Patent Grant
10590027
This application is the U.S. national phase of PCT Application No. PCT/CN2016/076885, filed on Mar. 21, 2016, which claims the priority to Chinese Patent Application No. 201610146263.2 filed Mar. 15, 2016, the disclosures of which are incorporated herein by reference in their entireties.
The present invention relates to a glass fiber, a composition for producing the same, and a composite material comprising the same.
Glass fiber is an inorganic fiber material that can be used to reinforce resins to produce composite materials with good performance. As a reinforcing base material for advanced composite materials, high-performance glass fibers were originally used mainly in the aerospace industry or the national defense industry. With the progress of science and technology and the development of economy, high-performance glass fibers have been widely used in civil and industrial fields such as wind blades, pressure vessels, offshore oil pipes and auto industry.
The original high-performance glass compositions were based on an MgO—Al2O3—SiO2 system and a typical solution was S-2 glass of American company OC. The modulus of S-2 glass is 89-90 GPa; however, the production of this glass is excessively difficult, as its forming temperature is up to about 1571° C. and its liquidus temperature up to 1470° C. and therefore it is difficult to realize large-scale industrial production. Thus, OC stopped production of S-2 glass fiber and transferred its patent to American company AGY.
Thereafter, OC developed HiPer-tex glass having a modulus of 87-89 GP, which were a trade-off for production scale by sacrificing some of the glass properties. However, as the design solution of HiPer-tex glass was just a simple improvement over that of S-2 glass, the forming temperature and liquidus temperature remained high, which causes difficulty in attenuating glass fiber and consequently in realizing large-scale industrial production. Therefore, OC also stopped production of HiPer-tex glass fiber and transferred its patent to the European company 3B.
French company Saint-Gobain developed R glass that is based on an MgO—CaO—Al2O3—SiO2 system, and its modulus is 86-89 GPa; however, the total contents of SiO2 and Al2O3 remain high in the traditional R glass, and there is no effective solution to improve the crystallization performance, as the ratio of Ca to Mg is inappropriately designed, thus causing difficulty in fiber formation as well as a great risk of crystallization, high surface tension and fining difficulty of molten glass. The forming temperature of the R glass reaches 1410° C. and its liquidus temperature up to 1350° C. All these have caused difficulty in effectively attenuating glass fiber and consequently in realizing large-scale industrial production.
In China, Nanjing Fiberglass Research & Design Institute developed an HS2 glass having a modulus of 84-87 GPa. It primarily contains SiO2, Al2O3 and MgO while also including certain amounts of Li2O, B2O3, CeO2 and Fe2O3. Its forming temperature is only 1245° C. and its liquidus temperature is 1320° C. Both temperatures are much lower than those of S glass. However, since its forming temperature is lower than its liquidus temperature, which is unfavorable for the control of glass fiber attenuation, the forming temperature has to be increased and specially-shaped tips have to be used to prevent a glass crystallization phenomenon from occurring in the fiber attenuation process. This causes difficulty in temperature control and also makes it difficult to realize large-scale industrial production.
To sum up, we find that, at present stage, the actual production of various high-performance glass fibers generally faces the difficulty of large-scale production with refractory-lined furnaces, specifically manifested by relatively high liquidus temperature, high rate of crystallization, relatively high forming temperature, refining difficulty of molten glass and a narrow temperature range (ΔT) for fiber formation and even a negative ΔT value. Therefore, most companies tend to reduce the production difficulty by compromising some of the glass properties, thus making it impossible to improve the strength and modulus of the above-mentioned glass fibers with the growth of production scale.
It is one objective of the present disclosure to provide a composition for producing a glass fiber. The resulting glass fiber has greatly increased mechanical properties and thermal stability; also, the composition for producing a glass fiber significantly lowers the liquidus and forming temperatures, crystallization rate and refining difficulties of the glass.
The composition according to the present invention is particularly suitable for large-scale production of glass fiber having excellent thermal stability with refractory-lined furnaces.
To achieve the above objective, in accordance with one embodiment of the present disclosure, there is provided a composition for producing glass fiber, the composition comprising percentage amounts by weight, as follows:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is greater than 0.01.
In a class of this embodiment, the content range of Li2O is 0.1-1.5% in percentage amounts by weight.
In a class of this embodiment, the composition contains Y2O3 in a content of 0.05-5% in percentage amounts by weight.
