The present invention relates to a high temperature superconductive Josephson tunnel junction. More particularly, the invention relates to a high temperature superconductive Josephson tunnel junction of which a plasma frequency varies depending on an intersecting angle.
A Josephson tunnel junction device using a superconductor (SIS-JJ device) is a basic superconductive device and it has been applied as a high frequency device, an SFQ device (a switching device utilizing flux of line of magnetic force), a SQUID magnetic sensor device and others. Further enhancement of performance is expected if the Josephson tunnel junction device can be made of a high temperature superconductor.
The inventors of the present application have already proposed formation of a Josephson junction in or near a bond of whisker crystals by intersecting whisker crystals of a high temperature superconductor and by heat treatment as a means of solving a technical problem of easily and quickly forming a Josephson junction having an excellent properties without requiring any expensive fine processing equipment (Japanese Patent Application No. 2000-250269). This application has not laid open at present, but it specifically proposes that a Josephson junction is formed by disposing two whisker crystals of a bismuth 2212 high temperature superconductor in a cross on an MgO substrate and putting the MgO substrate in a furnace for heat treatment in a baking condition of temperature of 850° C., oxygen partial pressure of 70% and baking time of 30 minutes.
The present invention is further advanced from the technology of the previous proposal and it is intended to provide a high temperature superconductive Josephson tunnel junction of which a plasma frequency varies depending on an intersecting angle, as a leading technology for creating a high temperature superconductive Josephson tunnel junction device capable of controlling properties.
To solve the problems aforementioned, the present invention provides a high temperature superconductive Josephson junction, wherein two single crystals of a high temperature superconductor are bonded on a substrate in a range of intersecting angles of 0 degree to 90 degrees, a single high temperature superconductive Josephson tunnel junction is formed in a bonded portion, and a plasma frequency of the high temperature superconductive Josephson tunnel junction varies depending on an intersecting angle (claim 1).
In the invention, preferably, the two single crystals are any one of a whisker, a finely processed single crystal and a thin film, or a combination of two types of them (claim 2), and the high temperature superconductor is a bismuth compound and its superconductive phase is any one of 2212 phase, 2201 phase and 2223 phase, or a combination of two or more types of them (claim 3).
A high temperature superconductive Josephson tunnel junction of the invention is specifically described below with examples.
A high temperature superconductive Josephson tunnel junction of the present invention is, as described above, a single high temperature superconductive Josephson tunnel junction formed in a bonded portion where two single crystals of a high temperature superconductor is bonded on a substrate in a range of intersecting angles of 0 degree to 90 degrees.
In a Josephson tunnel junction, a thin insulator layer is sandwiched between superconductors and the insulator layer is formed at an interface of two crystals. Therefore, in the high temperature superconductive Josephson tunnel junction of the invention, use of two single crystals, in one aspect, is for formation of an appropriate insulator layer at an interface. That is, a single Josephson tunnel junction is formed because the insulator layer formed at the interface of two single crystals is used. Unlike a polycrystal, a single crystal is uniform in an azimuth of a crystal. Therefore, as described below, in other aspect, the use of two single crystals is for controlling a plasma frequency fp of a high temperature Josephson tunnel junction by varying a critical electric current density based on an intersecting angle of the two single crystals.
In the high temperature superconductive Josephson tunnel junction of the invention, as described above, an intersecting angle of two high temperature superconductor single crystals bonded on the substrate, that is, an angle not larger of two angles formed by two intersecting bismuth high temperature superconductor single crystals, is in a range of 0 degree to 90 degrees. A plasma frequency fp of the high temperature superconductive Josephson tunnel junction which intersects and is bonded in the range varies because a critical current density Jc changes depending on an intersecting angle. In other words, in the high temperature superconductive Josephson tunnel junction of the invention, a plasma frequency fp varies depending on an intersecting angle and therefore the plasma frequency fp can be controlled by varying an intersecting angle of two high temperature superconductor single crystals to be bonded on the substrate.
The plasma frequency peculiar to a high temperature superconductor generally ranges from hundreds of GHz to several THz and hence a high temperature superconductive Josephson tunnel device using a high temperature superconductor can respond to higher frequencies, but could not respond to lower frequencies. However, by the high temperature superconductive Josephson tunnel junction of the invention, a plasma frequency fp can be changed in a range of two or three digits or more from a general plasma frequency peculiar to a high temperature superconductor to several GHz. As shown in examples, high frequency response (Shapiro steps) is observed, for example, at 20 GHz, which has been impossible to respond to. Theoretically, it is expected to respond to lower frequencies.
