Patent Grant
7700464
This invention relates generally to semiconductor films, and more specifically, to the fabrication of solar cells that use semiconductor films based on IB-IIIA-VIA compounds.
Solar cells and solar modules convert sunlight into electricity. These electronic devices have been traditionally fabricated using silicon (Si) as a light-absorbing, semiconducting material in a relatively expensive production process. To make solar cells more economically viable, solar cell device architectures have been developed that can inexpensively make use of thin-film, light-absorbing semiconductor materials such as copper-indium-gallium-sulfo-di-selenide, Cu(In, Ga)(S, Se)2, also termed CI(G)S(S). This class of solar cells typically has a p-type absorber layer sandwiched between a back electrode layer and an n-type junction partner layer. The back electrode layer is often Mo, while the junction partner is often CdS. A transparent conductive oxide (TCO) such as zinc oxide (ZnOx) is formed on the junction partner layer and is typically used as a transparent electrode. CIS-based solar cells have been demonstrated to have power conversion efficiencies exceeding 19%.
A central challenge in cost-effectively constructing a large-area CIGS-based solar cell or module is that the elements of the CIGS layer must be within a narrow stoichiometric ratio on nano-, meso-, and macroscopic length scale in all three dimensions in order for the resulting cell or module to be highly efficient. Achieving precise stoichiometric composition over relatively large substrate areas is, however, difficult using traditional vacuum-based deposition processes. For example, it is difficult to deposit compounds and/or alloys containing more than one element by sputtering or evaporation. Both techniques rely on deposition approaches that are limited to line-of-sight and limited-area sources, tending to result in poor surface coverage. Line-of-sight trajectories and limited-area sources can result in non-uniform three-dimensional distribution of the elements in all three dimensions and/or poor film-thickness uniformity over large areas. These non-uniformities can occur over the nano-, meso-, and/or macroscopic scales. Such non-uniformity also alters the local stoichiometric ratios of the absorber layer, decreasing the potential power conversion efficiency of the complete cell or module.
Alternatives to traditional vacuum-based deposition techniques have been developed. In particular, production of solar cells on flexible substrates using non-vacuum, semiconductor printing technologies provides a highly cost-efficient alternative to conventional vacuum-deposited solar cells. For example, T. Arita and coworkers [20th IEEE PV Specialists Conference, 1988, page 1650] described a non-vacuum, screen printing technique that involved mixing and milling pure Cu, In and Se powders in the compositional ratio of 1:1:2 and forming a screen printable paste, screen printing the paste on a substrate, and sintering this film to form the compound layer. They reported that although they had started with elemental Cu, In and Se powders, after the milling step the paste contained the Cu—In—Se2 phase. However, solar cells fabricated from the sintered layers had very low efficiencies because the structural and electronic quality of these absorbers was poor.
Screen-printed Cu—In—Se2 deposited in a thin-film was also reported by A. Vervaet et al. [9th European Communities PV Solar Energy Conference, 1989, page 480], where a micron-sized Cu—In—Se2 powder was used along with micron-sized Se powder to prepare a screen printable paste. Layers formed by non-vacuum, screen printing were sintered at high temperature. A difficulty in this approach was finding an appropriate fluxing agent for dense Cu—In—Se2 film formation. Even though solar cells made in this manner had poor conversion efficiencies, the use of printing and other non-vacuum techniques to create solar cells remains promising.
There is a widespread notion in the field, and certainly in the CIGS non-vacuum precursor field, that the most optimized dispersions and coating contain spherical particles and that any other shape is less desirable in terms of dispersion stability and film packing, particularly when dealing with nanoparticles. Accordingly, the processes and theories that dispersion chemists and coating engineers are geared toward involve spherical particles. Because of the high density of metals used in CIGS non-vacuum precursors, especially those incorporating pure metals, the use of spherical particles requires a very small size in order to achieve a well dispersed media. This then requires that each component be of similar size in order to maintain desired stoichiometric ratios, since otherwise, large particles will settle first. Additionally, spheroids are thought to be useful to achieve high packing density on a packing unit/volume basis, but even at high density, spheres only contact at tangential points which represent a very small fraction of interparticle surface area. Furthermore, minimal flocculation is desired to reduce clumping if good atomic mixing is desired in the resulting film.
Due to the aforementioned issues, many experts in the non-vacuum precursor CIGS community desire spherical nanoparticles in sizes that are as small as they can achieve. Although the use of traditional spherical nanoparticles is still promising, many fundamental challenges remain, such as the difficulty in obtaining small enough spherical nanoparticles in high yield and low cost (especially from CIGS precursor materials) or the difficulty in reproducibly obtaining high quality films. Furthermore, the lower interparticle surface area at contact points between spheroidal particles may serve to impede rapid processing of these particles since the reaction dynamics depend in many ways on the amount of surface area contact between particles.
Embodiments of the present invention address at least some of the drawbacks set forth above. The present invention provides for the use of non-spherical particles in the formation of high quality precursor layers which are processed into dense films. The resulting dense films may be useful in a variety of industries and applications, including but not limited to, the manufacture of photovoltaic devices and solar cells. More specifically, the present invention has particular application in the formation of precursor layers for thin film solar cells. The present invention provides for more efficient and simplified creation of a dispersion, and the resulting coating thereof. It should be understood that this invention is generally applicable to any processes involving the deposition of a material from dispersion. At least some of these and other objectives described herein will be met by various embodiments of the present invention.
In one embodiment of the present invention, a method is provided for transforming non-planar and/or planar precursor metals in an appropriate vehicle under the appropriate conditions to create dispersions of planar particles with stoichiometric ratios of elements equal to that of the feedstock or precursor metals, even after selective settling. In particular, planar particles described herein have been found to be easier to disperse, form much denser coatings, and anneal into films at a lower temperature and/or time than their counterparts made from spherical nanoparticles that have substantially similar composition but different morphology. Additionally, even unstable dispersions using large microflake particles that may require continuous agitation to stay suspended still create good coatings. In one embodiment of the present invention, a stable dispersion is one that remains dispersed for a period of time sufficient to allow a substrate to be coated. In one embodiment, this may involve using agitation to keep particles dispersed in the dispersion. In other embodiments, this may include dispersions that settle but can be re-dispersed by agitation and/or other methods when the time for use arrives.
In another embodiment of the present invention, a method is provided that comprises of formulating an ink of particles wherein substantially all of the particles are nanoflakes. In one embodiment, at least about 95% of all particles (based on total weight of all particles) are nanoflakes. In one embodiment, at least about 99% of all particles (based on total weight of all particles) are nanoflakes. In one embodiment, all particles are nanoflakes. In yet another embodiment, all particles are microflakes and/or nanoflakes. Substantially each of the nanoflakes contains at least one element from group IB, IIIA and/or VIA, wherein overall amounts of elements from group IB, IIIA and/or VIA contained in the ink are such that the ink has a desired or close to a desired stoichiometric ratio of the elements for at least the elements of group IB and IIIA. The method includes coating a substrate with the ink to form a precursor layer and processing the precursor layer in a suitable atmosphere to form a dense film. The dense film may be used in the formation of a semiconductor absorber for a photovoltaic device. The film may comprise of a fused version of the precursor layer which comprises of a plurality of individual particles which are unfused.
In yet another embodiment of the present invention, a material is provided that comprises of a plurality of nanoflakes having a material composition containing at least one element from Groups IB, IIIA, and/or VIA. The nanoflakes are created by milling or size reducing precursor particles characterized by a precursor composition that provides sufficient ductility (better: malleability, see later in patent) to form a planar shape from a non-planar and/or planar starting shape when milled or size reduced, and wherein overall amounts of elements from Groups IB, IIIA and/or VIA contained in the precursor particles combined are at a desired or close to a desired stoichiometric ratio of the elements for at least the elements of groups IB and IIIA. In one embodiment, planar includes those that particles that are wide in two dimensions, thin in every other dimension. The milling may transform substantially all of the precursor particles into nanoflakes. Alternatively, the milling transforms at least 50% of the precursor particles into nanoflakes. The milling may occur in an oxygen-free atmosphere to create oxygen-free nanoflakes. The milling may occur in an inert gas environment to create oxygen-free nanoflakes. These non-spherical particles may be nanoflakes that have its largest dimension (thickness and/or length and/or width) greater than about 20 nm, since sizes smaller than that tend to create less efficient solar cells. Milling can also be chilled and occur at a temperature lower than room temperature to allow milling of particles composed of low melting point material. In other embodiments, milling may occur at room temperature. Alternatively, milling may occur at temperatures greater than room temperature to obtain the desired malleability of the material. In one embodiment of the present invention, the material composition of the feedstock particles preferably exhibits a malleability that allows non-planar feedstock particles to be formed into substantially planar nanoflakes at the appropriate temperature. In one embodiment, the nanoflakes have at least one surface that is substantially flat.
In a still further embodiment according to the present invention, a solar cell is provided that comprises of a substrate, a back electrode formed over the substrate, a p-type semiconductor thin film formed over the back electrode, an n-type semiconductor thin film formed so as to constitute a pn junction with the p-type semiconductor thin film, and a transparent electrode formed over the n-type semiconductor thin film. The p-type semiconductor thin film results by processing a dense film formed from a plurality of nanoflakes having a material composition containing at least one element from Groups IB, IIIA, and/or VIA, wherein the resulting film has a void volume of 26% or less. In one embodiment, this number may be based on free volume of packed spheres of different diameter to minimize void volume. In another embodiment of the invention, the dense film has a void volume of about 30% or less. In other embodiments, the void volume is about 20% or less. In still other embodiments, the void volume is about 10% or less.
In another embodiment of the present invention, a method is provided for forming a film by using particles with particular properties. The properties may be based on interparticle size, shape, composition, and morphology distribution. As a nonlimiting example, the particles may be nanoflakes within a desired size range. Within the nanoflakes, the morphology may include particles that are amorphous, those that are crystalline, those that are more crystalline than amorphous, and those that are more amorphous than crystalline. The properties may also be based on interparticle composition and morphology distribution. In one embodiment of the present invention, it should be understood that the resulting flakes have a morphology where the flakes are less crystalline than the feedstock material from which the flakes are formed. Flakes are particles with at least one substantially planar surface and may include both nanoflakes and/or microflakes.
In yet another embodiment of the present invention, the method comprises formulating an ink of particles wherein about 50% or more of the particles (based on the total weight of all particles) are flakes each containing at least one element from group IB, IIIA and/or VIA and having a non-spherical, planar shape, wherein overall amounts of elements from group IB, IIIA and/or VIA contained in the ink are such that the ink has a desired stoichiometric ratio of the elements. In another embodiment, the term “50% or more” may be based on the number of particles versus the total number of particles in the ink. In yet another embodiment, at least about 75% or more of the particles (by weight or by number) are nanoflakes. The method includes coating a substrate with the ink to form a precursor layer and processing the precursor layer in a suitable processing condition to form a film. The film may be used in the formation of a semiconductor absorber for a photovoltaic device. It should be understood that suitable processing conditions may include, but are not limited to, atmosphere composition, pressure, and/or temperature. In one embodiment, substantially all of the particles are flakes with a non-spherical, planar shape. In one embodiment, at least 95% of all particles (based on weight of all particles combined) are flakes. In another embodiment, at least 99% of all particles (based on weight of all particles combined) are flakes. The flakes may be comprised of nanoflakes. In other embodiments, the flakes may be comprised of both microflakes and nanoflakes.
It should be understood that the planar shape of the nanoflakes may provide a number of advantages. As a nonlimiting example, the planar shape may create greater surface area contact between adjacent nanoflakes that allows the dense film to form at a lower temperature and/or shorter time as compared to a film made from a precursor layer using an ink of spherical nanoparticles wherein the nanoparticles have a substantially similar material composition and the ink is otherwise substantially identical to the ink of the present invention. The planar shape of the nanoflakes may also create greater surface area contact between adjacent nanoflakes that allows the dense film to form at an annealing temperature at least 50 degrees C. less as compared to a film made from a precursor layer using an ink of spherical nanoparticles that is otherwise substantially identical to the ink of the present invention.
