The present disclosure relates generally to a two component, curable organosiloxane composition having low viscosity and high temperature resistance.
Small internal combustion engines for use in lawn mowers, leaf blowers, generators, etc. are ubiquitous. These engines typically have a block surrounding and supporting most of the moving engine parts. Other engine parts such as a cylinder, head, cover, intake manifold, exhaust manifold, etc. are attached to the block or each other. A Transmission or other unit can be attached to the engine to provide a powertrain for some applications. Most small internal combustion engines rely on air for cooling rather than fluid. These air cooled engines can run at higher temperatures than liquid cooled engines and the components on air cooled engines can see higher service temperatures than in liquid cooled engines.
Many of the engine, transmission and other powertrain parts having sealing surfaces that are adjacent other sealing surfaces when the parts are assembled. A gasket can be disposed between the sealing surfaces to form a seal there between.
The conventional technology used for gaskets is pre-cut metal and/or fiber gaskets. These conventional gaskets have a number of limitations. All cut gaskets will experience compression set in service. If the compression set becomes too great, the sealing force will be lost and the gasket will leak. Proper performance of a cut gasket relies heavily on correct placement and correct clamp load. This requires a skilled assembler. The unit cost of a cut gasket is usually high. Further, each uniquely shaped sealing surface requires its own unique shaped cut gasket. This requires a manufacturer to maintain a parts inventory of many cut gaskets for each powertrain component, increasing cost.
Replacement of cut gaskets by curable liquid sealants has been tried. These replacement attempts have not always been commercially successful, especially when used in high temperature applications. Selected organosilicone compositions are the only practical sealant chemistry that will survive high engine and powertrain service temperatures without degradation. Some liquid, single component, curable organosiloxane compositions (sometimes referred to as single component RTV cure sealant) require moisture from the environment to cure. Once the sealing surfaces are assembled with sealant there between there may be insufficient moisture for curing. Applying the liquid single component, curable organosiloxane composition, to a powertrain component sealing surface and allowing it to cure before assembling the part to the mating sealing surface is not desirable as it adds excessive time and parts inventory to the assembly process. Further, the cured sealant has the same compression set limitations of the aforementioned cut gaskets.
Some liquid, single component, curable organosiloxane compositions can be cured by heat. A heat cured organosiloxane compositions is not desirable as it requires the manufacturer to purchase, run and maintain ovens and requires an inventory of parts running through the ovens.
A dual component, acetoxy cure organosiloxane composition can be applied in the mixed state, however adhesion to the metallic sealing surfaces is typically less than desired for the application. Further, acetoxy cure organosiloxane compositions form acetic acid on curing. The acetic acid may corrode metals used in the powertrain component.
Curable organosiloxane compositions may be extremely viscous and difficult to apply to a sealing surface. Some curable organosiloxane compositions do not have the desired resistance to oils and fuels used in engines and transmissions.
Thus, there is a need for new curable compositions that can be applied to a powertrain component sealing surface and cured to form a gasket that will retain physical properties after exposure to high service temperatures.
One embodiment of this disclosure describes a two part curable composition comprising organosiloxane polymer; water; crosslinker; catalyst. The curable composition can optionally comprise an organosilane such as hexamethyldisilazane (HMDS) or vinyltrimethoxysilane; adhesion promoter, plasticizer; colorant, filler and/or additives.
One embodiment of this disclosure describes a two part curable composition comprising organosiloxane polymer; water; an organosilane such as hexamethyldisilazane (HMDS) or vinyltrimethoxysilane; filler; crosslinker; adhesion promoter and catalyst. The curable composition can optionally comprise plasticizer; colorant, filler and/or additives.
One embodiment of this disclosure describes a two part curable composition. The first part typically comprises organosiloxane polymer and water. The second part typically comprises crosslinker; adhesion promoter and catalyst. Either or both parts can optionally further comprise an organosilane such as hexamethyldisilazane (HMDS) or vinyltrimethoxysilane, plasticizer, colorant, filler and/or additives.
Cured reaction products of the disclosed two part curable organosiloxane composition have good adhesion to metallic sealing surfaces and good resistance engine oil and other automotive fluids. These cured reaction products can surprisingly retain physical properties after long-term exposure to temperatures between 200° C. and 250° C. and can retain physical properties after exposure to temperatures between 250° C. to 300° C. for short periods (about 100 hours). In some variations the two part curable composition desirably does not emit reaction products that are corrosive to ferrous metallic substrates.
