Patent Grant
7767779
1) Field of the Invention
The present invention relates to a rigid, optically transparent, high index, impact resistant polythiourethane/urea material, which is particularly suited for making optical articles such as sun lenses, ophthalmic lenses and protective lenses.
2) Background of the Invention
Plastic materials are widely used in the optical field and particularly in the ophthalmic field for their lightness, high impact resistance and tintable capability by immersion in a bath containing an organic dye.
Optically transparent plastic materials having a high refractive index, higher than 1.53, are of major interest since they render it possible to manufacture optical articles such as lenses of lower thickness for an equivalent corrective power (optical power).
Of course, this increase in refractive index of the material shall not be at the expense of the other valuable properties such as transparency and impact resistance of the material.
Preferably, other required properties for the lens material are
U.S. Pat. No. 6,127,505 discloses a transparent, non-elastomeric, high index, high impact resistant polyurethane material which is a reaction product of:
Unfortunately, the polyurethanes obtained have relatively low refractive index,
of at most 1.53.
Thus, the aim of the present invention is i.a. to provide an optically transparent, rigid, high index, impact resistant material that would particularly be useful for making optical articles.
By high refractive index material, there is intended in the present invention a material having a refractive index,
higher than 1.53, preferably of at least 1.55 and most preferably of at least 1.57.
The above objective is reached according to the invention by providing a transparent, non elastomeric, high refractive index, impact resistant polythiourethane/urea material comprising the reaction product of:
The invention further concerns optical articles such as sun lenses, ophthalmic lenses and protective lenses made of the polythiourethane/urea material defined above.
The (α,ω))-diiso(thio)cyanate prepolymer is preferably an (α,ω)-diiso (thio)cyanate cycloaliphatic or aromatic prepolymer and most preferably such a prepolymer containing one or more sulfur atoms in its chain.
These prepolymers can be prepared by reacting an (α, ω)-diol or dithiol prepolymer, preferably further containing at least one sulfur atom in its chain, with one or more cycloaliphatic or aromatic diisocyanate or diisothiocyanate according to the following scheme:
(α, ω)-di-XH prepolymer (I)+cycloaliphatic or aromatic di-NCX (II)→(α, ω)-di-NCX prepolymer (III) with X=O or S.
The preferred prepolymers (I) are (α,ω)-dithiol prepolymers, further containing at least one sulfur atom in their chains.
Among these prepolymers there could be cited the following prepolymers:
where x and y are such that
in which R1 and R2 are, independently from each other, H, alkyl, aryl, alkoxy, alkylthio or arylthio; R3 and R4 are, independently from each other,
Ra designates H, alkyl, aryl, alkoxy, aryloxy, alkylthio or arylthio and, n is an integer from 0 to 4 and m is an integer from 1 to 6, and
Prepolymers of formula:
where n is such that the number average molecular weight (
where n is such that the number average molecular weight (
A preferred class of diepisulfides is comprised of diepisulfides of formula:
in which R1, R2, R3 and R4 are defined as above.
In R1, R2, R3 and R4 the alkyl and alkoxy groups are preferably C1-C6, more preferably C1-C4 alkyl and alkoxy groups such as methyl, ethyl, propyl, butyl, methoxy, ethoxy, propoxy and butoxy.
The preferred diepisulfides are those of formula:
and hyperbranched prepolymers resulting from the polymerization of the above mentioned diepisulfides, in particular diepisulfides of formulas (I″b) with DMES.
The prepolymers of formula (Ic) constitute a new class of polysulfides. These new soft polysulfides have high refractive indexes and can be prepared by thermal and/or photopolymerization, in the presence of an initiator, of 2-mercaptoethylsulfide (DMES) corresponding formula HS—CH2CH2—S—CH2CH2—SH and allylsulfide (AS) corresponding formula CH2═CHCH2—S—CH2—CH═CH2.
Preferably, prepolymers of formula (Ic) are prepared by photopolymerization in the presence of a photoinitiator.
The refractive index of these prepolymers (Ic) typically ranges from 1.57 to 1.62, preferably from 1.59 to 1.615.
Photopolymerization of prepolymers of formula (Id) is effected by mixing DMES and AS in the required proportions, such that the molar ratio Allyl is less than 2, preferably less than 1 and more preferably less than 0.8, adding at least one photoiniator and irradiating the mixture, preferably with an UV light. Preferably, UV light wavelength will range from 320 to 390 nm. UV light intensity typically ranges from 40 mW to 90 mW and total exposure time to UV light, either in one shot or several shots, ranges from 250 to 1650 seconds, preferably 300 to 1500 and more preferably 600 to 1000 seconds.
