1. Field
Embodiments discussed herein relate to a method of making monolithic Zirconium Carbide (ZrC).
2. Description of the Related Art
Zirconium Carbide (ZrC) is a ceramic that is used as tool bits, as a coating layer for nuclear fuel, and in ultra-high temperature (e.g., 3500° C.) applications. The ceramic is also corrosion and water resistant. High density (i.e., greater than 90% of a theoretical density of the ZrC) and small grain sizes (i.e., 1 to 12 μm) are desirable traits for ZrC because these traits lead to good material hardness and mechanical strength. ZrC should have low levels of impurities and a stoichiometric ratio that is approximately ZrC1.0.
Related methods for making monolithic discs of ZrC include “sintering” and “hot press”, but these methods have limitations. For the hot press method to produce ZrC with 90% density, very high temperatures, i.e., 2200 to 2700° C., are required. Even when high temperatures are used, the produced ZrC has a relatively large grain size (16 to 120 μm). Sintering also requires high temperatures (2200 to 2700° C.) to create monolithic discs. The result is a monolithic disc of ZrC with relatively large grain size (20 to 65 μm) and low density (70 to 90%).
Both processes produce monolithic discs of ZrC with large grain sizes. Large grain sizes correspond to reduced material hardness and mechanical strength. Both processes require relatively high energy to meet the high temperature requirements.
In light of the foregoing, there is a need for a method of making monolithic ZrC having high density (i.e. above 90%) and small grain sizes (1 to 12 μm).
To solve the above problems, other problems, or both, it is an aspect of the described embodiments to provide a method of producing monolithic ZrC, including raising a pressure applied to a ZrC powder until a final pressure of greater than 40 MPa is reached; and raising a temperature of the ZrC powder until a final temperature of less than 2200° C. is reached.
To solve the above problems, other problems, or both, it is an aspect of the described embodiments to provide a method of producing monolithic ZrC, including raising a temperature of a ZrC powder to a temperature of less than 2200° C., a density of the monolithic ZrC being 96%-98% of a theoretical density.
To solve the above problems, other problems, or both, it is an aspect of the described embodiments to provide a method of producing monolithic ZrC, the ZrC having a grain size of less than 12 microns.
Additional aspects, advantages, or both will be set forth in part in the description which follows and in, in part, will be apparent from the description, or may be learned by practice thereof.
These or other aspects and advantages or both will become more readily appreciated from the following description of embodiments, taken in conjunction with the accompanying drawings in which:
Embodiments are described below, examples of which are illustrated in the accompanying drawings, wherein like reference numerals refer to the like elements throughout. Although a few embodiments have been shown and described, those skilled in the art will appreciate that changes may be made in these embodiments without departing from the principles and spirit of the embodiments, the scope of which is defined in the appended claims and their equivalents.
The resulting hot-pressed ZrC has relatively small grain sizes (1-12 microns), thereby resulting in improved strength and damage resistance. Also, the density of the resulting hot-pressed ZrC is 96%-98% of a theoretical density.
The resulting hot-pressed ZrC has relatively small grain sizes (1-12 microns), thereby resulting in improved strength and damage resistance. Also, the density of the resulting hot-pressed ZrC is 96%-98% of a theoretical density.
The resulting hot-pressed ZrC has relatively small grain sizes (1-12 microns), thereby resulting in improved strength and damage resistance. Also, the density of the resulting hot-pressed ZrC is 96%-98% of a theoretical density.
This invention was made with U.S. Government support under DE-AC11-98FN38206 awarded by the United States Department of Energy. The U.S. Government has certain rights in the invention.
Number | Date | Country | |
---|---|---|---|
61768840 | Feb 2013 | US |