High resolution recording medium and method for producing same

Abstract

A high resolution recording medium is provided which employs at least two layers of inorganic material which act as filters for two different colors of visible light. In one embodiment, microphoto lithography techniques are used to create microinterference filters in the desired patterns on a glass substrate. Recording media constructed according to this invention exhibit increased stability with respect to time and improved resistance to light and heat damage as compared with prior art recording media employing organic dyes.

Description

BACKGROUND OF THE INVENTION

The invention relates to a recording medium for the reproduction of patterns with high resolution. The invention is directed in this respect particularly to the recording of large quantities of data per square millimeter (mm.sup.2). The invention moreover relates to a method for producing such recording media with high resolution patterns.

With the aid of microfilm techniques, large volumes of archives (libraries, drawings and other documents) may be stored in a very small space. The limits of microfilm reside in the resolution capacity of the image or of the recording films, that is, in the legibility of the recorded image following re-enlargement to approximately the dimensions of the original picture. One limit to the resolution of conventional microfilm is the result of the grain of the photographic emulsions used, which are typically 10 to 20 microns in diameter. In this connection, the resolution of photographic fine grain layers as indicated by the manufacturers does not provide a simple indication of the resolution of microfilm. The manufacturers measure resolution in lines per millimeter, that is, the finest reproduceable grid as determined photometrically. The photometer curve of such an exposed grid still distinctly shows maxima and minima. However, substantially more distinct contrasts are required for microfilm legibility, and these contrasts should be in black and white as far as possible and not in shades of gray. For exact documentation more or less sharp edges are needed. This means that the resolution indicated by the film manufacturer is much greater than the actual resolution of conventional microfilm.

Moreover, microfilms known to the prior art also may exhibit instability with respect to time, heat and light. Due to the shrinkage of the gelatin emulsion, patterns recorded thereon may be distorted with time and the films themselves may be distorted by heat. In color films the color of recorded images is subject to fading when exposed to light.

Photo-sensitized layers made from high polymers known as photo-resists offer the potential of substantially higher resolution than that obtained with photographic fine grain layers. By exposure to actinic light or with electrodes or ions, the chemical structure of these resists may be modified. In particular such exposure may change the solubility of the photo resist in specific "developer solutions."

The methods of "microphoto lithography" are well known in the prior art and have been applied in optics for the production of precise structures, such as graduated plates and graduations (see German Pat. No. 902,713). Of late they also have been used in semi-conductor technology in the so-called planar method for the fabrication of micro circuits. Likewise, lengthy messages (such as the text of the Bible, or highly reduced messages of U.S. Presidents with regard to the moon flight, etc.) have been produced on chrome-plated glass supports, with the aid of said micro lithography.

SUMMARY OF THE INVENTION

A primary object of this invention is to provide a recording medium, as well as a method for the fabrication of such a recording medium, where the data content to be accommodated on a unit of surface unit is increased considerably, while at the same time, the aforementioned disadvantages of distortion, fading, and sensitivity to heat are reduced.

This object is accomplished with a recording medium according to the invention as claimed. The pattern to be reproduced, which may be an image such as a map, a printed page, or a binary code for technical purposes, is recorded in multiple colors. At least two filter layers for different wave length ranges of visible light are used for the recording. Preferably, these filter layers are formed of inorganic materials that are resistant to heat and light damage.

Summarizing briefly, this invention is directed to the reproduction of highly complex multi-colored features (as they exist, for example, in detailed multi-colored maps) in a precise microstructure. The invention makes use of the principle derived from the science of chromatics that a multicolored representation increases the data content per unit of surface by one dimension as compared with a unicolored (black-white) representation.

A conventional example of this principle is found in colored maps where a precise accommodation of large quantities of data is required and where legibility is decisively increased by the use of more than one color. That is why this invention is well adapted for the representation of a colored micro-map. However, the invention is not limited to representing colored micro-maps, but instead relates in general to recording media with details (bits) which are stressed with reference to each other by different color hues and/or different color saturation.

