (a mass of discreet sawdust particles) was transferred to shallow glass trays and spread into a 1-1.5 cm thick layers for continued heating in an oven. Heat treatment was continued at 70.degree. C. for about 36 hours, at which time the material began transition from plastic to thermoset (i.e., product appears dry and not sticky).

Activation of the thermoset char was performed in a bench-scale, direct-fired rotary kiln by gradually raising the temperature to about 480.degree. C. Subsequently, the activated carbon was allowed to cool, washed with water, and dried.

The activated carbons were subjected to final densification step at different temperatures. A rotary kiln was heated to a temperature between either: 1) about 945.degree. C. to about 985.degree. C. (these samples are hereafter designated by the letter "A"), or 2) between about 1065.degree. C. to about 1120.degree. C. (samples "B"). Activated carbon was added to the kiln under an "inert" atmosphere maintained by a flow of nitrogen gas (0.5 cu ft/min) through the kiln. The off gases from the carbon were ignited and generally burned. After about 40 minutes the carbon was dumped under nitrogen into a purge pot and maintained under nitrogen until the carbon cooled to near ambient temperature.

These carbons were used to produce a series of carbon paste electrodes (as described below). The electrodes were utilized to assemble a series of CDLCs for evaluation, the results of which are noted in Table I below.

An electrolyte mixture of H.sub.2 SO.sub.4 (38% by weight) and water was slowly added to about 100 grams of carbon until the carbon was contained in a large excess of electrolyte. The carbon was allowed to soak in the electrolyte for approximately 48 hours under ambient pressure. The carbon was then vacuum filtered through a Buchner funnel to remove some of the excess electrolyte so that the carbon/electrolyte mixture became a paste. The carbon paste was then placed in a compression fixture with the fixture placed in a hydraulic press and compressed at about 3400 psi to remove excess electrolyte. A carbon aggregate was obtained which was removed from the compression fixture and granulated through a 400 (0.37 mm) mesh sieve.

A gasket, stamped out of a sheet of non-conductive butyl rubber, was submitted to a flat circular sheet of a conductive butyl rubber using an industrial adhesive. The nonconductive and conductive butyl rubbers are commercially available. The nonconductive butyl rubber gasket had internal diameter of 0.75 inches and an external diameter of 1.0 inch. The circular sheet of conductive butyl rubber had a thickness of about 0.004 inches (0.1 cm) and a diameter of about 1.0 inch.

Approximately 0.25 grams of the carbon paste granulate was placed into the cavity created by the gasket and the circular sheet of butyl rubber and compressed under a pressure of about 400 psi. A pair of such electrode assemblies were prepared and a polypropylene separator having a thickness of 0.001 inches and a diameter of about 1.0 inch was interposed between the electrode assemblies. The electrode assemblies, each having a carbon paste electrode, were adhered together with an adhesive to form a CDLC having two carbon paste electrodes. Three of these one-volt CDLC cells were connected in series and evaluated. The results are recorded in Table I below.

TABLE I______________________________________ Power EnergySample Current Resistance Capacitance Density DensityNo..sup.1 (amps).sup.2 (ohms).sup.3 (farads) (w/Kg) (whr/Kg)______________________________________Control 0.03 1.102 2.070 15.89 0.904 1.00 1.102 0.086 338.98 0.015 3.00 1.102 0.000 0.00 0.0001A 0.03 0.204 2.64 16.30 1.170 1.00 0.204 2.22 499.00 0.860 3.00 0.204 2.14 1279.00 0.6102A 0.03 0.265 3.26 16.02 1.450 1.00 0.265 2.83 488.40 1.050 3.00 0.265 2.76 1181.30 0.6652B 0.03 0.206 2.05 16.04 0.911 1.00 0.206 1.67 498.90 0.646 3.00 0.206 1.44 1276.00 0.4003A 0.03 0.301 2.85 16.02 1.260 1.00 0.301 2.41 482.00 0.870 3.00 0.301 2.43 1123.00 0.5323B 0.03 0.262 2.08 16.03 0.875 1.00 0.262 1.42 494.30 0.585 3.00 0.262 1.07 1234.00 0.3054A 0.03 0.350 3.62 16.01 1.600 1.00 0.350 3.02 473.00 1.050 3.00 0.350 3.00 1044.60 0.5654B 0.03 0.242 2.79 16.03 1.240 1.00 0.242 2.16 492.50 0.815 3.00 0.242 1.62 1218.00 0.4165A 0.03 0.325 4.26 19.04 1.890 1.00 0.325 3.39 477.70 1.200 3.00 0.325 3.21 1084.80 0.6505B 0.03 0.266 2.57 16.02 1.140 1.00 0.266 1.94 488.21 0.720 3.00 0.266 1.31 1382.90 0.3106A 0.03 0.333 2.71 16.01 1.200 1.00 0.333 2.65 476.30 0.934 3.00 0.333 2.71 1072.00 0.5386B 0.03 0.201 2.09 16.03 0.929 1.00 0.201 1.64 500.00 0.637 3.00 0.201 1.09 1284.00 0.311______________________________________ .sup.1. The control sample was not subjected to a final densification step. The A samples were subjected to a final densification step at a temperature between about 945.degree. C. to about 985.degree. C., while the B samples were densified at a temperature between about 1065.degree. C. to about 1120.degree. C. .sup.2. Current density can be calculated by dividing the current (amps) by the surface area of the electrode cell (about 2.85 cm.sup.2). .sup.3. Resistance was measured by impedance at 1000 hz.

The results can be interpreted in view of the following two equations:

E=1/2C(V-iR).sup.2 ; and P=1/2i(V-iR); where: E=energy, P=power, C=capacitance, V=voltage, i=current, and R=resistance.

