This invention relates to a method for processing polymeric material, particularly one which results in products of high strength and durability and the products so formed.
It is common practice to make all kinds of components and products from “plastics” using a variety of high-rate low-cost molding (injection, blow-molding and the like.) technologies. These objects can be fabricated at low labor costs but can have high dimensional tolerance, finish and the like. Examples range from all sorts of toys (GI Joe and Barbie Dolls) through all sorts of appliances, household goods, furniture and the like. The big advantage of plastic is that it can be manufactured at exceedingly low costs and has ubiquitous application when structural integrity is not required. The big disadvantage of monolithic thermoplastics is that they have low strength and stiffness and cannot be used for load-bearing structural applications. Advanced composites overcome this shortcoming by laminating reinforcing fibers into a polymeric matrix. There are three major disadvantages with advanced composites. First, the lamination process is highly labor intensive, not well suited to automation and results in components that are more expensive to produce that their metal equivalents. Second, reinforcement is achieved in essentially only two dimensions. Finally, high dimensional tolerance is hard to achieve and maintain leading to substantial fit-up, shimming and the like and high assembly (bonding and joining) costs. There is a clear and compelling need to develop technology that can produce structural components with high dimensional tolerance and finish at low manufacturing costs.
The above problems are well known and can be summarized as high manufacturing costs, mostly labor, not amenable to automation and the material is often sticky and disorderly in the lay-up stage. Also the mechanical fit-up for joining parts can be difficult and expensive. That is, it is estimated that 60% of manufacturing costs are incurred in joining components for major assemblies and subassemblies.
Thus, there is need and market for technology to produce large polymer articles of high strength in 3 dimensions, with good dimensional tolerance, so as to overcome the above prior art shortcomings.
There has now been discovered a method to make the above components and structures of polymeric material and yet be of surpassing strength in 3 dimensions.
Broadly, the present invention provides, a method for making strong load-bearing plastics which includes, forming a mixture of magnetically tagged, electrically tagged, and untagged polymeric rods and flowing the mixture of the three types of rods through a forming tool across which electric and magnetic fields are applied, to form an article or structure with 3-D orientation of the molecules therein due to application of electric, magnetic and flow fields and thus a product of high strength in 3 dimensions.
The invention also provides a method for making durable polymeric articles in which portions thereof are oriented in 3 dimensions, which invention also includes the polymeric products so made, including those products with 3-D dimensional strength and stiffness, reminiscent of metal.
The invention also provides a high-strength plastic article having 3-D orientation of plastic molecules therein.
By polymerics or polymeric material, as used herein, is meant a material that has been synthesized chemically by combining a number of similar chemical units (monomers) to form a molecule of much greater molecular weight.
By polymeric rod, as used herein, is meant a polymeric molecule of sufficient stiffness and length to have a sufficient turning moment to achieve the desired orientation or degree of alignment herein. The degree of molecular alignment is governed by the polymeric flow rate and the magnitude and direction of the magnetic and/or electric moments which, in turn, depend on the length of the molecule.
The polymeric rods discussed herein can include PBO, PBZT, PBLG and PHIC. Such rods can be chemically treated on their ends with organometallic functional groups, including those containing cobalt, iron, manganese, nickel, platinum and nanoparticles containing these elements, to be susceptible to alignment in a magnetic field and can be treated on their ends with anions, cations and charged nanoparticles, to be susceptible for an alignment in an electric field. And the size of such rods can be 10 nm to 10000 nm in length, per the invention.
The types of forming tools to be employed with the method of the present invention, can vary and can, in addition to an injection mold, be a resin transfer mold, an autoclave mold and the like.
The strength of the magnetic field employed herein, can be 1 to 100 K gauss and of the electric field can be 100 to 10000 Volts per meter as employed with the method of the present invention.
The flow rate of the mixture, as it moves in the molding tool, through the electric and magnetic fields, per the invention, is suitably 0.01 to 100 inches per second and preferably one inch per second.
By PBO, PBZT, PBLG and PHIC is meant poly (paraphenylene-2,6-benzobisoxazole), poly (paraphenylene-2,6-benzobisthiasole), poly(gamma-benzyl-L-glutamate) and poly(n-hexyl isocyanate) respectively.
The invention will become more apparent from the following detailed specification and drawings in which;
Referring in more detail to the drawings, the material system is formulated using engineered components with well-defined molecular structure. These units, shown schematically in
The neutral rod 10 is an example of an untagged molecule of the prior art and as it (alone) flows in numbers, through an extruder, or duct 11, in the direction 13, per
The invention however, provides a mixture of three types of rods 10, 12 & 14, described above, the orientation of which can be controlled as disclosed below.