The use of color offers more than a physical expansion of the code used heretofore in the art; the physiological effect resulting from the use of multiple colors also should be taken into account in the application of the invention. The present invention makes feasible multicolor presentation of many technical pictorial representations for the first time. This multicolor presentation is both physiologically and psychologically effective in many applications.

In the past various methods of color representation have been attempted. Lippman tried to build color photographs with the aid of the colors of thin layers via the Eidophororic method for color television, and color photography utilizes organic dyes with limited "light fastness."

According to one embodiment of the invention, recorded colors are generated by the interference of light. This interference is generated by interference layers which are built from thin inorganic layers and are relatively stable in time and resistant to light and heat. Multicolored micro images may be constructed with such thin inorganic interference layers.

An alternate embodiment of the invention employs grainless thin layers which are colored to selectively absorb portions of the visible spectrum. The granule sizes of these layers are below 20 nanometers (nm). Even at a thousand-fold re-enlargement, they are "grainless."

One method is particularly appropriate for the production of the aforementioned recording media. This method is known under the designation "micro photo lithography" and its origin goes back to the beginnings of photography and the use of grainless photo varnishes. This method utilizes layers of a photo sensitive compound, such as a photo resist, which are chemically modified by exposure to ultraviolet light, fine electron beams (screen micro styluses) and/or X-ray radiation or an ion probe. The lower limit of resolution in these known methods of reproduction is at graduation thickness of approximately 0.5 micron.

This invention has been demonstrated in the production of approximately 100 colored micro maps (for example, page L 8140 "Traunstein," scale 1:50,000 of the topographic map of the Bavarian Land Surveying Office, Munich) which reproduce on a glass surface area of 3 mm. by 3 mm. in full color and high precision the information contained in an original 600 mm by 600 mm. map. In addition, colored recording media of micro structures have been produced which, insofar as their durability (light fastness, temperature stability, color reproduction) is concerned, could not be realized according to prior art. The present invention records color with inorganic materials which are more stable than a large part of the colors present in nature.

BRIEF DESCRIPTION OF THE DRAWINGS

The following detailed description should be read with reference to the appended drawings, in which:

FIG. 1 is a transverse sectional view of a first embodiment of this invention; and

FIG. 2 is a transverse sectional view of a second embodiment of this invention.

DETAILED DESCRIPTION

The following description describes in detail the individual steps of a method for the production of a recording medium. For reasons of illustration, reference is made to the appended drawings. It is assumed in this connection that a micro map is to be produced with a scale of 1:10,000,000, for example, which is produced from colored portions of individual maps with a scale of 1:50,000, corresponding to a reduction of 1:200. The micro map contains all the information of the original map in an area of 3 .times. 3 mm.sup.2, and can be re-enlarged with clearly legible edges up to five times the original size, that is, at an enlargement factor of 1:1000.

It is to be assumed for the example described herein that first the light blue portions of the map (the lakes and streams) and dark blue portions (captions and depth lines) are to be produced according to the method of the invention. All of these features will be recorded in one color hue which is differentiated only by its saturation. In the printing process as such, this difference in saturation is produced by a screen used in conjunction with the light blue surfaces.

Blue color hue No. 17 of standard DIN 6164 is required for the reproduction and is determined by a filter layer of optical thickness 240 nm. The exact thickness somewhat depends on the reflecting surfaces used in conjunction with the filter layer.

The degree of saturation depends on the reflection/transparency of the reflecting layers adhering to the filter layer. They may be composed of very thin silver (Ag) layers or of alternating layers of high and low refraction materials. This will be elucidated in greater detail with reference to FIG. 1 and FIG. 2.

