Patent Application
20070116860
The present invention relates to an apparatus and method for forming a high-temperature superconducting film on a long tape substrate at speeds suitable for large-scale production, includes a spooling system for use in a high-throughput, continuous pulsed laser deposition (PLD) process.
In the past three decades, electricity has risen from 25% to 40% of end-use energy consumption in the United States. With this rising demand for power comes an increasingly critical requirement for highly reliable, high quality power. As power demands continue to grow, older urban electric power systems in particular are being pushed to the limit of performance, requiring new solutions.
Wire forms the basic building block of the world's electric power system, including transformers, transmission and distribution systems, and motors. The discovery of revolutionary high-temperature superconductor (HTS) compounds in 1986 led to the development of a radically new type of wire for the power industry; this discovery is the most fundamental advance in wire teleology in more than a century.
HTS wire offers best-in-class performance, carrying over one hundred times more current than do conventional copper and aluminum conductors of the same physical dimension. The superior power density of HTS wire will enable a new generation of power industry technologies. It offers major size, weight, and efficiency benefits. HTS technologies will drive down costs and increase the capacity and reliability of electric power systems in a variety of ways. For example, HTS wire is capable of transmitting two to five times more power through existing rights of way.
This new cable will offer a powerful tool to improve the performance of power grids while reducing their environmental footprints. However, to date only short lengths of coated conductor wire samples have been fabricated at high performance levels with any of the conventional fabrication processes.
In order for HTS technology to become commercially viable for use in the power generation and distribution industry, it will be necessary to develop techniques for continuous, high-throughput production of HTS tape. Several challenges must be overcome in order to enable the cost-effective production of long lengths (i.e., several kilometers) of HTS-coated conductor wire.
Vapor deposition is a process for manufacturing HTS tape in which vapors of superconducting material such as YBCO are deposited on a tape-like length of buffered metal substrate, thereby forming an HTS coating on the tape substrate. Well-known vapor deposition processes include physical vapor deposition (PVD), chemical vapor deposition (CVD)), and pulsed laser deposition (PLD). PLD has shown great promise for the deposition of superconducting thin films, due in large part to its operational simplicity, its flexibility in vacuum requirements, and the congruent, stoichiometric transfer of material that results from the generation of a highly forward-directed plume from target to substrate.
In a pulsed laser deposition (PLD) process in which a laser is used to evaporate a material, where atoms of the material subsequently coat a surface that is exposed to the evaporated material, thereby forming a film on that surface. PLD is a process suitable for manufacturing HTS wires with high current-carrying capacity In this case, a target comprising a stoichiometric chemical composition of the desired layer is ablated by a pulsing laser, forming a plume of ablated material to which a buffered substrate is exposed, thereby coating the buffered substrate with the desired material and forming a coated wire or tape. Using a PLD process it is possible to deposit a superconducting layer atop a translating flexible buffered polycrystalline metal tape in a continuous, assembly line manufacturing process. However, to date only short lengths of coated conductor wire samples have been fabricated at high performance levels using prior art vapor deposition processes and equipment.
The manufacture of long lengths of HTS tapes via a PLD process necessitates a system that provides for the translation of the tapes through a deposition chamber where they receive the desired thin film coating. Youm, U.S. Pat. No. 6,147,033, dated Nov. 14, 2000, and entitled “Apparatus And Method For Forming A Film On A Tape Substrate,” provides a tape transport system particularly well suited for translating a substrate tape through a deposition chamber.
As described by Youm, the superconducting film is deposited on the tape substrate wound around a cylindrical substrate holder inserted in an auxiliary chamber housed completely within a main deposition chamber. The cylindrical substrate holder rotates during the whole deposition process. Vapors of film materials are supplied form the main chamber through an opening between the two chambers. According to Youm, it is possible to form HTS film rapidly onto a tape substrate having a length up to 300 meters. While this represents a step toward the large-scale production of HTS coated tape, it is limited in its scalability. To achieve significantly longer lengths of HTS coated tape the cylindrical substrate holder must increase in size accordingly, making it impractical to be housed within the main vapor deposition chamber. Thus, a drawback of the vapor deposition process described in Youm is that the system is not easily scalable to produce long lengths (e.g., several kilometers) of HTS coated tape and is therefore not suited for the large-scale production of HTS coated wire.
Several other challenges must be overcome in order to enable the cost-effective production of long lengths (i.e., several kilometers) of HTS coated conductor wire.
A first challenge to the continuous deposition of HTS tapes utilizing a reel-to-reel tape transport system that is not overcome by Youm is the maintenance optimum tape tension throughout the extended deposition runs necessary to high-throughput systems. If the correct level of tautness is not maintained, the tape sags. This results in a variation in the target-to-substrate distance and a compromise of the thin film uniformity.
A second technical challenge to the continuous deposition of HTS tapes utilizing a reel-to-reel tape transport system that is not overcome by Youm is the maintenance of the tape at the optimal speed throughout extended deposition runs. As the spools rotate and the tape is translated through a chamber, the tape must remain at the same position within the deposition zone, regardless of the radii of tape housed on each spool. Lateral, as well as longitudinal, movement of the tape results in an inconsistent and non-uniform deposition resulting in variations in film thickness. The importance of film uniformity cannot be an overemphasized: if there is an insufficient superconducting quality at a single point over the entire length of a few hundred meters of tape, the current carrying capacity of the entire length of tape is compromised. Further, any elements that serve to position the tape must do so in such a way as to not induce stress or strain in the tape, which may damage the delicate thin films
Another technical challenge not overcome by Youm is how to wind the tape onto a spool subsequent to its undergoing the deposition process without damaging the delicate thin film housed thereon. The ceramic grains of superconducting films may fracture if bent beyond a certain strain, which may result in a decrease in the critical current-carrying capacity of the finished superconductor tape.
