High temperature fiber and method of making

Abstract
Disclosed is a method of making high temperature fiber including incorporating an inorganic atom into a polymer precursor fiber to form a modified polymer precursor fiber and converting the modified polymer precursor fiber to a high temperature fiber having a bonded inorganic atom.
Description
BACKGROUND

Exemplary embodiments pertain to the art of high temperature fibers.


Composite components are finding increased use in aerospace applications due to their unique, tailorable properties which can result in significant weight savings, increased performance and durability, as well as reductions in specific fuel consumption. In particular, gas turbine engines, such as aircraft engines, operate in severe environments and show significant benefit from incorporation of composite materials. Additionally, other aerospace components, such as aircraft brakes and friction materials, can benefit from incorporating composite materials.


As an example, ceramic matrix composite (CMC) components have desirable high temperature mechanical, physical, and chemical properties which allow gas turbine engines to operate at much higher temperatures with significant weight savings as compared to current engines with superalloy components. Ceramic matrix composites include fibers embedded in a ceramic matrix. There is an ongoing need for fibers with increased oxidation resistance and temperature resistance.


BRIEF DESCRIPTION

Disclosed is a method of making high temperature fiber including incorporating an inorganic species into a polymer precursor fiber to form a modified polymer precursor fiber and converting the modified polymer precursor fiber to a high temperature fiber having a bonded inorganic atom.


In addition to one or more of the features described above, or as an alternative to any of the foregoing embodiments, the bonded inorganic atom is bound to nitrogen, oxygen, silicon, boron, or carbon.


In addition to one or more of the features described above, or as an alternative to any of the foregoing embodiments, the bonded inorganic atom includes aluminum, a refractory metal, a lanthanide, silicon, boron, yttrium, or a combination thereof.


In addition to one or more of the features described above, or as an alternative to any of the foregoing embodiments, the bonded inorganic atom includes a refractory metal bound to carbon.


In addition to one or more of the features described above, or as an alternative to any of the foregoing embodiments, the polymer precursor fiber includes acrylic polymers, cellulosic polymers, phenolic polymers, polyolefins, polyacetylene, polyacrylonitrile, polyphenylene, polyvinylidene chloride, copolymers and terpolymers thereof, polyaromatic hydrocarbon polymers, and combinations of the foregoing.


In addition to one or more of the features described above, or as an alternative to any of the foregoing embodiments, the polymer precursor fiber includes polycarbosilanes, polysilazanes, polysilanes, polycarbosiloxanes, organo-silsesquioxane-containing polymers, sol-gel derived polymers, polysiloxanes, polyborosilazanes, polyaluminosilazanes, any of the foregoing including a metal, and combinations thereof.


In addition to one or more of the features described above, or as an alternative to any of the foregoing embodiments, the polymer precursor fiber includes ceramic particles.


In addition to one or more of the features described above, or as an alternative to any of the foregoing embodiments, the inorganic species is incorporated into the polymer precursor fiber by atomic layer deposition (ALD), molecular layer deposition (MLD), sequential vapor infiltration (SVI) or a combination thereof.


In addition to one or more of the features described above, or as an alternative to any of the foregoing embodiments, the polymer precursor fiber includes an existing inorganic atom. In the high temperature fiber the bonded inorganic atom may be the same as or different from the existing inorganic atom.


Also disclosed herein is a high temperature fiber including a core composition and a peripheral composition wherein the peripheral composition differs from the core composition and the peripheral composition includes a bonded inorganic atom.


In addition to one or more of the features described above, or as an alternative to any of the foregoing embodiments, the high temperature fiber includes a ceramic fiber, carbon fiber, fibers containing silicon, fibers containing boron, or a fiber containing any combination of silicon, carbon and/or boron.


In addition to one or more of the features described above, or as an alternative to any of the foregoing embodiments, the high temperature fiber includes carbon, SiC, SiBCN, SiNC, B4C, SiOC, SiAlCN, aluminum oxide, zirconium oxide, yttrium oxide, titanium dioxide, zirconium carbide, zirconium nitride, boron nitride, silicon nitride, aluminosilicate, silicon dioxide, E-glass, S-glass, and combinations thereof.


In addition to one or more of the features described above, or as an alternative to any of the foregoing embodiments, the bonded inorganic atom is a refractory metal atom bound to a carbon atom.


In addition to one or more of the features described above, or as an alternative to any of the foregoing embodiments, the bonded inorganic atom is bound to nitrogen, oxygen, silicon, boron or carbon.


Also disclosed herein is a composite having a high temperature fiber embedded in a matrix wherein the high temperature fiber includes a core composition and a peripheral composition wherein the peripheral composition differs from the core composition and the peripheral composition includes a bonded inorganic atom.


