High strength, high capacity filter media and structure

Information

  • Patent Grant
  • 7985344
  • Patent Number
    7,985,344
  • Date Filed
    Tuesday, November 20, 2007
    16 years ago
  • Date Issued
    Tuesday, July 26, 2011
    12 years ago
Abstract
In the filtration of fluid materials, the removal of particulate from the moving stream requires substantial pressure to maintain flow and substantial capacity for removing particulate. The filters of the invention are rugged, high wet strength materials having a basis weight, permeability and efficiency suitable to obtain substantial reduction in particulate loading from liquid streams without plugging or mechanical failure. In particular, the filters of the invention permit the removal of substantial proportions of particulate from non-aqueous streams including lubricant oils, hydraulic fluids and other contaminated streams.
Description
FIELD OF THE INVENTION

The invention relates to a filtration medium and a filter using the medium. The medium has high strength, efficiency and high capacity for filtration of particulate from a stream. The filter medium or media comprise a non-woven web suitable for removal of particulate from mobile fluids such as aqueous streams and non-aqueous streams including fuels, lubricating oils and hydraulic fluids. The invention relates to non-woven media layers obtaining sufficient wet strength, particulate efficiency, permeability and other properties to survive the common operating conditions, such as variation in flow rate, temperature, pressure and particulate loading while removing substantial particulate loads from the liquid stream. The invention further relates to filter structures comprising one or more layers of the particulate removing media with other layers of similar or dissimilar media. These layers can be supported on a porous or perforate support and can provide mechanical stability during filtering operations. Lastly, the invention relates to a method of filtering both aqueous and non-aqueous fluids.


BACKGROUND OF THE INVENTION

Non-woven webs have been manufactured for many years for many end uses, including filtration media. Such structures made from bicomponent or sheath-core materials are disclosed in, for example, Wincklhofer et al., U.S. Pat. No. 3,616,160; Sanders, U.S. Pat. No. 3,639,195; Perrotta, U.S. Pat. No. 4,210,540; Gessner, U.S. Pat. No. 5,108,827; Nielsen et al., U.S. Pat. No. 5,167,764; Nielsen et al., U.S. Pat. No. 5,167,765; Powers et al., U.S. Pat. No. 5,580,459; Berger, U.S. Pat. No. 5,620,641; Berger, U.S. Pat. No. 6,174,603; Hollingsworth et al., U.S. Pat. No. 6,146,436; Dong, U.S. Pat. No. 6,251,224; Sovari et al., U.S. Pat. No. 6,355,079; Hunter, U.S. Pat. No. 6,419,721; Cox et al., U.S. Pat. No. 6,419,839; Stokes et al., U.S. Pat. No. 6,528,439; Amsler, U.S. Pat. No. H2,086 and Amsler, U.S. Pat. No. 6,267,252. Such structures have been made by both air laid and wet laid processing and have been used in both air and liquid filtration applications with some degree of success. In this regard we have found that the previous non-woven webs that are used for particulate removal from mobile fluids often suffer from a lack of mechanical strength and short useful life when wet by liquid under filtration condition. Often the pressure of the fluid exceeds the wet burst strength of the media. The media can also become rapidly plugged and reduced in permeability causing reduced flow or failure of fluid movement. Burst or plugged media rapidly fail to filter particulate. A burst media would fail to protect the equipment from particulate it was designed to protect. Substantially increased or high pressure drop would restrict the fluid flow resulting in loss of fluid flow and power.


Many attempts to obtain non-woven structures with suitable perforate or porous supports have been attempted. Melt blown materials and thermal lamination techniques have been attempted, however, the resulting structures often obtain incorrect pore sizes, reduced efficiency, reduced permeability, lack of strength or other problems rendering the media or filter structure insufficient for useful filtration applications.


A substantial need exists for filtration media, filter structures and filtration methods that can be used for removing particulate materials from liquid compositions, such as aqueous liquids and in particular, non-aqueous liquids such as fuels, lubricating oils and hydraulic fluids. The invention provides such media, filtration structures and methods and provides a unique media or media layer combinations that achieve substantial permeability, high wet strength, substantial efficiency and long filtration life.


BRIEF DESCRIPTION OF THE INVENTION

We have found a filter media and a unique filter structure capable of removing particulate from liquid streams. The media comprises a thermally bonded sheet made by combining a substantial proportion of an inorganic glass fiber, a fiber blend of differing fiber diameters, and a bicomponent thermoplastic binder fiber. Such a medium can be made with optimal secondary fibers and other additive materials. These components combine to form a filter medium or non-woven material having substantial flow capacity, permeability and high strength. The media of the invention can maintain intact filtration capacity at high pressure for a substantial period of time. The media and filter operate at substantial flow rate, high capacity and substantial efficiency.


A first aspect of the invention comprises a filtration media or medium having a thermally bonded non-woven structure.


A second aspect of the invention comprises a bilayer filtration medium or media comprising at least one loading layer and at least one efficiency layer with the mobile fluid passing first through the loading layer.


A third aspect of the invention comprises a filter structure comprising a filtration media of the invention, a loading layer filtration media of the invention, an efficiency layer filtration media of the invention or combinations thereof also combined with other filtration layers, support structures and other filter components.


A fourth aspect of the invention comprises a depth loading layer that can be used as a stand alone layer or as a combination with an efficiency layer. The depth layer can be responsible for a large part of the high performance character of this media, where the depth loading media that does not compress or tear when subjected to application conditions.


Lastly, a fifth aspect of the invention comprises a method of filtering the mobile liquid phase having a particulate load using the filtration aspects of the invention.


In general, the technology can be applied to filtering liquid systems. In liquid filtering techniques, the collection mechanism is believed to be sieving. In a single layer the efficiency is that of the layer. The composite efficiency in a liquid application is limited by the efficiency of the single layer with the highest efficiency. The liquids would be directed through the media according to the invention, with particulates therein trapped in a sieving mechanism. In liquid filter systems, i.e. wherein the particulate material to be filtered is carried in a liquid, such applications include aqueous and non-aqueous and mixed aqueous/non-aqueous applications such as water streams, lube oil, hydraulic fluid, fuel filter systems or mist collectors. Aqueous streams include natural and man-made streams such as effluents, cooling water, process water, etc. Non-aqueous streams include gasoline, diesel fuel, petroleum and synthetic lubricants, hydraulic fluid, brake fluid and other ester based working fluids, cutting oils, food grade oil, etc. Mixed streams include dispersions comprising water in oil and oil in water compositions and aerosols comprising water and a non-aqueous component.


A substantial proportion of glass fiber is used in the manufacture of the media of the invention. The glass fiber provides pore size control and cooperates with the other fibers in the media to obtain a media of substantial flow rate, high capacity and substantial efficiency. The term glass fiber “source” means a glass fiber composition characterized by an average diameter and aspect ratio that is made available as a distinct raw material. Blends of fiber obtained from such sources that vary in diameter do not read on single source.


Other fibers called “secondary fibers” can also be used in the manufacture of the media layer of the invention. Secondary fibers are single component fibers that add some aspect of layer formation or filter property to the medium. Such secondary fibers can add to the filtration properties of the invention, but it can also act as “binder fibers” in binding the fibrous mat into a useful media web. These fibers can add to the filtration characteristic of the media or can add to the binder characteristic of the bicomponent fiber. The term “secondary fibers” can include a variety of different fibers from natural synthetic or specialty sources. Secondary fibers are typically monocomponent fibers with a diameter that can range from about 0.1 to about 100 micrometers and can be made from a variety of materials including naturally occurring cotton linters wool, various cellulosic and proteinaceous natural fibers, synthetic fibers including rayon, acrylic, aramide, nylon (including nylon 6, nylon 6,6, nylon 6,12, etc.), polyolefin (including polyethylene's, polypropylenes), polyester fibers (including polyethylene terephthalate, polybutylene terephthalate, PCT, etc). Additionally, the binder fiber can include fibers made from such polymers as polyvinyl chloride, polyvinyl alcohol. Secondary fibers can also include inorganic fibers such as carbon/graphite fiber, metal fiber, ceramic fiber and combinations thereof.