To achieve the proper bonding of the evaporated material to the substrate during a typical PVD, CVD, or PLD process it is necessary to heat the substrate. Thus, a substrate heater that is capable of sustaining the substrate at a process temperature ranging typically from 500 to 1500° C. is required Current PVD, CVD, or PLD processes typically employ a stationary substrate mounted on a stationary substrate holder, where the substrate holder incorporates a heating element. Since the substrate is in direct contact with the heated substrate holder, heating of the substrate takes place by conduction.
An example of a conventional stationary substrate heater is disclosed in Chen et al., U.S. Pat. No. 6,066,836, dated May 23, 2000 and entitled “High temperature resistive heater for a process chamber”. Chen et al. describes a structure for a processing apparatus such as a chemical vapor deposition chamber that includes a resistively heated substrate holder including a support surface that includes an additional resistive heating element. The heated substrate holder is disk-shaped to accommodate a substrate, such as a wafer, in a semiconductor application. Chen's substrate heater includes a heating element that provides a single heating zone, that is, one uniform temperature is maintained across the entire substrate
However, in the case of a continuously translating substrate as is necessary for a continuous flow manufacturing process, it is difficult to maintain a uniform temperature profile using resistive heaters as disclosed by the prior art, Any local loss of contact with the heating element by a rapidly moving substrate can cause large temperature variations and in turn inhomogeneities in the coating film. Consequently, a technical challenge to overcome is how to heat a rapidly moving substrate in a continuous flow high-throughput manufacturing process for producing long lengths of HTS-coated wire.
In the case of a translating substrate in a continuous flow manufacturing process, multiple temperature zones having different temperature requirements, such as a preheating zone, a deposition zone, and a cooling zone, are desirable. Current substrate heaters do not provide multiple heating zones with differing temperature ranges as required for continuous flow manufacturing of HTS-coated wire and thus are not suited for use in the large-scale production of HTS-coated wire,
In the PLD process, a film is deposited on a substrate by the action of a laser beam impinging on a target material that is located in close proximity to the substrate, thereby creating a plume of ablated material (plasma) to which the substrate is exposed. Conventional PLD systems utilize a single laser beam that impinges on a target mounted on a target manipulator. The target manipulator provides an appropriate target rotation and oscillation. In a particular well-known example, multi-target manipulators may hold multiple targets for sequential use in a PLD process. In this case, as the material of any given target is consumed during the PLD process, the multi-target manipulator indexes from one target to the next. However, in the large-scale continuous production of HTS-coated wire, a multi-laser beam PLD process, in which multiple laser beams impinge on multiple targets simultaneously, may be used, thereby simultaneously creating multiple overlapping plumes to which a translating substrate is exposed. In this way, the deposition region is expanded in length, thereby improving the overall throughput of the PLD process compared with a single laser/single target PLD process. Conventional target manipulators are therefore of limited use in a multilaser beam PLD application.
An example of a conventional target manipulator is described in Kim et al., U.S. Pat. No. 5,942,040, entitled “Multi-Target Manipulator For Pulsed Laser Deposition Apparatus.” Kim et al.discloses a multi-target manipulator for a pulsed laser deposition apparatus, including a driving mechanism that includes a stepping motor and a motion feed for providing rotation to the target disk driving shaft and the target driving motor shaft. The driving mechanism further includes a driving transmission and head-supporting member that transmits a rotational motion for rotating the target disk and the target so as to locate a target material on the focal point of the laser beam.
Although Kim et al provides a mulfi-target manipulator, the multiple targets are arranged on a circular disk with the intent of being indexed from one to another for consumption one at a time. Although it is conceivable that multiple lasers could be focused on all targets simultaneously, it is not practical for a continuous flow application in which a substrate tape is translating in a straight line, thereby requiring the targets to be arranged in a straight line. A further limitation is that Kim et al.'s the multi-target manipulator provides rotation to only one target at a time. This type of multi-target manipulator is therefore not suited for use in the large-scale production of HTS-coated wire utilizing a continuously translating substrate through a deposition chamber.
It is conceivable that several target manipulators, such as Kim et al.'s multi-target manipulator, could be used in combination with multiple laser beams arranged sequentially in a straight line along the path of the translating substrate tape. However, using such an arrangement of several conventional target manipulators in a multi-laser beam PLD system is very costly and therefore not practical. Also, conventional target manipulators occupy lot of space and as a result, there will be large gaps between targets. This will result in large gaps between plumes from the targets when used with multiple lasers. Consequently, this arrangement of several conventional target manipulators is not economically or practically suited for use in the large-scale production of HTS-coated wire.
It is therefore an object of the invention to provide a tape transport system well suited to the continuous high-throughput manufacture of HTS tapes.
It is another object of the invention to provide a tape transport system that maintains optimum tape tension throughout extended deposition runs.
It is yet another object of the invention to provide a tape transport system that maintains tapes at an optimal target-to-substrate distance throughout extended deposition runs.
It is yet another object of the invention to provide a tape transport system that prevents damage to the newly deposited superconducting films as the tape winds onto a take-up spool.
It is an object of the invention to provide a substrate heater for use with a non-stationary substrate in a continuous flow vapor deposition process.
It is another object of the invention to provide a substrate heater with multiple independent heating zones for use with a non-stationary substrate in a continuous flow vapor deposition process.