An increased capacitance resulted in a increased energy density than that obtained by the control sample. Likewise, a lowered resistance resulted in a higher power density. Therefore, as the data in Table I clearly indicate, the CDLCs made with the novel activated carbons achieved much higher energy densities than did the control CDLCs made with standard (control) carbon.

EXAMPLE 2

A series of carbons were prepared following the procedure listed in Example 1. These carbons were subsequently evaluated, and the results of the evaluations are shown in Table II below.

TABLE II______________________________________Surface Area and Pore Volume of Dry Carbon Samples % of carbon BET.sup.1 DFT.sup.2 having pore surface area surface area Pore volume volumes lessSample (m.sup.2 /g) (m.sup.2 /g) (cc/g) than 2 nm______________________________________Control.sup.3 1823 1470 0.90 931 1270 1110 0.60 932 1240 1150 0.56 1003 1440 1270 0.64 974 1480 1230 0.65 995 1520 1240 0.67 96______________________________________ .sup.1 Determined using standard Brunauer Emmet Teller method. .sup.2 Determined using standard Density Functional Theory method. .sup.3 The control sample carbon was not subjected to a final densification step.

These carbons were used to produce a series of carbon paste electrodes via the procedure noted in Example 1 with the following modifications. All carbon samples were dried in a vacuum oven at 200.degree. C. prior to being mixed with an organic electrolyte (1M tetraethylammonium tetrafluoroborate in gammabutyrolactone). The collector material employed in the CDLC cells consisted of a polymer-coated aluminum collector and a polyolefin membrane as the separator. The electrode was loaded at about 0.2-0.3 g per half cell.

The electrodes were utilized to produce a series of CDLCs for evaluation. Table III lists the resistances, gravimetric capacitances, and energy densities of the various carbons measured at 2 volts. The gravimetric capacitances reported in Table III were calculated by dividing the capacitance of the mass of dry carbon. The reported energy densities are based upon the weight of dry carbon electrodes and were calculated using the same equation listed in Example 1 above. Gravimetric capacitance and energy density was measured at a current density of 2 mA/cm.sup.2.

TABLE III______________________________________Electrical Properties of Activated Carbons Energy Resistance Capacitance DensitySample (ohms) (Farads/g) (kwh/Kg)______________________________________Control* 8.0 36 19.11 1.1 56 30.72 1.0 69 38.03 0.7 88 48.44 0.8 79 43.45 0.7 90 49.6______________________________________ *The control sample carbon was not subjected to a final densification step.

As shown in Table III above, greatly improved energy densities were obtained in those CDLCs containing carbons which had been subjected to a final densification. Capacitance values vary between 50-90 Farads/g and surface area from 1000-1270 m.sup.2 /g by as calculated using the standard Density Functional Theory.

Many modifications and variations of the present invention will be apparent to one of ordinary skill in the art in light of the above teaching. It is understood therefore that the scope of the invention is not to be limited by the foregoing description but rather is to be defined by the claims appended hereto.

Claims

1. A double layer energy storage cell with improved energy density, said cell comprising a pair of electrodes wherein at least one of said electrodes being a carbon paste electrode, a porous ionically conductive separator, and an ion insulating collector, the improvement wherein said carbon paste electrode comprises an activated lignocellulosic-based carbon having a pore volume of greater than about 0.45 cc/g, a median pore width of less than 2.0 nm, a specific surface area of greater than about 500 m.sup.2 /g, and a micropore content, based on the total particle volume of the activated carbon, of greater than about 75%.

2. The cell of claim 1 wherein the activated carbon exhibits a pore volume of greater than about 0.50 cc/g.

3. The cell of claim 1 wherein the activated carbon exhibits a specific surface area of about 1,000 m.sup.2 /g to about 2,500 m.sup.2 /g.

4. The cell of claim 1 wherein the activated carbon exhibits, based on the total particle volume of said activated carbon, a micropore content of greater than about 90%.

5. The cell of claim 1 wherein the activated carbon exhibits, based on the total particle volume of said activated carbon, a micropore content of greater than about 99%.

6. The cell of claim 1 wherein the carbon paste electrode contains an aqueous electrolyte.

7. The carbon paste electrode of claim 6 wherein the lignocellulosic-based carbon is derived from wood.

8. A double layer energy storage cell with improved energy density comprising a plurality of electrical double layer energy storage cells, said cells each comprising a pair of electrodes wherein at least one of said electrodes being a carbon paste electrode, a porous ionically conductive separator, and an ion insulating collector, the improvement wherein said carbon paste electrode comprise an activated lignocellulosic-based carbon having a pore volume of greater than about 0.45 cc/g, a median pore width of less than 2.0 nm, a specific surface area of greater than about 500 m.sup.2 /g, a micropore content based on the total particle volume of the activated carbon, of greater than about 75%.

9. The cell of claim 8 wherein the activated carbon exhibits a pore volume of greater than about 0.50 cc/g.

10. The cell of claim 8 wherein the activated carbon exhibits a specific surface area of about 1,000 m.sup.2 /g to about 2,500 m.sup.2 /g.

11. The cell of claim 8 wherein the activated carbon exhibits, based on the total carbon particle volume of said activated carbon, a micropore content greater than about 90%.

12. The cell of claim 8 wherein the activated carbon exhibits, based on the total carbon particle volume of said activated carbon, a micropore content of greater than about 99%.

13. The cell of claim 8 wherein the carbon paste electrode contains an aqueous electrolyte.

14. The carbon paste electrode of claim 8 wherein the lignocellulosic-based carbon is derived from wood.