1. Field
Embodiments discussed herein relate to a method of making monolithic Zirconium Carbide (ZrC).
2. Description of the Related Art
Zirconium Carbide (ZrC) is a ceramic that is used as tool bits, as a coating layer for nuclear fuel, and in ultra-high temperature (e.g., 3500° C.) applications. The ceramic is also corrosion and water resistant. High density (i.e., greater than 90% of a theoretical density of the ZrC) and small grain sizes (i.e., 1 to 12 μm) are desirable traits for ZrC because these traits lead to good material hardness and mechanical strength. ZrC should have low levels of impurities and a stoichiometric ratio that is approximately ZrC1.0.
Related methods for making monolithic discs of ZrC include “sintering” and “hot press”, but these methods have limitations. For the hot press method to produce ZrC with 90% density, very high temperatures, i.e., 2200 to 2700° C., are required. Even when high temperatures are used, the produced ZrC has a relatively large grain size (16 to 120 μm). Sintering also requires high temperatures (2200 to 2700° C.) to create monolithic discs. The result is a monolithic disc of ZrC with relatively large grain size (20 to 65 μm) and low density (70 to 90%).
Both processes produce monolithic discs of ZrC with large grain sizes. Large grain sizes correspond to reduced material hardness and mechanical strength. Both processes require relatively high energy to meet the high temperature requirements.
In light of the foregoing, there is a need for a method of making monolithic ZrC having high density (i.e. above 90%) and small grain sizes (1 to 12 μm).
To solve the above problems, other problems, or both, it is an aspect of the described embodiments to provide a method of producing monolithic ZrC, including raising a pressure applied to a ZrC powder until a final pressure of greater than 40 MPa is reached; and raising a temperature of the ZrC powder until a final temperature of less than 2200° C. is reached.
To solve the above problems, other problems, or both, it is an aspect of the described embodiments to provide a method of producing monolithic ZrC, including raising a temperature of a ZrC powder to a temperature of less than 2200° C., a density of the monolithic ZrC being 96%-98% of a theoretical density.
To solve the above problems, other problems, or both, it is an aspect of the described embodiments to provide a method of producing monolithic ZrC, the ZrC having a grain size of less than 12 microns.
Additional aspects, advantages, or both will be set forth in part in the description which follows and in, in part, will be apparent from the description, or may be learned by practice thereof.
These or other aspects and advantages or both will become more readily appreciated from the following description of embodiments, taken in conjunction with the accompanying drawings in which:
Embodiments are described below, examples of which are illustrated in the accompanying drawings, wherein like reference numerals refer to the like elements throughout. Although a few embodiments have been shown and described, those skilled in the art will appreciate that changes may be made in these embodiments without departing from the principles and spirit of the embodiments, the scope of which is defined in the appended claims and their equivalents.
The resulting hot-pressed ZrC has relatively small grain sizes (1-12 microns), thereby resulting in improved strength and damage resistance. Also, the density of the resulting hot-pressed ZrC is 96%-98% of a theoretical density.
The resulting hot-pressed ZrC has relatively small grain sizes (1-12 microns), thereby resulting in improved strength and damage resistance. Also, the density of the resulting hot-pressed ZrC is 96%-98% of a theoretical density.
The resulting hot-pressed ZrC has relatively small grain sizes (1-12 microns), thereby resulting in improved strength and damage resistance. Also, the density of the resulting hot-pressed ZrC is 96%-98% of a theoretical density.
This invention was made with U.S. Government support under DE-AC11-98FN38206 awarded by the United States Department of Energy. The U.S. Government has certain rights in the invention.
Number | Name | Date | Kind |
---|---|---|---|
5750450 | Bull | May 1998 | A |
6843943 | Adolfsson | Jan 2005 | B1 |
20140004271 | Allemand | Jan 2014 | A1 |
Number | Date | Country |
---|---|---|
WO 2012055865 | May 2012 | FR |
Entry |
---|
Chaplygin et al., Effect of Sintering Atmosphere on the Quality of Powder Metallurgical Hard Alloys Containing Zirconium and Hafnium Carbides, Poroshkovaya Met, No. 8 (116), (1972), pp. 81-84. |
Deryavko et al., Macrostresses in Sintered Carbides, Poroshkovaya Met, No. 5 (257), (1984), pp. 60-64. |
Anan'in et al., Effect of Shock Waves on Refractory Compounds, Poroshkovaya Met, No. 10 (142), (1974), pp. 100-104. |
Nezhevenko et al., Influence of the Density of Zirconium Carbide Compacts on the Density of Sintered Specimens, Poroshkovaya Met, No. 1, (1968), pp. 14-16. |
Kushtalova I. P., Investigation of the Sintering of Loosely Poured Titanium Carbide and Zirconium Carbide Powders, Poroshkovaya Met, No. 8 (56), (1967), pp. 7-9. |
Rempel et al., Preparation of Disordered and Ordered Highly Nonstoichiometric Carbides and Evaluation of their Homogeneity, Physics of the Solid State, vol. 42 (7), (2000), pp. 1280-1286. |
Gropyanov V.M., Effect of Dispersion on Powder Sintering, Ogneupory, No. 12, (1969), pp. 46-52. |
Kruglov et al., Effect of Structure and Substructure on the Strength of Sintered Zirconium Carbide Specimens, Poroshkovaya Met, No. 1 (193), (1979), pp. 59-64. |
Lanin et al., Non-Isothermal Sintering Parameters and their Influence on the Structure and Properties of Zirconium Carbide, Ceramics International, vol. 17, (1991) pp. 301-307. |
Lanin et al., Zirconium Carbide Recrystallization, Poroshkovaya Met, No. 2 (278), (1985), pp. 86-92. |
Andrievskii et al., Effect of Structural Vacancies in Interstitial Phases on their Sintering Shrinkage, Poroshkovaya Met, No. 6 (174), (1977), pp. 22-26. |
Ordan'yan et al., Isothermal Sintering Kinetics of Zirconium Carbide, Poroshkovaya Met, No. 12 (180), (1977), pp. 57-61. |
Bulychev et al., The Sintering of Zirconium Carbide, Poroshkovaya Met, No. 4 (172), (1977), pp. 38-42. |
Pierson H. O., Handbook of Refractory Carbides and Nitrides, Noyes Publications, Westwood, NJ (1996), p. 67. |
Gorinskii et al., Thermophysical Properties of Hot-Pressed TiC—C and ZrC—C Composite Materials at High Temperatures, Poroshkovaya Met, No. 4 (196), (1978), pp. 67-71. |
Barnier et al., Hot-Pressing Kinetics of Zirconium Carbide, Materials Science, vol. 21, (1986), pp. 2547-2552. |
Lengauer et al., Solid State Properties of Group IVb Carbonitrides, Alloys and Compounds, vol. 217, (1995), pp. 137-147. |
Spivak et al., Densification Kinetics in the Hot Pressing and Recrystallization of Carbides, Poroshkovaya Met, No. 11 (131), (1973), pp. 24-30. |
Mahday et al., Mechanically Induced Solid State Carburization for Fabrication of Nanocrystalline ZrC Refractory Material Powders, Alloys and Compounds, vol. 299, (2000), pp. 244-253. |
Number | Date | Country | |
---|---|---|---|
20140239559 A1 | Aug 2014 | US |
Number | Date | Country | |
---|---|---|---|
61768840 | Feb 2013 | US |