Any classical photoinitiator, in usual amount can be used for the photopolymerization process. Preferred photoinitiators are 1-hydroxycyclohexyl phenyl ketone (Irgacure® 184) and 2-hydroxy-2-methyl-1-phenylpropan-1-one (Darocur® 1173). The amount of photoinitiator used will usually range from 0.05% to 10% by weight, preferably from 1% to 5%, and more preferably from 1 to 2% by weight, based on the total weight of the polymerizable monomers present in the polymerization mixture.
Although the photoinitiator may be added to the polymerization mixture in one shot, generally before starting irradiation, it is preferred to add the photoinitiator in several shots during irradiation process of the mixture. With the addition of the photoinitiator in several shots, higher conversion rates of the allylsulfide and higher refractive indexes are obtained.
Similarly, thermal polymerisation is effected by simply mixing appropriate amounts of DMES and AS, adding to the mixture an effective amount of at least one thermal radical initiator, and heating the mixture at a temperature ranging from 30° C. to 80° C., preferably from 40° C. to 70° C. Any classical thermal initiator can be used, such as di(4-tert-butylcyclohexyl) peroxydicarbonate (P16S) and 2,2′-azobisisobutyronitrile (AIBN) in usual amounts.
Typically, the amount of thermal initiator will range from 0.05 to 10%, preferably 1 to 8%, by weight of the polymerizable monomers present in the mixture.
The thermal initiator may be added to the mixture in one shot at the beginning of the polymerisation or in several shots during the course of the polymerization process.
Polymerization is usually effected by bulk polymerization process but it can also be a solution polymerization process using any appropriate solvent or mixture of solvents. A preferred solvent is tetrahydrofuran (THF).
The cycloaliphatic or aromatic diiso(thio)cyanate (II) may be a cycloaliphatic or aromatic diisocyanate or a cycloaliphatic or aromatic diisothiocyanate or a mixture thereof.
Among the preferred cycloaliphatic diiso(thio)cyanate, there may be cited bis(iso(thio)cyanatemethyl) cyclohexane hexamethylene diiso(thio)cyanate and dicyclohexylmethane diiso(thio)cyanate and mixtures thereof.
The most preferred cycloaliphatic diisocyanate is Desmodur® W of formula:
and the corresponding diisothiocyanate of formula:
Among the aromatic diiso(thio)cyanates, there may be cited toluene diiso(thio)cyanate, phenylene diiso(thio)cyanate, ethylphenylene diiso(thio)cyanate, isopropylphenylene diiso(thio)cyanate, dimethylphenylene diiso(thio)cyanate, diethylphenylene diiso(thio)cyanate, diisopropylephenylene diiso(thio)cyanate, xylylene diiso(thio)cyanate, 4,4′-diphenylmethane diiso(thio)cyanate, naphtalene diiso(thio)cyanate.
The preferred aromatic diiso(thio)cyanate is xylylene diisocyanate (XDI).
The most preferred cycloaliphatic and aromatic diiso(thio)cyanates are Desmodur® W or the corresponding diiso(thio)cyanate or mixtures of these compounds with xylylene diisocyanate.
Usually, the molar ratio NCX/XH of the iso(thio)cyanate group to the hydroxyl or thiol group, during the reaction, ranges from 1.9 to 4.5, preferably from 3 to 3.5.
The reaction of prepolymer (I) and monomer (II) can be effected with or without a polymerization catalyst. Usually, the polymerization is effected at temperature ranging from 50 to 120° C. When no catalyst is used, of course, higher temperatures and longer times of polymerization are required.
Catalyst may be any known catalyst for the polymerization of the monomer.
Among the useful catalysts, there may be cited dimethyltindichloride, dibutyltindichloride and dibutyltindilaurate, cocatalysts or promoters such as N,N-dimethylcyclohexylamine and 1,4-diazabicyclo-[2,2,2]-octane (DABCO) could also be used with the catalyst to enhance its activity.
To prepare the final polythiourethane/urea material according to the invention, the (α,ω)-di-NCX prepolymer (III) is reacted with an aromatic primary diamine according to the following scheme:
(α, ω)-di-NCX prepolymer (III)+aromatic di-NH2 (IV)→final material X═O or S
During this reaction step, in order to obtain the best properties of impact resistance for the material, it is preferred that the molar ratio NH2/NCX be kept in the range of 0.90 to 1.10 and preferably 0.93 to 0.95.
Among the aromatic primary diamines (IV) that may be used in the second reaction step, preferred aromatic diamines are those which include at least one sulfur atom in their molecules.
Among these sulfur containing aromatic amines there may be cited the amines of formula:
and mixtures thereof;
in which R represents a hydrogen atom or an alkyl group, preferably a C1 to C6 alkyl group and more preferably a methyl group, and
R′ is an alkyl group, preferably a C1 to C6 alkyl group, and more preferably a methyl group.
