(1) Field of the Invention
The present invention relates to a cathode body used in a cathode-ray tube or the like.
(2) Description of the Related Art
Also, the cathode sleeve 102 and a cathode holding member 105 are fixed concentrically by means of three cathode sleeve supporting members 106, where both ends of each of the three supporting members 106 are welded to a side surface of the cathode sleeve 102 and onto a top end of the cathode holding member 105, respectively.
The cathode body 100 is produced by following a procedure composed of the following six processes.
1. First Welding Process
An end of each of the three supporting members 106 is welded to a side surface of the cathode sleeve 102.
2. Baking/Blacking Process
Metal particles are sprayed onto an inner surface of the cathode sleeve 102. The inner surface of the cathode sleeve 102 is then baked to be blacked.
3. Second Welding Process
The cap member 103 is welded to an opening of the cathode sleeve 102.
4. Layer Forming Process
The electron emission material layer 104 is formed by spraying an electron emission material onto an outer surface of the cap member 103.
5. Third Welding Process
The other end of each of the three supporting members 106 is welded onto the top end of the cathode holding member 105.
6. Heater Inserting Process
The heater 101 is inserted into the cathode sleeve 102, and the heater 101 and the cathode sleeve 102 are welded together.
Here, for the sake of convenience, an interim product obtained after the layer forming process is referred to as a cathode body member 107.
Similarly, an interim product obtained after the third welding process is referred to as a heater case 108 (not illustrated). Also, an interim product obtained after the first welding process to which the cathode sleeve supporting members 106 have been attached is referred to as a cathode sleeve structure 109 (not illustrated).
Meanwhile, the cathode sleeve supporting members 106 of the conventional cathode body 100 are made of Ni—Fe having low thermal conductivity, to minimize the heat loss caused by the heat flow from the cylindrical cathode sleeve 102 to the cathode holding member 105. Also, each of the cathode sleeve supporting members 106 is long and approximately 0.3 mm wide and 0.1 mm thick. As a result, the cathode sleeve supporting members 106 apt to be deformed by external forces.
Though being weak as described above, the cathode sleeve supporting members 106 are protected from external forces after the third welding process in which they are welded to the cathode holding member 105 that has high strength. However, it sometimes happens that the cathode sleeve supporting members 106 are deformed by external forces when the cathode body member 107 is stored, transferred, or loaded on an assembly jig, between the layer forming process and the third welding process.
In the third welding process, the welding is performed by automated welding equipment, and the cathode body member 107 needs to be positioned accurately for the welding. As a result, to put the cathode body member 107 at an accurate position and direction, a parts feeder is used. However, when passing through the parts feeder, or when being transferred from the parts feeder onto a welding rack, the cathode body member 107 apt to be deformed by external forces.
If a cathode body 100 containing a deformed cathode sleeve supporting member 106 is used in a final product, the cap member 103 is shifted from a position at which it is expected to be, and a distance between the electron emission material layer 104 and a control electrode (G1 electrode) deviates from a specified value in design. When this happens, a desired level of cut-off voltage is not obtained.
Deformed cathode body members 107 should be discarded so as not to be welded.
Also, if the cathode body member 107 fails to be positioned accurately in the third welding process, the cathode sleeve supporting members 106 are not welded to the cathode holding member 105 at correct positions as shown in
If a welding defect is found in a heater case 108 after the welding process, the defective heater case 108 should also be discarded.
An object of the present invention is therefore to provide a high-yield cathode body, cathode sleeve structure, and cathode-ray tube, and a cathode sleeve substrate from which such a cathode sleeve structure is produced.
Another object of the present invention is to provide production methods of the high-yield cathode sleeve substrate and cathode body.
The above first object is fulfilled by
(1) a cathode sleeve structure for housing a heater, comprising: a case member that is cylindrical and an end thereof is open; a plurality of supporting members that extend radially from vicinities of the end of the case member; and a linkage member that connects the plurality of supporting members, wherein the case member, the plurality of supporting members, and the linkage member are formed as one piece.
The supporting members of the cathode sleeve structure are typically thin to suppress the heat loss. In a production of a conventional cathode sleeve structure, any portion of the supporting members may be deformed before they are bonded to the holding member. In contrast, in the above-stated construction, since the supporting members are connected by the linkage member, the movement of the supporting members is restricted until they are bonded to the holding member. At the same time, if an external force is exerted on any supporting member, the force is distributed to the other supporting members, and the supporting members are prevented from being deformed.
Accordingly, in a production of a cathode body using the cathode sleeve structure, the number of products with defects by the deformation of the supporting members is reduced. This improves the yield in the cathode body production.
(2) In the cathode sleeve structure of (1), the linkage member may connect the plurality of supporting members at free ends of the supporting members, while the other ends are connected to the case member.
With the above-stated construction, the number of deformed supporting members is further reduced since the supporting members have no free end.
(3) In the cathode sleeve structure of (2), the linkage member may be substantially on a circle.
With the above-stated construction, an external force exerted on any supporting member is more apt to be distributed to the other supporting members.
(4) In the cathode sleeve structure of (3), the case member may have a first end and a second end, the first end being the end that is open, and the plurality of supporting members are bent at vicinities of boundaries between the case member and the supporting members, substantially at a same angle toward the second end.
With the above-stated construction, the supporting members are prevented from varying in shape. That is to say, the condition in which an external force is applied to each supporting member is unified.
(5) In the cathode sleeve structure of (4), the angle at which the plurality of supporting members are bent may be smaller than 90 degrees with respect to a central axis of the case member.
With the above-stated construction, the cathode sleeve structure becomes shorter. This reduces the area of an apparent surface on which an external force is exerted, making the cathode sleeve structure less susceptible to external forces.
(6) In the cathode sleeve structure of (1), when the number of the plurality of supporting members is expressed by n, an opening angle between each pair of adjacent supporting members may be approximately 360/n degrees.
With the above-stated construction, the condition in which an external force is applied to each supporting member is unified.
(7) In the cathode sleeve structure of (1), a principal element of a material of the case member, the plurality of supporting members, and the linkage member may be selected from the group consisting of Ni, Fe, Co, Ta, Mo, and Nb.
The above-stated construction provides more options for choice of materials, and gives more freedom in designing the cathode sleeve structure.
(8) In the cathode sleeve structure of (7), the material may contain one or more metals selected from the group consisting of Mg, Si, Cr, W, and Al.
With the above-stated construction, it is possible to use such metal content as a reducing agent for the electron emission material.