The preferred filter structure of the invention comprises at least one filtration media layer of the invention supported on a mechanically stable perforate support structure. The filtration layer can comprise two media layers, a loading layer and an efficiency layer, of the invention with cooperating functions to achieve excellent particulate removal at high efficiency. While the differences between the loading and efficiency layers can be difficult to separate when made in serial fashion, we believe that the layers have the following general and preferred characteristics.









TABLE 1







General Characteristics













Weight







Lbs/
Perm,
Thickness
Loading
βx =


Description
3000 ft2
Ft-min−1
Inches
gms/ft2
75 μm















Efficiency layer
15-50
5-50
0.01-0.02
12
9


Loading layer
25-50
40-200
0.015-0.025
23
12


Laminated
 50-150
5-50
0.04-0.05
17
9


composite







Nw loading layer
25-50
50-125
0.01-0.02




New efficiency
50-75
10-45 
0.02-0.04
13
10


layer







New composite
 50-150
10-50 
0.025-0.055
19
11
















TABLE 2







Preferred Characteristics













Weight







Lbs/
Perm,
Thickness
Loading
βx =


Description
3000 ft2
Ft-min−1
Inches
gms/ft2
75 μm















Efficiency layer
40-50
20-40
0.01-0.02
12
9


Loading layer
35-45
120-140
0.015-0.025
23
12


Laminated
100-125
15-35
0.04-0.05
17
9


composite







Nw loading layer
30-40
100-140
0.01-0.02




New efficiency
50-75
20-40
0.02-0.04
13
10


layer







New composite
 75-127
15-40
0.025-0.055
19
11
















TABLE 3







Specific Characteristics













Weight







Lbs/
Perm,
Thickness
Loading
βx =


Description
3000 ft2
Ft-min−1
Inches
gms/ft2
75 μm















Efficiency layer
42
28
0.018
12
9


Loading layer
40
135
0.022
23
12


Laminated
110
21
0.045-0.050
17
9


composite







Nw loading layer
35
115
0.015-0.020




New efficiency
65
30
0.03
13
10


layer







New composite
100
22
0.05
19
11









The perforate structure supports the media under the influence of fluid under pressure passing through the media. The filter structure of the invention can also be combined with additional layers of the perforate support, high permeability mechanically stable scrim and additional filtration layers such as a loading layer. This multilayer media commonly is housed in a filter cartridge commonly used in the filtration of non-aqueous liquids.


“Bicomponent fiber” means a thermoplastic material having at least one fiber portion with a melting point and a second thermoplastic portion with a lower melting point. The physical configuration of these fibers is typically in a “side-by-side” or “Sheath-core” structure. In side-by-side structure, the two resins are typically extruded in a connected form in a side-by-side structure. In the sheath-core structure, the low melting point (about 100 to 120° C. thermoplastic is typically extruded around a fiber of the higher melting typically over 240° C.) point material. The lower melting polymer acting as a thermoplastic binding agent, the melt polymer adhering the component and the higher melting thermoplastic acting as a structural material. In use, the bicomponent fibers typically have a fiber size or diameter of about 10 to 20 micrometers and are typically in a fiber form having a length of about 6 to about 12 mm, preferably about 6 mm. The cross-sectional structure of such fibers can be, as discussed above, the “side-by-side” or “Sheath-core” structure or other structures that provide the same thermal bonding function. The value of the bicomponent fiber is that the relatively low molecular weight resin can melt under sheet forming conditions to act to bind the bicomponent fiber, and other fibers present in the sheet making material into a mechanically stable sheet. Typically, the polymers of the bicomponent (Sheath-core and side-by-side) fibers are made up of different thermoplastic materials, such as for example, polyolefin/polyester (Sheath-core) bicomponent fibers whereby the polyolefin, e.g. polyethylene sheath, melts at a temperature lower than the core, e.g. polyester. Typical thermoplastic polymers include polyolefins, e.g. polyethylene, polypropylene, polybutylene, and copolymers thereof, polytetrafluoroethylene, polyesters, e.g. polyethylene terephthalate, polyvinyl acetate, polyvinyl chloride acetate, polyvinyl butyral, acrylic resins, e.g. polyacrylate, and polymethylacrylate, polymethylmethacrylate, polyamides, namely nylon, polyvinyl chloride, polyvinylidene chloride, polystyrene, polyvinyl alcohol, polyurethanes, cellulosic resins, namely cellulosic nitrate, cellulosic acetate, cellulosic acetate butyrate, ethyl cellulose, etc., copolymers of any of the above materials, e.g. ethylene-vinyl acetate copolymers, ethylene-acrylic acid copolymers, styrene-butadiene block copolymers, Kraton rubbers and the like. Particularly preferred in the present invention is a bicomponent fiber known as 271P available from DuPont. Other fibers include FIT 201, Kuraray N720 and the Nichimen 4080. All of these demonstrate the characteristics of cross-linking the sheath poly upon completion of first melt. This is important for liquid applications where the application temperature is typically above the sheath melt temperature. If the sheath does not fully crystallize then the sheath polymer will remelt in application and coat or damage downstream equipment and components.


“Glass fiber” is fiber made using glass of various types. The glass fibers used in papers of the present invention include glass types known by the designations: A, C, D, E, Zero Boron E, ECR, AR, R, S, S-2, N, and the like, and generally, any glass that can be made into fibers either by drawing processes used for making reinforcement fibers or spinning processes used for making thermal insulation fibers. Such fiber is typically used as a collection of fiber of diameter about 0.1 to 10 micrometers and an aspect ratio (length divided by diameter) of about 10 to 10,000.


We have found that by blending various proportions that substantially improved permeability can be obtained by blending various fiber diameters. Typically, glass fibers produced in a product having a fiber diameter within a certain range of variation. We have found that blending various (average fiber diameter) sizes of fibers, about 0.1 to about 1 micron, about 0.3 to 2, about 0.5 to 3 about 0.75 to 5 or about 3 to 10 micrometers, can result in high permeability and excellent flow. The term blend in this context means that the medium contains at least some of at least two different fiber sources of differing dimensions typically different diameters.


Some amount of a resinous binder component is necessary to obtain adequate strength for the non-woven media of this invention. Resin used as binder can be in the form of water soluble or dispersible polymer added directly to the paper making dispersion or in the form of thermoplastic binder fibers of the resin material intermingled with the aramide and glass fibers to be activated as a binder by heat applied after the non-woven is formed. Dispersing the fibers and then adding the binder material or dispersing the binder material and then adding the fibers comprise two processes for dispersion formation. Combining a dispersion of fibers with a dispersion of the binder material can also, make the dispersion. The concentration of fibers in the dispersion can range from 0.01 to 1 weight percent based on the total weight of the dispersion. The concentration of binder material in the dispersion can range from 5 to 50 weight percent based on the weight of the fibers; and, if the binder material is fibrids, the concentration can range from 15 to 35 weight percent based on the total weight of the paper.


Wet laid or dry laid processes can be used. In making the media of the invention, a fiber mat is formed using either wet or dry processing. The mat is heated to form the media by internally adhering the fibers. The bicomponent fiber used in the media of the invention permits the fiber to fuse into a mechanically stable mass. The bicomponent fiber having a thermally bonding exterior sheath causes the bicomponent fiber to bind with other fibers in the media layer. The bicomponent fiber cooperates with the aqueous resin and other fibers to form the medium.


