The present application claims priority to Chinese Patent Application No. 202010665076.1, filed on Jul. 10, 2020 and entitled “High-modulus glass fiber composition, glass fiber and composite material thereof,” the disclosure of which is incorporated herein by reference in its entirety.
The invention relates to a high-modulus glass fiber composition, in particular, to a high-modulus glass fiber composition that can be used as a reinforcing base material for advanced composite materials, and to a glass fiber and a composite material thereof.
As a reinforcing base material for advanced composite materials, high-modulus glass fibers were originally used mainly in special fields such as aviation, aerospace, and national defense. With the progress of science and technology and the development of economy, high-modulus glass fibers have been widely used in civil and industrial fields such as large wind blades, pressure vessels, optic cable reinforcing cores and auto industry. Taking the field of wind power as an example, with the rapid development of large wind blades, the proportion of high modulus glass fiber used in place of ordinary glass fiber is increasing. At present, the pursuit of glass fiber having better modulus properties and the realization of mass production for this glass fiber has become an important trend of development for high modulus glass fibers.
The original high-strength and high-modulus glass is S-glass. Its composition is based on an MgO—Al2O3—SiO2 system. As defined by ASTM, S-glass is a type of glass mainly comprising the oxides of magnesium, aluminum and silicon. A typical solution of S-glass is S-2 glass developed by the U.S. The combined weight percentage of SiO2 and Al2O3 in the S-2 glass is as high as 90%, and the weight percentage of MgO is about 10%. As a result, the S-2 glass is not easy to melt and refine, and there are many bubbles in the molten glass. Further, the forming temperature of S-2 glass fiber is as high as 1571° C. and the liquidus temperature is as high as 1470° C., and its crystallization rate is also very high. As such, it is overly difficult to produce S-2 glass fiber and the large-scale tank furnace production of S-2 glass fiber cannot be achieved, and it is even difficult to realize one-step production. For these reasons, the production scale and efficiency of S-2 glass fiber are both very low while its price is high, making it impractical to achieve a large-scale industrial use.
An HS series high-strength glass that is comparable to S-glass has been developed by China. The composition of the HS glass primarily contains SiO2, Al2O3 and MgO while also including relatively high contents of Li2O, B2O3 and Fe2O3. Its forming temperature is in a range from 1310° C. to 1330° C. and its liquidus temperature is from 1360° C. to 1390° C. The temperatures of these two ranges are much lower than those of S glass. However, since the forming temperature of HS glass is lower than its liquidus temperature, the ΔT value is negative, which is unfavorable for efficient formation of glass fiber, the forming temperature has to be increased and special bushings and bushing tips have to be used to prevent a glass crystallization phenomenon from occurring in the fiber drawing process. This causes difficulty in temperature control and also makes it difficult to realize large-scale industrial production. In addition, due to the introduction of high contents of Li2O and B2O3, with the combined content generally being over 2% or even 3%, the mechanical properties and corrosion resistance of glass are adversely affected. Moreover, the elastic modulus of HS glass is similar to that of S-glass.
Japanese patent JP8231240 discloses a glass fiber composition which contains 62-67% of SiO2, 22-27% of Al2O3, 7-15% of MgO, 0.1-1.1% of CaO and 0.1-1.1% of B2O3, expressed in percentage by weight on the basis of the total composition. Compared with S glass, the amount of bubbles formed with this composition is significantly lowered, but the fiber formation remains difficult, as its forming temperature goes beyond 1460° C.
The production of high-modulus glass fibers in the existing technologies described above generally faces great production difficulties, specifically manifested by high forming temperature and high liquidus temperature, high rate of crystallization, narrow temperature ranges (ΔT) for fiber formation, great melting and refining problems, and many bubbles in the molten glass. To reduce production difficulties, most companies and institutions tend to sacrifice some of the glass properties, thus making it impossible to substantially improve the modulus of above-mentioned glass fibers.