The mixed two part curable organosiloxane composition can have a surprisingly low viscosity and high extrusion rates to allow the mixed composition to be injected into a small cavity.
One embodiment of this disclosure describes the cured reaction products of a two part curable composition comprising organosiloxane polymer; water; an organosilane such as hexamethyldisilazane (HMDS) or vinyltrimethoxysilane; crosslinker; adhesion promoter; catalyst and optionally comprising plasticizer; colorant, filler and/or additives.
One embodiment of this disclosure describes a gasket disposed between sealing surfaces of internal combustion engine or other powertrain component parts wherein the gasket comprises cured reaction products of the above described two part curable composition.
The disclosed compounds include any and all isomers and steroisomers. In general, unless otherwise explicitly stated the disclosed materials and processes may be alternately formulated to comprise, consist of, or consist essentially of, any appropriate components, moieties or steps herein disclosed. The disclosed materials and processes may additionally, or alternatively, be formulated so as to be devoid, or substantially free, of any components, materials, ingredients, adjuvants, moieties, species and steps used in the prior art compositions or that are otherwise not necessary to the achievement of the function and/or objective of the present disclosure.
When the word “about” is used herein it is meant that the amount or condition it modifies can vary some beyond the stated amount so long as the function and/or objective of the disclosure are realized. The skilled artisan understands that there is seldom time to fully explore the extent of any area and expects that the disclosed result might extend, at least somewhat, beyond one or more of the disclosed limits. Later, having the benefit of this disclosure and understanding the concept and embodiments disclosed herein, a person of ordinary skill can, without inventive effort, explore beyond the disclosed limits and, when embodiments are found to be without any unexpected characteristics, those embodiments are within the meaning of the term about as used herein.
As used herein for each of the various embodiments, the following definitions apply:
Unless otherwise specifically defined, “aliphatic” means saturated or unsaturated, straight, branched or cyclic hydrocarbon groups.
Unless otherwise specifically defined, “alkoxy” refers to the general formula —O— alkyl.
Unless otherwise specifically defined, “alkyl” refers to a linear, branched or cyclic saturated organic group having from 1 to about 9 carbon atoms including, for example, methyl, ethyl, propyl, butyl, hexyl, octyl, isopropyl, isobutyl, tert-butyl, cyclopropyl, cyclohexyl, cyclooctyl, vinyl and allyl. Unless otherwise specifically defined, an alkyl group can be substituted or unsubstituted. Unless otherwise specifically limited, a cyclic alkyl group includes monocyclic, bicyclic and polycyclic rings, for example norbornyl, adamantyl and related terpenes.
Unless otherwise specifically defined, an aromatic ring is an unsaturated ring structure having about 5 to about 6 ring members and including only carbon as ring atoms. Unless otherwise specifically defined, an aromatic ring can be substituted or unsubstituted.
Unless otherwise specifically defined, “aromatic” or “aryl” refers to cyclic conjugated hydrocarbon structures (CI-12) that include only carbon as ring atoms and which may optionally be substituted or unsubstituted, for example phenyl, biphenyl or naphthyl.
Unless otherwise specifically defined, “hal”, “halo” and “halogen” refer to an atom selected from fluorine, chlorine, bromine and iodine.
Unless otherwise specifically defined, the term “oligomer” means a defined, small number of repeating monomer units such as 10-25,000 units, and desirably 10-100 units which have been polymerized to form a molecule, and is a subset of the term polymer.
Unless otherwise specifically defined, the term “polymer” refers to any polymerized product greater in chain length and molecular weight than an oligomer, i.e. a degree of polymerization greater than 25,000.
Unless otherwise specifically defined, room temperature is about 23-25° C. and room humidity is about 50% relative humidity.
Unless otherwise specifically limited the term substituted means substituted by at least one below described substituent group in any possible position or positions. Substituent groups for the above moieties useful in the disclosed compounds are those groups that do not significantly diminish the activity of the disclosed compound, for example, H, halogen, N3, NCS, CN, NO2, NX1X2, OX3, C(X4)3, OAc, O-acyl, O-aroyl, NH-acyl, NH-aroyl, NHCOalkyl, CHO, C(halogen)3, COOX4, SO3H, PO3H2, SO2NX1X2, CONX1X2, C(O)CF3, alkyl, alcohol, alkoxy, alkylmercapto, alkylamino, di-alkylamino, aryl, alkaryl, sulfonamide or thioalkoxy wherein X1 and X2 each independently comprise H or alkyl, or X1 and X2 together comprise part of a heterocyclic ring having about 4 to about 7 ring members and optionally one additional heteroatom selected from O, N or S, or X1 and X2 together comprise part of an imide ring having about 5 to about 6 members and X4 comprises H, alkyl, loweralkylhydroxy, or alkyl-NX1X2. Unless otherwise specifically limited, a substituent group may be in any possible position or any possible positions if multiply substituted.