Generally, in a high temperature superconductive Josephson tunnel junction, as compared with a high temperature superconduction proximity effect device, IcRn (a product of a critical current density and a shunt resistance, a value representing a signal processing capacity of a Josephson junction) is large. When a high temperature superconductive Josephson tunnel junction device utilizing the high temperature superconductive Josephson tunnel junction of the invention is applied, for example, to a magnetic sensor, since a SQUID output is in proportion to the IcRn, the SQUID output increases, it is considered that the output/input ratio, that is, sensitivity is enhanced. Moreover, in a high temperature superconductive Josephson tunnel junction device, since a respondable maximum operating frequency fmax is also in proportion to the IcRn, as the IcRn increases, the fmax is considered to be higher. When a high temperature superconductive Josephson tunnel junction device utilizing the high temperature superconductive Josephson tunnel junction of the invention is applied, for example, to a high frequency receiver, a receiver enhanced in a frequency property from fp to fmax will be possible. When applied to an SFQ device, a fast device operating at switching time τ=1/fmax is obtained and it is expected that a quantum computer using a SIS (superconductor/insulator/superconductor) junction may be produced.
When forming the high temperature superconductive Josephson tunnel junction of the invention, two single crystals of a high temperature superconductor are disposed on a substrate at an intersecting angle in a range of 0 degree to 90 degrees and the two single crystals are bonded by heat treatment as is similar to the previous proposal. A condition of heat treatment is temperature ranging from 0 degree to a melting point of a high temperature superconductor and an oxygen partial pressure ranging from 0 to 100%. Bonding faces of the two high temperature superconductor single crystals are any one of face a, face b and face c, or a combination of two faces of them. The two thin high temperature superconductor single crystals are any one of a whisker, a finely processed single crystal and a thin film, or a combination of two types of them.
A high temperature superconductor used in the high temperature superconductive Josephson tunnel junction of the invention is not particularly specified in a material classification and may be properly selected from various materials generally regarded as a high temperature superconductor. In the examples, described below, a bismuth high temperature superconductor is selected and a superconductive phase in this case is any one of 2212 phase, 2201 phase and 2223 phase, or a combination of two or more types of them. A high temperature superconductor may be properly adjusted in composition, by adding elements or replacing elements, as far as a superconductive property may not be spoiled.
Two whisker single crystals of 2212 phase of bismuth high temperature superconductor were disposed on an MgO substrate by intersecting in a range of 0 degree to 90 degrees, were put in an electric furnace to heat in a condition of temperature of 850 degrees and oxygen partial pressure of 70%, and were bonded together mutually on face c.
With respect to a high temperature superconductive Josephson tunnel junction thus obtained, critical current densities Jc were measured and from a change of the measured Jc, a change of plasma frequency fp of the high temperature superconductive Josephson tunnel junction depending on intersecting angles α was estimated. The result is shown in a graph in
As understood from a graph in
On the basis of these findings, a high frequency of 20 GHz was emitted to the high temperature superconductive Josephson tunnel junction obtained. As a result, as shown in
Further, with respect to the high temperature superconductive Josephson tunnel junction, changes of a critical current Ic were investigated by applying a magnetic field. The result is shown in a graph in
A critical current density is determined by dividing a current value before standardization by area and it is a value proportional to the axis of ordinates in the graph in
Two whisker single crystals of 2212 phase of bismuth high temperature superconductor were disposed on an MgO substrate by intersecting at an intersecting angle of 90 degrees and put in an electric furnace to heat in a condition of temperature of 850 degrees and oxygen partial pressure of 70%. Face b and face c were bonded.
The present invention is not limited to the examples alone, but may be variously modified in a type of a high temperature superconductor, a shape of a single crystal, a condition of heat treatment and other details.
As described specifically above, according to the invention, a high temperature superconductive Josephson tunnel junction of which plasma frequency varies depending on the intersecting angle is realized.
Number | Date | Country | Kind |
---|---|---|---|
2002-275873 | Sep 2002 | JP | national |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/JP03/11912 | 9/18/2003 | WO | 3/17/2005 |