High solids acrylic dispersion lacquer

Abstract

A high solids acrylic dispersion lacquer coating composition having an acrylic polymer binder content of about 25-45% by weight in a nonaqueous medium; wherein the acrylic polymer is a blend of(1) Polymer A of methyl methacrylate and a polymerized monomer of allyl methacrylate, alkyl amino alkyl methacrylate or mixtures thereof;(2) Copolymer B of methyl methacrylate and an alkyl acrylate having 6-12 carbon atoms in the alkyl group; and(3) A graft copolymer of Polymer A which forms a backbone of the graft copolymer and Copolymer B attached to the backbone which forms side chains of the graft copolymer; andwhereinthe nonaqueous medium is a blend of(a) an aliphatic solvent which at 25.degree. C. is a nonsolvent for Polymer A and a solvent for Copolymer B; and(b) a coalescing solvent for the binder;the composition is useful as an exterior finish for automobiles and trucks.

Description

BACKGROUND OF THE INVENTION

This invention is related to a coating composition and in particular to a higher solids acrylic dispersion lacquer coating composition in a nonaqueous medium.

Acrylic dispersion lacquer coating compositions are well-known and are shown in Fryd and Lee U.S. Pat. No. 3,660,537 issued May 2, 1972 and Lee and Victorius Canadian Pat. No. 957,792 granted Nov. 12, 1974. Compositions, such as described in the above patents, have been widely used in the automotive industry as a high quality exterior coating for automobiles and trucks and provide finishes of a high quality. However, these compositions do not comply with air pollution regulations that are being promulgated by many states and at the present state of the art cannot be brought into compliance with these regulations even with expensive pollution abatement equipment and techniques.

There is a need for a coating composition that will meet the following requirements: comply with current and future air pollution regulations with the use of pollution abatement equipment and techniques, form finishes an automobiles and trucks that have a good appearance, particularly good glamour, that are durable and weatherable and that can be spot repaired using conventional refinish procedures. The novel coating composition of this invention meets the above requirements.

SUMMARY OF THE INVENTION

A high solids acrylic polymer dispersion lacquer coating composition having an acrylic polymer binder content of about 25-45% by weight in a nonaqueous medium; wherein the acrylic polymer binder is a blend of

(1) Polymer A of polymerized methyl methacrylate and a monomer from the group of allyl methacrylate, alkyl amino alkyl methacrylate or mixtures thereof and having a weight average molecular weight, measured by gel permeation chromatography, of about 90,000-130,000; (2) Copolymer B of polymerized methyl methacrylate and an alkyl acrylate having 6-12 carbon atoms in the alkyl group and having a weight average molecular weight, measured as above, of 20,000-40,000; and (3) A graft copolymer of Polymer A which forms a backbone of the graft copolymer and Copolymer B attached to the backbone which forms side chains of the graft copolymer and having a weight average molecular weight of about 110,000-170,000; wherein the nonaqueous medium is a blend of (a) an aliphatic solvent which at 25.degree. C. is a nonsolvent for Polymer A and a solvent for Copolymer B; and (b) a coalescing solvent which at 50.degree. C. is a solvent for the binder and at 25.degree. C. is a nonsolvent for the binder.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The acrylic dispersion lacquer coating composition has an acrylic polymer binder content of about 25-45% by weight and is in a nonaqueous medium. The acrylic polymer binder is a blend of a Polymer A, a Copolymer B and a graft copolymer having a backbone and side chains attached thereto of Polymer A which forms the backbone and Copolymer B forms the side chains.

In the dispersion lacquer, Copolymer B is in solution. Polymer A is not in solution but is kept dispersed by the graft copolymer. The dispersion has a relatively high polymer solids content and a viscosity that allows spray application. Upon application of the dispersion to a substrate, a substantial amount of aliphatic nonsolvent evaporates and the dispersion is converted to a relatively high viscosity liquid on the substrate. This high viscosity liquid does not sag or flow on the substrate upon application. On baking of the coating, the remaining solvents coalesce the polymers into a smooth, glossy and continuous finish.

The acrylic polymer binder comprises about 25-45% by weight of Polymer A, 5-25% by weight of Copolymer B and 40-60% by weight of the graft copolymer. One particularly preferred acrylic binder comprises 35% by weight of Polymer A, 15% by weight of Copolymer B and 50% by weight of graft copolymer.

Polymer A is comprised of polymerized methyl methacrylate and allyl methacrylate, and optionally an alkyl amino alkyl methacrylate. Typically, Polymer A is comprised of 90-99.5% by weight, based on the weight of Polymer A, of methyl methacrylate, 0.1-5% of allyl methacrylate and 0.4-5% by weight of alkyl amino alkyl methacrylate. Polymer A has a weight average molecular weight of about 90,000-130,000 and preferably 100,000-115,000.

The molecular weights of polymers referred to herein are determined by gel permeation chromatography using polymethyl methacrylate as a standard.

