HIGH-VOLTAGE POSITIVE ELECTRODE MATERIAL FOR LITHIUM BATTERY AND PREPARATION METHOD THEREOF

Abstract

A high-voltage positive electrode material for a lithium battery and a preparation method thereof are provided. The high-voltage positive electrode material for a lithium battery includes a material represented by the following formula (1):

Description

CROSS-REFERENCE TO RELATED APPLICATION

This application claims the priority benefit of Taiwan application no. 105144042 filed on Dec. 30, 2016. The entirety of the above-mentioned patent applications is hereby incorporated by reference herein and made a part of this specification.

TECHNICAL FIELD

The disclosure relates to a lithium battery technique, and more particularly, to a high-voltage positive electrode material for a lithium battery and a preparation method thereof.

BACKGROUND

The energy density of a lithium battery is related to the operating voltage thereof, and therefore the development of a 5 V high-voltage positive electrode material is quite beneficial for increasing energy density. LiNi_0.5Mn_1.5O₄ has properties such as high operating voltage (about 4.7 V), high energy density, long cycle life, and resistance to high-rate charge and discharge, and therefore meets the energy density requirement above. However, the capacity of such material is degraded due to factors such as dissolution of manganese, Jahn-Teller distortion, and gas generation, and therefore such material currently cannot be readily commercialized.

Therefore, a positive electrode material for a high-voltage lithium battery having the effects of high operating voltage, high energy density, long cycle life, resistance to high-rate charge and discharge, and a more stable structure is urgently needed.

SUMMARY

In one embodiment of the disclosure, a high-voltage positive electrode material for a lithium battery includes a material represented by the following formula (1):

LiNi_0.5-x-yMn_1.5-x-yMg_3xCr_2yO₄  (1)

wherein x>0, y>0, and 0<3x+2y≤0.1.

In another embodiment of the disclosure, a preparation method of a high-voltage positive electrode material for a lithium battery includes preparing a precursor using a coprecipitation method and then mixing and sintering the precursor and lithium salt to produce the material represented by formula (1) above. The precursor includes nickel (Ni), manganese (Mn), magnesium (Mg), and chromium (Cr).

To make the aforementioned more comprehensible, several embodiments accompanied with drawings are described in detail as follows.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings are included to provide further understanding, and are incorporated in and constitute a part of this specification. The drawings illustrate exemplary embodiments and, together with the description, serve to explain the principles of the disclosure.

FIG. 1 shows the steps of the preparation process of a high-voltage positive electrode material for a lithium battery according to an embodiment of the disclosure.

FIG. 2 is an XRD control chart of the high-voltage positive electrode material for a lithium battery of preparation example 1 and pristine lithium nickel manganese oxide (LNMO).

FIG. 3 is a particle size distribution curve of the high-voltage positive electrode material for a lithium battery of preparation example 1.

FIG. 4 is a 1,000-magnification SEM image of the high-voltage positive electrode material for a lithium battery of preparation example 1.

FIG. 5 is a 10,000-magnification SEM image of the high-voltage positive electrode material for a lithium battery of preparation example 1.

FIG. 6A is an 0 element map of the high-voltage positive electrode material for a lithium battery of preparation example 1.

FIG. 6B is a Mn element map of the high-voltage positive electrode material for a lithium battery of preparation example 1.

FIG. 6C is a Ni element map of the high-voltage positive electrode material for a lithium battery of preparation example 1.

FIG. 6D is a Cr element map of the high-voltage positive electrode material for a lithium battery of preparation example 1.

FIG. 6E is a Mg element map of the high-voltage positive electrode material for a lithium battery of preparation example 1.

FIG. 7A is a capacity curve of the positive electrode material for a lithium battery of comparative example 1 obtained under different charge and discharge rates.

FIG. 7B is a capacity curve of the positive electrode material for a lithium battery of comparative example 2 obtained under different charge and discharge rates.

FIG. 7C is a capacity curve of the positive electrode material for a lithium battery of comparative example 3 obtained under different charge and discharge rates.

FIG. 7D is a capacity curve of the positive electrode material for a lithium battery of comparative example 4 obtained under different charge and discharge rates.

FIG. 7E is a capacity curve of the positive electrode material for a lithium battery of comparative example 5 obtained under different charge and discharge rates.

FIG. 7F is a capacity curve of the positive electrode material for a lithium battery of comparative example 6 obtained under different charge and discharge rates.

