High-Index Silicoborate and Borosilicate Glasses

Abstract

Glass compositions include titania (TiO2), lanthanum oxide (La2O3) and boron oxide (B2O3) as essential components and may optionally include silica (SiO2), niobia (Nb2O5), zirconia (ZrO2), yttria (Y2O3), bismuth oxide (Bi2O3), tungsten oxide (WO3), zinc oxide (ZnO) and other components. The glasses may be characterized by high refractive index at 587.56 nm at comparably low density at room temperature.

Description

FIELD

The present disclosure generally relates to borate and silicoborate glasses having a high refractive index and low density.

BACKGROUND

Glass is used in a variety of optical devices, examples of which include augmented reality devices, virtual reality devices, mixed reality devices, eye wear, etc. Desirable properties for this type of glass often include a high refractive index and a low density. Additional desirable properties may include high transmission in the visible and near-ultraviolet (near-UV) range of the electromagnetic spectrum and/or low optical dispersion. It can be challenging to find glasses having the desired combination of these properties and which can be formed from compositions having good glass-forming ability. For example, generally speaking, as the refractive index of a glass increases, the density also tends to increase. Species such as TiO₂ and Nb₂O₅ are often added to increase the refractive index of a glass without increasing the density of the glass. However, these materials often absorb blue and UV light, which can undesirably decrease the transmittance of light in this region of the spectrum by the glass. Often, attempts to increase the refractive index of a glass while maintaining a low density, and without decreasing transmittance in the blue and UV region of the spectrum, can result in a decrease in the glass-forming ability of the material. For example, crystallization and/or liquid-liquid phase separation can occur during cooling of the glass melt at cooling rates that are generally acceptable in the industry. Typically, the decrease in glass-forming ability appears as the amount of certain species, such as ZrO₂, Y₂O₃, Sc₂O₃, BeO, etc. increases.

Low density, high refractive index glasses often belong to one of two types of chemical systems, based on the glass formers used: (a) silicoborate or borosilicate glasses in which SiO₂ and/or B₂O₃ are used as the main glass formers and (b) phosphate glasses in which P₂O₅ is used as a main glass former. Glasses which rely on other oxides as main glass formers, such as GeO₂, TeO₂, Bi₂O₃, and V₂O₅, can be challenging to use due to cost, glass-forming ability, optical properties, and/or production requirements.

Phosphate glasses can be characterized by a high refractive index and low density, however, phosphate glasses can be challenging to produce due to volatilization of P₂O₅ from the melts and/or risks of platinum incompatibility. In addition, phosphate glasses are often highly colored and may require an extra bleaching step to provide a glass having the desired transmittance characteristic. Furthermore, phosphate glasses exhibiting a high refractive index also tend to have an increase in optical dispersion.

Silicoborate and borate glasses are typically easier to produce and can exhibit a high transmittance without a bleaching step. However, silicoborate and borosilicate glasses typically exhibit an increase in density at increasing refractive indices, compared to phosphate glasses.

In view of these considerations, there is a need for borate and silicoborate glasses having a high refractive index, a low density, and a high transmittance to blue light.

SUMMARY

According to an embodiment of the present disclosure, a glass comprises a plurality of components, the glass having a composition of the components comprising greater than or equal to 12.0 mol.% and less than or equal to 35.0 mol.% TiO₂, greater than or equal to 2.5 mol.% and less than or equal to 20.0 mol.% ZrO₂, greater than or equal to 0.5 mol.% and less than or equal to 40.0 mol.% B₂O₃, greater than or equal to 0.5 mol.% and less than or equal to 30.0 mol.% Nb₂O₅, greater than or equal to 0.0 mol.% and less than or equal to 20.0 mol.% Bi₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 15.0 mol.% P₂O₅, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% Al₂O_3, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% Gd₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 8.0 mol.% WO₃, greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.% PbO, greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.% V₂O₅, greater than or equal to 0.0 mol.% and less than or equal to 1.5 mol.% ZnO, greater than or equal to 95.0 mol.% R_mO_n, greater than or equal to 0.5 mol.% and less than or equal to 35.0 mol.% RE_mO_n, a sum of SiO₂ + B₂O₃ + P₂O₅ greater than or equal to 10.0 mol.% and a sum of TiO₂ + Nb₂O₅ greater than or equal to 0.0 mol.% and less than or equal to 42.0 mol.%, wherein the composition of the components satisfies the condition: SiO₂ + B₂O₃ - P₂O₅ [mol.%] ≥ 0.000, and the glass satisfies the condition: P_n - (1.765 + 0.057 * P_d) > 0.000, where P_n is a parameter predicting a value of a refractive index at 587.56 nm, n_d, calculated from the glass composition in terms of mol.% of the components according to the Formula (I):

and P_d is a parameter predicting a value of density at room temperature, d_RT, calculated from the glass composition in terms of mol.% of the components according to the Formula (II):

where R_mO_n is a total sum of all oxides, RE_mO_n is a total sum of rare earth metal oxides, and an asterisk (*) means multiplication.

According to another embodiment of the present disclosure, a glass comprises a plurality of components, the glass having a composition of the components comprising greater than or equal to 1.0 mol.% and less than or equal to 13.5 mol.% ZrO₂, greater than or equal to 0.3 mol.% and less than or equal to 35.0 mol.% TiO₂, greater than or equal to 0.3 mol.% and less than or equal to 29.5 mol.% B₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 9.0 mol.% WO₃, greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.% PbO, greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% Gd₂O₃, greater than or equal to 0.0 at.% and less than or equal to 2.0 at.% F, a sum of TiO₂ + Nb₂O₅ + La₂O₃ greater than or equal to 10.0 mol.% and less than or equal to 70.0 mol.%, a sum of SiO₂ + B₂O₃ + P₂O₅ greater than or equal to 10.0 mol.%, a sum of RE_mO_n + WO₃ + ZrO₂ greater than or equal to 5.0 mol.%, a sum of SiO₂ + Y₂O₃ + Gd₂O₃ greater than or equal to 0.3 mol.%, a sum of V₂O₅ + MoO₃ greater than or equal to 0.0 mol.% and less than or equal to 3.0 mol.% and may optionally contain one or more components selected from Bi₂O₃, CaO, BaO, ZnO, Na₂O, Al₂O₃, Li_zO, GeO₂, TeO₂, K₂O, SrO and MgO, wherein the composition of the components satisfies the conditions: TiO₂ / (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃) [mol.%] ≥ 0.050, SiO₂ + B₂O₃ - P₂O₅ [mol.%] ≥ 1.0 and La₂O₃ / TiO₂ [mol.%] ≤ 1.5, and the glass satisfies the condition: P_n - (1.99 + 0.083 * (TiO₂ / (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃))) > 0.000, where P_n is a parameter predicting a refractive index at 587.56 nm, n_d, calculated from the glass composition in terms of mol.% of the components according to the Formula (I):

where RE_mO_n is a total sum of rare earth metal oxides, and an asterisk (*) means multiplication.

According to one more embodiment of the present disclosure, a glass comprises a plurality of components, the glass having a composition of the components comprising greater than or equal to 0.5 mol.% and less than or equal to 45.0 mol.% B₂O₃, greater than or equal to 0.1 mol.% and less than or equal to 25.0 mol.% Bi₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 8.0 mol.% WO₃, a sum of SiO₂ + B₂O₃ + P₂O₅ is greater than or equal to 10.0 mol.%, a sum of TiO₂ + Nb₂O₅ greater than or equal to 8.5 mol.%, a sum of RE_mO_n + WO₃ + ZrO₂ greater than or equal to 4.5 mol.% and may optionally contain one or more components selected from CaO, BaO, ZnO, Na₂O, Al₂O₃, Li₂O, PbO, GeO₂, TeO₂, K₂O, SrO and MgO, wherein the composition of the components satisfies the condition: SiO₂ + B₂O₃ - P₂O₅ [mol.%] ≥ 0.100, and the glass satisfies the condition: P_n > 2.045, where P_n is a parameter predicting a refractive index at 587.56 nm, n_d, calculated from the glass composition in terms of mol.% of the components according to the Formula (I):

where RE_mO_n is a total sum of rare earth metal oxides, and an asterisk (*) means multiplication.

These and other aspects, objects, and features of the present disclosure will be understood and appreciated by those skilled in the art upon studying the following specification, claims, and appended drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a plot illustrating the relationship between the refractive index n_d and the refractive index parameter P_n calculated by formula (I) for some Comparative Glasses and some Exemplary Glasses according to an embodiment of the present disclosure.

FIG. 2 is a plot illustrating the relationship between the density d_RT and the density parameter P_d calculated by formula (II) for some Comparative Glasses and some Exemplary Glasses according to an embodiment of the present disclosure.

FIG. 3 is a plot of an exemplary cooling schedule according to a “15 min test” condition and a “2.5 min test” condition for some Exemplary Glasses according to an embodiment of the present disclosure.

FIG. 4 is a plot illustrating the relationship between the density parameter P_d and the refractive index parameter P_n for some Comparative Glasses and some Exemplary Glasses according to an embodiment of the present disclosure.

FIG. 5 is a plot illustrating the relationship between the density at room temperature d_RT and the refractive index at 587.56 nm n_d for some Comparative Glasses and some Exemplary Glasses according to an embodiment of the present disclosure.

FIG. 6 is a plot illustrating the relationship between the ratio TiO₂ / (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃) and the refractive index parameter P_n for some Comparative Glasses and some Exemplary Glasses according to an embodiment of the present disclosure.

FIG. 7 is a plot illustrating the relationship between the ratio TiO₂ / (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃) and the refractive index at 587.56 nm n_d for some Comparative Glasses and some Exemplary Glasses according to an embodiment of the present disclosure.

DETAILED DESCRIPTION

In the following detailed description, for purposes of explanation and not limitation, example embodiments disclosing specific details are set forth to provide a thorough understanding of various principles of the present disclosure. However, it will be apparent to one having ordinary skill in the art, having had the benefit of the present disclosure, that the present disclosure may be practiced in other embodiments that depart from the specific details disclosed herein. Moreover, descriptions of well-known devices, methods and materials may be omitted so as not to obscure the description of various principles of the present disclosure. Finally, wherever applicable, like reference numerals refer to like elements.

Unless otherwise expressly stated, it is in no way intended that any method set forth herein be construed as requiring that its steps be performed in a specific order. Accordingly, where a method claim does not actually recite an order to be followed by its steps, or it is not otherwise specifically stated in the claims or descriptions that the steps are to be limited to a specific order, it is in no way intended that an order be inferred, in any respect. This holds for any possible non-express basis for interpretation, including, without limitation, matters of logic with respect to arrangement of steps or operational flow; plain meaning derived from grammatical organization or punctuation; the number or type of embodiments described in the specification.

As used herein, the term “and/or,” when used in a list of two or more items, means that any one of the listed items can be employed by itself, or any combination of two or more of the listed items can be employed. For example, if a composition is described as containing components A, B, and/or C, the composition can contain A alone; B alone; C alone; A and B in combination; A and C in combination; B and C in combination; or A, B, and C in combination.

Modifications of the disclosure will occur to those skilled in the art and to those who make or use the disclosure. Therefore, it is understood that the embodiments shown in the drawings and described above are merely for illustrative purposes and not intended to limit the scope of the disclosure, which is defined by the following claims, as interpreted according to the principles of patent law, including the doctrine of equivalents.

As used herein, the term “about” means that amounts, sizes, formulations, parameters, and other quantities and characteristics are not and need not be exact, but may be approximate and/or larger or smaller, as desired, reflecting tolerances, conversion factors, rounding off, measurement error and the like, and other factors known to those skilled in the art. When the term “about” is used in describing a value or an end-point of a range, the disclosure should be understood to include the specific value or end-point referred to. Whether or not a numerical value or end-point of a range in the specification recites “about,” the numerical value or end-point of a range is intended to include two embodiments: one modified by “about,” and one not modified by “about.” It will be further understood that the end-points of each of the ranges are significant both in relation to the other end-point, and independently of the other end-point.

The term “component” refers to a material or compound included in a batch composition from which a glass is formed. Components include oxides, including but not limited to those expressed in Formulas (I), and (II), and the claims. Representative components include B₂O₃, P₂O₅, Al₂O₃, CuO, Cu₂O, RO, R₂O, SnO₂, MnO₂, RE_mO_n, SiO₂, Ta₂O₅, ZnO, WO₃, Nb₂O₅, TiO₂, ZrO₂, Bi₂O₃, TeO₂, etc. Other representative components include halogens (e.g. F, Br, CI). Whenever a component is included as a term in a mathematical expression or formula, it is understood that the component refers to the amount of the component in units of mol.% in the batch composition of the glass. For example, the expression “B₂O₃ + P₂O₅” refers to the sum of the amount of B₂O₃ in units of mol.% and the amount of P₂O₅ in units of mol.% in the batch composition of the glass. A mathematical expression or formula is any expression or formula that includes a mathematical operator such as “+”, “-”, “*”, “/”, “min”, or “max”.

Unless otherwise specified, the amount or content of a component in a glass composition is expressed herein in units of mol.% (mole percent).

The term “formed from” can mean one or more of comprises, consists essentially of, or consists of. For example, a component that is formed from a particular material can comprise the particular material, consist essentially of the particular material, or consist of the particular material.

The terms “free” and “substantially free” are used interchangeably herein to refer to an amount and/or an absence of a particular component in a glass composition that is not intentionally added to the glass composition. It is understood that the glass composition may contain traces of a particular constituent component as a contaminant or a tramp in an amount of less than 0.10 mol.%.

As used herein, the term “tramp”, when used to describe a particular constituent component in a glass composition, refers to a constituent component that is not intentionally added to the glass composition and is present in an amount of less than 0.10 mol.%. Tramp components may be unintentionally added to the glass composition as an impurity in another constituent component and/or through migration of the tramp component into the composition during processing of the glass composition.

Unless otherwise specified, the term “glass” is used to refer to a glass made from a glass composition disclosed herein.

The symbol “*” means multiplication when used in any formula herein.

The term “log” means logarithm in base 10.

Temperature is expressed herein in units of °C (degrees Celsius).

Density is expressed herein in units of g/cm³.

Viscosity is expressed herein in units of P (Poise).

The term “glass former” is used herein to refer to a component that, being solely present in the glass composition (i.e., without other components, except for tramps), is able to form a glass when cooling the melt at a rate of not greater than about 300° C./min.

The term “modifier”, as used herein, refers to the oxides of monovalent or divalent metals, i.e., R₂O or RO, where “R” stands for a cation. Modifiers can be added to a glass composition to change the atomic structure of the melt and the resulting glass. In some embodiments, the modifier may change the coordination numbers of cations present in the glass formers (e.g., boron in B₂O₃), which may result in forming a more polymerized atomic network and, as a result, may provide better glass formation.

As used herein, the term “RO” refers to a total content of divalent metal oxides, the term “R₂O” refers to a total content of monovalent metal oxides, and the term “Alk₂O” refers to a total content of alkali metal oxides. The term R₂O encompasses alkali metal oxides (Alk₂O), in addition to other monovalent metal oxides, such as Ag₂O, TI₂O, and Hg₂O, for example. As discussed below, in the present disclosure, a rare earth metal oxide is referred to herein by its normalized formula (RE₂O₃) in which the rare earth metal RE has the redox state “+3,” and thus rare earth metal oxides are not encompassed by the term RO.

As used herein, the term “rare earth metals” refers to the metals listed in the Lanthanide Series of the IUPAC Periodic Table, plus yttrium and scandium. As used herein, the term “rare earth metal oxides,” is used to refer to the oxides of rare earth metals in different redox states, such as “+3” for lanthanum in La₂O₃, “+4” for cerium in CeO₂, “+2” for europium in EuO, etc. In general, the redox states of rare earth metals in oxide glasses may vary and, in particular, the redox state may change during melting, based on the batch composition and/or the redox conditions in the furnace where the glass is melted and/or heat-treated (e.g., annealed). Unless otherwise specified, a rare earth metal oxide is referred to herein by its normalized formula in which the rare earth metal has the redox state “+3.” Accordingly, in the case in which a rare earth metal having a redox state other than “+3” is added to the glass composition batch, the glass compositions are recalculated by adding or removing some oxygen to maintain the stoichiometry. For example, when CeO₂ (with cerium in redox state “+4”) is used as a batch component, the resulting as-batched composition is recalculated assuming that two moles of CeO₂ is equivalent to one mole of Ce₂O₃, and the resulting as-batched composition is expressed in terms of Ce₂O₃. As used herein, the term “RE_mO_n” is used to refer to the total content of rare earth metal oxides in all redox states present, and the term “RE₂O₃” is used to refer to the total content of rare earth metal oxides in the “+3” redox state, also specified as “trivalent equivalent”.

Unless otherwise specified, all compositions are expressed in terms of as-batched mole percent (mol%). As will be understood by those having ordinary skill in the art, various melt constituents (e.g., fluorine, alkali metals, boron, etc.) may be subject to different levels of volatilization (e.g., as a function of vapor pressure, melt time and/or melt temperature) during melting of the constituents. As such, the term “about,” in relation to such constituents, is intended to encompass values within about 0.2 mol% when measuring final articles as compared to the as-batched compositions provided herein. With the forgoing in mind, substantial compositional equivalence between final articles and as-batched compositions is expected.

In the case when fluorine or other halogen (chlorine, bromine, and/or iodine) is added to or is present in an oxide glass, the molecular representation of the resulting glass composition may be expressed in different ways. In the present disclosure, the content of fluorine as a single term, when present, is expressed in terms of atomic percent (at.%), which is determined based on the fraction of fluorine in a total sum of all atoms in a glass composition multiplied by a factor of 100.

In the present disclosure, the following method of representation of fluorine-containing compositions and concentration ranges is used. The concentration limits for all oxides (e.g. SiO₂, B₂O₃, Na₂O, etc.) are presented under the assumption that the respective cations (such as, for example, silicon [Si₄⁺], boron [B₃⁺], sodium [Na⁺], etc.) are initially presented in the form of the corresponding oxides. When fluorine is present, for the purposes of calculating the concentration of components of the composition, some part of the oxygen in the oxide is equivalently replaced with fluorine (i.e. one atom of oxygen is replaced with two atoms of fluorine). The fluorine is assumed to be present in the form of silicon fluoride (SiF₄); accordingly, the total sum of all oxides plus SiF₄ is assumed to be 100 mole percent in all compositions.

The measured density values for the glasses reported herein were measured at room temperature in units of g/cm³ by Archimedes method in water with an error of 0.001 g/cm³. As used herein, density measurements at room temperature (specified as d_RT) are indicated as being measured at 20° C. or 25° C., and encompass measurements obtained at temperatures that may range from 20° C. to 25° C. It is understood that room temperature may vary between about 20° C. to about 25° C., however, for the purposes of the present disclosure, the variation in density within the temperature range of 20° C. to 25° C. is expected to be less than the error of 0.001 g/cm³, and thus is not expected to impact the room temperature density measurements reported herein.

As used herein, good glass forming ability refers to a resistance of the melt to devitrification as the material cools. Glass forming ability can be measured by determining the critical cooling rate of the melt. The terms “critical cooling rate” or “v_cr” are used herein to refer to the minimum cooling rate at which a melt of a given composition forms a glass free of crystals visible under an optical microscope under magnification of 500x. The critical cooling rate can be used to measure the glass-forming ability of a composition, i.e., the ability of the melt of a given glass composition to form glass when cooling. Generally speaking, the lower the critical cooling rate, the better the glass-forming ability.

The term “liquidus temperature” (T_liq) is used herein to refer to a temperature above which the glass composition is completely liquid with no crystallization of constituent components of the glass. The liquidus temperature values reported herein were obtained by measuring samples using either DSC or by isothermal hold of samples wrapped in platinum foil. For samples measured using DSC, powdered samples were heated at 10 K/min to 1250° C. The end of the endothermal event corresponding to the melting of crystals was taken as the liquidus temperature. For the second technique (isothermal hold), a glass block (about 1 cm³) was wrapped in platinum foil, to avoid volatilization, and placed in a furnace at a given temperature for 17 hours. The glass block was then observed under an optical microscope to check for crystals.

The refractive index values reported herein were measured at room temperature, unless otherwise specified. The refractive index values for a glass sample were measured using a Metricon Model 2010 prism coupler refractometer with an error of about + 0.0002. Using the Metricon, the refractive index of a glass sample was measured at two or more wavelengths of about 406 nm, 473 nm, 532 nm, 633 nm, 828 nm, and 1064 nm. The measured dependence characterizes the dispersion and was then fitted with a Cauchy’s law equation or Sellmeier equation to allow for calculation of the refractive index of the sample at a given wavelength of interest between the measured wavelengths. The term “refractive index n_d” is used herein to refer to a refractive index calculated as described above at a wavelength of 587.56 nm, which corresponds to the helium d-line wavelength. The term “refractive index n_c” is used herein to refer to a refractive index calculated as described above at a wavelength of 656.3 nm. The term “refractive index n_F” is used herein to refer to a refractive index calculated as described above at a wavelength of 486.1 nm. The term “refractive index n_g” is used herein to refer to a refractive index calculated as described above at a wavelength of 435.8 nm.

As used herein, the terms “high refractive index” or “high index” refer to a refractive index value of a glass that is greater than or equal to at least 1.80, unless otherwise indicated. Where indicated, embodiments of the terms “high refractive index” or “high index” refer to a refractive index value of a glass that is greater than or equal to at least 1.85, greater than or equal to 1.90, or greater than or equal to 1.95, or greater than or equal to 2.00.

The glass transition temperature (T_g) is measured by differential scanning calorimeter (DSC) at the heating rate of 10 K/min after cooling in air.

Glass composition may include boron oxide (B₂O₃). According to some embodiments of the present disclosure, boron oxide may play a role of a glass former. As a glass former, B₂O₃ may increase the liquidus viscosity and, therefore, inhibit crystallization. However, adding B₂O₃ to a glass composition may cause liquid-liquid phase separation, which may cause devitrification and/or a reduction in the visible transmittance of the glass. Also, adding B₂O₃ to the high-index glasses reduces the refractive index. Accordingly, the amount of boron oxide is limited, or glasses may be substantially free of B₂O₃. In embodiments, the glass composition may contain boron oxide (B₂O₃) in an amount from greater than or equal to 0.3 mol.% to less than or equal to 45.0 mol.% and all ranges and sub-ranges between the foregoing values. In some embodiments, the glass composition may contain B₂O₃ in an amount greater than or equal to 0.3 mol.%, greater than or equal to 5.0 mol.%, greater than or equal to 10.0 mol.%, greater than or equal to 14.0 mol.%, greater than or equal to 15.0 mol.%, greater than or equal to 16.0 mol.%, greater than or equal to 16.4 mol.%, greater than or equal to 16.9 mol.%, greater than or equal to 25.0 mol.%, greater than or equal to 30.0 mol.%, greater than or equal to 35.0 mol.%, or greater than or equal to 40.0 mol.%. In some other embodiments, the glass composition may contain B₂O₃ in an amount less than or equal to 45.0 mol.%, less than or equal to 40.0 mol.%, less than or equal to 35.0 mol.%, less than or equal to 30.0 mol.%, less than or equal to 29.5 mol.%, less than or equal to 25.0 mol.%, less than or equal to 24.0 mol.%, less than or equal to 22.5 mol.%, less than or equal to 20.4 mol.%, less than or equal to 20.0 mol.%, or less than or equal to 10.0 mol.%. In some more embodiments, the glass composition may contain B₂O₃ in an amount greater than or equal to 0.3 mol.% and less than or equal to 29.5 mol.%, greater than or equal to 0.5 mol.% and less than or equal to 45.0 mol.%, greater than or equal to 0.5 mol.% and less than or equal to 40.0 mol.%, greater than or equal to 10.0 mol.% and less than or equal to 35.0 mol.%, greater than or equal to 13.67 mol.% and less than or equal to 24.41 mol.%, greater than or equal to 15.0 mol.% and less than or equal to 22.5 mol.%, greater than or equal to 16.0 mol.% and less than or equal to 20.0 mol.%, greater than or equal to 16.4 mol.% and less than or equal to 20.4 mol.%, greater than or equal to 16.9 mol.% and less than or equal to 20.4 mol.%, greater than or equal to 0.3 mol.% and less than or equal to 45.0 mol.%, greater than or equal to 0.3 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 5.0 mol.% and less than or equal to 45.0 mol.%, greater than or equal to 5.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 10.0 mol.% and less than or equal to 20.0 mol.%, greater than or equal to 14.0 mol.% and less than or equal to 45.0 mol.%, greater than or equal to 14.0 mol.% and less than or equal to 20.0 mol.%, greater than or equal to 15.0 mol.% and less than or equal to 20.0 mol.%, greater than or equal to 16.4 mol.% and less than or equal to 20.0 mol.%.