In a class of this embodiment, the composition contains La2O3 in a content of 0.05-3% in percentage amounts by weight.
In a class of this embodiment, the total weight percentage of SiO2+Al2O3 is less than 82%.
In a class of this embodiment, the total weight percentage of SiO2+Al2O3 is 70-81%.
In a class of this embodiment, the content range of MgO is 6-12% in percentage amounts by weight.
In a class of this embodiment, the content range of Sm2O3 is 0.05-3% in percentage amounts by weight.
In a class of this embodiment, the content range of Gd2O3 is 0.05-2% in percentage amounts by weight.
In a class of this embodiment, the total weight percentage of Sm2O3+Gd2O3 is 0.1-4%.
In a class of this embodiment, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is greater than or equal to 0.02.
In a class of this embodiment, the composition comprises the following components expressed as percentage amounts by weight:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is greater than 0.01.
In a class of this embodiment, the composition comprises the following components expressed as percentage amounts by weight:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is greater than 0.01.
In a class of this embodiment, the composition comprises the following components expressed as percentage amounts by weight:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is greater than 0.01.
In a class of this embodiment, the composition comprises the following components expressed as percentage amounts by weight:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is greater than or equal to 0.02.
In a class of this embodiment, the composition comprises the following components expressed as percentage amounts by weight:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is greater than 0.01.
In a class of this embodiment, the composition comprises the following components expressed as percentage amounts by weight:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is greater than 0.01.
In a class of this embodiment, the content range of SrO is 0.1-2% in percentage amounts by weight.
In a class of this embodiment, the range of the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is 0.02-0.15.
In a class of this embodiment, the range of the weight percentage ratio C2=Y2O3(Sm2O3+Gd2O3+Y2O3) is greater than 0.4.
In a class of this embodiment, the total weight percentage of Gd2O3+La2O3 is 0.5-1.5%.
In a class of this embodiment, the total weight percentage of Gd2O3+La2O3+TiO2 is 1-3.5%.
In a class of this embodiment, the composition contains CeO2 in a content of 0-1% in percentage amounts by weight.
According to another aspect of this invention, a glass fiber produced with the composition for producing a glass fiber is provided.
According to yet another aspect of this invention, a composite material incorporating the glass fiber is provided.
The main inventive points of the composition for producing a glass fiber according to this invention include: introducing the rare earth oxides Sm2O3 and Gd2O3 so as to utilize the high accumulation effect and good synergistic effect between these two ions that have small radiuses and high field strength, controlling the ratio of (Li2O+Sm2O3+Gd2O3)/Al2O3, reasonably configuring the content ranges of Sm2O3, Gd2O3, Li2O, Al2O3, CaO, MgO and CaO+MgO+SrO respectively, utilizing the mixed alkali earth effect of CaO, MgO and SrO, and selectively introducing Y2O3, La2O3 and CeO2 at appropriate amounts.
Specifically, the composition for producing a glass fiber according to the present invention comprises the following components expressed as percentage amounts by weight:
The effect and content of each component in the composition for producing a glass fiber is described as follows:
SiO2 is a main oxide forming the glass network and has the effect of stabilizing all the components. In the composition for producing a glass fiber of the present invention, the content range of SiO2 is 52-67%. Preferably, the SiO2 content range can be 54-64%, and more preferably can be 54-62%.
Al2O3 is another main oxide forming the glass network. When combined with SiO2, it can have a substantive effect on the mechanical properties and thermal stability of the glass. Too low of an Al2O3 content will make it impossible to obtain sufficiently high mechanical properties and thermal stability; too high of a content will significantly increase the viscosity of glass, thereby causing refining difficulties and high crystallization risks. In the composition for producing a glass fiber of the present invention, the content range of Al2O3 is 12-24%. Preferably, the Al2O3 content can be 13-23%, and more preferably can be 13-22%.
In a glass system, Al2O3 is typically present in two forms, i.e., the four-coordinated [AlO4] and the six-coordinated [AlO6]. In the composition for producing a glass fiber of the present invention, the rare earth oxides Sm2O3 and/or Gd2O3 can be introduced. In accordance with the lanthanide contraction effect, on the one hand, these two oxides have high alkalinity and can provide considerable non-bridging oxygen, which helps to produce more four-coordinated [AlO4] in the glass structure and is thus advantageous for Al3+ ions to enter the glass network so as to strengthen the compactness of the glass; and, on the other hand, with small ionic radiuses, high electric charges and high field strength, the Sm3+ and Gd3+ ions are usually present as external ions at the gaps of the glass network, and they have a strong accumulation effect on anions, further strengthening the structural stability of glass and increasing the mechanical properties and thermal stability of glass.