(9) In the cathode sleeve structure of (1), a principal element of a material of the case member, the plurality of supporting members, and the linkage member may be Cr.
With the above-stated construction, it is possible to form a black layer on the case member (the cathode sleeve) only by heating, without spraying metal powder thereon.
(10) In the cathode sleeve structure of (9), the material may contain one or more metals selected from the group consisting of Mg, Si, W, and Al.
With the above-stated construction, it is possible to use such metal content as a reducing agent for the electron emission material.
(11) In the cathode sleeve structure of (1), the case member may have a first end and a second end, the first end being the end that is open, and the second end is blocked by a member that is formed as one piece with the case member.
With the above-stated construction, the second end is automatically blocked as the case member is formed. That is to say, since there is no need for having a process in which a certain different member is slipped over and welded to the case member, other than a process for forming the case member, the chance that an external force is exerted on a supporting member is reduced.
The above first object is also fulfilled by
(12) a cathode sleeve structure for housing a heater, comprising: a case member that is cylindrical and an end thereof is open; a plurality of supporting members that extend radially from vicinities of the end of the case member; and a plurality of extending members that extend from the plurality of supporting members, respectively, portions of each pair of adjacent extending members being close to each other, wherein the case member, the plurality of supporting members, and the plurality of extending members are formed as one piece.
With the above-stated construction, if an external force is exerted in a direction in which adjacent supporting members get near, the extending members extending from the adjacent supporting members contact each other. This restricts the movement of the supporting members, and at the same time distributes the force to the other supporting members, preventing the deformation of the supporting members.
Accordingly, in a production of a cathode body using the cathode sleeve structure, the number of products with defects by the deformation of the supporting members is reduced. This improves the yield in the cathode body production.
(13) In the cathode sleeve structure of (12), the plurality of extending members may respectively extend from free ends of the plurality of supporting members, while the other ends are connected to the case member.
With the above-stated construction, if an external force is exerted on a supporting member and an extending member extending from the supporting member contacts another extending member within the elastic deformation, the movement of the end of the supporting member is restricted.
(14) In the cathode sleeve structure of (13), the plurality of extending members may be substantially on a same circle.
With the above-stated construction, if an external force is exerted on a supporting member, extending members are apt to contact each other, and at the same time, the external force is apt to be distributed to other supporting members.
(15) In the cathode sleeve structure of (14), the portions of each pair of adjacent extending members being close to each other may be ends thereof.
With the above-stated construction, if an external force is exerted on a supporting member, ends of extending members are apt to contact each other.
(16) In the cathode sleeve structure of (15), the shortest distance between each pair of adjacent extending members may be no greater than 0.5 mm.
With the above-stated construction, if an external force is exerted on a supporting member and an extending member extending from the supporting member contacts another extending member within the elastic deformation, the movement of the supporting member is restricted by the extending member. This also restricts the deformation of the supporting member since the external force is distributed to other supporting members.
The first object is also fulfilled by
(17) a cathode sleeve structure for housing a heater, comprising: a case member that is cylindrical and has a first end and a second end, the first end being open, and the case member being thicker at the first end than any other portions thereof so that a step is formed on an outer surface at the first end; and a plurality of supporting members that extend radially from the step at the first end of the case member, and are bent at vicinities of boundaries between the step and the supporting members toward the second end.
With the above-stated construction, the supporting members are bent at vicinities of boundaries between (i) the step where the case member is thicker and (ii) the supporting members, a crack is less apt to be caused by the bending.
(18) In the cathode sleeve structure of (17), each of the plurality of supporting members may be a plate being t mm thick, and a length of the step in a longitudinal direction of the case member is no smaller than t mm and no larger than 3.5 t mm.
The above-stated construction prevents a crack from being generated by the bending, without a great increase the heat loss.
The first object is also fulfilled by
(19) a cathode body, comprising: the cathode sleeve structure defined in (1); and a holding member that is bonded to either (a) ends of the plurality of supporting members or (b) the linkage member so that the cathode sleeve structure is fixed substantially at a center of the holding member.
In the cathode sleeve structure, the case member is held by the holding member that is bonded to either (a) ends of the plurality of supporting members or (b) the linkage member.
The supporting members of the cathode sleeve structure are typically thin to suppress the heat loss. In a production of a conventional cathode sleeve structure, any portion of the supporting members may be deformed before they are bonded to the holding member. In contrast, in the above-stated construction, since the supporting members are connected by the linkage member, the movement of the supporting members is restricted until they are bonded to the holding member. At the same time, if an external force is exerted on any supporting member, the force is distributed to the other supporting members, and the supporting members are prevented from being deformed.
Accordingly, in a production of a cathode body using the cathode sleeve structure, the number of products with defects by the deformation of the supporting members is reduced. This improves the yield in the cathode body production.
The first object is also fulfilled by
(20) a cathode body, comprising: the cathode sleeve structure defined in (12); and a holding member that surrounds the cathode sleeve structure and is bonded to either (i) ends of the plurality of supporting members or (ii) the plurality of extending members so that the cathode sleeve structure is fixed substantially at a center of the holding member.
With the above-stated construction, the movement of the supporting members is restricted by the extending members until the supporting members are bonded to the holding member. At the same time, if an external force is exerted on any supporting member, the force is distributed to the other supporting members, and the supporting members are prevented from being deformed.
Accordingly, in a production of a cathode body using the cathode sleeve structure, the number of products with defects by the deformation of the supporting members is reduced. This improves the yield in the cathode body production.
The first object is also fulfilled by
(21) a cathode ray tube, comprising: an electron gun including the cathode body defined in (20). The above-stated construction improves the yield of the cathode body used in the cathode ray tube, thus improving the yield of the cathode ray tube.
The first object is also fulfilled by
(22) a cathode sleeve substrate from which a cathode sleeve structure is produced, comprising: a plurality of case members projecting from a surface of a thin metal plate; and a plurality of supporting members that are part of the thin metal plate and extend from vicinities of a root of each case member radially.
With the above-stated construction in which a plurality of sets of a case member and supporting members are formed on a thin metal plate, it is possible to store and transfer the plurality of sets of a case member and supporting members without supporting them directly, but by supporting only part of the thin metal plate.
That is to say, the case members and supporting members are less apt to receive an external force directly.
Furthermore, the case members and supporting members are formed at predetermined positions on the thin metal plate. As a result, when they are processed by automated equipment while they are part of the thin metal plate, the positioning is easy.
(23) The cathode sleeve substrate of (22) may further comprise a linkage member that connects, for each case member, the plurality of supporting members.