Glass composition may include silica (SiO₂). Silica may play a role of glass-former. Silica, as well as B₂O₃, may help to increase the liquidus viscosity (viscosity at the liquidus temperature) and, therefore, inhibit crystallization. However, adding SiO₂ to a glass composition may cause liquid-liquid phase separation, which may cause devitrification and/or a reduction in the transmittance of the glass. Also, SiO₂ is a low-index component and makes it difficult to achieve high index. Accordingly, the content of SiO₂ is limited, or glasses may be substantially free of SiO₂. In embodiments, the glass composition may contain silica (SiO₂) in an amount from greater than or equal to 0.0 mol.% to less than or equal to 22.1 mol.% and all ranges and sub-ranges between the foregoing values. In some embodiments, the glass composition may contain SiO₂ in an amount greater than or equal to 0.0 mol.%, greater than or equal to 4.7 mol.%, greater than or equal to 5.0 mol.%, greater than or equal to 10.0 mol.%, greater than or equal to 11.0 mol.%, or greater than or equal to 20.0 mol.%. In some other embodiments, the glass composition may contain SiO₂ in an amount less than or equal to 22.1 mol.%, less than or equal to 20.0 mol.%, less than or equal to 17.5 mol.%, less than or equal to 16.5 mol.%, less than or equal to 15.0 mol.%, less than or equal to 13.4 mol.%, or less than or equal to 10.0 mol.%. In some more embodiments, the glass composition may contain SiO₂ in an amount greater than or equal to 0.0 mol.% and less than or equal to 15.0 mol.%, greater than or equal to 4.68 mol.% and less than or equal to 13.4 mol.%, greater than or equal to 5.0 mol.% and less than or equal to 20.0 mol.%, greater than or equal to 10.0 mol.% and less than or equal to 20.0 mol.%, greater than or equal to 10.0 mol.% and less than or equal to 17.5 mol.%, greater than or equal to 11.0 mol.% and less than or equal to 16.5 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 22.1 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 4.7 mol.% and less than or equal to 22.1 mol.%, greater than or equal to 4.7 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 5.0 mol.% and less than or equal to 22.1 mol.%, greater than or equal to 5.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 10.0 mol.% and less than or equal to 22.1 mol.%, greater than or equal to 10.0 mol.% and less than or equal to 13.4 mol.%, greater than or equal to 11.0 mol.% and less than or equal to 22.1 mol.%, greater than or equal to 11.0 mol.% and less than or equal to 13.4 mol.%.

Glass composition may include phosphorus oxide (P₂O_s) as an additional glass former. Greater amounts of P₂O₅ may increase the melt viscosity at a given temperature, which may inhibit crystallization from the melt when cooling and, therefore, may improve the glass-forming ability of the melt (i.e. lower the critical cooling rate of the melt). However, P₂O₅ significantly decreases the refractive index. Also, in some cases P₂O₅ may stimulate liquid-liquid phase separation, which may cause crystallization of glass forming melts when cooling and/or loss of transmittance. Additionally, P₂O₅ can increase the liquidus temperature of a given composition due to the low solubility of refractory phosphate phases, such as rare earth phosphates and zirconia phosphate. Accordingly, the content of P₂O₅ in high-index glasses is limited, or glasses may be free of P₂O₅. In embodiments, the glass composition may contain phosphorus oxide (P₂O₅) in an amount from greater than or equal to 0.0 mol.% to less than or equal to 15.0 mol.% and all ranges and sub-ranges between the foregoing values. In some embodiments, the glass composition may contain P₂O₅ in an amount greater than or equal to 0.0 mol.%, greater than or equal to 5.0 mol.%, greater than or equal to 9.0 mol.%, greater than or equal to 10.0 mol.%, greater than or equal to 11.0 mol.%, or greater than or equal to 13.0 mol.%. In some other embodiments, the glass composition may contain P₂O₅ in an amount less than or equal to 15.0 mol.%, less than or equal to 13.0 mol.%, less than or equal to 11.0 mol.%, less than or equal to 10.0 mol.%, less than or equal to 9.0 mol.%, or less than or equal to 5.0 mol.%. In some more embodiments, the glass composition may contain P₂O₅ in an amount greater than or equal to 0.0 mol.% and less than or equal to 15.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.%, greater than or equal to 5.0 mol.% and less than or equal to 15.0 mol.%, greater than or equal to 5.0 mol.% and less than or equal to 9.0 mol.%, greater than or equal to 9.0 mol.% and less than or equal to 15.0 mol.%, greater than or equal to 9.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 10.0 mol.% and less than or equal to 15.0 mol.%, greater than or equal to 10.0 mol.% and less than or equal to 11.0 mol.%, greater than or equal to 11.0 mol.% and less than or equal to 15.0 mol.%, greater than or equal to 11.0 mol.% and less than or equal to 13.0 mol.%.

Glass composition may have limitations for the amount of all oxides. When a glass composition completely or mostly consists of oxides, containing zero or a small amount of non-oxide components (such as halides, chalcogenides and others), it may become easier to melt and preserve from crystallization, phase separation, volatilization of components and other undesirable effects. Accordingly, in some embodiments of the present disclosure, the glass composition may be required to contain high amount of oxide components, or not to contain non-oxide components in remarkable amounts.

In some embodiments, the glass composition may contain a sum of all oxides R_mO, in an amount greater than or equal to 95.0 mol.%.

Glass composition may have limitations for the amount of rare earth metal oxides. In some embodiments, the glass composition may contain rare earth metal oxides RE_mO_n in an amount greater than or equal to 0.5 mol.%, or greater than or equal to 20.0 mol.%. In some other embodiments, the glass composition may contain rare earth metal oxides RE_mO_n in an amount less than or equal to 35.0 mol.% or less than or equal to 20.0 mol.%. In some more embodiments, the glass composition may contain RE_mO_n in an amount greater than or equal to 0.5 mol.% and less than or equal to 35.0 mol.%, or greater than or equal to 0.5 mol.% and less than or equal to 20.0 mol.%.

Glass composition may include lanthanum oxide (La₂O₃). Lanthanum oxide is a high-index component that has little effect on transmittance in the visible range. Also, addition of La₂O₃ may inhibit phase separation. However, La₂O₃ provides higher density relative to other high-index components, such as, for example, TiO₂, Nb₂O₅ or WO₃. Also, when added in high amount, it may cause crystallization of refractory species, like lanthanum disilicate (La₂Si₂O₇), lanthanum zirconate (La₂ZrO₅) and others, and, accordingly, reduce glass forming ability. For this reason, the content of La₂O₃ should be limited. In embodiments, the glass composition may contain lanthanum oxide (La₂O₃) in an amount from greater than or equal to 0.0 mol.% to less than or equal to 70.0 mol.% and all ranges and sub-ranges between the foregoing values. In some embodiments, the glass composition may contain La₂O₃ in an amount greater than or equal to 0.0 mol.%, greater than or equal to 5.0 mol.%, greater than or equal to 10.0 mol.%, greater than or equal to 15.0 mol.%, greater than or equal to 20.0 mol.%, greater than or equal to 21.0 mol.%, greater than or equal to 22.0 mol.%, greater than or equal to 40.0 mol.%, greater than or equal to 50.0 mol.%, or greater than or equal to 60.0 mol.%. In some other embodiments, the glass composition may contain La₂O₃ in an amount less than or equal to 70.0 mol.%, less than or equal to 60.0 mol.%, less than or equal to 50.0 mol.%, less than or equal to 40.0 mol.%, less than or equal to 30.0 mol.%, less than or equal to 27.5 mol.%, less than or equal to 26.25 mol.%, less than or equal to 24.0 mol.%, or less than or equal to 10.0 mol.%. In some more embodiments, the glass composition may contain La₂O₃ in an amount greater than or equal to 15.0 mol.% and less than or equal to 30.0 mol.%, greater than or equal to 20.0 mol.% and less than or equal to 30.0 mol.%, greater than or equal to 20.0 mol.% and less than or equal to 27.5 mol.%, greater than or equal to 21.0 mol.% and less than or equal to 26.25 mol.%, greater than or equal to 21.83 mol.% and less than or equal to 24.03 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 70.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 10.0 mol.% and less than or equal to 70.0 mol.%, greater than or equal to 10.0 mol.% and less than or equal to 24.0 mol.%, greater than or equal to 15.0 mol.% and less than or equal to 24.0 mol.%, greater than or equal to 20.0 mol.% and less than or equal to 70.0 mol.%, greater than or equal to 20.0 mol.% and less than or equal to 24.0 mol.%.

Glass composition may include yttria (Y₂O₃). Yttria behaves like lanthanum oxide, but may provide a given refractive index at a lower density, while still not providing undesirable coloring. However, adding Y₂O₃ in high amounts to the glass compositions may adversely cause crystallization of the glass melts when cooling. Accordingly, in some embodiments, the content of Y₂O₃ may be limited. In embodiments, the glass composition may contain yttria (Y₂O₃) in an amount from greater than or equal to 0.0 mol.% to less than or equal to 10.0 mol.% and all ranges and sub-ranges between the foregoing values. In some embodiments, the glass composition may contain Y₂O₃ in an amount greater than or equal to 0.0 mol.%, greater than or equal to 0.5 mol.%, greater than or equal to 0.75 mol.%, greater than or equal to 3.0 mol.%, or greater than or equal to 5.0 mol.%. In some other embodiments, the glass composition may contain Y₂O₃ in an amount less than or equal to 10.0 mol.%, less than or equal to 8.0 mol.%, less than or equal to 6.25 mol.%, less than or equal to 6.0 mol.%, less than or equal to 5.5 mol.%, or less than or equal to 5.0 mol.%. In some more embodiments, the glass composition may contain Y₂O₃ in an amount greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 8.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 6.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.%, greater than or equal to 0.5 mol.% and less than or equal to 6.25 mol.%, greater than or equal to 0.75 mol.% and less than or equal to 5.5 mol.%, greater than or equal to 2.54 mol.% and less than or equal to 5.28 mol.%, greater than or equal to 0.5 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 0.5 mol.% and less than or equal to 5.0 mol.%, greater than or equal to 0.75 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 0.75 mol.% and less than or equal to 5.0 mol.%, greater than or equal to 3.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 3.0 mol.% and less than or equal to 5.0 mol.%.

Glass composition may include gadolinium oxide (Gd₂O₃). Gadolinium oxide behaves like lanthanum oxide, providing high refractive index without compromising visible transmittance, but adversely increasing the density of glass. Also, gadolinium oxide is more expensive than other rare earth metal oxides, such as La₂O₃ and Y₂O₃. Accordingly, in some embodiments, the content of Gd₂O₃ in a glass composition is limited, or a glass composition may be substantially free of Gd₂O₃. In embodiments, the glass composition may contain gadolinium oxide (Gd₂O₃) in an amount from greater than or equal to 0.0 mol.% to less than or equal to 10.0 mol.% and all ranges and sub-ranges between the foregoing values. In some embodiments, the glass composition may contain Gd₂O₃ in an amount greater than or equal to 0.0 mol.%, greater than or equal to 5.0 mol.%, greater than or equal to 7.0 mol.%, greater than or equal to 8.0 mol.%, or greater than or equal to 9.0 mol.%. In some other embodiments, the glass composition may contain Gd₂O₃ in an amount less than or equal to 10.0 mol.%, less than or equal to 9.0 mol.%, less than or equal to 8.0 mol.%, less than or equal to 7.0 mol.%, less than or equal to 5.0 mol.%, less than or equal to 2.0 mol.%, less than or equal to 1.35 mol.%, or less than or equal to 1.2 mol.%. In some more embodiments, the glass composition may contain Gd₂O₃ in an amount greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 1.35 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 1.2 mol.%, greater than or equal to 5.0 mol.% and less than or equal to 7.0 mol.%.

Glass composition may include alumina (Al₂O₃). Alumina may increase the viscosity of glass forming melts at high temperature, which may reduce the critical cooling rate and improve the glass forming ability. However, addition of Al₂O₃ may cause crystallization of refractory minerals, such as aluminum titanate (Al₂TiO₅), aluminum niobate (AINbO₄) and others, in the melt when cooling, or may lower the solubility of ZrO₂ in the liquid, causing a drastic increase on the liquidus temperature or necessitating a lower ZrO₂ content of a composition. Accordingly, the amount of Al₂O₃ is limited, or glasses may be substantially free of Al₂O₃. In embodiments, the glass composition may contain alumina (Al₂O₃) in an amount from greater than or equal to 0.0 mol.% to less than or equal to 10.0 mol.% and all ranges and sub-ranges between the foregoing values. In some embodiments, the glass composition may contain Al₂O₃ in an amount greater than or equal to 0.0 mol.%, greater than or equal to 5.0 mol.%, greater than or equal to 7.0 mol.%, greater than or equal to 8.0 mol.%, or greater than or equal to 9.0 mol.%. In some other embodiments, the glass composition may contain Al₂O₃ in an amount less than or equal to 10.0 mol.%, less than or equal to 9.0 mol.%, less than or equal to 8.0 mol.%, less than or equal to 7.0 mol.%, or less than or equal to 5.0 mol.%. In some more embodiments, the glass composition may contain Al₂O₃ in an amount greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.%, greater than or equal to 5.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 5.0 mol.% and less than or equal to 7.0 mol.%, greater than or equal to 7.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 7.0 mol.% and less than or equal to 8.0 mol.%, greater than or equal to 8.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 8.0 mol.% and less than or equal to 9.0 mol.%.

Glass composition may include vanadia (V₂O₅). Vanadia provides the highest ratio of the refractive index to density among all oxides. However, vanadia may cause undesirable dark coloring and may also raise environmental concerns. For these reasons, the content of vanadia in the glasses is limited, or glass compositions may be free of V₂O₅. In embodiments, the glass composition may contain vanadia (V₂O₅) in an amount from greater than or equal to 0.0 mol.% to less than or equal to 10.0 mol.% and all ranges and sub-ranges between the foregoing values. In some embodiments, the glass composition may contain V₂O₅ in an amount greater than or equal to 0.0 mol.%, greater than or equal to 5.0 mol.%, greater than or equal to 7.0 mol.%, greater than or equal to 8.0 mol.%, or greater than or equal to 9.0 mol.%. In some other embodiments, the glass composition may contain V₂O₅ in an amount less than or equal to 10.0 mol.%, less than or equal to 9.0 mol.%, less than or equal to 8.0 mol.%, less than or equal to 7.0 mol.%, less than or equal to 5.0 mol.%, less than or equal to 3.0 mol.%, or less than or equal to 0.1 mol.%. In some more embodiments, the glass composition may contain V₂O₅ in an amount greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 0.1 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 5.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 5.0 mol.% and less than or equal to 7.0 mol.%, greater than or equal to 7.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 7.0 mol.% and less than or equal to 8.0 mol.%, greater than or equal to 8.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 8.0 mol.% and less than or equal to 9.0 mol.%.

Glass composition may include lead oxide (PbO). Adding lead oxide to a glass composition may increase the refractive index without causing crystallization or phase separation of the glass forming melt and not compromising the visible transmittance. However, adding PbO may adversely increase the density of glass. Also, PbO raises environmental concerns. Accordingly, in some embodiments of the present disclosure the content of PbO in glass composition is limited, or, preferably, a glass composition can be substantially free of PbO. In embodiments, the glass composition may contain lead oxide (PbO) in an amount from greater than or equal to 0.0 mol.% to less than or equal to 10.0 mol.% and all ranges and sub-ranges between the foregoing values. In some embodiments, the glass composition may contain PbO in an amount greater than or equal to 0.0 mol.%, greater than or equal to 5.0 mol.%, greater than or equal to 7.0 mol.%, greater than or equal to 8.0 mol.%, or greater than or equal to 9.0 mol.%. In some other embodiments, the glass composition may contain PbO in an amount less than or equal to 10.0 mol.%, less than or equal to 9.0 mol.%, less than or equal to 8.0 mol.%, less than or equal to 7.0 mol.%, less than or equal to 5.0 mol.%, or less than or equal to 0.5 mol.%. In some more embodiments, the glass composition may contain PbO in an amount greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 0.5 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 5.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 5.0 mol.% and less than or equal to 7.0 mol.%, greater than or equal to 7.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 7.0 mol.% and less than or equal to 8.0 mol.%, greater than or equal to 8.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 8.0 mol.% and less than or equal to 9.0 mol.%.

Glass composition may include zinc oxide (ZnO). Zinc oxide provides a high ratio of refractive index to density and may increase the solubility of titania, which indirectly increases the refractive index of glasses. However, in some embodiments, at high concentrations of ZnO, the glass-forming ability of the melt may decrease and the melt may tend to crystallize during cooling. In embodiments, the glass composition may contain zinc oxide (ZnO) in an amount from greater than or equal to 0.0 mol.% to less than or equal to 10.0 mol.% and all ranges and sub-ranges between the foregoing values. In some embodiments, the glass composition may contain ZnO in an amount greater than or equal to 0.0 mol.%, greater than or equal to 5.0 mol.%, greater than or equal to 7.0 mol.%, greater than or equal to 8.0 mol.%, or greater than or equal to 9.0 mol.%. In some other embodiments, the glass composition may contain ZnO in an amount less than or equal to 10.0 mol.%, less than or equal to 9.0 mol.%, less than or equal to 8.0 mol.%, less than or equal to 7.0 mol.%, less than or equal to 5.0 mol.%, less than or equal to 4.0 mol.%, less than or equal to 3.0 mol.%, less than or equal to 2.7 mol.%, less than or equal to 1.5 mol.%, or less than or equal to 0.1 mol.%. In some more embodiments, the glass composition may contain ZnO in an amount greater than or equal to 0.0 mol.% and less than or equal to 4.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 3.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 2.7 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 1.5 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 0.1 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 5.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 7.0 mol.% and less than or equal to 8.0 mol.%.

Glass composition may include tungsten oxide (WO₃). WO₃ provides high refractive index without significantly increasing density or causing undesirable coloring. Also, addition of WO₃ to glass composition may decrease the liquidus temperature, which allows melting such glasses at lower temperatures, that, in turn, may increase the transmittance of such glasses. Also, addition of WO₃ may decrease the glass transition temperature T_g, which allows glass formation at lower temperatures. At high concentrations of WO₃, the liquidus temperature tends to increase, and the viscosity at the liquidus temperature drops, making it difficult to avoid crystallization of melts when cooling. Accordingly, the content of WO₃ should be limited, or glass compositions may be free of WO₃. In embodiments, the glass composition may contain tungsten oxide (WO₃) in an amount from greater than or equal to 0.0 mol.% to less than or equal to 9.0 mol.% and all ranges and sub-ranges between the foregoing values. In some embodiments, the glass composition may contain WO₃ in an amount greater than or equal to 0.0 mol.%, greater than or equal to 2.0 mol.%, greater than or equal to 5.0 mol.%, greater than or equal to 6.0 mol.%, greater than or equal to 7.0 mol.%, or greater than or equal to 8.0 mol.%. In some other embodiments, the glass composition may contain WO₃ in an amount less than or equal to 9.0 mol.%, less than or equal to 8.0 mol.%, less than or equal to 7.0 mol.%, less than or equal to 6.0 mol.%, less than or equal to 5.0 mol.%, less than or equal to 2.0 mol.%, less than or equal to 1.8 mol.%, or less than or equal to 1.6 mol.%. In some more embodiments, the glass composition may contain WO₃ in an amount greater than or equal to 0.0 mol.% and less than or equal to 9.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 8.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 6.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 1.8 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 1.6 mol.%, greater than or equal to 1.97 mol.% and less than or equal to 5.91 mol.%, greater than or equal to 2.0 mol.% and less than or equal to 5.0 mol.%, greater than or equal to 6.0 mol.% and less than or equal to 7.0 mol.%, greater than or equal to 7.0 mol.% and less than or equal to 8.0 mol.%.

Glass composition may include zirconia (ZrO₂). Zirconia can increase the refractive index while maintaining low density. ZrO₂ can also increase the viscosity of the melt, which may help to inhibit crystallization from the melt. ZrO₂ does not introduce coloring in the glass in the visible and near-UV ranges, which may help to maintain a high transmittance of the glass. However, high concentrations of zirconia may cause crystallization of refractory minerals, such as zirconia (ZrO₂), zircon (ZrSiO₄), calcium zirconate (CaZrO₃) and others, which may decrease the glass forming ability of the melt. In embodiments, the glass composition may contain zirconia (ZrO₂) in an amount from greater than or equal to 0.0 mol.% to less than or equal to 20.0 mol.% and all ranges and sub-ranges between the foregoing values. In some embodiments, the glass composition may contain ZrO₂ in an amount greater than or equal to 0.0 mol.%, greater than or equal to 1.0 mol.%, greater than or equal to 2.5 mol.%, greater than or equal to 4.0 mol.%, greater than or equal to 5.0 mol.%, greater than or equal to 5.3 mol.%, greater than or equal to 5.6 mol.%, greater than or equal to 6.5 mol.%, greater than or equal to 6.8 mol.%, greater than or equal to 10.0 mol.%, greater than or equal to 14.0 mol.%, greater than or equal to 16.0 mol.%, or greater than or equal to 18.0 mol.%. In some other embodiments, the glass composition may contain ZrO₂ in an amount less than or equal to 20.0 mol.%, less than or equal to 18.0 mol.%, less than or equal to 16.0 mol.%, less than or equal to 14.0 mol.%, less than or equal to 13.5 mol.%, less than or equal to 10.0 mol.%, less than or equal to 9.0 mol.%, less than or equal to 8.1 mol.%, less than or equal to 8.0 mol.%, less than or equal to 7.8 mol.%, or less than or equal to 5.0 mol.%. In some more embodiments, the glass composition may contain ZrO₂ in an amount greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 1.0 mol.% and less than or equal to 13.5 mol.%, greater than or equal to 2.5 mol.% and less than or equal to 20.0 mol.%, greater than or equal to 4.0 mol.% and less than or equal to 9.0 mol.%, greater than or equal to 5.3 mol.% and less than or equal to 8.1 mol.%, greater than or equal to 5.6 mol.% and less than or equal to 8.0 mol.%, greater than or equal to 6.5 mol.% and less than or equal to 8.0 mol.%, greater than or equal to 6.8 mol.% and less than or equal to 7.79 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 20.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.%, greater than or equal to 1.0 mol.% and less than or equal to 5.0 mol.%, greater than or equal to 2.5 mol.% and less than or equal to 5.0 mol.%, greater than or equal to 4.0 mol.% and less than or equal to 20.0 mol.%, greater than or equal to 4.0 mol.% and less than or equal to 5.0 mol.%, greater than or equal to 5.6 mol.% and less than or equal to 20.0 mol.%, greater than or equal to 5.6 mol.% and less than or equal to 7.8 mol.%.

Glass composition may include niobia (Nb₂O₅). Niobia can be used to increase the refractive index of glass while maintaining a low density. However, niobia can introduce a yellow coloring to the glass that cannot be bleached in the same manner as titania, which can result in a loss of transmittance in the blue and UV range. Niobia may cause crystallization and/or phase separation of the melt. In some embodiments, the glasses may be substantially free of Nb₂O₅. In embodiments, the glass composition may contain niobia (Nb₂O₅) in an amount from greater than or equal to 0.0 mol.% to less than or equal to 70.0 mol.% and all ranges and sub-ranges between the foregoing values. In some embodiments, the glass composition may contain Nb₂O₅ in an amount greater than or equal to 0.0 mol.%, greater than or equal to 0.5 mol.%, greater than or equal to 2.5 mol.%, greater than or equal to 4.5 mol.%, greater than or equal to 5.0 mol.%, greater than or equal to 6.79 mol.%, greater than or equal to 10.0 mol.%, greater than or equal to 40.0 mol.%, greater than or equal to 50.0 mol.%, or greater than or equal to 60.0 mol.%. In some other embodiments, the glass composition may contain Nb₂O₅ in an amount less than or equal to 70.0 mol.%, less than or equal to 60.0 mol.%, less than or equal to 50.0 mol.%, less than or equal to 40.0 mol.%, less than or equal to 30.0 mol.%, less than or equal to 10.0 mol.%, less than or equal to 9.25 mol.%, less than or equal to 8.6 mol.%, less than or equal to 7.7 mol.%, or less than or equal to 6.7 mol.%. In some more embodiments, the glass composition may contain Nb₂O₅ in an amount greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 0.5 mol.% and less than or equal to 30.0 mol.%, greater than or equal to 2.5 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 4.5 mol.% and less than or equal to 9.25 mol.%, greater than or equal to 5.0 mol.% and less than or equal to 6.7 mol.%, greater than or equal to 5.1 mol.% and less than or equal to 8.6 mol.%, greater than or equal to 6.79 mol.% and less than or equal to 7.7 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 70.0 mol.%, greater than or equal to 2.5 mol.% and less than or equal to 70.0 mol.%, greater than or equal to 2.5 mol.% and less than or equal to 6.7 mol.%, greater than or equal to 4.5 mol.% and less than or equal to 6.7 mol.%, greater than or equal to 6.79 mol.% and less than or equal to 70.0 mol.%, greater than or equal to 10.0 mol.% and less than or equal to 30.0 mol.%.