In order to solve the issue described above, the present invention aims to provide a high-modulus glass fiber composition. The composition can significantly increase the modulus of glass fiber, significantly reduce the refining temperature of molten glass, and improve the refining performance of molten glass; it can also optimize the hardening rate of molten glass, improve the cooling performance of glass fiber and reduce the crystallization rate. The composition is suitable for large-scale production of high-modulus glass fiber.
In accordance with one aspect of the present invention, there is provided a composition for producing high-modulus glass fiber, the composition comprising percentage by weight of the following components:
8-18%
≥25%
In a class of this embodiment, the composition comprises the following components expressed as percentage by weight:
8-18%
≥25%
In a class of this embodiment, the composition comprises the following components expressed as percentage by weight:
8-18%
≥25%
In addition, the total weight percentage of the above components is greater than or equal to 98%.
In a class of this embodiment, the weight percentage ratio C1═MgO/CaO is greater than or equal to 1.7.
In a class of this embodiment, the weight percentage ratio C2═Y2O3/MgO is greater than or equal to 0.8.
In a class of this embodiment, the weight percentage ratio C3═Y2O3/CaO is greater than or equal to 1.9.
In a class of this embodiment, the weight percentage ratio C4═Al2O3/Y2O3 is 1-2.5.
In a class of this embodiment, the content range of Y2O3 is 10.1-20% by weight.
In a class of this embodiment, the content range of SiO2 is 44-55.9% by weight.
In a class of this embodiment, the content range of Al2O3 is 15.8-20.4% by weight.
In a class of this embodiment, the content range of MgO is 9-15% by weight.
In a class of this embodiment, the content range of CaO is 0.5-5.9% by weight.
In a class of this embodiment, the weight percentage ratio C1═MgO/CaO is greater than or equal to 1.7, and the weight percentage ratio C2═Y2O3/MgO is greater than or equal to 0.8.
In a class of this embodiment, the weight percentage ratio C1═MgO/CaO is greater than or equal to 2.0, and the weight percentage ratio C2═Y2O3/MgO is greater than or equal to 0.9.
In a class of this embodiment, the weight percentage ratio C2═Y2O3/MgO is greater than or equal to 0.8, and the weight percentage ratio C3═Y2O3/CaO is greater than or equal to 2.1.
In a class of this embodiment, the weight percentage ratio C1═MgO/CaO is greater than or equal to 1.7, the weight percentage ratio C2═Y2O3/MgO is greater than or equal to 0.8, and the weight percentage ratio C3═Y2O3/CaO is greater than or equal to 2.1.
In a class of this embodiment, the weight percentage ratio C1═MgO/CaO is greater than or equal to 1.7, the weight percentage ratio C2═Y2O3/MgO is greater than or equal to 0.8, the weight percentage ratio C3═Y2O3/CaO is greater than or equal to 1.9, and the weight percentage ratio C4═Al2O3/Y2O3 is 1-2.1.
In a class of this embodiment, the composition comprises the following components expressed as percentage by weight:
In addition, the weight percentage ratio C1═MgO/CaO is greater than or equal to 1.7.
In a class of this embodiment, the composition comprises the following components expressed as percentage by weight:
8-16%
In addition, the weight percentage ratio C1═MgO/CaO is greater than or equal to 1.7, and the weight percentage ratio C2═Y2O3/MgO is greater than or equal to 0.8.
In a class of this embodiment, the content range of CeO2 is 0-2% by weight.
In a class of this embodiment, the composition further contains one or more of ZrO2, ZnO, B2O3, F2 and SO3, the combined weight percentage being less than 4%.
In a class of this embodiment, the composition further contains 0-0.9% by weight of ZrO2.
In a class of this embodiment, the composition comprises the following components expressed as percentage by weight:
8-18%
≥25%
In addition, the total weight percentage of the above components is greater than or equal to 99.5%.
In a class of this embodiment, the composition may be free of B2O3.
In a class of this embodiment, the composition may be free of MnO.
In a class of this embodiment, the composition may produce a molten glass that has a refining temperature of less than or equal to 1460° C.
According to another aspect of this invention, a glass fiber produced with the glass fiber composition is provided.
According to yet another aspect of this invention, a composite material including the above glass fiber is provided.