Unless otherwise specifically defined, the term “two part composition” or “2K composition” means a composition having two parts (A and B) each of which are intended to be stored separately until use and which react when combined together.
The disclosed curable organosiloxane composition is a two component composition. A two component composition has two components each of which is separately stable, but which upon mixing begin to cure and gel in about 5 minutes and fully cure in 24 to 168 hours at room temperature and humidity to produce a reaction product having desired properties.
The disclosed curable organosiloxane composition comprises organosiloxane polymer; water; crosslinker; catalyst. The curable composition can optionally comprise one or more of an organosilane such as hexamethyldisilazane (HMDS) or vinyltrimethoxysilane; adhesion promoter, plasticizer; colorant, filler and/or additives in either part.
The organosiloxane polymer can be any hydroxyl terminated polydimethyl siloxane (PDMS) such as a liquid hydroxy terminated compound of the formula
where n is an integer of 2 or more. Suitable hydroxyl terminated polydimethyl siloxane compounds have a viscosity at 25° C. of about 100 cP to about 100,000 cP, preferably about 750 cP to about 20,000 cP. Some useful organosilicone polymers are sold under the Masil® name by Emerald Performance Materials.
The plasticizer is an organosiloxane material that does not react with the other components of the composition but in which the other components can be carried. Useful plasticizers include inert silicone fluids such as polydimethylsiloxane. Desirably the plasticizer has a viscosity in the range of about 50-100,000 cP. Useful polydimethylsiloxane plasticizers are sold by Xiameter and Dow Corning Corporation.
The filler is typically in the physical form of a fiber, flake or powder. Typical filler size is about 1 to about 30 microns d50 particle size distribution. Some useful fillers include, for example, lithopone; zirconium silicate; Cristabolite; Cristabolite that has been surface treated such as with silane, epoxysilane, methacrylsilane, trimethylsilane, methylsilane or silazane; quartz; hydroxides such as calcium, aluminum, magnesium and iron hydroxide; diatomaceous earth; carbonates such as sodium, potassium, calcium, and magnesium carbonates; ceramic oxides and metal oxides such as iron, zinc, magnesium, chromic, cerium, zirconium and aluminum oxides; clay; fumed silica; precipitated silica; silica that has been surface treated with a silane or silazane such as the AEROSIL products available from Evonik Industries; silica that has been surface treated with an acrylate or methacrylate such as AEROSIL R7200 or R711 available from Evonik Industries; graphite; metal powder such as copper powder; synthetic fibers; and mixtures thereof. When used filler can be employed in concentrations effective to provide desired physical properties in the uncured composition and cured reaction products. A combination of fumed silica, precipitated silica, carbon black, copper powder and Cristabolite is preferred as compositions using this mixture retain their physical properties surprisingly well after exposure to high temperatures over long periods of time. Fillers such as calcium carbonate and ATH are not desirable as compositions using these fillers may not retain properties after exposure to high temperatures.
The water can help to promote curing through thick sections of the mixed composition. The water may be present as a liquid or in the form of a moisture containing filler or both. Advantageously, the water is included in the form of a moisture-containing filler. One useful water-containing filler is precipitated silica.
The crosslinker in the disclosed composition can be any compound that will react with the organosiloxane polymer to provide the desired property retention after high temperature exposure. Known crosslinkers for use with organosiloxane polymers include acetoxy compounds, oxime compounds, alkoxy compounds, benzamide compounds, amine compounds and aminoxy compounds. Some exemplary oxime containing organosiloxanes include those containing 2-butanone oxime, i.e. methyl ethyl ketoxime (MEKO) groups such as described in U.S. Pat. No. 3,189,576; organosiloxanes which contain both 2-butanone groups and alkoxy groups; organosiloxanes containing acetone oxime i.e. propanone oxime groups; organosiloxanes containing methyl isobutylketoxime groups; organosiloxanes containing bis-, tris-, or tetrakis-methyl isopropyl ketoxime (MIPKO) or methyl propyl ketoxime (MPKO) groups and acetonoximo.