With the above-stated construction, even after sets of a case member, supporting members, and linkage member are separated from the thin metal plate, the deformation of the supporting members is restricted by the linkage member.
(24) The cathode sleeve substrate of (22) may further comprise a plurality of extending members that extend, for each case member, from the plurality of supporting members, respectively, portions of each pair of adjacent extending members being close to each other.
With the above-stated construction, even after sets of a case member, supporting members, and extending members are separated from the thin metal plate, the deformation of the supporting members is restricted by the extending members.
The second object is fulfilled by
(25) a method of producing a cathode sleeve substrate from which a cathode sleeve structure is produced, comprising: a case member forming step for forming at least one cylindrical case member as a projection from a thin metal plate by partially deforming the thin metal plate; a supporting member forming step for forming a plurality of supporting members that extend from vicinities of a root of each case member radially, by removing parts of the thin metal plate; and a linkage member forming step for forming, by removing parts of the thin metal plate, a linkage member that connects the plurality of supporting members.
With the above-stated construction, each set of a case member, supporting members, and linkage member is formed by partially deforming and removing the thin metal plate.
That is to say, since there is no process of bonding each set of the case member, supporting members, and linkage member together and they are formed as one piece, the cathode sleeve substrate can easily be produced.
(26) In the cathode sleeve substrate production method of (25), in the case member forming step, a plurality of cylindrical case members may be formed as projections from the thin metal plate, in the supporting member forming step, the plurality of supporting members are formed for each case member, and in the linkage member forming step, the linkage member is formed for each case member.
With the above-stated construction, a plurality of sets of a case member, a plurality of supporting members, and a linkage member are stored and transferred as one thin metal plate.
(27) The cathode sleeve substrate production method of (26) may further comprise a bobbin winding step for winding, around a bobbin, the thin metal plate on which the case members, the supporting members, and the linkage member are formed.
With the above-stated construction, the case members, the supporting members, and the linkage member are less apt to receive an external force. This enables the cathode sleeve substrate to be stored and transferred while they keep the quality at the time of production.
The second object is also fulfilled by
(28) a method of producing a cathode sleeve substrate from which a cathode sleeve structure is produced, comprising: a case member forming step for forming at least one cylindrical case members as a projection from a thin metal plate by partially deforming the thin metal plate; a supporting member forming step for forming a plurality of supporting members that extend from vicinities of a root of the case member radially, by removing parts of the thin metal plate; and an extending member forming step for forming, by removing parts of the thin metal plate, a plurality of extending members that extend from the plurality of supporting members, respectively, portions of each pair of adjacent extending members being close to each other.
With the above-stated construction, each set of a case member, supporting members, and extending members is formed by partially deforming and removing the thin metal plate.
That is to say, since there is no process of bonding each set of the case member, supporting members, and extending members together and they are formed as one piece, the cathode sleeve substrate can easily be produced.
(29) In the cathode sleeve substrate production method of (28), in the case member forming step, a plurality of cylindrical case members may be formed as projections from the thin metal plate, in the supporting member forming step, the plurality of supporting members are formed for each case member, and in the extending member forming step, the plurality of extending members are formed for each case member.
With the above-stated construction, a plurality of sets of a case member, a plurality of supporting members, and a plurality of extending members are stored and transferred as one thin metal plate.
(30) The cathode sleeve substrate production method of (29) may further comprise a bobbin winding step for winding, around a bobbin, the thin metal plate on which the case members, the supporting members, and the extending members are formed.
With the above-stated construction, the case members, the supporting members, and the extending members are less apt to receive an external force. This enables the cathode sleeve substrate to be stored and transferred while they keep the quality at the time of production.
The second object is also fulfilled by
(31) a method of producing a cathode sleeve substrate from which a cathode sleeve structure is produced, comprising: a case member forming step for forming at least one cylindrical case member as a projection from a thin metal plate by partially deforming the thin metal plate; a step forming step for forming a step at the root of the case member by partially deforming the thin metal plate so that the root of the case member is thicker than any other portions thereof; and a supporting member forming step for forming a plurality of supporting members that extend from the step of the case member radially, by removing parts of the thin metal plate.
With the above-stated construction, each set of a case member, supporting members, and linkage member is formed by partially deforming and removing the thin metal plate.
That is to say, since there is no process of bonding each set of the case member, supporting members, and linkage member together and they are formed as one piece, the cathode sleeve substrate can easily be produced.
(32) In the cathode sleeve substrate production method of (31), in the case member forming step, a plurality of cylindrical case members may be formed as projections from the thin metal plate, and in the supporting member forming step, the plurality of supporting members are formed for each case member.
With the above-stated construction, a plurality of sets of a case member and a plurality of supporting members are stored and transferred as one thin metal plate.
The second object is also fulfilled by
(33) a method of producing a cathode body from the cathode sleeve substrate defined in (23), comprising: a separation step for separating, by cutting, sets of a case member, a plurality of supporting members, and a linkage member from the thin metal plate; and a welding step for, after the separation step, welding a cylindrical holding member to either (i) ends of the plurality of supporting members or (ii) the linkage member, for each set thereof.
With the above-stated construction, the supporting members are less apt to receive an external force directly. This prevents deformation of the supporting members.
(34) The cathode body production method of (33), wherein the separation step is performed in a latter half of the whole process of the cathode body production method, in a time series.
With the above-stated construction, in more than half processes, the case members, supporting members, and either the linkage member or extending members are kept to be contained in the cathode sleeve substrate. This provides areas other than these members on the cathode sleeve substrate to be used for supporting or binding thereof. This makes the case members, supporting members, and either the linkage member or extending members less apt to receive an external force directly, further improving the yield.
Furthermore, the case members and supporting members are formed at predetermined positions on the thin metal plate until they are separated from the thin metal plate. As a result, the positioning is easy.
(35) The cathode body production method of (34) may further comprise a slit forming step that is performed before the separation step and forms slits by either cutting or removing part of each linkage member.
The above-stated construction in which the linkage members have slits provides more freedom in press-molding the linkage members and supporting members.
The second object is also fulfilled by
(36) a method of producing a cathode body from the cathode sleeve substrate defined in (31), comprising: a separation step for separating, by cutting, sets of a case member and a plurality of supporting members from the thin metal plate; a bending step for bending each supporting member by pressing down the case member using an edge of the step as a point of application of force while fixing an end of each supporting member; and a welding step for, after the bending step, welding a holding member to the plurality of supporting members, for each set thereof.
With the above-stated construction having such a bending step, the bent supporting members are less apt to have a crack.