It is yet another object of the invention to provide a substrate heater that achieves the desired heating of a translating substrate by a combination of conductive and radiative heating during a continuous flow vapor deposition process.
It is an object of the invention to provide a multi-target manipulator that provides multiple targets arranged in line for simultaneous use in a multi-laser beam PLD process for the large-scale production of HTS-coated wire.
It is yet another object of the invention to cost-effectively provide a multi-target manipulator for use in a multi-laser beam PLD process for the large-scale production of HTS-coated wire.
It is an object of the present invention to provide a PLD apparatus and method for forming highly uniform HTS film on a tape substrate.
The present invention is a PLD system and method for use in the large-scale, high-throughput production of HTS coated wire. In particular, the present invention includes a high-throughput PLD manufacturing system that provides continuous production of HTS coated tape via the deposition of, for example, yttrium-barium-copper-oxide (YBa2Cu3O7 or “YBCO”) film onto a buffered metal substrate.
In its simplest form, the PLD system of the present invention includes a main deposition chamber disposed between a first and second vacuum chamber. The PLD system further includes a controlled reel-to-reel spooling system capable of translating buffered metal substrate tape through the multiple chambers. The spooling system includes a payout spool disposed within the first vacuum chamber for feeding the substrate tape into the deposition chamber and a take-up spool disposed within the second vacuum chamber for receiving the HTS-coated wire. The size of the deposition chamber is unaffected by the size of the spools which is variable depending on the length of the substrate tape wound thereon.
The main deposition chamber further includes elements that allow the formation of a deposition zone that is longer than those in conventional deposition systems without sacrificing the uniformity of deposition of the coating material on the substrate. Such elements include multiple laser beams, which impinge simultaneously upon multiple targets mounted on a multi-target manipulator, thereby simultaneously forming multiple plumes of HTS particles, to which the substrate is exposed in a deposition zone.
The presence of multiple overlapping plumes arranged sequentially effectively lengthens the deposition zone wherein the substrate is exposed to the evaporant material. The thickness of the HTS film deposited onto the substrate tape is controlled by the rotational speed of a payout and take-up spool within the spooling system, thereby controlling the time that the substrate is present in the deposition zone.
The reel-to-reel tape transport system includes a pair of spools driven by a pair of identical motors that force the rotation and thereby the translation of a substrate tape at a rate of between 10 and 500 meters per hour through one or more adjacent deposition chambers in which a layer of superconducting material, such as YBCO, is deposited. The motors are managed by a controller such that, as one motor drives the spools, the other imparts an amount of resistance sufficient to provide an optimal tension in the tape. A pair of idlers maintains the tape at an optimal position as it translates through a deposition zone. The idlers come into contact with the non-coated side of the tape as the tape winds off a payout spool and onto a take-up spool; the idlers shift in their positioning so as to accommodate the changing radii of tape housed on each spool.
Subsequent to undergoing the deposition of a superconducting layer, the tape is made to wind onto a take-up spool such that the HTS-coated side winds in an orientation toward the center of the spool rather than toward the outer perimeter of the spool, as the superconducting film is less likely to be damaged when under compressive strain rather than when under tensile strain. As an additional protective measure, a length of polymer interleaf may be wound into the take-up spool between tape layers as the tape winds onto the take-up spool, thereby protecting the superconducting layer form being scratched by the non-coated side of the substrate tape.
The system also includes a scalable multi-zone substrate heater for heating by a combination of conduction and radiation a continuously translating substrate in a high-throughput continuous production vapor deposition process. The multi-zone substrate heater of the present invention is suitable for use inside a vapor deposition chamber for depositing, for example, a HTS film on a buffered metal substrate tape translating through the deposition chamber.
In order to optimally reach the desired temperature profile across the entire length of a deposition zone within the deposition chamber, the multi-zone heater embodiment of the present invention includes an arrangement of heating elements that provides multiple temperature zones. Such temperature zones include, for example, a preheating zone providing a maximum temperature of 860° C., a deposition heating zone providing a maximum temperature of 900° C., and a cooling zone providing a maximum temperature of 860° C., where the preheating zone is oriented toward the entry point of the vapor deposition zone and the cooling zone is oriented toward the exit point of the vapor deposition zone.
In another embodiment of the invention, a plurality of deposition heating zones are arranged sequentially between the preheating zone and the cooling zone in a scalable fashion to accommodate process deposition zones of varying length depending on the size of the deposition chamber and/or the desired throughput.
For use in a pulsed laser deposition (PLD) process, the multi-zone heater of the present invention includes passages that enable one or more laser beams to pass unimpeded to one or more targets, which otherwise would be obstructed by the size of such a substrate heater that is necessary to accommodate the increased deposition zone length necessary to a high throughput PLD system. The multi-zone heater also allows for accurate monitoring of the substrate temperature via thermocouples and an optical pathway disposed through its structure that enables a pyrometer to make temperature measurements to the non-coated side of the translating tape.
The system also optionally includes a multi-target manipulator apparatus. The multi-target manipulator apparatus includes a plurality of target manipulators mechanically coupled to one another in a line via a bar or platen. Each target manipulator within the multi-target manipulator apparatus includes a target holder driven by an independent drive motor that provides rotational motion to the target holder via a shaft. Furthermore, the bar or platen connecting the plurality of target manipulators one to another is mechanically coupled to a common variable-speed actuator that provides the oscillatory motion in combination with the rotational motion provided by the respective motors.