With the aid of an apparatus known as an "ionograph," a glass platelet in the form of a substrate and purified in a manner known to the prior art shall be provided with the desired pattern. For that purpose, the glass platelet is placed into the equipment. The apparatus itself contains cathodes of a material appropriate for producing reflecting layers; preferably, a silver (Ag) cathode is provided. The cathodes remain permanently under vacuum. Following the introduction of the glass platelet into the ionograph and the loading of the ionograph with purified argon gas, a 27 megacycle HF voltage of about 3,000 volts is applied at a vacuum pressure of about 1 Pa, via a high performance capacitor having only a few ohms of capacitive resistance at a frequency of 27 megacycles, but which is extremely highly resistant for DC voltage. This voltage ignites a plasma. The electrons which, during the positive semi-wave of the high frequency, charge the silver cathode negatively are recombined by the argon ions during the negative semi-wave only to a small degree. In this manner, the Ag cathode remains charged negatively, and the accelerated Ag ions atomize the silver and generate a durable, grainless silver mirror on the glass substrate which is suitable for the following operations. The generation of the mirror layer is observed precisely by readings and interrupted, for example, at a thickness of 16 nanometers.

The so-called copying phase takes place immediately after the production of a nonstructured mirror layer on the glass substrate. For this, the mirror layer is coated with photo resist and, in the example selected, the micro mask for the dark blue portions of the original map (blue captions, depth lines in lakes and other symbols) is copied on the photo resist and developed. The unmasked silver layer areas now are removed again in the ionograph at reversed polarization, that is, with the use of the glass support as cathode. However, the silver layer below the areas protected by photo resist is preserved. Subsequently, the photo resist is removed with acetone or some similar solvent.

Next, the glass platelet is recoated with silver and, in an additional copying operation, the color micro mask for light blue (lakes and streams) is copied on and removed in the high frequency plasma as described above, and the photo resist is subsequently peeled off.

Now the glass substrate shows with precision all details of the finished pattern of the map which are to be reproduced in dark and light blue as a grainless silver layer. This layer is 32 nm thick at the locations where a dark blue color is to appear and at the locations where a light blue color is to be reproduced, the layer is 16 nm thick.

Now the entire glass platelet is covered with a spacer layer of vaporized clear glass with an optical thickness of 238 nm. When MgF.sub.2 is used, this corresponds to an actual thickness of 172 nm. A silver layer of 16 nm thickness is placed thereabove over the entire area, which, as in the copying phase described immediately above, is exposed with the micro mask for the light blue color and removed accordingly.

By varying the thickness of the spacer layer, 238 nm in the above example, any desired color hue from 13 to 24 according to DIN 6164 can be achieved. However, the color hues 1 to 12 according to this standard cannot be formed without problem. In fact, in spacer layers thicker than 210 nm additional interference minima move from the UV range into the visible range, thereby causing mixed colors. The production of the yellow-red color hues 1 to 12 according to the DIN standard 6164 thus is more complicated. For the color hues 13 to 24 any desired degree of saturation according to DIN 6164 can be adjusted by appropriate thickness of the silver layers.

The structure of the inorganic layers, as described above, is illustrated clearly in FIG. 1. In this Figure the reference symbols 1, 2 and 3 identify the silver layers applied in the three copying phases, while 4 identifies the transparent interference layer (spacer layer).

In this application, silver layer 2 is 16 nm thick and cooperates with the spacer layer 4 and the silver layer 3 to form an interference filter which passes blue light. Silver layer 1 is also 16 nm thick. This thickness combines with the 16 nm thickness of layer 2 to produce a combined layer 32 nm thick which cooperates with the spacer layer 4 and the silver layer 3 to form an interference filter which passes blue light in increased intensity. The spacer layer 4 is located on the silver layer 2 in a thickness of 238 nm. The silver layer 3 itself again has a thickness of 16 nm.

As a result, the light exiting in the area of arrow 5 appears dark blue (color 17:8), the light exiting in the area of arrow 6 appears light blue (color 17:4), and the light exiting from other regions, for example, in the area of arrow 7, appears white (not vary-colored).