Advantageously, the crosslinker is one or more alkoxy containing organosiloxane compounds and/or one or more oxime containing organosiloxane compounds. Preferable the crosslinker is an oxime containing organosiloxane compound. Curable compositions using oxime crosslinkers do not emit corrosive byproducts and have desirable temperature resistance, oil and fluid resistance and high adhesion.
The adhesion promoter is a compound that helps promote adhesion of the cured composition to a surface. Useful adhesion promoters can be aminosilane compounds such as, but are not limited to, silane compounds containing amino-alkyl groups, such as gamma-ureidopropyltrimethoxy silane, 3-aminopropyl trimethoxysilane, N,N′-bis(3-trimethoxy silylpropyl)urea, gamma-aminopropyltrimethoxysilane, N-(2-aminoethyl)-3-aminopropyltriethoxysilane, N-(2-aminoethyl)-3-aminopropyltrimethoxysilane, timethoxysilylpropyldiethylene triamine, tertiary alkyl carbamate silane, and aminoethyl-3-aminopropyl-methyl-dimethylsilane. Other desirable amino-containing silane compounds include silane compounds containing amino-cycloaliphatic groups such as methyl tris (cyclohexylamino)silane and silane compounds containing amino-aromatic groups such as methyl tris-(N-methylbenzamido)silane. Some examples of commercially available adhesion promoters include octyl trimethoxysilane (commercially available from Witco Corporation, Greenwich, Conn. under the trade designation A-137), glycidyl trimethoxysilane (commercially available from Witco under the trade designation A-187), methacryloxypropyl trimethoxysilane (commercially available from Witco under the trade designation of A-174), vinyl trimethoxysilane, tetraethoxysilane and its partial condensation products.
The catalyst promotes reaction of the mixed parts. Some exemplary catalysts include an organometallic compound including metals such as titanium, tin, or zirconium. Illustrative examples of the organotitanium compounds include tetraisopropoxy titanate and tetrabutoxy titanate. Illustrative examples of the organotin compounds include dibutyltin dilaurate, dibutyltin diacetate, dibutyltin dioctoate, dimethyltin carboxylate and dioctyltin carboxylate. Illustrative examples of the organozirconium compounds includes zirconium octanoate. Effective amounts of organometallic catalysts are those that will facilitate cure of the mixed composition.
The disclosed composition can optionally include one or more additives so long as they do not inhibit the curing mechanism or intended use. Exemplary additives include one or more of plasticizer, colorant, filler, antioxidant, heat stabilizer, moisture scavenger, inhibitor, odor mask, and the like.
The colorant can be a pigment or dye to provide a desired color beneficial to the intended application. Exemplary colorants include titanium dioxide, carbon black, C.I. Pigment Blue 28, C.I. Pigment Yellow 53 and phthalocyanine blue BN. In some applications the colorant can be, or include, a fluorescent dye to allow inspection of the applied composition under UV radiation. The coloring agent will be present in amounts sufficient to allow for desired coloration or detection.
The two component organosiloxane composition comprises a Part A and a Part B that are stored separately until just before use. Mixing the two parts initiates a reaction, with the mixture gelling in about 5 minutes and fully curing in 24 to 168 hours at room temperature to produce a reaction product. Part A typically comprises organosiloxane polymer and water. Part A can also include filler if the water is in the form of a water containing filler. Part A can optionally contain an organosilane such as hexamethyldisilazane (HMDS) or vinyltrimethoxysilane; plasticizer; one or more additional fillers; and one or more additives.
Part B typically comprises an organosilane such as hexamethyldisilazane (HMDS) or vinyltrimethoxysilane; crosslinker; adhesion promoter and catalyst. Part B can optionally comprise plasticizer; one or more fillers; and one or more additives.
Each of the two-parts (A and B) remain shelf stable for until such time as they are combined together and permitted to react. The components can be mixed at A:B ratios of 10:1 to 2:1 and typically at 4:1.
The disclosed curable compositions when mixed can have a viscosity below 200,000 cP. The disclosed curable compositions when mixed can advantageously have a viscosity in the range of about 30,000 cP to about 100,000 cP. The disclosed curable compositions when mixed can typically have a viscosity in the range of about 40,000 cP to about 50,000 cP. Viscosity can be measured at 10 s−1 with 25 mm/2 deg cone, using Physica model MCR 301 rheometer.