In the high-modulus glass fiber composition according to the present invention, by introducing a high content of Y2O3, reasonably configuring the respective content ranges of SiO2, Al2O3, Y2O3, CaO and MgO as well as the ratios therebetween, controlling the content ranges of alkali earth metal oxides and alkali metal oxides as well as the ratios therebetween, and controlling the content ranges of (Al2O3+MgO) and (MgO+Y2O3) respectively, while utilizing the special compensation effect and accumulation effect of yttrium ions in the glass structure as well as the mixed effect of alkali earth metal, enhancing the synergistic effects between magnesium ions and calcium ions, between yttrium ions and magnesium ions, between yttrium ions and calcium ions, and between yttrium ions and aluminum ions, and further controlling the ratios of MgO/CaO, Y2O3/MgO, Y2O3/CaO and Al2O3/Y2O3, the composition enables the glass to have a more compact stacking structure and a higher difficulty of ions reorganization and arrangement during the crystallization process. Therefore, the composition for producing a glass fiber of this invention can significantly increase the glass modulus and reduce the glass crystallization rate. In the meantime, the composition can also significantly reduce the glass refining temperature, improve the refining performance, optimize the hardening rate of molten glass, and improve the cooling performance of glass fiber.
Specifically, the high-modulus glass fiber composition according to the present invention comprises the following components expressed as percentage by weight:
8-18%
≥25%
The effect and content of each component in the glass fiber composition is described as follows:
SiO2 is a main oxide forming the glass network. Compared with the S-glass, in order to increase the glass modulus, the glass fiber composition according to the present invention contains a significantly reduced amount of silica while introducing a high content of yttrium oxide. In the glass fiber composition of the present invention, the content range of SiO2 is 43-58%. Preferably, the SiO2 content range can be 44-57%, more preferably 44-55.9%, even more preferably 45-54.9%, and still even more preferably 45-54%.
Al2O3 is another oxide forming the glass network. When combined with SiO2, it can have a substantive effect on the mechanical properties of the glass. Too low of an Al2O3 content will make it impossible to obtain sufficiently high mechanical properties, while too high of an Al2O3 content will significantly increase the risk of crystallization. Therefore, the content range of Al2O3 in this invention is 15.5-23%. Preferably, the Al2O3 content can be 15.8-21%, more preferably 15.8-20.4%, even more preferably 16.5-19.8%, and still even more preferably 17-19.6%.
Further, in order to obtain sufficiently high mechanical properties of glass fiber and to reduce the fiber forming temperature, the sum of the weight percentages of SiO2+Al2O3 can be 65-78%. Preferably, the sum of the weight percentages of SiO2+Al2O3 can be 65-76%, more preferably 66-74.5%, and even more preferably 66-73%.
In the present invention, MgO and CaO mainly play the role of regulating the viscosity and crystallization of the glass. In the glass fiber composition of this invention, the weight percent range of MgO is 8-18%. Preferably, the weight percent range of MgO can be 8-16%, more preferably 9-15%, even more preferably 9.4-13.5%, and still even more preferably 9.4-12%. In the glass fiber composition of this invention, the weight percent range of CaO is 0.1-7.5%. Preferably, the weight percent range of CaO can be 0.1-6.5%, more preferably 0.5-5.9%, even more preferably 0.5-4.9%, and still even more preferably 1-4.5%.
In the high-modulus glass fiber according to the present invention, the sum of the weight percentages of Al2O3+MgO can be greater than or equal to 25%. Preferably, the sum of the weight percentages of Al2O3+MgO can be greater than or equal to 26%, more preferably can be 26-35%, and even more preferably 26.5-32%.
Y2O3 is an important rare earth oxide. As the external ions of the glass network, Y3+ ions have large coordination numbers, high field strength and high electric charge, and high accumulation capability, which would help improve the structural stability of the glass and increase the glass modulus and strength. In the glass fiber composition of this invention, the content range of Y2O3 is 7.1-22%. Preferably, the content range of Y2O3 is 8.1-22%, more preferably 10.1-20%, even more preferably 11.4-20%, and still even more preferably 12.3-20%. Furthermore, the content range of Y2O3 is preferably 13.1-20%, and more preferably 14.6-20%.
