Patent Application
20190106598
The present disclosure relates to a ski wax composition including superhydrophobic carbon nano particles (CNPs) and a preparation method thereof. More particularly, the present disclosure relates to a ski wax composition including a wax and superhydrophobic CNPs and a preparation method thereof.
Skiing is one of representative winter sports and is becoming more and more common all over the world, and the number of people enjoying skiing is on a dramatically increasing trend. In order to increase a running speed in skiing by reducing a frictional force on an ice surface or a snow surface, ski waxes are used. To reduce friction on the ice or snow surface, ski waxes have been developed to have hydrophobicity. It is known that the higher the surface roughness, the greater the hydrophobicity and the lower the frictional forces on the ice or snow surface.
Methods of preparing ski waxes having increased hydrophobicity by mixing a fluorine resin, such as polytetrafluoroethylene (PTFE), molybdenum disulphide, gallium, indium, titanium oxide, and carbon nanoparticles, such as fullerene or diamond nano particles, have been used (Japanese Laid-Open Publication No. 2013-117016). However, it is relatively difficult to produce fullerene or diamond nano particles, and undesired particle agglomeration may occur, making it difficult to disperse the particles into a wax. Thus, a separate surfactant, such as isopropyl alcohol, should be inevitably added. However, hydrophobicity of a wax surface may decrease due to the added surfactant, resulting in degradation of the overall performance.
Accordingly, the present inventors have made extensive efforts to develop a ski wax composition having maximized hydrophobicity to provide superb friction reducing performance and having increased productivity, and as a result, have found that the productivity can be improved and noticeably excellent friction reducing performance is exhibited when superhydrophobic CNPs are added, thereby completing the present disclosure.
It is an object of the present disclosure to provide a ski wax composition including a wax and superhydrophobic carbon nano particles (CNPs).
It is another object of the present disclosure to provide a preparation of a ski wax composition including (a) adding superhydrophobic CNPs to a wax, and (b) performing sonication.
In accordance with an aspect of the present disclosure, the above and other objects can be accomplished by providing a ski wax composition including a wax and superhydrophobic carbon nano particles (CNPs).
In addition, in accordance with another aspect of the present disclosure, the above and other objects can be accomplished by providing a preparation of a ski wax composition including (a) adding superhydrophobic CNPs to a wax, and (b) performing sonication.
As described above, according to the ski wax composition including superhydrophobic CNPs of the present disclosure, and the preparation method thereof, the hydrophobicity and retention capacity of the wax can be increased, thereby maximizing friction reducing performance of a ski wax on an ice surface or a snow surface. In addition, since the superhydrophobic CNPs, which can be easily prepared, are used, the productivity of the ski wax composition can be improved and superb friction reducing performance can be exhibited. Further, since the superhydrophobic CNPs are dispersed into the wax by a simple sonication process, a problem caused by adding a surfactant can be solved. Therefore, the ski wax composition according to the present disclosure can be widely applied to industrial fields associated with the winter sports, including skiing.
Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art. Generally, the nomenclature used herein is method well known and commonly employed in the art.
The present disclosure relates a ski wax composition, and a preparation method thereof, which can improve the hydrophobicity and retention capacity of the wax can be increased by adding superhydrophobic CNPs to the wax, thereby maximizing friction reducing performance of a ski wax on an ice surface or a snow surface (
The “superhydrophobic carbon nano particles” used herein specifically refer to carbon or hydrocarbon particles having superhydrophobicity. The superhydrophobic carbon nano particles are preferably diamond like carbon (DLC) nano particles, which may be prepared by glow discharging C2H2 under a high pressure. The DLC nano particles have a diameter in the range of 30 to 50 nm and a contact angle of approximately 128° (Dai, Wei, et al., “Porous carbon nanoparticle networks with tunable absorbability”, Scientific reports 3 (2013): 2524).
In one aspect, the present disclosure relates to a ski wax composition including a wax and superhydrophobic carbon nano particles (CNPs) (DLC nano particles).
In the present disclosure, the ski wax composition may further include a wax additive.