FIG. 7G is a capacity curve of the high-voltage positive electrode material for a lithium battery of preparation example 1 obtained under different charge and discharge rates.

FIG. 8A is a capacity curve of the high-voltage positive electrode material for a lithium battery of preparation example 2 obtained under different charge and discharge rates.

FIG. 8B is a capacity curve of the high-voltage positive electrode material for a lithium battery of preparation example 3 obtained under different charge and discharge rates.

FIG. 8C is a capacity curve of the high-voltage positive electrode material for a lithium battery of preparation example 4 obtained under different charge and discharge rates.

FIG. 9A is a capacity curve of the positive electrode material for a lithium battery of comparative example 1 at low temperature.

FIG. 9B is a capacity curve of the positive electrode material for a lithium battery of comparative example 2 at low temperature.

FIG. 9C is a capacity curve of the positive electrode material for a lithium battery of comparative example 3 at low temperature.

FIG. 9D is a capacity curve of the high-voltage positive electrode material for a lithium battery of preparation example 1 at low temperature.

FIG. 10A is a capacity curve of the positive electrode material for a lithium battery of comparative example 1 at 0.1 C at high temperature.

FIG. 10B is a capacity curve of the high-voltage positive electrode material for a lithium battery of preparation example 1 at 0.1 C at high temperature.

FIG. 11A is a cycle performance chart of preparation example 1 and comparative example 1 at room temperature.

FIG. 11B is a cycle performance chart of preparation example 1 and comparative example 1 at high temperature.

DETAILED DESCRIPTION OF DISCLOSED EMBODIMENTS

The disclosure relates to a high-voltage positive electrode material for a lithium battery including a material represented by the following formula (1):

LiNi_0.5-x-yMn_1.5-x-yMg_3xCr_2yO₄  (1)

wherein x>0, y>0, and 0<3x+2y≤0.1.

In the disclosure, the “high-voltage” positive electrode material refers to a working voltage of 4.6 V or more and a charge cutoff voltage of 5V or more.

In an embodiment, Mn in formula (1) is Mn(IV), i.e. Mn(4+). Moreover, the material is, for instance, spherical particles consisted of nanoparticles, wherein a size of the nanoparticle is between about 100 nm and 800 nm, and the material is actually sub-micron level, such as an average particle size between 1 micron and 20 microns.

FIG. 1 shows the steps of the preparation process of a high-voltage positive electrode material for a lithium battery according to an embodiment of the disclosure.

In FIG. 1, step 100 is performed to prepare a precursor using a coprecipitation method, wherein the precursor includes nickel (Ni), manganese (Mn), magnesium (Mg), and chromium (Cr). In the present embodiment, the coprecipitation method can include first preparing a metal solution based on the desired stoichiometry, then respectively selecting at least one chelating agent and at least one precipitant for preparation, and then controlling the reaction temperature, pH, feeding speed, stirring speed, and the presence of a protective atmosphere as needed to synthesize the desired precursor. The chelating agent is, for instance, ammonia water or ammonium sulfate, and the precipitant is, for instance, sodium hydroxide or potassium hydroxide. In an embodiment, the reaction temperature is, for instance, between 30° C. and 50° C., the pH is, for instance, 9 to 11, the feeding speed is, for instance, between 10 mL/H and 100 mL/H, and the stirring speed is, for instance, between 800 rpm and 2000 rpm. If a protective atmosphere is to be added in the coprecipitation method, then an inert gas can be used as the protective atmosphere. Moreover, the step of preparing the precursor requires various chemicals as the source of the metal elements; for instance, nickel nitrate, nickel sulfate, or nickel acetate can be used as the nickel source; manganese nitrate, manganese sulfate, or manganese acetate can be used as the manganese source; magnesium nitrate, magnesium sulfate, or magnesium acetate can be used as the magnesium source; and chromium nitrate, chromium sulfate, or chromium acetate can be used as the chromium source.

The positive electrode material of the present embodiment can prevent decomposition and release of oxygen atoms via the addition of transition metal magnesium having a greater bond energy with oxygen, and thus it can reduce Jahn-Teller distortion and reduce irreversible capacity. Moreover, chromium metal doping can increase the discharge capacity of a 5 V platform and inhibit the generation of Mn³⁺ to slow down further reaction and decomposition with the electrolyte solution so as to improve battery performance, and therefore previous issues of the lithium nickel manganese oxide material can be solved.

