High strength stainless steel

FIELD OF THE INVENTION
This invention relates to an austenitic-martensitic stainless steel which is suitable to be used as a material for parts and elements, in which high strength, high toughness, high ductility and corrosion resistance are required, such as thin leaf spring, thin plate coil, cutlery, cutting tool body, etc., and which is especially suitable as a material for parts in which high strength and high ductility are required.
BACKGROUND OF THE INVENTION
For manufacturing the above-mentioned parts and elements, martensitic stainless steels, work-hardenable austenitic stainless steels, precipitation-hardenable stainless steels, etc. have conventionally been used.
Martensitic stainless steels are hardened by quenching from the austenitic state at an elevated temperature to cause martensitic transformation. Steels of SUS 410, 410J, 420J1, 420J2, 440A, 440B, 440C, etc. are typical examples of these steels, which have conventionally been used. Although these steels are low in strength and toughness in the annealed state, considerably high strength and toughness are attained by quenching and tempering. Therefore, these steels are widely used as inexpensive materials.
However, as martensitic stainless steels are not satisfactory for use in which high corrosion resistance is required, in such a field, work-hardenable austenitic stainless steels are used. These steels are Cr-Ni austenitic steels which are in the metastable state at ordinary temperatures and are hardened by cold rolling. The hardened steels are of two phases consisting of austenitie and martensite and therefore excellent in strength and ductility and also excellent in corrosion resistance. Typical examples of these steels are SUS 301, 304, etc. The strength of these steels depends upon the degree of cold working as stipulated in JIS G4313 and intensive cold working is required in order to attain high strength.
Precipitation-hardenable stainless steels contain precipitation-hardening elements and are hardened by heat-treatment, and therefore afford articles of good shape. Therefore, these steels are employed when shape requirements of products are strict and corrosion resistance is an important factor.
Typical examples of these steels are SUS 630, which contains Cu, and SUS 631, which contains Al. The former is hardened by solution treatment followed by aging during which a Cu-rich phase is precipitated. But the hardness thereof is 140 kgf/mm.sup.2 at the highest. The latter is hardened by first subjecting to solution treatment, then transforming tbe metastable austenite phase partly or wholly to the martensite phase by cold working, for instance, and thereafter precipitating a Ni.sub.3 Al intermetallic compound by aging. This can provide considerably high strength materials.
As a method for transforming the austenite phase of SUS 631 to martensite phase and then aging it, treatments such as TH 1050, RH 950, CH, etc. can be resorted to. But the strength attained by the former two treatments is 130 kgf/mm.sup.2 at the highest, while a strength as high as 190 kgf/mm.sup.2 can be attained by the CH treatment. In the CH treatment, the steel is first subjected to cold working to convert the austenite phase to the austenite-martensite two phases as in the case of work-hardenable stainless steels, and is thereafter subjected to aging. The strength after the cold working is around 150 kgf/mm.sup.2, depending on the degree of cold working. But the above-mentioned high strength is attained by precipitation of the Ni.sub.3 Al intermetallic compound when the steel is age-hardened.
Of the above-described stainless steels, martensitic stainless steels must be subjected to quenching and tempering in order to attain strength and toughness. The heat treatments are troublesome. In quenching, materials are heated to a high temperature (950.degree.-1100.degree. C.), wherefrom they are quenched. Rapid mertensitic transformation deteriorate shape of treated articles. In order to prevent such trouble, a special heat treatment such as press-quenching is required.
In the case of austenitic stainless steels, high degree cold working is required in order to attain high strength. But if high strength is attained, ductility is sacrificed, and the shape of sheet products and strip products is often deteriorated.
Further, in the case of precipitation-hardenable stainless steels, SUS 630 does not attain high strength, and SUS 631 often devlops surface roughness and is impaired in toughness and ductility because the steel contains 0.75-1.50% Al which has a strong affinity for oxygen and nitrogen, and alumina type inclusions are formed during the steel-making and coagulated inclusions of AlN are formed when the steel is cast.
Japanese Laid-open Patent Publication No. 52-007317 disclose a steel substantially contained in % by weight, C: .ltoreq.0.02%, S: .ltoreq.1.00%, Mn: .ltoreq.2.00%, P: .ltoreq.0.040%, S: .ltoreq.0.003%, Ni: 5.00-8.50%, Cr: 16.00-21.00%, Cu: 0.50-4.00%, N: <0.20%, O: .ltoreq.0.015% and the balance being Fe and unavoidable impurities. This steel is for compression forming and, therefore work-hardenability and formation of martensite are restricted by reducing C content, increasing N and adding Cu and reducing Si. That is, hardness of the resulting products are not satisfactory.
