High yield ratio-type, hot rolled high strength steel sheet excellent in formability or in both of formability and spot weldability, and production thereof

Description

TITLE OF THE INVENTION
High yield ratio-type, hot rolled high strength steel sheet excellent in formability or in both formability and spot weldability, and production thereof.
TECHNICAL FIELD
The present invention relates to a hot rolled high strength steel sheet (plate) with a high ductility and an excellent formability or excellent formability and spot weldability, directed to use in automobiles, industrial machines, etc. and to a process for producing the same.
BACKGROUND ART
Prior Art
Due to keen demands for lighter weight of automobile steel sheets and safety assurance at collisions of automobiles as main backgrounds, higher strength is required for steel sheets. However, workability is required even for the high strength steel sheets, and steel sheets capable of satisfying the requirements for both strength and workability are in keen demand. Heretofore, dual phase steel (which will be hereinafter referred to as "DP steel") comprising ferrite and martensite has been proposed for hot rolled steel sheets for use in the field that has required a good ductility. It is known that DP steel has a better strength-ductility balance than those of solid solution-intensified, high strength steel sheets and precipitation-intensified, high strength steel sheets, but its strength-ductility balance limit is at TS.times.T.E1.ltoreq.2,000. That is, DP steel fails to meet more strict requirements in the current situations.
As means capable of meeting the requirements in the current situations to attain TS.times.T.E1>2,000, it has been proposed to utilize retained austenite. For example, Japanese Patent Application Kokai (Laid-open) No. 60-43425 discloses a process for producing a steel sheet containing retained austenite, which comprises hot rolling a steel sheet in a temperature range of Ar.sub.3 to Ar.sub.3 +50.degree. C., retaining the steel sheet in a temperature range of 450.degree. to 650.degree. C. for 4 to 20 seconds and coiling it at a temperature of not more than 350.degree. C., and also Japanese Patent Application Kokai (Laid-open) No. 60-165320 discloses a process for producing a steel sheet containing retained austenite, which comprises conducting high reduction rolling of a steel sheet at a finishing temperature of not less than 850.degree. C., at an entire draft of at least 80%, a total draft of at least 60% for final three passes and a draft of at least 20% for the ultimate pass, and then conducting cooling to 300.degree. C. or less at a cooling speed of at least 50.degree. C./s.
However, these conventional processes are not preferable in practice from the viewpoints of energy saving and productivity improvement, because of retention at 450.degree. to 650.degree. C. for 4 to 20 seconds during the cooling, coiling at a low temperature such as 350.degree. C. or less, high reduction rolling, etc. Furthermore, the workability of the steel sheets produced by these processes is at TS.times.T.E1<2,400, which would not always have fully satisfied the level required by users. That is, steel sheets having a higher TS.times.T.E1 (desirably more than 2,400) and a high productivity process for producing such steel sheets have still been in demand. On the other hand, in view of the actual formability, not only a good strength-ductility balance, but excellent uniform elongability (stretchability), enlargeability or hole expansibility (enlargeability into a flange shape), bendability, secondary workability, and toughness are also required. Furthermore, in the service field of these steel sheets, spot welding is more and more used, and thus an excellent spot weldability is also required. Still further, not only a higher tensile strength, but also a higher yield ratio (higher yield strength) is required from the viewpoint of strength assurance.
That is, the field of actual application can be considerably broadened by satisfying these requirements at the same time.
(Problems to be solved by the invention)
The present invention provides a hot rolled, high strength steel sheet having an excellent workability, containing retained austenite and being capable of attaining TX.times.T.E1.gtoreq.2,000, which is over the limit of the prior art, and also a process for producing the same. Furthermore, the present invention provides a hot rolled, high strength steel sheet having an excellent formability (strength-ductility balance, uniform elongability, enlargeability, bendability, secondary workability and toughness), a high yield ratio and an excellent spot weldability at the same time and also a process for producing the same.
DISCLOSURE OF INVENTION
To solve the above-mentioned problems, the present invention uses the following means (1) to (20):
(1) A high yield ratio-type, hot rolled high strength steel sheet excellent in both formability and spot weldability, characterized by comprising 0.05 to less than 0.16% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, the balance consisting essentially of Fe, as chemical components, being composed of three phases of ferrite, bainite and retained austenite as microstructure, and having a ferrite grain size (d.sub.F) of not more than 5 .mu.m, a ratio (V.sub.F /d.sub.F) of ferrite volume fraction (V.sub.F) to ferrite grain size (d.sub.F) of not less than 20, a volume fraction of retained austenite having a grain size of not more than 2 .mu.m being not less than 5%, and a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.4, and a uniform elongation of not less than 15% as characteristics.
(2) A high yield ratio-type, hot rolled high strength steel sheet excellent in both formability and spot weldability, characterized by comprising 0.05 to less than 0.16% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, and 0.0005 to 0.01% by weight of Ca or 0.005 to 0.05% by weight of REM, the balance being Fe and inevitable elements, as chemical components, being composed of three phases of ferrite, bainite and retained austenite as microstructure, and having a ferrite grain size (d.sub.F) of not more than 5 .mu.m, a ratio (V.sub.F /d.sub.F) of ferrite volume fraction (V.sub.F) to ferrite grain size (d.sub.F) of not less than 20, a volume fraction of retained austenite having a grain size of not more than 2 .mu.m being not less than 5%, and a yield (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.4, ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 and a uniform elongation of not less than 15% as characteristics.
(3) A process for producing a high yield ratio-type, hot rolled high strength steel sheet having both an excellent formability and spot weldability, and also having a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.4 and a uniform elongation of not less than 15%, characterized by conducting a finish-rolling of a slab prepared by casting a steel comprising 0.05 to less than 0.16% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, the balance consisting essentially of Fe, as chemical components, in an end temperature range of Ar.sub.3 .+-.50.degree. C. at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
(4) A process for producing a high yield ratio-type, hot rolled high strength steel sheet having both an excellent formability and spot weldability, and also having a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.4 and a uniform elongation of not less than 15%, characterized by conducting a finish-rolling of a slab prepared by casting a steel containing 0.05 to less than 0.16% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, and 0.0005 to 0.01% by weight of Ca or 0.005 to 0.05% by weight of REM, the balance being Fe and inevitable elements, as chemical components, in an end temperature range of Ar.sub.3 .+-.50.degree. C., at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
(5) A process for producing a high yield ratio-type, hot rolled high strength steel sheet having both an excellent formability and spot weldability, and also having a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.4 and a uniform elongation of not less than 15%, characterized by conducting a finish-rolling of a slab prepared by casting a steel comprising 0.05 to less than 0.16% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, the balance consisting essentially of Fe, as chemical components, at an end temperature of not less than Ar.sub.3 -50.degree. C., at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table down to a temperature T.sub.1 in a range of not more than Ar.sub.3 to more than Ar.sub.1 at a rate of less than 30.degree. C./second, and from T.sub.1 downwards at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
(6) A process for producing a high yield ratio-type, hot rolled high strength steel sheet having both an excellent formability and spot weldability, and also having a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%) an enlargement ratio (d/d.sub.o) of not less than 1.4 and a uniform elongation of not less than 15%, characterized by conducting a finish-rolling of a slab prepared by casting a steel comprising 0.05 to less than 0.16% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, and 0.0005 to 0.01% by weight of Ca or 0.005 to 0.05% by weight of REM, the balance being Fe and inevitable elements, as chemical components, at an end temperature of not less than Ar.sub.3 -50.degree. C., at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table down to a temperature T.sub.1 in a range of not more than Ar.sub.3 to more than Ar.sub.1, at a rate of less than 30.degree. C./second, and from T.sub.1 downwards at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
(7) A process for producing a high yield ratio-type, hot rolled high strength steel sheet having both an excellent formability and spot weldability, and also having a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.4 and a uniform elongation of not less than 15%, characterized by conducting a finish-rolling of a slab prepared by casting a steel comprising 0.05 to less than 0.16% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, the balance consisting essentially of Fe, as chemical components, at an end temperature of not less than Ar.sub.3 -50 .degree. C., at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table down to a temperature T.sub.1 in a range of not more than Ar.sub.3 to more than Ar.sub.1 at a rate of not less than 30.degree. C./second, and from T.sub.1 downwards to a temperature T.sub.2 in a range of not more than T.sub.1 to more than Ar.sub.1 at a rate of less than 30.degree. C./second, and furthermore from T.sub.2 downwards at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
(8) A process for producing a high yield ratio-type, hot rolled high strength steel sheet having both an excellent formability and spot weldability, and also having a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.4 and a uniform elongation of not less than 15%, characterized by conducting a finish-rolling of a slab prepared by casting a steel comprising 0.05 to less than 0.16% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, and 0.0005 to 0.01% by weight of Ca or 0.005 to 0.05% by weight of REM, the balance being Fe and inevitable elements, as chemical components, at an end temperature of not less than Ar.sub.3 -50.degree. C., at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table down to a temperature T.sub.1 in a range of not more than Ar.sub.3 to more than Ar.sub.1 at a rate of not less than 30.degree. C./second, and from T.sub.1 downwards to a temperature T.sub.2 in a range of not more than T.sub.1 to more than Ar.sub.1 at a rate of less than 30.degree. C./second, and furthermore from a T.sub.2 and downwards at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
(9) A high yield ratio-type, hot rolled high strength steel sheet excellent in formability, characterized by comprising 0.16 to less than 0.30% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, the balance consisting essentially of Fe, as chemical components, being composed of three phases of ferrite, bainite, and retained austenite as microstructures, and having a ferrite grain size (d.sub.F) of not more than 5 .mu.m, a ratio (V.sub.F /d.sub.F) of ferrite volume fraction (V.sub.F) to ferrite grain size (d.sub.F) of not less than 7, a volume fraction of retained austenite having a grain size of not more than 2 .mu.m being not less than 5%, and a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.1, and a uniform elongation of not less than 10% as characteristics.