FIG. 2 clearly illustrates that alternating layers of high and low refractory partial layers may be used as reflecting layers in place of silver layers. Again, it is assumed in FIG. 2 that the color blue is to be reproduced, and a spacer layer of corresponding thickness is provided. In contrast to the embodiment of FIG. 1, the low refractory partial layers 8 and 9 adjacent the interference layer are covered by high refractory partial layers 10 both against the interference layer as well as between each other and toward the exterior, as represented schematically on a highly enlarged scale in FIG. 2. As a result, in the area outside the alternating layers, for example in the area of arrow 11, white light (nonvary-colored) exits.

MgF.sub.2, SiO.sub.2, ThF.sub.4, SiO Ta.sub.2 O.sub.5, Fe.sub.2 O.sub.3 or other oxides, fluorides and/or sulfides are appropriate materials for the spacer layers (interference layers) for the method according to the invention. According to one advantageous embodiment of this invention, the spacer layer first is applied to a substrate surface provided with corresponding reflecting layers., This spacer layer is applied in a thick layer (approximately 10 times thicker than what is needed for the use of the individual colors), and subsequently removed under plasma-chemical modification to a thickness commensurate with the desired colors. In the finished recording medium, the thickness of the spacing layer determines the color hue, while the saturation is determined by the reflective capacity of the mirrors, as explained above in connection with FIG. 1.

It will be obvious to persons skilled in the art that the techniques described above may be used to record mixed colors by consecutively applying different color hues in superposition. Mixed colors may be used for form different colors in adjacent regions. In one region a mixed color is formed by superimposing two spacer layers of differing thicknesses separated by a reflecting layer. These two spacer layers are bounded by reflecting layers at the top and bottom, and a mixed color results. In an adjacent area, the same two spacer layers are deposited, but no reflecting layer is interposed between them, and accordingly, a single color is produced rather than a mixed color.

It also is possible to use the method of this invention to produce multicolored structures with fluorescent luminous colors, by using materials for the spacer layers which convert incoming UV light into visible luminous radiation and emit this visible light. MgF.sub.2, ZuS and similar materials may be appropriately used as materials for this operation.

Hard glass (zerodur and quartz glass) are particularly appropriate as substrates for the microstructures to be applied. Such hard glass substrates can be reprojected at high light levels without requiring major expenditures for heat filtration. Ordinary color films would be charred by such reprojection within seconds.

A particularly advantageous embodiment of the method according to the invention is described below in the form of an example. Once again, it is assumed for reasons of better illustration that a micro map shall be produced in a diapositive on a glass substrate.

First, the glass substrate is covered with a thin layer of Cd.sub.S, Fe.sub.2 O.sub.3, As.sub.2 S.sub.3, or a similar organic compound. Then the substrate is coated with photo resist and the the negative micro mask for the color blue is copied onto the photo resist. Subsequently the aforementioned organic compound layer is removed in the areas where the color blue will be reproduced down to the glass surface and then the photo resist is peeled off. Now the substrate again is clear glass in the area where the color blue will be reproduced and otherwise it is yellow-brown due to the inherent color of the thin Fe.sub.2 O.sub.3 layer.

As a second step a blue layer combination is now applied as a silver layer in a positive micro mask "lakes, rivers and forests" in structurized form. That way all blue areas (lakes, streams) and green areas (forests) are present as structure of the map as regions in which a reflecting silver layer has been deposited. However, below the green areas (forests) there is the Fe.sub.2 O.sub.3 layer (or another suitable layer), while below the blue areas (lakes) the substrate is clear glass. Thus, lakes and streams are blue (color hue 17), woods and similar areas, however, are green (hue 22) as a mixture of the yellow and blue colors. The other areas (fields, etc.) are yellow. Legends remain colorless (nonvary-colored) and transparent.