Such a medium typically comprises a thin layer with substantial filtration properties. In many applications, especially those involving relatively high flow rates, an alternative type of filter media, sometimes generally referred to as “depth” media, can be used. A typical depth media comprises a relatively thicker tangle of fibrous material than standard media. Depth media is generally defined in terms of its porosity, density or percent solids content. For example, a 2-3% solidity media would be a depth media mat of fibers arranged such that approximately 2-3% of the overall volume comprises fibrous materials (solids), the remainder being air or gas space. Another useful parameter for defining depth media is fiber diameter. If percent solidity is held constant, but fiber diameter (size) is reduced, pore size is reduced; i.e. the filter becomes more efficient and will more effectively trap smaller particles. A typical conventional depth media filter is a deep, relatively constant (or uniform) density, media, i.e. a system in which the solidity of the depth media remains substantially constant throughout its thickness. By “substantially constant” in this context, it is meant that only relatively minor fluctuations in density, if any, are found throughout the depth of the media. Such fluctuations, for example, may result from a slight compression of an outer engaged surface, by a container in which the filter media is positioned. In general, a depth media arrangement can be designed to provide “loading” of particulate materials substantially throughout its volume or depth. Thus, such arrangements can be designed to load with a higher amount of particulate material, relative to surface-loaded systems, when full filter lifetime is reached. However, in general the tradeoff for such arrangements has been efficiency, since, for substantial loading, a relatively low solids media is desired. Gradient density systems such as those in the patents referred to above have been designed to provide for substantial efficiency and longer life. In some instances, surface-loading media is utilized as a “polish” filter in such arrangements. In the preferred wet laid processing, the medium is made from an aqueous furnish comprising a dispersion of fibrous material in aqueous medium. The aqueous liquid of the dispersion is generally water, but may include various other materials such as pH adjusting materials, surfactants, defoamers, or other processing aids and the like. The aqueous liquid is usually drained from the dispersion by conducting the dispersion onto a screen or other perforated support retaining the dispersed solids and passing the liquid to yield a wet paper composition. The wet composition, once formed on the support, is usually further dewatered by vacuum or other pressure forces and further dried by evaporating the remaining liquid.


The media of this invention can be made on equipment of any scale from laboratory screens to commercial-sized papermaking machinery such as Fourdrinier, inclined wire, and cylinder wire machines, and combinations of them. The general process involves making a dispersion of fibers, glass fibers, and binder material in an aqueous liquid, draining the liquid from the dispersion to yield a wet composition, and heating the wet composition to both dry and thermally bond the fiber into a layer to form the useful medium. This can be done in one step or a series of steps.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 shows in graphical data our experience in the use of bicomponent fibers in filtration media. The use of bicomponent fiber (all other variables being held constant) provides substantial increase in filtration capacity of the media of the invention, the media maintaining substantial mechanical strength.



FIG. 2 shows an increase in effective particulate loading resulting from the use of a bicomponent fiber.



FIG. 3 shows an increase in effective particulate loading resulting from the use of a bicomponent fiber in a resin saturated media.



FIG. 4 shows multipass results of similar hand sheets that can be resin saturated or resin free.



FIG. 5 is a cross section of a spin on cartridge filter aspect of the invention using a pleated media layer for filtering liquids.



FIG. 6 is a cross sectional top view of the pleated media of the invention supported by a perforate metal support. This combination is one aspect of the supported media of the invention.



FIG. 7 shows a side view of the down flow side of a pleated media of the invention supported by a screen support.





DETAILED DESCRIPTION OF THE INVENTION

The medium or media of the invention relates to a composite, non-woven, air laid or wet laid material having formability, stiffness and rigidity, and mechanical stability for filtration properties; high particulate loading capability, low pressure drop during use and a pore size and efficiency suitable for use in filtering fluids. Preferably, the filtration media of the invention is typically wet laid and is made up of randomly oriented array of media fiber and bicomponent fiber that are bonded together using the bicomponent binder fiber and the binder resin of the invention. Heat is used to activate the thermoplastic binding agents in the binder fiber and the resin. The media that can be used in the filters and methods of the invention contain a media fiber, a bicomponent binder fiber, a binder and other components. The medium or media can be formed into substantially planar sheets or formed into a variety of geometric shapes using forms to hold the wet composition during thermal bonding. The media fiber of the invention includes glass, metal, silica and other related fibers. The preferred fiber for use in the invention is a glass fiber having an aspect ratio of 10 to 10,000 and a diameter that can range from about 0.1 to about 10 micrometers in diameter while preferred materials are blends of glass fiber of differing dimensions.


The filter media of the present invention is typically suited for high efficiency filtration properties such that liquids, including aqueous and non-aqueous fuel, lubricant, hydraulic or other such fluids can be rapidly filtered to remove contaminating particulates.


We have found that two filter media of this description can be combined, a loading layer and an efficiency layer, each of said layers having distinct structures and filtration properties to form a composite layer. The layers are distinct structures with different filtration properties that cooperate to obtain filtration performance. In the manufacturing process is formed the efficiency layer first, allowing more of the finer glass fibers to deposit on the efficiency or wire side of the medium. This aids in forming a gradient structure for improved loading performance. The loading layer is then formed on top of the efficiency layer. Preferably before the efficiency layer is completely formed. This allows some intermingling of the fibers between the two layers, forming a gradient structure and enhancing the strength and bond between the layers. When adding the loading layer you also allow the finer fibers to more intermingle with the efficiency layer. When forming the efficiency layer some of the finest fibers are lost through the forming screen or wire. When you form the loading layer, you loose very few of the finest fibers because they are captured and intermingled with the original efficiency layer. The performance, both filtration and physical properties, of sheets formed together vs formed separately and laid on top of each other are different. The efficiency layer is a highly efficient layer having suitable porosity efficiency permeability and other filtration characteristics to remove any remaining harmful particulate from the fluid stream as the fluid passes through the filter structure. The loading filtration media of the invention has a basis weight of about 33 to about 65 g-m−2. The efficiency layer has a basis weight of about 65 to about 130 g-m−2. The efficiency layer has a mean flow pore size smaller than the loading layer that ranges from about 2 to about 10 micrometers. The loading layer has a permeability that ranges from about 80 to 160 ft-min−1. The efficiency layer has a permeability of about 10 to 50 ft-min−1. The loading layer or the efficiency layer of the invention has a wet bursting strength of greater than about 5 psi, typically about 10 to about 30 psi. The combined filtration layer has a permeability of about 15 to 40 ft-min−1, a wet burst strength of 10 to 30 psi and a basis weight of 130 to 200 g-m−2. Microfiber glass is not coated or sized. Only large chopped glass is sized. Both types are used in this application. These commercially available fibers are characteristically coated or sized with a sizing. Such coatings cause the otherwise ionically neutral glass fibers to form and remain in bundles. Manufacturers of glass fibers commonly employ sizes such as this. The sizing composition and cationic antistatic agent eliminates fiber agglomeration and permits a uniform dispersion of the glass fibers upon agitation of the dispersion in the tank. Blends of glass fibers can substantially aid in improving permeability of the materials. We have found that combining two or more sources of glass fiber having an average particle size of about 0.3 to 0.5 micron, glass fiber having an average particle diameter of about 1 to 2 micron, glass fiber having an average particle diameter of about 3 to 6 micrometers or glass fiber with a particle diameter of about 6 to 10 micrometers in varying proportions can substantially improve permeability. We believe such glass fiber blends obtain a controlled pore size resulting in a defined permeability in the media layer.


Binder resins can typically comprise solvent based, water soluble or water sensitive polymer materials. Water based latex as the saturate resin. One could easily use solvent based resins such as phenols and epoxy phenolic blends just as easily. Polymer materials are typically provided in either dry form or aqueous dispersions. Such useful polymer materials include acrylic polymers, ethylene vinyl acetate polymers, ethylene vinyl polyvinyl alcohol, ethylene vinyl alcohol polymers, polyvinyl pyrrolidone polymers, and natural gums and resins useful in aqueous solution. Various combinations of polymers for the bicomponent fiber may be useful in the present invention, but it is important that the first polymer component melt at a temperature lower than the melting temperature of the second polymer component and typically below 300° F. Further, the bicomponent fibers are integrally mixed and evenly dispersed with the pulp fibers. Melting of the first polymer component of the bicomponent fiber is necessary to allow the bicomponent fibers to form a tacky skeletal structure, which upon cooling, captures and binds many of the pulp fibers, as well as binds to other bicomponent fibers. The bicomponent fiber used in the media of this invention generally has a length of 0.1 to 10 millimeters and a diameter of 10 to 20 micrometers.