In the glass fiber composition of this invention, the sum of the weight percentages of Y2O3+MgO can be greater than or equal to 16.5%. Preferably, the sum of the weight percentages of Y2O3+MgO can be greater than or equal to 17.5%, more preferably can be 17.5-34%, and even more preferably 18.1-33%.
The Y3+ ions and Ca2+ ions can replace each other well for network filling, as their ionic radiuses are almost the same, 0.09 nm for the Y3+ ion and 0.1 nm for the Ca2+ ion, both being noticeably larger than that of either Al3+ (0.0535 nm) or Mg2+ (0.072 nm). Meanwhile, in the present invention, by considering the differences of field strength between Y3+ ions and Mg2+ ions, and between Y3+ ions and Ca2+ ions, as well as the mixed alkali earth effect between Ca2+ ions and Mg2+ ions, and by introducing a high amount of Y2O3 while properly controlling the ratios therebetween accordingly, the movement and arrangement of other ions in the glass would be effectively inhibited, so that the crystallization tendency of the glass is significantly minimized; also, the hardening rate of molten glass would be effectively regulated and the cooling performance of the glass would be improved. Further, the ratios of MgO/CaO, Y2O3/MgO, Y2O3/CaO and Al2O3/Y2O3 are rationally controlled in this invention, so that not only can a better effect of structural stacking be achieved, but also the crystal phases formed in the glass crystallization can be effectively restrained due to a strengthened competition among the crystal phases; and thus the crystallization tendency of the glass would be effectively controlled. The main crystal phases include cordierite (Mg2Al4Si5O8), anorthite (CaAl2Si2O8), diopside (CaMgSi2O6), and a mixture thereof.
Further, the weight percentage ratio C1═MgO/CaO is greater than or equal to 1.7. Preferably, the weight percentage ratio C1 is greater than or equal to 2.0, more preferably greater than or equal to 2.3, and even more preferably greater than or equal to 2.5.
Further, the weight percentage ratio C2═Y2O3/MgO is greater than or equal to 0.8. Preferably, the weight percentage ratio C2 is greater than or equal to 0.9, more preferably greater than or equal to 1.0, and even more preferably greater than or equal to 1.1.
Further, the weight percentage ratio C3═Y2O3/CaO is greater than or equal to 1.9. Preferably, the weight percentage ratio C3 is greater than or equal to 2.1, more preferably greater than or equal to 2.3, and even more preferably greater than or equal to 2.9.
Further, the weight percentage ratio C4═Al2O3/Y2O3 is 1-2.5. Preferably, the weight percentage ratio C4 is 1-2.1, more preferably 1-2, and even more preferably 1.2-2.
Furthermore, the combined weight percentage of CaO+MgO can be 9-20%. Preferably, the combined weight percentage of CaO+MgO can be 9.5-18%, more preferably can be 9.5-17%, and even more preferably can be 10-16%.
Both Na2O and K2O can reduce glass viscosity and are good fluxing agents. Compared with Na2O and K2O, Li2O can not only significantly reduce glass viscosity thereby improving the glass melting performance, but also help improve the mechanical properties of glass. However, the introduced amount of alkali metal oxides should be controlled, as the raw materials containing these oxides are very costly and, when there is an excessive amount of alkali metal ions in the glass fiber composition, the structural stability of the glass will be affected and thus the corrosion resistance of the glass will be noticeably impaired. Therefore, in the glass fiber composition according to the present invention, the content range of Na2O is 0.01-2%, preferably 0.01-1.5%, more preferably 0.05-0.9%, and even more preferably 0.05-0.45%.
In the glass fiber composition according to the present invention, the content range of K2O is 0-1.5%, preferably 0-1%, and more preferably 0-0.5%.
In the glass fiber composition according to the present invention, the content range of Li2O is 0-0.9%, preferably 0-0.6%, more preferably 0-0.3%. In another embodiment of this invenition, the glass fiber composition can be free of Li2O.