The planar shape of the nanoflakes may create greater surface area contact between adjacent nanoflakes relative to adjacent spherical nanoparticles and thus promotes increased atomic intermixing as compared to a film made from a precursor layer made from an ink of the present invention. The planar shape of the nanoflakes creates a higher packing density in the dense film as compared to a film made from a precursor layer made from an ink of spherical nanoparticles of the same composition that is otherwise substantially identical to the ink of the present invention.
The planar shape of the nanoflakes may also create a packing density of at least about 76% in the precursor layer. The planar shape of the nanoflakes may create a packing density of at least 80% in the precursor layer. The planar shape of the nanoflakes may create a packing density of at least 90% in the precursor layer. The planar shape of the nanoflakes may create a packing density of at least 95% in the precursor layer. Packing density may be mass/volume, solids/volume, or non-voids/volume.
The planar shape of the nanoflakes results in grain sizes of at least about 1 micron in the semiconductor absorber of a photovoltaic device. The planar shape of the nanoflakes may results in grain sizes of at least about 2.0 μm in at least one dimension in the semiconductor absorber of a photovoltaic device. In other embodiments, the nanoflakes results in grain sizes of at least about 1.0 μm in at least one dimension in the semiconductor absorber of a photovoltaic device. In still further embodiments, the nanoflakes results in grain sizes of at least about 0.5 μm in at least one dimension in the semiconductor absorber of a photovoltaic device. The planar shape of the nanoflakes may result in grain sizes of at least about 0.3 μm wide in the semiconductor absorber of a photovoltaic device. In other embodiments, the planar shape of the nanoflakes results in grain sizes of at least about 0.3 μm wide in the semiconductor absorber of a photovoltaic device when the nanoflakes are formed from one or more of the following: copper selenide, indium selenide, or gallium selenide.
The planar shape of the nanoflakes provides a material property to avoid rapid and/or preferential settling of the particles when forming the precursor layer. The planar shape of the nanoflakes provides a material property to avoid rapid and/or preferential settling of nanoflakes having different material compositions, when forming the precursor layer. The planar shape of the nanoflakes provides a material property to avoid rapid and/or preferential settling of nanoflakes having different particle sizes, when forming the precursor layer. The planar shape of the nanoflakes provides a material property to avoid grouping of nanoflakes in the ink and thus enables a finely dispersed solution of nanoflakes.
The planar shape of the nanoflakes provides a material property to avoid undesired grouping of nanoflakes of a particular class in the ink and thus enables an evenly dispersed solution of nanoflakes. The planar shape of the nanoflakes provides a material property to avoid undesired grouping of nanoflakes of a specific material composition in the ink and thus enables an evenly dispersed solution of nanoflakes. The planar shape of the nanoflakes provides a material property to avoid grouping of nanoflakes of a specific phase separation in the precursor layer resulting from the ink. The nanoflakes have a material property that reduces surface tension at interface between nanoflakes in the ink and a carrier fluid to improve dispersion quality.
In one embodiment of the present invention, the ink may be formulated by use of a low molecular weight dispersing agent whose inclusion is effective due to favorable interaction of the dispersing agent with the planar shape of the nanoflakes. The ink may be formulated by use of a carrier liquid and without a dispersing agent. The planar shape of the nanoflakes provides a material property to allow for a more even distribution of group IIIA material throughout in the dense film as compared to a film made from a precursor layer made from an ink of spherical nanoparticles that is otherwise substantially identical to the ink of the present invention. In another embodiment, the nanoflakes may be of random planar shape and/or a random size distribution.
The nanoflakes may be of non-random planar shape and/or a non-random size distribution. The nanoflakes may each have a length and/or largest lateral dimension less than about 500 nanometers and greater than about 20 nanometers. The nanoflakes may each have a length and/or largest lateral dimension between about 300 nanometers and 50 nanometers. The nanoflakes may each have a thickness of about 100 nm or less. In other embodiments, the lengths of the planar nanoflakes are about 500 nm to about 1 nm. As a nonlimiting example, the nanoflakes may have lengths and/or largest lateral dimension of about 300 nm to about 10 nm. In other embodiments, the nanoflakes may be of thickness in the range of about 200 nm to about 20 nm. In another embodiment, these nanoflakes may be of thickness in the range of about 100 nm to about 10 nm. In one embodiment, these nanoflakes may be of thickness in the range of about 200 nm to about 20 nm. The nanoflakes may each have a thickness less than about 50 nm. The nanoflakes thicknesses of less than about 20 nm. The nanoflakes may have an aspect ratio of at least about 5 or more. The nanoflakes may have an aspect ratio of at least about 10 or more. The nanoflakes have an aspect ratio of at least about 15 or more.
The nanoflakes may be oxygen free. The nanoflakes may be a single metal. The nanoflakes may be an alloy of group IB, IIIA elements. The nanoflakes may be a binary alloy of group IB, IIIA elements. The nanoflakes may be a ternary alloy of group IB, IIIA elements. The nanoflakes may be a quaternary alloy of group IB, IIIA, and/or VIA elements. The nanoflakes may be group IB-chalcogenide particles and/or group IIIA-chalcogenide particles. Again, the particles may be particles that are substantially oxygen-free, which may include those that include less than about 1 wt % of oxygen. Other embodiments may use materials with less than about 5 wt % of oxygen. Still other embodiments may use materials with less than about 3 wt % oxygen. Still other embodiments may use materials with less than about 2 wt % oxygen. Still other embodiments may use materials with less than about 0.5 wt % oxygen. Still other embodiments may use materials with less than about 0.1 wt % oxygen.
In one embodiment of the present invention, the coating step occurs at room temperature. The coating step may occur at atmospheric pressure. The method may further comprise depositing a film of selenium onto the dense film. The processing step may be accelerated via thermal processing techniques using at least one of the following: pulsed thermal processing, exposure to a laser beam, or heating via IR lamps, and/or similar or related methods. The processing may comprise of heating the precursor layer to a temperature greater than about 375° C. but less than a melting temperature of the substrate for a period of less than 15 minutes. The processing may comprise of heating the precursor layer to a temperature greater than about 375° C. but less than a melting temperature of the substrate for a period of 1 minute or less. In another embodiment of the present invention, processing may comprise of heating the precursor layer to an annealing temperature but less than a melting temperature of the substrate for a period of 1 minute or less. The suitable atmosphere may comprise of a hydrogen atmosphere. In another embodiment of the present invention, the suitable atmosphere comprises a nitrogen atmosphere. In yet another embodiment, the suitable atmosphere comprises a carbon monoxide atmosphere. The suitable atmosphere may be comprised of an atmosphere having less than about 10% hydrogen. The suitable atmosphere may be comprised of an atmosphere containing selenium. The suitable atmosphere may be comprised of an atmosphere of a non-oxygen chalcogen. In one embodiment of the present invention, the suitable atmosphere may comprise of a selenium atmosphere providing a partial pressure greater than or equal to vapor pressure of selenium in the precursor layer. In another embodiment, the suitable atmosphere may comprise of a non-oxygen atmosphere containing chalcogen vapor at a partial pressure of the chalcogen greater than or equal to a vapor pressure of the chalcogen at the processing temperature and processing pressure to minimize loss of chalcogen from the precursor layer, wherein the processing pressure is a non-vacuum pressure. In yet another embodiment, the chalcogen atmosphere may be used with one or more binary chalcogenides (in any shape or form) at a partial pressure of the chalcogen greater than or equal to a vapor pressure of the chalcogen at the processing temperature and processing pressure to minimize loss of chalcogen from the precursor layer, wherein optionally, the processing pressure is a non-vacuum pressure.
In yet another embodiment of the present invention, prior to the step of formulating the ink, there is included a step of creating nanoflakes. The creating step comprises of providing feedstock particles containing at least one element of groups IB, IIIA, and/or VIA, wherein substantially each of the feedstock particles have a composition of sufficient malleability to form a planar shape from a non-planar starting shape and milling the feedstock particles to reduce at least the thickness of each particle to less than 100 nm. The milling step may occur in an oxygen free atmosphere to create substantially oxygen-free nanoflakes. The substrate may be a rigid substrate. The substrate may be a flexible substrate. The substrate may be an aluminum foil substrate or a polymer substrate, which is a flexible substrate in a roll-to-roll manner (either continuous or segmented) using a commercially available web coating system. The rigid substrate may be comprised of at least one material selected from the group: glass, soda-lime glass, steel, stainless steel, aluminum, polymer, ceramic, metal plates, metallized ceramic plates, metallized polymer plates, metallized glass plates, and/or any single or multiple combination of the aforementioned. The substrate may be at different temperatures than the precursor layer during processing. This may enable the substrate to use materials that would melt or become unstable at the processing temperature of the precursor layer. Optionally, this may involve actively cooling the substrate during processing.
In yet another embodiment of the present invention, a method is provided for formulating an ink of particles wherein a majority of the particles are nanoflakes each containing at least one element from group IB, IIIA and/or VIA and having a non-spherical, planar shape, wherein the overall amounts of the elements from group IB, IIIA and/or VIA contained in the ink are such that the ink has a desired stoichiometric ratio of the elements. The method may include coating a substrate with the ink to form a precursor layer, and processing the precursor layer to form a dense film for growth of a semiconductor absorber of a photovoltaic device. In one embodiment, at least 60% of the particles (by weight or by number) are microflakes. In yet another embodiment, at least 70% of the particles (by weight or by number) are microflakes. In another embodiment, at least 80% of the particles (by weight or by number) are microflakes. In another embodiment, at least 90% of the particles (by weight or by number) are microflakes. In another embodiment, at least 95% of the particles (by weight or by number) are microflakes.
A further understanding of the nature and advantages of the invention will become apparent by reference to the remaining portions of the specification and drawings.
It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory only and are not restrictive of the invention, as claimed. It may be noted that, as used in the specification and the appended claims, the singular forms “a”, “an” and “the” include plural referents unless the context clearly dictates otherwise. Thus, for example, reference to “a material” may include mixtures of materials, reference to “a compound” may include multiple compounds, and the like. References cited herein by hereby incorporated by reference in their entirety, except to the extent that they conflict with teachings explicitly set forth in this specification.
In this specification and in the claims which follow, reference will be made to a number of terms which shall be defined to have the following meanings:
“Optional” or “optionally” means that the subsequently described circumstance may or may not occur, so that the description includes instances where the circumstance occurs and instances where it does not. For example, if a device optionally contains a feature for a barrier film, this means that the barrier film feature may or may not be present, and, thus, the description includes both structures wherein a device possesses the barrier film feature and structures wherein the barrier film feature is not present.
According to embodiments of the present invention, an active layer for a photovoltaic device may be fabricated by first formulating an ink of non-spherical particles each containing at least one element from groups IB, IIIA and/or VIA, coating a substrate with the ink to form a precursor layer, and heating the precursor layer to form a dense film. Optionally, it should be understood that in some embodiments, densification of the precursor layer may not be needed, particularly if the precursor materials are oxygen-free and/or substantially oxygen-free. Thus, the heating step may optionally be skipped if the particles are processed air-free and are oxygen-free. In a preferred embodiment, the non-spherical particles are nanoflakes that are substantially planar in shape. The dense film may be processed in a suitable atmosphere to form a group IB-IIIA-VIA compound. The resulting group IB-IIIA-VIA compound is preferably a compound of Cu, In, Ga and selenium (Se) or sulfur S of the form CuIn(1−x)GaxS2(1−y)Se2y, where 0≦x≦1 and 0≦y≦1. It should also be understood that the resulting group IB-IIIA-VIA compound may be a compound of Cu, In, Ga and selenium (Se) or sulfur S of the form CuzIn(1−x)GaxS2(1−y)Se2y, where 0.5≦z≦1.5, 0≦x≦1.0 and 0≦y≦1.0.