Meanwhile, under such strong accumulation effect, the movement and rearrangement of other ions will be effectively inhibited, so that the thermal stability of glass can be improved and the glass crystallization tendency can be reduced. Furthermore, with similar ionic radiuses and coordination states, the Sm3+ and Gd3+ ions can have a good synergistic effect and an excellent result can be achieved by using the two ions simultaneously. Therefore, in the composition for producing a glass fiber of the present invention, the combined weight percentage of Sm2O3+Gd2O3 can be 0.05-4.5%, and preferably can be 0.1-4%. Further, the Sm2O3 content can be 0.05-3%. Further, the Gd2O3 content can be 0.05-2%. In addition, the combined weight percentage of SiO2+Al2O3 can be less than 82%, and preferably can be 70-81%.
Both K2O and Na2O can reduce glass viscosity and are good fluxing agents. Compared with Na2O and K2O, Li2O can not only significantly reduce glass viscosity thereby improving the glass melting performance, but also obviously help improve the mechanical properties of glass. In addition, a small amount of Li2O provides considerable free oxygen, which helps more aluminum ions to form tetrahedral coordination and enhances the network structure of the glass. However, as too many alkali metal ions in the glass composition would affect the thermal and chemical stabilities of the glass, the introduced amount should be limited. Therefore, in the composition for producing a glass fiber of the present invention, the total content range of Li2O+Na2O+K2O is lower than 2%. Further, the content range of Li2O is 0.1-1.5%.
In addition, in order to help more aluminum ions to enter the glass network to form tetrahedral coordination, in the composition for producing a glass fiber of the present invention, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 can be greater than 0.01, preferably can be greater than or equal to 0.02, and more preferably can be 0.02-0.15.
Further, the rare earth oxides Y2O3 and La2O3 can be selectively introduced to the glass fiber composition of this invention. As the coordination states, ionic radiuses and field strength of Y3+ and La3+ ions are different from those of Sm3+ and Gd3+, when used simultaneously, these four ions could offer the following advantages: (1) more coordination states of the ions outside the glass network would be produced, which helps to enhance the structural stability of the glass; (2) the hexa-coordination of yttrium ions assisted by the octahedron of other ions would further enhance the structural integrity and modulus of the glass; and (3) it would be less likely for the ions to form regular arrangements at lowered temperatures, which help to reduce the growth rate of crystal phases and thus further increase the resistance to glass crystallization. However, compared with Sm2O3 and Gd2O3, Y2O3 and La2O3 are weak alkalines and, when used in a large amount, alkali metal oxides would be needed to provide a certain amount of free oxygen for filling in the vacancies. Therefore, in the composition for producing a glass fiber of the present invention, the weight percentage of Y2O3 can be 0.05-5% and the weight percentage of La2O3 can be 0.05-3%. In order to increase the mechanical properties of the glass, the weight percentage ratio C2=Y2O3/(Sm2O3+Gd2O3+Y2O3) can be greater than 0.4. The inventors also find that the use of gadolinium oxide in combination with lanthanum oxide would play a significant role in improving the thermal stability of the glass. Further, the combined weight percentage of Gd2O3+La2O3 can be 0.5-1.5%.
CaO, MgO and SrO primarily have the effect of controlling the glass crystallization and regulating the glass viscosity. Particularly on the control of the glass crystallization, the inventors have obtained unexpected effects by controlling the introduced amounts of them and the ratios between them. Generally, for a high-performance glass based on the MgO—CaO—Al2O3—SiO2 system, the crystal phases it contains after glass crystallization include mainly diopside (CaMgSi2O6) and anorthite (CaAl2Si2O3). In order to effectively inhibit the tendency for these two crystal phases to crystallize and decrease the glass liquidus temperature and the rate of crystallization, this invention has rationally controlled the total content of CaO+MgO+SrO and the ratios between them and utilized the mixed alkali earth effect to form a compact stacking structure, so that more energy are needed for the crystal nucleases to form and grow. In this way, the glass crystallization tendency is inhibited. Further, a glass system containing strontium oxide has more stable glass structure, thus improving the glass properties. In the composition for producing a glass fiber of the present invention, the range of the total content of CaO+MgO+SrO can be 10-24%. As a network modifier, too much CaO would increase the crystallization tendency of the glass that lead to the precipitation of crystals such as anorthite and wollastonite from the glass melt. Therefore, the content range of CaO in this invention can be less than 16%, and preferably less than 14%. MgO has the similar effect in the glass network as CaO, yet the field strength of Mg2+ is higher, which plays an important role in increasing the glass modulus. In the composition for producing a glass fiber of the present invention, the content range of MgO can be less than 13%, and preferably can be 6-12%. Further, the content range of SrO can be less than 3%, and preferably can be 0.1-2%.