The preferred materials for the water soluble or dispersible binder polymer are water soluble or water dispersible thermosetting resins such as acrylic resins, methacrylic resins, polyamide resins, epoxy resins, phenolic resins, polyureas, polyurethanes, melamine formaldehyde resins, polyesters and alkyd resins, generally, and specifically, water soluble acrylic resins. methacrylic resins, polyamide resins, that are in common use in the papermaking industry. Such thermoplastic binder resin materials are typically aqueous dispersions of vinyl thermoplastic resins including vinyl acetate materials, vinyl chloride resins, polyvinyl alcohol resins, polyvinyl acetate resins, polyvinyl acetyl resins, acrylic resins, methacrylic resins, polyamide resins, polyethylene vinyl acetate copolymer resins, thermosetting resins such as urea phenol, urea formaldehyde, melamine, epoxy, polyurethane, curable unsaturated polyester resins, polyaromatic resins, resorcinol resins and similar elastomer resins. Such binder resins typically coat the fiber and adhere fiber to fiber in the final non-woven matrix. Sufficient resin is added to the furnish to fully coat the fiber without causing film over the pores formed in the sheet material. The resin can be added to the furnish during papermaking or can be applied to the media after formation.


The latex binder, used to bind together the three-dimensional non-woven fiber web in each non-woven layer or used as the additional adhesive, can be selected from various latex adhesives known in the art. The skilled artisan can select the particular latex adhesive depending upon the type of fibers that are to be bound. The latex adhesive may be applied by known techniques such as spraying, foaming, curtain coating, gravure rolling or size pressing saturation techniques. The amount of solids in the latex adhesive used depends, inter alia, on the weight of the fibers in each layer. Generally, latex adhesives having from 15 to 25% solids are used.


Non-woven media of the invention can contain fibers made from a number of both hydrophilic and hydrophobic fibers. These fibers cooperate with the glass fiber and the bicomponent fiber to form a mechanically stable, but strong, permeable filtration media that can withstand the mechanical stress of the passage of fluid materials and can maintain the loading of particulate during use. The fiber characteristics are typically expressed as denier, typically is considered to indicate the weight in grams of 9000 meters of fiber.


The secondary thermoplastic fibers include, but are not limited to, polyester fibers, polyamide fibers, polypropylene fibers, copolyetherester fibers, polyethylene terephthalate fibers, polybutylene terephthalate fibers, polyetherketoneketone (PEKK) fibers, polyetheretherketone (PEEK) fibers, liquid crystalline polymer (LCP) fibers, and mixtures thereof. Polyamide fibers include, but are not limited to, nylon 6, 66, 11, 12, 612, and high temperature “nylons” (such as nylon 46) including cellulosic fibers, polyvinyl acetate, polyvinyl alcohol fibers (including various hydrolysis of polyvinyl alcohol such as 88% hydrolyzed, 95% hydrolyzed, 98% hydrolyzed and 99.5% hydrolyzed polymers), cotton, viscous rayon, thermoplastic such as polyester, polypropylene, polyethylene, etc., polyvinyl acetate, polylactic acid, and other common fiber types. The thermoplastic fibers are generally fine (about 0.5-20 denier), short (about 0.1-5 cm), staple fibers, possibly containing precompounded conventional additives, such as antioxidant, stabilizers, lubricants, tougheners, etc. In addition, the thermoplastic fibers may be surface treated with a dispersing aid. The preferred thermoplastic fibers are polyamide and polyethylene terephthalate fibers, with the most preferred being polyethylene terephthalate fibers.


The sheet media of the invention are typically made using papermaking processes. The media can be planar or can be made in various geometric forms. Such wet laid processes are particularly useful and many of the fiber components are designed for aqueous dispersion processing. However, the media of the invention can be made by air laid processes that use similar components adapted for aid laid processing. The machines used in wet laid sheet making include hand laid sheet equipment, Fourdrinier papermaking machines, cylindrical papermaking machines, inclined papermaking machines, combination papermaking machines and other machines that can take a properly mixed paper furnish, form a layer of the furnish components, remove the fluid aqueous components to form a wet sheet. A fiber slurry containing the materials are typically mixed to form a uniform fiber slurry. The fiber slurry is then subjected to a wet laid papermaking process. Once the slurry is formed into a wet laid sheet, the wet laid sheet can then be dried, cured or otherwise processed to form a dry permeable, but real sheet or medium. Once sufficiently dried and processed to filtration media, the sheets are typically about 0.01 to 0.1 or 0.02 to 0.08 inch in thickness, having a basis weight of about 30 to 250 g-m−2. For a commercial scale process, the bicomponent mats of the invention are generally processed through the use of papermaking-type machines such as commercially available Fourdrinier, wire cylinder, Stevens Former, Roto Former, Inver Former, Venti Former, and inclined Delta Former machines. Preferably, an inclined Delta Former machine is utilized. A bicomponent mat of the invention can be prepared by forming bicomponent fiber and media or glass fiber slurries and combining the slurries in mixing tanks, for example. The amount of water used in the process may vary depending upon the size of the equipment used. The furnish may be passed into a conventional head box where it is dewatered and deposited onto a moving wire screen where it is dewatered by suction or vacuum to form a non-woven bicomponent web. The web can then be coated with a binder by conventional means, e.g., by a flood and extract method or roll coating techniques and passed through a drying oven that dries the mat and cures the binder and thermally bonds the sheet or medium. The resulting mat may be collected in a large roll.


Synthetic especially polyester and glass fiber multi-layer filtration media can be made using both bi-component PET/PET as well as monomer PVA binder fiber and acrylic latex resin. Both efficiency and loading layers are formed nearly simultaneously on a paper machine. Filtration media is suitable for mobile and in-plant hydraulic applications as well as mobile equipment lube oil applications.


EXPERIMENTAL
The Description of the Hand Sheet Making Procedure

Eight experimental 12 inch by 12 inch size hand sheets were made using the furnish recipes in Table 3 using the following procedure.


Procedure:


The materials were selected and weight them into individual containers. For example, to make one batch of 12 inch by 12 inch size hand sheets, 76 grams of select fibers or fibers (depends on the furnish requirements) is used. The fibers were dispersed in known quantity of water, using a blender. If there is insufficient capacity in the blender to disperse all of the fibers in one batch at a time, sub-divide the batch into more manageable parts, with enough sulfuric acid, to reduce pH to about 2.5 to aide dispersion and improve the final formation of the filter media. Combine all parts of fiber dispersion in one container, and then add additional water keeping careful account of quantity of water used to reach a final sheet forming consistency (typically about 0.05%), then stir sufficiently to get uniform dispersion, 15 minutes should be sufficient, before hand sheet formation. This method ensures that a known consistency (fiber weight to water volume of material) is obtained and the materials proportions are equal for each hand sheet. The paper making wire is placed on the screen in the box. The box is closed and water is added. Add 2.5 liters of fiber dispersion to the box with agitation. Drain to form the sheet. Dry sheet, using vacuum to remove excess water allow to air dry or add heat using a print dryer, drum dryer, hot plate or other device. Apply heat above the melt temperature of the sheath polymer of the bi-component fiber.


A resin saturating procedure is used to saturate hand sheets with resin for strength and durability. Place hand sheets on rack in the oven and dried at 300° F. (150° C.) for 10 minutes and then weighed to obtain initial basis weight. Using resin formulation, select resin ingredients and measure all of them into individual containers, then combine them with water. Using a size press laboratory saturating system, adjust the upper roll pressure to 40 psi. Fill saturating pan with the resin solution. Dip handsheet into resin pan and saturate it on both wire and felt side. A support scrim for either wire, felt or both sides may be used in laboratory saturating to prevent sticking and improve handling. Remove the scrim, if used and place wet handsheet on rack in the oven and dry it at 300° F. (150° C.) until dry, and then measure the basis weight. Calculate resin pick up (express as percent) using the formula:

Resin pick up=(Saturated weight−Initial weight)·100/Initial weight

If resin pick up is different than target pickup level adjust resin concentration in steps until target level is achieved. With the right resin pickup level, saturate a batch of handsheets. Remove scrims if used and place wet handsheets on racks allowing them to air overnight. Place dry dried sheets on racks in the oven at 300° F. (150° C.) for 10 minutes, measure weight and calculate the final basis weight and the resin pickup.