These and the other objects, advantages and features of the invention will become apparent from the following description thereof taken in conjunction with the accompanying drawings which illustrate a specific embodiment of the invention.
In the drawings:
The following describes a cathode body production method in Embodiment 1 with reference to the attached drawings.
Embodiment 1
Construction
As shown in
As shown in
The cathode body member 12 is constructed as follows. A cap member 15, which is made of Ni at a purity degree of 99.9%, is fitted on an end of a cylindrical cathode sleeve structure 14 and welded to the cathode sleeve structure 14. A heater 11 is housed in the cathode sleeve structure 14. An electron emission material layer 16, which is made of an alkaline earth metal that has BaO (barium oxide) as main component, is formed on an outer surface of the cap member 15.
More specifically, three cathode sleeve supporting members 14b, which are examples of thin-plate supporting members, extend radially from a lower end of a cylindrical heater case member 14a that is an example of a heater case and is made of Ni at a purity degree of 99.9%. Each end of the extending cathode sleeve supporting members 14b is connected to a ring-shaped outer linkage member 14c that is an example of a linkage member. The outer linkage member 14c and the cathode holding member 13 are spot-welded together at three spots.
The inner surface of the heater case member 14a has been baked to be blacked.
The purpose of blacking the inner surface of the heater case member 14a is to facilitate absorption of heat coming from the heater, and enable the cathode to operate with a small amount of power provided by the heater.
Each cathode sleeve supporting member 14b extends from the heater case member 14a and is bent at its root toward the cap member 15 at an acute angle.
When viewed downward from any point on an extension of the axis of the cylindrical cathode body member 12, each adjacent pair of the cathode sleeve supporting members 14b forms an angle of 120°.
The shape of the outer linkage member 14c substantially matches the cross-sectional profile of the cathode holding member 13. The outer linkage member 14c and the cathode holding member 13 are spot-welded together at three spots (indicated by the signs “X” in
The cylindrical heater case member 14a, cathode sleeve supporting members 14b, and outer linkage member 14c are formed as one piece by, for example, pressing or stamping a thin Ni plate.
That is to say, the construction of these members is different from the conventional technique in which both ends of each of three supporting members are welded to the cathode sleeve and the cathode holding member, respectively.
The outer linkage member 14c restricts the motion of the cathode sleeve supporting members 14b.
For example, when an external force is applied to any of three cathode sleeve supporting members 14b, the outer linkage member 14c distributes the external force to the other cathode sleeve supporting members 14b. As understood from this, the construction enhances the tolerance of cathode sleeve supporting members 14b to the external force.
Also, with the construction in which the outer linkage member 14c substantially matches the cross-sectional profile of the cathode holding member 13 in shape, it is possible to weld the outer linkage member 14c and the cathode holding member 13 in so far they are concentric. That is to say, even if the outer linkage member 14c and the cathode holding member 13 shift from each other circumferentially, a welding defect does not occur since welding areas are ensured.
Production Method
Now, a method of producing the cathode body 10 in Embodiment 1 will be described.
The first process in producing the cathode body 10 is a cathode sleeve substrate forming process in which a plurality of three-dimensional, cathode sleeve interim bodies 14d, which will be described later, are formed on a thin Ni belt 20, and wound around a bobbin 24 (see
The next process is a baking/blacking process in which an inner surface of an interim body of the cylindrical heater case member 14a for housing the heater is blacked (see
The baking/blacking process is followed by a first welding process in which the cap member 15 is welded to the interim body of the cylindrical heater case member 14a at the opening thereof (see
The layer forming process is followed by a separation process in which the parts to be used as the cathode bodies 10 are separated from the Ni belt (see
That is to say, the above processes before the separation process have been performed while the objects of the processes are held in the Ni belt.
After the separation process, the cathode sleeve supporting members 14b are bent to generate the cathode body member 12 in a bending process (see
In the next process, a heater welding process, the heater is inserted into the cathode sleeve structure 14, and the heater and the cathode sleeve structure 14 are welded together to form the cathode body 10 (see
Now, each process will be detailed.
1. Cathode Sleeve Substrate Forming Process
First, a belt that is 0.1 mm thick and made of Ni at a purity degree of 99.9% is pressed by, for example, deep drawing to form a plurality of cup-shaped protrusions. The tops of the protrusions are then cut to make openings. This forms bodies (hereinafter referred to as heater case member interim bodies 14e) that are to become the heater case members 14a later.
Portions of the Ni belt surrounding (i) bodies (hereinafter referred to as supporting member interim bodies 14f) that are to become the cathode sleeve supporting members 14b later and (ii) bodies (hereinafter referred to as outer linkage member interim bodies 14g) that are to become the outer linkage members 14c later are stamped out to form a plurality of bodies (hereinafter referred to as cathode sleeve interim bodies 14d) that are to become the cathode sleeve structures 14 later. In each cathode sleeve interim body 14d, the heater case member interim body 14e, the supporting member interim bodies 14f, and the outer linkage member interim body 14g are formed as one piece.
This process of forming the cathode sleeve interim bodies 14d on a thin metal belt is referred to as the cathode sleeve substrate forming process. Also, the thin metal belt on which the cathode sleeve interim bodies 14d are formed is referred to as a cathode sleeve substrate 22.
As shown in
The cathode sleeve substrate 22 in which the plurality of cathode sleeve interim bodies 14d have been formed is wound in the bobbin 24 with such a tension as can maintain the shapes of the heater case member interim bodies 14e, the supporting member interim bodies 14f, and the outer linkage member interim bodies 14g. The bobbin 24 holding the cathode sleeve substrate 22 is then stored and transferred.
2. Baking/Blacking Process
In the baking/blacking process, inner surfaces of the heater case member interim bodies 14e are blacked as follows.
The cathode sleeve substrate 22 is unwound from the bobbin 24. Then, as shown in
More particularly, the tungsten-alumina powder is composed of a high-melting-point metal and an inorganic binder, where the high-melting-point metal is composed of tungsten powder having average particle diameter of 1 μm and sintered alumina having average particle diameter of 5–10 μm.
It should be noted here that if the main component of the cathode sleeve substrate 22 is chrome, the inner surface of each heater case member interim body 14e can be blacked only by baking, without applying the tungsten-alumina powder.
3. First Welding Process
In the first welding process, as shown in
The first welding process is performed while the cathode sleeve interim bodies 14d is integral with the cathode sleeve substrate 22.