In operation, the multi-target manipulator apparatus, having multiple target holders upon which are placed multiple targets, respectively, allows multiple laser beams to impinge simultaneously upon the targets. As a result, multiple plumes of ablated material, to which a substrate is exposed for a predetermined time, are formed, thereby forming a film on the substrate. Furthermore, due to the appropriate spacing between the multiple target manipulators arranged in a line, the resulting plumes slightly overlap one to another and therefore ensure uniformity of film deposition over an expanded deposition zone length.
The multi-target manipulator apparatus of the present invention is especially suitable for use in a multi-laser beam PLD process for the large-scale production of HTS-coated wire.
The deposition chamber 102 is a chamber designed specifically for pulsed laser deposition applications, such as a 12- or 18-inch vacuum chamber commercially available by Neocera, although those skilled in the art will appreciate that a number of alternative vendors manufacture vacuum chambers in a variety of shapes and sizes that may be implemented as the deposition chamber 102 of the present invention. The surrounding vacuum chambers 104 and 106 may be of a variety of dimensions and serve in the present invention to house elements of the spooling system.
Housed within the deposition chamber 102 are one or more target manipulators, for example, a target manipulator 122 that includes a motor 123 and a target holder 124 mechanically connected via a shaft 125. The target holder 124 is a mount onto which a target 136 composed of HTS material, such as YBCO or cerium oxide (CeO2), depending upon the application, is placed. The target 136 is available commercially from suppliers such as Target Materials, Praxair, and Superconductive Components. In its simplest from, the target manipulator 122 may be one of many off-the-shelf models available to the industry that enables translation and rotation (rastering) of the target 136 and/or target indexing (target selection in multiple target holders) in such a way as to ensure a uniform wearing away of the target 136 during the PLD process and to prevent surface irregularities or undesirable microstructures from developing on the target 136 due to repeated ablation events in localized regions.
Alternatively, to provide maximum throughput, the target manipulator 122 is a multi-target manipulator apparatus suitable to handle multiple instantiations of the target 136 for use in a multi-laser PLD process. In this case, the multi-target manipulator is useful in a multiple or split laser beam PLD system having a single or multi-zone substrate heater. This multi-target manipulator suitably provides the required rotating and variable-speed side-to-side oscillating motion to multiple instantiations of the target 136 simultaneously each having a laser beam impinging upon their surface concurrently, thereby maximizing the deposition zone and thus optimizing the throughput in the continuous production PLD process.
Multiple instantiations of the target holder 124 of the target manipulator 122 are oriented when installed toward a substrate heater 200 that is also housed within the deposition chamber 102. The substrate heater 200 is a heating device used to heat and maintain the temperature of the substrate to within a range of approximately 750 to 900° C. In its simplest form, the substrate heater 200 may be a conductive or radiant heater that is available commercially from vendors such as Thermionics, Thermocoax, Neocera, and PVD Products. However, for the purpose of continuous, long tape deposition, a heater with combined conductive and radiative heat transfer is preferred in order to achieve optimum substrate temperature as the substrate moves through the deposition zone. Alternatively, to provide maximum throughput, the substrate heater 200 is a multi-zone heater. Such a multi-zone heater includes multiple independently controlled and monitored temperature zones (e.g., a preheating zone providing a maximum temperature of 860° C., one or more deposition heating zones each providing a maximum temperature of 900° C., and a cooling zone providing a maximum temperature of 860° C.) arranged sequentially along the axis of the tape translation in order to optimally reach the desired temperatures across the entire length of an expanded deposition zone made possible by the use of a target manipulator 122 suitable to handle multiple instantiations of the target 136 in combination with a multiple or split laser beam PLD system.
Furthermore, in a preferred embodiment, the substrate heater 200 is a scalable multi-zone heater design that includes multiple “deposition heating zones” arranged sequentially along the axis of the tape translation to accommodate process deposition zones of varying length within deposition chamber 102.
The design of the multi-zone heater allows multiple laser beams to pass unobstructed to multiple instantiations of the target 136 and allows for accurate monitoring of the substrate temperature via thermocouples throughout the continuous PLD process.
As shown in more detail in
The payout spool 128 is a reel onto which an extended length of the substrate tape 140 is wound. A typical diameter of the payout spool 128 is eight inches. The payout spool 128 may contain a protective interleaf material wound between the layers of the substrate tape 142 contained thereon for protective purposes. The take-up spool 130 is a reel onto which the substrate tape winds after it is exposed to a pulsed laser deposition process in the deposition chamber 102. A typical diameter of the take-up spool 132 is eight inches. If disposed near the deposition zone, the take-up spool 132 and/or the payout spool 128 may be cooled.
The motors 124 and 133 are connected to the payout spool 122 and the take-up spool 130, respectively. The motors 124 and 133 are identical and serve one of two functions: one motor serves to drive a spool and translate the substrate tape 140 through deposition chamber(s) 102, while the other motor serves to provide a preset amount of tension in the substrate tape. In
The controllers 126 and 135 control the action of the motors 124 and 132, respectively. The controllers 126 and 135 are responsible for maintaining the translation of the substrate tape 140 through the deposition chamber(s) 102 at the optimum speed and proper tension, as well as ensuring a compact winding of the substrate tape 140 onto the take-up spool 130. The controllers 126 and 135 may provide real time information about the tension of the tape 140 to an externally located control source or, alternately, tension may be actively monitored with the use of a tension-sensing device such as a load cell (not shown). Such a load cell mechanism may come into contact with the tape 140 and communicate actively with the controllers 126 and 135 in a feedback loop. The controllers 126 and 135 may then compare the communicated tension with a preset tension value stored within their memories and subsequently adjust the tension of the tape 140 via control of the motor 124 and/or 133.