(10) A high yield ratio-type, hot rolled high strength steel sheet excellent in formability, characterized by comprising 0.16 to less than 0.30% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, and 0.0005 to 0.01% by weight of Ca or 0.005 to 0.05% by weight of REM, the balance being Fe and inevitable elements, as chemical components, being composed of three phases of ferrite, bainite, and retained austenite as microstructures, and having a ferrite grain size (d.sub.F) of not more than 5 .mu.m, a ratio (V.sub.F /d.sub.F) of ferrite volume fraction (V.sub.F) to ferrite grain size (d.sub.F) of not less than 7, a volume fraction of retained austenite having a grain size of not more than 2 .mu.m being not less than 5%, and a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.1, and a uniform elongation of not less than 10% as characteristics.
(11) A process for producing a high yield ratio-type, hot rolled high strength steel sheet having an excellent formability and also a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.1, and a uniform elongation of not less than 10%, characterized by conducting a finish-rolling of a slab prepared by casting a steel comprising 0.16 to less than 0.30% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, the balance consisting essentially of Fe, as chemical components, in an end temperature range of Ar.sub.3 .+-.50.degree. C. at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
(12) A process for producing a high yield ratio-type, hot rolled high strength steel sheet having an excellent formability and also a yield ratio (YR) of not less than 60%, ratio (d/d.sub.o) of not less than 1.1, and a uniform elongation a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement of not less than 10%, characterized by conducting a finish-rolling of a slab prepared by casting a steel comprising 0.16 to less than 0.30% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, and 0.0005 to 0.01% by weight of Ca or 0.005 to 0.05% by weight of REM, the balance being Fe and inevitable elements, as chemical components, at an end temperature range of Ar.sub.3 .+-.50.degree. C. at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
(13) A process for producing a high yield ratio-type, hot rolled high strength steel sheet having an excellent formability and also a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.1, and a uniform elongation of not less than 10%, characterized by conducting a finish-rolling of a slab prepared by casting a steel comprising 0.16 to less than 0.30% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, the balance consisting essentially of Fe, as chemical components, at an end temperature of not less than Ar.sub.3 -50.degree. C., at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table down to a temperature T.sub.1 in a range of not more than Ar.sub.3 to more than Ar.sub.1 at a rate of less than 30.degree. C./second, and from T.sub.1 downwards at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
(14) A process for producing a high yield ratio-type, hot rolled high strength steel sheet having an excellent formability and also a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.1, and a uniform elongation of not less than 10%, characterized by conducting a finish-rolling of a slab prepared by casting a steel comprising 0.16 to less than 0.30% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, and 0.0005 to 0.01% by weight of Ca or 0.005 to 0.05% by weight of REM, the balance being Fe and inevitable elements, as chemical components, at an end temperature of not less than Ar.sub.3 -50.degree. C., at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table down to a temperature T.sub.1 in a range of not more than Ar.sub.3 to more than Ar.sub.1, at a rate of less than 30.degree. C./second and from T.sub.1 downwards at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
(15) A process for producing a high yield ratio-type, hot rolled high strength steel sheet having an excellent formability and also a yield ratio (YR) of not less than 60%, ratio (d/d.sub.o) of not less than 1.1, and a uniform elongation a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement of not less than 10%, characterized by conducting a finish-rolling of a slab prepared by casting a steel comprising 0.16 to less than 0.30% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, the balance consisting essentially of Fe, as chemical components, at an end temperature of not less than Ar.sub.3 -50.degree. C. at an entire draft of not less than 80%, and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table down to a temperature T.sub.1 in a range of not more than Ar.sub.3 to more than Ar.sub.1 at a rate of not less than 30.degree. C./second, from T.sub.1 downwards to a temperature T.sub.2 in a range of not more than T.sub.1 to more than Ar.sub.1 at a rate of less than 30.degree. C./second, and furthermore from T.sub.2 downwards at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
(16) A process for producing a high yield ratio-type, hot rolled high strength steel sheet having an excellent formability and also a yield ratio (YR) of not less than 60%, ratio (d/d.sub.o) of not less than 1.1, and a uniform elongation a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement of not less than 10%, characterized by conducting a finish-rolling of a slab prepared by casting a steel comprising 0.16 to less than 0.30% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, and 0.0005 to 0.01% by weight of Ca or 0.005 to 0.05% by weight of REM, the balance being Fe and inevitable elements, as chemical elements, at an end temperature of not less than Ar.sub.3 -50 .degree. C. at an entire draft of not less than 80%, and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table down to a temperature T.sub.1 in a range of not more than Ar.sub.3 to more than Ar.sub.1 at a rate of not less than 30.degree. C./second, from T.sub.1 downwards to a temperature T.sub.2 in a range of not more than T.sub.1 to more than Ar.sub.1 at a rate of less than 30.degree. C./second, and furthermore from T.sub.2 downwards at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
(17) A process for producing a high yield ratio-type, hot rolled high strength steel sheet excellent in both formability and spot weldability according to any one of the above mentioned items (3) to (8), characterized in that the hot finish-rolling initiation temperature of the steel is not more than Ar.sub.3 +100.degree. C.
(18) A process for producing a high yield ratio-type, hot rolled high strength steel sheet excellent in both formability and spot weldability according to any one of the above mentioned items (3) to (8), characterized in that after the coiling the steel sheet is cooled to 200.degree. C. or less at a cooling speed of not less than 30.degree. C./hour.
(19) A process for producing a high yield ratio-type, hot rolled high strength steel excellent in formability according to any one of the above mentioned items (11) to (16), characterized in that the hot finish-rolling initiation temperature of the steel is not more than Ar.sub.3 +100.degree. C.
(20) A process for producing a high yield ratio-type, hot rolled high strength steel sheet excellent in formability according to any one of the above mentioned items (11) to (16), characterized in that after the coiling the steel sheet is cooled to 200.degree. C. or less at a cooling speed of not less than 30.degree. C./hour.
(Function)
As a result of extensive tests and studies, the present inventors have solved the problems of the prior art and have found a hot rolled high strength steel sheet having an excellent formability, a high yield ratio and an excellent spot weldability together, and a process for producing the same.
Firstly, the microstructure of a steel sheet that can meet an excellent formability and a high yield ratio at the same time must be composed of three phases of ferrite, bainite and retained austenite, where the retained austenite has grain sizes of not more than 2 .mu.m at a volume fraction of not less than 5%; ferrite grain size (d.sub.F) is not more than 5 .mu.m; and V.sub.F /d.sub.F (V.sub.F : ferrite volume fraction in %, d.sub.F : ferrite grain size in .mu.m) is not less than 20 (or not less than 7 when C is in a range of 0.15 to less than 0.3% by weight, because finer retained austenite grains can be readily formed).