One preferred composition of Polymer A comprises 97-99.5% by weight of methyl methacrylate, 0.4-1% by weight of diethylaminoethyl methacrylate and 0.1-2% by weight of allyl methacrylate having a weight average molecular weight of 100,000-115,000.

Typical alkyl amino alkyl methacrylates that are used to form Polymer A are: dimethylaminoethyl methacrylate, diethylaminoethyl methacrylate, dipropylaminoethyl methacrylate, methylethylaminoethyl methacrylate, butylaminoethyl methacrylate, tertiarybutylaminoethyl methacrylate, diethylaminopropyl methacrylate, diethylaminobutyl methacrylate, diethylaminopentyl methacrylate, diethylaminohexyl methacrylate and the like. Diethylaminoethyl methacrylate is preferred to form a quality coating composition.

Copolymer B is comprised of polymerized methyl methacrylate and an alkyl acrylate having 6-12 carbon atoms in the alkyl group. Typically, Copolymer B is comprised of about 40-60% by weight of methyl methacrylate and 40-60% by weight of the alkyl acrylate. Copolymer B has a weight average molecular weight of about 20,000-40,000. One preferred composition of Copolymer B comprises 40-60% by weight of methyl methacrylate and 40-60% by weight of 2-ethylhexyl acrylate.

Typical alkyl acrylates that are used to form Copolymer B are: hexyl acrylate, 2-ethylhexyl acrylate, nonyl acrylate, decyl acrylate, lauryl acrylate and the like. 2-Ethylhexyl acrylate is preferred to form a high quality product.

The graft copolymer has a backbone of Polymer A and side chains of Copolymer B attached thereto. Generally, the graft copolymer contains about 50-80% by weight of Polymer A and 20-50% by weight of Copolymer B and has a weight average molecular weight of about 110,000-170,000.

The nonaqueous medium used in the composition is a blend of (1) an organic aliphatic solvent which at 25.degree. C. is a nonsolvent for Polymer A and remains a nonsolvent at elevated temperatures for Polymer A and is a solvent for Copolymer B at 25.degree. C. and (2) a coalescing solvent which at 50.degree. C. and above is a solvent for the binder and form a high quality finish. At 25.degree. C. the coalescing solvent preferably is not a solvent for the binder as only a small percentage of the binder may solubilized or swollen by the coalescing solvent. Generally, the nonaqueous medium of the composition contains about 35-65% by weight, based on the weight of the nonaqueous medium, of the aliphatic solvent and 35-65% by weight of coalescing solvent.

If the aliphatic solvent and the coalescing solvent are not compatible up to about 15% by weight, based on the weight of the nonaqueous medium, of a bridging solvent can be added to make the aliphatic solvent and coalescing solvent compatible. Usually 5-10% by weight of a bridging solvent is used.

Also, it may be desirable to add up to 20% by weight, based on the weight of the nonaqueous medium, of a coalescing solvent which is a solvent for the binder at 25.degree. C. The use of these coalescing solvents results in lower binder solids content of the composition and the use of these solvents is kept to a minimum.

Typical aliphatic solvents are petroleum fractions that have a boiling point range of about 100.degree.-160.degree. C. and may contain up to about 10% by weight of aromatic solvents.

Typical bridging solvents are toluene, xylene, high solvency hydrocarbons having a boiling point range of 180.degree.-220.degree. C.

Typical coalescing solvents which are solvents for the binder at 50.degree. C. but not solvents at 25.degree. C. are as follows:

diethylene glycol monohexylether, diethylene glycol 2-ethyl hexyl ether, ethylene glycol monobutylether, 2-ethyl hexanol, isooctylalcohol and other 8 carbon atoms alcohols, slow evaporating high solvency hydrocarbon having a boiling point of 182.degree.-219.degree. C., 2-(2-butoxy-ethoxy)isopropanol, 2-(2-methoxy-isopropoxy)isopropanol, 2-methoxy isopropanol, 2-propoxy isopropanol, 2-butoxy isopropanol.

Typical coalescing solvents which are solvents for the binder at 25.degree. C. are as follows: diethylene glycol monobutyl ether acetate, diethylene glycol monohexyl ether acetate, diethylene glycol 2-ethyl hexyl ether acetate, ethylene glycol monobutyl ether acetate, ethylene glycol 2-ethyl hexyl ether acetate, diethyl phthalate, isobutyrate ester of 2,2,4-trimethyl-1,3-pentanediol and a mixture of methyl esters of succinic acid, glutaric acid and adipic acid.