These low viscosities allow the mixed composition to be injected into small cavities at high extrusion rates. The disclosed curable compositions when mixed can have an extrusion rate greater than 100 grams/minute (g/min). The disclosed curable compositions when mixed can advantageously have an extrusion rate in the range of about 100 to about 200 g/min. The disclosed curable compositions when mixed can typically have an extrusion rate in the range of about 150 to about 200 g/min. This is surprisingly higher than extrusion rates of about 50 grams/minute seen for other high temperature resistant compositions. Extrusion rate can found by measuring the amount of composition per minute extruded at 6 bar through a Quadro MFQX 10.7-24 static mixer from Sulzer Mixpac USA.
The disclosed curable compositions when mixed can be used in a variety of application areas where the cured composition must retain a mix of properties, such as tensile strength and elongation and hardness and lap shear strength after exposure to temperatures of 250° C. for long periods, such as up to 42 days or more, and exposures to 300° C. for short periods, such as up to 3 days or more, are desired. In some desirable embodiments cured reaction products of the mixed curable compositions can retain 70% to 120% of their cured tensile strength and elongation and hardness and lap shear strength properties after exposure to temperatures of 250° C. for up to 42 days. In some desirable embodiments cured reaction products of the mixed curable compositions can retain 80% to 110% of their cured tensile strength and elongation and hardness and lap shear strength properties after exposure to temperatures of 250° C. for up to 42 days. In some desirable embodiments cured reaction products of the mixed curable compositions can retain 50% to 130% of their cured tensile strength and elongation and hardness and lap shear strength properties after exposure to temperatures of 300° C. for periods of up to 3 days.
Some exemplary compositions for part A are provided below. The wt. % of all components in Part A will equal 100 wt. %.
Some exemplary compositions for part B are provided below. The wt. % of all components in Part B will equal 100 wt. %.
The following examples are included for purposes of illustration so that the disclosure may be more readily understood and are in no way intended to limit the scope of the disclosure unless otherwise specifically indicated.
The following tests were used in the Examples.
Tensile strength was tested according to ISO 37.
Elongation was tested according to ISO 37.
Shore hardness was tested according to ASTM D2240.
Lap shear strength was tested according to ASTM D1002.
Extrusion rate was measured by extruding the test composition at 6 bar through a Quadro MFQX 10.7-24 static mixer from Sulzer Mixpac USA.
Viscosity was measured at 10 s−1 with 25 mm/2 deg cone, using Physica model MCR 301 rheometer.
The following materials were used in the Examples.
AMMO is an aminosilane adhesion promoter available from Evonik Industries AG, Germany.
Aerosil R8200 is a surface treated fumed silica available from Evonik Industries AG, Germany.
Black iron oxide Fe3O4, 99.5% purity, <45 microns.
Copper powder, >99% purity, <45 microns.
LM400 is an oxime crosslinker available from Rheinmetall Nitrochemie, Germany.
Fumed silica is available as Aerosil from Evonik Industries AG, Germany.
Hexamethyldisilazane.
Hydroxy terminated PDMS, 6,000 cP.
Plasticizer is methyl terminated PDMS, 1,000 cP.
Carbon black filler, 23 micron average particle size, 150 M2/gram surface area.
Quartz filler, 96.3% purity, <5 microns.
Silbond 8000TST is a surface treated Cristabolite powder available from Qwarzwerke Gruppe, Germany.
Surface treated fumed silica is available as Aerosil from Evonik Industries AG, Germany.
UL 38 is a dioctyltin carboxylate based catalyst available from Momentive Performance Materials, Inc.
Zeothix 95 is a precipitated silica available from J.M. Huber Corporation.
1hydroxy terminated PDMS.
2Silbond 8000TST.
3Zeothix 95.
Example 1-A was made as follows. Add Cristobalite powder, colorant, hexamethyldisilazane and most of the organosiloxane polymer to a mixer. Mix these ingredients at high speed and heat to 100° C. for 30 min. While heating vacuum strip for 30 min. Cool to room temperature. Add the remaining ingredients and mix for 30 minutes with vacuum while keeping the batch temperature below 50° C. The final Part A composition had a viscosity of about 40,000-50,000 cP.
1methyl terminated PDMS.
2Aerosil R8200.
3Silbond 8000TST.
4LM400
5AMMO
6UL 38.