In Table 1, their relations are shown, and their points are summarized in the following items 1 to 3:
TABLE 1__________________________________________________________________________Microstructure of steel sheet Bainite, otherCharacteristics .gamma..sub.R V.sub.F /d.sub.F .gtoreq. 20 V.sub.F /d.sub.F .gtoreq. phase thanof steel sheet .ltoreq.2 .mu.m .gtoreq.5% d.sub.F .ltoreq. 5 .mu.m 0.05% .ltoreq. C <0.15% 0.15% .ltoreq. C ferrite,__________________________________________________________________________ .gamma..sub.RStrength-ductility balance .largecircle. .largecircle. .largecircle.Uniform elongation .largecircle. .largecircle. .largecircle.(stretchability)Enlargeability .largecircle. .largecircle. .largecircle.(enlargeability into flange shape)Bendability .largecircle. .largecircle. .largecircle.Secondary workability .largecircle. .largecircle. .largecircle. .largecircle.Toughness .largecircle. .largecircle. .largecircle. .largecircle. .largecircle.Yield ratio (yield strength) .largecircle. .largecircle. .largecircle. .largecircle.__________________________________________________________________________ .largecircle. shows a strong corelation
1 Increase in the retained austenite contributes to improvements of strength-ductility balance and uniform elongation, and its effect is enhanced by making the retained austenite grains finer. By making the retained austenite grains finer, the enlargeability or the hole expansibility, bendability, secondary workability and toughness can be maintained in an excellent level. That is, by making the content of retained austenite 5% or more and the grain size not more than 2 .mu.m, an excellent strength-ductility balance, an excellent uniform elongation, an excellent enlargeability, an excellent bendability, an excellent secondary workability and an excellent toughness can be obtained at the same time.
2 Increase in V.sub.F /d.sub.F contributes to improvements of the secondary workability and toughness and an increase in the yield ratio through an increase in the ferrite volume fraction and finer ferrite grain size (d.sub.F .ltoreq.5 .mu.m).
3 By making the microstructure composed of three phases of ferrite, bainite and retained austenite, that is, by avoiding the inclusion of pearlite and martensite, the enlargeability, bendability, secondary workability and toughness can be maintained at an excellent level, whereby a high yield ratio can be also maintained.
Secondly, in order to contain retained austenite at a volume fraction of not less than 5%, as shown in FIGS. 1 and 2, it is necessary to control a Si content to 0.5-3.0% by weight, a Mn content to 0.5 to 3.0% by weight, and a Si+Mn content to more than 1.5 to 6.0% by weight, and make a V.sub.F /d.sub.F ratio not less than 20, in case of 0.05 to less than 0.15% by weight of C, and to control a Si content to 0.5 to 3.0% by weight, a Mn content to 0.5 to 3.0% by weight and a Si+Mn content to more than 1.5 to 6.0% by weight and make a V.sub.F /d.sub.F not less than 7, in case of 0.15 to less than 0.30% by weight of C. In order to make the retained austenite grain size not more than 2 .mu.m, it is necessary to make a finish-rolling ultimate pass strain speed not less than 30/second, as shown in FIG. 3.
Thirdly, in order to obtain a best spot weldability (inside-nugget breakage=0), it is necessary that a C content is less than 0.15% by weight, a Si+Mn content is not more than 6% by weight, a Si content and a Mn content are each not more than 3.0% by weight and a P content is not more than 0.02% by weight, as shown in FIG. 4.
Fourthly, in the case that a very stringent surface property is required, it is effective to control the heating temperature to not more than 1,170.degree. C. and a Si content to 1.0 to 2.0% by weight.
Fifthly, in order to obtain an excellent enlargeability (d/d.sub.o .gtoreq.1.4), it is necessary to make a C content less than 0.15% by weight and a S content not more than 0.01% by weight, and it is also effective to add Ca or REM thereto, as shown in FIG. 5. In order to obtain a particularly excellent enlargeability (d/d.sub.o =1.5), it is further necessary to make a C content less than 0.10% by weight.
That is, various combined characteristics required for a hot rolled high strength steel sheet can be satisfied only by strict component control and strict structure control according to the present invention.
The present inventors have made further studies of hot rolling conditions for obtaining the above-mentioned micorstructure and have found a process for producing a hot rolled high strength steel sheet.
At first, component control values and the reasons for the control will be explained below.
Not less than 0.05% by weight of C must be added to assure the retained austenite (which will be hereinafter referred to as "retained .gamma."). In order to prevent embrittlement at the welded parts, thereby obtaining the best spot weldability, and to obtain an excellent enlargeability (d/d.sub.o) of not less than 1.4, the upper limit of C content must be less than 0.15% by weight. When the best enlargeability, d/d.sub.o .gtoreq.1.5 is needed, the upper limit must be less than 0.10% by weight. C is also a reinforcing element, and the tensile strength will be increased with increasing C content, but d/d.sub.o will be lowered at the same time, rendering the spot weldability inevitably disadvantageous.
Si and Mn are reinforcing elements. Si also promotes formation of ferrite (which will be hereinafter referred to as ".alpha."), thereby suppressing formation of carbides. Thus, it has an action to assure the retained .gamma.. Mn has an action to stabilize .gamma. to assure the retained .gamma.. In order to fully perform the functions of Si and Mn, it is necessary to control the individual lower limits of Si and Mn and also the lower limits of Si+Mn at the same time. That is, it is necessary to control the individual lower limits of Si and Mn to not less than 0.5% by weight and the lower limit of Si+Mn to more than 1.5% by weight. Even excessive addition of Si and Mn saturates the above-mentioned effects, resulting in deterioration of weldability and slab cracking to the contrary, and thus it is necessary that the individual upper limits of Si and Mn are not more than 3.0% by weight and the upper limit of Si+Mn is not more than 6.0% by weight. When a particularly excellent surface state is required, it is desirable that a Si content is 1.0 to 2.0% by weight.
P is effective for assuring the retained .gamma., and in the present invention, the upper limit thereof is set to 0.02% by weight to keep the best secondary workability, toughness and weldability. When the requirements for these characteristics are not so strict, up to 0.2% by weight of P can be added to increase the retained .gamma..
Upper limit of S is set to 0.01% by weight to prevent deterioration of enlargeability due to the sulfide-based materials.
Not less than 0.005% by weight of Al is added for deoxidization and to increase the .alpha. volume fraction by making .gamma. grains finer by AIN, make .alpha. grans finer, and increase the retained .gamma. and make the retained .gamma. grains finer, and the upper limit is set to 0.10% by weight because of saturation of the effects. Up to 3% by weight of Al may be added to promote an increase in the retained .gamma..
Not less than 0.0005% by weight of Ca is added to control the shape of sulfide-based materials (spheroidization), and its upper limit is set to 0.01% by weight because of saturation of the effects and adverse effect due to an increase in the sulfide-based materials (deterioration of enlargeability). For the same reason, an REM content is set to a range of 0.005 to 0.05% by weight.
The foregoing are reasons for addition of the main components. At least one of Nb, Ti, Cr, Cu, Ni, V, B, and Mo may be added in such a range as to assure the strength and make the grains finer, but not as to deteriorate the characteristics.
From the viewpoint of how to obtain the above-mentioned microstructure, values for heating control, rolling control, cooling control, coiling control, etc. and reasons for the control will be explained below.
In order to prevent deterioration of workability due to the appearance of working structure (working .alpha.), particularly the deterioration of strength-ductility balance (deterioration of elongation), the lower limit of finish-rolling end temperature is set to Ar.sub.3 -50.degree. C. In case of one-stage cooling (FIG. 6). the upper limit of finish-rolling end temperature is set to Ar.sub.3 +50.degree. C. to assure the effect on an increase in the .alpha. volume fraction, the effect on making the .alpha. grains finer, and the effect on an increase in the retained .gamma. finer grains in the rolling step. In case of 2-stage cooling and 3-stage cooling (FIG. 6), as will be explained later, the effect on an increase in the .alpha. volume fraction, the effect on making the .alpha. grains finer and the effect on an increase in the retained .gamma. finer grains can be expected in the cooling step, and thus it is not necessary to set the upper limit of finish-rolling end temperature, but the upper limit is preferably set to Ar.sub.3 +50.degree. C. to further improve the above-mentioned effects.
The entire draft of finish-rolling must be not less than 80% to assure the effect on an increase in the .alpha. volume fraction, the effect on making the .alpha. grains finer and the effect on an increase in the retained .gamma. finer grains, and preferably the individual draft of 4 passes on the preceding stage must be not less than 40%.