The high solids acrylic polymer dispersion is prepared according to the following process:

Step (1) About 50-70% by weight of the monomers for Polymer A and the backbone of the graft copolymers, i.e., methyl methacrylate monomers and allyl methacrylate and/or alkyl aminoalkyl methacrylate monomers, are charged into a polymerization vessel with a coalescing solvent such as diethylene glycol monohexyl ether, optionally, a bridging solvent such as toluene and other low boiling solvents such as methanol or a blend of acetone and petroleum ether which control the reflux temperatures of the resulting reaction mixture to less than 95.degree. C. The resulting mixture is heated to its reflux, temperature (less than 95.degree. C.) and held at this temperature for 2-10 minutes. Step (2) About 0.1-2% by weight, based on the weight of Polymer A and the backbone of the graft copolymer, of an azo polymerization catalyst, such as azobisisobutyronitrile is added with a coalescing solvent to the reaction mixture and heated to its reflux temperature for about 5-10 minutes;

Step (3) The remaining 30-50% by weight of the monomers for Polymer A and the backbone of the graft copolymer and a coalescing solvent such as, diethylene glycol monohexyl ether, and about 0.1-2% by weight, based on the total weight of the monomers for Polymer A and the backbone of the graft copolymer, of the aforementioned azo polymerization catalyst with a coalescing solvent as described above are slowly added to the reaction mixture at a uniform rate over a 50-120 minute period while maintaining the reaction mixture at its reflux temperature but below 95.degree. C.

Step (4) About 40-60% by weight of the monomers such as methyl methacrylate monomers and 2-ethylhexyl acrylate monomers for Copolymer B and the side chains of the graft copolymer and about 0.5-2% by weight, based on the weight of the above monomers, of a peroxy polymerization catalyst such as t-butyl peroxy pivalate for graft polymer formation are added and the reaction mixture is held at its reflux temperature for about 5-20 minutes; Step (5) The remaining 40-60% by weight of the above monomers of step (4) with the above peroxy polymerization catalyst in the same amount are added at a uniform rate over a 20-50 minute period while maintaining the reaction mixture at its reflux temperature; Step (6) About 2-10% by weight, based on the weight of the monomers for Polymer A, Copolymer B and the graft copolymer, of methyl methacrylate monomer with about 0.1-1% by weight of azo polymerization catalyst and the above peroxy polymerization catalyst are added at a uniform rate over a 5-30 minute period and the reaction mixture is held at its reflux temperature for about 10-30 minutes; Step (7) About 15-25% by weight, based on the weight of the reaction mixture, of an aliphatic hydrocarbon solvent which is a nonsolvent for Polymer A and the backbone of the graft copolymer is added at a uniform rate over a 40-60 minute period; and Step (8) About 5-10% by weight, based on the weight of the reaction mixture, of an aliphatic hydrocarbon solvent of step (7) containing about 0.1-10% by weight based on the weight of the nonsolvent, of a peroxy polymerization catalyst described above in step (4) are added over a 40-60 minute period and the resulting reaction mixture is cooled to an ambient temperature.

Generally, the coating composition is pigmented. Pigments are usually used in a pigment to binder weight ratio of about 1/100 to about 150/100.

The pigments are introduced into the coating composition by first forming a mill base with a compatible dispersing resin by conventional techniques such as sand grinding, attritor grinding or ball milling. Then the mill base is blended with the film-forming binder as shown in the Examples. Polymers such as those described in Orvis U.S. Pat. No. 3,790,523 issued Feb. 5, 1974 (Column 2, line 65--Column 3, line 28) and cellulose acetate butyrate can be used as dispersing resins.

The following are examples of the great variety of pigments which are used in the coating composition: metallic oxides, preferably titanium dioxide, zinc oxide, and the like, metal hydroxides, metal flakes, such as aluminum flake, bronze flake, "Afflair" pigments, i.e., mica-coated with titanium dioxide, metal powders, chromates, such as lead chromates, sulfides, sulfates, carbonates, carbon black, silica, talc, china clay, phthalocyanine pigments such as copper phthalocyanine blue, iron blues, organic reds, organic maroons, and other organic pigments.

About 0.1 to 10% by weight, based on the weight of the binder, in addition to the other binder constituents of ultraviolet light stabilizers can be added to the coating composition. Typical ultraviolet light stabilizers are described hereinafter. It may also be desirable to add about 0.1-5% by weight, based on the weight of the binder, of an antioxidant, described hereinafter, to the coating composition.

About 0.1-5% by weight, based on the weight of the binder, of iron pyrophosphate can be added to the coating composition to improve certain properties of the composition such as improved resistance to deterioration of finishes caused by high humidity. One typically useful iron pyrophosphate is prepared according to the teachings of Jackson U.S. Pat. No. 3,074,895 issued Jan. 22, 1963.

About 0.01-1% by weight, based on the weight of the binder, of silicone anticratering agents can be used such as polyalkene oxide siloxane and silicone glycol copolymers.

The coating composition can contain about 15-30% by weight, based on the weight of the binder, of a plasticizer. Typical plasticizers are for example, phthalate esters such as butylbenzyl phthalate, dibutyl phthalate, 2-ethylhexylbenzyl phthalate, dicyclohexyl phthalate, dibenzyl phthalate, butylcyclohexyl phthalate, di-2-ethylhexyl ester of hexamethylene diphthalate, di-(methylcyclohexyl)phthalate. One preferred plasticizer of this group is butylbenzyl phthalate. Other plasticizers that can be used are mixed benzoic acid and fatty oil acid esters of pentaerythritol, poly(propylene adipate)dibenzoate, diethylene glycol dibenzoate, ethylene glycol adipate benzoate and neopentyl glycol adipate benzoate. Other plasticizers are tetrabutylthiodisuccinate, butylphthalyl butyl glycolate, acetyltributyl citrate, dibenzyl sebacate, tricresyl phosphate, toluene ethylsulfonamide.