It is possible to replace part of the polyurea segments of the final material by adding one or more of the following monomers to the aromatic diamine in the second step of polymerization.
Thus, a polyurea segment can be replaced by a hard urethane and/or a thiourethane segment by adding a cycloaliphatic or aromatic diisocyanate such as xylylène diisocyanate and/or a diol or a dithiol such as:
HS—CH2CH2—S—CH2CH2—SH
A polyurea segment can also be partly replaced by highly crosslinked areas by adding to the amine during the second step of polymerization tri and tetra alcohols and/or thiols such as:
or polythiols such as those of formula:
and mixtures thereof,
or polyols such as those of formula:
HO—CH2—CHOH—CH2OH
HS—CH2—CHOH—CH2OH
HS—CH2CHOH—CHOH—CH2—SH
This second reaction step is effected by simply mixing prepolymer (III) with the diamine (IV) and the optional additional monomers, if any, and by heating at a temperature above 100° C., generally ranging from 100° C. to 130° C. up to the obtention of the final cured polythiourethane/urea material.
Conventional additives such as inhibitors, dyes, UV absorbers, perfumes, deodorants, antioxydants, antiyellowing agents and release agents may be added to the material of the present invention in the usually used quantities.
These additives may be added either in the first step or in the second step of preparation of the final material, but are preferably added during the second step.
The following examples illustrate the present invention. In the examples, unless otherwise stated, all parts and percentages are by weight.
I.1 Preparation of polysulfides PS1 to PS7.
The polymerization reaction between AS and DMES was carried out in the presence of a photoinitiator, under UV. The equipment used to generate the UV light was an EFOS Ultracure 100 SS PLUS equipped with an optic fiber (lamp #320-60651).
The UV light was shined above the surface of the monomer mixture. The light intensities reported were measured using a UV-MO2 irradiance meter equipped with a UV-35 sensor (320-390 nm sensing wavelength). Several experimental conditions were studied in order to maximize the refractive index of the reaction product as well as the allyl conversion. The experimental conditions and the results are reported in Table I.
Two photoinitiators were tried: 1-hydroxycyclohexyl phenyl ketone (Irgacure® 184) and 2-hydroxy-2-methyl-1-phenyl-propan-1-one (Darocur® 1173). As shown in Table 1 (runs PS1 and PS2), a significant increase of the refractive index of the mixture was noticed in both cases. The refractive index of the polymer made was about the same between the two initiators. Darocur® 1173 is a liquid that is easier to handle and to disperse in the monomer mixture than Irgacure® 184 (which is a powder). Thefore, Darocur® 1173 is preferably used in the experiments.
Allyl conversion is measured by FTIR according to the following formula:
The 1636 cm−1 signal corresponds to the allyl group. The 1672 cm−1 signal corresponds to the phenyl groups of the photoinitiator and was used as an internal reference.
As shown in Table I (PS2 and PS3), the refractive index of the polymer made shows a slight increase when the photoinitiator concentration is varied between 1.0% and 2.1%.
The increase of the UV intensity from 40 mW to 90 mW results in slight increase of the refractive index of the polymer and a higher conversion of the allyl groups (Table I, PS4 and PS5). On the other hand, the increase of the UV exposure time from 600 s to 960 s resulted in a significant increase of both the refractive index and the allyl groups conversion (Table I, PS6 and PS7).
As reported in Table I, PS6 and PS7 where polymerized with the same amount of photoinitiator added to the monomer mixture, either in five shots (PS6) or in one shot (PS7). The results show that the increase of the refractive index of the polymer and the conversion of the allyl groups were much higher when the photoinitiator was added in five shots. Under these conditions, a refractive index (nD25) of 1.5974 and an allyl conversion of 93% were reached.
I.2 Preparation of Polysulfides PS8 to PS10
The polymerization reaction between AS and DMES was carried out as previously mentioned using the quantities and conditions indicated in Table II. In particular a fusion lamp system equipped with a D Bulb was used for polymerizing PS10.
I.3 Preparation of polysulfides PS11 to PS13
The polymerization reaction between AS and DMES was usually carried out in bulk or in the presence of tetrahydrofuran (THF) as a solvent, with the conditions indicated in Table III.
The allyl conversion in the final product was similar to the one obtained in the absence of THF.
I.4 Preparation of polysulfides PS14 to PS21
All the experiments carried out so far used an Allyl/SH molar ratio of about 0.739. In order to study the effect of this molar ratio on the properties of the polysulfides made, a series of experiments have been conducted where the Allyl/SH molar ratio was varied from 0.500 to 1.354. The experimental conditions as well as the results of these syntheses were reported in Table IV.
As shown, the refractive indexes, the allyl conversion and precipitation yields of the polysulfides were all similar to each other.