It should be understood that group IB, IIIA, and VIA elements other than Cu, In, Ga, Se, and S may be included in the description of the IB-IIIA-VIA materials described herein, and that the use of a hyphen (“—” e.g., in Cu—Se or Cu—In—Se) does not indicate a compound, but rather indicates a coexisting mixture of the elements joined by the hyphen. It is also understood that group IB is sometimes referred to as group 11, group IIIA is sometimes referred to as group 13 and group VIA is sometimes referred to as group 16. Furthermore, elements of group VIA (16) are sometimes referred to as chalcogens. Where several elements can be combined with or substituted for each other, such as In and Ga, or Se, and S, in embodiments of the present invention, it is not uncommon in this art to include in a set of parentheses those elements that can be combined or interchanged, such as (In, Ga) or (Se, S). The descriptions in this specification sometimes use this convenience. Finally, also for convenience, the elements are discussed with their commonly accepted chemical symbols. Group IB elements suitable for use in the method of this invention include copper (Cu), silver (Ag), and gold (Au). Preferably the group IB element is copper (Cu). Group IIIA elements suitable for use in the method of this invention include gallium (Ga), indium (In), aluminum (Al), and thallium (Tl). Preferably the group IIIA element is gallium (Ga) or indium (In). Group VIA elements of interest include selenium (Se), sulfur (S), and tellurium (Te), and preferably the group VIA element is either Se and/or S. It should be understood that mixtures such as, but not limited to, alloys, solid solutions, and compounds of any of the above can also be used.
Method of Forming a Film
Referring now to
As seen in
Referring now to
It should be understood that different types of nanoflakes 108 may be used to form the precursor layer 106. In one nonlimiting example, the nanoflakes are elemental nanoflakes, i.e., nanoflakes having only a single atomic species. The nanoflakes may be single metal particles of Cu, Ga, In or Se. Some inks may have only one type of nanoflakes. Other inks may have two or more types of nanoflakes which may differ in material composition and/or other quality such as but not limited to shape, size, interior architecture (e.g. a central core surrounded by one or more shell layers), exterior coating (be more explanatory on this one, maybe use words like core-shell), or the like. In one embodiment, the ink used for precursor layer 106 may contain nanoflakes comprising one or more group IB elements and nanoflakes comprising one or more different group IIIA elements. Preferably, the precursor layer (106) contains copper, indium and gallium. In another embodiment, the precursor layer 106 may be an oxygen-free layer containing copper, indium and gallium. Optionally, the ratio of elements in the precursor layer may be such that the layer, when processed, forms a compound of CuInxGa1−x, where 0≦x≦1. Those of skill in the art will recognize that other group IB elements may be substituted for Cu and other group IIIA elements may be substituted for In and Ga. Optionally, the precursor may contain Se as well, such as but not limited to Cu—In—Ga—Se plates. This is feasible if the precursor is oxygen-free and densification is not needed. In still further embodiments, the precursor material may contain nanoflakes of group IB, IIIA, and VIA elements. In one nonlimiting example, the precursor may contain Cu—In—Ga—Se nanoflakes, which would be particularly advantageous if the nanoflakes are formed air free and densification prior to film formation is not needed.
Optionally, the nanoflakes 108 in the ink may be alloy nanoflakes. In one nonlimiting example, the nanoflakes may be binary alloy nanoflakes such as Cu—In, In—Ga, or Cu—Ga. Alternatively, the nanoflakes may be a binary alloy of group IB, IIIA elements, a binary alloy of Group IB, VIA elements, and/or a binary alloy of group IIIA, VIA elements. In other embodiments, the particles may be a ternary alloy of group IB, IIIA, and/or VIA elements. For example, the particles may be ternary alloy particles of any of the above elements such as but not limited to Cu—In—Ga. In other embodiments, the ink may contain particles that are a quaternary alloy of group IB, IIIA, and/or VIA elements. Some embodiments may have quaternary or multi-nary nanoflakes. The ink may also combine nanoflakes of different classes such as but not limited to elemental nanoflakes with alloy nanoflakes or the like. In one embodiment, the nanoflakes used to form the precursor layer 106 preferably contains no oxygen other than those amounts unavoidably present as impurities. Optionally, the microflakes contain less than about 0.1 wt % of oxygen. In other embodiments, the microflakes contain less than about 0.5 wt % of oxygen. In still further embodiments, the microflakes contain less than about 1.0 wt % of oxygen. In yet another embodiment, the microflakes contain less than about 3.0 wt % of oxygen. In other embodiments, the microflakes contain less than about 5.0 wt % of oxygen.
Optionally, the nanoflakes 108 in the ink may be chalcogenide particles, such as but not limited to, a group IB or group IIIA selenide. In one nonlimiting example, the nanoflakes may be a group IB-chalcogenide formed with one or more elements of group IB (new-style: group 11), e.g., copper (Cu), silver (Ag), and gold (Au). Examples include, but are not limited to, CuxSey, wherein x is in the range of about 1 to 10 and y is in the range of about 1 to 10. In some embodiments of the present invention, x≦y. Alternatively, some embodiments may have selenides that are more selenium rich, such as but not limited to, CulSex (where x>1). This may provide an increased source of selenium as discussed in commonly assigned, co-pending U.S. patent application Ser. No. 11/361,522 filed on Feb. 22, 2006 and fully incorporated herein by reference. In another nonlimiting example, the nanoflakes may be a group IIIA-chalcogenide formed with one or more elements of group IIIA (new style: group 16), e.g., aluminum (Al), indium (In), gallium (Ga), and thallium (Tl). Examples include InxSey and GaxSey wherein x is in the range of about 1 to about 10 and y is in the range of about 1 to about 10. Still further, the nanoflakes may be a Group IB-IIIA-chalcogenide compound of one or more group IB elements, one or more group IIIA elements and one or more chalcogens. Examples include CuInGa—Se2. Other embodiments may replace the selenide component with another group VIA element such as but not limited to sulfur, or combinations of multiple group VIA elements such as both sulfur and selenium.
It should be understood that the ink used in the present invention may include more than one type of chalcogenide nanoflakes. For example, some may include nanoflakes from both group IB-chalcogenide(s) and group IIIA-chalcogenide(s). Others may include nanoflakes from different group IB-chalcogenides with different stoichiometric ratios. Others may include nanoflakes from different group IIIA-chalcogenides with different stoichiometric ratios.
Optionally, the nanoflakes 108 in the ink may also be particles of at least one solid solution. In one nonlimiting example, the nano-powder may contain copper-gallium solid solution particles, and at least one of indium particles, indium-gallium solid-solution particles, copper-indium solid solution particles, and copper particles. Alternatively, the nano-powder may contain copper particles and indium-gallium solid-solution particles. [DEFINITION OF SOLID SOLUTION. I'M LEANING TOWARDS LEAVING OUT THE DEFINITION AND GOING WITH PLAIN MEANING].
One of the advantages of using nanoflake-based dispersions is that it is possible to vary the concentration of the elements within the precursor layer 106 from top to bottom by building the precursor layer in a sequence of thinner sub-layers, which when combined, form the precursor layer. The material may be deposited to form the first, second layer or subsequent sub-layers, and reacted in at least one suitable atmosphere to form the corresponding component of the active layer. In other embodiment, the sub-layers may be reacted as the sub-layers are deposited. The relative elemental concentration of the nanoflakes that make up the ink for each sub-layer may be varied. Thus, for example, the concentration of gallium within the absorber layer may be varied as a function of depth within the absorber layer. The precursor layer 106 (or selected constituent sub-layers, if any) may be deposited using a precursor material formulated with a controlled overall composition having a desired stoichiometric ratio. More details on one method of building a layer in a sequence of sub-layers can be found in commonly assigned, copending U.S. patent application Ser. No. 11/243,492 filed Oct. 3, 2005 and fully incorporated herein by reference for all purposes.
It should be understood that the film may be a layer made from a dispersion, such as but not limited to an ink, paste, or paint. A layer of the dispersion can be spread onto the substrate and annealed to form the precursor layer 106. By way of example the dispersion can be made by forming oxygen-free nanoflakes containing elements from group IB, group IIIA and intermixing these nanoflakes and adding them to a vehicle, which may encompass a carrier liquid (such as but not limited to a solvent), and any additives.
Generally, an ink may be formed by dispersing the nanoflakes in a vehicle containing a dispersant (e.g., a surfactant or polymer) along with (optionally) some combination of other components commonly used in making inks. In some embodiments of the present invention, the ink is formulated without a dispersant or other additives. The carrier liquid may be an aqueous (water-based) or non-aqueous (organic) solvent. Other components include, without limitation, dispersing agents, binders, emulsifiers, anti-foaming agents, dryers, solvents, fillers, extenders, thickening agents, film conditioners, anti-oxidants, flow and leveling agents, plasticizers and preservatives. These components can be added in various combinations to improve the film quality and optimize the coating properties of the nanoflake dispersion. An alternative method to mixing nanoflakes and subsequently preparing a dispersion from these mixed nanoflakes would be to prepare separate dispersions for each individual type of nanoflake and subsequently mixing these dispersions. It should be understood that, due to favorable interaction of the planar shape of the nanoflakes with the carrier liquid, some embodiments of the ink may be formulated by use of a carrier liquid and without a dispersing agent.
The precursor layer 106 from the dispersion may be formed on the substrate 102 by any of a variety of solution-based coating techniques including but not limited to wet coating, spray coating, spin coating, doctor blade coating, contact printing, top feed reverse printing, bottom feed reverse printing, nozzle feed reverse printing, gravure printing, microgravure printing, reverse microgravure printing, comma direct printing, roller coating, slot die coating, meyerbar coating, lip direct coating, dual lip direct coating, capillary coating, ink-jet printing, jet deposition, spray deposition, and the like, as well as combinations of the above and/or related technologies.
In some embodiments, extra chalcogen, alloys particles, or elemental particles, e.g., micron- or sub-micron-sized chalcogen powder may be mixed into the dispersion containing the nanoflakes so that the nanoflakes and extra chalcogen are deposited at the same time. Alternatively the chalcogen powder may be deposited on the substrate in a separate solution-based coating step before or after depositing the dispersion containing the nanoflakes. In other embodiment, group IIIA elemental material such as but not limited to gallium droplets may be mixed with the flakes. This is more fully described in commonly assigned, copending U.S. patent application Ser. No. 11/361,522 filed on Feb. 22, 2006 and fully incorporated herein by reference. This may create an additional layer 107 (shown in phantom in
Note that the solution-based deposition of the proposed mixtures of nanoflakes does not necessarily have to be performed by depositing these mixtures in a single step. In some embodiments of the present invention, the coating step may be performed by sequentially depositing nanoflake dispersions having different compositions of IB-, IIIA- and chalcogen-based particulates in two or more steps. For example, the method may be to first deposit a dispersion containing an indium selenide nanoflake (e.g. with an In-to-Se ratio of ˜1), and subsequently deposit a dispersion of a copper selenide nanoflake (e.g. with a Cu-to-Se ratio of ˜1) and a gallium selenide nanoflake (e.g. with a Ga-to-Se ratio of ˜1) followed optionally by depositing a dispersion of Se. This would result in a stack of three solution-based deposited layers, which may be sintered together. Alternatively, each layer may be heated or sintered before depositing the next layer. A number of different sequences are possible. For example, a layer of InxGaySez with x≧0 (larger than or equal to zero), y≧0 (larger than or equal to zero), and z≧0 (larger than or equal to zero), may be formed as described above on top of a uniform, dense layer of CuwInxGay with w≧0 (larger than or equal to zero), x≧0 (larger than or equal to zero), and y≧0 (larger than or equal to zero), and subsequently converting (sintering) the two layers into CIGS. Alternatively a layer of CuwInxGay may be formed on top of a uniform, dense layer of InxGaySez and subsequently converting (sintering) the two layers into CIGS.
In alternative embodiments, nanoflake-based dispersions as described above may further include elemental IB, and/or IIIA nanoparticles (e.g., in metallic form). These nanoparticles may be in nanoflake form, or optionally, take other shapes such as but not limited to spherical, spheroidal, oblong, cubic, or other non-planar shapes. These particles may also include emulsions, molten materials, mixtures, and the like, in addition to solids. For example CuxInyGazSeu materials, with u>0 (larger than zero), with x≧0 (larger than or equal to zero), y ≧0 (larger than or equal to zero), and z≧0 (larger than or equal to zero), may be combined with an additional source of selenium (or other chalcogen) and metallic gallium into a dispersion that is formed into a film on the substrate by sintering. Metallic gallium nanoparticles and/or nanoglobules and/or nanodroplets may be formed, e.g., by initially creating an emulsion of liquid gallium in a solution. Gallium metal or gallium metal in a solvent with or without emulsifier may be heated to liquefy the metal, which is then sonicated and/or otherwise mechanically agitated in the presence of a solvent. Agitation may be carried out either mechanically, electromagnetically, or acoustically in the presence of a solvent with or without a surfactant, dispersant, and/or emulsifier. The gallium nanoglobules and/or nanodroplets can then be manipulated in the form of a solid-particulate, by quenching in an environment either at or below room temperature to convert the liquid gallium nanoglobules into solid gallium nanoparticles. This technique is described in detail in commonly-assigned U.S. patent application Ser. No. 11/081,163 to Matthew R. Robinson and Martin R. Roscheisen entitled “Metallic Dispersion”, the entire disclosures of which are incorporated herein by reference.
