High-melting-point conductive oxide, method of manufacturing the same, and high-temperature electrically conductive material based on the oxide

Description

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to a high-melting-point conductive oxide, to a method of manufacturing the oxide, and to a high-temperature electrically conductive material used to form high-temperature heat-generating materials, such as heating elements for generating high temperatures in electric furnaces and the like, electrode material capable of being used at high temperatures, high-temperature light-emitting material including filament material for lamps and the like, and high-temperature thermocouple material and the like, utilizing heat produced when a current is passed through the oxide in an atmosphere containing oxygen.

[0003] 2. Description of the Prior Art

[0004] Electric furnaces that utilize resistance-heating employ a heating element material selected for that purpose. In air or an atmosphere including an oxygen, silicon carbide (SiC) heating elements can be used to obtain temperatures in the order of 1600° C., and molybdenum disilicide (MoSi2) heating elements can be used to obtain temperatures up to around 1700° C. Platinum (Pt) or platinum-rhodium (Pt-Rh) metal wire has a melting point of 1769° C., and can be used for electric furnaces that go up to 1500° C. Including the temperature dependency, the electrical resistivity of these heating elements is more or less metal-like. Heating elements of lanthanum-chromite, an oxide of lanthanum and chromium, has a semiconductor-like temperature dependency, but because of the material's relatively low electrical resistance, can be used to form general-purpose electric furnaces capable of obtaining temperatures of up to 1900° C.

[0005] To obtain higher temperatures with resistance-heating methods, zirconia (ZrO2) or thoria (ThO2) having a melting point or decomposition temperature of 2000° C. or more is used. Since these oxides are semiconductors, current flow can only occur at high temperatures of at least 1000° C. That is, since they have to be used in conjunction with other heating elements with metal-like resistivity, general-purpose electric furnaces that use these oxides as heating elements have not yet been realized. In hydrogen or an inert gas or other reducing atmosphere, the high-melting-point metals of molybdenum (Mo), tantalum (Ta) and tungsten (W) can be used to obtain high temperatures of up to 2000, 2100 and 2500° C., respectively. In the presence of very small amounts of oxygen (10−5 Torr or more), these heating elements readily form oxides, increasing their electrical resistance. For this reason, they cannot be used in an oxygen atmosphere.

[0006] Noble metals such as ruthenium (Ru), iridium (Ir) and rhodium (Rh) have high melting points (ruthenium: 2250° C.; iridium: 2457° C.; rhodium: 1963° C.). However, in an oxidizing atmosphere, at high temperatures these metals readily vaporize or oxidize. Moreover, the fact that they are noble metals mean that they are very expensive, costing four or five times more than gold, and they are not easy to machine, all of which makes it very difficult in practice to use them as heating element materials.

[0007] JP-A-HEI 6-223960 discloses high-frequency heating elements formed of oxides of ruthenium, iridium, rhodium or other elements. The invention of this disclosure has as its object the use of microwave absorption for heating applications such as microwave ovens and the like, and is characterized in that when the above materials are used to form heating elements for high-frequency heating, the materials exhibit good temperature elevation characteristics. The materials are intended for use at around 600° C. to 870° C., which is not the same as materials intended to be used at temperatures in the order of 2000° C.

[0008] Previously, resistance-heating to temperatures of 2000° C. or higher has only been possible using heating elements of tungsten or other such high-melting-point metal in a reducing atmosphere of hydrogen or an inert gas or the like. There have not been any suitable materials, that could be used in an oxidizing atmosphere, having a melting point in the order of 2000° C. and metal-like electrical resistivity. Therefore, there has not been a practical electric furnace capable of achieving a temperature of 1700° C. or higher. In other words, there has been no method of generating a high temperature of at least 1700° C. utilizing resistance-heating in an oxidizing atmosphere. Similarly, there has no thermocouple material to measure a temperature of 1700° C. or more. However, if there were a material having a metal-like low electrical resistance and a melting point of around 2000° C. in an oxidizing atmosphere, it would be possible to provide a method of resistance-heating at a previously unattainable temperature range, and it would also be possible to use a thermocouple to measure such high temperatures.

[0009] An object of the present invention is therefore to provide a high-temperature electrically conductive material that can be used for heating elements, electrode material, thermocouple material, light-emitting material and other such materials in an electric furnace that can be used in an oxidizing atmosphere at a high temperature of 1700° C. or more.

[0010] Another object of the present invention is to provide a high-melting-point electrically conductive oxide constituting the high-temperature electrically conductive material, and a method of manufacturing the same.