Further, the combined weight percentage of Na2O+K2O+Li2O can be 0.01-1.4%, preferably 0.05-0.9%. Further, the combined weight percentage of Na2O+K2O can be 0.01-1.2%, preferably 0.05-0.7%.
TiO2 can reduce the viscosity of glass at high temperatures and, with a synergistic effect produced in combination with titanium ions and yttrium ions, can improve the stacking effect and mechanical properties of the glass. In the glass fiber composition of this invention, the content range of TiO2 is 0.01-5%, preferably 0.01-3%, more preferably 0.05-1.5%, and even more preferably 0.05-0.9%.
Fe2O3 facilitates the melting of glass and can also improve the crystallization performance of glass. However, since ferric ions have a coloring effect, the introduced amount should be limited. In the glass fiber composition of this invention, the content range of Fe2O3 is 0.01-1.5%, preferably 0.01-1%, and more preferably 0.05-0.8%.
SrO can reduce the glass viscosity and produce a synergistic effect of alkaline earth metal ions with calcium ions and magnesium ions, which can help further reduce the glass crystallization tendency. In the glass fiber composition of this invention, the content range of SrO is 0-4%, preferably 0-2%, more preferably 0-1%, and even more preferably 0-0.5%. In another embodiment of this invention, the glass fiber composition can be free of SrO.
La2O3 can reduce the glass viscosity and improve the mechanical properties of glass, and has a certain synergistic effect with yttrium ions, which can further reduce the crystallization tendency of glass. CeO2 can enhance the crystallization tendency and refining performance of glass. In the glass fiber composition of this invention, the sum of the weight percentages of La2O3+CeO2 can be 0-5%, preferably 0-3%, and more preferably 0-1.5%.
Further, the content range of La2O3 in the glass fiber composition of this invention can be 0-3%, preferably 0-1.5%. In another embodiment of this invention, the glass fiber composition can be free of La2O3. Further, the content range of CeO2 in the glass fiber composition of this invention can be 0-2%, preferably 0-0.6%. In another embodiment of this invention, the glass fiber composition can be free of CeO2.
In addition to the above-mentioned main components, the glass fiber composition according to the present invention can also contain a small amount of other components with a combined content less than or equal to 4% by weight.
Further, the glass fiber composition according to the present invention contains one or more of ZrO2, ZnO, B2O3, F2 and SO3, and the total amount of ZrO2, ZnO, B2O3, F2 and SO3 is less than 4% by weight. Further, the total amount of ZrO2, CeO2, ZnO, B2O3, F2 and SO3 is less than 2% by weight.
Further, the glass fiber composition according to the present invention contains one or more of Sm2O3, Sc2O3, Nd2O3, Eu2O3 and Gd2O3, and the total amount of Sm2O3, Sc2O3, Nd2O3, Eu2O3 and Gd2O3 is less than 4% by weight.
Further, the glass fiber composition according to the present invention contains one or more of Ho2O3, Er2O3, Tm2O3, Tb2O3 and Lu2O3, and the total amount of Ho2O3, Er2O3, Tm2O3, Tb2O3 and Lu2O3 is less than 2% by weight.
Further, the glass fiber composition according to the present invention contains either or both of Nb2O5 and Ta2O5 with a combined content of less than 2% by weight.
Further, the glass fiber composition according to the present invention contains ZrO2 with a content range of 0-2.4% by weight. Further, the content range of ZrO2 can be 0-0.9%, and still further can be 0-0.3%. In another embodiment of this invention, the glass fiber composition can be free of ZrO2.
Further, the glass fiber composition according to the present invention contains B2O3 with a content range of 0-2% by weight. In another embodiment of this invention, the glass fiber composition can be free of B2O3.
Further, the glass fiber composition according to the present invention contains F2 with a content range of 0-1% by weight. Further, the content range of F2 can be 0-0.5%. Further, the glass fiber composition according to the present invention contains SO3 with a content range of 0-0.5% by weight.
Further, the combined weight percentage of other components can be less than or equal to 2%, and further can be less than or equal to 1%, and still further can be less than or equal to 0.5%.