Japanese Laid-Open Patent Publication No. 56-077364 discloses a steel comprising, by weight C: .ltoreq.0.15%, N: .ltoreq.0.15%, Si: 0.ltoreq.1.5%, Mn: 0.5-2.0%, Ni: 5.0-9.0%, Cr: 13.0-20.0%, Cu: 1.0-4.0%, and the balance being Fe and unavoidable impurities and having the Md.sub.(30) (.degree.C.) value of -30.degree.-80.degree. C., said Md.sub.(30) (.degree.C.) being defined as ##EQU1##
The Md.sub.(30) (.degree.C.) is the temperature at which 30% cold-worked super-cooled austenite transforms into martensite of 50% and represents austenite stability (instability). This steel is intended for a spring material as well as the present invention. However, this steel is not satisfactory in the balance of strength and elongation. This is because the Mn content is rather high, the Si content is rather low and S is not restricted.
U.S. Pat. No. 4,378,246 by the inventors including two of the inventors of the present invention discloses a martensitic precipitation-hardening type stainless steel for spring comprising in % by weight more than 0.03% but not more than 0.08% of C, 0.3 to 2.5% of Si, not more than 4.0% of Mn, 5.0 to 9.0% of Ni, 12.0 to 17.0% of Cr, 0.1 to 2.5% of Cu, 0.2 to 1.0% of Ti and not more than 1.0% of Al, the balance being Fe and having a specifically defined restricted austenite stability A' of less than 42, said A' being defined as ##EQU2## having a specifically defined Cr equivalent/Ni equivalent ratio of not more than 2.7, said ratio being defined as ##EQU3## and further having a specifically defined hardness increase by aging .DELTA.Hv of between 120 and 210, said .DELTA.Hv being defined as ##EQU4## This steel is genuinely martensitic precipitation-hardenable steel. The fact is represented by the A' value less than 42, the rather high Mn content and addition of precipitate-forming elements such as Ti and Al. The A' value is an index which represents existence of the residual austenite after solution treatment. When this value is less than 42, the steel is simply martensitic.
It is not that ductility is not considered as the upper limit of .DELTA.Hv is somewhat restricted. However, ductility of this steel is not sufficient.
DISCLOSURE OF THE INVENTION
The present invention intends to provide a new steel material of a type different from the above-described. That is, this invention provides a stainless steel which has good workability and is hardened by work-hardening of austenite and formation of minute work-induced martensite and further hardened by aging, probably strain aging accompanied by some precipitaion.
This invention provides a high strength stainless steel essentially consisting of not more than 0.10% C., more than 1.5% and not more than 2.95% Si, less than 0.5% Mn, not less than 4.0% and not more than 8.0% Ni, not less than 12.0% and not more than 18.0% Cr, not less than 0.5% and not more than 3.5% Cu, not more than 0.15% N and not more than 0.004% S, wherein the total content of C and N is more than 0.10%, the balance being Fe and incidental impurities including up to 0.020% Al and up to 0.020% Ti, and the A' value as defined below is 50-150 and the Md(N) as defined below is 35-95. ##EQU5##
The steel of this invention contains Si, which is a martensite inducer and martensite strengthener, in a larger amount of more than 1.5% and not more than 2.95% than the conventional steel; and it contains C and N, which are martensite phase strengtheners, in an amount of not less than 0.10% in total. Therefore, the martensite phase is easily induced from the metastable austenite after the solution treatment by light cold working because of the presence of the high level of Si; and the thus induced martensite phase is hardened by Si, C and N and thus products of good shape, high strength and high ductility can be obtained. And as a precipitation hardening element, Cu, which acts synergistically with Si and with which there is no risk of inclusion formation, is added, and aging is additionally carried out, and thus a higher strength is attained. Therefore, the steel of this invention can be used as a work-hardenable stainless steel which is superior to the conventional steel in strength and ductility an also can be used as a precipitation-hardenable stainless steel.
Now the reason why the composition is defined as stated above is explained.