Thus, with two copy operations, namely, with a negative micro mask (lakes, streams) and a positive micro mask (lakes, streams and forests) altogether four colors are obtained: color hue 17 (blue), color hue 22 (green), color hue 2 (yellow), and color hue 0 (nonvary-colored). This demonstrates one embodiment of the invention.

Any additional and new color hue produced by another copy operation produces twice as many new colors by blending with the color hues already produced previously in a partial area of the pattern. Thus, 10 individual copy operations produce 2.sup.10, or 1024 color hues with the technical application of a binary color code.

According to the four-color set of topology, two copy operations suffice completely, in theory, for producing any complex varying map structure. However, in practice the micro map is adjusted by adding still more colors to the conventional map, for example, red for main roads, and black for legends.

For example, the color red (8 according to DIN 6164) can be obtained in the following manner:

1. Reactive dust a substrate with Fe cathode for 10 minutes;

2. Copy the positive micro mask for main roads (red) onto the FeO.sub.3 ;

3. Peel and remove (Fe.sub.2 O.sub.3 with n = 2.9, and a thickness of 45 nm remains on the red details as an interference layer);

4. Vaporize a spacer layer of MgF.sub.2 with thickness 284 nm. (In cooperation with the MgF.sub.2 spacer layers for green (forests) and blue (lakes) and the Ag mirror, this spacer layer produces the color hue red. Steps 5 to 20 complete the red recording and at the same time record forests and lakes in green and blue.);

5. Vaporize Ag to a thickness of 20 nm;

6. Perform a second copying step using a positive micromask for forests;

7. Remove and peel the photo lacquer for 2 minutes;

8. Vaporize MgF.sub.2 to a thickness of 153 nm (T = 22 green) and metallize Ag to a thickness of 20 nm;

9. Perform a third copying step using a positive micromask for forests and main roads;

10. Remove and peel off the photo lacquer for 2 minutes;

11. Vaporize an intermediate layer of MgF.sub.2 to a thickness of 75 nm (interference color in UV);

12. Metallize Ag to a thickness of 16 nm;

13. Perform a fourth copying step using a positive micromask for depth lines (dark blue);

14. Remove and peel off photo lacquer;

15. Metallize Ag to a thickness of 16 nm;

16. Perform a fourth copying step using a positive micromask for lakes and rivers;

17. Remove and peel off photo lacquer;

18. Vaporize a MgF.sub.2 interference layer (blue) and metallize Ag to a depth of 16 nm;

19. Perform a fifth copying step using a positive micromask for lakes, rivers, and roads;

20. Remove and peel off photo lacquer;

21. Vaporize protective layer;

22. Metallize chrome (Cr mask black);

23. Repeat step 6 using a positive micromask for black legends, buildup, etc.;

24. Remove unprotected Cr layer;

25. Peel off photo lacquer;

26. Apply protective layer.

The invention has been explained on the basis of producing micro structures. However, the method according to the invention also is directly applicable to the multicolored representation of macroscopic symbols.

From original color maps (600 .times. 600 mm) on the scale of 1:50,000, micro maps were produced in a scale of 1:10,000,000 in a size of 3 .times. 3 mm. The total information content of a 1:50,000 map which contains a tremendous number of bits thus is accommodated on 9 mm.sup.2. This means that a map of the Federal Republic of West Germany can be reproduced in the same scale ratio on a glass plate of 100 .times. 100 mm in micro representation, with all details of the map being represented with the precision of a map of 1:50,000.

Persons skilled in the art of photo lithography and high vacuum vaporization technique are sufficiently familiar with the individual steps of copying, removal and vaporization, so that in the present application these steps have not been described in detail. It should be understood that various changes and modifications to the preferred embodiments described herein will be apparent to those skilled in the art. Such changes and modifications can be made without departing from the scope of the present invention and without diminishing its attendant advantages. It is, therefore, intended that such changes and modifications be covered by the following claims.

