Claims
- 1. A process for continuously coating a continuous porous substrate to prepare a composite filtration membrane comprising:
- providing a first liquid component;
- providing a first applicator means for applying the first liquid component onto the substrate, wherein said first applicator means comprises a slot die head or a direct gravure applicator;
- applying a quantitative amount of the first component onto the substrate to coat the substrate and form a liquid layer by relatively moving the substrate and the first applicator with respect to each other at a speed of between 20 and 200 feet per minute;
- providing a second liquid component;
- providing a second applicator means in tandem with the first applicator means for applying the second liquid component, wherein said second applicator means comprises a slot die head;
- applying a quantitative amount of the second liquid component onto the liquid layer to contact the second liquid component with the liquid layer by relatively moving the substrate coated with the liquid layer and the second applicator with respect to each other;
- allowing the first and second liquid component to interfacially polymerize to form a composite layer of a thickness of between about 25 .ANG. and 1 micron; and
- drying the composite layer to form a composite membrane.
- 2. The process as set forth in claim 1, wherein the relative movement of the substrate and the applicators comprises moving the substrate under the first applicator and the second applicator.
- 3. The process as set forth in claim 1, wherein the substrate comprises an asymmetrical microporous polymer supported by a carrier web.
- 4. The process as set forth in claim 1, wherein the composite membrane comprises a reverse osmosis membrane.
- 5. The process as set forth in claim 4, wherein the first liquid component comprises an aqueous solution of a first reactant in water.
- 6. The process as set forth in claim 5, wherein the first reactant comprises metaphenylenediamine.
- 7. The process as set forth in claim 5, wherein the aqueous solution further comprises a surfactant.
- 8. The process as set forth in claim 4, wherein the second liquid component comprises an organic solution.
- 9. The process as set forth in claim 8, wherein the organic solution comprises a second reactant and a co-solvent.
- 10. The process as set forth in claim 9, wherein the second reactant is selected from the group comprising trimesyol chloride, cyanuric chloride, bischloromethylpyridine, and modified trianzyl moieties.
- 11. The process as set forth in claim 9, wherein the co-solvent comprises a hydrocarbon solvent and a high boiling point solvent.
- 12. The process as set forth in claim 4, wherein the first liquid component comprises an aqueous solution of a first reactant in water, and the second liquid component comprises an organic solution of a second reactant and a co-solvent.
- 13. The process as set forth in claim 12, wherein the molar ratio of the first reactant to the second reactant is stoichiometric.
- 14. The process as set forth in claim 12, wherein the first reactant comprises metaphenylenediamine, and the second reactant comprises trimesyol chloride.
- 15. The process as set forth in claim 14, wherein the molar ratio of the first reactant to the second reactant is about 3 to 2.
- 16. The process as set forth in claim 1, wherein the composite membrane comprises a nanofiltration membrane.
- 17. The process as set forth in claim 16, wherein the first liquid component comprises an aqueous solution of a first reactant in water.
- 18. The process as set forth in claim 17, wherein the first reactant comprises poly(ethyleneimine) with a weight average molecular weight of about 60,000.
- 19. The process as set forth in claim 17, wherein the aqueous solution further comprises a surfactant.
- 20. The process as set forth in claim 16, wherein the second liquid component comprises an organic solution.
- 21. The process as set forth in claim 20, wherein the organic solution comprises a second reactant and a co-solvent.
- 22. The process as set forth in claim 21, wherein the second reactant possesses a nucleophilic site or sites capable of reacting to molecules, the second reactant selected from the group comprising cyanuric chloride, chlorinated pyridine, chlorinated pyrimidines, and modified trianzyl moieties.
- 23. The process as set forth in claim 16, wherein the first liquid component comprises an aqueous solution of a first reactant in water, and the second liquid component comprises an organic solution of a second reactant and a solvent.
- 24. The process as set forth in claim 23, wherein the molar ratio of the first reactant to the second reactant is stoichiometric.
- 25. The process as set forth in claim 23, wherein the first reactant comprises poly(ethyleneimine) and the second reactant comprises cyanuric chloride.
CROSS-REFERENCE TO RELATED APPLICATION
This application is entitled to priority pursuant to provisional application Ser. No. 60/048,954, filed Jun. 6, 1997, entitled Filtration Membrane.
US Referenced Citations (17)
Non-Patent Literature Citations (1)
Entry |
Modern Coating and Drying Technology, by Edward D. Cohen and Edgar B. Gutoff (No date). |