C is an austenite former and is effective for inhibiting formation of .delta.-ferrite at high temperature and strengthening the martensite phase induced by cold working. But the solution limit of C is restricted because of high Si content in the steel of this invention. Therefore, a high carbon content will cause deposition of chromium carbides at grain boundaries, which will induce abatement of ductility and resistance to intergranular corrosion. Therefore, the C content is limited to 0.10%.
Si is used usually as a deoxidizer. For this purpose, the Si content is not more than 1.0% as seen in work-hardenable austenitic stainless steels such as SUS 301, 304, etc., and precipitation hardenable stainless steel such as SUS 631. In the case of the steel of this invention, however, Si is contained in a higher amount than this, that is, more than 1.5%, so that the martensite phase is easily induced in cold working, that is, it is induced even by slight cold working and the formation thereof is promoted and the ratio of martensite phase to austenite phase is enhanced. The formed martensite is not only strengthened but it is dissolved in the remaining austenite phase to harden it and thus the hardness after working is enhanced. Also, in aging Si increases the aging effect in combination with Cu. As stated above, Si has many effects. In order to make Si exhibit such effects, Si must be contained in an amount of more than 1.5%, higher than the conventional content range. But if it exceeds about 3.0%, it induces high temperature cracking and causes some problems in manufacturing. More than 1.5% and not more than 2.95% is a suitable content.
Mn is an element which controls the stability of the austenite phase. The content is determined by taking into consideration the balance with the other elements. In the steel of the present invention, a higher content of Mn will cause abatement of ductility and also causes some problems when the steel is used. For this reason the Mn content is limited to 0.5%, rather remarkably lower than the conventional range.
Ni is an essential element for the formation of an austenite phase at both high temperatures and room temperature. In the case of the steel of this invention, metastable austenite must exist at room temperature and must be transformed into martensite phase by cold working. For this purpose, with less than 4.0% Ni, a large amount of .delta.-ferrite is formed at a higher temperature and the austenite phase becomes rather unstable than metastable at room temperature. On the other hand, with more than 8.0% Ni, the martensite phase is not easily induced by cold working. Therefore the Ni content is selected as 4.0-8.0%.
Cr is an essential element for obtaining corrosion resistance. In order to provide the steel with desired corrosion resistance, not less than 12% of Cr is required. But Cr is a ferrite former. If a higher amount of Cr is contained, a large amount of .delta.-ferrite is formed at high temperatures. Therefore, a correspondingly larger amount of austenite former elements (C, N, Ni, Mn, Cu, etc.) must be contained to inhibit formation of the .delta.-ferrite. And if large amounts of the austenite formers are contained, the austenite is in turn stabilized at room temperature and the steel is not hardened by cold working and aging. As such, the upper limit of the Cr content is defined as 18.0%.
Cu hardens the steel in aging in combination with Si. With too small an amount, the effect thereof is not remarkable and if too large an amount thereof is contained, it causes cracking. The proper amount is estimated as 0.5-3.5%.
N is an austenite former and is very effective for hardening both austenite phase and martensite phase. However, if N is contained in high amounts, it may cause blow holes when the steel is cast. Therefore, the N content is limited to not more than 0.15%.
S forms MnS in the presence of Mn, and brings about abatement of ductility and therefore it is an especially deleterious element in the steel of this invention. The upper limit thereof is restricted to 0.004% in order to avoid abatement of ductility.
C and N have similar effects and are interchangeable. Although the respective upper limits for these elements are as defined above, the total amount of these two elements must be not less than 0.10% to utilize their effect.
In addition to the above-mentioned elements, a slight residual amount of Al and Ti, which are used as deoxidizers, Ca and REM's (rare earth metals) which are used as desulfurizer, etc. and incidental inevitable impurities such as P are permitted to be present in the steel of the present invention. The steel of this invention is allowed to contain not more than 0.020% of Al, not more than 0.020% of Ti, although these elements are undesirable because they form non-metallic inclusions which impair ductility. Not more than 0.040% of P, not more than 0.01% of Ca and not more than 0.02% of REM's are allowed.
Preferably, the high strength stainless steel of this invention contains not more than 0.08% C, more than 1.5% and not more than 2.95% Si, less than 0.46% Mn, not less than 4.5% and not more than 7.5% Ni, not less than 14.0% and not more than 17.0% Cr, not less than 0.8% and not more than 3.0% Cu, not more than 0.13% N and not more than 0.0035% S.