Note that the method may be optimized by using, prior to, during, or after the solution deposition and/or sintering of one or more of the precursor layers, any combination of (1) any chalcogen source that can be solution-deposited, e.g. a Se or S nanopowder mixed into the precursor layers or deposited as a separate layer, (2) chalcogen (e.g., Se or S) evaporation, (3) an H2Se (H2S) atmosphere, (4) a chalcogen (e.g., Se or S) atmosphere, (5), an organo-selenium containing atmosphere, e.g. diethylselenide (6) an H2 atmosphere, (7) another reducing atmosphere, e.g. CO, (8) a wet chemical reduction step, and a (9) heat treatment.
Referring now to
Although pulsed thermal processing remains generally promising, certain implementations of the pulsed thermal processing such as a directed plasma are system, face numerous challenges. In this particular example, a directed plasma are system sufficient to provide pulsed thermal processing is an inherently cumbersome system with high operational costs. The direct plasma are system requires power at a level that makes the entire system energetically expensive and adds significant cost to the manufacturing process. The directed plasma are also exhibits long lag time between pulses and thus makes the system difficult to mate and synchronize with a continuous, roll-to-roll system. The time it takes for such a system to recharge between pulses also creates a very slow system or one that uses more than directed plasma are, which rapidly increase system costs.
In some embodiments of the present invention, other devices suitable for rapid thermal processing may be used and they include pulsed layers used in adiabatic mode for annealing (Shtyrokov E I, Sov. Phys.—i Semicond. 9 1309), continuous wave lasers (10-30W typically) (Ferris S D 1979 Laser-Solid Interactions and Laser Processing (New York: AIP)), pulsed electron beam devices (Kamins T I 1979 Appl. Phys. Leti. 35 282-5), scanning electron beam systems (McMahon R A 1979 J. Vac. Sci. Techno. 16 1840-2) (Regolini J L 1979 Appl. Phys. Lett. 34 410), other beam systems (Hodgson R T 1980 Appl. Phys. Lett. 37 187-9), graphite plate heaters (Fan J C C 1983 Mater. Res. Soc. Proc. 4 751-8) (M W Geis 1980 Appl. Phys. Lett. 37 454), lamp systems (Cohen R L 1978 Appl. Phys. Lett. 33 751-3), and scanned hydrogen flame systems (Downey D F 1982 Solid State Technol. 25 87-93). In some embodiment of the present invention, non-directed, low density system may be used. Alternatively, other known pulsed heating processes are also described in U.S. Pat. Nos. 4,350,537 and 4,356,384. Additionally, it should be understood that methods and apparatus involving pulsed electron beam processing and rapid thermal processing of solar cells as described in expired U.S. Pat. No. 3,950,187 (“Method and apparatus involving pulsed electron beam processing of semiconductor devices”) and U.S. Pat. No. 4,082,958 (“Apparatus involving pulsed electron beam processing of semiconductor devices”) are in the public domain and well known. U.S. Pat. No. 4,729,962 also describes another known method for rapid thermal processing of solar cells. The above may be applied singly or in single or multiple combinations with the above or other similar processing techniques with various embodiments of the present invention.
It should be noted that using nanoflakes typically results in precursor layers that sinter into a solid layer at temperatures as much as 50° C. lower than a corresponding layer of spherical nanoparticles. This is due in part because of the greater surface area contact between particles.
In certain embodiments of the invention, the precursor layer 106 (or any of its sub-layers) may be annealed, either sequentially or simultaneously. Such annealing may be accomplished by rapid heating of the substrate 102 and precursor layer 106 from an ambient temperature to a plateau temperature range of between about 200° C. and about 600° C. The temperature is maintained in the plateau range for a period of time ranging between about a fraction of a second to about 60 minutes, and subsequently reduced. Alternatively, the annealing temperature could be modulated to oscillate within a temperature range without being maintained at a particular plateau temperature. This technique (referred to herein as rapid thermal annealing or RTA) is particularly suitable for forming photovoltaic active layers (sometimes called “absorber” layers) on metal foil substrates, such as but not limited to aluminum foil. Other suitable substrates include but are not limited to other metals such as Stainless Steel, Copper, Titanium, or Molybdenum, metallized plastic foils, glass, ceramic films, and mixtures, alloys, and blends of these and similar or related materials. The substrate may be flexible, such as the form of a foil, or rigid, such as the form of a plate, or combinations of these forms. Additional details of this technique are described in U.S. patent application Ser. No. 10/943,685, which is incorporated herein by reference.
The atmosphere associated with the annealing step may also be varied. In one embodiment, the suitable atmosphere comprises a hydrogen atmosphere. However, in other embodiments where very low or no amounts of oxygen are found in the nanoflakes, the suitable atmosphere may be a nitrogen atmosphere, an argon atmosphere, a carbon monoxide atmosphere, or an atmosphere having less than about 10% hydrogen. These other atmospheres may be advantageous to enable and improve material handling during production.
Referring now to
Nanoflakes
Referring now to
As seen in
Referring still to
As seen in
It should be understood that the nanoflakes 108 of the present invention may be formed and/or size discriminated to provide a more controlled size and shape distribution. The size distribution of nanoflakes may be such that one standard deviation from a mean length and/or width of the nanoflakes is less than about 250 nm. In another embodiment, the size distribution of nanoflakes may be such that one standard deviation from a mean length and/or width of the nanoflakes is less than about 200 nm. In another embodiment, the size distribution of nanoflakes may be such that one standard deviation from a mean length and/or width of the nanoflakes is less than about 150 nm. In another embodiment, the size distribution of nanoflakes may be such that one standard deviation from a mean length and/or width of the nanoflakes is less than about 100 nm. In another embodiment, one standard deviation from a mean length of the nanoflakes is less than about 50 nm. In yet another embodiment, one standard deviation from a mean thickness of the nanoflakes is less than about 10 nm. In another embodiment of the invention, one standard deviation from a mean thickness of the nanoflakes is less than about 5 nm. The nanoflakes each have a thickness less than about 250 nm. In another embodiment, the nanoflakes each have a thickness less than about 100 nm. In another embodiment, the nanoflakes each have a thickness less than about 50 nm. In yet another embodiment, the nanoflakes each have a thickness less than about 20 nm. In terms of their shape, the nanoflakes may have an aspect ratio of at least about 10 or more. In another embodiment, the nanoflakes have an aspect ratio of at least about 15 or more. The nanoflakes are of random planar shape and/or a random size distribution. In other embodiments, the nanoflakes are of non-random planar shape and/or a non-random size distribution.
The stoichiometric ratio of elements may vary between individual nanoflakes so long as the overall amount in all of the particles combined is at the desired or close to the desired stoichiometric ratio for the precursor layer and/or resulting dense film. According to one preferred embodiment of that process, the overall amount of elements in the resulting film has a Cu/(In+Ga) compositional range of about 0.7 to about 1.0 and a Ga/(In+Ga) compositional range of about 0.05 to about 0.30. Optionally, the Se/(In+Ga) compositional range may be about 0.00 to about 4.00 such that a later step involving use of an additional source of Se may or may not be required.
Nanoflake Formation
Referring now to
It should be understood that the milling may use beads or microbeads made of materials harder and/or having a higher mass density than the feedstock particles to transform the feedstock particles to the appropriate size and shape. In one embodiment, these beads are glass, ceramic, alumina, porcelain, silicon carbide, or tungsten carbide beads, stainless steel balls with ceramic shells, iron balls with ceramic shells, or the like to minimize contamination risk to the nanoflakes. The mill itself or parts of the mill may also have a ceramic lining or a lining of another inert material or parts of the mill may be completely ceramic or made chemically and mechanically inert to minimize contamination of the slurry containing the nanoflakes. The beads may also be sieved regularly during the process.
The ball milling may occur in an oxygen-free environment. This may involve using a mill that is sealed from the outside environment and purged of air. Milling may then occur under an inert atmosphere or other oxygen-free environment. Some embodiments may involve placing the mill inside a hood or chamber that provides the sealing for an oxygen-free environment. The process may involve drying and degassing the vehicle or choosing anhydrous, oxygen-free solvent to begin with and loading without contact to air. The oxygen-free milling may create oxygen-free nanoflakes which in turn reduces the need for a step to remove oxygen from the particles. This could significantly reduce the anneal time associated with turning the nanoflakes precursor layer into the dense film. In some embodiments, the anneal time is in the range of about 30 seconds. Related to air-free nanoflake creation (size reduction), it should be understood that the present invention may also include air-free dispersion creation, and air-free coating, storage and/or handling.
The milling may occur at a variety of temperatures. In one embodiment of the present invention, the milling occurs at room temperature. In another embodiment, the milling occurs at a cryogenic temperature such as but not limited to ≦−175° C. This may allow milling to work on particles that may be liquid or not sufficiently brittle at room temperature for size reduction. The milling may also occur at a desired milling temperature wherein all precursor particles are solids and the precursor particles have a sufficient malleability at the milling temperature to form the planar shape from the non-planar or planar starting shape. This desired temperature may be at room temperature, above room temperature, or below room temperature and/or cycle between various temperatures. In one embodiment, the milling temperature may be less than about 15 degrees C. In another embodiment, the temperature is at less than about −175 degrees C. In yet another embodiment, the milling may be cooled by liquid nitrogen which is 80 K, being −193 C. Temperature control during milling may control possible chemical reaction between solvent, dispersant, feedstock material, and/or parts of the mill. It should be understood that in addition to the aforementioned, the temperature may also vary over different time periods of the milling process. As a nonlimiting example, the milling may occur at a first temperature over an initial milling time period and proceed to other temperatures for subsequent time periods during the milling.
The milling may transform substantially all of the precursor particles into nanoflakes. In some embodiments, the milling transforms at least about 50% (by weight of all of the precursor particles) of the precursor particles into nanoflakes. In other embodiments, it is at least 50% by volume of all the precursor particles being transformed to nanoflakes. Additionally, it should be understood that the temperature can be constant or changed during milling. This may be useful to adjust the material properties of the feedstock material or partially milled material to create particles of desired shape, size, and/or composition.
Although the present invention discloses a “top down” method for forming nanoflakes, it should be understood that other techniques may also be used. For example, quenching a material from the melt on a surface such as a liquid cooling bath. Indium (and likely gallium and selenium) nanoflakes may be formed by emulsifying molten indium while agitating and quenching at the surface of a cooling bath. It should be understood that any wet chemical, dry chemical, dry physical, and/or wet physical technique to make flakes can be used with the present invention (apart from dry or wet size reduction). Thus, the present invention is not limited to wet physical top-down methods (milling), but may also include dry/wet bottom-up approaches. It should also be noted that size reduction may optionally be a multi-step process. In one nonlimiting example, this may first involve taking mm-sized chunks/pieces that are dry grinded to <100 um, subsequently milled in one, two, three, or more steps with subsequent reducing bead size to the nanoflakes.
