Patent Application
20230088978
The invention relates generally to methods of manufacturing components formed of aluminum alloys, and more particularly components used in automotive vehicle applications.
Structural components for automotive vehicle applications, such as bumpers and reinforcements, are oftentimes formed from aluminum alloys, rather than steel, due to the lighter weight of aluminum alloys. Typically, the component is formed to a complex three-dimensional shape, depending on the particular application in which the component is used. A high strength and specific temper designation is also typically required in the finished component.
The high-strength, light-weight aluminum component can be manufactured using a warm or hot forming process. For example, a stamping process including heat treatment and post tempering in an oven can be used to achieve the desired strength and temper designation. The stamping process can then be followed by machining the component to the complex three-dimensional shape. However, hot or warm stamping with post tempering and machining processes require high manufacturing costs and capital investment, which ultimately increases the price of the aluminum component and could outweigh the other benefits.
The invention provides a method of manufacturing a high-strength, light-weight component formed of an aluminum alloy and having a complex three-dimensional shape with reduced manufacturing costs and capital investment. The method includes providing a blank formed of an aluminum alloy selected from the group consisting of a 2000, 6000, 7000, 8000, and 9000 series aluminum alloy, wherein the aluminum alloy has already been solution heat treated and tempered. The method further includes heating the heat treated and tempered blank to a temperature of 150° C. to 350° C.; and forming the blank into a component having a three-dimensional shape after the heating step. During or immediately after the forming step, the aluminum alloy has a tensile strength and yield strength close to its maximum tensile and yield strength, and thus no post heat treatment process is required. In addition, a complex three-dimensional shape can be achieved during the forming step, such that no post machining process is required.
The invention also provides a component having a three-dimensional shape for use in an automotive vehicle application. The aluminum alloy is selected from the group consisting of: a 2000, 6000, 7000, 8000, and 9000 series aluminum alloy, and the aluminum alloy of the finished component has a temper designation close to T6. The temper designation is achieved by heating a solution heat treated and tempered blank formed of the aluminum alloy to a temperature of 150° C. to 350° C. before forming the blank to the three-dimensional shape.
Other advantages of the present invention will be readily appreciated, as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings, wherein:
The invention provides a method of manufacturing a component 10 having a complex three-dimensional shape for use in an automotive vehicle application, such as a bumper or reinforcement. The component 10 is formed from an aluminum alloy to achieve a high strength and light-weight. In addition, the method can be performed with reduced manufacturing costs and reduced capital investment, compared to other methods used to manufacture similar high-strength, light-weight components.
The method first includes providing a blank 12 formed of the aluminum alloy. The blank 12 is typically a sheet of material, but can comprise any size and shape depending on the desired size and shape of the finished component 10. The aluminum alloy used to form the blank 12 is a 2000, 6000, 7000, 8000, or 9000 series aluminum alloy, which are internationally standardized alloys and well known in the art. Each series represents a different type of alloy, and each alloy within a series is registered by the Aluminum Association (AA). For example, aluminum alloys in the 2000 series are known as high strength alloys and typically include copper as the main alloying element, as well as magnesium. Alloys in the 6000 and 7000 series are also known as high strength alloys and are typically strengthened by heat treatment through precipitation of their main alloying elements, which are silicon and magnesium for the 6000 series, and copper, zinc, and magnesium for the 7000 series. The 8000 series alloys include less frequently used alloying elements, such as iron or tin. The 9000 series alloys are those that do not fall into one of the other series and are referred to as unassigned.
The blank 12 formed of the aluminum alloy is provided after already being solution heat treated and tempered. The solution heat treated and tempered blank 12 could be provided with a desired shape, or cut from a larger piece of material which has already been solution heat treated and tempered. Solution heat treating generally includes softening the aluminum alloy by heating and maintaining the alloy at an elevated temperature so that all of the alloying elements are in a single phase, solid solution. Tempering generally includes increasing the strength and/or hardness of the aluminum alloy by heating. After the solution heat treatment and tempering process, the aluminum alloy of the blank 12 typically has a temper designation of T4, or a temper designation that is close to T4. The T4 temper designation, as well as other temper designations T1-T10, are also registered by the Aluminum Association and are well known in the art. A list of all registered temper designations is published in the American National Standards Institute (ANSI) H35.1.