More preferably, the high strength stainless steel of this invention contains not more than 0.075% C, more than 1.5% and not more than 2.95% Si, less than 0.42% Mn, not less than 5.50% and not more than 7.30% Ni, not less than 14.5% and not more than 16.5% Cr, not less than 1.00% and not more than 2.65% Cu, not more than 0.125% N and not more than 0.003% S.
In any case, the total content of C and N should be not less than 0.10%.
The above-mentioned A' value as defined in the same way as in U.S. Pat. No. 4,378,246 must be more than 42. In the present invention the A' value is calculated with the Ti and Al contents as 0.02% respectively. The A' value as defined above is simply referred to in order to distinguish the steel of the present invention from that of U.S. Pat. No. 4,378,246, although the thus defined A' value is not inherently applicable to the steel of the present invention.
The Md(N) is an index which represents austenite stability at room temperature (25.degree. C.). The smaller this value, the more stable the austenite. Therefore, as the value is larger, more martensite is formed. If this value is less than 35, the resulting age-hardened steel material is insufficient in hardness. When this value exceeds 95, the resulting steel material is insufficient in ductility.

BRIEF EXPLANATION OF THE DRAWINGS
The invention will now be described by way of working examples with reference to the attached drawings.
FIG. 1 shows the relation between tensile strength and elongation of the steels of this invention (hereinafter called "inventive steels"), conventional steels and comparative steels in the cold-rolled state and age-hardened state. The circle, square and triangle symbols denote respectively the inventive steels, conventional steels and comparative steels. Blank symbols denote the cold-rolled state and solid black ones the age-hardened state. The solid line, broken line and one-dot chain line indicate respectively the data distributions of the inventive steels, conventional steels and comparative steels.
FIG. 2 shows the relation between tensile strength and elongation of Inventive Steel H1 and Comparative Steel e.
FIG. 3 is a graph representing the relation between the amount of the work-induced martensite and the Md(N) value of inventive steels and similar steels.
FIG. 4 is a graph representing the relation between the ratio of notch tensile strength (NTS)/tensile strength (TS) and the Md(N) value of inventive steels and similar steels.
FIG. 5 is a graph representing the relation between the .DELTA.Hv value and the Md(N) of the invention steels and similar steels.

DETAILED DESCRIPTION OF THE INVENTION
Inventive steels (H1-H4), conventional steels (A-C) and comparative steels (a-f) of the compositions as shown in Table 1 were prepared and hot-rolled by the usual method, and they were cold-rolled with varied degrees of reduction to form high strength cold-rolled steel sheet samples. The calculated A' values and Md(N) values are indicated in Table 1. A' values were calculated with the Ti and Al contents as 0.02% respectively. The amount of the martensite induced by cold working (.alpha.), hardness, tensile strength and elongation of the thus made steel sheet samples were measured. Then these high strength cold-rolled steel sheets were age-hardened, and hardness, tensile strength and elongation were measured. The results are shown in Table 2, wherein the difference in the hardness before and after aging (.DELTA.Hv) is also indicated. Of the results as shown in Table 2, the relation between tensile strength and elongation is shown in FIG. 1. Further, the relation between tensile strength and elongation of Inventive Steel H1 and Comparative Steel e, which is close to the inventive steels in properties in the cold-rolled state is shown in FIG. 2.
As is apparent from Table 2, the amounts of the induced martensite (.alpha.) of the inventive steels are larger than those of the conventional steels at the same reduction, since martensite is more easily induced by cold rolling in the inventive steels. In the inventive steels, more martensite is produced with less reduction.
As is apparent from FIG. 1, the inventive steels have a higher tensile strength and elongation than the conventional and comparative steels, both in the cold-rolled state and in the aged state, and show a remarkable increase in tensile strength by aging. That is to say, the inventive steels are superior to conventional work-hardenable austenitic stainless steels and precipitation-hardenable stainless steels in tensile strength and elongation both when they are used in the cold-rolled state and when they are used in the aged state. As the degree of cold-rolling can be reduced, good shape can be attained.
It will be apparent from a comparison of Table 1 and Table 2 that greater values of .DELTA.Hv are obtained in steels in which Si and Cu co-exist. It is understood that the age-hardening is caused by the synergistic action of Si and Cu.