Glass composition may include bismuth oxide (Bi₂O₃). Bi₂O₃ provides very high refractive index but leads to increase in density. It may also decrease the viscosity of melts at high temperatures, which may cause crystallization of the melts when cooling. Accordingly, the content of bismuth oxide should be limited, or glass compositions may be free of Bi₂O₃. In embodiments, the glass composition may contain bismuth oxide (Bi₂O₃) in an amount from greater than or equal to 0.0 mol.% to less than or equal to 25.0 mol.% and all ranges and sub-ranges between the foregoing values. In some embodiments, the glass composition may contain Bi₂O₃ in an amount greater than or equal to 0.0 mol.%, greater than or equal to 0.1 mol.%, greater than or equal to 5.0 mol.%, greater than or equal to 10.0 mol.%, greater than or equal to 19.0 mol.%, greater than or equal to 20.0 mol.%, greater than or equal to 21.0 mol.%, or greater than or equal to 23.0 mol.%. In some other embodiments, the glass composition may contain Bi₂O₃ in an amount less than or equal to 25.0 mol.%, less than or equal to 23.0 mol.%, less than or equal to 21.0 mol.%, less than or equal to 20.0 mol.%, less than or equal to 19.0 mol.%, less than or equal to 10.0 mol.%, less than or equal to 9.2 mol.%, or less than or equal to 5.0 mol.%. In some more embodiments, the glass composition may contain Bi₂O₃ in an amount greater than or equal to 0.0 mol.% and less than or equal to 20.0 mol.%, greater than or equal to 0.1 mol.% and less than or equal to 25.0 mol.%, greater than or equal to 0.12 mol.% and less than or equal to 9.15 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 25.0 mol.%, greater than or equal to 0.1 mol.% and less than or equal to 5.0 mol.%, greater than or equal to 5.0 mol.% and less than or equal to 9.2 mol.%, greater than or equal to 19.0 mol.% and less than or equal to 20.0 mol.%.

Glass composition may include titania (TiO₂). The levels of TiO₂ and/or Nb₂O₅ that are typically used in glasses to increase refractive index tend to decrease the transmittance in the near-UV region and shift the UV cut-off to higher wavelengths. Accordingly, the amount of TiO₂ is limited. In embodiments, the glass composition may contain titania (TiO₂) in an amount from greater than or equal to 0.0 mol.% to less than or equal to 39.1 mol.% and all ranges and sub-ranges between the foregoing values. In some embodiments, the glass composition may contain TiO₂ in an amount greater than or equal to 0.0 mol.%, greater than or equal to 0.3 mol.%, greater than or equal to 5.0 mol.%, greater than or equal to 12.0 mol.%, greater than or equal to 15.0 mol.%, greater than or equal to 20.0 mol.%, greater than or equal to 20.25 mol.%, greater than or equal to 22.0 mol.%, greater than or equal to 23.7 mol.%, greater than or equal to 24.1 mol.%, greater than or equal to 29.1 mol.%, or greater than or equal to 34.1 mol.%. In some other embodiments, the glass composition may contain TiO₂ in an amount less than or equal to 39.1 mol.%, less than or equal to 35.0 mol.%, less than or equal to 34.1 mol.%, less than or equal to 31.4 mol.%, less than or equal to 29.1 mol.%, less than or equal to 27.5 mol.%, less than or equal to 26.0 mol.%, less than or equal to 25.5 mol.%, less than or equal to 25.0 mol.%, less than or equal to 24.1 mol.%, less than or equal to 20.0 mol.%, or less than or equal to 5.0 mol.%. In some more embodiments, the glass composition may contain TiO₂ in an amount greater than or equal to 0.3 mol.% and less than or equal to 35.0 mol.%, greater than or equal to 12.0 mol.% and less than or equal to 35.0 mol.%, greater than or equal to 15.0 mol.% and less than or equal to 35.0 mol.%, greater than or equal to 20.0 mol.% and less than or equal to 27.5 mol.%, greater than or equal to 20.25 mol.% and less than or equal to 26.0 mol.%, greater than or equal to 20.25 mol.% and less than or equal to 25.5 mol.%, greater than or equal to 22.0 mol.% and less than or equal to 25.0 mol.%, greater than or equal to 23.7 mol.% and less than or equal to 31.35 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 39.1 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.%, greater than or equal to 0.3 mol.% and less than or equal to 5.0 mol.%, greater than or equal to 12.0 mol.% and less than or equal to 39.1 mol.%, greater than or equal to 12.0 mol.% and less than or equal to 20.0 mol.%, greater than or equal to 15.0 mol.% and less than or equal to 20.0 mol.%, greater than or equal to 20.0 mol.% and less than or equal to 24.1 mol.%, greater than or equal to 20.25 mol.% and less than or equal to 24.1 mol.%.

Glass composition may include fluorine (F). Adding fluorine to a glass composition is known to provide lower optical dispersion, which may improve the image quality. Also, fluorine can in some cases decrease the liquidus temperature, preventing a glass article from crystallization when cooling the melt. However, fluorine may raise ecological concerns. For that reason, the content of fluorine is limited, or glasses are free of fluorine. In embodiments, the glass composition may contain fluorine (F) in an amount from greater than or equal to 0.0 at.% to less than or equal to 2.0 at.% and all ranges and sub-ranges between the foregoing values. In some other embodiments, the glass composition may contain F in an amount less than or equal to 2.0 at.%, less than or equal to 1.0 at.%, or less than or equal to 0.1 at.%. In some more embodiments, the glass composition may contain F in an amount greater than or equal to 0.0 at.% and less than or equal to 2.0 at.%, greater than or equal to 0.0 at.% and less than or equal to 0.1 at.%.

In some embodiments, the glass composition may have a sum of La₂O₃ +TiO₂ +B₂O₃ +SiO₂ +ZrO₂ +Nb₂O₅ greater than or equal to 97.0 mol.%, greater than or equal to 98.0 mol.%, or greater than or equal to 99.0 mol.%. In some more embodiments, the glass composition may have a sum of La₂O₃ +TiO₂ +B₂O₃ +SiO₂ +ZrO₂ +Nb₂O₅ greater than or equal to 97.0 mol.% and less than or equal to 100 mol.%.

In some embodiments, the glass composition may have a sum of La₂O₃ +TiO₂ +B₂O₃ +SiO₂ +ZrO₂ +Nb₂O₅ +BaO +Y₂O₃ +CaO +Ga₂O₃ +Gd₂O₃ +ZnO +WO₃ +CeO₂ +SrO +Na₂O +Ta₂O₅ +Al₂O₃ greater than or equal to 99.0 mol.%, or greater than or equal to 99.5 mol.%. In some more embodiments, the glass composition may have a sum of La₂O₃ +TiO₂ +B₂O₃ +SiO₂ +ZrO₂ +Nb₂O₅ +BaO +Y₂O₃ +CaO +Ga₂O₃ +Gd₂O₃ +ZnO +WO₃ +CeO₂ +SrO +Na₂O +Ta₂O₅ +Al₂O₃ greater than or equal to 99.0 mol.% and less than or equal to 100 mol.%.

In some embodiments, the glass composition may have a sum of La₂O₃ +Y₂O₃ +Gd₂O₃ +TiO₂ +B₂O₃ +SiO₂ +ZrO₂ +Nb₂O₅ greater than or equal to 99.0 mol.%, or greater than or equal to 99.5 mol.%. In some more embodiments, the glass composition may have a sum of La₂O₃ +Y₂O₃ +Gd₂O₃ +TiO₂ +B₂O₃ +SiO₂ +ZrO₂ +Nb₂O₅ greater than or equal to 99.0 mol.% and less than or equal to 100 mol.%.

In some embodiments, the glass composition may have a sum of La₂O₃ +Y₂O₃ +Gd₂O₃ +TiO₂ +B₂O₃ +SiO₂ +ZrO₂ +Nb₂O₅ +CaO +BaO greater than or equal to 99.0 mol.%, or greater than or equal to 99.5 mol.%. In some more embodiments, the glass composition may have a sum of La₂O₃ +Y₂O₃ +Gd₂O₃ +TiO₂ +B₂O₃ +SiO₂ +ZrO₂ +Nb₂O₅ +CaO +BaO greater than or equal to 99.0 mol.% and less than or equal to 100 mol.%.

In some embodiments, the glass composition may have a sum of R₂O+RO greater than or equal to 0.0 mol.%, greater than or equal to 2.5 mol.%, or greater than or equal to 5.0 mol.%. In some other embodiments, the glass composition may have a sum of R₂O+RO less than or equal to 6.0 mol.%, less than or equal to 5.0 mol.%, less than or equal to 2.5 mol.%, or less than or equal to 1.0 mol.%. In some more embodiments, the glass composition may have a sum of R₂O+RO greater than or equal to 0.0 mol.% and less than or equal to 6.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 1.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 2.5 mol.%, greater than or equal to 2.5 mol.% and less than or equal to 6.0 mol.%, or greater than or equal to 2.5 mol.% and less than or equal to 5.0 mol.%.

In some embodiments, the glass composition may have a sum of RE_mO_n+WO₃+ZrO₂ greater than or equal to 0.0 mol.%, greater than or equal to 4.5 mol.%, greater than or equal to 5.0 mol.%, greater than or equal to 20.0 mol.%, or greater than or equal to 32.0 mol.%. In some other embodiments, the glass composition may have a sum of RE_mO_n+WO₃+ZrO₂ less than or equal to 36.0 mol.% or less than or equal to 20.0 mol.%. In some more embodiments, the glass composition may have a sum of RE_mO_n+WO₃+ZrO₂ greater than or equal to 0.0 mol.% and less than or equal to 36.0 mol.%, or greater than or equal to 0.0 mol.% and less than or equal to 20.0 mol.%, greater than or equal to 4.5 mol.% and less than or equal to 36.0 mol.%, or greater than or equal to 4.5 mol.% and less than or equal to 20.0 mol.%, greater than or equal to 5.0 mol.% and less than or equal to 36.0 mol.%, or greater than or equal to 5.0 mol.% and less than or equal to 20.0 mol.%.

In some embodiments, the glass composition may have a sum of SiO₂+B₂O₃ greater than or equal to 0.0 mol.%, or greater than or equal to 10.0 mol.%.

In some embodiments, the glass composition may have a sum of SiO₂+Y₂O₃+Gd₂O₃ greater than or equal to 0.0 mol.%, greater than or equal to 0.3 mol.%, greater than or equal to 8.7 mol.%, or greater than or equal to 10.0 mol.%. In some other embodiments, the glass composition may have a sum of SiO₂+Y₂O₃+Gd₂O₃ less than or equal to 15.9 mol.% or less than or equal to 10.0 mol.%. In some more embodiments, the glass composition may have a sum of SiO₂+Y₂O₃+Gd₂O₃ greater than or equal to 0.0 mol.% and less than or equal to 15.9 mol.%, or greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 0.3 mol.% and less than or equal to 15.9 mol.%, or greater than or equal to 0.3 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 8.7 mol.% and less than or equal to 15.9 mol.%.

In some embodiments, the glass composition may have a sum of TiO₂+Nb₂O₅ greater than or equal to 0.0 mol.%, greater than or equal to 8.5 mol.%, greater than or equal to 20.0 mol.%, greater than or equal to 25.0 mol.%, or greater than or equal to 40.0 mol.%. In some other embodiments, the glass composition may have a sum of TiO₂+Nb₂O₅ less than or equal to 42.0 mol.%, less than or equal to 40.0 mol.%, less than or equal to 38.0 mol.%, or less than or equal to 20.0 mol.%. In some more embodiments, the glass composition may have a sum of TiO₂+Nb₂O₅ greater than or equal to 0.0 mol.% and less than or equal to 42.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 40.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 38.0 mol.%, or greater than or equal to 0.0 mol.% and less than or equal to 20.0 mol.%, greater than or equal to 8.5 mol.% and less than or equal to 42.0 mol.%, greater than or equal to 8.5 mol.% and less than or equal to 40.0 mol.%, greater than or equal to 8.5 mol.% and less than or equal to 38.0 mol.%, or greater than or equal to 8.5 mol.% and less than or equal to 20.0 mol.%, greater than or equal to 20.0 mol.% and less than or equal to 42.0 mol.%, greater than or equal to 20.0 mol.% and less than or equal to 40.0 mol.%, or greater than or equal to 20.0 mol.% and less than or equal to 38.0 mol.%, greater than or equal to 25.0 mol.% and less than or equal to 42.0 mol.%, greater than or equal to 25.0 mol.% and less than or equal to 40.0 mol.%, or greater than or equal to 25.0 mol.% and less than or equal to 38.0 mol.%.

In some embodiments, the glass composition may have a sum of TiO₂+Nb₂O₅+La₂O₃ greater than or equal to 0.0 mol.%, greater than or equal to 10.0 mol.%, greater than or equal to 45.0 mol.%, or greater than or equal to 50.0 mol.%. In some other embodiments, the glass composition may have a sum of TiO₂+Nb₂O₅+La₂O₃ less than or equal to 70.0 mol.%, less than or equal to 63.0 mol.%, or less than or equal to 50.0 mol.%. In some more embodiments, the glass composition may have a sum of TiO₂+Nb₂O₅+La₂O₃ greater than or equal to 10.0 mol.% and less than or equal to 70.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 70.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 63.0 mol.%, or greater than or equal to 0.0 mol.% and less than or equal to 50.0 mol.%, greater than or equal to 10.0 mol.% and less than or equal to 63.0 mol.%, or greater than or equal to 10.0 mol.% and less than or equal to 50.0 mol.%, greater than or equal to 45.0 mol.% and less than or equal to 70.0 mol.%, greater than or equal to 45.0 mol.% and less than or equal to 63.0 mol.%, or greater than or equal to 45.0 mol.% and less than or equal to 50.0 mol.%.

In some other embodiments, the glass composition may have a sum of V₂O₅+MoO₃ less than or equal to 3.0 mol.%, less than or equal to 2.0 mol.%, or less than or equal to 1.0 mol.%. In some more embodiments, the glass composition may have a sum of V₂O₅+MoO₃ greater than or equal to 0.0 mol.% and less than or equal to 3.0 mol.%, greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.%, or greater than or equal to 0.0 mol.% and less than or equal to 1.0 mol.%.

In some embodiments, the glass composition may have a sum of WO₃+Bi₂O₃ greater than or equal to 0.0 mol.%, or greater than or equal to 5.0 mol.%. In some other embodiments, the glass composition may have a sum of WO₃+Bi₂O₃ less than or equal to 7.0 mol.% or less than or equal to 5.0 mol.%. In some more embodiments, the glass composition may have a sum of WO₃+Bi₂O₃ greater than or equal to 0.0 mol.% and less than or equal to 7.0 mol.%, or greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.%.

In some embodiments, the glass composition may have a sum of ZrO₂+HfO₂ greater than or equal to 0.0 mol.%, or greater than or equal to 1.0 mol.%.

In some embodiments, the glass composition may have a sum of SiO₂+B₂O₃+P₂O₅ greater than or equal to 10.0 mol.%, greater than or equal to 20.0 mol.%, greater than or equal to 26.0 mol.%, or greater than or equal to 30.0 mol.%. In some other embodiments, the glass composition may have a sum of SiO₂+B₂O₃+P₂O₅ less than or equal to 31.0 mol.%, less than or equal to 30.0 mol.%, or less than or equal to 20.0 mol.%. In some more embodiments, the glass composition may have a sum of SiO₂+B₂O₃+P₂O₅ greater than or equal to 10.0 mol.% and less than or equal to 31.0 mol.%, greater than or equal to 10.0 mol.% and less than or equal to 30.0 mol.%, or greater than or equal to 10.0 mol.% and less than or equal to 20.0 mol.%, greater than or equal to 20.0 mol.% and less than or equal to 31.0 mol.%, or greater than or equal to 20.0 mol.% and less than or equal to 30.0 mol.%, greater than or equal to 26.0 mol.% and less than or equal to 31.0 mol.%, or greater than or equal to 26.0 mol.% and less than or equal to 30.0 mol.%.

In some embodiments, glass composition may have limitations for SiO₂+B₂O₃-P₂O₅. The difference (SiO₂+B₂O₃-P₂O₅) indicates the primary glass formers. If this difference is positive, B₂O₃ and/or SiO₂ may be used as primary glassformer(s); if the difference is negative then the primary glass former may be P2O₅. In preferred embodiments of the present disclosure, the difference (SiO₂+B₂O₃-P₂O₅) is zero or positive. In some embodiments, the glass may have a difference SiO₂+B₂O₃-P₂O₅ greater than or equal to 0 mol.%, greater than or equal to 0.1 mol.%, greater than or equal to 1.0 mol.%, greater than or equal to 10.0 mol.%, greater than or equal to 20.0 mol.%, greater than or equal to 26.0 mol.%, or greater than or equal to 30.0 mol.%. In some other embodiments, the glass may have a difference SiO₂+B₂O₃-P₂O₅ less than or equal to 31.0 mol.%, less than or equal to 30.0 mol.%, less than or equal to 20.0 mol.%, or less than or equal to 10.0 mol.%. In some more embodiments, the glass may have a difference SiO₂+B₂O₃-P₂O₅ greater than or equal to 0 mol.% and less than or equal to 31.0 mol.%, greater than or equal to 0 mol.% and less than or equal to 30.0 mol.%, greater than or equal to 0 mol.% and less than or equal to 20.0 mol.%, or greater than or equal to 0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 0.1 mol.% and less than or equal to 31.0 mol.%, greater than or equal to 0.1 mol.% and less than or equal to 30.0 mol.%, greater than or equal to 0.1 mol.% and less than or equal to 20.0 mol.%, or greater than or equal to 0.1 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 1.0 mol.% and less than or equal to 31.0 mol.%, greater than or equal to 1.0 mol.% and less than or equal to 30.0 mol.%, greater than or equal to 1.0 mol.% and less than or equal to 20.0 mol.%, or greater than or equal to 1.0 mol.% and less than or equal to 10.0 mol.%, greater than or equal to 10.0 mol.% and less than or equal to 31.0 mol.%, greater than or equal to 10.0 mol.% and less than or equal to 30.0 mol.%, or greater than or equal to 10.0 mol.% and less than or equal to 20.0 mol.%, greater than or equal to 20.0 mol.% and less than or equal to 31.0 mol.%, or greater than or equal to 20.0 mol.% and less than or equal to 30.0 mol.%.

In some embodiments, glass composition may have limitations for a ratio SiO₂/(SiO₂+B₂O₃). It has been empirically found that SiO₂ and B₂O₃, when being presented together in a glass composition, may improve the glass forming ability of a melt and protect it from the liquid-liquid phase separation. Higher values of the ratio SiO₂/(SiO₂+B₂O₃) may help to improve the chemical durability, whereas lower values of this ratio may improve the solubility of the high index components. In some embodiments, the glass may have a ratio SiO₂/(SiO₂+B₂O₃)mol.% greater than or equal to 0.0, greater than or equal to =0.38, or greater than or equal to 0.5. In some other embodiments, the glass may have a ratio SiO₂/(SiO₂+B₂O₃)mol.% less than or equal to 0.75, less than or equal to 0.5, or less than or equal to 0.4. In some more embodiments, the glass may have a ratio SiO₂/(SiO₂+B₂O₃)mol.% greater than or equal to 0.0 and less than or equal to 0.4, greater than or equal to 0.38 and less than or equal to 0.75, greater than or equal to 0.0 and less than or equal to 0.75, greater than or equal to 0.0 and less than or equal to 0.5, greater than or equal to 0.38 and less than or equal to 0.5, or greater than or equal to 0.38 and less than or equal to 0.4.

In some embodiments, glass composition may have limitations for a ratio TiO₂/(TiO₂+Nb₂O₅+WO₃+Bi₂O₃). The ratio TiO₂/(TiO₂+Nb₂O₅+WO₃+Bi₂O₃) determines the mole fraction of TiO₂ in a total sum of components that provide highest refractive indexes. When the ratio TiO₂/(TiO₂+Nb₂O₅+WO₃+Bi₂O₃) is too low, it may be difficult to reach low density at high refractive index. When the ratio TiO₂/(TiO₂+Nb₂O₅+WO₃+Bi₂O₃) is too high, the glass melt may tend to phase separation or crystallization when cooling, or provide undesirable coloring that may decrease blue transmittance. Typically, a higher ratio TiO₂/(TiO₂+Nb₂O₅+WO₃+Bi₂O₃) indicates a potentially higher refractive index at a given density, but lower blue transmittance. Accordingly, in some embodiments of the present disclosure it may be desirable to reach higher refractive indexes at a given ratio TiO₂/(TiO₂+Nb₂O₅+WO₃+Bi₂O₃). In some embodiments, the glass may have a ratio TiO₂/(TiO₂+Nb₂O₅+WO₃+Bi₂O₃)Mol. % greater than or equal to 0.05, or greater than or equal to 0.5. In some other embodiments, the glass may have a ratio TiO₂/(TiO₂+Nb₂O₅+WO₃+Bi₂O₃)Mol. % less than or equal to 0.8 or less than or equal to 0.5. In some more embodiments, the glass may have a ratio TiO₂/(TiO₂+Nb₂O₅+WO₃+Bi₂O₃)Mol. % greater than or equal to 0.05 and less than or equal to 0.8, or greater than or equal to 0.05 and less than or equal to 0.5.

In some embodiments, glass composition may have limitations for a ratio La₂O₃/TiO₂. The La₂O₃/TiO₂ ratio refers to two primary high index components, TiO₂ and La₂O₃. When the ratio La₂O₃/TiO₂ is low, the glass may have lower density, but also lower blue transmittance. When the ratio La₂O₃/TiO₂ is high, the glass may have higher blue transmittance, but also higher density. Also, if the ratio La₂O₃/TiO₂ is very high or very low, in some cases the glass melt may tend to phase separation. Accordingly, in some embodiments of the present disclosure, the ratio La₂O₃/TiO₂ may be limited. In some embodiments, the glass may have a ratio La₂O₃/TiO₂ greater than or equal to 0.75 mol.%, or greater than or equal to 1.2 mol.%. In some other embodiments, the glass may have a ratio La₂O₃/TiO₂ less than or equal to 1.5 mol.%, less than or equal to 1.2 mol.%, or less than or equal to 0.94 mol.%. In some more embodiments, the glass may have a ratio La₂O₃/TiO₂ greater than or equal to 0.75 mol.% and less than or equal to 1.5 mol.%, greater than or equal to 0.75 mol.% and less than or equal to 1.2 mol.%, or greater than or equal to 0.75 mol.% and less than or equal to 0.94 mol.%.

In some embodiments, the glass may have a refractive index at 587.56 nm n_d from greater than or equal to 1.950 to less than or equal to 2.150 and all ranges and sub-ranges between the foregoing values. In some embodiments, the glass may have a refractive index at 587.56 nm n_d greater than or equal to 1.950, greater than or equal to 2.000, greater than or equal to 2.025, greater than or equal to 2.045, greater than or equal to 2.050, greater than or equal to 2.058, greater than or equal to 2.100, greater than or equal to 2.120, or greater than or equal to 2.140. In some other embodiments, the glass may have a refractive index at 587.56 nm n_d less than or equal to 2.150, less than or equal to 2.140, less than or equal to 2.120, less than or equal to 2.100, less than or equal to 2.070, less than or equal to 2.050, or less than or equal to 2.000. In some more embodiments, the glass may have a refractive index at 587.56 nm n_d greater than or equal to 1.950 and less than or equal to 2.070, greater than or equal to 1.950 and less than or equal to 2.150, greater than or equal to 1.950 and less than or equal to 2.000, greater than or equal to 2.000 and less than or equal to 2.050, greater than or equal to 2.025 and less than or equal to 2.050, greater than or equal to 2.050 and less than or equal to 2.070, greater than or equal to 2.058 and less than or equal to 2.070.