Claims

1. A high resolution recording medium comprising:

first and second patterned reflecting layers; and

a spacer layer interposed between the first and second reflecting layers, said first and second reflecting layers cooperating with said spacer layer to form a high resolution, patterned interference filter for recording a color pattern, wherein the thickness of the spacer layer is one factor determining the color recorded in the medium.

2. The recording medium of claim 1 wherein said spacer layer includes first and second regions of differing thickness to permit recording of a multicolored pattern.

3. The recording medium of claim 1 wherein the first and second reflecting layers comprise inorganic material.

4. The recording medium of claim 1 wherein the spacer layer comprises inorganic material.

5. The recording medium of claim 1 wherein said first reflecting layer includes first and second regions of differing optical reflectivity to permit recording of a colored pattern having multiple saturation values in the medium.

6. The recording medium of claim 1 further comprising a patterned absorbing layer of a material which absorbs light more strongly in a predetermined portion of the visible spectrum, said light absorbing layer acting as a color filter.

7. The recording medium of claim 1 wherein the reflecting layers are formed by vapor deposition.

8. The recording medium of claim 1 wherein the spacer layer is formed by vapor deposition.

9. A recording medium for recording a multicolored, high resolution pattern, said medium comprising:

first and second patterned reflecting layers;

a spacer layer interposed between the first and second reflecting layers, said spacer layer including first and second regions having differing thicknesses such that the first and second reflecting layers and the spacer cooperate to form a patterned interference filter for a first color in the first region and a second color in the second region.

10. The recording medium of claim 9 wherein the first reflecting layer includes first and second areas having differing reflectivity to permit the saturation of the color produced by the interference filter in the first region to differ in the two areas.

11. The recording medium of claim 9 wherein the first and second reflecting layers comprise inorganic material.

12. The recording medium of claim 9 wherein the spacer layer comprises substantially inorganic material.

13. The recording medium of claim 9 further including a patterned absorbing layer of a material which absorbs light more strongly in a predetermined portion of the visible spectrum, said light absorbing layer acting as a color filter.

14. The recording medium of claim 9 wherein the first and second reflecting layers are formed by vapor deposition.

15. The recording medium of claim 9 wherein the spacer layer is formed by vapor deposition.

16. A high resolution medium for recording a multi-colored pattern comprising:

first and second patterned reflecting layers;

a first spacer layer interposed between the first and second reflecting layers to form a first patterned interference filter therewith;

a second spacer layer superimposed over the first spacer layer and the second reflecting layer;

a third patterned reflecting layer superimposed over the second spacer layer, a first portion of said third reflecting layer cooperating with the first and second spacer layers and a portion of the first reflecting layer to form a second patterned interference filter having an overall spacer layer which includes both the first and second spacer layers, a second portion of the third reflecting layer cooperating with the second reflecting layer and the second spacer layer to form a third patterned interference filter.

17. The recording medium of claim 16 wherein the first and second spacer layers comprise inorganic material.

18. The recording medium of claim 16 wherein the first, second, and third reflecting layers comprise inorganic material.

19. The recording medium of claim 16 wherein at least one of the reflecting layers includes a first area having higher reflectivity than a second area to permit colors to varying saturation to be recorded in the first and second areas.

20. The recording medium of claim 16 wherein the first, second and third reflecting layers are formed by vapor deposition.

21. The recording medium of claim 16 wherein the first and second spacer layers are formed by vapor deposition.

22. A recording medium for recording a high resolution, multicolored pattern, said medium comprising:

at least two color filters for recording high resolution patterns, each of said color filters including first and second patterned layers comprising inorganic material and an unpatterned spacer layer interposed between the first and second patterned layers, said spacer layer comprising inorganic material which is substantially absorption-free in the visible spectrum, wherein the thickness of the spacer layer determines in part the color of each filter and the reflectivity of the patterned layers determines in part the saturation of said color.