The ultimate pass strain speed of finish-rolling must be not less than 30/second to assure the effect on making the .alpha. grains finer and the effect on an increase in the retained .gamma. finer grains.
The lower limit of cooling rate of the one-stage cooling shown in FIG. 6 must be 30.degree. C./second to prevent formation of pearlite.
In the two-stage cooling shown in FIG. 6, the first stage cooling must be carried out down to not more than Ar.sub.3 at a cooling rate of less than 30.degree. C./second to obtain the effect on an increase in the .alpha. volume fraction and the effect on an increase in the retained .gamma. finer grains. The second stage cooling must be started from a temperature of more than Ar.sub.1 at a cooling rate of not less than 30.degree. C./second to prevent formation of pearlite. It is not objectionable to keep the temperature constant in a temperature range of not more than Ar.sub.3 to more than Ar.sub.1. In order to maintain a TRIP phenomenon in a wide range of the strain region and obtain excellent characteristics, it is desirable to set the first stage cooling rate to 5.degree.-20.degree. C./second.
In the three-stage cooling shown in FIG. 6, the first stage cooling must be carried out to not more than Ar.sub.3 at a cooling rate of not less than 30.degree. C./second to make the .alpha. grains finer. The second stage cooling is carried out at a cooling rate of less than 30.degree. C./second to obtain the effect on an increase in the .alpha. volume fraction and the effect on an increase in the retained .gamma. finer grains, and the third stage cooling must be started from more than Ar.sub.1 at a cooling rate of not less than 30.degree. C./second to prevent formation of pearlite. It is not objectionable to keep the temperature constant in a range of not more than Ar.sub.3 to more than Ar.sub.1. In order to maintain a TRIP phenomenon in a wide range of strain region and obtain excellent characteristics, it is desirable to set the second stage cooling rate to 5.degree.-20.degree. C./second.
In any of the one-stage cooling, two-stage cooling and three-stage cooling, quenching may be carried out just after the rolling to obtain the effect on an increase in the .alpha. volume fraction, the effect on making .alpha. grains finer and the effect on an increase in the retained .gamma. finer grains or further to reduce the length of the cooling table.
Lower limit of coiling temperature must be more than 350.degree. C. to prevent formation of martensite and assure the retained .gamma.. Its upper limit must be less than 500.degree. C. to prevent formation of pearlite, suppress excessive bainite transformation and assure the retained .gamma..
The foregoing are reasons for control in the present process. In order to improve the effect on an increase in the .alpha. volume fraction, the effect on making the .alpha. grains finer and the effect on an increase in the retained .gamma. finer grains, means such as 1 to set the upper limit of the heating temperature to 1,170.degree. C., 2 to set the finish-rolling initiation temperature to not more than "rolling end temperature +100.degree. C.", etc. may be carried out alone or in combination. The upper limit of the heating temperature may be set at 1,170.degree. C. to assure the best surface property.
Furthermore, cooling after the coiling may be spontaneous cooling or forced cooling. In order to suppress excessive bainite transformation and improve the effect on assuring the retained .gamma. grains, cooling may be carried out down to less than 200.degree. C. at a cooling rate of not less than 30.degree. C./hour. Cooling may be carried out in combination with the above-mentioned heating temperature control and finish-rolling initiation temperature control.
Slabs for use in the rolling may be any of the so called reheated cold slabs, HCR and HDR, or may be slabs prepared by so called continuous steel casting.
Hot rolled steel sheets obtained according to the present invention may be used as plates for plating.

BRIEF DESCRIPTION OF DRAWINGS
FIG. 1 is a diagram showing conditions for making retained .gamma. not less than 5%.
FIG. 2 is a diagram showing conditions for making retained .gamma. not less than 5%.
FIG. 3 is a diagram showing conditions for making retained .gamma. grains having grain sizes of not more than 2 .mu.m, not less than 5%.
FIG. 4 is a diagram showing conditions for improving the spot weldability.
FIG. 5 is a diagram showing conditions for improving an enlargement ratio.
FIG. 6 is a diagram showing cooling steps at a cooling table.

BEST MODES FOR CARRYING OUT THE INVENTION
Examples are shown below.
Chemical components other than Fe of steel test pieces are shown in Table 2.
Hot rolled steel sheets according to Examples of the present invention and Comparative Examples are shown in Tables 3 and 4.
TABLE 2__________________________________________________________________________ OtherSteel additivespecies C Si Mn P S Al Ca REM element Si + Mn__________________________________________________________________________A 0.05 1.3 1.5 0.020 0.0002 0.021 -- -- -- 2.8B 0.09 0.9 1.9 0.015 0.0003 0.014 -- -- -- 2.8C 0.09 1.6 1.7 0.018 0.0004 0.025 0.0030 -- -- 3.3D 0.05 2.1 1.5 0.015 0.0001 0.028 -- -- -- 3.5E 0.09 2.0 1.1 0.010 0.0002 0.030 -- -- -- 3.1F 0.09 0.9 2.1 0.008 0.0003 0.015 -- 0.010 -- 3.0G 0.08 1.5 1.5 0.015 0.0002 0.012 -- -- Nb = 0.025 3.0H 0.07 1.6 1.6 0.016 0.0002 0.024 -- -- Cr = 0.2 3.2I 0.06 1.7 1.5 0.020 0.0003 0.015 -- -- Ti = 0.02 3.2J 0.07 1.5 1.5 0.010 0.0002 0.018 -- -- B = 0.0005 3.0K 0.05 1.4 1.6 0.020 0.0002 0.014 -- -- V = 0.03 3.0L 0.08 1.8 1.4 0.015 0.0002 0.013 -- -- Mo = 0.2 3.2M 0.10 1.5 1.5 0.018 0.0002 0.020 -- -- -- 3.0N 0.14 1.0 1.3 0.015 0.0002 0.015 -- -- -- 2.3O 0.10 2.0 1.1 0.001 0.001 0.011 -- -- -- 3.1P 0.14 1.3 1.3 0.009 0.003 0.024 -- -- -- 2.6Q 0.13 1.0 2.0 0.015 0.004 0.020 -- 0.013 -- 3.0R 0.10 1.5 1.5 0.012 0.002 0.018 -- -- V = 0.02 3.0S 0.11 1.6 1.4 0.018 0.002 0.017 -- -- B = 0.0004 3.0T 0.10 2.0 1.1 0.019 0.001 0.020 -- -- Ti = 0.01 3.1U 0.11 1.8 1.2 0.017 0.002 0.015 -- -- Cr = 0.1 3.0V 0.10 1.5 1.5 0.015 0.002 0.015 -- -- Nb = 0.015 3.0W 0.10 1.5 1.5 0.017 0.0004 0.020 0.0040 -- -- 3.0X 0.11 1.7 1.4 0.014 0.002 0.011 -- -- Mo = 0.1 3.1Y 0.05 1.3 1.5 0.018 0.0001 0.014 0.0035 -- -- 2.8Z 0.14 1.0 1.3 0.018 0.0003 0.017 0.0030 -- -- 2.3AA 0.07 2.0 2.0 0.020 0.002 0.016 0.0025 -- -- 4.0AB 0.20 1.5 1.5 0.018 0.002 0.015 0.0030 -- -- 3.0AC 0.13 0.3 1.2 0.017 0.0002 0.018 -- -- -- 1.5AA1 0.07 3.0 3.0 0.020 0.0002 0.015 0.0030 -- -- 6.0AA2 0.28 2.8 2.8 0.010 0.0001 0.030 -- -- -- 5.6AA3 0.32 2.8 2.8 0.009 0.0001 0.010 -- -- -- 5.6__________________________________________________________________________