Preferred plasticizers are coconut oil/ethylene glycol phthalate resins and ethylene glycol phthalate/ethylene glycol benzoate/ethylene glycol adipate resins.

The coating composition of this invention can be applied to a variety of substrates such as metal, e.g., phosphatized steel, uncoated steel, aluminum, fiberglass reinforced with resins, plastics, rigid polyurethanes, rigid synthetic rubbers and the like. These substrates are coated with a primer and usually a thin sealer coat is applied over the primer to enhance adhesion of the composition to the primer. Application of the coating composition is done by the usual methods of spraying, electrostatic spraying, dipping, brushing, flow coating and the like. The coating composition can be reduced to an application viscosity by the addition of a coalescing solvent/nonsolvent blend. A typical reducing solvent blend comprises a pretroleum naphtha and diethylene glycol monohexyl ether in about a 50/50 weight ratio. Generally, the composition is not reduced below 25% solids based on the binder. Preferably the composition is reduced to 30-35% solids based on binder.

After application, the coating is baked at about 150.degree.-225.degree. C. for 15 to 45 minutes. The resulting finish is about 0.1-5 mils thick, preferably, 1-3 mils thick, and has a good gloss. The finish does not yellow on baking and gives a hard, durable, scratch resistant, gasoline-resistant, weather-resistant, alkali-resistant, glossy finish which is suitable for automobile and truck bodies.

Another aspect of this invention is to utilize the composition as a clear coat/color coat finish for substrates. In this finish, a clear coat top layer is in firm adherence to a color coat layer that is in adherence with a substrate. The clear coat is a transparent film of the coating composition of this invention and the color coat is the coating composition of this invention containing pigments in a pigment to binder ratio of about 1/100 to 150/100 and other additives.

Optionally, the color coat can contain about 0.1-20% by weight, based on the weight of the binder of the color coat, of an ultraviolet light stabilizer. Another option is that the color coat and the clear coat each can contain about 0.5-20% by weight, based on the weight of the binder of the coat, of an ultraviolet light stabilizer and optionally, about 0.1-5% by weight, based on the weight of the binder of the coat, of an antioxidant; wherein the weight ratio of ultraviolet light stabilizer to antioxidant is about 1:1 to about 50:1.

Preferred, to form a durable finish, both the clear coat and the color coat contain about 0.5-8% by weight of an ultraviolet light stabilizer along with about 0.1-1% by weight of the antioxidant.

The thickness of the fully cured color coat and clear coat can vary. Generally, the color coat is about 0.4-1.5 mils thick and preferably 0.6-1.0 mils thick and the clear coat is about 0.5-6.0 mils thick and preferably 0.8-1.5 mils thick.

Any of the aforementioned conventional pigments can be used in the color coat including metallic flake pigments. The clear coat can also contain transparent pigments, i.e., pigments having the same or similar refractive index as the binder of the clear coat and are of a small particle size of about 0.015-50 microns. Typical pigments that can be used in the clear coat in a pigment to binder weight ratio of about 1/1000 to 10/100 are inorganic siliceous pigments, such as silica pigments. These pigments have a refractive index of about 1.4-1.6.

Typical ultraviolet light stabilizers that are useful are as follows:

Benzophenones such as hydroxy dodecyloxy benzophenone, 2,4-dihydroxybenzophenone, hydroxybenzophenones containing sulfonic groups and the like.

Triazoles such as 2-phenyl-4-(2',4'-dihydroxybenzoyl)-triazoles, substituted benzotriazoles such as hydroxy-phenyl triazoles and the like.

Triazines such as 3,5-dialkyl-4-hydroxyphenyl derivatives of triazine, sulfur containing derivatives of diallyl-4-hydroxy phenyl triazines, hydroxy phenyl-1,3,5-triazine and the like.

Benzoates such as dibenzoate of diphenylol propane, tertiary butyl benzoate of diphenylol propane, and the like.

Other ultraviolet light stabilizers that can be used include lower alkyl thiomethylene containing phenols, substituted benzenes such as 1,3-bis-(2'-hydroxybenzoyl)benzene, metal derivatives of 3,5-di-t-butyl-4-hydroxy phenyl propionic acid, asymmetrical oxalic acid diarylamides, alkylhydroxyphenyl-thioialkanoic acid ester and the like.

Particularly useful ultraviolet light stabilizers that can be used are hindered amines of bipiperidyl derivatives such as those in Murayama et al., U.S. Pat. No. 4,061,616, issued Dec. 6, 1977.