In the present disclosure, the superhydrophobic CNPs are contained in the ski wax composition preferably in an amount of 0.5 to 10% by weight, more preferably in an amount of 2.5% by weight. If the amount of the superhydrophobic CNPs is less than 0.5% by weight, a friction reducing effect is negligibly low. If the amount of the superhydrophobic CNPs is greater than 10% by weight, a noticeable change in the friction reducing effect is not exhibited, suggesting that the cost effectiveness is lowered.
In the present disclosure, the wax may be alkane in a solid phase at room temperature, preferably C20-C60 alkane, and the wax additive may be fluoroalkane or perfluoroalkane, but not limited thereto (
In another aspect, the present disclosure relates to a preparation method of a ski wax composition comprising the steps of (a) adding superhydrophobic CNPs to a wax, and (b) performing sonication.
In the present disclosure, the step (a) may further include adding a wax additive.
In the present disclosure, the step (a) may include adding 0.5 to 10%, more preferably 2.5%, by weight of the superhydrophobic CNPs. If the amount of the superhydrophobic CNPs is less than 0.5% by weight, a friction reducing effect is negligibly low. If the amount of the superhydrophobic CNPs is greater than 10% by weight, a noticeable change in the friction reducing effect is not exhibited, suggesting that the cost effectiveness is lowered.
In the present disclosure, the wax in the step (a) may be alkane in a solid phase at room temperature, preferably C20-C60 alkane, and the wax additive in the step (a) may be fluoroalkane or perfluoroalkane (
Hereinafter, the present disclosure will be described in further detail with reference to examples. It will be obvious to a person having ordinary skill in the art that these examples are illustrative purposes only and are not to be construed to limit the scope of the present disclosure. Thus, the substantial scope of the present disclosure will be defined by the appended claims and equivalents thereof.
A ski wax composition was prepared by adding 0.5 to 10% by weight of DLC nano particles (Dai, Wei, et al., “Porous carbon nanoparticle networks with tunable absorbability”, Scientific reports 3 (2013): 2524) using a common wax (Racing mix wet, Holmenkol) as a base.
The common wax and the DLC nano particles were together transferred to a vessel and then hermetically sealed. Thereafter, the wax was heated in a water bath or melted in an oven maintained at a temperature of 120° C. to allow the DLC nano particles to be soaked into the wax. Then, boiled water was put into a sonicator, and the wax was taken out from the water bath or the oven to then be immediately transferred to the sonicator, followed by performing sonication for one minute. According to the kind of common wax used, the cycle of heating the wax in the water bath or the melting the wax in the oven and performing sonication was repeated once or twice. After cooling, the resultant product was taken out from the vessel, thereby completing the ski wax composition.
In order to confirm the friction reducing effect of the ski wax composition prepared in Example 1, two kinds of common waxes (i.e., Main Wax HF manufactured by Vola and Racing Mix Wet manufactured by Holmenkol) and the ski wax composition prepared in Example 1 (i.e., Wax+CNP) were compared and analyzed in terms of friction reducing performance.
Friction coefficients were measured using a rotary type friction tester (Micro Fluid Mechanics Laboratory, Seoul National University), and as a result, it was confirmed that the ski wax composition prepared in Example 1 (Wax+CNP), which contained DLC nano particles added in an amount of 5% by weight, showed an approximately 20% reduction in the friction coefficient, compared to the common waxes (
In addition, DLC nano particles in amounts of 0.6%, 1.2%, 2.5% and 5% by weight were added to paraffin waxes in the same manner as in Example 1, and appearances of the mixtures were observed (
Consequently, it was conformed that the CNPs exposed on the surface of the ski wax composition made adhesion with respect to the ice surface decreased, and rendered friction reducing performance.
Although the present disclosure has been described in detail with reference to the specific features, it will be apparent to those skilled in the art that this description is only for a preferred embodiment and does not limit the scope of the present disclosure. Thus, the substantial scope of the present disclosure will be defined by the appended claims and equivalents thereof.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2017-0039870 | Mar 2017 | KR | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/KR2017/004202 | 4/19/2017 | WO | 00 |