Referring further to FIG. 1, in step 110, the precursor and lithium salt are mixed and then sintered to produce the material represented by formula (1) above, wherein the temperature for sintering is, for instance, between 600° C. and 800° C., the time for sintering is, for instance, between 8 hours and 24 hours, and the atmosphere for sintering can be air or oxygen. The oxygen during sintering is, for example, 99.99% pure oxygen, the air is, for example, general atmosphere, and the lithium salt is, for instance, lithium hydroxide or lithium carbonate.

In the following, experiments are provided to verify the effect of the positive electrode material for a lithium battery of the invention, but the disclosure is not limited to the following experiments.

<Raw Materials>

Nickel source: nickel sulfate.

Manganese source: manganese sulfate.

Magnesium source: magnesium sulfate.

Chromium source: chromium sulfate.

Chelating agent: ammonia water, ammonium sulfate.

Precipitant: sodium hydroxide.

Lithium salt: lithium carbonate.

The above are all purchased from Showa Corporation.

Preparation Example 1

31.39 g/L of the nickel source, 62.23 g/L of the manganese source, 1.84 g/L of the magnesium source, and 1.95 g/L of the chromium source were made into a metal solution based on the desired stoichiometry, and then 839.51 g/L of ammonia water and 13.21 g/L of ammonium sulfate were respectively prepared as the chelating agent, and 46.59 g/L of sodium hydroxide was prepared as a precipitant, wherein the reaction temperature was 40° C., the pH was about 10.10, the feeding speed was about 40 mL/H, and the stirring speed was about 1500 rpm, and a desired precursor was synthesized in the present of a protective atmosphere (nitrogen).

Then, the precursor and the lithium salt were sufficiently mixed at a molar ratio of 1:1.05 and then sintered to produce a material: LiNi_0.48Mn_1.48Mg_0.03Cr_0.02O₄, wherein the sintering temperature was about 750° C., the time was about 24 hours, and the sintering atmosphere was air.

X-ray diffraction analysis (XRD) was performed on the product of preparation example 1, and the result was compared to the diffraction curve of pristine LNMO to obtain FIG. 2. It can be known from FIG. 2 that LiNi_0.48Mn_1.48Mg_0.03Cr_0.02O₄ of preparation example 1 does not change the crystal structure of LNMO. Moreover, the product of preparation example 1 was analyzed by dynamic light scattering (DLS), and the results are shown in FIG. 3. According to FIG. 3, the material of preparation example 1 has an average particle size (D₅₀) of about 12 microns.

Next, a scanning electron microscopy energy dispersive spectroscopy (SEM/EDS) analysis was performed on the product of preparation example 1 to obtain the SEM images of FIG. 4 and FIG. 5, wherein FIG. 4 is a 1,000-magnification SEM image and FIG. 5 is a 10,000-magnification SEM image. It can be observed from FIG. 4 that the particle size of the composite material is generally at the sub-micron level, and it can be observed from FIG. 5 that a single spherical microparticle is consisted of smaller nanoparticles. FIG. 6A to FIG. 6E are respectively O, Mn, Ni, Cr, and Mg element maps of the positive electrode material for a lithium battery of preparation example 1, wherein the bright regions (or bright spots) are locations of a single element, and the dark regions are locations of other elements. Therefore, it can be seen from FIG. 6A to FIG. 6E that the analysis regions have a plurality of material particles, and at the same time, O, Mn, Ni, Cr, and Mg are present at the same locations, and therefore the particle can be confirmed to be a composite material of lithium-nickel-manganese-chromium-magnesium oxide.

Comparative Example 1

Preparation was made according to the method of preparation example 1, but the LNMO material (LiNi_0.5Mn_1.5O₄) was not doped or modified.

Comparative Example 2

Preparation was made according to the method of preparation example 1, but magnesium was not doped. The resulting material was LNMO doped with 0.02 moles of chromium, and the formula thereof is LiNi_0.49Mn_1.49Cr_0.02O₄.

Comparative Example 3

Preparation was made according to the method of preparation example 1, but chromium was not doped. The resulting material was LNMO doped with 0.03 moles of magnesium, and the formula thereof is LiNi_0.49Mn_1.49Mg_0.03O₄.

Comparative Example 4

Preparation was made according to the method of preparation example 1, but Cr(III) was changed to Al(III) (aluminum sulfate). The resulting material was LNMO doped with 0.03 moles of magnesium and 0.02 moles of aluminum, and the formula thereof is LiNi_0.48Mn_1.48Mg_0.03Al_0.02O₄.