It should be understood that the feedstock particles for use with the present invention may be prepared by a variety of methods. By way of example and not limitation, U.S. Pat. No. 5,985,691 issued to B. M. Basol et al describes a particle-based method to form a Group IB-IIIA-VIA compound film. Eberspacher and Pauls in U.S. Pat. No. 6,821,559 describe a process for making phase-stabilized precursors in the form of fine particles, such as sub-micron multinary metal particles, and multi-phase mixed-metal particles comprising at least one metal oxide. Bulent Basol in U.S. Published Patent application number 20040219730 describes a process of forming a compound film including formulating a nano-powder material with a controlled overall composition and having particles of one solid solution. Using the solid-solution approach, Gallium can be incorporated into the metallic dispersion in non-oxide form—but only with up to approximately 18 relative atomic percent (Subramanian, P. R. and Laughlin, D. E., in Binary Alloy Phase Diagrams, 2nd Edition, edited by Massalski, T. B. 1990. ASM international, Materials Park, Ohio, pp1410-1412; Hansen, M., Constitution of Binary Alloys. 1958. 2nd Edition, McGraw Hill, pp.582-584.) U.S. patent application Ser. No. 11/081,163 describes a process of forming a compound film by formulating a mixture of elemental nanoparticles composed of the IB, the IIIA, and, optionally, the VIA group of elements having a controlled overall composition. Discussion on chalcogenide powders may also be found in the following: [(1) Vervaet, A. et al., E. C. Photovoltaic Sol. Energy Conf., Proc. Int. Conf., 10th (1991), 900-3.; (2) Journal of Electronic Materials, Vol. 27, No. 5, 1998, p. 433; Ginley et al.; (3) WO 99,378,32; Ginley et al.; (4) U.S. Pat. No. 6,126,740]. These methods may be used to create feedstock to be size reduced. Others may form precursor sub-micron-sized particles ready for solution-position. All documents listed above are fully incorporated herein by reference for all purpose.
Ink Preparation
To formulate the dispersion used in the precursor layer 106, the nanoflakes 108 are mixed together and with one or more chemicals including but not limited to dispersants, surfactants, polymers, binders, cross-linking agents, emulsifiers, anti-foaming agents, dryers, solvents, fillers, extenders, thickening agents, film conditioners, anti-oxidants, flow agents, leveling agents, and corrosion inhibitors.
The inks created using the present invention may optionally include a dispersant. Some embodiments may not include any dispersants. Dispersants (also called wetting agents) are surface-active substances used to prevent particles from aggregating or flocculating, thus facilitating the suspension of solid materials in a liquid medium and stabilizing the dispersion thereby produced. If particle surfaces attract one another, then flocculation occurs, often resulting in aggregation and decreasing stability and/or homogeneity. If particle surfaces repel one another, then stabilization occurs, where particles do not aggregate and tend not to settle out of solution as fast.
An efficient dispersing agent can typically perform pigment wetting, dispersing, and stabilizing. Dispersing agents are different depending on the nature of the ink/paint. Polyphosphates, styrene-maleinates and polyacrylates are often used for aqueous formulations whereas fatty acid derivatives and low molecular weight modified alkyd and polyester resins are often used for organic formulations.
Surfactants are surface-active agents that lower the surface tension of the solvent in which they dissolve, serving as wetting agents, and keeping the surface tension of an (aqueous) medium low so that an ink interacts with a substrate surface. Certain types of Surfactants are also used as dispersing agents. Surfactants typically contain both a hydrophobic carbon chain and a hydrophilic polar group. The polar group can be non-ionic. If the polar group is ionic, the charge can be either positive or negative, resulting in cationic or anionic surfactants. Zwitterionic surfactants contain both positive and negative charges within the same molecule; one example is N-n-Dodecyl-N,N-dimethyl betaine. Certain surfactants are often used as dispersant agents for aqueous solutions. Representative classes include acetylene diols, fatty acid derivatives, phosphate esters, sodium polyacrylate salts, polyacrylic acids, soya lecithin, trioctylphosphine (TOP), and trioctylphosphine oxide (TOPO).
Binders and resins are often used to hold together proximate particles in a nascent or formed dispersion. Examples of typical binders include acrylic monomers (both as monofunctional diluents and multifunctional reactive agents), acrylic resins (e.g. acrylic polyol, amine synergists, epoxy acrylics, polyester acrylics, polyether acrylics, styrene/acrylics, urethane acrylics, or vinyl acrylics), alkyd resins (e.g. long-oil, medium-oil, short-oil, or tall oil), adhesion promoters such as but not limited to polyvinyl pyrrolidone (PVP), amide resins, amino resins (such as but not limited to melamine-based or urea-based compounds), asphalt/bitumen, butadiene acrylonitriles, cellulosic resins (such as but not limited to cellulose acetate butyrate (CAB)), cellulose acetate proprionate (CAP), ethyl cellulose (EC), nitrocellulose (NC), or organic cellulose ester), chlorinated rubber, dimer fatty acids, epoxy resin (e.g. acrylates, bisphenol A-based resins, epoxy UV curing resins, esters, phenol and cresol (Novolacs), or phenoxy-based compounds), ethylene co-terpolymers such as ethylene acrylic/methacrylic Acid, E/AA, E/M/AA or ethylene vinyl acetate (EVA), fluoropolymers, gelatin (e.g. Pluronic F-68 from BASF Corporation of Florham Park, N.J.), glycol monomers, hydrocarbon resins (e.g. aliphatic, aromatic, or coumarone-based such as indene), maelic resins, modified urea, natural rubber, natural resins and gums, rosins, modified phenolic resins, resols, polyamide, polybutadienes (liquid hydroxyl-terminated), polyesters (both saturated and unsaturated), polyolefins, polyurethane (PU) isocyanates (e.g. hexamethylene diisocynate (HDI), isophorone diisocyanate (IPDI), cycloaliphatics, diphenylmethane disiocyanate (MDI), toluene diisocynate (TDI), or trimethylhexamethylene diisocynate (TMDI)), polyurethane (PU) polyols (e.g. caprolactone, dimer-based polyesters, polyester, or polyether), polyurethane (PU) dispersions (PUDs) such those based on polyesters or polyethers, polyurethane prepolymers (e.g. caprolactone, dimer-based polyesters, polyesters, polyethers, and compounds based on urethane acrylate), Polyurethane thermoplastics (TPU) such as polyester or polyether, silicates (e.g. alkyl-silicates or water-glass based compounds), silicones (amine functional, epoxy functional, ethoxy functional, hydroxyl functional, methoxy functional, silanol functional, or cinyl functional), styrenes (e.g. styrene-butadiene emulsions, and styrene/vinyl toluene polymers and copolymers), or vinyl compounds (e.g. polyolefins and polyolefin derivatives, polystyrene and styrene copolymers, or polyvinyl acetate (PVAC)).
Emulsifiers are dispersing agents that blend liquids with other liquids by promoting the breakup of aggregating materials into small droplets and therefore stabilize the suspension in solution. For example, sorbitan esters are used as an emulsifier for the preparation of water-in-oil (w/o) emulsions, for the preparation of oil absorption bases (w/o), for the formation of w/o type pomades, as a reabsorption agent, and as a non toxic anti-foaming agent. Examples of emulsifiers are sorbitan esters such as sorbitan sesquioleate (Arlacel 60), sorbitan sesquioleate (Arlacel 83), sorbitan monolaurate (Span 20), sorbitan monopalmitate (Span 40), sorbitan monostearate (Span 60), sorbitan tristearate (Span 65), sorbitan mono-oleate (Span 80), and sorbitan trioleate (Span 85) all of which are available, e.g., from Uniqema of New Castle, Del. Other polymeric emulsifiers include polyoxyethylene monostearate (Myrj 45), polyoxyethylene monostearate (Myrj 49), polyoxyl 40 stearate (Myrj 52), polyoxyethylene monolaurate (PEG 400), polyoxyethylene monooleate (PEG 400 monoleate) and polyoxyethylene monostearate (PEG 400 monostearate), and the Tween series of surfactants including but not limited to polyoxyethylene sorbitan monolaurate (Tween 20), polyoxyethylene sorbitan monolaurate (Tween 21), polyoxyethylene sorbitan monopalmitate (Tween 40), polyoxyethylene sorbitan monostearate (Tween 60), polyoxyethylene sorbitan tristearate (Tween 61), polyoxyethylene sorbitan mono-oleate (Tween 80), polyoxyethylene sorbitan monooleate (Tween 81), and polyoxyethylene sorbitan tri-oleate (Tween 85) all of which are available, e.g., from Uniqema of New Castle, Del. Arlacel, Myrj, and Tween are registered trademarks of ICI Americas Inc. of Wilmington, Del.
Foam may form from the release of various Ga—Ses during the coating/printing process, especially if the printing process takes place at high speeds. Surfactants may adsorb on the liquid-air interface and stabilize it, accelerating foam formation. Anti-foaming agents prevent foaming from being initiated, while defoaming agents minimize or eliminate previously-formed foam. Anti-foaming agents include hydrophobic solids, fatty oils, and certain surfactants, all of which penetrate the liquid-air interface to slow foam formation. Anti-foaming agents also include both silicate, silicone and silicone-free materials. Silicone-free materials include microcrystalline wax, mineral oil, polymeric materials, and silica- and surfactant-based materials.
Solvents can be aqueous (water-based) or non-aqueous (organic). While environmentally friendly, water-based solutions carry the disadvantage of a relatively higher surface tension than organic solvents, making it more difficult to wet substrates, especially plastic substrates. To improve substrate wetting with polymer substrates, surfactants may be added to lower the ink surface tension (while minimizing surfactant-stabilized foaming), while the substrate surfaces are modified to enhance their surface energy (e.g. by corona treatment). Typical organic solvents include acetate, acrylates, alcohols (butyl, ethyl, isopropyl, or methyl), aldehydes, benzene, dibromomethane, chloroform, dichloromethane, dichloroethane, trichloroethane, cyclic compounds (e.g. cyclopentanone or cyclohexanone), esters (e.g. butyl acetate or ethyl acetate), ethers, glycols (such as ethylene glycol or propylene glycol), hexane, heptane, aliphatic hydrocarbons, aromatic hydrocarbons, ketones (e.g. acetone, methyl ethyl ketone, or methyl isobutyl ketone), natural oils, terpenes, terpinol, toluene.
Additional components may include fillers/extenders, thickening agents, rheology modifiers, surface conditioners, including adhesion promoters/bonding, anti-gelling agents, anti-blocking agents, antistatic agents, chelating/complexing agents, corrosion inhibitors, flame/rust inhibitors, flame and fire retardants, humectants, heat stabilizers, light-stabilizers/UV absorbers, lubricants, pH stabilizers, and materials for slip control, anti-oxidants, and flow and leveling agents. It should be understood that all components may be added singly or in combination with other components.
Roll-to-Roll Manufacturing
Referring now to
Photovoltaic Device
Referring now to
The n-type semiconductor thin film 308 serves as ajunction partner between the compound film and the transparent conducting layer 309. By way of example, the n-type semiconductor thin film 308 (sometimes referred to as a junction partner layer) may include inorganic materials such as cadmium sulfide (CdS), zinc sulfide (ZnS), zinc hydroxide, zinc selenide (ZnSe), n-type organic materials, or some combination of two or more of these or similar materials, or organic materials such as n-type polymers and/or small molecules Layers of these materials may be deposited, e.g., by chemical bath deposition (CBD) and/or chemical surface deposition (and/or related methods), to a thickness ranging from about 2 nm to about 1000 nm, more preferably from about 5 nm to about 500 nm, and most preferably from about 10 nm to about 300 nm. This may also configured for use in a continuous roll-to-roll and/or segmented roll-to-roll and/or a batch mode system.
The transparent conductive layer 309 may be inorganic, e.g., a transparent conductive oxide (TCO) such as but not limited to indium tin oxide (ITO), fluorinated indium tin oxide, zinc oxide (ZnO) or aluminum doped zinc oxide, or a related material, which can be deposited using any of a variety of means including but not limited to sputtering, evaporation, CBD, electroplating, sol-gel based coating, spray coating, chemical vapor deposition (CVD), physical vapor deposition (PVD), atomic layer deposition (ALD), and the like. Alternatively, the transparent conductive layer may include a transparent conductive polymeric layer, e.g. a transparent layer of doped PEDOT (Poly-3,4-Ethylenedioxythiophene), carbon nanotubes or related structures, or other transparent organic materials, either singly or in combination, which can be deposited using spin, dip, or spray coating, and the like or using any of various vapor deposition techniques. Combinations of inorganic and organic materials can also be used to form a hybrid transparent conductive layer. Thus, the layer 309 may optionally be an organic (polymeric or a mixed polymeric-molecular) or a hybrid (organic-inorganic). Examples of such a transparent conductive layer are described e.g., in commonly-assigned US Patent Application Publication Number 20040187917, which is incorporated herein by reference.
