Claims
- 1. A process for preparing an ionomer assisted electrode structure for use in an electrolysis cell, wherein said electrode structure comprises a hydrated ion exchange membrane having a first surface and a second surface and at least one catalyst ionomer layer, wherein said catalyst ionomer layer comprises hydrated and swollen ionomer solids bonded to discrete catalyst particles, wherein said catalyst ionomer layer is bonded to at least said first surface of said hydrated ion exchange membrane, and wherein said process comprises the steps of:
- a. forming an aqueous solution comprising from about 0.10 to about 20% by weight swollen ionomer solids and from about 0.15 to about 30% by weight catalyst, based on the total weight of said aqueous solution;
- b. heating said solution to a temperature of from about 40.degree. C. to about 110.degree. C. until a dry powder residue remains;
- c. forming a homogeneous solid paste comprising a quantity of said dry powder residue and a quantity of a fast drying or subliming agent;
- d. pressing said homogeneous solid paste onto at least said first surface of said ion exchange membrane at a temperature of from about 121.degree. C. to about 232.degree. C. and at a pressure of from about 2.1 to about 27.6 MPa;
- e. optionally repeating steps (a) through (d) wherein said homogeneous solid paste is pressed onto said second surface of said ion exchange membrane; and
- f. rehydrating said ion exchange membrane and said ionomer solids of said homogeneous solid paste.
- 2. The process for preparing an ionomer assisted electrode structure of claim 1 which further comprises the steps of:
- a. acid rinsing said ion exchange membrane and said catalyst ionomer layer or layers of said electrode structure to remove cation impurities;
- b. rinsing said acid rinsed ion exchange membrane and said catalyst ionomer layer or layers of said electrode structure with deionized water; and
- c. rehydrating said ion exchange membrane and said catalyst ionomer layer or layers of said electrode structure.
- 3. The process for preparing an ionomer assisted electrode structure of claim 1 wherein the step of forming an aqueous solution comprises the steps of:
- a. mixing a quantity of ionomer solids with a mixture comprising water and alcohol to form an ionomer solids mixture;
- b. forming a layered ionomer solids mixture having at least a first layer comprising swollen ionomer solids, water, residual alcohol and organics and a second layer by subjecting said mixture to temperatures of from about 275.degree. C. to about 300.degree. C. and to pressures of from about 6.9 to about 13.8 MPa for at least 30 minutes;
- c. decanting a volume of said first layer of said layered ionomer solids mixture;
- d. diluting said volume of said first layer with deionized water;
- e. reducing said volume of said first layer at least by 50%; and
- f. optionally adjusting said volume of said first layer to obtain a first layer having a total ionomer solids content of from about 0.10 to about 20% by weight, based on the total weight of said volume of said first layer.
- 4. The process for preparing an ionomer assisted electrode structure of claims 1 or 2 wherein the rehydrating step comprises heating said electrode structure in deionized water to a temperature of from about 90.degree. C. to about 110.degree. C. for from about 15 minutes to about 3 hours.
- 5. The process for preparing an ionomer assisted electrode structure of claim 1 wherein the step of forming a solid paste further includes the step of: passing said dry powder residue through a screen having an average mesh size of from about 100 to about 400.
Parent Case Info
This is a division of application Ser. No. 08/188,487, field on Jan. 28, 1994, now U.S. Pat. No. 5,470,448.
US Referenced Citations (1)
Number |
Name |
Date |
Kind |
5266177 |
Watanabe et al. |
Nov 1993 |
|
Foreign Referenced Citations (3)
Number |
Date |
Country |
0631337A2 |
Jun 1994 |
EPX |
2549083 |
May 1977 |
DEX |
54-110435 |
Aug 1979 |
JPX |
Non-Patent Literature Citations (3)
Entry |
Abstract of DE 2549083 (H. Meier) May 5, 1977. |
Abstract of JP 54110435 (Hiroshi et al.) Aug. 29, 1979. |
Bibliographic data for JP 54110435 (Hiroshi et al.) Aug. 29, 1979. |
Divisions (1)
|
Number |
Date |
Country |
Parent |
188487 |
Jan 1994 |
|