In some embodiments, the glass may have a density at room temperature d_RT from greater than or equal to 4.50 g/cm³ to less than or equal to 5.50 g/cm³ and all ranges and sub-ranges between the foregoing values. In some embodiments, the glass may have a density at room temperature d_RT greater than or equal to 4.50 g/cm³, greater than or equal to 4.90 g/cm³, greater than or equal to 5.20 g/cm³, greater than or equal to 5.30 g/cm³, or greater than or equal to 5.40 g/cm³. In some other embodiments, the glass may have a density at room temperature d_RT less than or equal to 5.50 g/cm³, less than or equal to 5.40 g/cm³, less than or equal to 5.30 g/cm³, less than or equal to 5.20 g/cm³, or less than or equal to 4.90 g/cm³. In some more embodiments, the glass may have a density at room temperature d_RT greater than or equal to 4.50 g/cm³ and less than or equal to 5.50 g/cm³, greater than or equal to 4.50 g/cm³ and less than or equal to 4.90 g/cm³, greater than or equal to 4.90 g/cm³ and less than or equal to 5.50 g/cm³, greater than or equal to 4.90 g/cm³ and less than or equal to 5.20 g/cm³, greater than or equal to 5.20 g/cm³ and less than or equal to 5.50 g/cm³, greater than or equal to 5.20 g/cm³ and less than or equal to 5.30 g/cm³, greater than or equal to 5.30 g/cm³ and less than or equal to 5.50 g/cm³, greater than or equal to 5.30 g/cm³ and less than or equal to 5.40 g/cm³.

In some embodiments, the glass may have a liquidus temperature T_liq less than or equal to 1260° C.

In some embodiments, the glass, when having a thickness of 10 mm, may have a transmittance at a wavelength of 460 nm TX_460nm, % greater than or equal to 70.

In some embodiments, the glass may have a quantity n_d - (1.765 + 0.057 * d_RT) greater than or equal to 0.000.

In some embodiments, the glass may have a quantity n_d - (1.99 + 0.083 * (TiO₂ / (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃))) greater than or equal to 0.000.

In some embodiments, the glass may have a quantity n_d - (2.005 + 0.083 * (TiO₂ / (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃))) greater than or equal to 0.000.

Refractive index n_d and density d_RT are properties of glass that can be predicted from the glass composition. A linear regression analysis of the Exemplary Glasses of the present disclosure in the EXAMPLES section below and other glass compositions reported in the literature was performed to determine equations that can predict the composition dependences of the refractive index n_d and the density d_RT.

The training dataset of glass compositions satisfying the compositional limitations specified in Table 1 below and having measured values of the properties of interest (n_d and d_ar), about 100 glass compositions for each property (n_d and d_RT), were randomly selected from literature data presented in the publicly available SciGlass Information System database and from the Exemplary Glasses from the embodiments presented herein. The linear regression analysis on the above-specified dataset, with the exclusion of outliers, was used to determine the formulas (I) and (II) presented in Table 2 below for predictive parameters P_n and P_d that predict n_d and d_RT, respectively. Another subset of glass compositions satisfying the compositional limitations of Table 1 was used as a validation set to evaluate the ability to interpolate within the compositional limitations of Table 1 and was used to establish to the standard deviations specified in the Table 2 for the predictive parameters P_n and P_d. An external dataset of prior art glass compositions, also randomly selected from the SciGlass Information System database, was used to evaluate the ability to predict the properties (n_d and d_RT) outside of the compositional limits of Table 1 with reasonable accuracy. Multiple iterations of this process were performed in order to determine the best formula for each property (n_d and d_RT). Formulas (I) and (II) in Table 2 are the result of the analysis.

The data for the Comparative Glass compositions used in the linear regression modeling, including the training dataset, validation dataset and external dataset were obtained from the publically available SciGlass Information System database. Formulas (I) and (II) below were obtained from the linear regression analysis:

In Formulas (I) and (II) and Tables 1 and 2, P_n is a predictive parameter that predicts the refractive index at 587.56 nm, n_d, calculated from the components of the glass composition expressed in mol.%, and P_d is a predictive parameter that predicts the density at room temperature, d_RT, calculated from the components of the glass composition expressed in mol.%.

In Formulas (I) and (II), each component of the glass composition is listed in terms of its chemical formula, where the chemical formula refers to the concentration of the component expressed in mol.%. For example, for purposes of Formulas (I) and (II), La₂O₃ refers to the concentration of La₂O₃, expressed in mol.%, in the glass composition. It is understood that not all components listed in Formulas (I) and (II) are necessarily present in a particular glass composition and that Formulas (I) and (II) are equally valid for glass compositions that contain less than all of the components listed in the formulas. It is further understood that Formulas (I) and (II) are also valid for glass compositions within the scope and claims of the present disclosure that contain components in addition to the components listed in the formulas. If a component listed in Formulas (I) and (II) is absent in a particular glass composition, the concentration of the component in the glass composition is 0 mol.% and the contribution of the component to the value calculated from the formulas is zero.

Composition Space Used for Modeling
Property	nd	dRT, g/cm3
Component limits	Min, mol.%	Max, mol.%	Min, mol.%	Max, mol.%
La2O3	10	40	10	40
TiO2	10	40	10	40
B2O3	10	30	10	30
SiO2	0	20	0	20
ZrO2	0	10	0	10
Nb2O5	0	15	0	15
CaO	0	15	0	15
BaO	0	10	0	10
Y2O3	0	10	0	10
ZnO	0	10	0	10
Gd2O3	0	10	0	10
Na2O	0	10	0	10
WO3	0	15	0	15
Al2O3	0	10	0	10
Li2O	0	8	0	8
F	0	0.5 [at.%]	0	2 [at.%]
Bi2O3	Not limited	Not limited	0	25
Other species	0	Not limited	0	Not limited

Property prediction models
Property	Abbreviation	Unit	Predicting Parameter	Regression Formula	Composition Unit	Standard Deviation
Refractive index at 587.56 nm	nd		Pn	Formula (I)	Mol.%	0.017
Density at room temperature	dRT	g/cm3	Pd	Formula (II)	Mol.%	0.076

FIG. 1 is a plot of the parameter P_n calculated by Formula (I) as a function of measured refractive index n_d for some Comparative Glasses (“Comp. Glasses”) taken from the literature and some Exemplary Glasses (“Ex. Glasses”). As illustrated by the data in FIG. 1, the compositional dependence of the parameter P_n had a standard deviation within a range of ± 0.017 unit of the measured n_d for the majority of glasses, which corresponds to the standard error specified in Table 2.

FIG. 2 is a plot of the parameter P_d calculated by Formula (II) as a function of measured density d_RT for some Literature Glasses (“Comp. Glasses”) and some Exemplary Glasses (“Ex. Glasses”). As illustrated by the data in FIG. 2, the compositional dependence of the parameter P_d had a standard deviation within a range of ± 0.076 unit of the measured d_RT for the majority of glasses, which corresponds to the standard deviation specified in Table 2.

Table 3 identifies the combination of components and their respective amounts according to some embodiments of the present disclosure. The Exemplary Glasses A in Table 3 may include additional components according to any aspects of the present disclosure as described herein. In Table 3, R_mO_n is a total sum of all oxides.

Exemplary Glasses A
Component                        Amount (mol.%)
TiO2                             12.0 to 35.0 mol.%
ZrO2                             2.5 to 20.0 mol.%
B2O3                             0.5 to 40.0 mol.%
Nb2O5                            0.5 to 30.0 mol.%
Bi2O3                            0.0 to 20.0 mol.%
P2O5                             0.0 to 15.0 mol.%
Al2O3                            0.0 to 10.0 mol.%
Gd2O3                            0.0 to 10.0 mol.%
WO3                              0.0 to 8.0 mol.%
PbO                              0.0 to 5.0 mol.%
V2O5                             0.0 to 5.0 mol.%
Total sum of all oxides RmOn     ≥ 95.0 mol.%
Sum of (SiO2+B2O3+P2O5)          ≥ 10.0 mol.%
Total sum of rare earth metal oxides REmOn 0.5 to 35.0 mol.%
Sum of (TiO2+Nb2O5)              0.0 to 42.0 mol.%

Exemplary Glasses A according to embodiments of the present disclosure may satisfy the following condition:

where chemical formulas refer to the amounts of components in glass, expressed in mol.%.

According to some embodiments of the present disclosure, Exemplary Glasses A may also satisfy the following condition:

${\text{n}}_{\text{d}}-\left(1.765+0.057*{\text{d}}_{\text{RT}}\right)>0.000,$

where n_d is a refractive index at 587.56 nm, and d_RT is a density at room temperature.

Table 4 identifies the combination of components and their respective amounts according to some embodiments of the present disclosure. The Exemplary Glasses B in Table 4 may include additional components according to any aspects of the present disclosure as described herein. In Tables 4 and 5, RE_mO_n is a total sum of all rare earth oxides

Exemplary Glasses B
Component                 Amount (mol.%)
ZrO2                      1.0 to 13.5 mol.%
TiO2                      0.3 to 35.0 mol.%
B2O3                      0.3 to 29.5 mol.%
WO3                       0.0 to 9.0 mol.%
PbO                       0.0 to 5.0 mol.%
Sum of (TiO2+Nb2O5+La2O3) 10.0 to 70.0 mol.%
Sum of (SiO2+B2O3+P2O5)   ≥ 10.0 mol.%
Sum of (REmOn+WO3+ZrO2)   ≥ 5.0 mol.%
Sum of (SiO2+Y2O3+Gd2O3)  ≥ 0.3 mol.%

Exemplary Glasses B according to embodiments of the present disclosure may optionally fluorine (F) in an amount 0.0 to \2.0 at.%.

According to some embodiments of the present disclosure, Exemplary Glasses B may also satisfy the following condition:

where chemical formulas refer to the amounts of components in glass, expressed in mol.%.

According to some embodiments of the present disclosure, Exemplary Glasses B may also satisfy the following condition:

where chemical formulas refer to the amounts of components in glass, expressed in mol.%.

According to some embodiments of the present disclosure, Exemplary Glasses B may also satisfy the following condition:

where chemical formulas refer to the amounts of components in glass, expressed in mol.%.

According to some embodiments of the present disclosure, Exemplary Glasses B may also satisfy the following condition:

where n_d is a refractive index at 587.56 nm.

According to some embodiments of the present disclosure, Exemplary Glasses B may also satisfy the following condition:

where n_d is a refractive index at 587.56 nm.

Table 5 identifies the combination of components and their respective amounts according to some embodiments of the present disclosure. The Exemplary Glasses C in Table 5 may include additional components according to any aspects of the present disclosure as described herein.

Exemplary Glasses C
Component               Amount (mol.%)
B2O3                    0.5 to 45.0 mol.%
Bi2O3                   0.1 to 25.0 mol.%
WO3                     0.0 to 8.0 mol.%
Sum of (SiO2+B2O3+P2O5) ≥ 10.0 mol.%
Sum of (TiO2+Nb2O5)     ≥ 8.5 mol.%
Sum of (REmOn+WO3+ZrO2) ≥ 4.5 mol.%

Exemplary Glasses C according to embodiments of the present disclosure may satisfy the following condition:

where chemical formulas refer to the amounts of components in glass, expressed in mol.%.

According to some embodiments of the present disclosure, Exemplary Glasses C may also have a refractive index at 587.56 nm n_d of greater than or equal to 2.045.

EXAMPLES

The following examples describe various features and advantages provided by the disclosure, and are in no way intended to limit the invention and appended claims.

To prepare the glass samples for some exemplary glasses of the present disclosure, about 15 grams of each sample (content of intended components in the as-batched compositions was more than 99.99 wt %) was melted from batch raw materials at a temperature of about 1300° C. in platinum or platinum-rhodium crucibles (Pt:Rh=80:20) for 1 hour. One of two controlled cooling conditions were applied. In the first condition (referred to as “15 min test” or “15 min devit test”), the cooling conditions were controlled so that it took about 15 min for the samples to cool from 1100° C. to 500° C. in air inside a furnace. In the second condition (referred to as “2.5 min test” or “2.5 min devit test”), the cooling conditions were controlled so that it took about 2.5 min for the samples to cool from 1100° C. to 500° C. in air inside a furnace. Temperature readings were obtained by direct reading of the furnace temperature or using an IR camera reading with calibration scaling. The first condition (15 min test) approximately corresponds to a cooling rate of up to 300° C./min at a temperature of 1000° C. and the second test approximately corresponds to a cooling rate of up to 600° C./min at 1000° C. The temperature of 1000° C. corresponds approximately to the temperature at which the cooling rate was expected to approach a maximum. When the temperature is lower, the cooling rate also decreases significantly. Typical schedules of the first and second cooling regimes are shown in FIG. 3. For these samples, observations referred to as “15-min devit test” and “2.5-min devit test”, are specified in Table 6 below; the observation “1” is used to denote that a glass composition passed the indicated devit test, where a composition is deemed to have passed the indicated devit test if a melt of the composition forms a glass free of crystals visible under an optical microscope under magnification from 100x to 500x. The observation “0” is used to denote that a glass composition failed the indicated devit test.

To prepare other glass samples for exemplary glasses of the present disclosure, unless otherwise specified, a one kilogram batch of the components was prepared in a pure platinum crucible. The crucible was placed in a furnace set at a temperature of 1250° C., the temperature in the furnace was then raised to 1300° C. and held at 1300° C. for 2 hours. The furnace temperature was then reduced to 1250° C. and the glass was allowed to equilibrate at this temperature for an hour before being poured on a steel table and annealed at Tg for an hour.

Some sample melts were also melted in a “one liter” platinum crucible heated by the Joule effect. In this process, approximately 5000 g of raw materials (components as batched) was used. The crucible was filled with the batch components in 1.5 hours at temperatures between 1150° C. and 1250° C. Once filled, a hold at temperature between 1200° C. and 1350° C. was done for 0.5 to one hour. During this step, the glass melt was continuously stirred (20 to 60 rpm). The hold was then extended for 0.5 to one hour with the stirrer off. A conditioning step was then done at temperatures between 1050° C. and 1300° C. and the melt was allowed to equilibrate for 0.5 to 1 hour while stirring at a rate of 20 to 60 rpm. The glass was then delivered through a tube and cast on a cooled graphite table to form the glass. The glass was formed into a bar 5 to 25 mm in thick, 30 to 60 mm wide, and 40 to 90 cm long. The glass was placed at about Tg in a lehr oven for 1 hour for a rough annealing. The bars were then annealed in a static furnace for one hour at about Tg and the temperature was then lowered at 1° C./min.

Some of samples were bleached after melting to improve the transmittance. The bleaching process was performed at the temperatures between 500° C. and T_x, the crystallization onset temperature. When the bleaching temperature is less than about 500° C., the rate of bleaching is slow and time required for bleaching is too long to be practical. When the bleaching temperature exceeds T_x, the glass may crystallize when heat treating. The higher the bleaching temperature, the faster the rate of the bleaching process, but lower transmittance is typically observed when bleaching at fast rates. Accordingly, the temperature and time of bleaching was selected to come to an acceptable transmittance within a reasonable time, such as less than or equal to 24 hours, or less than or equal to 48 hours, or less than or equal to 96 hours, or like. Before bleaching, the glasses were heated from room temperature to the bleaching temperature at a rate from 3 to5° C./min. After bleaching, the glasses were cooled from the bleaching temperature to the room temperature at a rate from 1 to3° C./min.

No chemical analysis of the tested samples was performed because chemical analysis was performed for similar samples prepared in independent meltings by XRF (X-ray fluorescence - for all oxides, except for B₂O₃ and Li₂O), by ICP-OES (inductively coupled plasma optical emission spectroscopy - for B₂O₃) and by FES (flame emission spectroscopy - for Li₂O). These analyses gave deviations from the batched compositions within ±2.0 mass %.

Some Exemplary Glasses were exposed to Nanostrip 2X cleaning solution. Dried glass samples were submerged in 600 ml of Nanostrip 2X solution (Capitol Scientific, 85% H₂SO₄ and <1% H₂O₂) for 50 min at 70° C. while stirring at 400 rpm. The ratio of surface area to volume of the glass samples used in this test was 0.08 cm^-1. After 50 minutes, the samples were quenched in deionized water and rinsed in 18 MΩ water, and then dried by high-pure nitrogen gas and placed in a desiccator overnight. Weight loss normalized to surface area (mg/cm²) and weight loss percentage (wt%) were calculated.

In Tables 6 and 7, the abbreviation “n” with a subscript refers to the refractive index at a corresponding wavelength in nm; for example, n_632.8nm refers to the refractive index at wavelengths of 632.8 nm.

Exemplary Glass Compositions
Exemplary Glass	1	2	3	4	5	6	7	8
Composition - mol.%
TiO2	mol.%	32.72	32.72	30.72	30.71	32.71	32.76	31.85	31.84
B2O3	mol.%	16.64	12.65	12.65	10.64	10.64	10.15	13.67	13.68
La2O3	mol.%	24.68	24.68	26.67	26.68	24.69	24.70	24.03	24.02
SiO2	mol.%	8.43	12.44	12.45	14.45	12.43	11.84	13.40	13.41
Nb2O5	mol.%	6.98	6.98	6.98	6.98	6.98	6.98	6.79	6.79
ZrO2	mol.%	8.01	8.00	8.00	8.00	8.00	8.01	5.78	5.79
Y2O3	mol.%	2.54	2.54	2.54	2.54	2.54	2.55	4.47	2.47
ZnO	mol.%	0	0	0	0	2.01	3.00	0	0
Gd2O3	mol.%	0	0	0	0	0	0	0	2.00
Composition constraints
SiO2 + B2O3 + P2O5	mol.%	25.07	25.08	25.09	25.09	23.07	22.00	27.07	27.09
TiO2 + Nb2O5	mol.%	39.70	39.70	37.70	37.68	39.69	39.74	38.65	38.64
SiO2 + B2O3 - P2O5	mol.%	25.07	25.08	25.09	25.09	23.07	22.00	27.07	27.09
TiO2 + Nb2O5 + La2O3	mol.%	64.38	64.38	64.37	64.37	64.38	64.44	62.68	62.65
REmOn + WO3 + ZrO2	mol.%	35.23	35.22	37.21	37.23	35.23	35.26	34.28	34.27
SiO2 + Y2O3 + Gd2O3	mol.%	10.98	14.97	14.98	16.99	14.97	14.39	17.87	17.88
TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)	mol.%	0.8242	0.8242	0.8149	0.8149	0.8242	0.8243	0.8243	0.8241
La2O3 / TiO2	mol.%	0.7543	0.7544	0.8683	0.8688	0.7547	0.7540	0.7544	0.7542
Measured properties
nd			2.065	2.0595
dRT	g/cm3		5.139
Predicted and calculated properties
Pn [for nd]		2.0672	2.0697	2.0742	2.0755	2.0795	2.0846	2.0564	2.0612
Pd [for dRT]	g/cm3	5.1508	5.1712	5.2795	5.2907	5.2426	5.277	5.098	5.1904
Pn - (1.765 + 0.057 * Pd)		0.0086	0.0099	0.0082	0.0089	0.0157	0.0188	8.800E-	3.300E-
								04	04
Pn - (1.99 + 0.083 * (TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)))		0.0088	0.0112	0.0165	0.0179	0.0211	0.0262	-0.0019	0.0028
Pn - (2.005 + 0.083 * (TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)))		-0.0062	-0.0038	0.0015	0.0029	0.0061	0.0112	-0.0169	-0.0122

Exemplary Glass	9	10	11	12	13	14	15	16
Composition - mol.%
TiO2	mol.%	31.84	30.00	28.00	25.99	29.83	31.84	29.85	30.43
B2O3	mol.%	13.68	13.67	13.67	13.69	13.67	13.67	13.68	20.42
La2O3	mol.%	24.02	24.03	24.02	24.02	24.02	24.03	24.02	23.35
Bi2O3	mol.%	0	0	0	0	4.47	2.47	0	0
SiO2	mol.%	13.40	13.40	13.41	13.41	13.41	13.41	13.40	5.43
Nb2O5	mol.%	6.80	6.80	6.79	6.79	6.80	6.80	6.79	7.70
ZrO2	mol.%	5.79	5.78	5.79	5.79	7.79	7.79	5.79	6.80
Y2O3	mol.%	2.47	4.48	4.47	4.47	0	0	6.47	5.84
WO3	mol.%	2.00	1.85	3.85	5.85	0	0	0	0
Na2O	mol.%	0	0	0	0	0	0	0	0.0258
Ta2O5	mol.%	0	0	0	0	0	0	0	0.0072
Composition constraints
SiO2 + B2O3 + P2O5	mol.%	27.09	27.07	27.08	27.10	27.08	27.08	27.08	25.85
TiO2 + Nb2O5	mol.%	38.63	36.79	34.79	32.78	36.63	38.64	36.64	38.13
SiO2 + B2O3 - P2O5	mol.%	27.09	27.07	27.08	27.10	27.08	27.08	27.08	25.85
TiO2 + Nb2O5 + La2O3	mol.%	62.66	60.82	58.81	56.80	60.65	62.66	60.66	61.47
REmOn + WO3 + ZrO2	mol.%	34.28	36.14	38.13	40.12	31.82	31.81	36.28	35.99
SiO2 + Y2O3 + Gd2O3	mol.%	15.87	17.88	17.88	17.88	13.41	13.41	19.87	11.27
TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)	mol.%	0.7835	0.7763	0.7245	0.6728	0.7259	0.7745	0.8146	0.7982
La2O3 / TiO2	mol.%	0.7545	0.8011	0.8580	0.9240	0.8052	0.7545	0.8047	0.7673
Measured properties
nd						2.070	2.0579
dRT	g/cm3	5.117	5.154
15-min devit test (0/1)									1
Tliq	°C								1281
Predicted and calculated properties
Pn [for nd]		2.0556	2.0581	2.0598	2.0614	2.0942	2.0746	2.0588	2.0643
Pd [for dRT]	g/cm3	5.1099	5.1579	5.2223	5.2862	5.4181	5.2434	5.1495	5.1059
Pn - (1.765 + 0.057 * Pd)		-6.500E-04	-8.900E-04	-0.0029	-0.0049	0.0204	0.0107	3.400E-04	0.0082
Pn - (1.99 + 0.083 * (TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)))		5.800E-04	0.0037	0.0097	0.0156	0.0440	0.0203	0.0013	0.0079
Pn - (2.005 + 0.083 * (TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)))		-0.0144	-0.0113	-0.0053	5.700E-04	0.0290	0.0053	-0.0138	-0.0071

Exemplary Glass	17	18	19	20	21	22	23	24
Composition - mol.%
TiO2	mol.%	16.96	16.98	16.97	16.97	16.97	16.96	16.98	16.98
B2O3	mol.%	28.53	29.03	29.46	31.39	30.09	30.77	29.34	29.95
La2O3	mol.%	21.56	18.50	16.03	19.97	19.98	19.97	19.97	19.97
Bi2O3	mol.%	8.79	11.83	11.00	9.30	8.27	13.11	12.39	17.97
SiO2	mol.%	9.25	10.32	10.84	7.51	5.97	7.71	6.12	8.00
Nb2O5	mol.%	5.58	5.93	8.20	7.71	5.68	4.33	1.86	0
ZrO2	mol.%	7.14	7.26	7.36	6.99	6.99	6.99	7.00	6.98
WO3	mol.%	2.03	0	0	0	5.91	0	6.19	0
CeO2	mol.%	0.12	0.12	0.0916	0.12	0.11	0.12	0.12	0.11
CaO	mol.%	0.0319	0.0322	0.0312	0.0317	0.032	0.0332	0.0336	0.0351
Ta2O5	mol.%	0.004	0.0041	0.0079	0.008	0.0041	0.0042	0	0
Composition constraints
SiO2 + B2O3 + P2O5	mol.%	37.80	39.38	40.32	38.93	36.08	38.51	35.48	37.96
TiO2 + Nb2O5	mol.%	22.56	22.92	25.18	24.69	22.66	21.30	18.85	16.99
SiO2 + B2O3 - P2O5	mol.%	37.80	39.38	40.32	38.93	36.08	38.51	35.48	37.96
TiO2 + Nb2O5 + La2O3	mol.%	44.13	41.43	41.22	44.67	42.65	41.29	38.83	36.97
REmOn + WO3 + ZrO2	mol.%	30.80	25.83	23.45	27.04	32.95	27.04	33.23	27.03
SiO2 + Y2O3 + Gd2O3	mol.%	9.259	10.33	10.85	7.516	5.973	7.718	6.125	8.000
TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)	mol.%	0.5085	0.4888	0.4692	0.4995	0.4609	0.4932	0.4537	0.4858
La2O3 / TiO2	mol.%	1.271	1.090	0.9443	1.176	1.177	1.177	1.176	1.176
Measured properties
dRT	g/cm3				5.308	5.457	5.603	5.737
15-min devit test (0/1)		1	1	1
n531.9nm								2.0619
n632.8nm								2.0371
Predicted and calculated properties
Pn [for nd]		2.0459	2.0578	2.048	2.0461	2.0516	2.071	2.0789	2.1028
Pd [for dRT]	g/cm3	5.4649	5.4739	5.2549	5.3235	5.4743	5.6624	5.8517	6.0951
Pn - (1.765 + 0.057 * Pd)		-0.0306	-0.0193	-0.0166	-0.0223	-0.0255	-0.0167	-0.0196	-0.0096
Pn - (1.99 + 0.083 * (TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)))		0.0137	0.0272	0.0190	0.0147	0.0233	0.0401	0.0514	0.0725
Pn - (2.005 + 0.083 * (TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)))		-0.0013	0.0122	0.0040	-3.300E-04	0.0083	0.0251	0.0364	0.0575