In addition to one or more of the features described above, or as an alternative to any of the foregoing embodiments, the high temperature fiber includes a ceramic fiber, carbon fiber, fibers containing silicon, fibers containing boron, or a fiber containing any combination of silicon, carbon and/or boron.


In addition to one or more of the features described above, or as an alternative to any of the foregoing embodiments, the bonded inorganic atom is a refractory metal atom bound to a carbon atom.


In addition to one or more of the features described above, or as an alternative to any of the foregoing embodiments, the bonded inorganic atom is bound to nitrogen, oxygen, silicon, boron or carbon.







DETAILED DESCRIPTION

A detailed description of one or more embodiments of the disclosed apparatus and method are presented herein by way of exemplification and not limitation with reference to the Figures.


A high temperature fiber, as used herein, refers to a fiber which maintains shape and integrity at temperatures greater than or equal to 800° C. High temperature fibers can be used in composites having a variety of matrices such as polymer, metal, glass, glass/ceramic, ceramic or a combination thereof.


An inorganic atom, as used herein, refers to any atom except carbon. A bonded inorganic atom refers to an inorganic atom that is bonded to other atom(s) that form the high temperature fiber. The bonded inorganic atom is bonded to as many other atoms as permitted by its valency and oxidation state.


Composites exhibit a significant amount of damage tolerance when under an applied load. In ceramic matrix composites (CMC) in particular, this damage tolerance is predominantly due to the formation of multiple matrix cracks that aid in the redistribution of stresses. However, the formation of matrix cracks can result in environmental exposure to the fiber which can result in fiber oxidation. High temperature fibers having a bonded inorganic atom, when exposed to high temperatures, may have greater resistance to oxidation because the inorganic atom may oxidize and form a protective oxide.


Described herein is a method of making high temperature fibers. The method includes incorporating an inorganic species into a polymer precursor fiber to form a modified polymer precursor fiber and converting the modified polymer precursor fiber to the high temperature fiber having a bonded inorganic atom.


Exemplary polymer precursor fibers are fibers formed of polymers, optionally in combination with ceramic particles. The polymer precursor fibers can be converted, typically through pyrolyzing or other thermal or radiation treatment, to a high temperature fiber such as a ceramic fiber, carbon fiber, fiber containing silicon, fiber containing boron, fiber containing nitrogen, fiber containing oxygen, and fiber containing any combination of silicon, carbon, nitrogen, oxygen and/or boron. Exemplary polymers for forming carbon fibers include acrylic polymers, cellulosic polymers, phenolic polymers, polyolefins, polyacetylene, polyacrylonitrile, polyphenylene, polyvinylidene chloride, copolymers and terpolymers thereof polyaromatic hydrocarbon polymer (mesophase pitch), and combinations of the foregoing. Exemplary polymers for forming fibers containing silicon include polycarbosilanes, polysilazanes, polysilanes, polycarbosiloxanes, organo-silsesquioxane-containing polymers, sol-gel derived polymers, polysiloxanes, polyborosilazanes, polyaluminosilazanes, any of the foregoing including a metal such as aluminum, zirconium, titanium, boron, hafnium and the like, and combinations thereof. Fiber precursors to SiBCN, SiNC, B4C, SiOC, Si3N4, BN and SiAlCN fibers can also be used. The polymer precursor fiber may comprise ceramic particles such as oxides, carbides, nitrides, borides, glasses and combinations thereof. The polymer precursor fiber may be (partially or fully) cross linked, cured, or densified but requires pyrolysis or other thermal or radiation treatment under controlled atmosphere to convert to a high temperature fiber.


The polymer precursor fiber may comprise an inorganic atom. The methods described herein provide ways to supplement the existing inorganic atoms with additional inorganic atoms which may be chemically the same or different from the existing inorganic atoms. For example, a SiBCN fiber may be modified with either more B or Al or both.


The inorganic species is incorporated into the polymer precursor fiber by atomic layer deposition (ALD), molecular layer deposition (MLD), sequential vapor infiltration (SVI) or a combination thereof “Incorporated” includes chemical bonding and/or infiltration into the volume of the polymer precursor fiber. Chemical bonding includes all types of chemical bonding, for example, covalent and ionic. The inorganic species includes an inorganic atom and at least one leaving group (or reactive functional group). Exemplary inorganic species include metal containing species such as organometallic compounds and inorganic compounds. The term “sequential vapor infiltration” includes variants such as multiple pulse infiltration and sequential infiltration synthesis. Sequential vapor infiltration diffuses reactants into the precursor fiber and incorporates the inorganic species below the surface of the polymer precursor fiber. Incorporated inorganic species result in bonded inorganic atoms following conversion steps to form the high temperature fiber. Atomic layer deposition and molecular layer deposition bond the inorganic species at the surface of the polymer precursor fiber and may build up the fiber surface with multiple cycles. SVI, ALD and/or MLD may be combined to result in the desired distribution of inorganic species and final high temperature fiber diameter.