Typical antioxidants that are useful are as follows: tetrakis alkylene(di-alkyl hydroxy aryl)alkyl ester alkanes such as tetrakis methylene 3(3',5'-dibutyl-4'hydroxyphenyl)propionate methane, reaction product of p-amino diphenylamine and glycidyl methacrylate, reaction product of n-hexyl-N'-phenyl-p-phenylene diamine and glycidyl methacrylate, pentaerythritol tetrakis(thioglycolate), trimethylol propane tris(thioglycolate), trimethylol ethane tris(thioglycoate), N-(4-anilino phenyl)acrylamide and the like.

One preferred combination of ultraviolet light stabilizer and antioxidant is 2-hydroxy-4-dodecyloxy benzophenone or a substituted 2(2-hydroxyphenyl)benzotriazole and tetrakis methylene 3(3',5'-dibutyl-4'hydroxyphenyl)propionate methane.

The clear coat/color coat finish is applied by conventional spraying techniques and preferably the clear coat is applied to the color coat while the color coat is still wet. Other conventional application techniques as described above can be used. The finish is then baked at the above temperature.

The following Examples illustrate the invention. All parts and percentages are on a weight basis unless otherwise indicated. All molecular weights are determined by gel permeation chromatography using polymethyl methacrylate as a standard.

EXAMPLE 1

An acrylic polymer dispersion is prepared as follows:

______________________________________ Parts by Weight______________________________________Portion 1Methyl methacrylate monomer 151.84Diethyl aminoethyl methacrylate 2.48monomerAllyl methacrylate monomer 0.37Acetone 10.83Petroleum ether 7.37Toluene 45.86Diethylene glycol monohexyl ether 53.88Portion 2Solvent of mixed methyl esters of 16.90succinic acid, glutaric acidand adipic acidAzobisisobutyronitrile 0.74Portion 3Methyl methacrylate monomer 98.21Allyl methacrylate monomer 0.87Acetone 3.63Diethylene glycol monohexyl ether 34.16Petroleum ether 2.50Solvent of mixed methyl esters 27.58of succinic acid, glutaric acidand adipic acidAzobisisobutyronitrile 1.22Portion 42-Ethylhexyl acrylate monomer 22.93Methyl methacrylate monomer 5.18Petroleum ether 4.59Diethylene glycol monohexyl ether 13.4075% solution of t-butyl peroxy 0.33pivalate in mineral spiritsPortion 52-Ethylhexyl acrylate monomer 22.93Methyl methacrylate monomer 3.44Petroleum ether 2.29Diethylene glycol monohexyl ether 13.3775% solution of t-butyl peroxy 0.33pivalate in mineral spiritsPortion 6Methyl methacrylate monomer 14.22Diethylene glycol monohexyl ether 9.27Azobisisobutyronitrile 0.3275% solution of t-butyl 0.16peroxyl pivalate in mineral spiritsPortion 7Aliphatic hydrocarbon (petroleum 165.09fraction having essentiallythe same evaporation rate asmineral spirits but limited to8% of 8 carbon atom aromatics andabove, aniline point measured byASTM-D 1012-62 of 60 to 67.degree. C.)Portion 8Aliphatic hydrocarbon (described above) 57.3275% solution of t-butyl peroxy 0.28pivalate in mineral spiritsTotal 787.85______________________________________

Portion 1 is charged into a reaction vessel equipped with a stirrer, reflux condenser, thermometer, heat source and a nitrogen inlet. During the reaction, the constituents in the vessel are under constant agitation. Portion 1 is heated to its reflux temperature and held for 5 minutes at this temperature. The heat source is turned off. The heat resulting from the reaction maintains the reaction temperature of the resulting reaction mixture. Portion 2 is added to the reaction mixture and the mixture is held for 10 minutes at its reaction temperature. Portion 3 is added to the reaction mixture at a uniform rate over a 80 minute period and then the reaction mixture is held at its reaction temperature for an additional 15 minutes. Portion 4 is added to and the reaction mixture which is held at its reaction temperature for 15 minutes. Portion 5 is added to the reaction mixture at a uniform rate over a 35 minute period. Portion 6 is then added at a uniform rate over a 20 minute period and the reaction mixture is held at its reaction temperature for an additional 20 minutes. Portion 7 is then added at a uniform rate over a 50 minute period. Portion 8 is then added over a 50 minute period and the reaction mixture is cooled to 50.degree. C. and then filtered.

The resulting acrylic polymer dispersion has a polymer weight solid content of 40% and contains about 35% of a polymer of methyl methacrylate/allyl methacrylate/diethyl aminoethyl methacrylate in a weight ratio of about 98.4/0.6/1.0 and has a weight average molecular weight of about 110,000, 15% of a copolymer of 2-ethylhexyl acrylate/methyl methacrylate in a 1/1 weight ratio having a weight average molecular weight of about 30,000 and 50% of a graft copolymer of the above polymer which forms the backbone of the graft copolymer and the above copolymer which forms side chains of the graft copolymer having a weight average molecular weight of about 140,000.