4. Layer Forming Process
In the layer forming process, an oxide cathode, namely the electron emission material layer 16 is formed by, for example, spraying an alkaline earth metal that is an electron emission material, onto a masking material sheet so that the electron emission material passes through an opening of the masking material sheet and heaps on the outer surface of the cap member 15.
5. Separation Process
In the separation process, as shown in
It is desirable from the viewpoint of preventing deformation of the cathode sleeve supporting members 14b that if the total number of processes is expressed by “n”, the separation process should be performed in n/2th process or onward when n is an even number, and in (n+1)/2th process or onward when n is an odd number, that is, in the latter half of the whole process.
6. Bending Process
In the bending process, first the interim product 12a shown in
It should be noted here that the cross-sectional view of the interim product 12a shown in
As shown in
As shown in
7. Second Welding Process
In the second welding process, the ring-shaped outer linkage member 14c of the cathode body member 12 and the cylindrical cathode holding member 13 are welded together.
First, as shown in
With this operation, the ring-shaped outer linkage member 14c of the cathode body member 12 and the cylindrical cathode holding member 13 are fixed to each other by welding.
As described above, in the second welding process of Embodiment 1, the ring-shaped outer linkage member 14c is spot-welded to a top end of the cathode holding member 13, while in the conventional method, free ends of the three supporting members 106 are spot-welded onto a top end of the cathode holding member 105.
With the above-described construction of Embodiment 1, even if the cathode body member 12 and the cathode holding member 13 shift from each other due to rotation, the outer linkage member 14c always overlaps the top end of the cathode holding member 13. This prevents occurrence of welding defects since welding areas are ensured.
8. Heater Welding Process
As shown in
This completes the cathode body 10.
As described above, the cathode body 10 is produced in eight processes. Of these, in the first five processes including the separation process, the object of the processes is stored and transferred as the cathode sleeve substrate 22 which is in a form in which the supporting member interim bodies 14f, which have a weak construction, are less prone to being directly applied external forces.
That is to say, even if no special storage jig or transfer jig is used, the weak supporting member interim bodies 14f and cathode sleeve supporting members 14b are prevented from being deformed by external forces. In such arrangements, off course, the object component is not mounted on such a special storage jig or transfer jig in the baking/blacking process or a welding process.
A number of operations of catching hold of a component or placing it on a certain place are performed in the conventional production method. In contrast, the production method of Embodiment 1 hardly requires such operations. As a result, the present production method can prevent the cathode sleeve supporting members 14b, which are prone to being deformed during such operations, from being deformed.
Further, even after the interim product 12a is separated in the separation process, an external force exerted on a cathode sleeve supporting member 14b is distributed to the other supporting members 14b by the outer linkage member 14c to which the three supporting members 14b are connected. Accordingly, this construction prevents the cathode sleeve supporting members 14b from being deformed by external forces during storage or transfer.
Yield Improvement Confirmation Test
Now, the cathode body 10 having been produced through the above-described processes and having the above-described construction will be discussed in terms of the yield.
The inventors of the present invention made a prototype of the cathode body 10 through the processes in Embodiment 1 to have the unique construction, and checked the yield of the prototype in terms of: (i) deformation of the cathode sleeve supporting members 14b in the baking/blacking process; (ii) deformation of the cathode sleeve supporting members 14b to the level of unusable state that occurs in the second welding process when the cathode body member 12 is mounted on a welding apparatus to be welded to the cathode holding member 13; (iii) deformation of the cathode sleeve supporting members 14b during the welding in the second welding process; and (iv) welding defect caused during the welding in the second welding process.
The specifications of the prototype of the cathode body 10 are as follows.
The cathode sleeve structure 14 is formed using a Ni plate that is 0.05 mm thick.
The cylindrical heater case member 14a has an outer diameter of 1.6 mm. The cathode sleeve supporting member 14b is 0.3 mm wide and 3 mm long. The ring-shaped outer linkage member 14c is 0.2 mm wide.
The cap member 15 is slipped over and welded to the cathode sleeve structure 14.
The specifications of a test sample of the conventional cathode body 100 that was prepared for the sake of comparison are as follows.
The sample of the conventional cathode body 100 has the cathode sleeve 102 and the cathode sleeve supporting members 106 as separate components, and does not have an equivalent of the ring-shaped outer linkage member 14c shown in
The following Table 1 shows the results of the yield improvement confirmation test the inventors conducted.
As Table 1 indicates, for each of the items (i) to (iv), the cathode body 10 in Embodiment 1 is superior to the conventional cathode body 100 in yield.
Especially, the effect of the cathode body 10 for preventing (i) deformation of the cathode sleeve supporting members 14b in the baking/blacking process is prominent.
The reason why the yield of (iv) welding defect in the welding process has been improved in the cathode body 10 of Embodiment 1 is considered as follows. Conventionally, the cathode sleeve supporting members 14b can be welded only at their ends. In contrast, in the cathode body 10 of Embodiment 1, welding can be performed on the whole area of the ring-shaped outer linkage member 14c. With this construction, even if a welding position on the outer linkage member 14c shifts circumferentially, a welding defect does not occur.
Also, the total yield of the items (i) to (iv) is 95.1% in the cathode body 10 in Embodiment 1 and 55.2% in the conventional cathode body 100. That is to say, the cathode body 10 and its production method in Embodiment 1 provide an approximately double improvement in yield.
Also, with such a construction and production method, even if an external force is exerted on a cathode sleeve supporting member 14b in a production process of the cathode body 10, the external force is distributed to the other supporting members 14b by the outer linkage member 14c, and the cathode sleeve supporting members 14b are prevented from being deformed by external forces.
In the present production method, interim products are transferred in the form of the cathode sleeve substrate 22 which is less prone to being directly applied external forces. With such arrangements, the weak cathode sleeve supporting members 14b constituting the cathode sleeve substrate 22 are prevented from being deformed by external forces. This improves the cathode body 10 in yield.
Variations
In Embodiment 1, the cathode sleeve supporting members 14b are made from plane plates. Not limited to this, the cathode sleeve supporting members 14b may be sticks, with their cross-sectional profile substantially being a circle.
In Embodiment 1, the top end of the cathode holding member 13 is circular, when viewed from above. Not limited to this, the top end of the cathode holding member 13 may be, for example, rectangular. Note that in correspondence with adoption of the shape, the shape of the outer linkage member 14c of the cathode sleeve structure 14 should also be rectangular.