The idlers 130 and 134 are rotating elements that are in contact with the none-coated side of the substrate tape 140. A typical diameter of the idlers 130 and 134 is between three and five inches. The idlers 128 and 136 maintain the translating substrate tape 140 at a consistent orientation within the deposition zone. The idlers 128 and 136 prevent movement of the substrate tape 142 in any direction except for that of its translation, ensuring the substrate tape 140 is exposed to an optimum portion of the plume 142. A precise distance from the plume 142 (typically two inches) must be maintained to ensure a uniform and consistent deposition of material onto the substrate tape 140. Additionally, it is likely that there may be additional pairs of idlers included in applications in which the spooling system 120 translates the substrate tape 142 through more than one adjacent deposition chambers. The idlers 128 and 136 additionally allow for adjustment in the positioning of the substrate tape 140, as is desirable when it is determined that the substrate-to-target 144 distance must change.
In operation, the payout spool 122 containing the substrate tape 140, which has been exposed to a buffer deposition process such as IBAD, is received from the buffer layer deposition processing area and is mounted in the payout spool 122 location of the spooling system 120. The take-up spool 130 is similarly mounted, and a leader section of tape attached to the take-up spool 130 is laced under the idler 136, through the slit 119, in some cases through a multi-zone substrate heater, through the slit 138, and under the idler 128, and is spot-welded or spliced to the substrate tape 140. The heater is turned on, the motor 132 and the motor 124 are engaged, the substrate tape 140 translates through the deposition chamber 102 at a constant rate of between 10 and 500 meters per hour, and a PLD process occurs that deposits a superconducting layer atop the substrate tape 140.
During translation of the substrate tape 142 (from left to right, as seen in
The substrate tape 140 winds onto the take-up spool 132 such that the HTS-coated side of the substrate tape 140 is oriented toward the center of the take-up spool 132. The ceramic film deposited on the substrate tape 140 is less likely to be damaged when under compressive stress than when under tensile stress, as the ceramic grains atop the substrate tape 140 may fracture when bent beyond a certain strain, resulting in a decrease in the critical current-carrying capacity of the finished superconductor tape. As an additional protective measure, a length of polymer interleaf may be wound into the take-up spool 132 between layers as the substrate tape 140 winds onto the take-up spool 132, protecting the superconducting layer of the substrate tape 140 from being scratched by the non-coated side of the substrate tape 140, Polymer interleaf layers may also be included in the payout spool 128 and collected by a collector spool as the substrate tape 140 rolls off the payout spool 128. Additionally, the substrate tape 140 may undergo silver sputtering in a chamber adjacent to the deposition chamber 102 before winding onto the take-up spool 132 to provide a protective coating to the substrate tape 140.
The substrate tape 140 is an extended length of buffered substrate that may have dimensions of one centimeter in width and upwards of one hundred meters in length. An example of the substrate 140 is a buffered metal (e.g., polycrystalline nickel alloy) tape. In the case of a buffered metal tape, the substrate 140 is composed of for example, Hastelloy, Inconel, or stainless steel that has been cleaned and polished and measures, for example, between 25 and 100 microns in thickness, with, for example, a yttria-stabilized zirconia (YSZ), cerium oxide (CeO2) or magnesium oxide (MgO) buffer layer deposited thereon by one of several well-known deposition techniques, such as ion beam assisted deposition (IBAD). Optionally, the substrate 140 may include “dummy tape,” or a length of non-processed substrate, at both ends to allow easier lacing through the multi-laser beam PLD system 100 and easier subsequent handling.
In operation, the laser 142 emits a pulsed laser beam 210 that subsequently passes through a commercially available adjustable focus optical lens 144 and then reflects off a mirror 146 that is a light-reflecting surface available commercially from suppliers such as Roper Scientific. The PLD system 100 includes a laser port 148 that has a quartz window through which the laser beam 210 enters into the deposition chamber 102. Because a laser beam, such as the laser beam 210, is operating continuously during the PLD process, contaminate particles of the target material may tend to cloud the laser window within the laser port 148 over time. Thus, in the preferred embodiment, the laser port 148 includes a laser beam delivery system that monitors and automatically maintains a laser beam 210 of constant energy by monitoring the intensity of the laser beam 210 via sensors and feeding back to a controller such that the laser 142 power level may be adjusted up or down accordingly.
A plume 212 is a plasma cloud resulting from the material of the target 136 melting and subsequently evaporating explosively when impinged upon by the laser beam 210.
The PLD system 100 further includes various controls and monitoring devices, such as a mass flow controller (MFC) 150 that regulates the mass of gas that enters the deposition chamber 102; a vacuum pump 152 mounted to the deposition chamber 102 via a pump port 154 in chamber wall 120, where the vacuum pump 152 may be a combination of a mechanical pump and a turbo-molecular pump and functions to assist in controlling the pressure inside the deposition chamber 102 and purging gas from the deposition chamber 102, and where the pump port 154 also acts as the outlet through which gas is purged from the deposition chamber 102; a pressure gauge 156 that is a pressure-sensing device, such as a capacitance monometer, a hot cathode, a cold cathode, a convectron, or a number of other applicable instruments; and an electron gun 158 that during operation emits an electron stream 214 into the deposition chamber 102 and onto the deposited HTS layers of the substrate 140 at a grazing angle less than five degrees. The electron stream 214 impinges on the layers deposited on the substrate 140 and is diffracted and analyzed at a RHEED pattern analysis area 160. The RHEED pattern analysis area 160 is an analysis area at which a diffraction pattern is produced due to the interaction of the incident electron stream 214 and the crystalline arrangement of the surface of film deposited onto the substrate 140. RHEED diffraction patterns, often represented by an Ewald sphere, are produced when the momentum of incident electron stream 214 and that of the diffracted electron beam differ by a reciprocal lattice vector of the deposition surface, and are used to monitor the growth, crystallinity, and crystal orientation of the film (layers deposited onto the substrate 140) in situ. Additionally, other in situ monitoring tools that may be incorporated into the PLD system 100 include a helium neon (HeNe) laser with a HeNe pass filter and photodiode, an X-ray diffractometer system, or an X-ray fluorescence system.