TABLE 3





Furnish Characteristics







Efficiency Layer (% based on dry weight)










Basis Weight of dried layer
65 to 138 g-m−2



Latex resin
Up to 25%



PVA binder fiber
0 to 2%



PET/PET sheath core bi-
At least 5%



component binder fiber



Glass fiber
50 to 95%



Secondary polyester fiber
0 to 55%







Loading Layer










Basis Weight of dried layer
33 to 65 g-m−2



Latex resin
Up to 25%



PVA binder fiber
0 to 2%



PET/PET sheath core bi-
up to 15%



component binder fiber



Glass fiber
70 to 90%



Secondary polyester fiber
0 to 25%










A second set of single layer hand sheets were prepared using the disclosed procedure for testing. The furnish formulations are found in the following Table 4. The polyvinyl alcohol (PVA) binder resin was used at 1%.









TABLE 4







Furnish information









Furnish (dry weight %)











Glass Fiber
Furnish A
Furnish C
Furnish D
Furnish G


(average diameter)
(93 g-m−2)
(93 g-m−2)
(93 g-m−2)
(93 g-m−2)





GLASS FIBER 706
 9%
 9%
 9%
11%


(0.3 micron)


GLASS FIBER
40%
40%
40%
28%


110X (2 micron)


GLASS FIBER
30%
30%
39%
30%


112X (3 micron)


GLASS FIBER
10%
10%




Lauscha EC 6-6 SC


(6 micron)


GLASS FIBER
10%





Lauscha EC 10-12 SC


(10 micron)


PVA (88%
 1%
 1%
 1%
 1%


hydrolyzed)


SPG 056-11


BICOMPONENT FIBER

10%
20%
30%


(DuPont 271P
















TABLE 5







Handsheet Datasheet






















Target



Dry
Wet
Dry







Binder
Resin
Weight,
Thickness,
Permeability,
Tensile,
Tensile,
Burst,
Loading,
β @
β @


Furnish
Type
Fiber
Pickup
g-m−2
inches
ft-min−1
lbs/(in width)
lbs/(in width)
psi
gms-ft−2
10μ
75μ






















A
base
 0%
 0%
109
0.031
27
2.2
0.9
8.6
8.5
4.15
6.98


C
base
10%
 0%
101
0.030
29
2.4
1.3
8.4
8.7
4.66
7.76


D
base
20%
 0%
103
0.052
31
1.4
0.8
8.5
10.6
5.17
8.95


G
base
30%
 0%
101
0.035
32
1.6
0.8
10.3
12.8
6.15
10.76


A
saturated
 0%
10%
124
0.033
23
6.5
5.7
8.5
5.3
3.75
6.41


C
saturated
10%
10%
111
0.031
28
4.1
7.4
8.3
8.8
4.57
7.54


D
saturated
20%
10%
112
0.051
29
4.2
3.1
8.3
8.6
5.34
8.80


G
saturated
30%
10%
111
0.035
31
10.9
10.6
15.2
9.9
5.93
9.77









Table 5 shows that in this experiment that the saturated hand sheets (e.g. Furnish D and G) have comparable permeability, β and loading filtration properties compared to the unsaturated version but have improved wet tensile strength.



FIG. 2 shows that testing conducted on handsheets of Table 5 (flatsheet media samples) using a miniflow Bench according to ISO 16889 test standard. Base results show a 52% increase in loading using 30% bi-component fiber versus the control (0% bi-component).



FIG. 3 shows, in the hand sheets of Table 4, that saturated results provide a 55% increase in loading using 30% bi-component fiber versus the saturated control (0%).



FIG. 4 shows both base and saturated handsheet loading data using 0% bi-component with no resin as a control. This also highlights a key benefit of using bi-component fiber; addition of saturate resin detracts from loading performance. If you compare the dry burst strength of the base sheet with 30% bi-component fiber (10.3 psi) to the dry burst strength of the bi-component with and with saturate resin, you will see that much more then 10% resin pick-up is needed to achieve the same strength.



FIG. 5 is a cross sectional view of a spin on cartridge filter of the invention. In FIG. 5, cartridge 50 is shown with an exterior shell 58, typically plastic or metallic. At one end of the cartridge structure, is a contact surface end seal 59, a spin on threaded mounting means 60 including an outlet annular space 52. The contact surface has inlet aperture 51 or liquid inlet 51 that permits a liquid having a potential particulate load to enter the cartridge 50. The cartridge contains pleated media 54 sealed at both ends using seal plates 56 and 55 to force the liquid through pleated media 54 using liquid flow path 53. The pleated media material of the invention 54 is typically mechanically insufficient to maintain filtration properties without some form of support. The cartridge 50 of the invention supports pleated media 54 using a support layer 57 which prevents the pleated media from collapsing under the force of the liquid passing through the cartridge.



FIG. 6 shows one embodiment of a supported pleated media of the invention. In FIG. 6, a pleated media 54 is shown supported on a perforate media support 61. The fluid flow 63 is shown wherein the fluid penetrates the media and the perforate support into the interior of the structure. The perforate media comprises apertures or pores 62 in the support to permit liquid flow from the exterior of the media to the interior of the filter structure. The apertures or pores 62 are surrounded by metal 61 maintaining a mechanically stable support to prevent collapse of the pleated media 54.



FIG. 7 is a side view of the down stream side of a screen supported media of the invention. In FIG. 7, supported media 70 is shown wherein pleated media 54 is supported by a screen support 71. Generally to FIG. 6, fluid passes the media side of the supported media through the screen-supported side of the media to the interior of the cartridge structure.


Test method ISO 16889 “Hydraulic Fluid Power Filters—Multipass Method for Evaluating Filtration of a Filter Element” was used to obtain the loading and β data. βresults are reported per paragraph 12.6 in this test method. β is a filter rating system used by the hydraulic industry. βx=(number of particles>stated size upstream of the filter)/(number of particles>stated size downstream of the filter). The “x” subscript indicates the micron size of the particles. For example, if 1,000 particles 15 micrometers and greater were counted upstream of the filter, and 50 of those same size particles were counted downstream, the β would be 20 or β15=20. Stated another way, the filter is 95% efficient on particles 15 micrometers and larger. Testing conducted on handsheets (flatsheet media samples) using DCI Miniflow Bench according to ISO 16889 test standard. Base results (see FIG. 2) show a 52% increase in loading using 30% bi-component fiber versus the control (0% bi-component).


Permeability relates to the quantity of air (ft3-min−1-ft−2 or ft-min−1) that will flow through a filter medium at a pressure drop of 0.5 inches of water. In general, permeability, as the term is used is assessed by the Frazier Permeability Test according to ASTM D737 using a Frazier Permeability Tester available from Frazier Precision Instrument Co. Inc., Gaithersburg, Md. or a TexTest 3300 or TexTest 3310 available from Advanced Testing Instruments Corp (ATI), 243 East Black Stock Rd. Suite 2, Spartanburg, S.C. 29301, (864)989-0566, www.aticoiporation.com. Pore size referred to in this disclosure means mean flow pore diameter determined using a capillary flow porometer instrument like Model APP 1200 AEXSC sold by Porus Materials, Inc., Cornell University Research Park, Bldg. 4.83 Brown Road, Ithaca, N.Y. 14850-1298, 1-800-825-5764, www.pmiapp.com.


Kahlbaugh et al., U.S. Pat. No. 5,082,476, disclose a filter design using a depth media comprising a foam substrate with pleated components combined with the microfiber materials of the invention. Stifelman et al., U.S. Pat. No. 5,104,537, relate to a filter structure useful for filtering liquid media. Liquid is entrained into the filter housing, passes through the exterior of the filter into an interior annular core and then returns to active use in the structure.