In Embodiment 1, the cathode holding member 13 and the outer linkage member 14c are welded together. Not limited to this, the outer linkage member 14c may be formed to connect each cathode sleeve supporting member 14b at some midpoint thereof as shown in
The above-mentioned construction has the same effect, provided by the outer linkage member 14c, of distributing an external force exerted on a cathode sleeve supporting member 14b to the other cathode sleeve supporting members 14b, as is the case with Embodiment 1. However, the above-mentioned construction does not have the effect of preventing a welding defect from occurring when the welding position is shifted. As a result, the relative position between the cathode sleeve supporting members 14b and the cathode holding member 13 should be controlled strictly.
In Embodiment 1, each of the extending cathode sleeve supporting members 14b is connected to the outer linkage member 14c. However, not limited to this, at least a pair of cathode sleeve supporting members 14b adjacent to each other, among a plurality of cathode sleeve supporting members 14b, may be connected to each other by the outer linkage member 14c.
For example, suppose that three cathode sleeve supporting members 14b1, 14b2, and 14b3 are provided. Then, the cathode sleeve supporting members 14b1 and 14b2 are connected together by the outer linkage member 14c, but the cathode sleeve supporting member 14b3 is not connected to any other cathode sleeve supporting members.
In this case, if an external force is exerted on any of the cathode sleeve supporting members 14b1 and 14b2, the force is distributed to the other supporting member, and therefore the supporting members are prevented from being deformed.
In this case, the resistance of the cathode sleeve supporting member 14b3 to the deformation is the same as the conventional one. However, since the resistance to the deformation of the other two cathode sleeve supporting members has improved, the resistance to the deformation of the cathode sleeve supporting members has improved as a whole.
In Embodiment 1, the outer linkage member 14c is shaped like a ring. Not limited to this, the ring-shaped outer linkage member 14c may be divided into three pieces that correspond to the three cathode sleeve supporting members 14b, respectively, as shown in
For the sake of conveniences, a gap between each pair of such pieces of the ring-shaped outer linkage member 14c is referred to as a slit 14h, and such a piece of the ring-shaped outer linkage member 14c is referred to as an extended outer linkage member 14i.
With this construction, when an external force in a certain range of force levels is exerted on a cathode sleeve supporting member 14b, the cathode sleeve supporting member 14b is elastically deformed, and an extended outer linkage member 14i connected to the cathode sleeve supporting member 14b comes into contact with the other extended outer linkage members 14i. As a result of this, the external force is distributed to the other cathode sleeve supporting members 14b.
After the external force is removed, the cathode sleeve supporting member 14b and the corresponding extended outer linkage member 14i return to the original positions.
The inventors of the present invention found that the above-stated effect is obtained when the slit 14h is 0.5 mm in width.
Also, with the above-described construction, since the cathode sleeve supporting members 14b do not connect to each other due to gaps between the extended outer linkage members 14i, when the cathode sleeve supporting members 14b and the extended outer linkage members 14i are formed, they are less prone to having defects such as a crack even if they have some plastic deformation. This reduces restrictions imposed on the shapes of these members in the formation process.
More particularly, when, as in Embodiment 1, the cylindrical heater case member 14a, cathode sleeve supporting members 14b, and outer linkage member 14c are formed as one piece, it is impossible to further decrease a bending angle θ (see
In connection with this variation, the ring-shaped outer linkage member 14c may not be completely separated into three pieces, but may have slits that stops halfway through the width so that pieces demarcated by the slits connect to each other.
In Embodiment 1, the ring-shaped outer linkage member 14c is spot-welded to a top end of the cathode holding member 13 at a plurality of spots. However, the ring-shaped outer linkage member 14c and the top end of the cathode holding member 13 may be welded over the whole circumference.
In Embodiment 1, the cap member 15 is formed separately from the heater case member interim bodies 14e. However, the cap member 15 and the heater case member interim bodies 14e may be formed as one piece, which can be achieved by omitting the process of cutting the tops of the cut-shaped protrusions formed on the Ni belt, as shown in
In this variation, the first welding process in which the cap member 15 is welded to the heater case member interim body 14e is not necessary. This further reduces the chance that the cathode sleeve supporting members 14b may be deformed.
In the description provided so far, the ring-shaped outer linkage member 14c and the cathode holding member 13 are welded together. Not limited to this, the following is possible, for example.
As shown in
In this way, the cathode sleeve supporting members 14b of the cathode sleeve structure 14 are welded to the cathode holding member 13.
In such a production method, although a process of cutting the outer linkage member 14c is additionally performed, a conventional welding apparatus can be used. Furthermore, since the cathode sleeve supporting members 14b are not liberated until immediately before the cathode body member 12 and the cathode holding member 13 are welded together, it is possible to protect the cathode sleeve supporting members 14b from deformation until immediately before the welding.
In connection with this variation, the ring-shaped outer linkage member 14c may be cut as shown in
In Embodiment 1, in the first five processes including the separation process among a total of eight processes, the cathode sleeve substrate 22 containing a plurality of cathode sleeve interim bodies 14d is stored and transferred. Not limited to this, the cathode sleeve interim bodies 14d may be separated from the cathode sleeve substrate 22 in the first process and then stored and transferred in the following processes, for example.
In this case, if an external force is exerted on a supporting member interim body 14f of a separated cathode sleeve interim body 14d, the external force is distributed to the other supporting member interim bodies 14f by the outer linkage member interim body 14g to which the three supporting member interim bodies 14f are connected and fixed. The supporting member interim body 14f is protected from deformation in this way.
In Embodiment 1, the cathode sleeve structure 14 is made of Ni at a purity degree of 99.9%. Embodiment 1 also provides particular dimensions of the cathode sleeve structure 14 and the cathode sleeve supporting members 14b, and a particular method of blacking that is used in the baking/blacking process. However, not limited to these particulars, the materials, dimensions or the baking/blacking method may be modified variously in so far as they are no worse than conventional ones in terms of the heat loss and the product quality, on condition that the heater case member 14a, the cathode sleeve supporting members 14b, and the outer linkage member 14c are formed as one piece.
The inventors of the present invention conducted a performance test on six electron guns in which six different cathode bodies are embedded, respectively, to detect materials, dimensions, and baking/blacking methods that can replace those disclosed in Embodiment 1, on condition that they are no worse than conventional ones in terms of the heat loss and the product quality.
The measurement object of each test is the cathode sleeves of two outer cathode bodies among three cathode bodies in each inline-type electron gun.
Specifications of Test Samples
1. Specifications of Conventional Cathode Body 100
Specifications of a conventional cathode body 100 prepared for the test are as follows.