TiO2 has not only a certain fluxing effect, but also can significantly enhance the thermal and chemical stabilities of the glass. The inventors have found that the thermal stability of the glass would be greatly increased as a result of the use of TiO2 in combination with gadolinium oxide and lanthanum oxide. However, since an excessive amount of Ti4+ ions could have a certain coloring effect on the glass, the introduced amount should be limited. Therefore, in the composition for producing a glass fiber of the present invention, the content range of TiO2 is lower than 3%. Further, the total content range of Gd2O3+La2O3+TiO2 can be 1-3.5%.
Fe2O3 facilitates the melting of glass and can also improve the crystallization performance of glass. However, since ferric ions and ferrous ions have a coloring effect, the introduced amount should be limited. Therefore, in the composition for producing a glass fiber of the present invention, the content range of Fe2O3 can be less than 1.5%.
In the composition for producing a glass fiber of the present invention, an appropriate amount of CeO2 can be selectively introduced to further improve the glass crystallization and refining performance. In the composition for producing a glass fiber of the present invention, the CeO2 content can be 0-1%.
In addition, the composition for producing a glass fiber of the present invention can include small amounts of other components with a total content not greater than 2%.
In the composition for producing a glass fiber of the present invention, the beneficial effects produced by the aforementioned selected ranges of the components will be explained by way of examples through the specific experimental data.
The following are examples of preferred content ranges of the components contained in the composition for producing a glass fiber according to the present invention, wherein the glass fiber obtained therefrom has an elastic modulus greater than 90 GPa.
Composition 1
The composition for producing a high performance glass fiber according to the present invention comprises the following components expressed as percentage amounts by weight:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is greater than 0.01.
Composition 2
The composition for producing a high performance glass fiber according to the present invention comprises the following components expressed as percentage amounts by weight:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is greater than 0.01.
Composition 3
The composition for producing a high performance glass fiber according to the present invention comprises the following components expressed as percentage amounts by weight:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is greater than 0.01.
Composition 4
The composition for producing a high performance glass fiber according to the present invention comprises the following components expressed as percentage amounts by weight:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is greater than or equal to 0.02.
Composition 5
The composition for producing a high performance glass fiber according to the present invention comprises the following components expressed as percentage amounts by weight:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is greater than 0.01.
Composition 6
The composition for producing a high performance glass fiber according to the present invention comprises the following components expressed as percentage amounts by weight:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is greater than 0.01.
Composition 7
The composition for producing a high performance glass fiber according to the present invention comprises the following components expressed as percentage amounts by weight:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is greater than 0.01.
Composition 8
The composition for producing a high performance glass fiber according to the present invention comprises the following components expressed as percentage amounts by weight:
In addition, the range of the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is 0.02-0.15.
Composition 9
The composition for producing a high performance glass fiber according to the present invention comprises the following components expressed as percentage amounts by weight:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is greater than 0.01, and the weight percentage ratio C2=Y2O3/(Sm2O3+Gd2O3+Y2O3) is greater than 0.4.
The glass fiber made from a composition according to composition 9 has an elastic modulus of greater than 95 GPa.
Composition 10
The composition for producing a high performance glass fiber according to the present invention comprises the following components expressed as percentage amounts by weight:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is greater than 0.01
Composition 11
The composition for producing a high performance glass fiber according to the present invention comprises the following components expressed as percentage amounts by weight:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is greater than 0.01
In order to better clarify the purposes, technical solutions and advantages of the examples of the present invention, the technical solutions in the examples of the present invention are clearly and completely described below. Obviously, the examples described herein are just part of the examples of the present invention and are not all the examples. All other exemplary embodiments obtained by one skilled in the art on the basis of the examples in the present invention without performing creative work shall all fall into the scope of protection of the present invention. What needs to be made clear is that, as long as there is no conflict, the examples and the features of examples in the present application can be arbitrarily combined with each other.