Example 1-B was made as follows. Add plasticizer, Cristobalite powder, and fumed silica to a mixer. Mix at high speed and heat to 100° C. for 30 min with vacuum. Cool to room temperature. Add oxime crosslinker and mix for 5 minutes with vacuum. Add adhesion promoter and mix for 5 minutes with vacuum. Add catalyst and mix 5 minutes with vacuum. Add hexamethyldisilazane and mix 5 minutes with vacuum. The final Part B composition had a viscosity of about 40,000-50,000 cP.
The two parts are mixed at a ratio of 4:1 by volume (i.e. 4 parts 1-A:1 part 1-B). The uncured mixture had a viscosity of 40,000 to 50,000 cP. The uncured mixture had an extrusion rate of 190 grams/minute. After 1 week at 25° C./50% R.H. the cured properties of the resulting reaction products are:
1AD-14 strips from Q-panel.
The two parts are mixed at a ratio of 4:1 by volume (i.e. 4 parts 1-A:1 part 1-B). After 1 week at 25° C./50% R.H. followed by 6 weeks at 250° C. the cured properties of the resulting reaction products are:
1AD-14 strips from Q-panel.
The two parts are mixed at a ratio of 4:1 by volume (i.e. 4 parts 1-A:1 part 1-B). After 1 week at 25° C./50% R.H. followed by 3 Days at 300° C. the cured properties of the resulting reaction products are:
1AD-14 strips from Q-panel.
1hydroxy terminated PDMS.
2Aerosil R8200.
3Zeothix 95.
Example 2-A was made as follows. Add fumed silica, iron oxide powder, colorant, hexamethyldisilazane and most of the organosiloxane polymer to a mixer. Mix these ingredients at high speed and heat to 100° C. for 30 min. While heating vacuum strip for 30 min. Cool to room temperature. Add the remaining ingredients and mix for 30 minutes with vacuum while keeping the batch temperature below 50° C. The final Part A composition had a viscosity of about 45,000-55,000 cP.
1methyl terminated PDMS.
2Aerosil R8200.
3LM400
4AMMO.
5UL 38.
Example 2-B was made as follows. Add plasticizer, quartz filler, and fumed silica to a mixer. Mix at high speed and heat to 100° C. for 30 min with vacuum. Cool to room temperature. Add oxime crosslinker and mix for 5 minutes with vacuum. Add adhesion promoter and mix for 5 minutes with vacuum. Add catalyst and mix 5 minutes with vacuum. Add hexamethyldisilazane and mix 5 minutes with vacuum. The final Part B composition had a viscosity of about 45,000-55,000 cP.
The two parts are mixed at a ratio of 4:1 by volume (i.e. 4 parts 2-A:1 part 2-B). The uncured mixture had a viscosity of 45,000-55,000 cP. The uncured mixture had an extrusion rate of 190 grams/minute. After 1 week at 25° C./50% R.H. the cured properties of the resulting reaction products are:
1AD-14 strips from Q-panel.
The two parts are mixed at a ratio of 4:1 by volume (i.e. 4 parts 2-A:1 part 2-B). After 1 week at 25° C./50% R.H. followed by 6 weeks at 250° C. the cured properties of the resulting reaction products are:
1AD-14 strips from Q-panel.
The two parts are mixed at a ratio of 4:1 by volume (i.e. 4 parts 2-A:1 part 2-B). After 1 week at 25° C./50% R.H. followed by 3 days at 300° C. the cured properties of the resulting reaction products are:
1AD-14 strips from Q-panel.
As shown in the following Table, cured reaction products of the disclosed compositions retain their mix of properties better than some other commercial products after exposure to temperatures of 250° C. for 42 days.
1Loctite 5920 Ultra Copper RTV silicone available from Henkel Corporation.
2Loctite 59675 Red High Temperature RTV silicone available from Henkel Corporation.
3Loctite 5612 high temperature RTV silicone available from Henkel Corporation.
4CAF 99 Black from Blue Star
As shown in the following Table, cured reaction products of the disclosed compositions retain their mix of properties better than some other commercial products after exposure to temperatures of 300° C. for 3 days.
1Loctite 5920 Ultra Copper RTV silicone available from Henkel Corporation.
2Loctite 59675 Red High Temperature RTV silicone available from Henkel Corporation.
3Loctite 5612 high temperature RTV silicone available from Henkel Corporation.
The proceeding description is meant to be exemplary and it is to be understood that variations and modifications may be employed without departing from the concept and intent of the invention as defined in the following claims.
| Number | Date | Country | |
|---|---|---|---|
| 62189251 | Jul 2015 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/US2016/036127 | Jun 2016 | US |
| Child | 15862939 | US |