The cylindrical cathode sleeve 102 is made of 20% of Cr (chromium) and 80% of Ni (nickel), has an outer diameter of 1.6 mm, and is 2.5 mm high and 0.04 mm thick. The cathode sleeve supporting member 106 is 2.5 mm long, 0.3 mm wide, and 0.1 mm thick.
The cathode sleeve supporting member 106 is made of Ni—Fe and is welded to the cathode sleeve 102 and the cathode holding member 105.
The cathode sleeve 102 has been baked in humid hydrogen. Black chromic oxide has been formed on the inner and outer surfaces of the cathode sleeve 102.
The cap member 103 is made of Ni at a purity degree of 99.9%. Also, a BaCO3 layer, which is approximately 0.065 mm thick, has been formed as the electron emission material layer 104, on an outer surface the cap member 103.
The heater 101 is a 0.65 watt heater.
2. Specifications of Cathode Body as Comparative Example (1)
Specifications of a cathode body as a comparative example (1), which was produced in the same way as the cathode body 10 in Embodiment 1 except that it did not undergo the baking/blacking process, are as follows.
The cathode sleeve structure is the same as the cathode body 10 in Embodiment 1 in that it is made of Ni at a purity degree of 99.9%, but is different in that the cylindrical heater case member 14a has a diameter of 1.5 mm, and is 2.5 mm high and 0.1 mm thick.
The cathode sleeve supporting member is the same as the cathode body 10 in Embodiment 1 in that it is 0.3 mm wide, but is different in that it is 2.0 mm long and 0.1 mm thick.
The cap member 15 is made of Ni at a purity degree of 99.9%. Also, a layer, which is approximately 0.065 mm thick and whose principal element is BaO (barium oxide), has been formed as the electron emission material layer 104, on an outer surface the cap member 15.
The heater is a 0.65 watt heater.
3. Specifications of Cathode Body as Comparative Example (2)
Specifications of a cathode body as a comparative example (2) differ from those of the cathode body 10 in Embodiment 1 only in that, as shown in
4. Specifications of Cathode Body as Comparative Example (3)
Specifications of a cathode body as a comparative example (3) are the same as those of the cathode body as the comparative example (1) in terms of the material and quality, except that the inner surface of the cathode sleeve structure has been blacked by a combination of a high-melting-point metal and an inorganic binder, where the high-melting-point metal is composed of tungsten powder having average particle diameter of 1 μm and sintered alumina having average particle diameter of 5–10 μm.
5. Specifications of Cathode Body as Comparative Example (4)
Specifications of a cathode body as a comparative example (4) are the same as those of the cathode body as the comparative example (1) in terms of the material and quality, except that 0.1% of Mg (magnesium) has been added to the material (Ni) of the cathode sleeve structure 14.
6. Specifications of Cathode Body as Comparative Example (5)
Specifications of a cathode body as a comparative example (4) are the same as those of the cathode body as the comparative example (1) in terms of the material and quality, except that the cathode sleeve structure 14 has been blacked by allowing the cathode sleeve structure made of 20% of Cr and 80% of Ni to undergo a hydrogen process, then an oxidation process at approximately 700° C., then a baking process at approximately 1000° C. in humid hydrogen, so that a layer of Cr2O3 is formed on a surface of the cathode sleeve structure.
Now, the results of the test conducted on the above-described six test samples will be described.
Note that in
Test Results
The inventors measured the temperatures of the cathode bodies as the test samples at the initial stage, and obtained the variations, namely the standard deviation.
The reason why the inventors obtained the temperature variations is as follows.
A color cathode ray tube contains three cathode bodies. If the operation temperatures of the cathode bodies vary greatly, the speeds at which the electron emission characteristics of the electron emission material layers degrade differ from each other, then the three electron beam currents of the cathode ray tube vary. This causes the white balance to come undone, and causes color tone deficiencies.
It should be noted here that the electron beam current of each cathode body is obtained as a ratio of an electric current value after a lapse of 2,000 hours to the initial one.
It has been found that the variation in the temperature of cathode body is caused by the difference in the amount of heat conducted from the heater 11 to the electron emission material layer 16.
That is to say, a challenge to be addressed in the product or production is to suppress the difference in the amount of conducted heat.
Here, as shown in
The obtained values indicate that the comparative examples (1) to (5) have smaller variation in the temperature immediately after the operation start, than the conventional cathode body.
The tendency is prominent in the comparative examples (3) and (5).
As shown in
The obtained values indicate that the comparative examples (1) to (5) have smaller variation in the temperature after a lapse of 2,000 hours, than the conventional cathode body.
The tendency is prominent in the comparative examples (3) and (5), as is the case with the initial stage.
As shown in
The results indicate that the comparative examples (1) to (5) have smaller variation in the electron beam current, than the conventional cathode body.
The tendency is prominent in the comparative example (4).
As shown in
The results indicate that the comparative examples (1) to (5) have smaller variation in the time required to display a stable image, than the conventional cathode body.
The tendency is prominent in the comparative examples (2), (3), and (5), where the time required to display a stable image is relatively short.
As understood from the above-described test results, the comparative examples (1) to (5) have enough qualities as the products since they have smaller variations in the temperature and electron beam current, compared with the conventional cathode body.
It is considered that one of the reasons why the cathode bodies (1) to (5) have smaller variations in the temperature and electron beam current than the conventional one is that the cylindrical heater case member 14a and the cathode sleeve supporting member 14b are formed as one piece, not bonded together by welding, and that therefore the obtained products are stable in shape and the variation in the heat loss is suppressed in each cathode body.
Also, in the cathode bodies as the comparative examples (1) to (4), the cathode sleeve structure is made of a material whose principal element is Ni. However, Fe (iron), Co (cobalt), or Cr may be used as the principal element of the cathode sleeve structure. Also, the cathode sleeve structure may be made of a material that contains Ni as its principal element, and Fe or Co as well.
Here, an optimal combination of materials may be selected from the above-described options, considering the heat conductivity, coefficient of thermal expansion, rigidity, and cost of the cathode sleeve structure 14.
To increase the heat resistance, it is desirable to form the cathode sleeve structure 14 using, as its principal element, any of Ta (tantalum), Mo (molybdenum), and Nb (niobium) that have high melting points of no lower than 2,000° C.
In the cathode body as the comparative example (4), Mg is used as an additive. However, Cr, Si (silicon), W (tungsten), or Al (aluminum) may be used as an additive, instead of Mg. Also, any combination of the above-mentioned metals may be used as an additive in the cathode body.
Also, the cathode sleeve structure 14 may be formed by containing, as its principal element, any of Fe, Co, Ta, Mo, Nb, and Cr, and any combination of metals selected from Mg, Si, Cr, W, and Al as an additive. Needless to say, Cr is not used both as its principal element and an additive.