Gillingham et al., U.S. Pat. No. 5,820,646, disclose a corrugated or Z filter structure that uses a specific pleated filter design involving plugged passages that require a fluid stream to pass through at least one layer of filter media in a “Z” shaped path to obtain proper filtering performance. The filter media formed into the pleated Z shaped format can contain the fine fiber media of the invention.


While the invention has been described in connection with specific embodiments thereof, the invention is capable of further modifications and this application is intended to cover any variations, uses, or adaptations of the invention following the description of the invention and including known or customary practice within the art to which the invention pertains and as may be applied to the essential features hereinbefore set forth and as follows in scope of the appended claims.

Claims
  • 1. A method of filtering a non-aqueous liquid comprising a fuel, a lubricant, a hydraulic fluid, or a brake fluid, the method consisting essentially of: passing the non-aqueous liquid with a particulate load through a filter medium comprising a layer comprising 5 to 50 wt % of a bicomponent binder fiber, about 50 to 95 wt % of a glass fiber, and about 0.5 to 25 wt % of a binder resin, the layer having a basis weight of about 30 to 250 g-m−2, the layer having a permeability of 10 to 50 ft-min−1, a wet bursting strength of about 5 lb-in−2 to 30 lb-in−2; and removing the particulate load.
  • 2. The method of claim 1 wherein the medium comprises a first layer comprising a loading layer having a basis weight of about 25 to 75 g-m−2 and a second layer comprising an efficiency layer having a basis weight of about 50 to 150 g-m−2, wherein the loading layer comprises about 1 to 25% of a bicomponent binder fiber and about 70 to 90 w % of a glass fiber, and the efficiency layer comprises about 5 to 25 wt % of a bicomonent binder fiber and about 50 to 95 wt % of a glass fiber.
  • 3. The method of claim 2 wherein the glass fiber comprises a blend of two or more glass fiber sources that differ by average diameter.
  • 4. The method of claim 2 wherein the glass fiber comprises a blend of three or more glass fiber sources that differ by average diameter.
  • 5. The medium of claim 2 wherein the glass fiber comprises a blend of a first fiber having a diameter of less than 0.5 microns and a second glass fiber having diameter of greater than 5 microns.
  • 6. The method of claim 1 wherein the medium comprising a wet bursting strength of about 10 lb-in−2 to 30 lb-in−2.
  • 7. The method of claim 1 wherein the medium comprises a mean flow pore size of about 2 to about 10 micrometers.
CROSS REFERENCE TO RELATED APPLICATION

This application is a divisional of application Ser. No. 10/982,538, filed Nov. 5, 2004, which application is incorporated herein by reference.