Those of skill in the art will be able to devise variations on the above embodiments that are within the scope of these teachings. For example, it is noted that in embodiments of the present invention, portions of the IB-IIIA precursor layers (or certain sub-layers of the precursor layers or other layers in the stack) may be deposited using techniques other than nanoflake-based inks. For example precursor layers or constituent sub-layers may be deposited using any of a variety of alternative deposition techniques including but not limited to solution-deposition of spherical nanopowder-based inks, vapor deposition techniques such as ALD, evaporation, sputtering, CVD, PVD, electroplating and the like.
Referring now to
Referring now to
Extra Source of Chalcogen
It should be understood that the present invention using nanoflakes may also use an extra chalcogen source in a manner similar to that described in copending, U.S. patent application Ser. No. 11/290,633 , wherein the precursor material contains 1) chalcogenides such as, but not limited to, copper selenide, and/or indium selenide and/or gallium selenide and/or 2) a source of extra chalcogen such as, but not limited to, Se or S nanoparticles less than about 200 nanometers in size. In one nonlimiting example, the chalcogenide and/or the extra chalcogen may be in the form of nanoflakes and/or nanoflakes while the extra source of chalcogen may be flakes and/or non-flakes. The chalcogenide nanoflakes may be one or more binary alloy chalcogenides such as, but not limited to, group IB-binary chalcogenide nanoparticles (e.g. group IB non-oxide chalcogenides, such as Cu—Se, CuS or CuTe) and/or group IIIA-chalcogenide nanoparticles (e.g., group IIIA non-oxide chalcogenides, such as Ga(Se, S, Te), In(Se, S, Te) and Al(Se, S, Te). In other embodiments, the nanoflakes may be non-chalcogenides such as but not limited to group IB and/or IIIA materials like CuIn, CuGa, and/or InGa. If the chalcogen melts at a relatively low temperature (e.g., 220° C. for Se, 120° C. for S) the chalcogen is already in a liquid state and makes good contact with the nanoflakes. If the nanoflakes and chalcogen are then heated sufficiently (e.g., at about 375° C.), the chalcogen reacts with the chalcogenides to form the desired IB-IIIA-chalcogenide material.
Referring now to
Although not limited to the following, the chalcogenide particles 502 may be obtained starting from a binary chalcogenide feedstock material, e.g., micron size particles or larger. Examples of chalcogenide materials available commercially are listed in Table I below.
Examples of chalcogen powders and other feedstocks commercially available are listed in Table II below.
Printing A Layer of the Extra Source of Chalcogen
Referring now to
In one embodiment of the present invention, the precursor layer 606 may be between about 4.0 to about 0.5 microns thick. The layer 608 containing chalcogen particles 607 may have a thickness in the range of about 4.0 microns to about 0.5 microns. The chalcogen particles 607 in the layer 608 may be between about 1 nanometer and about 25 microns in size, preferably between about 25 nanometers and about 300 nanometers in size. It is noted that the chalcogen particles 607 may be initially larger than the final thickness of the IB-IIIA-VIA compound film 610. The chalcogen particles 607 may be mixed with solvents, carriers, dispersants etc. to prepare an ink or a paste that is suitable for wet deposition over the precursor layer 606 to form the layer 608. Alternatively, the chalcogen particles 607 may be prepared for deposition on a substrate through dry processes to form the layer 608. It is also noted that the heating of the layer 608 containing chalcogen particles 607 may be carried out by an RTA process, e.g., as described above.
The chalcogen particles 607 (e.g., Se or S) may be formed in several different ways. For example, Se or S particles may be formed starting with a commercially available fine mesh powder (e.g., 200 mesh/75 micron) and ball milling the powder to a desirable size. A typical ball milling procedure may use a ceramic milling jar filled with grinding ceramic balls and a feedstock material, which may be in the form of a powder, in a liquid medium. When the jar is rotated or shaken, the balls shake and grind the powder in the liquid medium to reduce the size of the particles of the feedstock material. Optionally, the process may include dry (pre-) grinding of bigger pieces of material such as but not limited to Se. The dry-grinding may use pieces 2-6 mm and smaller, but it would be able to handle bigger pieces as well. Note that this is true for all size reductions where the process may start with bigger feedstock materials, dry grinding, and subsequently starting wet grinding (such as but not limited to ball milling). The mill itself may range from a small media mill to a horizontal rotating ceramic jar.
Referring now to
Optionally, it should be understood that the extra source of chalcogen may be mixed with and/or deposited within the precursor layer, instead of as a discrete layer. In one embodiment of the present invention, oxygen-free particles or substantially oxygen free particles of chalcogen could be used. If the chalcogen is used with microflakes and/or plate shaped precursor materials, densification might not end up an issue due to the higher density achieved by using planar particles, so there is no reason to exclude printing Se and/or other source of chalcogen within the precursor layer as opposed to a discrete layer. This may involve not having to heat the precursor layer to the previous processing temperatures. In some embodiments, this may involve forming the film without heating above about 400° C. In some embodiments, this may involve not having to heat above about 300° C.
In still other embodiments of the present invention, multiple layers of material may be printed and reacted with chalcogen before deposition of the next layer. One nonlimiting example would be to deposit a Cu—In—Ga layer, anneal it, then deposit an Se layer then treat that with RTA, follow that up by depositing another precursor layer rich in Ga, followed by another deposition of Se, and finished by a second RTA treatment. More generically, this may include forming a precursor layer (either heat or not) then coating a layer of the extra source of chalcogen (then heat or not) then form another layer of more precursor (heat or not) and then for another layer of the extra source of chalcogen (then heat or not) and repeat as many times as desired to grade the composition or nucleating desired crystal sizes. In one nonlimiting example, this may be used to grade the gallium concentration. In another embodiment, this may be used to grade the copper concentration. In yet another embodiment, this may be used to grade the indium concentration. In a still further embodiment, this may be used to grade the selenium concentration. In yet another embodiment this may be used to grade the selenium concentration. Another reason would be to first grow copper rich films to get big crystals and then to start adding copper-poor layers to get the stoichiometry back. Of course this embodiment can combined to allow the chalcogen to be deposited in the precursor layer for any of the steps involved.
Referring now to
Chalcogen-rich Chalcogenide Particles
Referring now to
The purpose of providing an extra source of chalcogen is to first create liquid to enlarge the contact area between the initial solid particles (flakes) and the liquid. Secondly, when working with chalcogen-poor films, the extra source adds chalcogen to get to the stoichiometric desired chalcogen amount. Third, chalcogens such as Se are volatile and inevitably some is lost during processing. So, main purpose is to create liquid. There are also a variety of other routes to increase the amount of liquid when the precursor layer is processed. These routes include but are not limited to: 1) Cu—Se more Se-rich than Cu2-xSe (>377° C., even more liquid above >523° C.); 2) Cu—Se equal to or more Se-rich than Cu2Se when adding additional Se (>220° C.); 3) In—Se of composition In4Se3, or in between In4Se3 and In1Se1, (>550° C.); 4) In—Se equal to or more Se-rich than In4Se3 when adding additional Se (>220° C.); 5) In—Se in between In and In4Se3 (>156° C., preferably in an oxygen-free environment since In is created 6) Ga-emulsion (>29° C., preferably oxygen-free); and hardly (but possible) for Ga—Se. Even when working with Se vapor, it still would be tremendously advantageous to create additional liquid in the precursor layer itself using one of the above methods or by a comparable method.
Referring now to
Referring still to
Referring now to
The amount of extra chalcogen provided by all of the particles overall is at a level that is equal to or above the stoichiometric level found in the compound after processing. In one embodiment of the present invention, the excess amount of chalcogen comprises an amount greater than the sum of 1) a stoichiometric amount found in the final IB-IIIA-chalcogenide film and 2) a minimum amount of chalcogen necessary to account for losses during processing to form the final IB-IIIA-chalcogenide having the desired stoichiometric ratio. Although not limited to the following, the excess chalcogen may act as a flux that will liquefy at the processing temperature and promote greater atomic intermixing of particles provided by the liquefied excess chalcogen. The liquefied excess chalcogen may also ensure that sufficient chalcogen is present to react with the group IB and IIIA elements. The excess chalcogen helps to “digest” or “solubilize” the particles or flakes. The excess chalcogen will escape from the layer before the desired film is fully formed.
Referring now to
It should be understood that a variety of chalcogenide particles may also be combined with non-chalcogenide particles to arrive at the desired excess supply of chalcogen in the precursor layer. The following table (Table IV) provides a non-limiting matrix of some of the possible combinations between chalcogenide particles listed in the rows and the non-chalcogenide particles listed in the columns.
In yet another embodiment, the present invention may combine a variety of chalcogenide particles with other chalcogenide particles. The following table (Table V) provides a non-limiting matrix of some of the possible combinations between chalcogenide particles listed for the rows and chalcogenide particles listed for the columns.
Nucleation Layer
Referring now to
As shown in
Referring now to
Referring still to
Nucleation Layer by Thermal Gradient
Referring now to
As seen in
As seen in
After the nucleation layer has formed, preferably consisting of material identical or close to the final IB-IIIA-chalcogenide compound, the entire precursor layer, or optionally only those portions of the precursor layer that remain more or less unprocessed, will be heated to the processing temperature so that the remaining material will begin to convert into the final IB-IIIA-chalcogenide compound in contact with the nucleation layer. The nucleation layer guides the crystal formation and minimizes the possibility of areas of the substrate forming pinhole or having other abnormalities due to uneven crystal formation.
It should be understood that in addition to the aforementioned, the temperature may also vary over different time periods of precursor layer processing. As a nonlimiting example, the heating may occur at a first temperature over an initial processing time period and proceed to other temperatures for subsequent time periods of the processing. Optionally, the method may include intentionally creating one or more temperature dips so that, as a nonlimiting example, the method comprises heating, cooling, heating, and subsequent cooling. In one embodiment of the present invention, this may involve lowering the temperature from between about 50° C. to about 200° C. from a temperature in an initial time period.
Nucleation Layer by Chemical Gradient
Referring now to
Referring now to
As shown in
Referring now to
The rationale behind the use of chalcogen grading, or more general a grading in melting temperature from bottom to top, is to control the relative rate of crystallization in depth and to have the crystallization happen e.g. faster at the bottom portion of the stack of precursor layers than at the top of the stack of precursor layers. The additional rationale is that the common grain structure in typical efficient solution-deposited CIGS cells where the cells have large grains at the top of the photoactive film, which is the part of the photoactive film that is mainly photoactive, and small grains at the back, still have appreciable power conversion efficiencies. It should be understood that in other embodiments, a plurality of many layers of different precursor materials may be used to build up a desired gradient of chalcogen, or more general, a desired gradient in melting temperature and/or subsequent solidification into the final IB-IIIA-chalcogenide compound, or even more general, a desired gradient in melting and/or subsequent solidification into the final IB-IIIA-chalcogenide compound, either due to creating a chemical (compositional) gradient, and/or a thermal gradient, in the resulting film. As nonlimiting examples, the present invention may use particles and/or microflakes and/or nanoflakes with different melting points such as but not limited to lower melting materials Se, In4Se3, Ga, and Cu1Se1, compared to higher melting materials In2Se3, Cu2Se.
Referring now to
Optionally, as shown in
Optionally, as shown in
Referring still to
Optionally, in a second method, sodium may also be introduced into the stack by sodium doping the nanoflakes and/or particles in the precursor layer 916. As a nonlimiting example, the nanoflakes and/or other particles in the precursor layer 916 may be a sodium containing material such as, but not limited to, Cu—Na, In—Na, Ga—Na, Cu—In—Na, Cu—Ga—Na, In—Ga—Na, Na—Se, Cu—Se—Na, In—Se—Na, Ga—Se—Na, Cu—In—Se—Na, Cu—Ga—Se—Na, In—Ga—Se—Na, Cu—In—Ga—Se—Na, Na—S, Cu—S—Na, In—S—Na, Ga—S—Na, Cu—In—S—Na, Cu—Ga—S—Na, In—Ga—S—Na, and/or Cu—In—Ga—S—Na. In one embodiment of the present invention, the amount of sodium in the nanoflakes and/or other particles may be less than about 1 at. % or less. In another embodiment, the amount of sodium may be about 0.5 at. % or less. In yet another embodiment, the amount of sodium may be about 0.1 at. % or less. It should be understood that the doped particles and/or flakes may be made by a variety of methods including milling feedstock material with the sodium containing material and/or elemental sodium.