TABLE 3__________________________________________________________________________ Microstructure Steel V.sub.F d.sub.F V.sub.F .gamma..sub.R V.sub.B V.sub.P V.sub.M Grain sizeDistinction No. species (%) (.mu.m) d.sub.F (%) (%) (%) (%) of .gamma..sub.R__________________________________________________________________________The invention 1 A 88 4.00 22.0 5 7 0 0 .ltoreq.2 .mu.mThe invention 2 B 70 3.24 21.6 5 25 0 0 .ltoreq.2 .mu.mThe invention 3 C 84 3.59 23.4 10 6 0 0 .ltoreq.2 .mu.mThe invention 4 D 84 3.49 24.1 9 7 0 0 .ltoreq.2 .mu.mThe invention 5 E 84 3.59 23.4 10 6 0 0 .ltoreq.2 .mu.mThe invention 6 F 73 3.33 21.9 6 21 0 0 .ltoreq.2 .mu.mThe invention 7 M 69 3.25 21.2 5 26 0 0 .ltoreq.2 .mu.mThe invention 8 N 60 2.99 20.1 5 35 0 0 .ltoreq.2 .mu.mThe invention 9 O 78 3.45 22.6 9 13 0 0 .ltoreq.2 .mu. mThe invention 10 P 74 3.43 21.6 10 16 0 0 .ltoreq.2 .mu.mThe invention 11 Q 78 3.45 22.6 12 10 0 0 .ltoreq.2 .mu.mThe invention 12 W 78 3.45 22.6 9 13 0 0 .ltoreq.2 .mu.mThe invention 13 Y 80 3.42 23.4 7 13 0 0 .ltoreq.2 .mu.mThe invention 14 Z 63 3.09 20.4 6 31 0 0 .ltoreq.2 .mu.mThe invention 15 AA 78 3.38 23.1 8 14 0 0 .ltoreq.2 .mu.mThe invention 16 AB 56.6 2.83 20.0 5 44 0 0 .ltoreq.2 .mu.mThe invention 17 AA1 75 3.00 25.0 10 15 0 0 .ltoreq.2 .mu.mThe invention 18 AA2 40 3.00 13.0 13 43 0 0 .ltoreq.2 .mu.mComp. Ex. 19 AC 61 2.90 21.0 0 39 0 0 --Comp. Ex. 20 Z 80 3.76 21.3 2 11 7 0 .ltoreq.2 .mu.mComp. Ex. 21 B 79 3.46 22.8 1 12 0 8 .ltoreq.2 .mu.mComp. Ex. 22 Z 80 3.75 21.3 5 15 0 0 >2 .mu.mComp. Ex. 23 AA3 24 3.00 8.0 13 61 0 0 .ltoreq.2 .mu.m__________________________________________________________________________
TABLE 4__________________________________________________________________________ Characteristics of steel sheet Steel TS/YP YR T.El/U.El Spot Secondary Tough- Surface Bend-Distinction No. species (kgf/mm.sup.2) (%) (%) TS .times. T.El d/d.sub.o weldability workability ness state ability__________________________________________________________________________The invention 1 A 52/41 78.8 42.5/27.7 2210 1.71 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 2 B 60/46 76.7 37.2/24.2 2230 1.55 .largecircle. .largecircle. .largecircle. .largecircle. .largecircle.The invention 3 C 67.5/57 84.4 38.8/25.9 2620 1.58 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 4 D 62.5/54 86.4 40.5/25.8 2530 1.68 .largecircle. .largecircle. .largecircle. .largecircle. .largecircle.The invention 5 E 64.5/54 83.7 40.2/27.3 2590 1.55 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 6 F 63/49 77.8 36.2/23.6 2280 1.58 .largecircle. .largecircle. .largecircle. .largecircle. .largecircle.The invention 7 M 65/49 75.4 33.8/20.8 2200 1.50 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle. 3The invention 8 N 83.5/59 70.7 26.2/15.4 2190 1.45 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 9 O 66.5/54 81.2 37.9/25.0 2520 1.50 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 10 P 67/52 77.6 38.8/27.7 2600 1.46 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 11 Q 71/58 81.7 38.9/27.8 2760 1.48 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 12 W 65/53 81.5 38.6/25.9 2510 1.53 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 13 Y 52/44 84.6 45.4/30.2 2360 1.73 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 14 Z 67/48 71.6 34.2/23.3 2290 1.46 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 15 AA 74/61 82.4 32.8/18.9 2430 1.62 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 16 AB 85/68 80.0 28.0/18.0 2380 1.34 .DELTA. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 17 AA1 85/60 70.5 26.0/15.0 2210 1.42 .largecircle. .largecircle. .largecircle. .largecircle. .largecircle.The invention 18 AA2 110/90 81.8 22.0/12.0 2420 1.2 .DELTA. .largecircle. .largecircle. .largecircle. .largecircle.Comp. Ex. 19 AC 60/41 74.5 28.3/14.1 1700 1.48 .largecircle. .largecircle. .largecircle. .largecircle. .largecircle.Comp. Ex. 20 Z 67/50 74.6 25.4/13.5 1700 1.38 .largecircle. x x .circleincircle. xComp. Ex. 21 B 80/44 55 23.8/14.9 1900 1.22 .largecircle. x x .circleincircle. xComp. Ex. 22 Z 66/49 74.2 26.5/14.5 1749 1.29 .largecircle. x x .circleincircle. xComp. Ex. 23 AA3 123/100 81.3 20.5/12.0 2251 1.05 x .largecircle. .largecircle. .largecircle. .largecircle.__________________________________________________________________________
Nos. 1 to 18 relate to examples of the present invention, where high yield ratio-type, hot rolled high strength steel sheets excellent in both formability and spot weldability could be obtained. However, No. 16 and No. 18 had a somewhat lower spot weldability due to a higher C content, but had a good workability.
Good surface property was obtained. Particularly good surface property was obtained in Nos. 1, 3, 5, and 7 to 16, because the Si content was in a range of 1.0 to 2.0% by weight.
Nos. 19 to 23 relate to Comparative Examples, where No. 19 had lower Si content and Si+Mn content than the lower limit, and no retained .gamma. was obtained and both strength-ductility balance and uniform elongation were deteriorated; No. 20 contained pearlite and lower retained .gamma. content than 5%, and thus the strength-ductility balance, uniform elongation, enlargeability, bendability, secondary workability and toughness were deteriorated; No. 21 contained martensite and had lower retained .gamma. content than 5%, and the strength-ductility balance, uniform elongation, enlargeability, bendability, secondary workability and toughness were deteriorated, and the yield ratio was lower than 60%; No. 22 maintained 5% of retained .gamma. content, but its grain size was more than 2 .mu.m, and thus the strength-ductility balance, uniform elongation, enlargeability, bendability, secondary workability and toughness were deteriorated; and No. 23 had a higher C content than the upper limit and thus the spot weldability and enlargeability were deteriorated.
Even in the steel species G-L, R-V and X of Table 2, high yield ratio, hot rolled high strength steel sheets excellent in both of formability and spot weldability could be obtained, and their surface states were also better.
Processes for producing hot rolled steel sheets according to examples of the present invention and comparative examples are shown in Table 5 to 10.