The method next includes heating the solution heat treated and tempered blank 12 to an elevated temperature in an oven or furnace 14, as shown in
The heating time and temperature should be selected so that the temper designation of the resulting component 10 is about T6, or close to T6, but preferably does not exceed a T6 temper, which could cause over-aging and corrosion issues. The time and temperature of the heating step can also be used to achieve the desired yield strength and/or tensile strength in the finished component 10. For example, for a 7000 series aluminum alloy, if the heating step includes holding the blank 12 at 204° C. for 6 minutes, then the yield strength and tensile strength of the 7000 series aluminum alloy after the heating step is about 75% of the yield strength ratio and tensile strength ratio, i.e. 75% of the maximum tensile yield and maximum tensile strength; and the finished component 10 has a yield strength and tensile strength of about 80% of the tensile strength ratio and yield strength ratio. In another embodiment, wherein the heating step is conducted at 232° C. for 6 minutes, the yield strength and tensile strength of the aluminum alloy is about 50% of the yield strength ratio and tensile strength ratio after the heating step, and the yield strength and tensile strength of the aluminum alloy in the resulting component 10 is about 70% of the yield strength ratio and tensile strength ratio. If the heating step is conducted at 275° C. for 6 minutes, then the yield strength and tensile strength of the aluminum alloy is about 30% of the yield strength ratio and tensile strength ratio after the heating step, and the yield strength and tensile strength of the aluminum alloy in the resulting component 10 is about 60% of the yield strength ratio and tensile strength ratio.
After the heating step, the method includes quickly transferring the heated blank 12 to the forming apparatus 16, as shown in
In the exemplary embodiment of
Once the heated blank 12 is disposed in the forming apparatus 16, the method includes forming the heated blank 12 while the blank 12 is still at an elevated temperature, for example at a temperature of at least 150° C., or 150° C. to 350° C., or 190° C. to 225° C., or at least 204° C. The forming step typically includes stamping or pressing the blank 12 between upper forming tool 18 and lower forming tool 20. However, other techniques can be used to form the blank 12 to the desired shape after heating the solution heat treated and tempered blank 12 to the temperature of 150° C. to 350° C. and transferring the heated blank 12 to the furnace within 15 seconds. The alloy composition and temperature of the heating step allows complex three-dimensional shapes to be formed during the forming step without any post machining, which reduces manufacturing costs.
After the forming step, the finished component 10 is removed from the forming apparatus 16 and is ready for use in an automotive vehicle application, as shown in
The method described above provides a blank 12 with a high temper designation and strength after the heating step, and allows the aluminum alloy to maintain a high temper designation and strength during and after the forming step. For example, when the solution heat treated and tempered blank 12 provided at the beginning of the process (before the heating step) has a temper designation around T4, then the finished component 10 has a temper designation around T6, and preferably slightly below T6. The temper designation around T6 is achieved during the forming step, or immediately after the forming step. In other words, the aluminum alloy of the finished component 10 has a tensile strength equal to or greater than the minimum tensile strength of the same aluminum alloy having a temper designation of about T6. Thus, the component 10 is strong enough for use in many automotive vehicle applications, such as bumpers and reinforcements, without a costly post heating step.
The method can also including cooling or quenching the component 10 after the forming step. However, the cooling or quenching step does not change the physical or chemical properties of the aluminum alloy of the component 10. For example, the cooling step can including cooling the component 10 to room temperature, for example a temperature of about 30° C. In one embodiment, the cooling step is conducted in the forming apparatus 16, for example by conventional water cooling. In another embodiment, the component 10 is naturally cooled at room temperature outside the forming apparatus 16.
Another aspect of the invention provides a component 10 having a complex three-dimensional shape for use in an automotive vehicle application and manufactured according to the method described above. The component 10 is formed from an aluminum alloy selected from a 2000, 6000, 7000, 8000, and 9000 series aluminum alloy. The aluminum alloy of the finished component 10 also has a temper designation which is close to T6, and preferably not greater than T6. As described above, the temper designation of the finished component 10 is achieved by heating a solution heat treated and tempered blank 12 formed of the aluminum alloy to a temperature of 150° C. to 350° C. before forming the blank 12 to the three-dimensional shape. The aluminum alloy of the finished component 10 preferably has a tensile strength equal to or greater than the minimum tensile strength provided by a temper designation of about T6. In one embodiment, the component 10 is used in a bumper or reinforcement application, but it can be used in various other applications, particularly those requiring light-weight and high strength.
Many modifications and variations of the present invention are possible in light of the above teachings and may be practiced otherwise than as specifically described while within the scope of the following claims.
This U.S. Continuation patent application claims the benefit of U.S. Divisional patent application Ser. No. 16/988,836 filed Aug. 10, 2020 entitled “High Strength Aluminum Stamping”, which claims the benefit of U.S. National Stage patent application Ser. No. 15/113,821 filed Jul. 23, 2016 now U.S. Pat. No. 10,774,408 entitled “High Strength Aluminum Stamping,” which claims the benefit of PCT International Patent Application Serial No. PCT/US2015/012588 filed Jan. 23, 2015 entitled “High Strength Aluminum Stamping,” which claims the benefit of U.S. Provisional Patent Application Ser. No. 61/931,254 filed Jan. 24, 2014, entitled “High Strength Aluminum Hot Stamping,” the entire disclosures of the applications being considered part of the disclosure of this application and hereby incorporated by reference.
| Number | Date | Country | |
|---|---|---|---|
| 61931254 | Jan 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15113821 | Jul 2016 | US |
| Child | 16988836 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16988836 | Aug 2020 | US |
| Child | 18070159 | US |