US Referenced Citations (418)
Number Name Date Kind
2764602 Ahlbrecht Sep 1956 A
2764603 Ahlbrecht Sep 1956 A
2801706 Asker Aug 1957 A
2803656 Ahlbrecht Aug 1957 A
3073735 Till et al. Jan 1963 A
3147064 Brown Sep 1964 A
3255131 Ahlbrecht Jun 1966 A
3279151 Kauer, Jr. et al. Oct 1966 A
3303621 Hill Feb 1967 A
3450755 Ahlbrecht Jun 1969 A
3505794 Nutter et al. Apr 1970 A
3589956 Kranz et al. Jun 1971 A
3595731 Davies et al. Jul 1971 A
3616160 Wincklhofer Oct 1971 A
3616183 Brayford et al. Oct 1971 A
3620819 Croce Nov 1971 A
3639195 Sanders Feb 1972 A
3653181 Becker Apr 1972 A
3705480 Wireman Dec 1972 A
3714763 Suzuki Feb 1973 A
3728848 Vest Apr 1973 A
3744256 Cobb et al. Jul 1973 A
3891417 Wade Jun 1975 A
3917448 Wood Nov 1975 A
3934238 Pavlov Jan 1976 A
3937860 Gusman et al. Feb 1976 A
3972694 Head Aug 1976 A
3998988 Shimomai et al. Dec 1976 A
4042522 Falk Aug 1977 A
4045350 Kupf et al. Aug 1977 A
4047914 Hansen et al. Sep 1977 A
4069158 Bertocchio et al. Jan 1978 A
4069244 Mueller Jan 1978 A
4079675 Beumel Mar 1978 A
4088726 Cumbers May 1978 A
4090967 Falk May 1978 A
4102785 Head et al. Jul 1978 A
4111815 Walker et al. Sep 1978 A
4160059 Samejima Jul 1979 A
4161422 Lawson et al. Jul 1979 A
4161590 Mueller Jul 1979 A
4161602 Mueller Jul 1979 A
4169754 Perrotta Oct 1979 A
4177141 Nakamura et al. Dec 1979 A
4189338 Ejima et al. Feb 1980 A
4210540 Perrotta Jul 1980 A
4211819 Kunimune et al. Jul 1980 A
4231768 Seibert et al. Nov 1980 A
4234655 Kunimune et al. Nov 1980 A
4239278 Skilliter Dec 1980 A
4239516 Klein Dec 1980 A
4254731 Taylor Mar 1981 A
4267016 Okazaki et al. May 1981 A
4269888 Ejima et al. May 1981 A
4272318 Walker et al. Jun 1981 A
4274914 Keith et al. Jun 1981 A
4309475 Hoffman, Jr. Jan 1982 A
4318774 Powell et al. Mar 1982 A
4321108 Goddard et al. Mar 1982 A
4327936 Sekiguchi May 1982 A
4370152 Luper Jan 1983 A
4388086 Bauer Jun 1983 A
4423995 Karis Jan 1984 A
4429001 Kolpin et al. Jan 1984 A
4443233 Moran Apr 1984 A
4457974 Summers Jul 1984 A
4487617 Dienes et al. Dec 1984 A
4500384 Tomioka et al. Feb 1985 A
4501598 Long Feb 1985 A
RE31849 Klein Mar 1985 E
4504289 Walker Mar 1985 A
4536440 Berg Aug 1985 A
4545789 Lato Oct 1985 A
4548624 Walker Oct 1985 A
4551378 Carey, Jr. Nov 1985 A
4552603 Harris, Jr. et al. Nov 1985 A
4555430 Mays Nov 1985 A
4579774 Kuwazuru et al. Apr 1986 A
4597218 Friemel et al. Jul 1986 A
4604205 Ayers Aug 1986 A
4610678 Weisman et al. Sep 1986 A
4627863 Klein Dec 1986 A
4657804 Mays et al. Apr 1987 A
4659467 Spearman Apr 1987 A
4661132 Thornton et al. Apr 1987 A
4676807 Miller Jun 1987 A
4677929 Harris Jul 1987 A
4681801 Eian et al. Jul 1987 A
4684576 Tabor et al. Aug 1987 A
4688511 Gerlach et al. Aug 1987 A
4689057 Gasper Aug 1987 A
4713285 Klein Dec 1987 A
4726817 Roger Feb 1988 A
4729371 Krueger et al. Mar 1988 A
4732809 Harris, Jr. et al. Mar 1988 A
4734208 Pall et al. Mar 1988 A
4764189 Yanagawa et al. Aug 1988 A
4765812 Homonoff et al. Aug 1988 A
4765915 Diehl Aug 1988 A
4807619 Dyrud et al. Feb 1989 A
4814033 Spearman et al. Mar 1989 A
4816224 Vogel et al. Mar 1989 A
4838903 Thomaides et al. Jun 1989 A
4838905 Billiet et al. Jun 1989 A
4840838 Wyss Jun 1989 A
4868032 Eian et al. Sep 1989 A
4874666 Kubo et al. Oct 1989 A
4886058 Brostrom et al. Dec 1989 A
4889764 Chenoweth et al. Dec 1989 A
4904385 Wessling et al. Feb 1990 A
4911789 Rieunier et al. Mar 1990 A
4917714 Kinsley, Jr. Apr 1990 A
4919753 Johnson et al. Apr 1990 A
4933129 Huykman Jun 1990 A
4983434 Sassa Jan 1991 A
5022964 Crane et al. Jun 1991 A
5027781 Lewis Jul 1991 A
5034040 Walcott Jul 1991 A
5042468 Lambert Aug 1991 A
5045210 Chen et al. Sep 1991 A
5057368 Largman et al. Oct 1991 A
5066538 Huykman Nov 1991 A
5068141 Kubo et al. Nov 1991 A
5080791 Sims Jan 1992 A
5082476 Kahlbaugh et al. Jan 1992 A
5087278 Suzuki Feb 1992 A
5089119 Day et al. Feb 1992 A
5092911 Williams Mar 1992 A
5104537 Stifelman et al. Apr 1992 A
5108827 Gessner Apr 1992 A
5110330 Loughron May 1992 A
5131387 French et al. Jul 1992 A
5147553 Waite Sep 1992 A
5147721 Baron et al. Sep 1992 A
5167764 Nielsen et al. Dec 1992 A
5167765 Nielsen et al. Dec 1992 A
5190569 McGrath Mar 1993 A
5190812 Joseph et al. Mar 1993 A
5208098 Stover May 1993 A
5212131 Belding May 1993 A
5246474 Greatorex Sep 1993 A
5246772 Manning Sep 1993 A
5275743 Miller et al. Jan 1994 A
5283106 Seller et al. Feb 1994 A
5284704 Kochesky et al. Feb 1994 A
5302443 Manning et al. Apr 1994 A
5307796 Kronzer et al. May 1994 A
5334446 Quantrille et al. Aug 1994 A
5336286 Alexander et al. Aug 1994 A
5354603 Errede et al. Oct 1994 A
5364456 Kahlbaugh et al. Nov 1994 A
5366631 Adiletta Nov 1994 A
5380580 Rogers et al. Jan 1995 A
5405682 Shawyer et al. Apr 1995 A
5415676 Tokar et al. May 1995 A
5436980 Weeks et al. Jul 1995 A
5454945 Spearman Oct 1995 A
5458960 Nieminen et al. Oct 1995 A
5468572 Zguris et al. Nov 1995 A
5472467 Pfeffer Dec 1995 A
5486410 Groeger et al. Jan 1996 A
5508079 Grant et al. Apr 1996 A
5508093 Mehdorn Apr 1996 A
5509340 Kawamura Apr 1996 A
5545453 Grant Aug 1996 A
5545475 Korleski Aug 1996 A
5575832 Boyd Nov 1996 A
5580459 Powers et al. Dec 1996 A
5581647 Onishi et al. Dec 1996 A
5584784 Wu Dec 1996 A
5597645 Pike et al. Jan 1997 A
5605746 Groeger et al. Feb 1997 A
5607735 Brown Mar 1997 A
5616408 Oleszczuk et al. Apr 1997 A
5620641 Berger Apr 1997 A
5620785 Watt et al. Apr 1997 A
5633082 Berger May 1997 A
5643467 Romanco Jul 1997 A
5643653 Griesbach et al. Jul 1997 A
5645057 Watt et al. Jul 1997 A
5645689 Ruf et al. Jul 1997 A
5645690 Cox, Jr. Jul 1997 A
5662728 Groeger Sep 1997 A
5665235 Gildersleeve et al. Sep 1997 A
5667562 Midkiff Sep 1997 A
5672399 Kahlbaugh et al. Sep 1997 A
5672415 Sawyer et al. Sep 1997 A
5677058 Neal et al. Oct 1997 A
5679042 Varona Oct 1997 A
5705119 Takeuchi et al. Jan 1998 A
5709735 Midkiff et al. Jan 1998 A
5711878 Ogata et al. Jan 1998 A
5721180 Pike et al. Feb 1998 A
5728187 Kern et al. Mar 1998 A
5728298 Hamlin Mar 1998 A
5753002 Glucksman May 1998 A
5755963 Sugiura et al. May 1998 A
5779847 Groeger Jul 1998 A
5783505 Duckett Jul 1998 A
5785725 Cusick et al. Jul 1998 A
5792711 Roberts Aug 1998 A
5795835 Bruner et al. Aug 1998 A
5800586 Cusick et al. Sep 1998 A
5800884 D'Anna et al. Sep 1998 A
5804286 Quantrille et al. Sep 1998 A
5820646 Gillingham et al. Oct 1998 A
5837627 Halabisky et al. Nov 1998 A
5840245 Coombs et al. Nov 1998 A
5853439 Gieseke et al. Dec 1998 A
5885390 Alkire et al. Mar 1999 A
5911213 Ahlborn et al. Jun 1999 A
5932104 Kawamura Aug 1999 A
5935879 Helwig et al. Aug 1999 A
5935883 Pike Aug 1999 A
5948344 Cusick et al. Sep 1999 A
5952252 Shawver et al. Sep 1999 A
5954962 Adiletta Sep 1999 A
5965468 Marmon et al. Oct 1999 A
5972166 Helwig et al. Oct 1999 A
5972477 Kim et al. Oct 1999 A
5976998 Sandor et al. Nov 1999 A
5981410 Hansen et al. Nov 1999 A
5989432 Gildersleeve et al. Nov 1999 A
5989688 Barge et al. Nov 1999 A
5993501 Cusick et al. Nov 1999 A
5993943 Bodaghi et al. Nov 1999 A
6007608 Johnson Dec 1999 A
6007898 Kim et al. Dec 1999 A
6013587 Truong et al. Jan 2000 A
6024782 Freund et al. Feb 2000 A
6041782 Angadjivand et al. Mar 2000 A