TABLE 5__________________________________________________________________________Examples of one-stage cooling Production conditions Finish- Finish- Finish- rolling rolling Finish- rolling ultimate Heating initiation rolling entire pass strain Cooling Coiling Cooling Steel temp. temp. end temp. draft speed/ rate temp. afterDistinction No. species .degree.C. .degree.C. .degree.C. % second .degree.C./sec .degree.C. coiling__________________________________________________________________________The invention 24 C 1170 905 800 93 200 40 360 SpontaneousThe invention 25 C 1100 895 790 88 180 35 375 SpontaneousThe invention 26 C 1200 860 800 89 40 45 390 SpontaneousThe invention 27 C 1050 920 850 92 100 50 380 SpontaneousThe invention 28 C 1150 900 810 96* 300 50 450 SpontaneousThe invention 29 C 1180 910 800 94 190 75** 420 40.degree. C./hrThe invention 30 AA1 1190 920 810 92 70 50 400 SpontaneousComp. Ex. 31 C 1180 850 740 95 100 45 505 SpontaneousComp. Ex. 32 C 1170 900 820 93 20 20 380 SpontaneousComp. Ex. 33 C 1160 905 810 91 150 50 550 SpontaneousComp. Ex. 34 C 1200 910 800 89 120 45 300 SpontaneousComp. Ex. 35 C 1170 920 860 93 20 60 395 Spontaneous__________________________________________________________________________ *At least 40% for receding four passes **Quenching right after finishrolling
TABLE 6__________________________________________________________________________Examples of one-stage cooling__________________________________________________________________________ Microstructure .gamma..sub.R (grain V.sub.F / size: Steel sheet characterisitcs Steel d.sub.F .ltoreq.2 .mu.m) TS/YP YR T.El/U.ElDistinction No. species .gtoreq. 20 .gtoreq. 5% P M kgf/mm.sup.2 % %__________________________________________________________________________The invention 24 C .largecircle. .largecircle. none none 68/57 83.8 38.6/25.0The invention 25 C .largecircle. .largecircle. none none 67.5/56.5 83.7 39.0/26.0The invention 26 C .largecircle. .largecircle. none none 67/56 83.6 39.2/26.2The invention 27 C .largecircle. .largecircle. none none 69/56 81.2 37/24The invention 28 C .largecircle. .largecircle. none none 67.3/57 84.7 37.5/26.3The invention 29 C .largecircle. .largecircle. none none 66.5/56.5 85.0 39.6/26.7The invention 30 AA1 .largecircle. .largecircle. none none 80.2/59.5 74.2 32.4/20.5Comp. Ex. 31 C x* x yes none 65.0/58.0 89.2 26.1/14.8Comp. Ex. 32 C .largecircle. x yes none 65/54 83.1 27.0/14Comp. Ex. 33 C .largecircle. x yes none 63/52 82.5 27.2/14Comp. Ex. 34 C .largecircle. x none yes 80/43 51.2 24.9/14.9Comp. Ex. 35 C x x none none 69.5/48.7 70.0 26.5/14.5__________________________________________________________________________ Steel sheet characteristics Spot Sec. Steel weld- work- Tough- Surface Bend-Distinction No. species TS .times. T.El d/d.sub.o ability ability ness state ability__________________________________________________________________________The invention 24 C 2625 1.57 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 25 C 2633 1.58 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 26 C 2626 1.58 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 27 C 2553 1.56 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 28 C 2658 1.58 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 29 C 2633 1.57 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 30 AA1 2598 1.48 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.Comp. Ex. 31 C 1697 1.39 .largecircle. x x .circleincircle. xComp. Ex. 32 C 1755 1.39 .largecircle. x x .circleincircle. xComp. Ex. 33 C 1714 1.39 .largecircle. x x .circleincircle. xComp. Ex. 34 C 1992 1.23 .largecircle. x x .circleincircle. xComp. Ex. 35 C 1842 1.50 .largecircle. x x .circleincircle. .largecircle.__________________________________________________________________________ *Working structure (working .alpha.) formed
TABLE 7__________________________________________________________________________Examples of two-stage cooling Production conditions Finish- Finish- Finish- rolling Cooling rolling Finish- rolling ultimate Cooling rate rate Heating initiation rolling entire pass strain CR.sub.1 CR.sub.2 shift Coiling Cooling Steel temp. temp. end temp. draft speed/ .degree.C./ .degree.C./ temp. T.sub.1 temp. afterDistinction No. species .degree.C. .degree.C. .degree.C. % sec sec sec .degree.C. .degree.C. coiling__________________________________________________________________________The invention 36 B 1160 915 810 93 150 15 105 760 400 SpontaneousThe invention 37 B 1175 900 820 92 190 5 60 780 385 SpontaneousThe invention 38 B 1150 960 830 94* 100 9 50 770 415 SpontaneousThe invention 39 B 1180 940 820 89 180 10 80 760 400 SpontaneousThe invention 40 B 1200 950 830 91 190 12 60 770 380 35.degree. C./hrThe invention 41 AA1 1190 945 830 91 210 12 60 770 390 SpontaneousComp. Ex. 42 B 1100 800 720 92 150 13 75 680 510 SpontaneousComp. Ex. 43 B 1190 930 840 77 100 25 80 750 450 SpontaneousComp. Ex. 44 B 1180 990 870 91 190 40 85 650 440 SpontaneousComp. Ex. 45 B 1170 950 840 90 120 25 20 700 500 SpontaneousComp. Ex. 46 B 1160 945 830 93 20 19 90 590 480 SpontaneousComp. Ex. 47 B 1200 970 860 89 50 10 45 820 400 Spontaneous__________________________________________________________________________ *At least 40% for preceding four passes
TABLE 8__________________________________________________________________________Examples of two-stage cooling__________________________________________________________________________ Microstructure .gamma..sub.R (grain V.sub.F / size: Steel sheet characterisitcs Steel d.sub.F .ltoreq.2 .mu.m) TS/YP YR T.El/U.ElDistinction No. species .gtoreq. 20 .gtoreq. 5% P M kgf/mm.sup.2 % %__________________________________________________________________________The invention 36 B .largecircle. .largecircle. none none 60/47 78.3 37.1/24.2The invention 37 B .largecircle. .largecircle. none none 59/47 79.7 38.0/25.0The invention 38 B .largecircle. .largecircle. none none 60/46 76.7 38.5/26The invention 39 B .largecircle. .largecircle. none none 60.5/47 77.7 37.0/24.1The invention 40 B .largecircle. .largecircle. none none 60.5/47 77.7 38.2/25.8The invention 41 AA1 .largecircle. .largecircle. none none 81.3/58.2 71.6 28.4/18.5Comp. Ex. 42 B x* x yes none 57/48 84.2 27.5/14.8Comp. Ex. 43 B x x none none 62/43.4 70.0 28/14Comp. Ex. 44 B x x none none 65/56.6 70.0 27/13Comp. Ex. 45 B .largecircle. x yes none 55/45 81.8 28/14.7Comp. Ex. 46 B .largecircle. x yes none 56/45 80.4 27/14Comp. Ex. 47 B x x none none 66/46.2 70.0 26/13__________________________________________________________________________ Steel sheet characteristics Spot Sec. Steel weld- work- Tough- Surface Bend-Distinction No. species TS .times. T.El d/d.sub.o ability ability ness state ability__________________________________________________________________________The invention 36 B 2226 1.55 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 37 B 2242 1.56 .largecircle. .largecircle. .largecircle. .largecircle. .largecircle.The invention 38 B 2310 1.56 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 39 B 2239 1.55 .largecircle. .largecircle. .largecircle. .largecircle. .largecircle.The invention 40 B 2311 1.55 .largecircle. .largecircle. .largecircle. .largecircle. .largecircle.The invention 41 AA1 2310 1.43 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.Comp. Ex. 42 B 1568 1.39 .largecircle. x x .circleincircle. xComp. Ex. 43 B 1736 1.50 .largecircle. x x .largecircle. .largecircle.Comp. Ex. 44 B 1755 1.51 .largecircle. x x .largecircle. .largecircle.Comp. Ex. 45 B 1540 1.38 .largecircle. x x .circleincircle. xComp. Ex. 46 B 1512 1.39 .largecircle. x x .circleincircle. xComp. Ex. 47 B 1716 1.52 .largecircle. x x .largecircle. .largecircle.__________________________________________________________________________ *Working structure (working .alpha.) formed
TABLE 9__________________________________________________________________________Examples of three-stage cooling Production conditions Finish- Finish- Finish- Finish- rolling Cooling Heat- rolling rolling rolling ultimate Cooling rate rate ing initiation end entire pass strain CR.sub.1 CR.sub.2 CR.sub.3 shift temp Coiling Cooling Steel temp. temp. temp. draft speed/ .degree.C./ .degree.C./ .degree.C./ T.sub.1 T.sub.2 temp. afterDistinction No. species .degree.C. .degree.C. .degree.C. % sec sec sec sec .degree.C. .degree.C. .degree.C. coiling__________________________________________________________________________The invention 48 AA 1170 900 800 94* 100 50 5 50 750 725 380 40.degree. C./hrThe invention 49 AA 1190 970 850 93 50 90 15 90 700 600 410 SpontaneousThe invention 50 C 1200 930 820 92 80 40 7 40 700 680 405 SpontaneousThe invention 51 C 1180 960 870 91 190 85 18 85 710 610 390 SpontaneousThe invention 52 C 1190 970 860 92 210 95 8 100 650 600 390 SpontaneousThe invention 53 AA1 1185 960 840 93 150 90 15 90 700 600 410 SpontaneousComp. Ex. 54 C 1200 980 865 94 200 60 35 60 670 600 440 SpontaneousComp. Ex. 55 C 1160 980 870 93 170 80 9 20 660 600 480 SpontaneousComp. Ex. 56 C 1200 990 880 92 180 40 7 60 840 805 430 SpontaneousComp. Ex. 57 C 1180 970 870 82 25 25 15 85 710 620 400 Spontaneous__________________________________________________________________________ *At least 40% for preceding four passes
TABLE 10__________________________________________________________________________Examples of three-stage cooling__________________________________________________________________________ Microstructure .gamma..sub.R (grain V.sub.F / size: Steel sheet characterisitcs Steel d.sub.F .ltoreq.2 .mu.m) TS/YP YR T.El/U.ElDistinction No. species .gtoreq. 20 .gtoreq. 5% P M kgf/mm.sup.2 % %__________________________________________________________________________The invention 48 AA .largecircle. .largecircle. none none 74.2/61 82.2 34.8/21.8The invention 49 AA .largecircle. .largecircle. none none 73/60.5 82.9 34.5/24.5The invention 50 C .largecircle. .largecircle. none none 67/57 85.1 39/26The invention 51 C .largecircle. .largecircle. none none 68/58 85.3 37/24The invention 52 C .largecircle. .largecircle. none none 67/56 83.6 38/25The invention 53 AA1 .largecircle. .largecircle. none none 85/61 71.8 26.2/15.1Comp. Ex. 54 C x x none none 71/49.7 70.0 25/12Comp. Ex. 55 C .largecircle. x yes none 64/53 82.8 27/14Comp. Ex. 56 C x x none none 70/49 70.0 26/13Comp. Ex. 57 C x x none none 66/55 83.3 27/13__________________________________________________________________________ Steel sheet characteristics Spot Sec. Steel weld- work- Tough- Surface Bend-Distinction No. species TS .times. T.El d/d.sub.o ability ability ness state ability__________________________________________________________________________The invention 48 AA 2582 1.63 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 49 AA 2519 1.64 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 50 C 2613 1.58 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 51 C 2516 1.59 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 52 C 2546 1.59 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.The invention 53 AA1 2227 1.43 .largecircle. .largecircle. .largecircle. .circleincircle. .largecircle.Comp. Ex. 54 C 1775 1.58 .largecircle. x x .circleincircle. .largecircle.Comp. Ex. 55 C 1728 1.39 .largecircle. x x .circleincircle. xComp. Ex. 56 C 1820 1.59 .largecircle. x x .circleincircle. .largecircle.Comp. Ex. 57 C 1792 1.50 .largecircle. x x .circleincircle. .largecircle.__________________________________________________________________________
Tables 5 and 6 show processes for producing a hot rolled steel sheet in case of one-stage cooling at the cooling table according to the present examples and comparative examples, shown in FIG. 6.