The following mill bases are prepared:

______________________________________White Mill Base Parts By Weight______________________________________Portion 1Polymeric Dispersant Solution 8.44(62% polymer solids in toluene inwhich the polymer comprises methylmethacrylate/2-ethylhexyl acrylatehaving a number average molecularweight of 4500 and further reactedwith mercaptoethanol, a polyiso-cyanate and ammonia)Toluene 11.56Ethylene glycol monoethyl ether 2.00acetatePortion 2Titanium dioxide pigment 68.00Portion 3Acrylic polymer dispersion (prepared 2.00abovePortion 4Hydrocarbon Solvent 8.00Total 100.00______________________________________

Portion 1 is charged into a mixer and mixed for 5 minutes. Portion 2 is added and mixed for 2 hours and then Portion 3 is added and mixed for 30 minutes. Portion 4 is added and mixed for 30 minutes. The resulting mixture is then ground for one pass through a conventional 8 gallon sand mill containing 70 pounds of sand to form a white mill base.

______________________________________Green Mill Base Parts By Weight______________________________________Portion 1Ethylene glycol monoethyl- 10.00ether acetateToluene 20.00Polymeric dispersant solution 15.00(described above)Acrylic polymer dispersion 15.00(prepared above)VM and P Naphtha 25.00Portion 2"Monastral" green pigment B 15.00(phthalocyanine pigment)Total 100.00______________________________________

Portion 1 is premixed and then Portion 2 is added and the resulting composition is ground two passes in a conventional 8 gallon sand mill containing 70 pounds of sand at the rate of 30 gallons per minute to form a dispersion.

______________________________________Yellow Mill Base Parts By Weight______________________________________Portion 1Polymeric dispersant solution 28.40(described above)Toluene 12.60Portion 2Ferrite Yellow Pigment (iron 46.00oxide pigment)Portion 3Acrylic Polymer dispersion 3.00(prepared above)VM and P Naphtha 10.00Total 100.00______________________________________

Portion 1 is charged into a mixing vessel and mixed for 10 minutes and then Portion 2 is added and mixed for 1 hour. Portion 3 is added and mixed for 10 minutes and then Portion 4 is added and mixed for 30 minutes. The resulting mixture is charged into a sand mill, described above, and ground for one pass to form a dispersion.

______________________________________Blue Mill Base Parts By Weight______________________________________Portion 1Polymeric dispersant solution 15.00(described above)Toluene 36.00Portion 2"Monastral" blue flake 15.00(phthalocyanine pigment)Portion 3Acrylic polymer dispersion 20.00(prepared above)Portion 4VM and P Naphtha 14.00Total 100.00______________________________________

Portion 1 is charged into a mixing vessel and mixed for 10 minutes and then Portion 2 is added and mixed for 30 minutes. Portion 3 is added and mixed for 30 minutes and Portion 4 then is added and mixed for 30 minutes. The resulting mixture is charged into a conventional sand mill, described above, and ground for two passes to form a dispersion.

______________________________________Black Mill Base Parts By Weight______________________________________Portion 1Polymeric dispersant solution 38.00(described above)Toluene 17.00VM and P Naphtha 20.00Acrylic polymer dispersion 5.00(described above)Portion 2Carbon black pigment 20.00Total 100.00______________________________________

Portion 1 is premixed and Portion 2 is added and the resulting mixture is charged into an attritor containing 1/8 inch steel balls as the grinding media and ground for 3 hours to a 0.5 mil fineness.

______________________________________Aluminum Mill Base Parts By Weight______________________________________Portion 1Polyester resin plasticizer 11.50(85% of a polyester resin ofethylene glycol adipate/ethyleneglycol benzoate/ethylene glycolphthalate having an acid No. ofless than 10 and 15% of butylbenzylphthalate)Toluene 8.50Acrylic polymer dispersion 15.00(prepared above)Portion 2Aluminum flake paste (65% solids 12.50aluminum flake in aliphatic solvent)Portion 3Acrylic polymer resin dispersion 52.50(described above)Total 100.00______________________________________

Portion 1 is charged into a mixing vessel and mixed for 5 minutes. Portion 2 is added and mixed for 1 hour and then Portion 3 is added and mixed for 3 hours to form a dispersion.

A white high solids acrylic dispersion lacquer is formed as follows:

______________________________________ Parts By Weight______________________________________Portion 1Acrylic polymer dispersion 625.93(prepared above)Polyester resin plasticizer 25.73solution (described above)Alkyd resin plasticizer solution 25.73(85% of a coconut oil/ethylene glycol phthalateresin having an acid No.less than 10 and 15% butylbenzyl phthalate)Butyl benzyl phthalate 18.01Flow control agent (1% solution 0.29of light weight silicone oil inxylene)Portion 2White Mill Base 190.16(prepared above)Yellow Mill Base 0.86(prepared above)Black Mill Base 0.29(prepared above)Total 887.00______________________________________

Portion 1 is charged into a mixing vessel and mixed for 5 minutes and then Portion 2 is added and mixed for 1 hour to form the lacquer.