Exemplary Glass	25	26	27	28	29	30	31	32
Composition - mol.%
TiO2	mol.%	16.97	19.97	30.43	30.41	30.90	31.10	30.74	31.19
B2O3	mol.%	28.93	31.41	20.42	24.41	20.42	20.42	20.41	20.41
La2O3	mol.%	19.17	21.96	23.35	20.85	23.63	24.03	23.13	23.90
Bi2O3	mol.%	8.12	9.15	0	0	0	0	0	0
SiO2	mol.%	9.76	9.49	5.43	0.0267	5.44	5.44	5.43	5.43
Nb2O5	mol.%	7.70	7.84	7.70	7.70	7.22	7.02	7.39	6.94
ZrO2	mol.%	7.23	0	6.80	6.80	6.80	6.80	6.79	6.81
Y2O3	mol.%	0	0	5.84	5.34	5.56	5.16	6.07	5.29
WO3	mol.%	1.97	0	0	4.44	0	0	0	0
CeO2	mol.%	0.11	0.14	0	0	0	0	0	0
CaO	mol.%	0.031	0.0319	0	0	0	0	0	0
Na2O	mol.%	0	0	0.0258	0.0259	0.0257	0.0257	0.0257	0.0257
Ta2O5	mol.%	0.0079	0.0081	0.0072	0.0073	0.0072	0.0072	0.0072	0.0072
Composition constraints
SiO2 + B2O3 + P2O5	mol.%	38.71	40.94	25.85	24.44	25.85	25.86	25.85	25.84
TiO2 + Nb2O5	mol.%	24.69	27.83	38.13	38.11	38.12	38.12	38.13	38.14
SiO2 + B2O3 - P2O5	mol.%	38.71	40.94	25.85	24.44	25.85	25.86	25.85	25.84
TiO2 + Nb2O5 + La2O3	mol.%	43.87	49.80	61.48	58.96	61.75	62.15	61.26	62.04
REmOn + WO3 + ZrO2	mol.%	28.44	22.04	35.99	37.42	35.99	35.99	35.99	35.99
SiO2 + Y2O3 + Gd2O3	mol.%	9.768	9.501	11.27	5.364	11.00	10.60	11.50	10.71
TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)	mol.%	0.4883	0.5404	0.7982	0.7148	0.8105	0.8160	0.8062	0.8179
La2O3 / TiO2	mol.%	1.130	1.100	0.7673	0.6855	0.7648	0.7726	0.7522	0.7664
Measured properties
15-min devit test (0/1)		1
Tliq	°C			1300	1300	1280	1269	1286	1269
Predicted and calculated properties
Pn [for nd]		2.0374	2.0387	2.0641	2.0686	2.0622	2.0617	2.0625	2.0613
Pd [for dRT]	g/cm3	5.2625	5.2265	5.105	5.1007	5.1126	5.1235	5.0984	5.1202
Pn - (1.765 + 0.057 * Pd)		-0.0276	-0.0242	0.0082	0.0128	0.0058	0.0046	0.0069	0.0045
Pn - (1.99 + 0.083 * (TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)))		0.0068	0.0039	0.0079	0.0192	0.0050	0.0039	0.0056	0.0034
Pn - (2.005 + 0.083 * (TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)))		-0.0082	-0.0111	-0.0071	0.0043	-0.0100	-0.0111	-0.0094	-0.0116

Exemplary Glass	33	34	35	36	37	38	39	40
Composition - mol.%
TiO2	mol.%	31.32	31.78	31.84	29.16	29.21	27.94	30.29	29.94
B2O3	mol.%	20.41	20.41	13.67	22.05	24.04	23.65	21.95	22.34
La2O3	mol.%	23.86	24.69	24.03	23.10	21.83	22.86	23.50	23.42
Bi2O3	mol.%	0	0	0	0.76	0.73	1.50	0.57	0.76
SiO2	mol.%	5.44	5.44	13.40	4.21	1.47	2.99	4.29	3.99
Nb2O5	mol.%	6.80	6.35	6.80	8.45	8.43	9.20	7.74	7.95
ZrO2	mol.%	6.80	6.80	7.79	6.81	6.80	6.80	6.80	6.80
Y2O3	mol.%	5.32	4.50	2.47	5.43	5.19	5.04	4.83	4.76
WO3	mol.%	0	0	0	0	2.28	0	0	0
Na2O	mol.%	0.0256	0.0256	0	0.0263	0.0263	0.0268	0.026	0.0261
Ta2O5	mol.%	0.0072	0.0072	0	0.0074	0.0074	0.0075	0.0073	0.0073
Composition constraints
SiO2 + B2O3 + P2O5	mol.%	25.85	25.85	27.07	26.26	25.51	26.64	26.24	26.33
TiO2 + Nb2O5	mol.%	38.13	38.13	38.64	37.62	37.64	37.14	38.03	37.89
SiO2 + B2O3 - P2O5	mol.%	25.85	25.85	27.07	26.26	25.51	26.64	26.24	26.33
TiO2 + Nb2O5 + La2O3	mol.%	61.99	62.82	62.67	60.71	59.46	59.99	61.52	61.31
REmOn + WO3 + ZrO2	mol.%	35.99	35.99	34.29	35.34	36.09	34.70	35.13	34.98
SiO2 + Y2O3 + Gd2O3	mol.%	10.77	9.942	15.87	9.641	6.659	8.026	9.125	8.749
TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)	mol.%	0.8216	0.8335	0.8241	0.7600	0.7187	0.7232	0.7848	0.7746
La2O3 / TiO2	mol.%	0.7618	0.7769	0.7546	0.7920	0.7472	0.8181	0.7759	0.7824
Measured properties
dRT	g/cm3			5.080
15-min devit test (0/1)								1	1
Tliq	°C	1263	1269		1284	1285	1275
Predicted and calculated properties
Pn [for nd]		2.0605	2.0593	2.0533	2.0703	2.0725	2.0765	2.0654	2.0672
Pd [for dRT]	g/cm3	5.1184	5.1414	5.092	5.133	5.1301	5.1609	5.1225	5.130
Pn - (1.765 + 0.057 * Pd)		0.0038	0.0012	-0.0019	0.0127	0.0150	0.0173	0.0085	0.0098
Pn - (1.99 + 0.083 * (TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)))		0.0023	8.300E-05	-0.0051	0.0172	0.0228	0.0265	0.0103	0.0129
Pn - (2.005 + 0.083 * (TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)))		-0.0127	-0.0149	-0.0201	0.0022	0.0078	0.0115	-0.0047	-0.0021

Exemplary Glass	41	42	43	44	45	46	47	48
Composition - mol.%
TiO2	mol.%	31.14	30.43	30.15	30.43	30.42	30.42	30.43	30.42
B2O3	mol.%	21.31	21.23	21.58	21.23	20.89	21.24	21.06	20.92
La2O3	mol.%	23.72	23.72	23.67	23.72	23.72	23.73	23.73	23.73
Bi2O3	mol.%	0.23	0.38	0.54	0.38	0.20	0.12	0.11	0.11
SiO2	mol.%	4.77	4.82	4.57	4.82	4.68	4.82	4.73	4.67
Nb2O5	mol.%	7.22	7.44	7.60	7.44	7.44	7.44	7.44	7.44
ZrO2	mol.%	6.80	6.80	6.80	6.80	6.80	6.80	6.80	6.80
Y2O3	mol.%	4.78	5.14	5.04	5.14	5.13	5.13	5.13	5.14
Li2O	mol.%	0	0	0	0	0.70	0	0.37	0.64
K2O	mol.%	0	0	0	0	0	0.27	0.17	0.10
Na2O	mol.%	0.0257	0.026	0.0261	0.026	0.0258	0.0258	0.0258	0.0257
Ta2O5	mol.%	0.0072	0.0073	0.0073	0.0073	0.0072	0.0072	0.0072	0.0072
Composition constraints
SiO2 + B2O3 + P2O5	mol.%	26.08	26.05	26.15	26.05	25.57	26.06	25.79	25.60
TiO2 + Nb2O5	mol.%	38.36	37.87	37.75	37.87	37.85	37.86	37.86	37.86
SiO2 + B2O3 - P2O5	mol.%	26.08	26.05	26.15	26.05	25.57	26.06	25.79	25.60
TiO2 + Nb2O5 + La2O3	mol.%	62.08	61.59	61.42	61.59	61.57	61.59	61.59	61.59
REmOn + WO3 + ZrO2	mol.%	35.30	35.66	35.52	35.66	35.65	35.66	35.67	35.66
SiO2 + Y2O3 + Gd2O3	mol.%	9.550	9.956	9.615	9.956	9.814	9.949	9.865	9.811
TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)	mol.%	0.8069	0.7955	0.7874	0.7955	0.7994	0.8010	0.8013	0.8013
La2O3 / TiO2	mol.%	0.7619	0.7796	0.7850	0.7796	0.7799	0.7799	0.7798	0.7799
Measured properties
15-min devit test (0/1)		1	1	1
Tliq	°C		1264	1268	1272	1275	1274	1278	1283
Predicted and calculated properties
Pn [for nd]		2.0616	2.0648	2.0661	2.0648	2.0634	2.0603	2.0612	2.0619
Pd [for dRT]	g/cm3	5.1088	5.1328	5.1386	5.1328	5.1233	5.104	5.1095	5.1137
Pn - (1.765 + 0.057 * Pd)		0.0054	0.0073	0.0082	0.0073	0.0064	0.0044	0.0050	0.0054
Pn - (1.99 + 0.083 * (TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)))		0.0047	0.0088	0.0107	0.0088	0.0071	0.0038	0.0047	0.0054
Pn - (2.005 + 0.083 * (TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)))		-0.0103	-0.0062	-0.0043	-0.0062	-0.0079	-0.0112	-0.0103	-0.0096

Exemplary Glass	49	50	51	52	53	54	55	56
Composition - mol.%
TiO2	mol.%	30.42	30.43	30.41	30.41	30.42	30.42	30.43	30.44
B2O3	mol.%	21.05	21.25	21.25	21.04	21.24	21.05	21.25	20.92
La2O3	mol.%	23.72	23.72	23.72	23.71	23.73	23.72	23.72	23.72
Bi2O3	mol.%	0.10	0.19	0	0	0.11	0.10	0.19	0.10
SiO2	mol.%	4.73	4.82	4.83	4.74	4.82	4.73	4.82	4.67
Nb2O5	mol.%	7.44	7.44	7.44	7.44	7.44	7.44	7.44	7.44
ZrO2	mol.%	6.80	6.80	6.80	6.80	6.80	6.80	6.80	6.80
Y2O3	mol.%	5.13	5.13	5.13	5.13	5.13	5.13	5.13	5.14
Li2O	mol.%	0.37	0	0	0.43	0	0.37	0	0.64
K2O	mol.%	0.19	0.19	0.39	0.27	0.27	0.19	0.19	0.10
Na2O	mol.%	0.0258	0.0258	0.0257	0.0257	0.0258	0.0258	0.0258	0.0257
Ta2O5	mol.%	0.0072	0.0072	0.0072	0.0072	0.0072	0.0072	0.0072	0.0072
Composition constraints
SiO2 + B2O3 + P2O5	mol.%	25.78	26.07	26.08	25.78	26.06	25.78	26.07	25.59
TiO2 + Nb2O5	mol.%	37.86	37.87	37.85	37.85	37.86	37.86	37.87	37.87
SiO2 + B2O3 - P2O5	mol.%	25.78	26.07	26.08	25.78	26.06	25.78	26.07	25.59
TiO2 + Nb2O5 + La2O3	mol.%	61.58	61.58	61.57	61.56	61.59	61.58	61.58	61.60
REmOn + WO3 + ZrO2	mol.%	35.66	35.65	35.65	35.64	35.66	35.66	35.65	35.66
SiO2 + Y2O3 + Gd2O3	mol.%	9.864	9.957	9.960	9.875	9.950	9.864	9.957	9.809
TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)	mol.%	0.8014	0.7995	0.8035	0.8035	0.8011	0.8014	0.7995	0.8015
La2O3 / TiO2	mol.%	0.7798	0.7794	0.7799	0.7797	0.7799	0.7798	0.7794	0.7794
Measured properties
nd			2.0533
dRT	g/cm3	4.909	4.946
2.5-min devit test (0/1)				1	1	1	1	1	1
15-min devit test (0/1)		1	1
Tg	°C	714	719
Tx	°C	814	827
n531.9nm			2.0667
n632.8nm			2.0453
Predicted and calculated properties
Pn [for nd]		2.0611	2.0615	2.0582	2.0593	2.0602	2.0611	2.0615	2.0619
Pd [for dRT]	g/cm3	5.1088	5.1115	5.0909	5.0973	5.1038	5.1088	5.1115	5.1132
Pn - (1.765 + 0.057 * Pd)		0.0049	0.0051	0.0030	0.0037	0.0043	0.0049	0.0051	0.0054
Pn - (1.99 + 0.083 * (TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)))		0.0046	0.0051	0.0015	0.0026	0.0038	0.0046	0.0051	0.0054
Pn - (2.005 + 0.083 * (TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)))		-0.0104	-0.0099	-0.0135	-0.0124	-0.0112	-0.0104	-0.0099	-0.0096

Exemplary Glass	57	58	59	60	61	62	63	64
Composition - mol.%
TiO2	mol.%	30.43	30.44	30.43	30.43	30.43	27.83	25.84	31.35
B2O3	mol.%	21.06	21.25	20.89	21.05	21.23	13.69	13.69	13.68
La2O3	mol.%	23.72	23.73	23.72	23.73	23.72	24.02	24.03	24.02
Bi2O3	mol.%	0.18	0.28	0.19	0.28	0.38	6.47	8.47	0.50
SiO2	mol.%	4.74	4.81	4.68	4.72	4.82	13.41	13.39	13.41
Nb2O5	mol.%	7.44	7.44	7.44	7.44	7.44	6.79	6.79	6.79
ZrO2	mol.%	6.80	6.80	6.80	6.81	6.80	7.79	7.79	7.79
Y2O3	mol.%	5.13	5.13	5.13	5.13	5.14	0	0	2.47
Li2O	mol.%	0.37	0	0.70	0.38	0	0	0	0
K2O	mol.%	0.10	0.10	0	0	0	0	0	0
Na2O	mol.%	0.0258	0.0259	0.0258	0.0259	0.026	0	0	0
Ta2O5	mol.%	0.0072	0.0073	0.0072	0.0073	0.0073	0	0	0
Composition constraints
SiO2 + B2O3 + P2O5	mol.%	25.80	26.06	25.57	25.77	26.05	27.10	27.08	27.09
TiO2 + Nb2O5	mol.%	37.86	37.87	37.87	37.87	37.87	34.62	32.63	38.14
SiO2 + B2O3 - P2O5	mol.%	25.80	26.06	25.57	25.77	26.05	27.10	27.08	27.09
TiO2 + Nb2O5 + La2O3	mol.%	61.58	61.60	61.58	61.60	61.59	58.64	56.66	62.15
REmOn + WO3 + ZrO2	mol.%	35.65	35.66	35.65	35.67	35.66	31.81	31.82	34.28
SiO2 + Y2O3 + Gd2O3	mol.%	9.870	9.939	9.812	9.857	9.956	13.41	13.39	15.87
TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)	mol.%	0.7998	0.7978	0.7995	0.7977	0.7955	0.6773	0.6286	0.8113
La2O3 / TiO2	mol.%	0.7795	0.7795	0.7795	0.7798	0.7796	0.8631	0.9299	0.7661
Measured properties
nd									2.0557
dRT	g/cm3						5.533	5.673
2.5-min devit test (0/1)		1	1	1	1	1
Tg	°C						696	684	740
Tx	°C						802	783
Predicted and calculated properties
Pn [for nd]		2.0623	2.063	2.0634	2.0642	2.0648	2.1137	2.1336	2.0581
Pd [for dRT]	g/cm3	5.1167	5.1211	5.1231	5.1281	5.1328	5.5921	5.768	5.1348
Pn - (1.765 + 0.057 * Pd)		0.0057	0.0061	0.0064	0.0069	0.0073	0.0300	0.0398	4.000E-04
Pn - (1.99 + 0.083 * (TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)))		0.0060	0.0068	0.0071	0.0080	0.0088	0.0675	0.0914	7.400E-04
Pn - (2.005 + 0.083 * (TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)))		-0.0091	-0.0082	-0.0080	-0.0070	-0.0062	0.0525	0.0764	-0.0143

Exemplary Glass	65	66	67
Composition - mol.%
TiO2	mol.%	30.86	30.35	23.70
B2O3	mol.%	13.67	13.68	16.53
La2O3	mol.%	24.03	24.02	22.70
Bi2O3	mol.%	1.00	1.50	5.00
SiO2	mol.%	13.39	13.39	14.55
Nb2O5	mol.%	6.79	6.79	5.00
ZrO2	mol.%	7.79	7.79	8.01
Y2O3	mol.%	2.47	2.47	4.50
Composition constraints
SiO2 + B2O3 + P2O5	mol.%	27.07	27.07	31.09
TiO2 + Nb2O5	mol.%	37.65	37.14	28.70
SiO2 + B2O3 - P2O5	mol.%	27.07	27.07	31.09
TiO2 + Nb2O5 + La2O3	mol.%	61.68	61.16	51.41
REmOn + WO3 + ZrO2	mol.%	34.29	34.29	35.21
SiO2 + Y2O3 + Gd2O3	mol.%	15.86	15.87	19.06
TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)	mol.%	0.7984	0.7854	0.7032
La2O3 / TiO2	mol.%	0.7787	0.7916	0.9580
Measured properties
nd		2.0583	2.0605
Tg	°C		739	696
Tx	°C			829
Predicted and calculated properties
Pn [for nd]		2.0632	2.068	2.0649
Pd [for dRT]	g/cm3	5.1793	5.2229	5.4342
Pn - (1.765 + 0.057 * Pd)		0.0030	0.0053	-0.0099
Pn - (1.99 + 0.083 * (TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)))		0.0069	0.0129	0.0165
Pn - (2.005 + 0.083 * (TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)))		-0.0081	-0.0021	0.0015

Table 7 below lists the glass compositions and properties for Comparative Glasses C1-C32.

Compositions and Properties of Comparative Example Glasses
Comparative Examples	C1	C2	C3	C4	C5	C6	C7	C8
Reference		[4]	[6]	[10]	[5]	[3]	[9]	[1]	[2]
Composition - mol.%
La2O3	mol.%	13.98	26.70	23.31	19.99	22.68	22.73	22.70	22.29
Nb2O5	mol.%	11.98	4.70	5.59	17.99	5.55	5.55	5.67	5.57
TiO2	mol.%	26.47	22.68	31.38	12.99	31.92	31.78	31.04	30.46
B2O3	mol.%	19.96	13.01	14.22	34.98	18.27	18.28	14.80	14.53
SiO2	mol.%	15.47	7.54	11.24	0.0575	7.59	7.54	11.52	11.30
ZrO2	mol.%	6.99	12.50	8.31	6.99	9.03	9.19	8.30	8.15
CaO	mol.%	5.00	0	0	0	0	0	0	0
CeO2	mol.%	0.0853	0	0	0	0	0	0	0
Ta2O5	mol.%	0.0121	1.72	0	0.0156	0	0	0	0
Al2O3	mol.%	0.0131	2.67	0	0	0	0	0	0
MgO	mol.%	0.0331	0	0	0	0	0	0	0
Gd2O3	mol.%	0	3.80	0	0	4.97	4.93	0	0
Y2O3	mol.%	0	4.49	4.92	0	0	0	4.96	4.87
As2O3	mol.%	0	0.18	0	0	0	0	0	0
WO3	mol.%	0	0	0.50	7.00	0	0	0.50	0.49
Li2O	mol.%	0	0	0.52	0	0	0	0.51	0.51
CO2	mol.%	0	0	0	0	0	0	0	1.24
SO2	mol.%	0	0	0	0	0	0	0	0.59
nd			2.0145	2.050		2.0533	2.0533	2.050	2.050
dRT	g/cm3		4.950	5.100		5.270	5.270
Tliq	oC			1250.0		1260.0	1260.0
Tg	oC					738.00	738.00
n531.9 nm			2.0261	2.0630		2.0663	2.0663	2.0630	2.0630
n632.8 nm			2.0075	2.0422		2.0454	2.0454	2.0421	2.0421
Pn [for nd]		1.975	2.083	2.058	2.033	2.064	2.065	2.050	2.047
Pd [for dRT]	g/cm3	4.322	5.715	5.165	4.793	5.338	5.342	5.116	5.108

Comparative Examples	C9	C10	C11	C12	C13	C14	C15	C16
Reference		[7]	[8]	[14]	[9]	[10]	[11]	[3]	[7]
Composition - mol.%
La2O3	mol.%	12.78	22.47	0.73	22.61	23.27	19.12	22.50	11.35
Nb2O5	mol.%	8.09	4.43	9.50	5.52	5.58	5.45	4.43	5.08
TiO2	mol.%	33.63	34.38	20.66	27.07	31.33	34.46	34.35	34.01
B2O3	mol.%	11.96	12.94	2.74	15.36	13.09	13.53	12.95	12.94
SiO2	mol.%	11.18	15.29	28.22	11.65	12.51	9.64	15.31	10.81
ZrO2	mol.%	5.56	7.02	5.71	9.13	8.30	6.47	7.04	8.18
CaO	mol.%	3.59	0	28.15	0	0	0	0	0
Ta2O5	mol.%	0	0	0	2.27	0	0	0	0
Al2O3	mol.%	0	0	0.26	0	0	0	0	0
MgO	mol.%	1.33	0	0	0	0	0	0	0
Gd2O3	mol.%	0.74	3.11	0	4.90	0	0	3.06	0.55
Y2O3	mol.%	0.30	0.38	0	0	4.91	0	0.36	0.82
WO3	mol.%	0	0	0	0	0.50	0	0	0.40
Li2O	mol.%	0	0	3.98	0	0.52	0	0	0
BaO	mol.%	8.85	0	0	0	0	11.34	0	13.13
Yb2O3	mol.%	0.34	0	0	0	0	0	0	0.13
SrO	mol.%	0.78	0	0	0	0	0	0	1.41
ZnO	mol.%	0.83	0	0	1.49	0	0	0	1.14
Sb2O3	mol.%	0.0461	0	0.006	0	0	0	0	0.045
HfO2	mol.%	0	0	0.0581	0	0	0	0	0
Measured properties
nd		2.0137	2.048	1.9395	2.0451	2.051	2.040	2.048	2.016
dRT	g/cm3	4.720	5.140	3.710	5.420	5.100	4.950	5.140	4.720
Tliq	°C		1260.0	1400.0	1250.0	1250.0	1250.0	1260.0
Log(ηliq)	P						0.50000
Tg	°C	684.00	750.00		746.00			750.00	682.00
n531.9nm		2.0271	2.0612	1.9523	2.0577	2.0640	2.0550	2.0612	2.0291
n632.8nm		2.0056	2.0400	1.9318	2.0374	2.0432	2.0310	2.0400	2.0081
TX460nm, %				93.000
Predicted and calculated properties
Pn [for nd]		2.020	2.040	1.881	2.047	2.057	2.033	2.040	2.001
Pd [for dRT]	g/cm3	4.761	5.143	3.792	5.364	5.166	5.035	5.141	4.809