Further, the refining temperature of the glass fiber composition according to the present invention can be less than or equal to 1485° C. Further, the refining temperature can be less than or equal to 1460° C., and still further less than or equal to 1445° C.
Further, the modulus of glass fiber formed from the glass fiber composition of this invention can be greater than or equal to 95 GPa. Further, the modulus of glass fiber can be 97-115 GPa.
In the glass fiber composition according to the present invention, the beneficial effects produced by the aforementioned selected ranges of the components will be explained by way of examples through the specific experimental data.
The following are examples of preferred content ranges of the components contained in the glass fiber composition according to the present invention.
The high-modulus glass fiber composition according to the present invention comprises the following components expressed as percentage by weight:
8-18%
≥25%
wherein, the total weight percentage of the above components is greater than or equal to 98%, the weight percentage ratio C1═MgO/CaO is greater than or equal to 1.7, and the weight percentage ratio C2═Y2O3/MgO is greater than or equal to 0.8.
The high-modulus glass fiber composition according to the present invention comprises the following components expressed as percentage by weight:
8-16%
wherein, the weight percentage ratio C1═MgO/CaO is greater than or equal to 2.0, and the weight percentage ratio C2═Y2O3/MgO is greater than or equal to 0.9.
The high-modulus glass fiber composition according to the present invention comprises the following components expressed as percentage by weight:
The high-modulus glass fiber composition according to the present invention comprises the following components expressed as percentage by weight:
8-18%
≥25%
wherein, the weight percentage ratio C1═MgO/CaO is greater than or equal to 1.7.
The high-modulus glass fiber composition according to the present invention comprises the following components expressed as percentage by weight:
8-18%
≥25%
wherein, the total weight percentage of the above components is greater than or equal to 98%, the weight percentage ratio C2═Y2O3/MgO is greater than or equal to 0.8, and the weight percentage ratio C3═Y2O3/CaO is greater than or equal to 2.1.
The high-modulus glass fiber composition according to the present invention comprises the following components expressed as percentage by weight:
8-18%
≥25%
wherein, the weight percentage ratio C1═MgO/CaO is greater than or equal to 1.7, the weight percentage ratio C2═Y2O3/MgO is greater than or equal to 0.8, and the weight percentage ratio C3═Y2O3/CaO is greater than or equal to 2.9.
The high-modulus glass fiber composition according to the present invention comprises the following components expressed as percentage by weight:
8-18%
≥25%
wherein, the weight percentage ratio C3═Y2O3/CaO is greater than or equal to 2.9.
The high-modulus glass fiber composition according to the present invention comprises the following components expressed as percentage by weight:
8-18%
≥25%
wherein, the weight percentage ratio C1═MgO/CaO is greater than or equal to 1.7, the weight percentage ratio C2═Y2O3/MgO is greater than or equal to 0.8, and the weight percentage ratio C4═Al2O3/Y2O3 is 1-2.
In order to better clarify the purposes, technical solutions and advantages of the examples of the present invention, the technical solutions in the examples of the present invention are clearly and completely described below. Obviously, the examples described herein are just part of the examples of the present invention and are not all the examples. All other exemplary embodiments obtained by one skilled in the art on the basis of the examples in the present invention without performing creative work shall all fall into the scope of protection of the present invention. What needs to be made clear is that, as long as there is no conflict, the examples and the features of examples in the present application can be arbitrarily combined with each other.
The basic concept of the present invention is that the components of the glass fiber composition expressed as percentage by weight are: 43-58% of SiO2, 15.5-23% of Al2O3, 8-18% of MgO, greater than or equal to 25% of (Al2O3+MgO), 0.1-7.5% of CaO, 7.1-22% of Y2O3, greater than or equal to 16.5% of (MgO+Y2O3), 0.01-5% of TiO2, 0.01-1.5% of Fe2O3, 0.01-2% of Na2O, 0-1.5% of K2O, 0-0.9% of Li2O, 0-4% of SrO, and 0-5% of (La2O3+CeO2). The composition can significantly increase the modulus of glass fiber, significantly reduce the refining temperature of molten glass, and improve the refining performance of molten glass; it can also optimize the hardening rate of molten glass, improve the cooling performance of glass fiber and reduce the crystallization rate. The composition is suitable for large-scale production of high-modulus glass fiber.