It is apparent from FIG. 2 that Comparative Steel e which contains higher amounts of Mn and S is inferior to the inventive steels in elongation at the strength level after age-hardening. It is understood that ductility is inferior when the steel contains Mn and S in higher amounts.
TABLE 1__________________________________________________________________________ Elements (%) C Si Mn S Ni Cr N Cu Al Remarks Ms (.degree.C.) Md (N) A' value__________________________________________________________________________InventiveSteelsH1 0.028 2.67 0.46 0.002 6.50 15.88 0.103 1.75 -- -61.6 73 62.3H2 0.059 2.72 0.42 0.001 6.56 15.97 0.099 1.74 -- -114.0 56 88.8H3 0.075 2.49 0.22 0.002 5.93 15.80 0.125 2.43 -- -125.4 43 102.0H4 0.042 2.18 0.36 0.002 5.85 15.10 0.098 2.65 -- 12.6 74 73.7ConventionalSteelsA 0.105 0.52 1.05 0.004 7.09 16.82 0.025 0.05 -- SUS301 -95.1 66.7 128.0B 0.120 0.50 1.13 0.006 7.54 17.50 0.015 0.07 -- " -161.23 38.8 141.7C 0.085 0.41 0.57 0.005 7.39 16.72 0.011 0.05 1.18 SUS631 -33.5 83.7 110.2ComparativeSteelsa 0.013 2.69 0.30 0.008 9.91 12.01 0.016 1.70 -- 66.1 93.97 50.5b 0.027 2.01 0.42 0.005 7.96 14.93 0.061 0.91 -- -19.9 91.3 61.1c 0.104 0.28 1.00 0.007 6.59 16.07 0.017 1.79 -- -9.9 49.0 127.6d 0.063 0.22 1.00 0.006 6.60 15.68 0.062 1.80 -- 0.7 62.7 92.5e 0.074 2.78 1.47 0.008 5.59 15.43 0.061 1.92 -- -30.6 68.8 101.1f 0.071 2.83 2.10 0.002 7.91 13.40 0.086 0.03 -- -146.8 80.9 98.7__________________________________________________________________________
TABLE 2__________________________________________________________________________ As rolled As aged 400.degree. C. .times. 1 hr Sample Reduction .alpha. H'dness T.S. El. H'dness T.S. El. No. (%) (%) Hv (10) (kg/mm.sup.2) (%) Hv (10) (kg/mm.sup.2) (%) .DELTA.Hv__________________________________________________________________________Inventive H1 40 63.0 455 154 6.7 547 185 3.2 92steels 45 68.5 469 163 5.0 568 200 2.5 99 50 72.0 488 169 4.0 589 206 2.1 101 55 74.5 500 175 3.1 599 220 1.7 96 H2 40 63.5 481 167 6.1 580 196 3.1 99 45 64.5 502 175 4.4 601 208 2.3 99 50 67.0 520 183 4.0 612 219 2.0 92 55 69.5 534 191 3.4 628 225 1.6 94 H3 45 43.5 469 162 5.9 571 196 3.0 102 50 49.0 490 170 5.0 595 205 2.1 105 55 54.0 511 178 4.1 619 219 1.7 108 H4 45 45.5 428 147 7.2 526 178 3.1 98 50 51.5 440 151 6.3 541 180 2.6 101 55 57.3 456 159 4.4 551 187 2.0 95Conventional A 45 39.5 440 149 6.7 467 155 3.5 27steels 50 43.5 451 155 5.1 490 163 2.4 39 55 47.0 465 162 4.5 503 171 1.5 38 B 55 32.5 464 161 4.5 506 178 1.8 40 60 45.0 504 177 2.4 544 194 1.4 40 C* 45 44.5 420 143 7.0 520 182 1.7 100 50 49.0 445 153 5.6 549 189 1.2 104 55 58.0 451 159 4.6 558 195 1.1 107Comparative a 50 43.0 379 127 4.3 476 160 2.1 95Steels 60 55.5 410 136 2.9 506 171 1.0 96 b 50 56.0 415 140 5.2 482 164 2.8 67 60 65.0 441 149 3.1 507 172 1.4 66 c 50 60.5 473 165 4.4 514 180 2.0 43 60 69.0 500 183 1.9 542 195 1.6 42 d 50 67.0 444 157 2.6 503 174 2.3 59 60 76.0 459 172 2.0 516 182 1.5 57 e 40 48.0 459 160 5.6 549 188 1.8 90 45 50.5 473 162 5.0 558 194 1.7 85 50 55.5 486 167 4.0 580 202 1.5 94 55 59.5 499 173 3.3 592 212 1.2 93 f 50 46.5 447 149 4.8 500 170 2.1 53 60 54.0 479 161 2.7 528 180 0.9 49__________________________________________________________________________ *Conventional Steel C was aged at 480.degree. C. for 1 hour.