Reference	[4]	[12]	[13]	[15]	[18]	[16]	[17]	[8]
Comparative Examples	C17	C18	C19	C20	C21	C22	C23	C24
Composition - mol.%
La2O3	mol.%	14.21	0.72	0.72	14.43	0	21.67	23.43	20.99
Nb2O5	mol.%	3.00	8.36	8.36	18.64	0	7.19	9.59	5.07
TiO2	mol.%	33.73	26.08	26.08	16.45	23.52	16.97	31.96	33.06
B2O3	mol.%	17.00	2.71	2.71	22.96	17.65	28.51	22.84	13.45
SiO2	mol.%	9.98	21.04	21.04	4.48	5.89	8.92	1.66	13.57
ZrO2	mol.%	6.99	5.74	5.74	6.55	2.36	7.13	1.59	7.95
CaO	mol.%	14.99	16.92	16.92	0	0	0.031	0.78	0
CeO2	mol.%	0.0878	0	0	0	0	0.13	0	0
Ta2O5	mol.%	0	0	0	1.36	0	0.0079	0	0
Al2O3	mol.%	0	0	0	0	17.64	0	0	0
MgO	mol.%	0	0	0	0	0	0	1.47	0
Gd2O3	mol.%	0	0	0	0	0	0	0.97	0
Y2O3	mol.%	0	0	0	0	0	0	0.56	0
WO3	mol.%	0	0	0	0	0	3.44	0	0
Li2O	mol.%	0	3.94	3.94	0	0	0	0	0
BaO	mol.%	0	14.47	14.47	0	0	0	0	0
Yb2O3	mol.%	0	0	0	0	0	0	0	3.40
ZnO	mol.%	0	0	0	0	0	0	2.89	2.51
Sb2O3	mol.%	0	0.0069	0.0069	0	0	0	0	0
Fe2O3	mol.%	0.0073	0	0	0	0	0	0	0
GeO2	mol.%	0	0	0	15.13	0	0	0	0
Er2O3	mol.%	0	0	0	0	32.94	0	0	0
Bi2O3	mol.%	0	0	0	0	0	6.01	0	0
Na2O	mol.%	0	0	0	0	0	0	2.26	0
Measured properties
nd			1.9729	1.9729	2.000	1.911		2.0023	2.051
dRT	g/cm3		4.167	4.167					5.210
Tliq	°C			1230.0					1240.0
Tg	°C		664.30	664.30					731.00
Tx	°C		818.20
n531.9nm			1.9863	1.9863	2.0132			2.0142	2.0643
n632.8nm			1.9647	1.9647	1.9920			1.9951	2.0429
Predicted and calculated properties
Pn [for nd]		1.960	1.928	1.928	1.996	2.038	2.030	2.050	2.052
Pd [for dRT]	g/cm3	4.507	4.184	4.184	4.412	5.715	5.281	4.959	5.192

Comparative Examples	C25	C26	C27	C28	C29	C30	C31	C32
Reference	[3]	[9]	[21]	[9]	[8]	[3]	[19]	[20]
Composition - mol.%
La2O3	mol.%	20.98	20.99	28.61	21.65	21.64	21.65	12.26	16.19
Nb2O5	mol.%	5.08	5.07	1.61	5.23	5.22	5.23	8.87	5.22
TiO2	mol.%	33.22	33.05	22.93	34.09	34.10	34.27	17.51	34.76
B2O3	mol.%	13.46	13.47	19.13	13.87	13.86	13.86	7.26	15.95
SiO2	mol.%	13.54	13.55	8.46	13.98	14.02	14.01	2.80	13.86
ZrO2	mol.%	7.79	7.94	11.40	8.24	8.21	8.04	12.31	9.01
Ta2O5	mol.%	0	0	0	0	0	0	8.39	0
Gd2O3	mol.%	0	0	1.87	0	0	0	0	1.92
Y2O3	mol.%	0	0	1.04	0.37	0.37	0.37	0	3.07
Yb2O3	mol.%	3.40	3.40	0	0	0	0	0	0
ZnO	mol.%	2.52	2.52	4.96	2.58	2.58	2.58	0	0
GeO2	mol.%	0	0	0	0	0	0	30.60	0
Measured pro perties
nd		2.051	2.051	2.0359	2.054	2.054	2.054	2.028	2.0425
dRT	g/cm3	5.210	5.210		4.960	4.960	4.960
Tliq	°C	1240.0	1240.0		1250.0	1250.0	1250.0
Tg	°C	731.00	731.00		721.00	721.00	721.00	722.00
n531.9nm		2.0643	2.0643	2.0462	2.0677	2.0677	2.0677	2.0413	2.0565
n632.8nm		2.0429	2.0429	2.0295	2.0457	2.0457	2.0457	2.0200	2.0341
Predicted and calculated properties
Pn [for nd]		2.052	2.052	2.024	2.026	2.026	2.026	1.970	2.016
Pd [for dRT]	g/cm3	5.188	5.192	5.550	4.940	4.938	4.934	4.782	4.791

The reference key for each of the Comparative Glasses listed in Table 7 is as follows: [1] CN111320384A; [2] JP2020169116A; [3] JP6943995; [4] US20220073410A1; [5] U.S. Pat. Application Serial No. 17/683,527 (filed Mar. 1, 2022); [6] US4584279A; [7] US9169152B2; [8] US9302930B2; [9] US9643880B2; [10] WO2019131123A1; [11] JP2021102549A; [12] US8852745B2; [13] WO2014057584A1; [14] WO2021171950A1; [15] JPH09278480; [16] US20220073410A1; [17] TW202012333; [18] US5747397A; [19] JP2006151758A; [20] JPS6033229; [21] US9487432B2.

FIG. 4 is a plot showing the relationship between the parameter P_d that predicts density at room temperature and the parameter P_n that predicts refractive index at 587.56 nm for some of the Exemplary Glasses and some of the Comparative Glasses. The Exemplary Glasses (filled circles) are the Examples 1 to 4, 7, 8, 13 to 16, 27 to 34 and 51 to 66 from Table 6. The Comparative Glasses (open circles) are the Examples C1 to C10 from Table 7. The parameter P_d that predicts density at room temperature was determined according to Formula (II). The parameter P_n that predicts refractive index at 587.56 nm was determined according to Formula (1). All of the Exemplary Glasses and Comparative Glasses shown in FIG. 4 have the features specified in Table 8. In Table 8, the specification “Not limited” refers to a limitation that was not considered when selecting the compositions.

Limitations for glass compositions shown in FIGS. 4 and 5
Component	Unit	Min	Max
TiO2	mol.%	12	35
ZrO2	mol.%	2.5	20
B2O3	mol.%	0.5	40
Nb2O5	mol.%	0.5	30
Bi2O3	mol.%	0	20
P2O5	mol.%	0	15
Al2O3	mol.%	0	10
Gd2O3	mol.%	0	10
WO3	mol.%	0	8
PbO	mol.%	0	5
V2O5	mol.%	0	5
ZnO	mol.%	0	1.5
RmOn	mol.%	95	Not limited
REmOn	mol.%	0.5	35
SiO2 + B2O3 + P2O5	mol.%	10	Not limited
TiO2 + Nb2O5	mol.%	0	42
GeO2 + TeO2	mol.%	0	Not limited
SiO2 + B2O3 - P2O5	mol.%	0	Not limited

The Comparative Glasses of FIG. 4 were selected as having the highest value of the parameter P_n over the range of values of the parameter P_d shown in FIG. 4 among the known glasses that have the features specified in Table 8.

The line corresponding to the formula y = 1.765 + 0.057 * x shown in FIG. 4 provides a visual representation of the differences between the Comparative Glasses having the features specified in Table 8 and the Exemplary Glasses 1 to 4, 7, 8, 13 to 16, 27 to 34 and 51 to 66. As can be seen in FIG. 4, the mentioned Exemplary Glasses (filled circles) and none of the Comparative Glasses (open circles) represented in FIG. 4 fall above the line y = 1.765 + 0.057 * x, where y corresponds to the parameter P_n that predicts refractive index at 587.56 nm and x corresponds to the parameter P_d that that predicts density at room temperature. In other words, some of the Exemplary Glasses and none of the Comparative Glasses represented in FIG. 4 satisfy the following formula (III):

$\begin{array}{cc}{\text{P}}_{\text{n}}-\left(1.765+0.057*{\text{P}}_{\text{d}}\right)>0.00& \text{­­­(III)}\end{array}$

The Exemplary Examples represented in FIG. 4 are, by prediction, superior in terms of the combination of P_d and P_n to the best known Comparative Glasses that have the features specified in Table 8.

FIG. 5 is a plot showing the relationship between the density at room temperature d_RT and the refractive index at 587.56 nm n_d for some of the Exemplary Glasses and some of the Comparative Glasses. The Exemplary Glass (filled circle) is Example 2 from Table 6. The Comparative Glasses (open circles) are the Examples C10 to C19 from Table 7. All of the Exemplary Glasses and Comparative Glasses shown in FIG. 5 have the features specified in Table 8.

The Comparative Glasses of FIG. 5 were selected as having the highest measured values of the refractive index at 587.56 nm n_d over the range of measured density at room temperature d_RT shown in FIG. 5 among the known glasses that have the mentioned features specified in Table 8.

The line corresponding to the formula y = 1.765 + 0.057 * x shown in FIG. 5 provides a visual representation of the differences between the Comparative Glasses having the features specified in Table 8 and the Exemplary Glass 2. As can be seen in FIG. 5, the mentioned Exemplary Glass (filled circles) and none of the Comparative Glasses (open circles) represented in FIG. 5 fall above the line y = 1.765 + 0.057 * x, where y corresponds to n_d and x corresponds to d_RT. In other words, some of the Exemplary Glasses and none of the Comparative Glasses represented in FIG. 5 satisfy the following formula (IV):

$\begin{array}{cc}{\text{n}}_{\text{d}}-\left(1.765+0.057*{\text{d}}_{\text{RT}}\right)>0.00& \text{­­­(IV)}\end{array}$

This means that, under the conditions specified in Table 8 above, some of the Exemplary Glasses have higher measured values of the refractive index at 587.56 nm n_d at comparable measured values of the density at room temperature d_RT than the best of the Comparative Glasses satisfying the same conditions. This can be interpreted as these Exemplary Glasses, according to measurements, have higher values of n_d at comparable values of d_RT among the glasses, i.e. they are, according to measurement, superior in terms of a combination of d_RT and n_d (i.e. lower d_RT for a given n_d or higher n_d for a given d_RT) to the best known Comparative Glasses that have the features specified in Table 8.

The values of all attributes specified in Table 8 and Formulas (III) and (IV) for the Comparative Glasses C1 to C19 plotted in FIGS. 4 and 5 are presented in Table 9 below. Full compositions of the Comparative Glasses are presented in Table 7. Full compositions and attributes of the Exemplary Glasses are presented in Table 6.

Attributes of Comparative Example Glasses Having the Features Specified in Table 8
Ex. #	C1	C2	C3	C4	C5	C6	C7	C8
Composition
Ex. #	C1	C2	C3	C4	C5	C6	C7	C8
TiO2	mol.%	26.46	22.68	31.38	12.99	31.92	31.75	31.04	30.85
ZrO2	mol.%	6.99	12.50	8.31	6.99	9.03	9.19	8.30	8.25
B2O3	mol.%	19.96	13.01	14.22	34.98	18.28	18.28	14.80	14.71
REmOn	mol.%	14.06	34.99	28.23	19.99	27.65	27.65	27.66	27.50
Nb2O5	mol.%	11.98	4.70	5.59	17.99	5.55	5.55	5.67	5.64
Bi2O3	mol.%	0	0	0	0	0	0	0	0
P2O5	mol.%	0	0	0	0	0	0	0	0
Al2O3	mol.%	0.0157	2.67	0	0	0	0	0	0
Gd2O3	mol.%	0	3.80	0	0	4.97	4.93	0	0
WO3	mol.%	0	0	0.50	7.00	0	0	0.50	0.49
PbO	mol.%	0.0018	0	0	0	0	0	0	0
V2O5	mol.%	0	0	0	0	0	0	0	0
ZnO	mol.%	0.0033	0	0	0	0	0	0	0
SiO2 + B2O3 + P2O5	mol.%	35.44	20.55	25.46	35.04	25.85	25.85	26.32	26.16
TiO2 + Nb2O5	mol.%	38.44	27.39	36.98	30.97	37.47	37.30	36.71	36.49
GeO2 + TeO2	mol.%	0	0	0	0	0	0	0	0
SiO2 + B2O3 - P2O5	mol.%	35.44	20.55	25.46	35.04	25.85	25.85	26.32	26.16
dRT	g/cm3
nd
nd - (1.765 + 0.057 * dRT)
Pd	g/cm3	4.3217	5.7151	5.1648	4.7926	5.3379	5.341	5.1158	5.1133
Pn		1.9749	2.0829	2.0576	2.0329	2.0644	2.0643	2.0505	2.0492
Pn - (1.765 + 0.057 * Pd)		-0.0364	-0.0078	-0.0018	-0.0053	-0.0049	-0.0051	-0.0061	-0.0072

Ex. #	C9	C10	C11	C12	C13	C14	C15	C16
Composition
TiO2	mol.%	33.63	34.38	20.66	27.08	31.33	34.46	34.37	34.01
ZrO2	mol.%	5.56	7.02	5.71	9.14	8.30	6.47	7.04	8.17
B2O3	mol.%	11.96	12.94	2.74	15.37	13.09	13.53	12.93	12.94
REmOn	mol.%	14.16	25.95	0.73	27.52	28.18	19.12	25.92	12.85
Nb2O5	mol.%	8.09	4.43	9.50	5.52	5.58	5.45	4.43	5.09
Bi2O3	mol.%	0	0	0	0	0	0	0	0
P2O5	mol.%	0	0	0	0	0	0	0	0
Al2O3	mol.%	0	0	0.26	0	0	0	0	0
Gd2O3	mol.%	0.74	3.11	0	4.90	0	0	3.07	0.55
WO3	mol.%	0	0	0	0	0.50	0	0	0.40
PbO	mol.%	0	0	0	0	0	0	0	0
V2O5	mol.%	0	0	0	0	0	0	0	0
ZnO	mol.%	0.83	0	0	1.50	0	0	0	1.14
SiO2 + B2O3 + P2O5	mol.%	23.14	28.22	30.96	26.99	25.59	23.17	28.24	23.75
TiO2 + Nb2O5	mol.%	41.72	38.81	30.16	32.60	36.91	39.91	38.80	39.09
GeO2 + TeO2	mol.%	0	0	0	0	0	0	0	0
SiO2 + B2O3 - P2O5	mol.%	23.14	28.22	30.96	26.99	25.59	23.17	28.24	23.75
Measured properties
dRT	g/cm3		5.140	3.710	5.420	5.100	4.950	5.140	4.720
nd			2.048	1.9395	2.0451	2.051	2.040	2.048	2.016
nd - (1.765 + 0.057 * dRT)			-0.010	-0.037	-0.0288	-0.0047	-0.0072	-0.010	-0.018
Predicted and calculated properties
Pd	g/cm3	4.7605	5.1432	3.7917	5.3639	5.1658	5.0348	5.1416	4.8093
Pn		2.0201	2.0405	1.8806	2.0472	2.0573	2.0326	2.0402	2.0011
Pn - (1.765 + 0.057 * Pd)		-0.0163	-0.0177	-0.1005	-0.0236	-0.0022	-0.0194	-0.0179	-0.0380

Ex. #	C17	C18	C19
Composition
TiO2	mol.%	33.73	26.08	26.08
ZrO2	mol.%	6.99	5.74	5.74
B2O3	mol.%	17.00	2.71	2.71
REmOn	mol.%	14.29	0.72	0.72
Nb2O5	mol.%	3.00	8.36	8.36
Bi2O3	mol.%	0	0	0
P2O5	mol.%	0	0	0
Al2O3	mol.%	0	0	0
Gd2O3	mol.%	0	0	0
WO3	mol.%	0	0	0
PbO	mol.%	0	0	0
V2O5	mol.%	0	0	0
ZnO	mol.%	0	0	0
SiO2 + B2O3 + P2O5	mol.%	26.98	23.76	23.76
TiO2 + Nb2O5	mol.%	36.74	34.45	34.45
GeO2 + TeO2	mol.%	0	0	0
SiO2 + B2O3 - P2O5	mol.%	26.98	23.76	23.76
Measured properties
dRT	g/cm3	4.471	4.167	4.167
nd		2.000	1.9729	1.9729
nd - (1.765 + 0.057 * dRT)		-0.0198	-0.0297	-0.0297
Predicted and calculated properties
Pd	g/cm3	4.5071	4.1835	4.1835
Pn		1.9597	1.9281	1.9281
Pn - (1.765 + 0.057 * Pd)		-0.0622	-0.0754	-0.0754

As follows from FIGS. 4 and 5, both predicted and measured property data confirms that some of the Exemplary Glasses have a better combination of density at room temperature d_RT and refractive index at 587.56 nm n_d than the best of the Comparative Glasses that have the features specified in Table 8.

TiO₂ provides high refractive index at a lower density than Nb₂O₅, WO₃ and Bi₂O₃, but may adversely decrease the blue transmittance of glass. That is why in some embodiments of the present disclosure it is desirable to reach high refractive indexes, adding lower amount of TiO₂ comparing to other high index components. Accordingly, reaching higher refractive indexes at comparable values of the molar ratio TiO₂/(TiO₂+Nb₂O₅+WO₃+Bi₂O₃) indirectly indicates a potential advantage in terms of blue transmittance in combination with high refractive index and low density.

FIG. 6 is a plot showing the relationship between the ratio TiO₂/ (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃) and the predictive parameter P_n for some of the Exemplary Glasses and some of the Comparative Glasses. The Exemplary Glasses (filled circles) are the Examples 1 to 6, 8 to 19, 23, 25, 27 to 34 and 51 to 67 from Table 6. The Comparative Glasses (open circles) are the Examples C3, C7, C8 and C20 to C26 from Table 7. The parameter P_n that predicts refractive index at 587.56 nm was determined according to Formula (I). All of the Exemplary Glasses and Comparative Glasses shown in FIG. 6 have the features specified in Table 10. In Table 10, the specification “Not limited” refers to a limitation that was not considered when selecting the compositions.

Limitations for glass compositions shown in FIGS. 6 and 7
Component	Unit	Min	Max
ZrO2	mol.%	1	13.5
TiO2	mol.%	0.3	35
B2O3	mol.%	0.3	29.5
WO3	mol.%	0	9
PbO	mol.%	0	5
Gd2O3	mol.%	0	2
F	at.%	0	2
TiO2 + Nb2O5 + La2O3	mol.%	10	70
SiO2 + B2O3 + P2O5	mol.%	10	Not limited
REmOn + WO3 + ZrO2	mol.%	5	Not limited
SiO2 + Y2O3 + Gd2O3	mol.%	0.3	Not limited
V2O5 + MoO3	mol.%	0	3
WO3 + Bi2O3	mol.%	0	Not limited
SiO2 + B2O3 - P2O5	mol.%	1	Not limited
La2O3 / TiO2	mol.%	Not limited	1.5
TiO2/ (TiO2 + Nb2O5 + WO3 + Bi2O3)	mol.%	0	Not limited

The Comparative Glasses shown in FIG. 6 were selected as having the highest value of the parameter P_n that predicts refractive index at 587.56 nm over the range of the ratio TiO₂/ (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃) shown in FIG. 6 among the known glasses that have the features specified in Table 10.

The line corresponding to the formula y = 1.99 + 0.083 * x shown in FIG. 6 provides a visual representation of the differences between the Comparative Glasses having the features specified in Table 10 and the Exemplary Glasses 1 to 6, 8 to 19, 23, 25, 27 to 34 and 51 to 67. As can be seen in FIG. 6, the mentioned Exemplary Glasses (filled circles) and none of the Comparative Glasses (open circles) represented in FIG. 6 fall above the line y = 1.99 + 0.083 * x, where y corresponds to the parameter P_n that predicts refractive index at 587.56 nm and x corresponds to the ratio TiO₂ / (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃). In other words, some of the Exemplary Glasses and none of the Comparative Glasses represented in FIG. 6 satisfy the following formula (V)(a):

As can also be seen in FIG. 6, some of Exemplary Glasses and none of the Comparative Glasses represented in FIG. 6 fall above the line y = 2.005 + 0.083 * x, where y corresponds to the parameter P_n that predicts refractive index at 587.56 nm and x corresponds to the ratio TiO₂ / (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃). In other words, some of the Exemplary Glasses and none of the Comparative Glasses represented in FIG. 6 satisfy the following formula (V)(b):

The Exemplary Examples represented in FIG. 6 are, by prediction, superior in terms of the combination of the ratio TiO₂ / (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃) and the predictive parameter P_n (i.e. lower ratio for a given P_n or higher P_n for a given ratio) to the best known Comparative Glasses that have the features specified in Table 10.

FIG. 7 is a plot showing the relationship between the ratio TiO₂/ (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃) and the measured refractive index at 587.56 nm n_d for some of the Exemplary Glasses and some of the Comparative Glasses. The Exemplary Glasses (filled circles) are the Examples 2, 3, 13, 14, 23, 65 and 66 from Table 6. The Comparative Glasses (open circles) are the Examples C7, C8, C13, C20 and C27 to C32 from Table 7. All of the Exemplary Glasses and Comparative Glasses shown in FIG. 7 have the features specified in Table 10. In Table 10, the specification “Not limited”, if appears, refers to a limitation that was not considered when selecting the compositions.

The Comparative Glasses of FIG. 7 were selected as having the highest measured values of the refractive index at 587.56 nm n_d over the range of values of the ratio TiO₂/ (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃) shown in FIG. 7 among the known glasses that have the mentioned features specified in Table 10.

The line corresponding to the formula y = 1.99 + 0.083 * x shown in FIG. 7 provides a visual representation of the differences between the Comparative Glasses having the features specified in Table 10 and the Exemplary Glasses 2, 3, 13, 14, 23, 65 and 66. As can be seen in FIG. 7, the mentioned Exemplary Glasses (filled circles) and none of the Comparative Glasses (open circles) represented in FIG. 7 fall above the line y = 1.99 + 0.083 * x, where y corresponds to n_d and x corresponds to the ratio TiO₂ / (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃). In other words, some of the Exemplary Glasses and none of the Comparative Glasses represented in FIG. 7 satisfy the following formula (VI)(a):

As can also be seen in FIG. 7, some of Exemplary Glasses and none of the Comparative Glasses represented in FIG. 7 fall above the line y = 2.005 + 0.083 * x, where y corresponds to n_d and x corresponds to the ratio TiO₂ / (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃). In other words, some of the Exemplary Glasses and none of the Comparative Glasses represented in FIG. 7 satisfy the following formula (VI)(b):

The Exemplary Examples represented in FIG. 7 that satisfy the formula (VI)(b) are characterized by the highest values of n_d at comparable values of the ratio TiO₂/ (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃) among the glasses that have the features specified in Table 10.

This means that, under the conditions specified in Table 10 above, some of the Exemplary Glasses have higher measured values of the refractive index at 587.56 nm n_d at comparable measured values of the ratio TiO₂ / (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃) than the best of the Comparative Glasses satisfying the same conditions. This can be interpreted as these Exemplary Glasses, according to measurements, have higher values of n_d at comparable values of TiO₂ / (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃) among the glasses, i.e. they are, according to measurement, superior in terms of a combination of TiO₂ / (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃) and n_d to the best known Comparative Glasses that have the features specified in Table 10.

The values of all attributes specified in Table 10 and Formulas (V)(a), (V)(b), (VI)(a) and (VI)(b) for the Comparative Glasses C3, C7, C8, C13 and C20 to C32 plotted in FIGS. 6 and 7 are presented in Table 11 below. Full compositions of comparative example glasses are presented in Table 7. Full compositions and attributes of the Exemplary Glasses are presented in Table 6.