The cathode body in Embodiment 1 has been described in terms of an oxide cathode that is used in a general-purpose cathode ray tube. However, the cathode body is applicable to an impregnation-type cathode that is used in a high-brightness, high-definition cathode ray tube.
The cathode body to be applied to a high-brightness, high-definition cathode ray tube may be formed by covering a porous tungsten pellet with a cap, and welding the tungsten pellet to the cathode sleeve structure 14, not by forming the electron emission material layer 16 on the cap member 15 by spraying the electron emission material.
Alternatively, the cathode body may be formed by welding the tungsten pellet onto the top-surface member 14j shown in
Embodiment 2
The following describes a cathode body 30 in Embodiment 2.
Construction
As is the case with the cathode body 10 in Embodiment 1, the cathode body 30 is used in a cathode ray tube and includes a cathode for generating electrons and a member for supporting the cathode.
The cathode body 30 has the same construction as the cathode body 10 except that the heater case member 14a and the heater case member interim bodies 14e are partially modified in shape.
The following will describe the differences between the cathode body 30 and the cathode body 10.
Note that for the sake of conveniences, some components of the cathode body 30 in Embodiment 2 are assigned different reference numbers from corresponding components in Embodiment 1. The cathode body member 32, interim product 32a, cathode holding member 33, cathode sleeve structure 34, heater case member 34a, cathode sleeve supporting members 34b, outer linkage member 34c, cathode sleeve interim bodies 34d, heater case member interim bodies 34e, supporting member interim bodies 34f, outer linkage member interim bodies 34g in Embodiment 2 correspond to the components 12, 12a, 13, 14, 14a, 14b, 14c, 14d, 14e, 14f, and 14g in Embodiment 1, respectively.
As shown in
Production Method
Now, a production method of the cathode body 30 will be described.
The flange 34k is formed in the first process in Embodiment 1, the cathode sleeve substrate forming process. The other processes are the same as Embodiment 1, except that in the bending process, a bending jig in a different shape from that in Embodiment 1 is used.
The following is a description of the cathode sleeve substrate forming process and the bending process which are different from Embodiment 1.
Cathode Sleeve Substrate Forming Process
The heater case member interim body 14e of the cathode body 10 in Embodiment 1 has a constant thickness t0 0.05 mm, except for portions from which the supporting member interim bodies 14f extend. In contrast, the heater case member interim body 34e of the cathode body 30f in Embodiment 2 has the flange 34k that is 0.03 mm (t2−t0) thick and 0.1 mm high, as shown in
Bending Process
As shown in
It should be noted here that the cross-sectional view of the interim product 32a shown in
As shown in
As shown in
In the bending process in Embodiment 1, the supporting member interim bodies 14f being 0.05 mm thick are bent while they are directly sandwiched by the bending jigs 28a and 28b. In such an operation, a shearing force may be applied to bucking B (see
In the bending process in Embodiment 2, when the bending jig 38a is lowered to bend the supporting member interim bodies 34f, the tip 38d of the bending jig 38a is contacting the top surface of the thick flange 34k, not the thin supporting member interim bodies 34f. As a result, bucking D is less apt to have a crack.
That is to say, the shape improved by the flange 34k and the improved bending process further increase the yield of the cathode body 30.
Restriction in Height of Flange 34k
Though the flange 34k increases the yield of the cathode body 30 as described above, it may increase the amount of heat loss, namely amount of heat conducted from the cathode sleeve structure 34 to the cathode holding member 33.
More specifically, the higher the height “h” of the flange 34k is, the larger the amount of heat loss, namely amount of heat conducted from the cathode sleeve structure 34 to the cathode holding member 33 is.
The inventors, after an elaborate investigation, have found that when the heater case member 34a is 0.05 mm thick and the cathode sleeve supporting member 34b is 0.05 mm thick and 0.25 mm wide, a certain correspondence between (a) the heat loss and (b) a value (hereinafter referred to as shape ratio value (C)) obtained by dividing the height h of the flange 34k by the thickness t1 of the cathode sleeve supporting member 34b is observed.
As shown in
The inventors determined an upper limit of the shape ratio value (C) to be 3.5, considering the above-described deterioration in the heat loss.
The inventors also determined a lower limit of the shape ratio value (C) to be 1. This is because when the height h of the flange 34k is smaller than the thickness t1 of the cathode sleeve supporting member 34b, that is, when the shape ratio value (C) is smaller than 1, the tip 38d of the bending jig 38a contacts the cathode sleeve supporting members 34b faster in the bending process, and the cathode sleeve supporting members 34b is apt to have a crack due to a shearing force.
The inventors have also found that to improve the yield in the bending process while restricting the heat loss, it is desirable to set the shape ratio value (C) to 2. This is because the inventors noted that when the shape ratio value (C) increases gradually and reaches 2, the heat loss starts to change (increase) greatly.
For the above reason, the height h of the flange 34k is set to 0.1 mm in correspondence with the desirable value “2” of the shape ratio value (C).
With the above-described construction and method, when the cathode sleeve supporting members 34b are bent in the bending process for the cathode body 30, a direct application of the shearing force to the cathode sleeve supporting members 34b is prevented. This prevents the cathode sleeve supporting members 34b from having a crack, and improves the yield of the cathode body.
In Embodiment 2, the heater case member interim body 34e is formed to have a thickness t2 of 0.08 mm at the lower part where the flange 34k extends. However, not limited to this, the thickness may be varied in so far as the flange 34k can hold the tip 38d of the bending jig 38a at its top when the bending jig 28a is lowered, and the heat loss does not exceed a permissible limit.
Although the present invention has been fully described by way of examples with reference to the accompanying drawings, it is to be noted that various changes and modifications will be apparent to those skilled in the art. Therefore, unless such changes and modifications depart from the scope of the present invention, they should be construed as being included therein.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2001-382676 | Dec 2001 | JP | national |
| 2002-098376 | Apr 2002 | JP | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4184100 | Takanashi et al. | Jan 1980 | A |
| 4370588 | Takahashi et al. | Jan 1983 | A |
| 5164631 | Lee | Nov 1992 | A |
| 5422536 | Hale et al. | Jun 1995 | A |
| 5780959 | Pruvost et al. | Jul 1998 | A |
| Number | Date | Country |
|---|---|---|
| 58175231 | Oct 1983 | JP |
| Number | Date | Country | |
|---|---|---|---|
| 20030173886 A1 | Sep 2003 | US |