With continued reference to
The target 136 is mounted to the target holder 124 within the vacuum environment of the deposition chamber 102 in close proximity to the substrate 140, onto which the evaporant material, such as YBCO, is to be deposited.
The vacuum environment of the deposition chamber 102 is developed by the vacuum pump 152 and monitored by the pressure gauge 156. Oxygen is pumped into the deposition chamber 102 via the MFC 150. The substrate 140 is heated to an optimal deposition temperature between 500 and 900° C., preferably between about 750 and about 830° C., by the radiant substrate heater 200. The pulsed laser beam 210, which is generated by the laser 142 located outside the deposition chamber 102, is focused by the lens 144, reflects off the mirror 146, and is directed into the deposition chamber 102 through the laser port 148 to impinge upon a portion of the target 136, causing the formation of the plume 212, which emanates from that portion of the target 136 radiated by the laser beam 210 toward the substrate 140 in a highly forward-directed fashion. The particles contained in the plume 212 are thus deposited onto the surface of the substrate 140 as the tape translates through the deposition chamber 102 at a predetermined speed controlled by the rotational speed of the take-up spool 132.
The target 136 is rastered, or rotated and translated, by the target manipulator 122 during the laser impingement events to prevent undesirable microstructures (cones) from developing on the surface of the target 136 and, further, to assure an even wearing away of the target 136. As the HTS coated tape formed by the PLD process exits the deposition chamber 102 through the opening 119 in the chamber wall 118, it may optionally undergo silver sputtering in an adjacent chamber to provide a protective coating. Alternately, a protective film may wind onto the take-up spool 132 as the superconducting tape winds onto the take-up spool 132 to provide a protective barriers.
As the deposition process occurs, the in situ monitoring tools as described in
The deposition chamber 102 may additionally include several extra ports for user diagnostics or other applications, including, but not limited to, target and substrate view ports, ports for atomic absorption or emission spectroscopy, and a pair of ports for if situ ellipsometry.
To provide a PLD system 100 that is highly optimized for the continuous, high throughput production of HTS wire, the translation rate of the substrate 140 through the PLD system 100 is increased by expanding the length of the deposition zone in the following mainer. In an alternative embodiment that achieves all expanded length deposition zone, the PLD system 100 of the present invention includes multiple instantiations of the laser beam 210 for impinging upon multiple instantiations of the target 136 arranged sequentially along the axis of the tape translation, thereby forming multiple instantiations of the plume 212 simultaneously to which the substrate 140 is exposed. The multiple instantiations of the target 136 are mounted onto the target manipulator 122 that suitably designed to handle the multiple instantiations of the target 136. The multiple instantiations of the plume 212 are arranged sequentially along the axis of the tape translation and are slightly overlapping, thereby forming an expanded length deposition zone wherein the substrate 140 is exposed to the evaporant material. Furthermore, this expanded deposition zone provides a film deposition uniformity within +/−5%. The thickness of the HTS film deposited onto the substrate 140 is controlled by the rotational speed of the take-up spool 132, thereby controlling the time that the substrate 140 is present in the deposition zone.
Multiple instantiations of the laser beam 210 may be supplied by multiple instantiations of the laser 142, respectively, or by a single laser 142 having a laser output that is split into multiple instantiations of the laser beam 210 by optical devices that perform well-known laser splitting functions. In this case, the intensity of the laser beam from the laser 142 is sufficiently powerful, when split, to supply the energy to multiple instantiations of the laser beam 210 required for a PLD process.
With continued reference to
Multiple instantiations of the target 136 are mounted to multiple instalntiations of the target holder 124, respectively, of the target manipulator 122 within the vacuum environment of the deposition chamber 102 in close proximity to the substrate 140, onto which the evaporant material, such as YBCO, is to be deposited. The substrate 140 is heated by convection to an optimal deposition temperature between 500 and 900° C., preferably between about 750 and about 830° C., by the substrate heater 200 that in this embodiment is a radiant multi-zone substrate heater. Multiple instantiations of the pulsed laser beam 210 are focused by multiple instantiations of the lens 144, reflecting off multiple instantiations of the mirror 146, and are directed into the deposition chamber 102 through the multiple instantiations of the laser port 148. The target manipulator 122 suitably provides the required rotating and variable-speed side-to-side oscillating motion to multiple instantiations of the target 136 simultaneously, each having a laser beam 210 impinging upon their surface concurrently, causing the formation of multiple instantiations of the plume 212, which overlap and emanate toward the substrate 140, thereby maximizing the deposition zone and thus optimizing the throughput in the continuous production PLD process. The particles produced by multiple instantiations of the plume 212 are thereby deposited onto the surface of the substrate 140 as the tape translates through the deposition chamber 102 at a predetermined speed controlled by the rotational speed of the take-up spool 132.
Several key observations can be made regarding the multiple laser beam\target\plume arrangement of the PLD system 100 of the present invention:
For a given HTS film thickness, an increase in throughput is achieved that is directly proportional to the number of laser beams and targets operating simultaneously (i.e., thereby forming multiple plumes), as compared with a single laser beam system (i e., a single plume).