Attributes of Comparative Example Glasses Having the Features Specified in Table 10
Ex. #	C3	C7	C8	C13	C20	C21	C22	C23
Composition
TiO2	mol.%	31.38	31.04	30.85	31.33	16.45	23.53	16.97	31.95
B2O3	mol.%	14.22	14.80	14.71	13.09	22.96	17.65	28.51	22.86
WO3	mol.%	0.50	0.50	0.49	0.50	0	0	3.44	0
PbO	mol.%	0	0	0	0	0	0	0	0
Gd2O3	mol.%	0	0	0	0	0	0	0	0.96
F	mol.%	0	0	0	0	0	0	0	0
TiO2 + Nb2O5 + La2O3	mol.%	60.29	59.41	59.06	60.18	49.51	23.53	45.82	64.94
SiO2 + B2O3 + P2O5	mol.%	25.46	26.32	26.16	25.59	27.44	23.53	37.43	24.53
REmOn + WO3 + ZrO2	mol.%	37.04	36.46	36.24	36.98	20.98	35.29	32.36	26.52
SiO2 + Y2O3 + Gd2O3	mol.%	16.15	16.48	16.38	17.41	4.48	5.88	8.92	3.19
V2O5 + MoO3	mol.%	0	0	0	0	0	0	0	0
WO3 + Bi2O3	mol.%	0.50	0.50	0.49	0.50	0	0	9.45	0
TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)	mol.%	0.8373	0.8342	0.8342	0.8373	0.4688	1.000	0.5050	0.7692
SiO2 + B2O3 - P2O5	mol.%	25.46	26.32	26.16	25.59	27.44	23.53	37.43	24.53
La2O3 / TiO2	mol.%	0.7429	0.7316	0.7316	0.7430	0.8773	0	1.277	0.7329
Measured properties
nd			2.050	2.050	2.051	2.000
nd - (1.99 + 0.083 * TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3))			-0.0092	-0.0092	-0.0085	-0.0289
nd - (2.005 + 0.083 * TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3))			-0.0242	-0.0242	-0.0235	-0.0439
Predicted and calculated properties
Pn		2.0576	2.0505	2.0492	2.0573	1.9959	2.0376	2.0298	2.0497
Pn - (1.99 + 0.083 * TiO2/ (TiO2 + Nb2O5 + WO3 + Bi2O3))		-0.0019	-0.0088	-0.0100	-0.0022	-0.0330	-0.0354	-0.0022	-0.0041
Pn - (2.005 + 0.083 * TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3))		-0.0169	-0.0238	-0.0250	-0.0172	-0.0480	-0.0504	-0.0172	-0.0191

Ex. #	C24	C25	C26	C27	C28	C29	C30	C31	C32
Composition
TiO2	mol.%	33.06	33.23	33.04	22.93	34.09	34.10	34.28	17.51	34.76
B2O3	mol.%	13.44	13.45	13.45	19.13	13.87	13.87	13.87	7.26	15.95
WO3	mol.%	0	0	0	0	0	0	0	0	0
PbO	mol.%	0	0	0	0	0	0	0	0	0
Gd2O3	mol.%	0	0	0	1.87	0	0	0	0	1.92
F	mol.%	0	0	0	0	0	0	0	0	0
TiO2 + Nb2O5 + La2O3	mol.%	59.12	59.28	59.11	53.15	60.96	60.96	61.15	38.64	56.18
SiO2 + B2O3 + P2O5	mol.%	27.02	27.02	27.03	27.59	27.87	27.88	27.87	10.06	29.82
REmOn + WO3 + ZrO2	mol.%	32.35	32.17	32.34	42.91	30.25	30.22	30.05	24.56	30.20
SiO2 + Y2O3 + Gd2O3	mol.%	13.57	13.57	13.57	11.37	14.37	14.38	14.37	2.80	18.85
V2O5 + MoO3	mol.%	0	0	0	0	0	0	0	0	0
WO3 + Bi2O3	mol.%	0	0	0	0	0	0	0	0	0
TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3)	mol.%	0.8670	0.8676	0.8669	0.9344	0.8671	0.8672	0.8677	0.6636	0.8694
SiO2 + B2O3 - P2O5	mol.%	27.02	27.02	27.03	27.59	27.87	27.88	27.87	10.06	29.82
La2O3 / TiO2	mol.%	0.6348	0.6314	0.6351	1.247	0.6350	0.6347	0.6314	0.7001	0.4658
Measured properties
nd					2.0359	2.054	2.054	2.054	2.028	2.0425
nd - (1.99 + 0.083 * TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3))					-0.0317	-0.008	-0.008	-0.008	-0.0171	-0.0197
nd - (2.005 + 0.083 * TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3))					-0.0467	-0.023	-0.023	-0.023	-0.0321	-0.0347
Predicted and calculated properties
Pn		2.052	2.052	2.052	2.0245	2.0261	2.0259	2.026	1.9704	2.0155
Pn - (1.99 + 0.083 * TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3))		-0.0099	-0.0100	-0.0100	-0.0431	-0.0359	-0.0361	-0.0360	-0.0746	-0.0467
Pn - (2.005 + 0.083 * TiO2 / (TiO2 + Nb2O5 + WO3 + Bi2O3))		-0.0249	-0.0250	-0.0250	-0.0581	-0.0509	-0.0511	-0.0510	-0.0896	-0.0617

As follows from FIGS. 6 and 7, both predicted and measured property data confirms that some of the Exemplary Glasses have better combination of refractive index at 587.56 nm n_d and the ratio TiO₂ / (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃) than the best of the Comparative Glasses that have the features specified in Table 10.

The following non-limiting aspects are encompassed by the present disclosure. To the extent not already described, any one of the features of the first through the sixty-eighth aspect may be combined in part or in whole with features of any one or more of the other aspects of the present disclosure to form additional aspects, even if such a combination is not explicitly described.

According to a first aspect, the glass comprises a plurality of components, the glass having a composition of the components comprising greater than or equal to 12.0 mol.% and less than or equal to 35.0 mol.% TiO₂, greater than or equal to 2.5 mol.% and less than or equal to 20.0 mol.% ZrO₂, greater than or equal to 0.5 mol.% and less than or equal to 40.0 mol.% B₂O₃, greater than or equal to 0.5 mol.% and less than or equal to 30.0 mol.% Nb₂O₅, greater than or equal to 0.0 mol.% and less than or equal to 20.0 mol.% Bi₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 15.0 mol.% P₂O₅, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% Al₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% Gd₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 8.0 mol.% WO₃, greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.% PbO, greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.% V₂O₅, greater than or equal to 0.0 mol.% and less than or equal to 1.5 mol.% ZnO, greater than or equal to 95.0 mol.% R_mO_n, greater than or equal to 0.5 mol.% and less than or equal to 35.0 mol.% RE_mO_n, a sum of SiO₂ + B₂O₃ + P₂O₅ greater than or equal to 10.0 mol.% and a sum of TiO₂ + Nb₂O₅ greater than or equal to 0.0 mol.% and less than or equal to 42.0 mol.%, wherein the composition of the components satisfies the condition: SiO₂ + B₂O₃ - P₂O₅ [mol.%] ≥ 0.000, and the glass satisfies the condition: P_n - (1.765 + 0.057 * P_d) > 0.000, where P_n is a parameter predicting a refractive index at 587.56 nm, n_d, calculated from the glass composition in terms of mol.% of the components according to the Formula (I):

and P_d is a parameter predicting a density at room temperature, d_RT, calculated from the glass composition in terms of mol.% of the components according to the Formula (II):

where R_mO_n is a total sum of all oxides, RE_mO_n is a total sum of rare earth metal oxides, and an asterisk (*) means multiplication.

According to a second aspect, the glass of the first aspect, wherein the glass satisfies the condition: n_d - (1.765 + 0.057 * d_RT) > 0.000, where n_d is a refractive index at 587.56 nm and d_RT [g/cm³] is a density at room temperature.

According to a third aspect, the glass of any one of aspects 1-2, wherein the composition of the components comprises greater than or equal to 20.0 mol.% and less than or equal to 27.5 mol.% TiO₂, greater than or equal to 15.0 mol.% and less than or equal to 30.0 mol.% La₂O₃, greater than or equal to 15.0 mol.% and less than or equal to 22.5 mol.% B₂O₃, greater than or equal to 5.0 mol.% and less than or equal to 20.0 mol.% SiO₂, greater than or equal to 4.0 mol.% and less than or equal to 9.0 mol.% ZrO₂, greater than or equal to 2.5 mol.% and less than or equal to 10.0 mol.% Nb₂O₅, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% BaO, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% CaO, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% Ga₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% Y₂O₃ and greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% WO₃.

According to a fourth aspect, the glass of any one of aspects 1-3, wherein the composition of the components comprises one or more of the following components: greater than or equal to 20.25 mol.% and less than or equal to 26.00 mol.% TiO₂, greater than or equal to 20.0 mol.% and less than or equal to 27.5 mol.% La₂O₃, greater than or equal to 16.4 mol.% and less than or equal to 20.4 mol.% B₂O₃, greater than or equal to 10.0 mol.% and less than or equal to 17.5 mol.% SiO₂, greater than or equal to 5.3 mol.% and less than or equal to 8.1 mol.% ZrO₂, greater than or equal to 4.5 mol.% and less than or equal to 9.3 mol.% Nb₂O₅, greater than or equal to 0.5 mol.% and less than or equal to 6.3 mol.% Y₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 9.0 mol.% CaO, greater than or equal to 0.0 mol.% and less than or equal to 8.0 mol.% Ga₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 6.5 mol.% BaO, greater than or equal to 0.0 mol.% and less than or equal to 1.8 mol.% WO₃, greater than or equal to 0 mol.% and less than or equal to 1.35 mol.% Gd₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 0.9 mol.% SrO and greater than or equal to 0.0 mol.% and less than or equal to 0.9 mol.% Yb₂O₃.

According to a fifth aspect, the glass of any one of aspects 1-4, wherein the composition of the components comprises greater than or equal to 21.0 mol.% and less than or equal to 26.3 mol.% La₂O₃, greater than or equal to 20.25 mol.% and less than or equal to 25.50 mol.% TiO₂, greater than or equal to 16.9 mol.% and less than or equal to 20.4 mol.% B₂O₃, greater than or equal to 11.0 mol.% and less than or equal to 16.5 mol.% SiO₂, greater than or equal to 5.6 mol.% and less than or equal to 8.0 mol.% ZrO₂, greater than or equal to 5.1 mol.% and less than or equal to 8.6 mol.% Nb₂O₅, greater than or equal to 0.75 mol.% and less than or equal to 5.50 mol.% Y₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 8.0 mol.% CaO, greater than or equal to 0.0 mol.% and less than or equal to 7.5 mol.% Ga₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 5.5 mol.% BaO, greater than or equal to 0.0 mol.% and less than or equal to 1.6 mol.% WO₃, greater than or equal to 0.0 mol.% and less than or equal to 1.2 mol.% Gd₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 0.8 mol.% SrO and greater than or equal to 0.0 mol.% and less than or equal to 0.8 mol.% Yb₂O₃.

According to a sixth aspect, the glass of any one of aspects 1-5, wherein the composition of the components satisfy one or more of the following conditions: a sum of La₂O₃ + TiO₂ + B₂O₃ + SiO₂ + ZrO₂ + Nb₂O₅ + BaO + Y₂O₃ + CaO + Ga₂O₃ + Gd₂O₃ + ZnO + WO₃ + CeO₂ + SrO + Na₂O + Ta₂O₅ + Al₂O₃ greater than or equal to 99.0 mol.%, a sum of La₂O₃ + Y₂O₃ + Gd₂O₃ + TiO₂ + B₂O₃ + SiO₂ + ZrO₂ + Nb₂O₅ greater than or equal to 99.0 mol.%, a sum of La₂O₃ + Y₂O₃ + Gd₂O₃ + TiO₂ + B₂O₃ + SiO₂ + ZrO₂ + Nb₂O₅ + CaO + BaO greater than or equal to 99.0 mol.% and a sum of La₂O₃ + TiO₂ + B₂O₃ + SiO₂ + ZrO₂ + Nb₂O₅ greater than or equal to 97.0 mol.%.

According to a seventh aspect, the glass of any one of aspects 1-6, wherein the composition of the components comprises greater than or equal to 5.0 mol.% B₂O₃, greater than or equal to 5.0 mol.% La₂O₃, greater than or equal to 5.0 mol.% Nb₂O₅, greater than or equal to 5.0 mol.% SiO₂ and a sum of ZrO₂ + HfO₂ greater than or equal to 1.0 mol.%.

According to an eighth aspect, the glass of any one of aspects 1-7, wherein the composition of the components comprises a sum of R₂O + RO greater than or equal to 0.0 mol.% and less than or equal to 6.0 mol.%, where R₂O is a total sum of monovalent metal oxides, and RO is a total sum of divalent metal oxides.

According to a ninth aspect, the glass of the eighth aspect, wherein the composition of the components comprises a sum of R₂O + RO greater than or equal to 0.0 mol.% and less than or equal to 1.0 mol.%, where R₂O is a total sum of monovalent metal oxides, and RO is a total sum of divalent metal oxides.

According to a tenth aspect, the glass of any one of aspects 1-9, wherein the composition of the components satisfies the condition: 0.00 ≤ SiO₂ / (SiO₂ + B₂O₃) [mol.%] ≤ 0.40.

According to an eleventh aspect, the glass of any one of aspects 1-9, wherein the composition of the components satisfies the condition: 0.38 ≤ SiO₂ / (SiO₂ + B₂O₃) [mol.%] ≤ 0.75.

According to a twelfth aspect, the glass of any one of aspects 1-11, wherein the composition of the components comprises greater than or equal to 0.0 mol.% and less than or equal to 6.5 mol.% CaO and greater than or equal to 0.0 mol.% and less than or equal to 5.5 mol.% BaO and wherein the composition of the components is substantially free of ZnO.

According to a thirteenth aspect, the glass of any one of aspects 1-12, wherein the composition of the components comprises a sum of WO₃ + Bi₂O₃ greater than or equal to 0.0 mol.% and less than or equal to 7.0 mol.%.

According to a fourteenth aspect, the glass of any one of aspects 1-13, wherein the composition of the components comprises greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.% Y₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% Ta₂O₅, greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% TeO₂, greater than or equal to 0.0 mol.% and less than or equal to 0.5 mol.% GeO₂, greater than or equal to 0.0 mol.% and less than or equal to 0.5 mol.% PbO, greater than or equal to 0.0 mol.% and less than or equal to 0.2 mol.% As₂O₃ and greater than or equal to 0.0 mol.% and less than or equal to 0.2 mol.% Sb₂O₃, wherein the composition of the components is substantially free of fluorine and substantially free of V₂O₅.

According to a fifteenth aspect, the glass of any one of aspects 1-3 and 6-14, wherein the composition of the components comprises greater than or equal to 22.0 mol.% and less than or equal to 25.0 mol.% TiO₂, greater than or equal to 20.0 mol.% and less than or equal to 30.0 mol.% La₂O₃, greater than or equal to 16.0 mol.% and less than or equal to 20.0 mol.% B₂O₃, greater than or equal to 10.0 mol.% and less than or equal to 20.0 mol.% SiO₂, greater than or equal to 6.5 mol.% and less than or equal to 8.0 mol.% ZrO₂, greater than or equal to 5.0 mol.% and less than or equal to 6.7 mol.% Nb₂O₅, greater than or equal to 0.0 mol.% and less than or equal to 6.0 mol.% Y₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 3.0 mol.% BaO and greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% Gd₂O₃ and greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% of all other components in total.

According to a sixteenth aspect, the glass of any one of aspects 1-15, wherein the glass satisfies the conditions: 4.5 ≤ P_d ≤ 5.5 and 1.95 ≤ P_n ≤ 2.07.

According to a seventeenth aspect, the glass of any one of aspects 1-16, wherein the glass has a density at room temperature, d_RT, that is greater than or equal to 4.5 g/cm³ and less than or equal to 5.5 g/cm³ and a refractive index at 587.56 nm, n_d, that is greater than or equal to 1.95 and less than or equal to 2.07.

According to an eighteenth aspect, the glass of any one of aspects 1-17, wherein the glass has a liquidus temperature, T_liq, that is less than or equal to 1260° C.

According to a nineteenth aspect, the glass of any one of aspects 1-18, wherein when cooled in air from 1100° C. to 500° C. in 2.5 minutes, the glass does not crystallize.

According to a twentieth aspect, the glass of any one of aspects 1-19, wherein the glass has a transmittance at a wavelength of 460 nm, TX_460nm, that is greater than or equal to 70%.

According to a twenty-first aspect, a method for manufacturing an optical element, the method comprising processing a glass, wherein the glass is the glass of any one of aspects 1-20.

According to a twenty-second aspect, an optical element comprising a glass, wherein the glass is the glass of any one of aspects 1-21.

According to a twenty-third aspect, the glass comprises a plurality of components, the glass having a composition of the components comprising greater than or equal to 1.0 mol.% and less than or equal to 13.5 mol.% ZrO₂, greater than or equal to 0.3 mol.% and less than or equal to 35.0 mol.% TiO₂, greater than or equal to 0.3 mol.% and less than or equal to 29.5 mol.% B₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 9.0 mol.% WO₃, greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.% PbO, greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% Gd₂O₃, greater than or equal to 0.0 at.% and less than or equal to 2.0 at.% F, a sum of TiO₂ + Nb₂O₅ + La₂O₃ greater than or equal to 10.0 mol.% and less than or equal to 70.0 mol.%, a sum of SiO₂ + B₂O₃ + P₂O₅ greater than or equal to 10.0 mol.%, a sum of RE_mO_n + WO₃ + ZrO₂ greater than or equal to 5.0 mol.%, a sum of SiO₂ + Y₂O₃ + Gd₂O₃ greater than or equal to 0.3 mol.%, a sum of V₂O₅ + MoO₃ greater than or equal to 0.0 mol.% and less than or equal to 3.0 mol.% and may optionally contain one or more components selected from Bi₂O₃, CaO, BaO, ZnO, Na₂O, Al₂O₃, Li₂O, GeO₂, TeO₂, K₂O, SrO and MgO, wherein the composition of the components satisfies the conditions: TiO₂/ (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃) [mol.%] ≥ 0.050, SiO₂ + B₂O₃ - P₂O₅ [mol.%] ≥ 1.0 and La₂O₃ / TiO₂ [mol.%] ≤ 1.5, and the glass satisfies the condition: P_n - (1.99 + 0.083 * (TiO₂ / (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃))) > 0.000, where P_n is a parameter predicting a refractive index at 587.56 nm, n_d, calculated from the glass composition in terms of mol.% of the components according to the Formula (I):

where RE_mO_n is a total sum of rare earth metal oxides, and an asterisk (*) means multiplication.

According to a twenty-fourth aspect, the glass of the twenty-third aspect, wherein the glass satisfies the condition: n_d - (1.99 + 0.083 * (TiO₂ / (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃))) > 0.000, where n_d is a refractive index at 587.56 nm.

According to a twenty-fifth aspect, the glass of any one of aspects 23-24, wherein the glass satisfies the condition: n_d - (2.005 + 0.083 * (TiO₂ / (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃))) > 0.000, where n_d is a refractive index at 587.56 nm.

According to a twenty-sixth aspect, the glass of any one of aspects 23-25, wherein the glass satisfies the condition: P_n - (2.005 + 0.083 * (TiO₂ / (TiO₂ + Nb₂O₅ + WO₃ + Bi₂O₃))) > 0.000.

According to a twenty-seventh aspect, the glass of any one of aspects 23-26, wherein the composition of the components comprises greater than or equal to 20.0 mol.% and less than or equal to 27.5 mol.% TiO₂, greater than or equal to 15.0 mol.% and less than or equal to 30.0 mol.% La₂O₃, greater than or equal to 15.0 mol.% and less than or equal to 22.5 mol.% B₂O₃, greater than or equal to 5.0 mol.% and less than or equal to 20.0 mol.% SiO₂, greater than or equal to 4.0 mol.% and less than or equal to 9.0 mol.% ZrO₂, greater than or equal to 2.5 mol.% and less than or equal to 10.0 mol.% Nb₂O₅, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% BaO, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% CaO, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% Ga₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% Y₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 4.0 mol.% ZnO and greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% WO₃.

According to a twenty-eighth aspect, the glass of any one of aspects 23-27, wherein the composition of the components comprises one or more of the following components: greater than or equal to 20.25 mol.% and less than or equal to 26.00 mol.% TiO₂, greater than or equal to 20.0 mol.% and less than or equal to 27.5 mol.% La₂O₃, greater than or equal to 16.4 mol.% and less than or equal to 20.4 mol.% B₂O₃, greater than or equal to 10.0 mol.% and less than or equal to 17.5 mol.% SiO₂, greater than or equal to 5.3 mol.% and less than or equal to 8.1 mol.% ZrO₂, greater than or equal to 4.5 mol.% and less than or equal to 9.3 mol.% Nb₂O₅, greater than or equal to 0.5 mol.% and less than or equal to 6.3 mol.% Y₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 9.0 mol.% CaO, greater than or equal to 0.0 mol.% and less than or equal to 8.0 mol.% Ga₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 6.5 mol.% BaO, greater than or equal to 0.0 mol.% and less than or equal to 3.0 mol.% ZnO, greater than or equal to 0.0 mol.% and less than or equal to 1.8 mol.% WO₃, greater than or equal to 0 mol.% and less than or equal to 1.35 mol.% Gd₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 0.9 mol.% SrO and greater than or equal to 0.0 mol.% and less than or equal to 0.9 mol.% Yb₂O₃.

According to a twenty-ninth aspect, the glass of any one of aspects 23-28, wherein the composition of the components comprises greater than or equal to 21.0 mol.% and less than or equal to 26.3 mol.% La₂O₃, greater than or equal to 20.25 mol.% and less than or equal to 25.50 mol.% TiO₂, greater than or equal to 16.9 mol.% and less than or equal to 20.4 mol.% B₂O₃, greater than or equal to 11.0 mol.% and less than or equal to 16.5 mol.% SiO₂, greater than or equal to 5.6 mol.% and less than or equal to 8.0 mol.% ZrO₂, greater than or equal to 5.1 mol.% and less than or equal to 8.6 mol.% Nb₂O₅, greater than or equal to 0.75 mol.% and less than or equal to 5.50 mol.% Y₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 8.0 mol.% CaO, greater than or equal to 0.0 mol.% and less than or equal to 7.5 mol.% Ga₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 5.5 mol.% BaO, greater than or equal to 0.0 mol.% and less than or equal to 2.7 mol.% ZnO, greater than or equal to 0.0 mol.% and less than or equal to 1.6 mol.% WO₃, greater than or equal to 0.0 mol.% and less than or equal to 1.2 mol.% Gd₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 0.8 mol.% SrO and greater than or equal to 0.0 mol.% and less than or equal to 0.8 mol.% Yb₂O₃.

According to a thirtieth aspect, the glass of any one of aspects 23-29, wherein the composition of the components satisfy one or more of the following conditions: a sum of La₂O₃ + TiO₂ + B₂O₃ + SiO₂ + ZrO₂ + Nb₂O₅ + BaO + Y₂O₃ + CaO + Ga₂O₃ + Gd₂O₃ + ZnO + WO₃ + CeO₂ + SrO + Na₂O + Ta₂O₅ + Al₂O₃ greater than or equal to 99.0 mol.%, a sum of La₂O₃ + Y₂O₃ + Gd₂O₃ + TiO₂ + B₂O₃ + SiO₂ + ZrO₂ + Nb₂O₅ greater than or equal to 99.0 mol.%, a sum of La₂O₃ + Y₂O₃ + Gd₂O₃ + TiO₂ + B₂O₃ + SiO₂ + ZrO₂ + Nb₂O₅ + CaO + BaO greater than or equal to 99.0 mol.% and a sum of La₂O₃ + TiO₂ + B₂O₃ + SiO₂ + ZrO₂ + Nb₂O₅ greater than or equal to 97.0 mol.%.

According to a thirty-first aspect, the glass of any one of aspects 23-26 and 29-30, wherein the composition of the components comprises greater than or equal to 5.0 mol.% B₂O₃, greater than or equal to 5.0 mol.% Nb₂O₅, greater than or equal to 5.0 mol.% SiO₂, greater than or equal to 5.0 mol.% TiO₂ and a sum of ZrO₂ + HfO₂ greater than or equal to 1.0 mol.%.

According to a thirty-second aspect, the glass of any one of aspects 23-31, wherein the composition of the components comprises a sum of R₂O + RO greater than or equal to 0.0 mol.% and less than or equal to 6.0 mol.%, where R₂O is a total sum of monovalent metal oxides, and RO is a total sum of divalent metal oxides.

According to a thirty-third aspect, the glass of the thirty-second aspect, wherein the composition of the components comprises a sum of R₂O + RO greater than or equal to 0.0 mol.% and less than or equal to 1.0 mol.%.

According to a thirty-fourth aspect, the glass of any one of aspects 23-33, wherein the composition of the components satisfies the condition: 0.00 ≤ SiO₂ / (SiO₂ + B₂O₃) [mol.%] ≤ 0.40.

According to a thirty-fifth aspect, the glass of any one of aspects 23-33, wherein the composition of the components satisfies the condition: 0.38 ≤ SiO₂ / (SiO₂ + B₂O₃) [mol.%] ≤ 0.75.