That is, the components are mixed and the mixture is heated, if necessary, to attain a fluid state and then flowed through an extruder or duct 11 to the orientation stage 15, where a combination of magnetic, electric, and flow fields are applied, as indicated in
This process is carried out within a tool 22, as illustrated in
Thus it is known that long rod-like molecules can be used to produce polymeric fibers that have exceedingly high strength and stiffness in the longitudinal direction. These desirable macroscopic properties are a consequence of a high degree of intermolecular alignment along an axis parallel to the extrusion direction. Herein is disclosed a method of controlling molecular alignment of rod-like polymers in three dimensions. This enables the fabrication of detail structural components from a monolithic thermoplastic. In order to achieve this it is necessary to: (1) Synthesize rod-like polymers such as PBO or PBZT or related molecules, with well-defined length, (2) Activate the ends of these long rod-like molecules with tagants that increase their susceptibility to external fields such as magnetic or electric fields. This is done with an end-capping chemical reaction. (3) Formulate a mixture of untagged, magnetically tagged and electrically tagged polymers and (4) Flow this mixture through a ceramic forming tool across which mutually oriented electric and magnetic fields have been applied. The concept is indicated in
Because the polymer backbone is identical in all three components there is no problem associated with mixing and blending. It can prove useful to include nanoparticles or other pseudo-spherical or dumbbell-like molecules to act as viscosity modifiers. The essential point is that the untagged molecules will orient in the direction of the flow field but the magnetically tagged particles will align in the direction of the magnetic field while the electrically tagged polymers will align in the direction of the electric field. By adjusting the flow rate, symmetries and intensities of these external fields it is possible to control the degree and direction of molecular alignment and entanglement of the rods, thus enabling the production of molded plastic components with the strength and stiffness resembling metals.
The basic idea is to provide a new kind of plastic that can be injection molded but has aluminum-like mechanical properties/high dimensional tolerance/highly integrated, to minimize bonding and joining operations and rapid manufacturing surge capability. That is, the method of the present invention enables one to develop a new class of monolithic structural polymer that is engineered such that it is injection-moldable and is formulated so that the three-dimensional orientational and translational (secondary and tertiary) structure can be controlled over mesoscopic distance scales. Thus it is possible to make detailed assemblies and major sub-assemblies at exceedingly low manufacturing costs.
That is, an advantage and new feature of the present invention, is that this new material allows fabrication of detail parts and assemblies with strikingly low manufacturing and assembly costs. Essentially it will allow components like automobile bodies or airframe assemblies or other vehicles and even structures, such as bridge or building components, to be molded using the same sorts of technologies that are currently used in toy manufacturing. With labor costs in the United States considerably higher than those in many other parts of the world this technology can play an important part in maintaining international competitiveness. The present invention will remove a large component of the labor cost associated with parts manufacturing and assembly and thereby provide a huge cost advantage.
The invention can be used by the government or industry in the production of a large number of detail components, sub-assemblies and major assemblies that are currently made out of metal or from advanced composite materials. Further, ubiquitous applications are seen including in automotive, aerospace and general engineering.
Accordingly, this invention teaches a new structure of matter and materials processing procedures that yield a polymeric material system with mechanical properties that are comparable to metals. The material and manufacturing process is unique in that detail components and major integrated assemblies and sub-assemblies can be manufactured using low cost techniques such as injection-molding. The components are of high strength and stiffness (approximately that of aluminum) but have low density and can be formed with high dimensional tolerance to near net shape. Because integrated components and highly active geometries can be made in a single operation, bonding and joining and related assembly costs are greatly reduced. This is achieved by chemically synthesizing a set of novel rigid and semi-rigid molecules that incorporate end-groups that make each individual molecule particularly susceptible to molecular alignment using an externally applied field such as an electric field, a magnetic field, or a flow field. For example, a rod-like polymer such as PBZT is synthesized to have a particular molecular weight and weight average distribution. As indicated above, the synthetic process is conducted so as to end-cap the rod-like polymer with a chemical moiety or moieties that are magnetically active, as alluded above, e.g., ferrocenyl or related derivatives. Using the same synthetic procedure, starting materials and the like, a second synthesis is conducted but in this case the final step is to end-cap the polymer with ionic or dipolar species, as noted above, that will impart susceptibility to external electric fields. A third synthesis is conducted to produce a polymer with no end-caps and which is not therefore particularly sensitive to externally applied electric or magnetic fields but will, by virtue of the rod-like stereochemistry, be susceptible to molecular alignment in a flow field. These materials are then blended in the presence of a viscosity modifier, such as nanoparticles, that enable the system to melt and flow at reasonably low temperatures. Then, as discussed above, the material is injection molded into a ceramic tool, while electric and magnetic fields are applied. This allows local control of molecular orientations and entanglement in three dimensions so as to produce high-strength parts.
The invention described herein can be manufactured and used by or for the Government for governmental purposes without the payment of any royalty thereon.