Alternatively, for a given substrate translation speed, an increase in HITS film thickness is achieved that is directly proportional to the number of laser beams and targets operating simultaneously (i.e., thereby forming multiple plumes), as compared with a single laser beam system (i.e., a single plume).
High throughput is achieved without sacrificing the uniformity of the deposited material.
With references to
A second heating zone formed within the heater block 210 is a deposition zone 220 having a radiant heating element 222, such as a lamp, fed by a power feed 124. The power feed 124 is electrically connected to the external controller for controlling the power level of the heating element 222 and thereby control its temperature based on feedback to the external controller via a conventional thermocouple 226 that provides temperature measurements from within the deposition zone 220. The heating element 222 within the deposition zone 220 is typically capable of providing a maximum temperature of 900° C.
Lastly, a third heating zone formed within the heater block 210 is a cooling zone 228 likewise having a radiant heating element 230, such as a lamp, or a resistive heating element such as molybdenum disilicide or silicon carbide or nickel-iron alloys such as Kanthal, fed by a power feed 232. The power feed 232 is likewise electrically connected to the external controller for controlling the power level of the heating element 230 and thereby control its temperature based on feedback to the external controller via a conventional thermocouple 234 that provides temperature measurements from within the cooling zone 228. The heating element 230 within the cooling zone 228 is typically capable of providing a maximum temperature of 860° C.
A partition 236 provides the physical and thermal boundary between the preheating zone 212 and the deposition zone 220. Likewise, a partition 238 provides the physical and thermal boundary between the deposition zone 220 and the cooling zone 228. The length of the preheating zone 212, the deposition zone 220, and the cooling zone 228 each measures typically between 6.25 and 7.5 cm [2.5 and 3.0 inches]. Alternatively, the length of each zone can be changed by rearranging the thermal element connection according to requirements. In operation, the maximum ΔT between the preheating zone 212 and the deposition zone 220, and between the cooling zone 228 and the deposition zone 220 is typically 200° C., and the overall temperature stability of the heating zones is +/−5° C.
A shelf 240 forms the base of the multi-zone heater 200. Disposed within the shelf 240 is an aperture 242 that is positioned within the deposition zone 220. More specifically, the aperture 242 is a window that during the deposition process opens briefly to allow a plume of ablated material to reach a substrate 140 to which the aperture 242 is precisely aligned as the substrate 140 translates through the deposition zone 220. The substrate 140 is, for example, a buffered metal (e.g., polycrystalline nickel alloy) tape, depending upon the application.
A susceptor 244 is arranged along the entire length of the multi-zone heater 200, in contact with which the substrate 140 translates in close proximity to the heating elements 214, 222, and 230. The susceptor 244 provides a support for the substrate 140 as it travels through the deposition zone. The main role of the susceptor 244 is to provide a good heat transfer to the substrate 140 so as to maintain a uniform temperature profile in the deposition zone. The susceptor 244 is typically as long as the heater itself and wide enough to cover the entire deposition zone The thickness of the susceptor 244 is between 5 mm and 35 mm, preferably between 10 mm and 20 mm. The susceptor 244 is formed of a material, such as hastelloy or inconel or silicon carbide, that can conduct heat as well as transfer infrared radiation from the heating elements 214, 222, and 230 to the substrate 140. The susceptor 244 must be capable of withstanding the operating temperatures of the deposition process. To enable good thermal conduction, the susceptor is manufactured with a large radius of approximately 5 to 10 m. This radius enables the tape to be taut against the susceptor. The susceptor is thermally stable so that it does not deform when exposed to the high temperatures. Any deformation will prevent good contact between the substrate and the susceptor. Lastly, the susceptor 244 prevents the plume from contacting the inner components of the multi-zone heater 200.
A coolant chamber 246 formed within the heater block 210 provides containment for a coolant, such as water, to flow within the heater block 210. The coolant is necessary to prevent thermal diffusion from the multi-zone heater 200 to other elements within the deposition chamber. The coolant enters the coolant chamber 246 via a plurality of coolant inlets 248 and exits via a plurality of coolant outlets 250.
The multi-zone heater 200 is suitable to operate inside a deposition chamber, such as a PLD chamber, and thus is secured within the chamber via a plurality of standoffs 252. Lastly, and with reference to
With continued reference to
The temperature of the preheating zone 212 is set typically to between 750 and 830° C. via the element 214 under the control of the external controller connecting to the power feed 216. The temperature of the deposition zone 220 is set typically to about 850° C. via the element 222 under the control of the external controller connecting to the power feed 124. Lastly, the temperature of the cooling zone 228 is set typically to between 750 and 830° C. via the element 230 under the control of the external controller connecting to the power feed 232.
Thermocouples 218, 226, and 234 are placed in holes drilled in the body of the susceptor 244 itself and provide continuous temperature measurement feedback to the external controller such that the power level of the elements 214, 222, and 230, respectively, may be adjusted upon the detection of any temperature fluctuations during the deposition process, thereby maintaining the desired temperature within each zone. By placing the thermocouples in body of the susceptor, a better temperature stability can be maintained.
The substrate 140 translates along the length of the multi-zone heater 200 in a flow direction from the preheating zone 212 to the deposition zone 220 and finally exiting through the cooling zone 228. The tension and translation speed of the substrate 140 are maintained in a controlled fashion to achieve proper film uniformity and thickness.
The preheating zone 212 raises the temperature of the substrate 140 to between 750 and 830° C., preparing it for the deposition zone 220. Once inside the deposition zone 220, the temperature of the substrate 140 rises further to about 850° C. and a film of HTS material is deposited onto the substrate 140 via exposure to a plume of PITS material.