Incorporating the inorganic species into the polymer precursor fiber may result in a doped structure (i.e., present in an amount below levels which form a second phase), a multi-phase structure, a highly disordered structure, an amorphous structure, or a layered structure (when inorganic atoms are present primarily at or near the surface) upon conversion to the high temperature fiber. The inorganic species may also bond to more than one polymer chain in the polymer precursor fiber, thus acting as a cross linker and further stabilizing the polymer precursor fiber.


Exemplary inorganic atoms present in the inorganic species include aluminum, refractory metals, lanthanides, boron, silicon, yttrium, and combinations thereof. Exemplary refractory metals include titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten, manganese, technetium, rhenium, ruthenium, osmium, rhodium, and iridium.


The inorganic atom may be bonded to a nitrogen, oxygen, silicon, boron, or carbon atom in the high temperature fiber. The bonded inorganic atom may include a refractory metal covalently bound to a carbon atom. “Bonded” and “bonding” as used herein include all types of chemical bonding such as covalent and ionic bonds unless specifically limited to a specific kind of bonding.


Once the inorganic species is incorporated into the polymer precursor fiber to form the modified polymer precursor fiber, the modified polymer precursor fiber is converted to the high temperature fiber using known procedures such as pyrolysis or thermal conversion under controlled atmosphere(s), temperature(s) and time(s).


Exemplary high temperature fibers include carbon, SiC, SiBCN, SiNC, B4C, SiOC, SiAlCN, HfC, ZrC, Si3N4, BN, aluminum oxide, zirconium oxide, yttrium oxide, titanium dioxide, aluminosilicate, E-glass, S-glass, and combinations thereof.


The resulting high temperature fiber having a bonded inorganic atom may be incorporated into a composite. Composites, as used herein, refer to reinforcing materials dispersed in a matrix. Exemplary matrices include polymers, metals, ceramics, glasses and combinations thereof. Exemplary ceramic and glass matrices may include: SiC, SiCO, SiCNO, SiBCN, Si3N4, carbides such as boron carbide, zirconium carbide, hafnium carbide, carbon, mixed carbide/diboride matrices, aluminum oxide, mullite, zirconium oxide, borosilicate glasses, aluminosilicate glasses, high silica glasses, phosphate glasses, and combinations thereof.


The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the present disclosure. As used herein, the singular forms “a”, “an” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprises” and/or “comprising,” when used in this specification, specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, element components, and/or groups thereof.


While the present disclosure has been described with reference to an exemplary embodiment or embodiments, it will be understood by those skilled in the art that various changes may be made and equivalents may be substituted for elements thereof without departing from the scope of the present disclosure. In addition, many modifications may be made to adapt a particular situation or material to the teachings of the present disclosure without departing from the essential scope thereof. Therefore, it is intended that the present disclosure not be limited to the particular embodiment disclosed as the best mode contemplated for carrying out this present disclosure, but that the present disclosure will include all embodiments falling within the scope of the claims.