SUMMARY OF THE INVENTION

[0011] To attain the above object, the present invention provides a high-melting-point conductive oxide that is a Sr-Ru oxide comprising a mixture of a powdered Sr compound and Ru compound or Ru metal that is sintered at 900° C. to 1300° C. in an atmosphere containing oxygen to form a sintered body that is pulverized to a powder, shaped and again sintered at 1000° C. to 1500° C. in an atmosphere containing oxygen.

[0012] The above object is also attained by a high-melting-point conductive oxide that is a Sr-Ru oxide comprising a mixture of powdered SrCO3 and RuO2 that is sintered at 900° C. to 1300° C. in air to form a sintered body that is pulverized to a powder, shaped and again sintered at 1000° C. to 1500° C. in air.

[0013] The above object is also attained by a high-melting-point conductive oxide that is a Sr-Ru oxide single-crystal comprising a Sr-Ru oxide obtained as described above that is melted by concentrated infrared radiation or the like and recrystallized.

[0014] The present invention also includes the oxide and oxide single-crystal in which a molar ratio between the SrCO3 and the RuO2 is 2:1.

[0015] The above object is also attained by a method of manufacturing the high-melting-point conductive oxide, the method comprising mixing together powdered SrCO3 and RuO2 to form a mixture, sintering the mixture in air at 900° C. to 1300° C. to form a sintered body, pulverizing the sintered body to a powder, shaping the powder, and sintering the shaped powder in air at 1000° C. to 1500° C.

[0016] The present invention also includes a method of manufacturing the Sr-Ru oxide single-crystal by using focused infrared radiation or the like to melt the Sr-Ru oxide obtained as described above, and recrystallizing the melted oxide.

[0017] The present invention also provides high-temperature heating elements, high-temperature electrode material, light-emitting material and high-temperature thermocouple material comprised of the oxide or single-crystal for use in an atmosphere containing oxygen.

[0018] As described in the foregoing, as a material for use as heating elements, electrode material, light-emitting material and thermocouple material, of all the conductive oxides, there is used an oxide or single-crystal containing Sr and Ru, which in an atmosphere containing oxygen has the highest melting point and exhibits metal-like electrical resistance up to temperatures close to the highest melting point. The result is material properties that do not undergo change even at 2000° C. and can effect, for the first time, formation of oxidizing atmospheres at 2000° C. and measurement of temperatures in oxidizing atmospheres at 2000° C.

[0019] The above and other objects, further features of the invention, its nature and various advantages will be more apparent from the accompanying drawings and following detailed description of the invention.

BRIEF DESCRIPTION OF THE DRAWING

[0020]
FIG. 1 is a diagram illustrating the relationship between electrical resistance and temperature of a bar of Sr2RuO4 oxide of the present invention.

DESCRIPTION OF THE PREFERRED EMBODIMENT

[0021] As a result of studies, the present inventors discovered that among conductive oxides, Sr-Ru oxides had the highest melting point and, in atmospheres containing oxygen, exhibited metal-like electrical resistance at temperatures of up to around 2000° C. The present invention is based on this discovery, and relates to a Sr-Ru oxide comprising a mixture of a powdered Sr compound and Ru compound or Ru metal that is sintered at 900° C. to 1300° C. in an atmosphere containing oxygen to form a sintered body, that is then pulverized to a powder, shaped, and again sintered, at 1000° C. to 1500° C., in an atmosphere containing oxygen.

[0022] The strontium compound and ruthenium compound starting materials were used in the form of a carbonate (SrCO3) and an oxide (RuO2), but can be used in any form. It is preferable to use a powder having a particle size ranging from a few ten to a few hundred micrometers, but the particle size is not critical provided the powders are well mixed. This also applies to the particle size distribution. The proportion of the two components is determined based on what the resultant oxide is to be used for.

[0023] The preferred sintering temperature is from 900° C. to 1300° C. This is because a temperature lower than 900° C. will not decompose the starting SrCO3 material, while a temperature over 1300° C. will cause vaporization of the starting RuO2material, changing the composition. The sintering time will normally be within the range of two to 24 hours. The sintered body obtained by the above sintering is then pulverized to a powder, mixed, and press-formed to a required shape. The particle size of the powder ranges from a few ten to a few hundred micrometers. The formed body is then sintered for two to six hours at a temperature ranging from 1000° C. to 1500° C., that is to be higher than the primary sintering temperature. This secondary sintering is done to substantially bind the particles of the two materials, increase the strength of the oxide thus obtained and facilitate the workability.