The basic concept of the present invention is that the components of the composition for producing a glass fiber expressed as percentage amounts by weight are: 52-67% of SiO2, 12-24% of Al2O3, 0.05-4.5% of Sm2O3+Gd2O3, less than 2% of Li2O+Na2O+K2O, 10-24% of CaO+MgO+SrO, less than 16% of CaO, less than 13% of MgO, less than 3% of TiO2, and less than 1.5% of Fe2O3. The composition can not only greatly increase the mechanical properties and thermal stability of the glass, but also significantly lower the glass liquidus and forming temperatures and crystallization rate of the glass under equal conditions, which make it particularly suitable for the production of high-performance glass fiber having excellent thermal stability with refractory-lined furnaces.
The specific content values of SiO2, Al2O3, Sm2O3, Gd2O3, Y2O3, La2O3, CaO, MgO, Li2O, Na2O, K2O, Fe2O3, TiO2 and SrO in the composition for producing a glass fiber of the present invention are selected to be used in the examples, and comparisons with S glass, traditional R glass and improved R glass are made in terms of the following six property parameters,
The aforementioned six parameters and the methods of measuring them are well-known to one skilled in the art. Therefore, these parameters can be effectively used to explain the properties of the glass fiber composition of the present invention.
The specific procedures for the experiments are as follows: Each component can be acquired from the appropriate raw materials. Mix the raw materials in the appropriate proportions so that each component reaches the final expected weight percentage. The mixed batch melts and the molten glass refines. Then the molten glass is drawn out through the tips of the bushings, thereby forming the glass fiber. The glass fiber is attenuated onto the rotary collet of a winder to form cakes or packages. Of course, conventional methods can be used to deep process these glass fibers to meet the expected requirements.
The exemplary embodiments of the glass fiber composition according to the present invention are given below.
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is 0.09.
In Example 1, the measured values of the six parameters are respectively:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is 0.053.
In Example 2, the measured values of the six parameters are respectively:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is 0.141.
In Example 3, the measured values of the six parameters are respectively:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is 0.059, and the weight percentage ratio C2=Y2O3/(Sm2O3+Gd2O3+Y2O3) is 0.88.
In Example 4, the measured values of the six parameters are respectively:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is 0.071.
In Example 5, the measured values of the six parameters are respectively:
In addition, the weight percentage ratio C1=(Li2O+Sm2O3+Gd2O3)/Al2O3 is 0.053.
In Example 6, the measured values of the six parameters are respectively:
Comparisons of the property parameters of the aforementioned examples and other examples of the glass fiber composition of the present invention with those of the S glass, traditional R glass and improved R glass are further made below by way of tables, wherein the component contents of the glass fiber composition are expressed as weight percentage. What needs to be made clear is that the total amount of the components in the examples is slightly less than 100%, and it should be understood that the remaining amount is trace impurities or a small amount of components which cannot be analyzed.
It can be seen from the values in the above tables that, compared with the S glass and traditional R glass, the glass fiber composition of the present invention has the following advantages: (1) much higher elastic modulus; (2) much lower liquidus temperature, which helps to reduce crystallization risk and increase the fiber drawing efficiency; relatively high peak crystallization temperature, which indicates that more energy is needed for the formation and growth of crystal nucleuses during the crystallization process of glass, i.e. the crystallization risk of the glass of the present invention is smaller under equal conditions.
At the same time, compared with the improved R glass, the glass fiber composition of the present invention has the following advantages: (1) much higher elastic modulus; (2) relatively high peak crystallization temperature, which indicates that more energy is needed for the formation and growth of crystal nucleuses during the crystallization process of glass, i.e. the crystallization risk of the glass of the present invention is smaller under equal conditions; and lower liquidus temperature, which helps to reduce crystallization risk and increase the fiber drawing efficiency; (3) significantly increased softening temperature, which means the thermal stability of the glass has been significantly improved.
Both S glass and traditional R glass cannot enable the achievement of large-scale production with refractory-lined furnaces and, with respect to improved R glass, part of the glass properties is compromised to reduce the liquidus temperature and forming temperature, so that the production difficulty is decreased and the production with refractory-lined furnaces could be achieved. By contrast, the glass fiber composition of the present invention not only has a sufficiently low liquidus temperature and crystallization rate which permit the production with refractory-lined furnaces, but also significantly increases the glass modulus, thereby resolving the technical bottleneck that the modulus of S glass fiber and R glass fiber cannot be improved with the growth of production scale.