The specific content values of SiO2, Al2O3, MgO, CaO, Y2O3, TiO2, Fe2O3, Na2O, K2O, Li2O, SrO, La2O3, CeO2 and ZrO2 in the glass fiber composition of the present invention are selected to be used in the examples, and comparisons with the improved R glass, designated as B1, as disclosed in patent WO2016165506A2, the conventional R glass designated as B2, and the S glass designated as B3, are made in terms of the following eight property parameters,
(1) Forming temperature, the temperature at which the glass melt has a viscosity of 103 poise and which represents the typical temperature for fiber formation.
(2) Liquidus temperature, the temperature at which the crystal nucleuses begin to form when the glass melt cools off—i.e., the upper limit temperature for glass crystallization.
(3) Refining temperature, the temperature at which the glass melt has a viscosity of 102 poise and which represents the relative difficulty in refining molten glass and eliminating bubbles from the glass. Generally, when a refining temperature is lower, it will be more efficient to refine molten glass and eliminate bubbles under the same temperature.
(4) ΔT value, which is the difference between the forming temperature and the liquidus temperature and indicates the temperature range at which fiber drawing can be performed.
(5) ΔL value, which is the difference between the refining temperature and the forming temperature and indicates the hardening rate of molten glass. It can be used to represent the difficulty of glass melt cooling during fiber formation. Generally speaking, if the ΔL value is relatively small, the glass melt will be easier to cool off under the same fiberizing conditions, which is conducive to efficient drawing of glass fiber.
(6) Elastic modulus, the modulus defining the ability of glass to resist elastic deformation, which is to be measured on bulk glass according to ASTM E1876. It can be used to represent the modulus property of glass fiber.
(7) Crystallization area ratio, to be determined in a procedure set out as follows: Cut the bulk glass appropriately to fit in with a porcelain boat trough and then place the cut glass bar sample into the porcelain boat. Put the porcelain boat with the pretreated glass bar sample into a gradient furnace for crystallization and keep the sample for heat preservation for 5 hours. Take the porcelain boat with the sample out of the gradient furnace and air-cool it to room temperature. Finally, examine and measure the amounts and dimensions of crystals on the surfaces of each sample within a temperature range of 1050−1150° C., from a microscopic view by using an optical microscope, and then calculate the relative area ratio of crystallization with reference to S glass. A high area ratio would mean a high crystallization tendency and a high crystallization rate.
(8) Bubble content, to be determined in a procedure set out as follows: Use special molds to compress the glass batch materials in each example into samples of same shape and dimension, which will then be placed on the sample platform of a high temperature microscope. Heat the samples according to standard procedures up to the pre-set temperature of 1500° C., and then directly cool them off with the cooling of the microscope to the ambient temperature without heat preservation. Finally, each of the glass samples is examined under an optical microscope to determine the amount of bubbles in the samples, and then calculate the relative bubble content with reference to S glass. The higher the bubble content is, the more difficult the refining of the glass will be, and the quality of the molten glass will be hard to be guaranteed. Wherein, the amounts of bubbles are identified according to the magnification of the microscope.
The aforementioned eight parameters and the methods of measuring thereof are well-known to one skilled in the art. Therefore, these aforementioned parameters can be used to effectively explain the properties of the glass fiber composition according to the present invention.
The specific procedures for the experiments are as follows: each component can be acquired from the appropriate raw materials, and the raw materials are mixed according to specific proportions so that each component reaches the final expected weight percentage. The mixed batch is melted and refined. Then the molten glass is drawn out through the tips of the bushings, thereby forming the glass fiber. The glass fiber is attenuated onto the rotary collet of a winder to form cakes or packages. Of course, normal methods can be used to further process these glass fibers to meet the expected requirements.