The refractive index
was around 1.611 for most the precipitated polymers, which is higher than of the LP-33 polysulfide, a polysulfide having —S—S— linkages from Morton International
Structures of the polysulfides were confirmed by H NMR and 13C NMR spectrum.
n
n was measured by Gas peak chromatography (GPC)
The SH content of the polysulfides was measured by titration using iodine. As expected, the SH content decreased with the increase of the Allyl/SH molar ratio. When Allyl/SH=0.5, the end groups consist almost exclusively of SH, and the value of
I.5 Preparation of Polysulfide PS22
In a 100 ml three necked flask equipped with a magnetic stirrer, a heating mantle, an inlet for an inert gas on one port and a condenser on another port, we introduce 30.2016 g DMES, 16.4094 g Ally sulfide (Allyl/SH=0.734) and 2.6250 g 2,2′-Azobisisobutyronitrile (AIBN) previously dried, 2,2′-Azobisisobutyronitril (AIBN) received from Monomer-Polymer and Dajac Laboratories, Inc.
The mixture is heated to 65° C. Stirring was continued until the FTIR signal at 1636 cm−1 corresponding to the allyl groups disappeared (43 hours). This shows that AIBN is an effective initiator. The refractive index
of the mixture at this time was 1.6092. This product is dissolved in about 46 g of THF, and the solution is precipitated drop-wise in two liter of methanol.
After 24 hours, the supernant methanol solution is removed, and the white precipitate is dried under vacuum at room temperature.
The precipitation yield was about 80%. The refractive index
of the precipitated polysulfide was 1.6140. Its molecular weight by GPC was
Although the polymerization reaction between DMES and AS is successful when using a thermal radical initiator, the UV polymerization is a preferred polymerization method since the reaction times are much shorter (27 minutes in UV polymerization versus 43 hours in thermal polymerization).
The synthesis of these prepolymers was carried out under a blanket of dry nitrogen, at different temperatures, in the presence or absence of dimethyltindichloride catalyst. Several NCO/SH molar ratios were used. The reaction was followed by infra-red spectrometry for the NCO conversion (NCO signal at 2262 cm−1), Raman spectroscopy for the SH conversion (SH signal at 2520 cm−1) and by measuring the refractive index. After the reaction was stopped (by removing the heat source), the NCO content of the prepolymers was measured by titration.
Starting components, quantities and reaction conditions are given in Table V below.
Desmodur® W was Provided by BAYER:
NCO terminated prepolymer 1 obtained in step II above was reacted with Ethacure®-300 (which is a 80:20 mixture of the 2,4- and 2,6-isomers of dimethylthiotoluenediamine), and filled into −2.000 dioptries glass molds to make a lens. The experimental conditions of the casting and the properties of the lense are reported in Tables VI and VII. They show that the use of the polysulfide PS10 allows to reach a refractive index of 1.615, a good impact resistance.
Ethacure®-300 monomer was provided by Albermarle Corporation. It is an approximate 80:20 mixture of the 2,4- and 2,6-isomers of dimethylthiotoluenediamine, and has the following characteristics:
The results of Table VII show that the material of the invention exhibits both a higher refractive index and high impact resistance.
Impact energy (Dynatup) was measured using an impact test machine designed by General Research Corp. (Model 8210 Drop Weight Impact Test Machine). This machine has the capability to test materials over a wide range of velocities and energies. The velocities can reach up to 4.5 m/sec with a maximum standard drop eight of 36 inches. The cross-head weight can vary from approximately 4.1 to 27 kg.
E′ modulus is measured by dynamic mechanical analysis (DMA) using a Perkin Elmer DMA 7e equipment (3-point bending, heat from 5° C. to 180° C. at 2° C./min and a frequency of 1 Hz).
| Number | Name | Date | Kind |
|---|---|---|---|
| 3056841 | Saegebarth | Oct 1962 | A |
| 3413265 | Bertozzi | Nov 1968 | A |
| 4254229 | Schwindt et al. | Mar 1981 | A |
| 5191055 | Kanemura et al. | Mar 1993 | A |
| 5352758 | Kanemura et al. | Oct 1994 | A |
| 5484872 | Kanesaki et al. | Jan 1996 | A |
| 5837797 | Okazaki et al. | Nov 1998 | A |
| 5942158 | Okoroafor et al. | Aug 1999 | A |
| 5955206 | Okazaki et al. | Sep 1999 | A |
| 5973098 | Keita et al. | Oct 1999 | A |
| 6100362 | Okazaki et al. | Aug 2000 | A |
| 6127505 | Slagel | Oct 2000 | A |
| Number | Date | Country |
|---|---|---|
| 1085991 | Apr 1984 | SU |
| WO 0136507 | May 2001 | WO |
| WO 0136508 | May 2001 | WO |
| WO 0170841 | Sep 2001 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20030144452 A1 | Jul 2003 | US |