Incidentally, .DELTA.Hv values of Conventional Steel C and Comparative steel a are high. But tensile strength in the cold-rolled state of these steels is not high and therefore the increase in tensile strength by aging is not so large. The high .DELTA.Hv value of Comparative Steel C is based on precipitation of the intermetallic compound Ni.sub.3 Al.
For the sake of comparison, we reproduce Table 1 of U.S. Pat. No. 4,378,246 here as Table 3 in which Ms(.degree.C.) values and Md(N) values are incorporated.
As seen in Table 1 and 3, the Md(N) values of the steels % U.S. Pat. No. 4,378,246 are more than 100, while those of the present invention are 43-74 in the indicated working examples.
Further, we carried out the following experiment. Steels of the present invention and those of similar compositions, which are indicated in Table 4, were prepared in the same manner as described above and the cold-rolled sheets were subjected to aging at 400.degree. C. for 1 hour and mechanical properties were measured. The results are illustrated in FIGS. 3, 4 and 5.
FIG. 3 shows the relation between the Md(N) value and the amount of martensite formed from austenite. As seen there, the two are in the linearly proportional relation.
FIG. 4 shows the relation between the Md(N) value and the NTS (notch tensile strength)/TS (tensile strength) ratio. Said ratio is an index of toughness. FIG. 4 tells that when Md(N) exceeds 95, said ratio precipitously drops.
TABLE 3__________________________________________________________________________ A' Cr equ. Hv Md Specimen No. C Si Mn Ni Cr Cu Ti Al N value Ni equ. Value Ms (N)egree.C.)__________________________________________________________________________Steels of 1 0.033 1.45 0.31 7.40 14.90 1.00 0.34 0.020 0.015 39.83 2.32 162 101.5 115U.S. Pat. No. 2 0.047 0.65 1.00 6.70 14.50 0.51 0.32 0.45 0.009 39.57 2.42 188 146.8 1364,378,246 3 0.034 1.52 0.29 7.01 14.77 0.61 0.28 0.025 0.015 39.46 2.45 146 127.8 137 4 0.048 1.51 0.30 7.10 14.52 1.70 0.26 0.018 0.013 41.31 2.28 156 112.7 104 5 0.032 1.53 0.31 7.07 14.55 0.51 0.49 0.030 0.010 38.37 2.51 195 144.0 143 6 0.044 1.53 0.30 7.21 14.70 0.70 0.43 0.020 0.008 39.37 2.44 179 112.9 128 7 0.045 0.34 2.50 6.21 14.50 0.30 0.95 0.021 0.012 38.55 2.32 205 133.7 120 8 0.064 1.55 0.30 7.10 14.75 0.90 0.47 0.024 0.012 40.01 2.49 177 76.9 113 9 0.065 1.45 0.29 6.71 14.58 0.62 0.26 0.022 0.011 41.24 2.50 123 111.0 132 10 0.034 1.49 0.32 7.45 15.05 1.30 0.41 0.020 0.012 39.96 2.33 187 94.1 105Control 11 0.075 1.53 0.52 7.70 15.00 0.50 0.29 0.024 0.012 42.70 2.25 124 4.7 95.9 12 0.063 0.96 0.32 6.50 14.43 0.52 0.22 0.018 0.009 41.51 2.43 87 149.4 143.6 13 0.035 1.50 0.32 7.10 14.70 0.55 0.70 0.024 0.012 38.27 2.61 232 128.1 137.3 14 0.036 1.49 0.32 7.44 14.94 1.08 0.57 0.020 0.009 39.38 2.41 217 100.9 112.2 15 0.010 1.54 0.33 7.51 14.81 1.09 0.31 0.028 0.014 38.86 2.27 180 135.4 124.2 16 0.006 1.59 0.35 7.66 14.89 0.95 0.41 0.028 0.013 38.66 2.30 204 129.1 125.1 17 0.010 1.08 0.28 7.63 15.03 1.07 0.33 0.020 0.010 39.03 2.20 159 140.0 121.4 18 0.007 1.55 0.32 7.49 14.93 1.08 0.36 0.026 0.018 38.68 2.32 188 130.0 123.5 19 0.010 1.54 0.30 7.30 14.97 1.05 0.48 0.021 0.011 38.50 2.44 215 147.5 128.9 A (SUS301) 0.096 0.51 1.04 6.96 16.72 0.06 -- 0.020 0.010 not not not -42.3 80.3 calc'd calc'd calc'd B (17-7PH) 0.071 0.44 0.51 7.24 16.73 0.08 0.09 1.18 0.021 not not not -16.9 91.5 calc'd calc'd calc'd__________________________________________________________________________