According to a thirty-sixth aspect, the glass of any one of aspects 23-35, wherein the composition of the components comprises greater than or equal to 0.0 mol.% and less than or equal to 6.5 mol.% CaO and greater than or equal to 0.0 mol.% and less than or equal to 5.5 mol.% BaO and wherein the composition of the components is substantially free of ZnO.

According to a thirty-seventh aspect, the glass of any one of aspects 23-36, wherein the composition of the components comprises a sum of WO₃ + Bi₂O₃ greater than or equal to 0.0 mol.% and less than or equal to 7.0 mol.%.

According to a thirty-eighth aspect, the glass of any one of aspects 23-37, wherein the composition of the components comprises greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.% Y₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% Ta₂O₅, greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% TeO₂, greater than or equal to 0.0 mol.% and less than or equal to 0.5 mol.% GeO₂, greater than or equal to 0.0 mol.% and less than or equal to 0.5 mol.% PbO, greater than or equal to 0.0 mol.% and less than or equal to 0.2 mol.% As₂O₃ and greater than or equal to 0.0 mol.% and less than or equal to 0.2 mol.% Sb₂O₃, wherein the composition of the components is substantially free of fluorine and substantially free of V₂O₅.

According to a thirty-ninth aspect, the glass of any one of aspects 23-27 and 30-38, wherein the composition of the components comprises greater than or equal to 22.0 mol.% and less than or equal to 25.0 mol.% TiO₂, greater than or equal to 20.0 mol.% and less than or equal to 30.0 mol.% La₂O₃, greater than or equal to 16.0 mol.% and less than or equal to 20.0 mol.% B₂O₃, greater than or equal to 10.0 mol.% and less than or equal to 20.0 mol.% SiO₂, greater than or equal to 6.5 mol.% and less than or equal to 8.0 mol.% ZrO₂, greater than or equal to 5.0 mol.% and less than or equal to 6.7 mol.% Nb₂O₅, greater than or equal to 0.0 mol.% and less than or equal to 6.0 mol.% Y₂O₃ and greater than or equal to 0.0 mol.% and less than or equal to 3.0 mol.% BaO and greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% of all other components in total.

According to a fortieth aspect, the glass of any one of aspects 23-39, wherein the glass satisfies the conditions: 4.5 ≤ P_d ≤ 5.5 and 1.95 ≤ P_n ≤ 2.07.where P_d is a parameter predicting a density at room temperature, d_RT, calculated from the glass composition in terms of mol.% of the components according to the Formula (II):

According to a forty-first aspect, the glass of any one of aspects 23-40, wherein the glass has a density at room temperature, d_RT, that is greater than or equal to 4.5 g/cm³ and less than or equal to 5.5 g/cm³ and a refractive index at 587.56 nm, n_d, that is greater than or equal to 1.95 and less than or equal to 2.07.

According to a forty-second aspect, the glass of any one of aspects 23-41, wherein the glass has a liquidus temperature, T_liq, that is less than or equal to 1260° C.

According to a forty-third aspect, the glass of any one of aspects 23-42, wherein when cooled in air from 1100° C. to 500° C. in 2.5 minutes, the glass does not crystallize.

According to a forty-fourth aspect, the glass of any one of aspects 23-43, wherein the glass has a transmittance at a wavelength of 460 nm, TX_460nm, that is greater than or equal to 70%.

According to a forty-fifth aspect, a method for manufacturing an optical element, the method comprising processing a glass, wherein the glass is the glass of any one of aspects 23-44.

According to a forty-sixth aspect, an optical element comprising a glass, wherein the glass is the glass of any one of aspects 23-45.

According to a forty-seventh aspect, the glass comprises a plurality of components, the glass having a composition of the components comprising greater than or equal to 0.5 mol.% and less than or equal to 45.0 mol.% B₂O₃, greater than or equal to 0.1 mol.% and less than or equal to 25.0 mol.% Bi₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 8.0 mol.% WO₃, a sum of SiO₂ + B₂O₃ + P₂O₅ greater than or equal to 10.0 mol.%, a sum of TiO₂ + Nb₂O₅ greater than or equal to 8.5 mol.%, a sum of RE_mO_n + WO₃ + ZrO₂ greater than or equal to 4.5 mol.% and may optionally contain one or more components selected from CaO, BaO, ZnO, Na₂O, Al₂O₃, Li₂O, PbO, GeO₂, TeO₂, K₂O, SrO and MgO, wherein the composition of the components satisfies the conditions: SiO₂ + B₂O₃ - P₂O₅ [mol.%] ≥ 0.100, and the glass satisfies the condition: P_n > 2.045, where P_n is a parameter predicting a refractive index at 587.56 nm, n_d, calculated from the glass composition in terms of mol.% of the components according to the Formula (I):

where RE_mO_n is a total sum of rare earth metal oxides, and an asterisk (*) means multiplication.

According to a forty-eighth aspect, the glass of the forty-seventh aspect, wherein the glass has a refractive index at 587.56 nm, n_d, that is greater than or equal to 2.045.

According to a forty-ninth aspect, the glass of any one of aspects 47-48, wherein the composition of the components comprises greater than or equal to 20.0 mol.% and less than or equal to 27.5 mol.% TiO₂, greater than or equal to 15.0 mol.% and less than or equal to 30.0 mol.% La₂O₃, greater than or equal to 15.0 mol.% and less than or equal to 22.5 mol.% B₂O₃, greater than or equal to 5.0 mol.% and less than or equal to 20.0 mol.% SiO₂, greater than or equal to 4.0 mol.% and less than or equal to 9.0 mol.% ZrO₂, greater than or equal to 2.5 mol.% and less than or equal to 10.0 mol.% Nb₂O₅, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% BaO, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% CaO, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% Ga₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% Y₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 4.0 mol.% ZnO and greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% WO₃.

According to a fiftieth aspect, the glass of any one of aspects 47-49, wherein the composition of the components comprises one or more of the following components: greater than or equal to 20.25 mol.% and less than or equal to 26.00 mol.% TiO₂, greater than or equal to 20.0 mol.% and less than or equal to 27.5 mol.% La₂O₃, greater than or equal to 16.4 mol.% and less than or equal to 20.4 mol.% B₂O₃, greater than or equal to 10.0 mol.% and less than or equal to 17.5 mol.% SiO₂, greater than or equal to 5.3 mol.% and less than or equal to 8.1 mol.% ZrO₂, greater than or equal to 4.5 mol.% and less than or equal to 9.3 mol.% Nb₂O₅, greater than or equal to 0.5 mol.% and less than or equal to 6.3 mol.% Y₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 9.0 mol.% CaO, greater than or equal to 0.0 mol.% and less than or equal to 8.0 mol.% Ga₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 6.5 mol.% BaO, greater than or equal to 0.0 mol.% and less than or equal to 3.0 mol.% ZnO, greater than or equal to 0.0 mol.% and less than or equal to 1.8 mol.% WO₃, greater than or equal to 0 mol.% and less than or equal to 1.35 mol.% Gd₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 0.9 mol.% SrO and greater than or equal to 0.0 mol.% and less than or equal to 0.9 mol.% Yb₂O₃.

According to a fifty-first aspect, the glass of any one of aspects 47-50, wherein the composition of the components comprises greater than or equal to 21.0 mol.% and less than or equal to 26.3 mol.% La₂O₃, greater than or equal to 20.25 mol.% and less than or equal to 25.50 mol.% TiO₂, greater than or equal to 16.9 mol.% and less than or equal to 20.4 mol.% B₂O₃, greater than or equal to 11.0 mol.% and less than or equal to 16.5 mol.% SiO₂, greater than or equal to 5.6 mol.% and less than or equal to 8.0 mol.% ZrO₂, greater than or equal to 5.1 mol.% and less than or equal to 8.6 mol.% Nb₂O₅, greater than or equal to 0.75 mol.% and less than or equal to 5.50 mol.% Y₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 8.0 mol.% CaO, greater than or equal to 0.0 mol.% and less than or equal to 7.5 mol.% Ga₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 5.5 mol.% BaO, greater than or equal to 0.0 mol.% and less than or equal to 2.7 mol.% ZnO, greater than or equal to 0.0 mol.% and less than or equal to 1.6 mol.% WO₃, greater than or equal to 0.0 mol.% and less than or equal to 1.2 mol.% Gd₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 0.8 mol.% SrO and greater than or equal to 0.0 mol.% and less than or equal to 0.8 mol.% Yb₂O₃.

According to a fifty-second aspect, the glass of any one of aspects 47-51, wherein the composition of the components satisfy one or more of the following conditions: a sum of La₂O₃ + TiO₂ + B₂O₃ + SiO₂ + ZrO₂ + Nb₂O₅ + BaO + Y₂O₃ + CaO + Ga₂O₃ + Gd₂O₃ + ZnO + WO₃ + CeO₂ + SrO + Na₂O + Ta₂O₅ + Al₂O₅ greater than or equal to 99.0 mol.%, a sum of La₂O₃ + Y₂O₃ + Gd₂O₃ + TiO₂ + B₂O₃ + SiO₂ + ZrO₂ + Nb₂O₅ greater than or equal to 99.0 mol.%, a sum of La₂O₃ + Y₂O₃ + Gd₂O₃ + TiO₂ + B₂O₃ + SiO₂ + ZrO₂ + Nb₂O₅ + CaO + BaO greater than or equal to 99.0 mol.% and a sum of La₂O₃ + TiO₂ + B₂O₃ + SiO₂ + ZrO₂ + Nb₂O₅ greater than or equal to 97.0 mol.%.

According to a fifty-third aspect, the glass of any one of aspects 47-48 and 51-52, wherein the composition of the components comprises greater than or equal to 5.0 mol.% B₂O₃, greater than or equal to 5.0 mol.% La₂O₃, greater than or equal to 5.0 mol.% Nb₂O₅, greater than or equal to 5.0 mol.% SiO₂, greater than or equal to 5.0 mol.% TiO₂ and a sum of ZrO₂ + HfO₂ greater than or equal to 1.0 mol.%.

According to a fifty-fourth aspect, the glass of any one of aspects 47-53, wherein the composition of the components comprises a sum of R₂O + RO greater than or equal to 0.0 mol.% and less than or equal to 6.0 mol.%, where R₂O is a total sum of monovalent metal oxides and RO is a total sum of divalent metal oxides.

According to a fifty-fifth aspect, the glass of the fifty-fourth aspect, wherein the composition of the components comprises a sum of R₂O + RO greater than or equal to 0.0 mol.% and less than or equal to 1.0 mol.%..

According to a fifty-sixth aspect, the glass of any one of aspects 47-55, wherein the composition of the components satisfies the condition: 0.00 ≤ SiO₂ / (SiO₂ + B₂O₃) [mol.%] ≤ 0.40.

According to a fifty-seventh aspect, the glass of any one of aspects 47-55, wherein the composition of the components satisfies the condition: 0.38 ≤ SiO₂ / (SiO₂ + B₂O₃) [mol.%] ≤ 0.75.

According to a fifty-eighth aspect, the glass of any one of aspects 47-57, wherein the composition of the components comprises greater than or equal to 0.0 mol.% and less than or equal to 6.5 mol.% CaO and greater than or equal to 0.0 mol.% and less than or equal to 5.5 mol.% BaO and wherein the composition of the components is substantially free of ZnO.

According to a fifty-ninth aspect, the glass of any one of aspects 47-58, wherein the composition of the components comprises a sum of WO₃ + Bi₂O₃ greater than or equal to 0.0 mol.% and less than or equal to 7.0 mol.%.

According to a sixtieth aspect, the glass of any one of aspects 47-59, wherein the composition of the components comprises greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.% Y₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% Ta₂O₅, greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% TeO₂, greater than or equal to 0.0 mol.% and less than or equal to 0.5 mol.% GeO₂, greater than or equal to 0.0 mol.% and less than or equal to 0.5 mol.% PbO, greater than or equal to 0.0 mol.% and less than or equal to 0.2 mol.% As₂O₃ and greater than or equal to 0.0 mol.% and less than or equal to 0.2 mol.% Sb₂O₃, wherein the composition of the components is substantially free of fluorine and substantially free of V₂O₅.

According to a sixty-first aspect, the glass of any one of aspects 47-49 and 52-60, wherein the composition of the components comprises greater than or equal to 22.0 mol.% and less than or equal to 25.0 mol.% TiO₂, greater than or equal to 20.0 mol.% and less than or equal to 30.0 mol.% La₂O₃, greater than or equal to 16.0 mol.% and less than or equal to 20.0 mol.% B₂O₃, greater than or equal to 10.0 mol.% and less than or equal to 20.0 mol.% SiO₂, greater than or equal to 6.5 mol.% and less than or equal to 8.0 mol.% ZrO₂, greater than or equal to 5.0 mol.% and less than or equal to 6.7 mol.% Nb₂O₅, greater than or equal to 0.0 mol.% and less than or equal to 6.0 mol.% Y₂O₃, greater than or equal to 0.0 mol.% and less than or equal to 3.0 mol.% BaO and greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% Gd₂O₃ and greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% of all other components in total.

According to a sixty-second aspect, the glass of any one of aspects 47-61, wherein the glass satisfies the conditions: 4.5 ≤ P_d ≤ 5.5 and 2.045 ≤ P_n ≤ 2.07, where P_d is a parameter predicting a density at room temperature, d_RT, calculated from the glass composition in terms of mol.% of the components according to the Formula (II):

According to a sixty-third aspect, the glass of any one of aspects 47-62, wherein the glass has a density at room temperature, d_RT, that is greater than or equal to 4.5 g/cm³ and less than or equal to 5.5 g/cm³ and a refractive index at 587.56 nm, n_d, that is greater than or equal to 2.045 and less than or equal to 2.07.

According to a sixty-fourth aspect, the glass of any one of aspects 47-63, wherein the glass has a liquidus temperature, T_liq, that is less than or equal to 1260° C.

According to a sixty-fifth aspect, the glass of any one of aspects 47-64, wherein when cooled in air from 1100° C. to 500° C. in 2.5 minutes, the glass does not crystallize.

According to a sixty-sixth aspect, the glass of any one of aspects 47-65, wherein the glass has a transmittance at a wavelength of 460 nm, TX_{460 nm}, that is greater than or equal to 70%.

According to a sixty-seventh aspect, a method for manufacturing an optical element, the method comprising processing a glass, wherein the glass is the glass of any one of aspects 47-66.

According to a sixty-eighth aspect, an optical element comprising a glass, wherein the glass is the glass of any one of aspects 47-67.

Many variations and modifications may be made to the above-described embodiments of the disclosure without departing substantially from the spirit and various principles of the disclosure. All such modifications and variations are intended to be included herein within the scope of this disclosure and protected by the following claims.

To the extent not already described, the different features of the various aspects of the present disclosure may be used in combination with each other as desired. That a particular feature is not explicitly illustrated or described with respect to each aspect of the present disclosure is not meant to be construed that it cannot be, but it is done for the sake of brevity and conciseness of the description. Thus, the various features of the different aspects may be mixed and matched as desired to form new aspects, whether or not the new aspects are expressly disclosed.

Claims

1. A glass comprising a plurality of components, the glass having a composition of the components comprising: greater than or equal to 12.0 mol.% and less than or equal to 35.0 mol.% TiO2,greater than or equal to 2.5 mol.% and less than or equal to 20.0 mol.% ZrO2,greater than or equal to 0.5 mol.% and less than or equal to 40.0 mol.% B2O3,greater than or equal to 0.5 mol.% and less than or equal to 30.0 mol.% Nb2O5,greater than or equal to 0.0 mol.% and less than or equal to 20.0 mol.% Bi2O3,greater than or equal to 0.0 mol.% and less than or equal to 15.0 mol.% P2O5,greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% Al2O3,greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% Gd2O3,greater than or equal to 0.0 mol.% and less than or equal to 8.0 mol.% WO3,greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.% PbO,greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.% V2O5,greater than or equal to 0.0 mol.% and less than or equal to 1.5 mol.% ZnO,greater than or equal to 95.0 mol.% RmOn,greater than or equal to 0.5 mol.% and less than or equal to 35.0 mol.% REmOn,a sum of SiO2 + B2O3 + P2O5 greater than or equal to 10.0 mol.% anda sum of TiO2 + Nb2O5 greater than or equal to 0.0 mol.% and less than or equal to 42.0 mol.%, wherein the composition of the components satisfies the condition: and wherein the glass satisfies the condition:Pn−1.765+0.057*Pd>0.000,wherePn is a parameter predicting a refractive index at 587.56 nm, nd, calculated from the glass composition in terms of mol.% of the components according to the Formula (I): and Pd is a parameter predicting a density at room temperature, dRT, calculated from the glass composition in terms of mol.% of the components according to the Formula (II): where RmOn is a total sum of all oxides, REmOn is a total sum of rare earth metal oxides, and an asterisk (*) means multiplication.

2. The glass of claim 1, wherein the glass satisfies the condition: nd−1.765+0.057*dRT>0.000,wherend is a refractive index at 587.56 nm,dRT [g/cm3] is a density at room temperature.

3. The glass of claim 1, wherein the composition of the components comprises: greater than or equal to 20.0 mol.% and less than or equal to 27.5 mol.% TiO2,greater than or equal to 15.0 mol.% and less than or equal to 30.0 mol.% La2O3,greater than or equal to 15.0 mol.% and less than or equal to 22.5 mol.% B2O3,greater than or equal to 5.0 mol.% and less than or equal to 20.0 mol.% SiO2,greater than or equal to 4.0 mol.% and less than or equal to 9.0 mol.% ZrO2,greater than or equal to 2.5 mol.% and less than or equal to 10.0 mol.% Nb2O5,greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% BaO,greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% CaO,greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% Ga2O3,greater than or equal to 0.0 mol.% and less than or equal to 10.0 mol.% Y2O3 andgreater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% WO3.

4. The glass of claim 1, wherein the composition of the components comprises: greater than or equal to 22.0 mol.% and less than or equal to 25.0 mol.% TiO2,greater than or equal to 20.0 mol.% and less than or equal to 30.0 mol.% La2O3,greater than or equal to 16.0 mol.% and less than or equal to 20.0 mol.% B2O3,greater than or equal to 10.0 mol.% and less than or equal to 20.0 mol.% SiO2,greater than or equal to 6.5 mol.% and less than or equal to 8.0 mol.% ZrO2,greater than or equal to 5.0 mol.% and less than or equal to 6.7 mol.% Nb2O5,greater than or equal to 0.0 mol.% and less than or equal to 6.0 mol.% Y2O3,greater than or equal to 0.0 mol.% and less than or equal to 3.0 mol.% BaO andgreater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% Gd2O3 andgreater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% of all other components in total.

5. The glass of claim 1, wherein the glass satisfies the conditions: 4.5≤Pd≤5.5 and1.95≤Pn≤2.07..

6. The glass of claim 1, wherein when cooled in air from 1100° C. to 500° C. in 2.5 minutes, the glass does not crystallize.

7. A glass comprising a plurality of components, the glass having a composition of the components comprising: greater than or equal to 1.0 mol.% and less than or equal to 13.5 mol.% ZrO2,greater than or equal to 0.3 mol.% and less than or equal to 35.0 mol.% TiO2,greater than or equal to 0.3 mol.% and less than or equal to 29.5 mol.% B2O3,greater than or equal to 0.0 mol.% and less than or equal to 9.0 mol.% WO3,greater than or equal to 0.0 mol.% and less than or equal to 5.0 mol.% PbO,greater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% Gd2O3,greater than or equal to 0.0 at.% and less than or equal to 2.0 at.% F,a sum of TiO2 + Nb2O5 + La2O3 greater than or equal to 10.0 mol.% and less than or equal to 70.0 mol.%,a sum of SiO2 + B2O3 + P2O5 greater than or equal to 10.0 mol.%,a sum of REmOn + WO3 + ZrO2 greater than or equal to 5.0 mol.%,a sum of SiO2 + Y2O3 + Gd2O3 greater than or equal to 0.3 mol.%,a sum of V2O5 + MoO3 greater than or equal to 0.0 mol.% and less than or equal to 3.0 mol.% andoptionally comprising one or more components selected from Bi2O3, CaO, BaO, ZnO, Na2O, Al2O3, Li2O, GeO2, TeO2, K2O, SrO and MgO, wherein the composition of the components satisfies the conditions: and wherein the glass satisfies the condition:wherePn is a parameter predicting a refractive index at 587.56 nm, nd, calculated from the glass composition in terms of mol.% of the components according to the Formula (I): where REmOn is a total sum of rare earth metal oxides, and an asterisk (*) means multiplication.

8. The glass of claim 7, wherein the glass satisfies the condition: wherend is a refractive index at 587.56 nm.

9. The glass of claim 7, wherein the composition of the components satisfies the condition: .

10. The glass of claim 7, wherein the composition of the components comprises: greater than or equal to 22.0 mol.% and less than or equal to 25.0 mol.% TiO2,greater than or equal to 20.0 mol.% and less than or equal to 30.0 mol.% La2O3,greater than or equal to 16.0 mol.% and less than or equal to 20.0 mol.% B2O3,greater than or equal to 10.0 mol.% and less than or equal to 20.0 mol.% SiO2,greater than or equal to 6.5 mol.% and less than or equal to 8.0 mol.% ZrO2,greater than or equal to 5.0 mol.% and less than or equal to 6.7 mol.% Nb2O5,greater than or equal to 0.0 mol.% and less than or equal to 6.0 mol.% Y2O3 andgreater than or equal to 0.0 mol.% and less than or equal to 3.0 mol.% BaO andgreater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% of all other components in total.

11. The glass of claim 7, wherein the glass satisfies the conditions: 4.5≤Pd≤5.5 and1.95≤Pn≤2.07,wherePd is a parameter predicting a density at room temperature, dRT, calculated from the glass composition in terms of mol.% of the components according to the Formula (II): .

12. The glass of claim 7, wherein when cooled in air from 1100° C. to 500° C. in 2.5 minutes, the glass does not crystallize.

13. A glass comprising a plurality of components, the glass having a composition of the components comprising: greater than or equal to 0.5 mol.% and less than or equal to 45.0 mol.% B2O3,greater than or equal to 0.1 mol.% and less than or equal to 25.0 mol.% Bi2O3,greater than or equal to 0.0 mol.% and less than or equal to 8.0 mol.% WO3,a sum of SiO2 + B2O3 + P2O5 greater than or equal to 10.0 mol.%,a sum of TiO2 + Nb2O5 greater than or equal to 8.5 mol.%,a sum of REmOn + WO3 + ZrO2 greater than or equal to 4.5 mol.% andoptionally comprising one or more components selected from CaO, BaO, ZnO, Na2O, Al2O3, Li2O, PbO, GeO2, TeO2, K2O, SrO and MgO, wherein the composition of the components satisfies the condition: and the glass satisfies the condition:Pn>2.045,where• Pn is a parameter predicting a refractive index at 587.56 nm, nd, calculated from the glass composition in terms of mol.% of the components according to the Formula (I): where REmOn is a total sum of rare earth metal oxides and an asterisk (*) means multiplication.

14. The glass of claim 13, wherein the glass has a refractive index at 587.56 nm, nd that is greater than or equal to 2.045.

15. The glass of claim 13, wherein the composition of the components satisfies the condition: .

16. The glass of claim 13, wherein the composition of the components comprises: greater than or equal to 22.0 mol.% and less than or equal to 25.0 mol.% TiO2,greater than or equal to 20.0 mol.% and less than or equal to 30.0 mol.% La2O3,greater than or equal to 16.0 mol.% and less than or equal to 20.0 mol.% B2O3,greater than or equal to 10.0 mol.% and less than or equal to 20.0 mol.% SiO2,greater than or equal to 6.5 mol.% and less than or equal to 8.0 mol.% ZrO2,greater than or equal to 5.0 mol.% and less than or equal to 6.7 mol.% Nb2O5,greater than or equal to 0.0 mol.% and less than or equal to 6.0 mol.% Y2O3,greater than or equal to 0.0 mol.% and less than or equal to 3.0 mol.% BaO andgreater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% Gd2O3 andgreater than or equal to 0.0 mol.% and less than or equal to 2.0 mol.% of all other components in total.

17. The glass of claim 13, wherein the glass satisfies the conditions: 4.5≤Pd≤5.5 and2.045≤Pn≤2.07,wherePd is a parameter predicting a density at room temperature, dRT, calculated from the glass composition in terms of mol.% of the components according to the Formula (II): .

18. The glass of claim 13, wherein when cooled in air from 1100° C. to 500° C. in 2.5 minutes, the glass does not crystallize.