Optionally, in a third method, sodium may be incorporated into the ink itself, regardless of the type of particle, nanoparticle, microflake, and/or nanoflakes dispersed in the ink. As a nonlimiting example, the ink may include nanoflakes (Na doped or undoped) and a sodium compound with an organic counter-ion (such as but not limited to sodium acetate) and/or a sodium compound with an inorganic counter-ion (such as but not limited to sodium sulfide). It should be understood that sodium compounds added into the ink (as a separate compound), might be present as particles (e.g. nanoparticles), or dissolved. The sodium may be in “aggregate” form of the sodium compound (e.g. dispersed particles), and the “molecularly dissolved” form.
None of the three aforementioned methods are mutually exclusive and may be applied singly or in any single or multiple combination to provide the desired amount of sodium to the stack containing the precursor material. Additionally, sodium and/or a sodium containing compound may also be added to the substrate (e.g. into the molybdenum target). Also, sodium-containing layers may be formed in between one or more precursor layers if multiple precursor layer (using the same or different materials) are used. It should also be understood that the source of the sodium is not limited to those materials previously listed. As a nonlimiting example, basically, any deprotonated alcohol where the proton is replaced by sodium, any deprotonated organic and inorganic acid, the sodium salt of the (deprotonated) acid, sodium hydroxide, sodium acetate, and the sodium salts of the following acids: butanoic acid, hexanoic acid, octanoic acid, decanoic acid, dodecanoic acid, tetradecanoic acid, hexadecanoic acid, 9-hexadecanoic acid, octadecanoic acid, 9-octadecenoic acid, 11-octadecenoic acid, 9,12-octadecadienoic acid, 9,12,15-octadecatrienoic acid, and/or 6,9,12-octadecatrienoic acid.
Optionally, as seen in
Additionally, the sodium material may be combined with other elements that can provide a bandgap widening effect. Two elements which would achieve this include gallium and sulfur. The use of one or more of these elements, in addition to sodium, may further improve the quality of the absorber layer. The use of a sodium compound such as but not limited to Na2S, NaInS2, or the like provides both Na and S to the film and could be driven in with an anneal such as but not limited to an RTA step to provide a layer with a bandgap different from the bandgap of the unmodified CIGS layer or film.
Referring now to
The total number of printing steps can be modified to construct absorber layers with bandgaps of differential gradation. For example, additional layers (fourth, fifth, sixth, and so forth) can be printed (and optionally annealed between printing steps) to create an even more finely-graded bandgap within the absorber layer. Alternatively, fewer films (e.g. double printing) can also be printed to create a less finely-graded bandgap. For any of the above embodiments, it is possible to have different amounts of chalcogen in each layer as well to vary crystal growth that may be influenced by the amount of chalcogen present.
Additionally, it should be understood that any number of combinations of flake and non-flake particles may be used according to the present invention in the various layers. As a nonlimiting example, the combinations may include but are not limited to:
Although not limited to the following, the chalcogenide and non-chalcogenide materials may be selected from any of those listed in the Tables IV and V.
Reduced Melting Temperature
In yet another embodiment of the present invention, the ratio of elements within a particle or flake may be varied to produce more desired material properties. In one nonlimiting example, this embodiment comprises using desired stoichiometric ratios of elements so that the particles used in the ink have a reduced melting temperature. By way of nonlimiting example, for a group IB chalcogenide, the amount of the group IB element and the amount of the chalcogen is controlled to move the resulting material to a portion of the phase diagram that has a reduced melting temperature. Thus for CuxSey, the values for x and y are selected to create a material with reduced melting temperature as determined by reference to a phase diagram for the material. Phase diagrams for the following materials may be found in ASM Handbook, Volume 3 Alloy Phase Diagrams (1992) by ASM International and fully incorporated herein by reference for all purposes. Some specific examples may be found on pages 2-168, 2-170, 2-176, 2-178, 2-208, 2-214, 2-257, and/or 2-259.
As a nonlimiting example, copper selenide has multiple melting temperatures depending on the ratio of copper to selenium in the material. Everything more Se-rich (i.e. right on the binary phase diagram with pure Cu on the left and pure Se on the right) of the solid-solution Cu2-xSe will create liquid selenium. Depending on composition, the melting temperature may be as low as 221° C. (more Se rich than Cu1Se2), as low as 332° C. (for compositions between Cu1Se1 & Cu1Se2), and as low as 377° C. (for compositions between Cu2-xSe and Cu1Se1). At 523° C. and above, the material is all liquid for Cu—Se that is more Se-rich than the eutectic (˜57.9 wt.-% Se). For compositions in between the solid-solution Cu2-xSe and the eutectic (˜57.9 wt.-% Se), it will create a solid solid-solution Cu2-xSe and liquid eutectic (˜57.9wt.-% Se) at 523° C. and just above.
Another nonlimiting example involves gallium selenide which may have multiple melting temperatures depending on the ratio of gallium to selenium in the material. Everything more Se-rich (i.e. right on the binary phase diagram with pure Ga on the left and pure Se on the right) than Ga2Se3 will create liquid above 220° C., which is mainly pure Se. Making Ga—Se more Se-rich than Ga1Se1 is possible by making e.g. the compound Ga2Se3 (or anything more Se-rich than Ga1Se1), but only when adding other sources of selenium when working with a composition in between or equal to Ga1Se1 and Ga2Se3 (being an additional source of selenium or Se-rich Cu—Se) will liquefy the Ga—Se at processing temperature. Hence, an additional source of Se may be provided to facilitate the creation of a liquid involving gallium selenide.
Yet another nonlimiting example involves indium selenide which may have multiple melting temperatures depending on the ratio of indium to selenium in the material. Everything more Se-rich (i.e. right on the binary phase diagram with pure In on the left and pure Se on the right) than In2Se3 will create liquid above 220° C., which is mainly pure Se. Making In—Se more Se-rich than In1Se1 would create liquid for In2Se3 and also for In6Se7 (or a bulk composition in between In1Se1 and Se), but when dealing with a composition between or equal to In1Se1 and In2Se3, only by adding other sources of selenium (being an additional source of selenium or Se-rich Cu—Se) the In—se will liquefy at processing temperature. Optionally for In—Se, there is another way of creating more liquid by going in the “other” direction and using compositions that are less Se-rich (i.e. left on the binary phase diagram). By using a material composition between pure In and In4Se3 (or between In and In1,Se1 or between In and In6Se7 depending on temperature), pure liquid In can be created at 156° C. and even more liquid at 520° C. (or at a higher temperature when going more Se-rich moving from the eutectic point of ˜24.0 wt.-% Se up to In1Se1). Basically, for a bulk composition less Se-rich than the In—Se eutectic (˜24.0 wt.-% Se), all the In—Se will turn into a liquid at 520° C. Of course, with these type of Se poor materials, one of the other particles (such as but not limited to Cu1Se2 and/or Se) will be needed to increase the Se content, or another source of Se.
Accordingly, liquid may be created at our processing temperature by: 1) adding a separate source of selenium, 2) using Cu—Se more Se-rich than Cu2-xSe, 3) using Ga-emulsion (or In—Ga emulsion), or In (in an air free environment), or 4) using In—Se less Se-rich than In1Se1 though this may also require an air free environment. When copper selenide is used, the composition may be CuxSey, wherein x is in the range of about 2 to about 1 and y is in the range of about 1 to about 2. When indium selenide is used, the composition may be InxSey, wherein x is in the range of about 1 to about 6 and y is in the range of about 0 to about 7. When gallium selenide is used, the composition may be GaxSey, wherein x is in the range of about 1 to about 2 and y is in the range of about 1 to about 3.
It should be understood that adding a separate source of selenium will make the composition behave initially as more Se-rich at the interface of the selenide particle and the liquid selenium at the processing temperature.
Chalcogen Vapor Environment
Referring now to
Referring now to
Referring now to
Referring now to
While the invention has been described and illustrated with reference to certain particular embodiments thereof, those skilled in the art will appreciate that various adaptations, changes, modifications, substitutions, deletions, or additions of procedures and protocols may be made without departing from the spirit and scope of the invention. For example, with any of the above embodiments, nanoflakes may be replaced by and/or mixed with microflakes wherein the lengths and/or largest lateral dimension of the planar microflakes are about 500 nm or larger. The microflakes may each have a length less than about 5 microns and greater than about 500 mn. The microflakes may each have a length between about 3 microns and about 500 nm. The particles may be microflakes having lengths of greater than 500 nm. The particles may be microflakes having lengths of greater than 750 nm. The microflakes may each have a thickness of about 100 nm or less. The particles may be microflakes having thicknesses of about 75 nm or less. The particles may be microflakes having thicknesses of about 50 nm or less. The microflakes may each have a thickness less than about 20 nm. The microflakes may have lengths of less than about 2 microns and thicknesses of less than 100 nm. The microflakes may have lengths of less than about 1 microns and a thicknesses of less than 50 nm. The microflakes may have an aspect ratio of at least about 10 or more. The microflakes have an aspect ratio of at least about 15 or more.
As mentioned, some embodiments of the invention may include both nanoflakes and microflakes. Other may include flakes that are exclusively in the size range of nanoflakes or the size range of microflakes. With any of the above embodiments, the microflakes may be replaced by microrods which are substantially linear, elongate members. With any of the above embodiments, the nanoflakes may be replaced by nanorods which are substantially linear, elongate members. Still further embodiments may combine nanorods with nanoflakes in the precursor layer. Any of the above embodiments may be used on rigid substrate, flexible substrate, or a combinations of the two such as but not limited to a flexible substrate that become rigid during processing due to its material properties. In one embodiment of the present invention, the particles may be plates and/or discs and/or flakes and/or wires and/or rods of micro-sized proportions. In another embodiment of the present invention, the particles may be nanoplates and/or nanodiscs and/or nanoflakes and/or nanowires and/or nanorods of nano-sized proportions.
For any of the above embodiments, it should be understood that in addition to the aforementioned, the temperature may also vary over different time periods of precursor layer processing. As a nonlimiting example, the heating may occur at a first temperature over an initial processing time period and proceed to other temperatures for subsequent time periods of the processing. Optionally, the method may include intentionally creating one or more temperature dips so that, as a nonlimiting example, the method comprises heating, cooling, heating, and subsequent cooling. For any of the above embodiments, it is also possible to have two or more elements of IB elements in the chalcogenide particle and/or the resulting film.
Additionally, concentrations, amounts, and other numerical data may be presented herein in a range format. It is to be understood that such range format is used merely for convenience and brevity and should be interpreted flexibly to include not only the numerical values explicitly recited as the limits of the range, but also to include all the individual numerical values or sub-ranges encompassed within that range as if each numerical value and sub-range is explicitly recited. For example, a size range of about 1 nm to about 200 nm should be interpreted to include not only the explicitly recited limits of about 1 nm and about 200 nm, but also to include individual sizes such as 2 nm, 3 nm, 4 nm, and sub-ranges such as 10 nm to 50 nm, 20 nm to 100 nm, etc. . . .
The publications discussed or cited herein are provided solely for their disclosure prior to the filing date of the present application. Nothing herein is to be construed as an admission that the present invention is not entitled to antedate such publication by virtue of prior invention. Further, the dates of publication provided may be different from the actual publication dates which may need to be independently confirmed. All publications mentioned herein are incorporated herein by reference to disclose and describe the structures and/or methods in connection with which the publications are cited. The following related applications are fully incorporated herein by reference for all purposes: U.S. patent application Ser. No. 11/361,522, U.S. patent application Ser. No. 11/361,498, U.S. patent application Ser. No. 11/361,433, U.S. patent application Ser. No. 11/361,521, U.S. patent application Ser. No. 11/361,497, U.S. patent application Ser. No. 11/361,515, U.S. patent application Ser. No. 11/361,464, U.S. patent application Ser. No. 11/361,523, and U.S. patent application Ser. No. 11/361,103, all filed on Feb. 23, 2006. The following applications are also incorporated herein by reference for all purposes: U.S. patent application Ser. No. 11/290,633 entitled “CHALCOGENIDE SOLAR CELLS” filed Nov. 29, 2005, U.S. patent application Ser. No. 10/782,017, entitled “SOLUTION-BASED FABRICATION OF PHOTOVOLTAIC CELL” filed Feb. 19, 2004, U.S. patent application Ser. No. 10/943,657, entitled “COATED NANOPARTICLES AND QUANTUM DOTS FOR SOLUTION-BASED FABRICATION OF PHOTOVOLTAIC CELLS” filed Sep. 18, 2004, and U.S. patent application Ser. No. 11/081,163, entitled “METALLIC DISPERSION”, filed Mar. 16, 2005, and U.S. patent application Ser. No. 10/943,685, entitled “FORMATION OF CIGS ABSORBER LAYERS ON FOIL SUBSTRATES”, filed Sept. 18, 2004, the entire disclosures of which are incorporated herein by reference.