TABLE 4__________________________________________________________________________ Amount of NTS/ A'Sp. No C Si Mn S Ni Cr Cu N Md(N) .DELTA.Hv Martensite TS Ms (.degree.C.) Value Remarkes__________________________________________________________________________1 0.060 1.22 0.32 0.002 6.53 16.46 1.79 0.062 63 74 55 1.07 -27.6 89.8 X2 0.062 2.32 0.92 0.003 5.23 15.48 1.81 0.055 97 108 87 1.00 +50 90.0 X3 0.030 1.41 0.20 0.002 6.56 16.52 1.79 0.112 63 81 58 1.07 -66 64.4 X4 0.060 2.64 0.43 0.003 7.66 15.86 1.64 0.086 38 78 43 1.10 -54.7 90.6 O5 0.059 2.72 0.42 0.001 6.56 15.97 1.74 0.099 56 92 58 1.12 -114 88.8 H2 O6 0.073 2.54 0.53 0.003 5.35 15.13 1.71 0.054 103 105 95 0.80 +47.9 99.0 O7 0.106 2.58 1.04 0.004 6.96 16.30 1.79 0.019 30 48 29 1.12 -114 129.7 X8 0.028 2.67 0.46 0.003 6.50 15.88 1.75 0.103 73 101 72 1.10 -61.6 62.3 H1 O9 0.073 2.77 1.04 0.007 5.41 15.60 1.94 0.056 78 95 65 1.05 -2.1 99.9 X10 0.065 1.42 0.35 0.003 7.32 16.20 0.98 0.096 56 64 47 1.08 -136.6 94.1 X11 0.075 2.49 0.22 0.002 5.93 15.80 2.43 0.125 43 105 40 1.08 -125.4 102.0 H3 O12 0.037 2.01 0.42 0.005 7.96 15.30 0.91 0.061 80 67 76 1.05 -51.9 70.4 O13 0.066 2.83 1.54 0.008 6.12 16.64 2.07 0.110 21.5 45 20 1.10 -185.4 75.7 X14 0.074 2.78 1.47 0.008 5.56 15.43 1.92 0.061 69.5 99 56 1.00 -28.8 101.1 E X__________________________________________________________________________ O: invention steel, X: similar steel
FIG. 5 shows the relation between .DELTA.Hv and Md(N). FIG. 5 tells that under the Md(N) value of 35, the hardness increased by aging is insufficient. From the results shown in FIGS. 3, 4 and 5, it is understood that when the Md(N) value is between 35 and 95, the aged steel materials have good combination of hardness and ductility.
As has been described above, the steel of this invention is superior to known work-hardenable austenitic stainless steels and precipitation hardenable stainless steels in strength and ductility. The amounts of Mn, S, Ti, and Al, which form undesirable non-metallic inclusions, are carefully restricted and controlled, and in their stead, Cu, which does not produce undesirable inclusions, is added in a proper amount. This does not impair good surface smoothness, which is a characteristic of stainless steels. The steel is inexpensive since it does not contain no expensive elements.

Number	Name	Date	Kind
3785787	Yokota et al.	Jan 1974
4378246	Hoshino et al.	Mar 1983

Number	Date	Country
2453109	May 1975	DEX
56-77364	Jun 1981	JPX
62-50442	Mar 1987	JPX

High strength stainless steel

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

CROSS REFERENCE TO THE RELATED APPLICATION

US Referenced Citations (2)

Foreign Referenced Citations (3)

Continuation in Parts (1)