The above lacquer is reduced to a 34% volume solids by mixing the lacquer with the following thinner:

______________________________________ Parts By Weight______________________________________Petroleum Naphtha 50.00Diethylene glycol monohexyl ether 50.00Total 100.00______________________________________

The reduced lacquer is sprayed into phosphatized steel panels primed with an alkyd resin primer and coated with a sealer. Three coats are sprayed onto the panels and the panels are baked at about 165.degree. C. for 30 minutes to provide a finish that is about 2.2 mils thick. The resulting finish is smooth, glossy, water resistant, gasoline resistant, chip resistant, weatherable and has excellent distinctness of image. The lacquer is useful as a high quality automotive finish.

A blue metallic high solids acrylic dispersion lacquer is formed as follows:

______________________________________ Parts By Weight______________________________________Portion 1Hydrocarbon solvent 25.05(described above)Acrylic polymer dispersion 616.59(prepared above)Polyester resin plasticizer 28.55solution (described above)Alkyd resin plasticizer solution 34.41(described above)Butyl benzyl phthalate 27.232-Hydroxyl-4-dodecyloxy benzophenone 1.70Flow control agent (described above) 0.24Portion 2Aluminum Mill Base (prepared above) 50.89Blue Mill Base (prepared above) 10.80Black Mill Base (prepared above) 0.32Green Mill Base (prepared above) 0.22Total 796.00______________________________________

The above lacquer is reduced to a 34% volume solids by mixing the lacquer with the above thinner. The reduced lacquer is sprayed onto phosphatized steel panels primed and sealed as described above using the same spraying procedures and then the coated panels are baked under the above conditions giving a finish about 2.2 mils in thickness having the same properties as above including excellent metallic glamour. The lacquer is useful as a high quality automotive finish.

EXAMPLE 2

An acrylic polymer dispersion is prepared as follows:

______________________________________ Parts by Weight______________________________________Portion 1Methyl methacrylate monomer 627.1Diethyl aminoethyl methacrylate 10.8monomerAllyl methacrylate monomer 1.6Methanol 35.0Toluene 200.02-Ethyl hexanol 268.3Portion 2Methyl methacrylate monomer 35.0Azobisisobutyronitrile 3.3Portion 3Methyl methacrylate monomer 428.3Allyl methacrylate monomer 3.8Methanol 40.0Isobutyrate ester of 2,2,4-trimethyl- 310.01,3-pentanediolAzobisisobutyronitrile 5.3Portion 42-Ethylhexyl acrylate monomer 100.0Methyl methacrylate monomer 22.5Methanol 15.0Isobutyrate ester of 2,2,4-trimethyl- 62.11,3-pentanediol75% solution of t-butylperoxy 1.5pivalate in mineral spiritsPortion 52-Ethylhexyl acrylate monomer 100.0Methyl methacrylate monomer 15.02-Ethyl hexanol 55.075% solution of t-butylperoxy 1.5pivalate in mineral spiritsPortion 6Methyl methacrylate monomer 62.12-Ethyl hexanol 40.0Azobisisobutyronitrile 1.475% solution of t-butylperoxy 0.7pivalate in mineral spiritsPortion 7Aliphatic hydrocarbon (petroleum 770.0fraction having essentiallythe same evaporation rate asmineral spirits but limited to8% of 8 carbon atom aromatics andabove, aniline point measured byASTM-D 1012-62 of 60 to 67.degree. C.)Portion 8Aliphatic hydrocarbon (described above) 200.075% solution of t-butyl peroxy 1.2pivalate in mineral spiritsTotal 3416.5______________________________________

Portion 1 is charged into a reaction vessel equipped with a stirrer, reflux condenser, thermometer, heat source and a nitrogen inlet. During the reaction, the constituents in the vessel are under constant agitation. Portion 1 is heated to its reflux temperature and held for 5 minutes at this temperature. The heat source is turned off. The heat resulting from the reaction maintains the temperature of the reaction mixture. Portion 2 is added to the reaction mixture and the mixture is held for 10 minutes at this reaction temperature. Portion 3 is added to the reaction mixture at a uniform rate over a 90 minute period and then the reaction mixture is held at its reaction temperature for 15 minutes. Portion 4 is added to the reaction mixture and held at its reaction temperature for 15 minutes. Portion 5 is added to the reaction mixture at a uniform rate over a 35 minute period. Portion 6 is then added at a uniform rate over a 20 minute period and held at its reaction temperature for an additional 20 minutes. Portion 7 is then added at a uniform rate over a 50 minute period. Portion 8 is then added over a 50 minute period and the reaction mixture is cooled to 50.degree. C. and then filtered.

The resulting acrylic polymer dispersion has a polymer weight solids content of 40% and contains about 35% of a polymer of methyl methacrylate/allyl methacrylate/diethyl aminoethyl methacrylate in a weight ratio of about 98.4/0.6/1.0 and has a weight average molecular weight of about 110,000, 15% of a copolymer of 2-ethylhexyl acrylate/methyl methacrylate in a 1/1 weight ratio having a weight average molecular weight of about 30,000 and 50% of a graft copolymer of the above polymer which forms the backbone of the graft copolymer and the above copolymer which forms side chains of the graft copolymer having a weight average molecular weight of about 140,000.