While the above is a complete description of the preferred embodiment of the present invention, it is possible to use various alternatives, modifications and equivalents. Therefore, the scope of the present invention should be determined not with reference to the above description but should, instead, be determined with reference to the appended claims, along with their full scope of equivalents. Any feature, whether preferred or not, may be combined with any other feature, whether preferred or not. In the claims that follow, the indefinite article “A”, or “An” refers to a quantity of one or more of the item following the article, except where expressly stated otherwise. The appended claims are not to be interpreted as including means-plus-function limitations, unless such a limitation is explicitly recited in a given claim using the phrase “means for.”
This application is a continuation-in-part of commonly-assigned, co-pending application Ser. No. 11/290,633 entitled “CHALCOGENIDE SOLAR CELLS” filed Nov. 29, 2005 and Ser. No. 10/782,017, entitled “SOLUTION-BASED FABRICATION OF PHOTOVOLTAIC CELL” filed Feb. 19, 2004 and published as U.S. patent application publication 20050183767, the entire disclosures of which are incorporated herein by reference. This application is also a continuation-in-part of commonly-assigned, U.S. patent application Ser. No. 10/943,657, entitled “COATED NANOPARTICLES AND QUANTUM DOTS FOR SOLUTION-BASED FABRICATION OF PHOTOVOLTAIC CELLS” filed Sep. 18, 2004now U.S. Pat. No. 7,306,823, the entire disclosures of which are incorporated herein by reference. This application is a also continuation-in-part of commonly-assigned, co-pending U.S. patent application Ser. No. 11/081,163, entitled “METALLIC DISPERSION”, filed Mar. 16, 2005, the entire disclosures of which are incorporated herein by reference. This application is a also continuation-in-part of commonly-assigned, co-pending U.S. patent application Ser. No. 10/943,685, entitled “FORMATION OF CIGS ABSORBER LAYERS ON FOIL SUBSTRATES”, filed Sep. 18, 2004, the entire disclosures of which are incorporated herein by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3423301 | Sterns | Jan 1969 | A |
| 3586541 | Chamberlin | Jun 1971 | A |
| 3966568 | Crossley et al. | Jun 1976 | A |
| 4191794 | Shirland et al. | Mar 1980 | A |
| 4192721 | Fawcett et al. | Mar 1980 | A |
| 4404422 | Green et al. | Sep 1983 | A |
| 4522663 | Ovshinsky et al. | Jun 1985 | A |
| 4536607 | Wiesmann | Aug 1985 | A |
| 4622432 | Yamazaki | Nov 1986 | A |
| 4642140 | Noufi et al. | Feb 1987 | A |
| 4677250 | Barnett et al. | Jun 1987 | A |
| 4806436 | Tada et al. | Feb 1989 | A |
| 4940604 | Suyama et al. | Jul 1990 | A |
| 5013464 | Sugimura et al. | May 1991 | A |
| 5045409 | Eberspacher et al. | Sep 1991 | A |
| 5078804 | Chen et al. | Jan 1992 | A |
| 5141564 | Chen et al. | Aug 1992 | A |
| 5244509 | Arao et al. | Sep 1993 | A |
| 5277786 | Kawakami | Jan 1994 | A |
| 5286306 | Menezes | Feb 1994 | A |
| 5356839 | Tuttle et al. | Oct 1994 | A |
| 5401573 | Babel et al. | Mar 1995 | A |
| 5419781 | Hamakawa et al. | May 1995 | A |
| 5436204 | Albin et al. | Jul 1995 | A |
| 5441897 | Noufi et al. | Aug 1995 | A |
| 5445847 | Wada et al. | Aug 1995 | A |
| 5538903 | Aramoto et al. | Jul 1996 | A |
| 5567469 | Wada et al. | Oct 1996 | A |
| 5578503 | Karg et al. | Nov 1996 | A |
| 5626688 | Probst et al. | May 1997 | A |
| 5633033 | Nishitani et al. | May 1997 | A |
| 5677250 | Knapp | Oct 1997 | A |
| 5728231 | Negami et al. | Mar 1998 | A |
| 5730852 | Bhattacharya et al. | Mar 1998 | A |
| 5925228 | Panitz et al. | Jul 1999 | A |
| 5985691 | Basol et al. | Nov 1999 | A |
| 5994163 | Bodegard et al. | Nov 1999 | A |
| 6022487 | Daume et al. | Feb 2000 | A |
| 6107562 | Hashimoto et al. | Aug 2000 | A |
| 6121541 | Arya | Sep 2000 | A |
| 6124039 | Goetz et al. | Sep 2000 | A |
| 6124041 | Aoude et al. | Sep 2000 | A |
| 6126740 | Schulz et al. | Oct 2000 | A |
| 6127202 | Kapur et al. | Oct 2000 | A |
| 6150022 | Coulter et al. | Nov 2000 | A |
| 6228904 | Yadav et al. | May 2001 | B1 |
| 6268014 | Eberspacher et al. | Jul 2001 | B1 |
| 6323417 | Gillespie et al. | Nov 2001 | B1 |
| 6344272 | Oldenburg et al. | Feb 2002 | B1 |
| 6454886 | Martin et al. | Sep 2002 | B1 |
| 6472459 | Morales et al. | Oct 2002 | B2 |
| 6518086 | Beck et al. | Feb 2003 | B2 |
| 6593690 | McCormick et al. | Jul 2003 | B1 |
| 6641898 | Yazaki et al. | Nov 2003 | B2 |
| 6685986 | Oldenburg et al. | Feb 2004 | B2 |
| 6897603 | Mao et al. | May 2005 | B2 |
| 6974976 | Hollars | Dec 2005 | B2 |
| 7144627 | Halas et al. | Dec 2006 | B2 |
| 7306823 | Sager et al. | Dec 2007 | B2 |
| 20020006470 | Eberspacher et al. | Jan 2002 | A1 |
| 20020132045 | Halas et al. | Sep 2002 | A1 |
| 20020160195 | Halas et al. | Oct 2002 | A1 |
| 20020187347 | Halas et al. | Dec 2002 | A1 |
| 20030051664 | Stanbery | Mar 2003 | A1 |
| 20030052382 | Stanbery | Mar 2003 | A1 |
| 20030052391 | Stanbery | Mar 2003 | A1 |
| 20030054582 | Stanbery | Mar 2003 | A1 |
| 20030054661 | Stanbery | Mar 2003 | A1 |
| 20030054662 | Stanbery | Mar 2003 | A1 |
| 20030054663 | Stanbery | Mar 2003 | A1 |
| 20030192584 | Montello et al. | Oct 2003 | A1 |
| 20030205270 | Stanbery | Nov 2003 | A1 |
| 20030211646 | Stanbery | Nov 2003 | A1 |
| 20040144419 | Fix et al. | Jul 2004 | A1 |
| 20040209730 | Okoshi | Oct 2004 | A1 |
| 20040214001 | Oldenburg et al. | Oct 2004 | A1 |
| 20040219730 | Basol | Nov 2004 | A1 |
| 20050022747 | Stanbery | Feb 2005 | A1 |
| 20050035983 | Cruchon-Dupeyrat et al. | Feb 2005 | A1 |
| 20050058587 | Wagner | Mar 2005 | A1 |
| 20050150789 | Crane | Jul 2005 | A1 |
| 20050175836 | Kuehnle et al. | Aug 2005 | A1 |
| 20050183768 | Roscheisen et al. | Aug 2005 | A1 |
| 20050186342 | Sager et al. | Aug 2005 | A1 |
| 20050186805 | Stanbery | Aug 2005 | A1 |
| 20050194036 | Basol | Sep 2005 | A1 |
| 20050194038 | Brabec et al. | Sep 2005 | A1 |
| 20050202589 | Basol | Sep 2005 | A1 |
| 20050235869 | Cruchon-Dupeyrat et al. | Oct 2005 | A1 |
| 20050247340 | Zeira et al. | Nov 2005 | A1 |
| 20050266600 | Basol | Dec 2005 | A1 |
| 20050268962 | Gaudiana et al. | Dec 2005 | A1 |
| 20050272263 | Brabec et al. | Dec 2005 | A1 |
| 20060054506 | Natan et al. | Mar 2006 | A1 |
| 20060099146 | Chow et al. | May 2006 | A1 |
| 20060121701 | Basol | Jun 2006 | A1 |
| 20060134505 | Wang et al. | Jun 2006 | A1 |
| 20060165911 | Basol | Jul 2006 | A1 |
| 20060178012 | Basol | Aug 2006 | A1 |
| 20060189155 | Basol | Aug 2006 | A1 |
| 20060192955 | Jorgenson et al. | Aug 2006 | A1 |
| 20060207644 | Robinson et al. | Sep 2006 | A1 |
| 20060251874 | McClure et al. | Nov 2006 | A1 |
| 20070044834 | Berke et al. | Mar 2007 | A1 |
| 20070092648 | Duren et al. | Apr 2007 | A1 |
| 20070093006 | Basol | Apr 2007 | A1 |
| 20070093059 | Basol | Apr 2007 | A1 |
| 20070111367 | Basol | May 2007 | A1 |
| 20070145507 | Basol | Jun 2007 | A1 |
| 20070163383 | Van Duren et al. | Jul 2007 | A1 |
| 20070163637 | Robinson et al. | Jul 2007 | A1 |
| 20070163638 | Van Duren et al. | Jul 2007 | A1 |
| 20070163639 | Robinson et al. | Jul 2007 | A1 |
| 20070163640 | Van Duren et al. | Jul 2007 | A1 |
| 20070163642 | Van Duren et al. | Jul 2007 | A1 |
| 20070163643 | Van Duren et al. | Jul 2007 | A1 |
| 20070163644 | Van Duren et al. | Jul 2007 | A1 |
| 20070166453 | Van Duren et al. | Jul 2007 | A1 |
| 20070166964 | Basol | Jul 2007 | A1 |
| 20070169809 | Van Duren et al. | Jul 2007 | A1 |
| 20070169810 | Van Duren et al. | Jul 2007 | A1 |
| 20070169811 | Van Duren et al. | Jul 2007 | A1 |
| 20070169812 | Robinson et al. | Jul 2007 | A1 |
| 20070169813 | Robinson et al. | Jul 2007 | A1 |
| 20070178620 | Basol | Aug 2007 | A1 |
| 20080121277 | Robinson et al. | May 2008 | A1 |
| 20080124831 | Robinson et al. | May 2008 | A1 |
| 20080165235 | Rolly et al. | Jul 2008 | A1 |
| Number | Date | Country |
|---|---|---|
| 2741954 | Mar 1979 | DE |
| 793277 | Sep 1997 | EP |
| 61244004 | Oct 1986 | JP |
| 62-89369 | Apr 1987 | JP |
| 63-249379 | Oct 1988 | JP |
| 2001-04464 | Mar 1998 | JP |
| 2005119705 | Dec 2005 | KR |
| WO 02084708 | Oct 2002 | WO |
| WO 03007386 | Jan 2003 | WO |
| WO 03043736 | May 2003 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20070163637 A1 | Jul 2007 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11290633 | Nov 2005 | US |
| Child | 11361433 | US | |
| Parent | 11081163 | Mar 2005 | US |
| Child | 11290633 | US | |
| Parent | 10943657 | Sep 2004 | US |
| Child | 11081163 | US | |
| Parent | 10943685 | Sep 2004 | US |
| Child | 10943657 | US | |
| Parent | 10782017 | Feb 2004 | US |
| Child | 10943685 | US |