The plume of HTS material is generated by a pulsed laser beam impinging on the surface of the HTS target 136 via channel 254 where the plume of PITS material enters the multi-zone heater 200 via the aperture 242 that is synchronized with the pulsed laser beam impinging on the target 136. Having passed through the deposition zone 220, the translating substrate 140 passes into the cooling zone 228 where the temperature is lowered to between 750 and 830° C., preparing the substrate 140 to exit the deposition chamber.
Slots 256a and 256b provide unobstructed paths to the deposition surface of the substrate 140 to accommodate FTIR spectroscopy analyses throughout the deposition process. The FTIR spectroscopy yields information about the temperature, the thickness, and the uniformity of the film being deposited on the substrate 140. Likewise, the channel 258 provides an unobstructed path to the non-deposition surface of the substrate 140 so that the pyrometer (not shown) may monitor the temperature of the non-deposition surface of the substrate 140. Lastly, coolant continuously circulates through the coolant chamber 246 via the coolant inlets 248 and the coolant outlets 250 and thereby maintains the temperature of the heater block 210 and associated hardware at an acceptable level to prevent damage due to excessive heating.
Alternatively, it is noted that the multi-zone heater 200 of the present invention is not limited to a single preheating zone 212, deposition zone 220, and cooling zone 228, as shown in
In the case of a PLD system for continuous production of HTS-coated tape, the targets 136 are composed of HITS material, such as yttrium-barium-copper-oxide (YBa2Cu3O7 or “YBCO”) or cerium oxide (CeO2), depending upon the application. The targets 136 are available commercially from suppliers such as Target Materials, Praxair, and Superconductive Components.
In operation, the lasers 142a, 142b, and 142c producing the laser beams 210a, 210b, and 210c, respectively, that pass though their respective windows in the chamber wall 316 and strike the targets 136a, 136b, and 136c, respectively, as illustrated in
The targets 136a, 136b, and 136c are spaced in such a way as to obtain the desired plume overlap, and hence provide a uniform deposition over an expanded length of the substrate 140.
As well known in the art, target manipulators provide rotational motion as well as side-to-side oscillation. The side-to-side oscillation is provided with variable speed to optimize the target material usage. For illustration only,
With reference to the top and cross-sectional views of
With reference to the top and cross-sectional views of
With reference to the top and cross-sectional views of
In a first embodiment,
The multi-manipulator assembly 350 further includes a connection rod 320a and a connection rod 320b mechanically connected to the support bar 318 at opposing ends. The position and orientation of the connection rods 320a and 320b is not limited to that shown in
Alternatively, a single motor may be mechanically connected using conventional methods to all of the three shafts 316a, 316b, and 316c, subsequently driving the target holders 124a, 124b, and 124c, respectively.
The diameter “d” of the target holders 124a, 124b, and 124c is typically less than two inches so as to enable optimum inter-target spacing and, thus, optimum plume overlap and deposition uniformity. The spacing “e” between the center points of the target holders 124a, 124b, and 124c is set to allow for the optimum plume overlap. The length “l” of the support bar 318 may vary depending on the application and specific mounting requirements. The width “w” and thickness “t” of the support bar 318 are dimensions suitable to accommodate the shafts 316a, 316b, and 316c and are also dimensions suitable to provide strength to the support bar 318 to handle the overall mass of the multi-manipulator assembly 350.
If the multi-manipulator assembly 350 is located entirely within the deposition chamber of the multi-laser PLD system when installed, the variable-speed side-to-side actuator (not shown) and the motors 306a, 306b, and 306c are vacuum-compatible. Alternatively, if the variable-speed side-to-side actuator and the motors 306a, 306b, and 306c are located outside of the deposition chamber of the multi-laser PLD system 100 when installed, the support bar 318 and the shafts 316a, 316b, and 316c are fed through the chamber wall 316 such that a vacuum seal is maintained and such that the side-to-side motion of the multi-manipulator assembly 350 is still allowed.
In operation, the targets 136a, 136b, and 136c are glued onto the target holders 124a, 124b, and 124c, respectively, using a silver paste, such as Ted Pella. The rotator assemblies 310a, 310b, and 310c are activated simultaneously to provide simple rotating motion to the target holders 124a, 124b, and 124c, respectively, and subsequently to the targets 136a, 136b, and 136c, respectively, via the action of the conventional motors 306a, 306b, and 306c, respectively. The variable-speed actuator (not shown) attached to the connection rods 320a and 320b is activated to provide the variable-speed side-to-side oscillating motion to the target holders 124a, 124b, and 124c.
As a result, the multi-manipulator assembly 350 of the present invention provides the rotating and variable-speed side-to-side oscillating motion to the targets 136a, 136b, and 136c, thereby providing optimized operation time required in a high-throughput PLD process. Additionally, the use of the multi-manipulator assembly 350 of the present invention in a PLD process allows a faster film deposition process for a given thickness or allows for a thicker film deposition for a given PIE process speed.
It is important to note that the multi-manipulator assembly 350 of the present invention is not limited to three rotator assemblies as shown in
In a second embodiment,
The operation is identical to that of the multi-manipulator assembly 350 described in
If the motors 306a, 306b, and 306c are vacuum-compatible motors, the multi-manipulator assembly 400 is located entirely within the multi-laser PLD system. Alternatively, the motors 306a, 306b, and 306c mounted on the support plate 410 are disposed outside of the multi-laser PLD system 100 and the shafts 316a, 316b, and 316c are fed through the chamber wall.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10602294 | Jun 2003 | US |
| Child | 11554428 | Oct 2006 | US |