Nos. 24 to 30 relate to examples of the present invention, where high yield ratio-type, hot rolled high strength steel sheets excellent in both formarbility and spot weldability could be obtained and their surface states were found to be better.
Nos. 31 to 35 relate to comparative examples, where No. 31 had a lower rolling end temperature than the lower limit and a higher coiling temperature than the upper limit, and thus a working structure (working .alpha.) and pearlite were formed, and not less than 5% by weight of retained .gamma. having grain sizes of not more than 2 .mu.m could not be obtained, and, as a result, the strength-ductility balance, uniform elongation, enlargeability, bendability, secondary workability and toughness were deteriorated; No. 32 had a lower finish-rolling ultimate pass strain speed than the lower limit and a lower cooling rate than the lower limit, resulting in formation of pearlite, and not less than 5% of retained .gamma. having grain sizes of not more than 2 .mu.m could not be obtained, and, as a result, the strength-ductility balance, uniform elongation, enlargeability, bendability, secondary workability and toughness were deteriorated; No. 33 had a higher coiling temperature than the upper limit, resulting in formation of pearlite, and not less than 5% of retained .gamma. having grain sizes of not more than 2 .mu.m could not be obtained, and, as a result, the strength-ductility balance, uniform elongation, enlargeability, bendability, secondary workability and toughness were deteriorated; No. 34 had a lower coiling temperature than the lower limit, resulting in formation of martensite, and not less than 5% of retained .gamma. having grain sizes of not more than 2 .mu.m could not be obtained, and, as a result, the strength-ductility balance, uniform elongation, enlargeability, bendability, secondary workability and toughness were deteriorated, and the yield ratio was lower than 60%; and No. 35 had a higher finish-rolling end temperature than the upper limit and a lower finish-rolling ultimate pass strain speed than the lower limit, resulting in failure to attain such a relationship as V.sub.F /d.sub.F .gtoreq.20, and not less than 5% of retained .gamma. having grain sizes of not more than 2 .mu.m could not be obtained, and, as a result, the strength-ductility balance, uniform elongation, secondary workability and toughness were deteriorated.
Tables 7 and 8 show processes for producing hot rolled steel sheets in case of two-stage cooling at the cooling table according to the present examples and comparative examples, as shown in FIG. 6.
Nos. 36 to 41 relate to examples of the present invention, where high yield ratio-type, hot rolled high strength steel sheets excellent in both formability and spot weldability could be obtained and their surface states were found to be better.
Nos. 42 to 47 relate to comparative examples, where No. 42 had a lower finish-rolling end temperature than the lower limit and a higher coiling temperature than the upper limit, resulting in formation of working structure (working .alpha.) and pearlite, and not less than 5% of retained .gamma. having grain sizes of not more than 2 .mu.m could not be obtained, and, as a result, the strength-ductility balance, uniform elongation, enlargeability, bendability, secondary workability and toughness were deteriorated; No. 43 had a lower entire draft of finish-rolling than the lower limit, resulting in failure to attain such a relation as V.sub.F /d.sub.F >20, and not more than 5% of retained .gamma. having grain sizes of not less than 2 .mu.m could not be obtained, and, as a result, the strength-ductility balance, uniform elongation, secondary workability and toughness were deteriorated; No. 44 had a higher cooling rate at the first stage than the upper limit, resulting in failure to attain such a relation as V.sub.F /d.sub.F .gtoreq.20, and not less than 5% of retained .gamma. having grain sizes of not more than 2 .mu.m could not be obtained, and, as a result, the strength-ductility balance, uniform elongation, secondary workability and toughness were deteriorated; No. 45 had a lower cooling rate at the second stage than the lower limit, resulting in formation of pearlite, and not more than 5% of retained .gamma. having grain sizes of not more than 2 .mu.m could not be obtained, and, as a result, the strength-ductility balance, uniform elongation, enlargeability, bendability, secondary workability and toughness were deteriorated; No. 46 had a lower finish-rolling ultimate pass strain speed than the lower limit and a higher coiling temperature than the upper limit, resulting in formation of pearlite, and not less than 5% of retained .gamma. having grain sizes of not more than 2 .mu.m could not be obtained, and, as a result, the strength-ductility balance, uniform elongation, enlargeability, bendability, secondary workability and toughness were deteriorated; and No. 47 had a higher cooling end temperature (cooling rate shift temperature T.sub.1) at the first stage than the upper limit, resulting in failure to attain such a relation as V.sub.F /d.sub.F >20 and not less than 5% of retained .gamma. having grain size of not more than 2 .mu.m could not be obtained, and, as a result, the strength-ductility balance, uniform elongation, secondary workability and toughness were deteriorated.
Tables 9 and 10 show processes for producing hot rolled steel sheets in case of three-stage cooling at the cooling table according to the present examples and comparative examples, shown in FIG. 6.
Nos. 48 to 53 relate to examples of the present invention, where high yield ratio-type, hot rolled high strength steel sheets excellent in both formability and spot weldability could be obtained and their surface states were found to be better.
Nos. 54 to 56 relate to comparative examples, where No. 54 had a higher cooling rate at the second stage than the upper limit, resulting in failure to attain such a relation as V.sub.F /d.sub.F .gtoreq.20 and not less than 5% of retained .gamma. having grain sizes of not more than 2 .mu.m could not be obtained, and, as a result, the strength-ductility balance, uniform elongation, secondary workability and toughness were deteriorated; No. 55 had a lower cooling rate at the third stage than the lower limit, resulting in the formation of pearlite, and not less than 5% of retained .gamma. having grain sizes of not more than 2 .mu.m could not be obtained, and, as a result, the strength-ductility balance, uniform elongation, enlargeability, bendability, secondary workability and toughness were deteriorated; No. 56 had higher cooling end temperatures (cooling rate shift temperatures T.sub.1 and T.sub.2) at the first and second stages, respectively, than the upper limits, resulting in failure to attain such a relationship as V.sub.F /d.sub.F .gtoreq.20, and not less than 5% of retained .gamma. having grain sizes of not more than 2 .mu.m could not be obtained, and, as a result, the strength-ductility balance, uniform elongation, secondary workability and toughness were deteriorated; No. 57 had a lower finish-rolling ultimate strain speed than the lower limit, resulting in failure to attain such a relation as V.sub.F /d.sub.F .gtoreq.20, and not more than 5% of retained .gamma. having grain sizes of not less than 2 .mu.m could not be obtained, and, as a result, the strength-ductility balance, uniform elongation, secondary workability and toughness were deteriorated.