[0024] The resultant oxide has a metal-like electrical resistance that shows virtually no change up to the melting point of 2100° C. This is because even though the material is melted and recrystallized, the oxide thus obtained has the same composition, which does not change up to the melting point. Forming the thus-obtained oxide into a single-crystal reduces the electrical resistivity by two orders of magnitude and increases the strength. The oxide may be formed into a single-crystal by a known method whereby the oxide is melted and recrystallized, or is formed into a thin film and recrystallized, or other such method.

[0025] The ultrahigh-melting-point conductive oxide or single-crystal thus obtained is basically composed of Sr2RuO4, Sr3Ru2O7 or SrRuO3 or the like. Provided the object can be attained, a known heat-resistant material can be incorporated as a separate phase. The ultrahigh-melting-point conductive material of this invention can be used in an oxidizing atmosphere at up to around 2000° C., and it is to be understood that it can of course also be used in a reducing atmosphere. When the needs of the intended application require that the oxide have a large volume, it can be formed as a polycrystal. When just a few millimeters or less is enough, it can be used as a single-crystal or in the form of a thin film.

[0026] As described in the foregoing, the Sr-Ru oxide of this invention has the highest melting point among conductive oxides and in an atmosphere containing oxygen exhibits metal-like electrical resistance at up to 2000° C. This makes the oxide applicable for use as a resistance-heating element that in an atmosphere containing oxygen can generate high temperatures of 1700° C. and over, and in such an oxygen-containing atmosphere can be used as a high-temperature electrode material and as a light-emitting material. The Sr-Ru oxide can also be used as a thermocouple material, making it possible to measure high temperatures of 1700° C. or more in an oxidizing atmosphere.

[0027] Examples of the present invention will now be described. However, it is to be understood that the invention is not limited to the following examples.

EXAMPLE 1 (Manufacture of Sr2RuO4 oxide):

[0028] SrCO3 and RuO2 were put together at a molar ratio of 2:1 and thoroughly mixed, using an agate mortar, and sintered in air for 24 hours at 1200° C. The sintered body thus formed was pulverized to a powder that was press-formed into the shape of a bar 6 mm in diameter and 200 mm in length. This was sintered for three hours in air at 1300° C., resulting in a bar-shaped Sr2RuO4 oxide.

EXAMPLE 2 (High-temperature electrical characteristics of Sr2RuO4 oxide):

[0029] The bar of Sr2RuO4 oxide prepared in Example 1 was placed in an air atmosphere in an infrared image furnace equipped with a halogen lamp and an elliptical mirror. To measure the electrical resistance, silver paste was used to affix terminals to each end of the oxide bar, and a radiation thermometer was used to measure the temperature at the portion T0 heated to the highest temperature by the focused infrared rays. In this state, a digital multimeter was used to measure the electrical resistance by the 4-terminal method while raising the lamp voltage. The Sr2RuO4 started to melt when the temperature reached roughly 2100° C. As can be seen from FIG. 1, electrical resistivity rose with the elevation of the temperature, but up to the melting point stayed at a metal-like value of between 1 and 3 ohms.

[0030] In FIG. 1, I+ and I− are current terminals, and V+ and V− are voltage terminals. The temperature was not the same over the whole bar of oxide. The portion at which the concentration of infrared rays produced the highest temperature was the center of the oxide, and it was the temperature T0 at this point that was measured. The temperature was plotted along the horizontal axis of the graph. The temperature decreased as the distance from the center of the oxide increased, so that T0>T1>T2. Thus, it was revealed that up to a high temperature of around 2000° C., the Sr2RuO4 could be used as a resistance-heating element in an oxidizing atmosphere. It was also revealed that in an oxidizing atmosphere the Sr2RuO4 could be used as a high-temperature electrode material, a thermocouple material, and a lamp filament that emits light when a current is passed therethrough.

EXAMPLE 3 (Manufacture of Sr2RuO4 single-crystal):

[0031] As in Example 2, a bar of Sr2RuO4 oxide was placed in an air atmosphere in an infrared image furnace equipped with a halogen lamp and a rotating elliptical reflecting mirror. The oxide bar was suspended from the upper part of the furnace, and the lamp voltage was increased to heat the lower end of the oxide bar to 2100° C. to melt the oxide. The end was then brought into contact with a bar of the same oxide material fixed in position in the lower part of the space, to thereby maintain the melted portion. The lamp was then raised at a speed of 20 mm/h, moving the melted portion slowly upwards, obtaining Sr2RuO4 oxide through recrystallization.