Comparative Example 5

Preparation was made according to the method of preparation example 1, but Mg(II) was changed to Zn(II) (zinc sulfate). The resulting material was LNMO doped with 0.03 moles of zinc and 0.02 moles of chromium, and the formula thereof is LiNi_0.48Mn_1.48Zn_0.03Cr_0.02O₄.

Comparative Example 6

Preparation was made according to the method of preparation example 1, and doping of Mg(II), Zn(II), Cr(III), and Al(III) was performed at the same time. The resulting material was LNMO doped with 0.015 moles of magnesium, 0.015 moles of zinc, 0.01 moles of chromium, and 0.01 moles of aluminum. The formula thereof is LiNi_0.48Mn_1.48Mg_0.0015Zn_0.0015Cr_0.01Al_0.01O₄.

<Analysis Method>

A 2032 button cell was used as the vehicle for the to-be-proven material, wherein the negative electrode was lithium metal, the electrolyte solution was 1.0 M LiPF₆, and EC/DMC=1/2 vol %.

Experimental Example 1

A charge and discharge test was performed on batteries with the lithium battery positive electrode materials of comparative examples 1 to 6 and preparation example 1 at different charge and discharge rates and room temperature, and the results are respectively shown in FIG. 7A to FIG. 7G. FIG. 7A to FIG. 7F are capacity curves of comparative examples 1 to 6 obtained at different charge and discharge rates, and

FIG. 7G is a capacity curve of preparation example 1 obtained at different charge and discharge rates. Capacities at 6 C were respectively compared, the maximum capacity was the battery using the positive electrode material of preparation example 1. Under the same 6 C discharge rate, the discharge capacities of FIG. 7A to FIG. 7G were respectively 104.07 mAh/g, 110 mAh/g, 113.63 mAh/g, 92 mAh/g, 91 mAh/g, 100 mAh/g, and 125 mAh/g. All of the capacity curves are shifted more downward and to the left with higher discharge rates. Moreover, in comparative example 4 in which chromium is replaced by other metal elements, the capacity cannot be effectively increased; in comparative example 5 in which magnesium is replaced by other metal elements, the capacity cannot be effectively increased.

Preparation Example 2

Preparation was made according to the method of preparation example 1, but the mole content of magnesium was reduced to 0.01 moles. The resulting material was LiNi_0.4866Mn_1.4867Mg_0.01Cr_0.02O₄.

Preparation Example 3

Preparation was made according to the method of preparation example 1, but the mole content of magnesium was reduced to 0.02 moles. The resulting material was LiNi_0.4834Mn_1.4833Mg_0.02Cr_0.02O₄.

Preparation Example 4

Preparation was made according to the method of preparation example 1, but the mole content of magnesium was increased to 0.05 moles. The resulting material was LiNi_0.47Mn_1.47Mg_0.05Cr_0.02O₄.

Experimental Example 2

A charge and discharge test was performed on batteries using the lithium battery positive electrode materials of preparation examples 2 to 4 at different charge and discharge rates and room temperature, and the results are respectively shown in FIG. 8A to FIG. 8C. It can be obtained from FIG. 8A to FIG. 8C that, batteries using the positive electrode materials for a lithium battery of preparation examples 2 to 4 can have higher capacity at high charge and discharge rates.

Experimental Example 3

At a low temperature of −20° C., a charge and discharge test was performed on the batteries using the lithium battery positive electrode material of comparative example 1 and preparation example 1 at 0.5 C; and a charge and discharge test was performed on the batteries using the lithium battery positive electrode material of comparative examples 2 to 3 at 0.2 C. The results are respectively shown in FIG. 9A to FIG. 9D, wherein FIG. 9A to FIG. 9C are capacity curves of comparative examples 1 to 3 obtained at low temperature; and FIG. 9D is a capacity curve of preparation example 1 obtained at low temperature. Charge and discharge capacity ratios are shown in the figures, wherein the ratio of preparation example 1 reaches 88.4% and is significantly better than the results of comparative examples 1 to 3. In particular, under the test condition that the discharge rate (0.5 C) of preparation example 1 is higher than the discharge rate (0.2 C) of both comparative examples 2 to 3, the low-temperature discharge property of preparation example 1 is still better than those of the comparative examples above.