6045597 Choi Apr 2000 A
6071419 Beier et al. Jun 2000 A
6071641 Zguris et al. Jun 2000 A
6077391 Girondi Jun 2000 A
6099726 Gembolis et al. Aug 2000 A
6103181 Berger Aug 2000 A
6103643 Forsten Aug 2000 A
6110249 Medcalf et al. Aug 2000 A
6136058 Miller Oct 2000 A
6139595 Herman et al. Oct 2000 A
6143049 Gieseke et al. Nov 2000 A
6143441 Zguris Nov 2000 A
6146436 Hollingsworth et al. Nov 2000 A
6152120 Julazadeh Nov 2000 A
6156682 Fletemier et al. Dec 2000 A
6156842 Hoenig et al. Dec 2000 A
6165572 Kahlbaugh et al. Dec 2000 A
6169045 Pike et al. Jan 2001 B1
6171355 Gieseke et al. Jan 2001 B1
6171369 Schultink et al. Jan 2001 B1
6171684 Kahlbaugh et al. Jan 2001 B1
6174603 Berger Jan 2001 B1
6183536 Schultink et al. Feb 2001 B1
6186992 Roe et al. Feb 2001 B1
6187073 Gieseke et al. Feb 2001 B1
6190768 Turley et al. Feb 2001 B1
6197709 Tsai et al. Mar 2001 B1
6200669 Marmon et al. Mar 2001 B1
6203713 Tanny Mar 2001 B1
6241886 Kitagawa et al. Jun 2001 B1
6251224 Dong Jun 2001 B1
6264044 Meyering et al. Jul 2001 B1
6267252 Amsler Jul 2001 B1
6267843 Helwig et al. Jul 2001 B1
6290739 Gieseke et al. Sep 2001 B1
6300261 Young et al. Oct 2001 B1
6301887 Gorel et al. Oct 2001 B1
6306539 Zguris Oct 2001 B1
6316107 Lubnin et al. Nov 2001 B1
6330883 Berger Dec 2001 B1
6351078 Wang et al. Feb 2002 B1
6352947 Haley et al. Mar 2002 B1
6355076 Gieseke et al. Mar 2002 B2
6355079 Sorvari et al. Mar 2002 B1
6364976 Fletemier et al. Apr 2002 B2
6365001 Helwig et al. Apr 2002 B1
6372004 Schultink et al. Apr 2002 B1
6384369 Stenersen et al. May 2002 B1
6406789 McDaniel et al. Jun 2002 B1
6409785 Smithies et al. Jun 2002 B1
6409787 Smithies et al. Jun 2002 B1
6419721 Hunter Jul 2002 B1
6419839 Cox et al. Jul 2002 B1
6420626 Erspamer et al. Jul 2002 B1
6428610 Tsai et al. Aug 2002 B1
6440192 Guerin et al. Aug 2002 B2
6458456 Zainiev et al. Oct 2002 B1
6479147 Lubnin et al. Nov 2002 B2
6488811 Dong Dec 2002 B1
6495286 Zguris et al. Dec 2002 B2
6503447 Mondjian et al. Jan 2003 B1
6511774 Tsukuda et al. Jan 2003 B1
6517612 Crouch et al. Feb 2003 B1
6521321 Kahlbaugh et al. Feb 2003 B2
6528439 Stokes et al. Mar 2003 B1
6530366 Geiger et al. Mar 2003 B2
6530969 Gieseke et al. Mar 2003 B2
6540801 Gieseke et al. Apr 2003 B2
6541114 Katou et al. Apr 2003 B2
6547860 Buchwald et al. Apr 2003 B2
6555489 Pfeffer Apr 2003 B1
6576034 Berger Jun 2003 B2
6607997 Cox et al. Aug 2003 B1
6613704 Arnold et al. Sep 2003 B1
6616723 Berger Sep 2003 B2
6624099 Shah Sep 2003 B1
H2086 Amsler Oct 2003 H
6645388 Sheikh-Ali Nov 2003 B2
6649547 Arnold et al. Nov 2003 B1
6652614 Gieseke et al. Nov 2003 B2
6653381 Thames et al. Nov 2003 B2
6673864 Patel et al. Jan 2004 B2
6682576 Kiyotani et al. Jan 2004 B1
6682809 Van Rheenen Jan 2004 B2
6695148 Homonoff et al. Feb 2004 B2
6705270 Rau et al. Mar 2004 B1
6706086 Emig et al. Mar 2004 B2
6723142 Emerson et al. Apr 2004 B2
6723669 Clark et al. Apr 2004 B1
6740142 Buettner et al. May 2004 B2
6743273 Chung et al. Jun 2004 B2
6770356 O'Donnell et al. Aug 2004 B2
6797377 DeLucia et al. Sep 2004 B1
6815383 Arnold Nov 2004 B1
6818037 Tamaka et al. Nov 2004 B2
6821321 Chinn et al. Nov 2004 B2
6821672 Zguris Nov 2004 B2
6835311 Koslow Dec 2004 B2
6848866 McGinn Feb 2005 B1
6849330 Morin et al. Feb 2005 B1
6858057 Healey Feb 2005 B2
6860917 Henrichsen et al. Mar 2005 B2
6866692 Emerson et al. Mar 2005 B2
6872431 Kahlbaugh et al. Mar 2005 B2
6872674 Williams et al. Mar 2005 B2
6874641 Clary Apr 2005 B2
6875249 Gogins Apr 2005 B2
6878191 Escaffre et al. Apr 2005 B2
6883321 Fornof Apr 2005 B2
6916752 Berrigan et al. Jul 2005 B2
6923182 Angadjivand et al. Aug 2005 B2
6924028 Chung et al. Aug 2005 B2
6926961 Roth Aug 2005 B2
6936554 Singer et al. Aug 2005 B1
6939386 Sato et al. Sep 2005 B2
6939492 Jackson et al. Sep 2005 B2
6942711 Faulkner et al. Sep 2005 B2
6955708 Julos et al. Oct 2005 B1
6955775 Chung et al. Oct 2005 B2
6966940 Krisko et al. Nov 2005 B2
6991113 Nakajima Jan 2006 B2
7008144 McGinn Mar 2006 B2
7029516 Campbell et al. Apr 2006 B2
7037569 Curro et al. May 2006 B2
7049254 Bansal et al. May 2006 B2
7070640 Chung et al. Jul 2006 B2
7090715 Chung et al. Aug 2006 B2
7094270 Schultink et al. Aug 2006 B2
7115150 Johnson et al. Oct 2006 B2
7125470 Graef et al. Oct 2006 B2
7309372 Kahlbaugh et al. Dec 2007 B2
7314497 Kahlbaugh et al. Jan 2008 B2
7520994 Dong et al. Apr 2009 B2
20010000375 Kobayashi et al. Apr 2001 A1
20020007167 Dan et al. Jan 2002 A1
20020013111 Dugan et al. Jan 2002 A1
20020083690 Emig et al. Jul 2002 A1
20020116910 Berger Aug 2002 A1
20020121194 Buchwald et al. Sep 2002 A1
20020127939 Hwo et al. Sep 2002 A1
20020193030 Yao et al. Dec 2002 A1
20030008214 Zguris Jan 2003 A1
20030019193 Chinn et al. Jan 2003 A1
20030022575 Yoneda et al. Jan 2003 A1
20030039815 Roth Feb 2003 A1
20030082979 Bean et al. May 2003 A1
20030084788 Fraser, Jr. May 2003 A1
20030087568 Kinn et al. May 2003 A1
20030089092 Bause et al. May 2003 A1
20030096549 Ortega et al. May 2003 A1
20030106294 Chung et al. Jun 2003 A1
20030109190 Geel Jun 2003 A1
20030139110 Nagaoka et al. Jul 2003 A1
20030145569 Sato et al. Aug 2003 A1
20030148691 Pelham et al. Aug 2003 A1
20030150820 Dussaud et al. Aug 2003 A1
20030211799 Yao et al. Nov 2003 A1
20040116026 Kubose et al. Jun 2004 A1
20040134355 Kasmark, Jr. Jul 2004 A1
20040192141 Yang et al. Sep 2004 A1
20040221436 Ortega et al. Nov 2004 A1
20040242108 Russell et al. Dec 2004 A1
20040255783 Graham et al. Dec 2004 A1
20050026526 Verdegan et al. Feb 2005 A1
20050109683 Joyce et al. May 2005 A1
20050130031 Zguris Jun 2005 A1
20050160711 Yang Jul 2005 A1
20050210844 Kahlbaugh et al. Sep 2005 A1
20050214188 Rohrbach et al. Sep 2005 A1
20050233665 Groten et al. Oct 2005 A1
20060009106 Nishimura et al. Jan 2006 A1
20060094320 Chen et al. May 2006 A1
20060096263 Kahlbaugh et al. May 2006 A1
20060096932 Dema et al. May 2006 A1
20060101796 Kern et al. May 2006 A1
20060121811 Mangold et al. Jun 2006 A1
20060137317 Bryner et al. Jun 2006 A1
20060207932 Hajek et al. Sep 2006 A1
20060230731 Kalayci et al. Oct 2006 A1
20060242933 Webb et al. Nov 2006 A1
20060266701 Dickerson et al. Nov 2006 A1
20070039300 Kahlbaugh et al. Feb 2007 A1
20070227359 Choi Oct 2007 A1
20080073296 Dema et al. Mar 2008 A1
20090044702 Adamek et al. Feb 2009 A1
20090050578 Israel et al. Feb 2009 A1
20090266759 Green Oct 2009 A1
Foreign Referenced Citations (24)
Number Date Country
43 44 819 Jul 1994 DE
0 340 763 Nov 1989 EP
0 451 554 Oct 1991 EP
0 451 554 Oct 1994 EP
0 465 203 Mar 1996 EP
1 036 585 Sep 2000 EP
1 118 632 Aug 2001 EP
1 141 454 Oct 2001 EP
0 844 861 Mar 2002 EP
1 378 283 Jul 2002 EP
1 179 673 Dec 2002 EP
1 171 495 Mar 2003 EP
1 532 076 Nov 1978 GB
WO 9741167 Nov 1997 WO
WO 9947211 Sep 1999 WO
WO 0103802 Jan 2001 WO
WO 0245098 Jun 2002 WO
WO 03080904 Oct 2003 WO
WO 2004089509 Oct 2004 WO
WO 2005120678 Dec 2005 WO
WO 2006052656 May 2006 WO
WO 2006052732 May 2006 WO
WO 2006089063 Aug 2006 WO
WO 2009088647 Jul 2009 WO
Related Publications (1)
Number Date Country
20080073296 A1 Mar 2008 US
Divisions (1)
Number Date Country
Parent 10982538 Nov 2004 US
Child 11986377 US