Claims

1. A high-melting-point conductive oxide that is a Sr-Ru oxide comprising a mixture of a powdered Sr compound and Ru compound or Ru metal that is sintered at a primary temperature of 900° C. to 1300° C. in an atmosphere containing oxygen to form a sintered body that is pulverized to a powder, shaped and again sintered in an atmosphere containing oxygen at a secondary temperature of 1000° C. to 1500° C. higher than the primary temperature.
2. A high-melting-point conductive oxide that is a Sr-Ru oxide comprising a mixture of powdered SrCO3 and RuO2 that is sintered at a primary temperature of 900° C. to 1300° C. in air to form a sintered body that is pulverized to a powder, shaped and again sintered in air at a secondary temperature of 1000° C. to 1500° C. higher than the primary temperature.
3. A high-melting-point conductive oxide that is a Sr-Ru oxide single-crystal comprising a mixture of a powdered Sr compound and Ru compound or Ru metal that is sintered at a primary temperature of 900° C. to 1300° C. in an atmosphere containing oxygen to form a sintered body that is pulverized to a powder, shaped and again sintered in an atmosphere containing oxygen at a secondary temperature of 1000° C. to 1500° C. higher than the primary temperature, with a resulting Sr-Ru oxide being melted and recrystallized by focused infrared radiation.
4. A high-melting-point conductive oxide that is a Sr-Ru oxide single-crystal comprising a mixture of powdered SrCO3 and RuO2 that is sintered at a primary temperature of 900° C. to 1300° C. in air to form a sintered body that is pulverized to a powder, shaped and again sintered in air at a secondary temperature of 1000° C. to 1500° C. higher than the primary temperature, with a resulting Sr-Ru oxide being melted and recrystallized by focused infrared radiation.
5. The high-melting-point conductive oxide according to claim 2, wherein a molar ratio between the SrCO3 and the RuO2 is 2:1.
6. The high-melting-point conductive oxide according to claim 4, wherein a molar ratio between the SrCO3 and the RuO2 is 2:1.
7. A method of manufacturing an oxide, said method comprising mixing together powdered SrCO3 and Ru compound or Ru metal to form a mixture, sintering the mixture in air at a primary temperature of 900° C. to 1300° C. to form a sintered body, pulverizing the sintered body to a powder, shaping the powder, and sintering the shaped powder in air at a secondary temperature of 1000° C. to 1500° C. higher than the primary temperature.
8. A method of manufacturing high-melting-point conductive oxide single-crystal, said method comprising mixing together powdered SrCO3 and Ru compound or Ru metal to form a mixture, sintering the mixture in air at a primary temperature of 900° C. to 1300° C. to form a sintered body, pulverizing the sintered body to a powder, shaping the powder, sintering the shaped powder in air at a secondary temperature of 1000° C. to 1500° C. higher than the primary temperature, and using focused infrared radiation to melt and recrystallize resultant oxide.
9. A method of manufacturing the oxide according to claim 7, wherein the Ru compound is RuO2.
10. A method of manufacturing the single crystal according to claim 8, wherein the Ru compound is RuO2.
11. A heating element for high-temperature use in an atmosphere containing oxygen, comprising the oxide according to claim 1.
12. A heating element for high-temperature use in an atmosphere containing oxygen, comprising the oxide according to claim 2.
13. A heating element for high-temperature use in an atmosphere containing oxygen, comprising the single-crystal according to claim 3.
14. A heating element for high-temperature use in an atmosphere containing oxygen, comprising the single-crystal according to claim 4.
15. An electrode material for high-temperature use in an atmosphere containing oxygen, comprising the oxide according to claim 1.
16. An electrode material for high-temperature use in an atmosphere containing oxygen, comprising the oxide according to claim 2.
17. An electrode material for high-temperature use in an atmosphere containing oxygen, comprising the single-crystal according to claim 3.
18. An electrode material for high-temperature use in an atmosphere containing oxygen, comprising the single crystal according to claim 4.
19. A material for high-temperature thermocouple use in an atmosphere containing oxygen, comprising the oxide according to claim 1.
20. A material for high-temperature thermocouple use in an atmosphere containing oxygen, comprising the oxide according to claim 2.
21. A material for high-temperature thermocouple use in an atmosphere containing oxygen, comprising the single-crystal according to claim 3.
22. A material for high-temperature thermocouple use in an atmosphere containing oxygen, comprising the single-crystal according to claim 4.

Priority Claims (1)

Number	Date	Country	Kind
2000-170889	Jun 2000	JP

High-melting-point conductive oxide, method of manufacturing the same, and high-temperature electrically conductive material based on the oxide

Information

Publication Number

Date Filed

Date Published

Inventors

CPC

US Classifications

International Classifications

Abstract

Description

Claims

Priority Claims (1)