Experimental Example 4

At a high temperature of 45° C., a charge and discharge test was performed on the batteries using the lithium battery positive electrode material of comparative example 1 and preparation example 1 at 0.1 C, and the results are respectively shown in FIG. 10A and FIG. 10B. It can be known from FIG. 10B that preparation example 1 has higher capacity.

Experimental Example 5

At room temperature (about 25° C.) and a high temperature of 45° C., a charge and discharge cycle life test was respectively performed on the batteries using the lithium battery positive electrode material of comparative example 1 and preparation example 1 at 0.5 C, and the results are respectively shown in FIG. 11A and FIG. 11B. It can be known from FIG. 11B that, the battery using the lithium battery positive electrode material of preparation example 1 has a more stable charge and discharge performance at high temperature.

Based on the above, according to the addition of transition metal magnesium having a greater bond energy with oxygen, decomposition and release of oxygen atoms can be prevented, and therefore material cycle life property is improved. Moreover, in the disclosure, by doping chromium, discharge capacity of the 5 V platform can be increased and inhibit the production of Mn^3± to slow down further reaction and decomposition with the electrolyte solution, such that battery performance is increased.

Accordingly, the material obtained in the disclosure not only can efficiently improve material reversible capacity, reduce irreversible capacity, and improve the performance of material at high-rate discharge, but also can significantly improve low-temperature discharge property of the material.

It will be apparent to those skilled in the art that various modifications and variations can be made to the structure of the disclosed embodiments without departing from the scope or spirit of the disclosure. In view of the foregoing, it is intended that the disclosure cover modifications and variations of this disclosure provided they fall within the scope of the following claims and their equivalents.

Claims

1. A high-voltage positive electrode material for a lithium battery, comprising a material represented in formula (1) below: LiNi0.5-x-yMn1.5-x-yMg3xCr2yO4  (1)wherein x>0, y>0, and 0<3x+2y≤0.1.

2. The high-voltage positive electrode material for the lithium battery of claim 1, wherein the Mn is Mn(IV).

3. The high-voltage positive electrode material for the lithium battery of claim 1, wherein an average particle size of the material is between 1 micron and 20 microns.

4. A preparation method of a high-voltage positive electrode material for a lithium battery, comprising: preparing a precursor using a coprecipitation method, wherein the precursor comprises nickel (Ni), manganese (Mn), magnesium (Mg), and chromium (Cr); andmixing the precursor and a lithium salt and then performing sintering to produce a material represented by formula (1) below: LiNi0.5-x-yMn1.5-x-yMg3xCr2yO4  (1),wherein x>0, y>0, and 0<3x+2y≤0.1.

5. The preparation method of the high-voltage positive electrode material for the lithium battery of claim 4, wherein a reaction temperature of the coprecipitation method is 30° C. to 50° C.

6. The preparation method of the high-voltage positive electrode material for the lithium battery of claim 4, wherein a pH of the coprecipitation method is 9 to 11.

7. The preparation method of the high-voltage positive electrode material for the lithium battery of claim 4, wherein a feeding speed of the coprecipitation method is 10 mL/H to 100 mL/H.

8. The preparation method of the high-voltage positive electrode material for the lithium battery of claim 4, wherein a stirring speed of the coprecipitation method is 800 rpm to 2000 rpm.

9. The preparation method of the high-voltage positive electrode material for the lithium battery of claim 4, wherein a protective atmosphere of the coprecipitation method is an inert gas.

10. The preparation method of the high-voltage positive electrode material for the lithium battery of claim 4, wherein the step of preparing the precursor comprises selecting at least one chelating agent and at least one precipitant.

11. The preparation method of the high-voltage positive electrode material for the lithium battery of claim 10, wherein the chelating agent comprises ammonia water or ammonium sulfate, and the precipitant comprises sodium hydroxide or potassium hydroxide.

12. The preparation method of the high-voltage positive electrode material for the lithium battery of claim 4, wherein the step of preparing the precursor comprises: using nickel sulfate, nickel nitrate, or nickel acetate as a nickel source; using manganese sulfate, manganese nitrate, or manganese acetate as a manganese source; using magnesium sulfate, magnesium nitrate, or magnesium acetate as a magnesium source; and using chromium sulfate, chromium nitrate, or chromium acetate as a chromium source.

13. The preparation method of the high-voltage positive electrode material for the lithium battery of claim 4, wherein a temperature for the sintering is 600° C. to 800° C., a time for the sintering is 8 hours to 24 hours, and an atmosphere for the sintering is air or oxygen.