Comparisons of the property parameters used in the examples of the glass fiber composition according to the present invention with those of the S glass, conventional R glass and improved R glass are further made below by way of tables, wherein the component contents of the compositions for producing glass fibers are expressed in weight percentage. What needs to be made clear is that the total amount of the components in an example is slightly less than 100%, and it should be understood that the remaining amount is trace impurities or a small amount of components which cannot be analyzed.
It can be seen from the values in the above tables that, compared with the composition of S glass, the glass fiber composition according to the present invention has the following advantages: (1) much higher elastic modulus; (2) much lower refining temperature and bubble content, which means the molten glass of the present invention is easier to refine and the bubbles are easier to be discharged; and (3) much lower fiber forming temperature, liquidus temperature and crystallization area ratio.
Compared with the composition of the conventional R glass, the glass fiber composition according to the present invention has the following advantages: (1) much higher elastic modulus; (2) much lower refining temperature and bubble content, which means the molten glass of the present invention is easier to refine and the bubbles are easier to be discharged; (3) much lower ΔL value, which helps increase the fiber drawing efficiency as the molten glass is easier to cool off; and (4) much lower fiber forming temperature, liquidus temperature and crystallization area ratio.
Compared with the composition of the improved R glass, the glass fiber composition according to the present invention has the following advantages: (1) much higher elastic modulus; (2) much lower refining temperature and bubble content, which means the molten glass of the present invention is easier to refine and the bubbles are easier to be discharged; (3) much lower ΔL value, which helps increase the fiber drawing efficiency as the molten glass is easier to cool off; and (4) a lower crystallization area ratio, which means the molten glass of the present invention has relatively low crystallization rate and thus help reduce the crystallization risk.
Therefore, it can be concluded that the glass fiber composition according to the present invention has made a breakthrough in terms of glass modulus, refining and cooling performance, and crystallization rate. According to the present invention, under equal conditions, the modulus of glass is greatly raised, the refining temperature of molten glass is significantly lowered, the amount of bubbles in the molten glass is reduced and the glass shows excellent cooling performance. The overall technical solution of the present invention is excellent.
The glass fiber composition according to the present invention can be used for making glass fibers having the aforementioned excellent properties.
The glass fiber composition according to the present invention in combination with one or more organic and/or inorganic materials can be used for preparing composite materials having excellent performance, such as glass fiber reinforced base materials.
It is to be noted that, in this text, the terms “comprise/comprising,” “contain/containing” and any other variants thereof are non-exclusive, so that any process, method, object or device containing a series of elements contains not only such factors, but also other factors not listed clearly, or further contains inherent factors of the process, method, object or device. Without further restrictions, a factor limited by the phrase “comprises/comprising an/a . . . ,” does not exclude other identical factors in the process, method, object or device including the factors.
The foregoing embodiments are provided only for describing instead of limiting the technical solutions of the present invention. While particular embodiments of the invention have been shown and described, it will be obvious to one skilled in the art that modifications can be made to the technical solutions embodied by all the aforementioned embodiments, or that equivalent replacements can be made to some of the technical features embodied by all the aforementioned embodiments, without departing from the spirit and scope of the technical solutions of the present invention.
The high-modulus glass fiber composition according to the present invention can significantly increase the modulus of glass fiber, significantly reduce the refining temperature of molten glass, and improve the refining performance of molten glass; it can also optimize the hardening rate of molten glass, improve the cooling performance of glass fiber and reduce the crystallization rate. The composition is suitable for large-scale production of high-modulus glass fiber.
Compared with conventional glass fiber compositions, the glass fiber composition according to the present invention has made a breakthrough in terms of glass modulus, refining and cooling performance, and crystallization rate. According to the present invention, under equal conditions, the modulus of glass is greatly raised, the refining temperature of molten glass is significantly lowered, the amount of bubbles in the molten glass is reduced and the glass shows excellent cooling performance. The overall technical solution of the present invention is excellent.
Therefore, the present invention has good industrial applicability.
| Number | Date | Country | Kind |
|---|---|---|---|
| 202010665076.1 | Jul 2020 | CN | national |