A blue metallic high solids acrylic dispersion lacquer is formed using the same constituents as used in Example 1 except the above prepared acrylic polymer dispersion is substituted for the acrylic polymer dispersion of Example 1. The lacquer is reduced as in Example 1, spray applied to phosphatized primed and sealed steel panels described in Example 1 and baked under the same conditions as in Example 1. The resulting finish is about 2.2 mils thick and has the same properties as the finish of Example 1 including excellent metallic glamour.

Claims

1. A high solids acrylic dispersion lacquer coating composition having an acrylic polymer binder content of about 25-45% by weight in a nonaqueous medium; wherein the acrylic polymer binder consists essentially of about

(1) 25-45% by weight, based on the weight of the binder, of Polymer A comprising about 90-99.5% by weight, based on the weight of Polymer A, of polymerized methyl methacrylate and about 0.1-5% by weight, based on the weight of Polymer A, of polymerized allyl methacrylate and 0.4-5% by weight, based on the weight of Polymer A, of polymerized alkyl amino alkyl methacrylate and having a weight average molecular weight, measured by gel permeation chromatography, of about 90,000-130,000;

(2) 5-25% by weight, based on the weight of the binder, of Copolymer B comprising about 40-60% by weight, based on the weight of Copolymer B, of polymerized methyl methacrylate and 40-60% by weight, based on the weight of Copolymer B, of polymerized alkyl acrylate having 6-12 carbon atoms in the alkyl group and having a weight average molecular weight, measured as above, of about 20,000-40,000; and

(3) 40-60% weight, based on the weight of the binder, of a graft copolymer of Polymer A which forms a backbone of the graft copolymer and Copolymer B attached to the backbone which forms side chains of the graft copolymer; and

wherein

the nonaqueous medium comprises

(a) an aliphatic solvent which is at 25.degree. C. a nonsolvent for Polymer A and a solvent for Copolymer B; and

(b) a coalescing solvent which at 50.degree. C. and above is a solvent for the binder and at 25.degree. C. is a nonsolvent for the binder.

2. The coating composition of claim 1 containing pigment in a pigment to binder weight ratio of about 1/100 to 150/100.

3. The coating composition of claim 2 in which Polymer A consists essentially of methyl methacrylate, allyl methacrylate and diethyl amino methacrylate.

4. The coating composition of claim 2 in which Copolymer B consists essentially of methyl methacrylate and 2-ethylhexyl acrylate.

5. The coating composition of claim 3 in which Polymer A consists essentially of 90-99.5% by weight of methyl methacrylate, 0.1-5% by weight of allyl methacrylate and 0.4-5% by weight of diethyl amino ethyl methacrylate and having a weight average molecular weight of about 100,000-115,000.

6. The coating composition of claim 4 in which Copolymer B consists essentially of about 40-60% by weight of methyl methacrylate and 40-60% by weight of 2-ethylhexyl acrylate and has a weight average molecular weight of about 20,000-40,000.

7. The coating composition of claim 2 containing about 15-30% by weight, based on the weight of the composition, of a plasticizer.

8. The coating composition of claim 7 in which the plasticizer is selected from the group consisting of butyl benzyl phthalate, coconut oil/ethylene glycol phthalate resin or an ethylene glycol phthalate/ethylene glycol benzoate/ethylene glycol adipate resin.

9. The coating composition of claim 1 wherein the nonaqueous medium comprises about

(a) 35-65% by weight, based on the weight of the nonaqueous medium of an aliphatic solvent; and

(b) 35-65% by weight of coalescing solvent.

10. The high solids acrylic dispersion lacquers coating composition of claim 1 containing pigment in a pigment to binder ratio of about 1/100-150/100 and in which the acrylic polymer consists essentially of

(1) Polymer A consisting essentially of 90-99.5% by weight, based on the weight of Polymer A, of methyl methacrylate, 0.1-5% by weight of allyl methacrylate and 0.4-5% by weight of diethyl aminoethyl methacrylate and has a weight average molecular weight of about 100,000-115,000;

(2) Copolymer B consisting essentially of 40-60% by weight, based on the weight of Copolymer B, of methyl methacrylate and 40-60%, based on the weight of Copolymer B, of 2-ethylhexyl acrylate and has a weight average molecular weight of about 20,000-40,000;

(3) a graft copolymer of Polymer A which forms the backbone of the graft copolymer and Copolymer B which forms the side chains of the graft copolymer;

and

contains about 15-30% by weight, based on the weight of the composition, of an organic plasticizer; wherein the nonaqueous medium comprises about

(a) 35-65%, based on the weight of the nonaqueous medium, of an aliphatic nonsolvent for Polymer A and a solvent for Copolymer B which is a petroleum fraction having a boiling point of about 100.degree.-160.degree. C.;

(b) 35-65% by weight, based on the weight of the nonaqueous medium, of a coalescing solvent of diethylene glycol monohexyl ether.

11. The coating composition of claim 10 containing up to about 15% by weight based on the weight of the nonaqueous medium, of a bridging solvent comprising toluene.