Claims
  • 1. A method of making high temperature fiber comprising incorporating an inorganic species into a polymer precursor fiber to form a modified polymer precursor fiber and converting the modified polymer precursor fiber to a high temperature fiber having a bonded inorganic atom, wherein the polymer precursor fiber comprises polycarbosilanes.
  • 2. The method of claim 1, wherein the bonded inorganic atom is bound to nitrogen, oxygen, silicon, boron, or carbon.
  • 3. The method of claim 1, wherein the inorganic atom comprises a lanthanide.
  • 4. The method of claim 3, wherein the bonded inorganic atom comprises a refractory metal bound to carbon.
  • 5. The method of claim 1, wherein the inorganic species is incorporated into the polymer precursor fiber by atomic layer deposition (ALD), molecular layer deposition (MLD), sequential vapor infiltration (SVI) or a combination thereof.
  • 6. The method of claim 1, wherein the polymer precursor fiber comprises an existing inorganic atom.
  • 7. The method of claim 6, wherein the inorganic species comprises an inorganic atom that is chemically different from the existing inorganic atom.
  • 8. The method of claim 6, wherein the inorganic species comprises an inorganic atom that is chemically the same as the existing inorganic atom.
US Referenced Citations (35)
Number Name Date Kind
4942011 Bolt et al. Jul 1990 A
5204380 Seyferth Apr 1993 A
5558907 Steffier Sep 1996 A
5783139 Curran Jul 1998 A
6299988 Wang et al. Oct 2001 B1
6322889 Lara-Curzio Nov 2001 B1
6979490 Steffier Dec 2005 B2
8617652 Lee Dec 2013 B2
8906814 Lee Dec 2014 B2
9376750 George et al. Jun 2016 B2
9834849 Sammelselg et al. Dec 2017 B2
10092927 George et al. Oct 2018 B2
20040138046 Sherwood, Jr. et al. Jul 2004 A1
20050181192 Steffier Aug 2005 A1
20080119098 Palley et al. May 2008 A1
20090137043 Parsons et al. May 2009 A1
20100130082 Lee May 2010 A1
20100260998 Waicukauski Oct 2010 A1
20110155062 Kato et al. Jun 2011 A1
20120040581 Kim Feb 2012 A1
20130025458 Li et al. Jan 2013 A1
20150291473 Schmidt Oct 2015 A1
20160159694 Chamberlain et al. Jun 2016 A1
20160265143 Garnier Sep 2016 A1
20160326672 Higuchi et al. Nov 2016 A1
20170141383 Dadheech et al. May 2017 A1
20170190629 Lakrout et al. Jul 2017 A1
20170327948 Dadheech et al. Nov 2017 A1
20170342844 Schmidt et al. Nov 2017 A1
20180327327 Suyama et al. Nov 2018 A1
20190322595 Magdefrau et al. Oct 2019 A1
20210039999 Sheedy et al. Feb 2021 A1
20210040651 Sheedy et al. Feb 2021 A1
20210075016 Choi et al. Mar 2021 A1
20230304194 Sheedy et al. Sep 2023 A1
Foreign Referenced Citations (5)
Number Date Country
104213099 Dec 2014 CN
3556740 Oct 2019 EP
2467928 Aug 2010 GB
101855718 May 2018 KR
2013142344 Sep 2013 WO
Non-Patent Literature Citations (18)
Entry
Extended European Search Report for European Application No. 20188050.7; Application Filing Date: Jul. 28, 2020; dated Nov. 5, 2020; 7 pages.
Militzer et al., “Deposition of an organic-inorganic hybrid material onto carbon fibers via the introduction of furfuryl alcohol into the atomic layer deposition process of titania and subsequent pyrolysis”, Journal of Vacuum Science and Technology: Part A, AVS/AIP, vol. 35, No. 1, Nov. 9, 2016, 13 pages.
European Extended Seach Report for European Application No. 20188054.9; Application Filing Date: Jul. 28, 2020; dated Dec. 10, 2020; 9 pages.
Putkonen, et al., “Atomic layer deposition of Ti—Nb—O thin films onto electrospun fibers for fibrous and tubular catalyst support structures”, J. Vac. Scl. Technol. A 36(1), Jan./Feb. 2018, 7 pages.
European Office Action for EP Application No. 20188050.7, dated Feb. 23, 2023, pp. 1-5.
Final Office Action issued in U.S. Appl. No. 16/536,725 dated Mar. 31, 2023, pp. 1-7.
Bernardo et al., Advanced Ceramics from Preceramic Polymers Modified at the Nano-Scale: A Review, Materials, 2014, 30 pages.
U.S. Notice of Allowance for U.S. Appl. No. 16/536,688 dated Aug. 30, 2022, pp. 1-12.
Extended European Search Report issued in Application No. 20190288.9 dated Dec. 10, 2020, 12 pages.
Final Office Action issued in U.S. Appl. No. 16/536,725 dated Jun. 22, 2022, 8 pages.
Kayaci, Fatma et al., “Polymer-Inorganic Core-Shell Nanofibers by Electrospinning and Atomic Layer Desposition: Flexible Nylon Zn0 Core-Shell Nanofiber Mats and Their Photocatalytic Activity”, ACS Publications, Apl. Materials & Interfaces, 2012, pp. 6185-6194.
Non-Final Office Action issued in U.S. Appl. No. 16/536,725 dated Feb. 24, 2022, 29 pages.
Notice of Allowance issued in U.S. Appl. No. 16/536,688 dated Apr. 19, 2022, 9 pages.
Raj N. Singh, “High-Temperature Mechanical Preperties of a Uniaxially Reinforced Zircon-Silicon Carbide Composite”, Journal of the American Ceramic Society, vol. 73, No. 8, Aug. 1990, pp. 2399-2406.
Restriction Requirement issued in U.S. Appl. No. 16/536,725 dated Nov. 26, 2021, 5 pages.
Restriction Requirement issued in U.S. Appl. No. 16/536,688 dated Jun. 16, 2021, 7 pages.
U.S. NonFinal Office Action; U.S. Appl. No. 16/536,688; dated Nov. 8, 2021; 23 Pages.
Non Final Office Action for U.S. Appl. No. 18/083,817; dated Mar. 18, 2024; 7 pages.
Related Publications (1)
Number Date Country
20210039998 A1 Feb 2021 US