The composition for producing a glass fiber according to the present invention can be used for making glass fibers having the aforementioned properties.
The composition for producing a glass fiber according to the present invention in combination with one or more organic and/or inorganic materials can be used for preparing composite materials having improved characteristics, such as glass fiber reinforced base materials.
Finally, what should be made clear is that, in this text, the terms “contain”, “comprise” or any other variants are intended to mean “nonexclusively include” so that any process, method, article or equipment that contains a series of factors shall include not only such factors, but also include other factors that are not explicitly listed, or also include intrinsic factors of such process, method, object or equipment. Without more limitations, factors defined by such phrase as “contain a . . . ” do not rule out that there are other same factors in the process, method, article or equipment which include said factors.
The above examples are provided only for the purpose of illustrating instead of limiting the technical solutions of the present invention. Although the present invention is described in details by way of aforementioned examples, one skilled in the art shall understand that modifications can also be made to the technical solutions embodied by all the aforementioned examples or equivalent replacement can be made to some of the technical features. However, such modifications or replacements will not cause the resulting technical solutions to substantially deviate from the spirits and ranges of the technical solutions respectively embodied by all the examples of the present invention.
The composition for producing a glass fiber of the present invention not only has a sufficiently low liquidus temperature and crystallization rate which enable the production with refractory-lined furnaces, but also significantly increases the glass modulus, thereby resolving the technical bottleneck that the modulus of S glass fiber and R glass fiber cannot be improved with the enhanced production scale. Compared with the current main-stream high-performance glasses, the glass fiber composition of the present invention has made a breakthrough in terms of elastic modulus, crystallization performance and thermal stability of the glass, with significantly improved modulus, remarkably reduced crystallization risk and improved thermal stability under equal conditions. Thus, the overall technical solution of the present invention is particularly suitable for the tank furnace production of a high performance glass fiber having excellent thermal stability
| Number | Date | Country | Kind |
|---|---|---|---|
| 201610146263 | Mar 2016 | CN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2016/076885 | 3/21/2016 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2016/165531 | 10/20/2016 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20070158317 | Brix et al. | Jul 2007 | A1 |
| 20150018194 | Li et al. | Jan 2015 | A1 |
| 20160068428 | Li et al. | Mar 2016 | A1 |
| 20160152514 | Li et al. | Jun 2016 | A1 |
| 20180118608 | Zhang et al. | May 2018 | A1 |
| 20180179104 | Zhang | Jun 2018 | A1 |
| 20190100453 | Zhang | Apr 2019 | A1 |
| Number | Date | Country |
|---|---|---|
| 103086605 | May 2013 | CN |
| 105016622 | Nov 2015 | CN |
| 105392744 | Mar 2016 | CN |
| 105693100 | Jun 2016 | CN |
| 3406576 | Nov 2018 | EP |
| 3415474 | Dec 2018 | EP |
| S60141642 | Jul 1985 | JP |
| 2007015915 | Jan 2007 | JP |
| 2011011933 | Jan 2011 | JP |
| 1273339 | Nov 1986 | SU |
| Entry |
|---|
| Derwent Abstract 1987-211948, 1987 (Year: 1987). |
| From PCT/CN2016/076885, Written Opinion of the International Searching Authority, dated Dec. 6, 2016, with English translation from WIPO. |
| From PCT/CN2016/076885, International Preliminary Report on Patentability, dated Sep. 18, 2018, with English translation from WIPO. |
| From CN 2016101462632, First Office Action and Search Report, dated Nov. 17, 2017, with machine English translation from Global Dossier. |
| International Search Report for PCT/CN2016/076885, dated Dec. 6, 2016, and its English translation provided by WIPO. |
| Written Opinion of the International Search Authority for PCT/CN2016/076885, dated Dec. 6, 2016 and its English translation provided by Bing.com Microsoft Translator. |
| Extended European Search Report from EP app. No. 16779506.1, dated Feb. 13, 2019. |
| Notice of Reasons for Refusal from JP app. No. 2018548181, dated Aug. 20, 2019, with English translation from Global Dossier. |
| Number | Date | Country | |
|---|---|---|---|
| 20190077699 A1 | Mar 2019 | US |