Even in the steel species G-L, R-V and X of Table 2, high yield ratio-type, hot rolled high strength steel sheets having excellent formability and spot weldability together and a good surface state could be obtained according to the same processes of the present invention.
As is apparent from the foregoing, various practical cases and parts can be made available only according to the present invention with combined characteristics.
Evaluation of the characteristics has been made according to the following procedures:
Tensile tests were carried out according to JIS No. 5 to determine tensile strength (TS), yield strength (YP), yield ratio (YR=100.times.YP/TS), total elongation (T.E1), uniform elongation (U.E1), and strength-ductility balance (TS.times.T.E1).
Enlargeability or hole expansibility was expressed by an enlargement ratio (d/d.sub.o), determined by enlarging a punch hole, 20 mm in diameter (initial diameter:d.sub.o), with a 30.degree. cone punch from the flash-free side to measure a hole diameter (d) when a crack passed through the test piece in the thickness direction, and obtaining the ratio (d/d.sub.o).
Bendability was determined by bending a test piece, 35 mm.times.70 mm, at a 90.degree. V bending angle with 0.5 R at the tip end (bending axis being in the rolling direction), while making the flash existing side outside, and non-occurrence of cracks, 1 mm or longer, was expressed by a round mark ".circleincircle.", and the occurrence of such cracks by a crossed mark "X".
Secondary workability was determined by crushing a cup which was shaped from a punched plate (punch hole: 90 mm in diameter) at a drawing ratio of 1.8, at -50.degree. C. and non-occurrence of cracks was expressed by a round mark ".circleincircle." and the occurrence of cracks by a corssed mark "X".
Toughness was expressed by a round mark ".circleincircle." when the test piece was satisfactory at a transition temperature of -120.degree. C. or less, and by a crossed mark "X" when not.
Spot weldability was determined by dividing a spot-welding test piece into two orignial pieces by a chisel and non-occurrence of breakage inside the nugget (portion melted at the spot welding and solidified thereafter) was expressed by a round mark ".circleincircle." and the occurrence thereof by a crossed mark "X".
Surface state was visually inspected, and a very good surface state was expressed by a double round mark ".circleincircle." and a good surface state by a round mark ".circleincircle.".
Industrial Applicability
In the present invention, a hot rolled high strength steel sheet having combined characteristics not found in the prior art, that is, a hot rolled high strength steel sheet having an excellent formability, a high yield ratio and an excellent spot weldability, can be stably produced at a low cost, and applications and service conditions can be considerably expanded.

Claims

1. A process for producing a high yield ratio-type, hot rolled high strength steel sheet having both an excellent formability and spot weldability, and also having a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.4 and a uniform elongation of not less than 15%, which comprises conducting a finish-rolling of a slab prepared by casting a steel consisting essentially of 0.05 to less than 0.15% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, the balance consisting essentially of Fe, being composed of three phases of ferrite, bainite and retained austenite as microstructure, and having a ferrite grain size (d.sub.F) of not more than 5 .mu.m, a ratio (V.sub.F /d.sub.F) of ferrite volume fraction (V.sub.F) to ferrite grain size (d.sub.F) of not less than 20, and a volume fraction of retained austenite having a grain size of not more than 2 .mu.m being not less than 5%, at an end temperature range of Ar.sub.3 .+-.50.degree. C. at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
2. A process for producing a high yield ratio, hot rolled high strength steel sheet having both an excellent formability and spot weldability, and also having a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.4 and a uniform elongation of not less than 15%, which comprises conducting a finish-rolling of a slab prepared by casting a steel consisting essentially of 0.05 to less than 0.15% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, and 0.0005 to 0.01% by weight of Ca or 0.005 to 0.05% by weight of REM, the balance being Fe and inevitable elements, being composed of three phases of ferrite, bainite and retained austenite as microstructure, and having a ferrite grain size (d.sub.F) of not more than 5 .mu.m, a ratio (V.sub.F /d.sub.F) of ferrite volume fraction (V.sub.F) to ferrite grain size (d.sub.F) of not less than 20, and a volume fraction of retained austenite having a grain size of not more than 2 .mu.m being not less than 5%, at an end temperature range of Ar.sub.3 .+-.50.degree. C., at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
3. A process for producing a high yield ratio, hot rolled high strength steel sheet having both an excellent formability and spot weldability, and also having a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.4 and a uniform elongation of not less than 15%, which comprises conducting a finish-rolling of a slab prepared by casting a steel consisting essentially of 0.05 to less than 0.15% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, the balance consisting essentially of Fe, being composed of three phases of ferrite, bainite and retained austenite as microstructure, and having a ferrite grain size (d.sub.F) of not more than 5 .mu.m, a ratio (V.sub.F /d.sub.F) of ferrite volume fraction (V.sub.F) to ferrite grain size (d.sub.F) of not less than 20, and a volume fraction of retained austenite having a grain size of not more than 2 .mu.m being not less than 5%, at an end temperature of not less than Ar.sub.3 -50.degree. C., at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table down to a temperature T.sub.1 in a range of not more than Ar.sub.3 to more than Ar.sub.1 at a rate of less than 30.degree. C./second, and from T.sub.1 downwards at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
4. A process for producing a high yield ratio, hot rolled high strength steel sheet having both an excellent formability and spot weldability, and also having a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.4 and a uniform elongation of not less than 15%, which comprises conducting a finish-rolling of a slab prepared by casting a steel consisting essentially of 0.05 to less than 0.15% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, and 0.0005 to 0.01% by weight of Ca or 0.005 to 0.05% by weight of REM, the balance being Fe and inevitable elements, being composed of three phases of ferrite, bainite and retained austenite as microstructure, and having a ferrite grain size (d.sub.F) of not more than 5 .mu.m, a ratio (V.sub.F /d.sub.F) of ferrite volume fraction (V.sub.F) to ferrite grain size (d.sub.F) of not less than 20, and a volume fraction of retained austenite having a grain size of not more than 2 .mu.m being not less than 5%, at an end temperature of not less than Ar.sub.3 -50.degree. C. at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table down to a temperature T.sub.1 in a range of not more than Ar.sub.3 to more than Ar.sub.1, at a rate of less than 30.degree. C./second, and from T.sub.1 downwards at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
5. A process for producing a high yield ratio, hot rolled high strength steel sheet having both an excellent formability and spot weldability, and also having a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.4 and a uniform elongation of not less than 15%, which comprises conducting a finish-rolling of a slab prepared by casting a steel consisting essentially of 0.05 to less than 0.15% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, the balance consisting essentially of Fe, being composed of three phases of ferrite, bainite and retained austenite as microstructure, and having a ferrite grain size (d.sub.F) of not more than 5 .mu.m, a ratio (V.sub.F /d.sub.F) of ferrite volume fraction (V.sub.F) to ferrite grain size (d.sub.F) of not less than 20, and a volume fraction of retained austenite having a grain size of not more than 2 .mu.m being not less than 5%, at an end temperature of not less than Ar.sub.3 -50.degree. C., at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table down to a temperature T.sub.1 in a range of not more than Ar.sub.3 to more than Ar.sub.1 at a rate of not less than 30.degree. C./second, and from T.sub.1 downwards to a temperature T.sub.2 in a range of not more than T.sub.1 to more than Ar.sub.1 at a rate of less than 30.degree. C./second, and furthermore from T.sub.2 downwards at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
6. A process for producing a high yield ratio, hot rolled high strength steel sheet having both an excellent formability and spot weldability, and also having a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.4 and a uniform elongation of not less than 15%, which comprises conducting a finish-rolling of a slab prepared by casting a steel consisting essentially of 0.05 to less than 0.15% by weight of C, 0.5 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 1.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, and 0.0005 to 0.01% by weight of Ca or 0.005 to 0.05% by weight of REM, the balance being Fe and inevitable elements, being composed of three phases of ferrite, bainite and retained austenite as microstructure, and having a ferrite grain size (d.sub.F) of not more than 5 .mu.m, a ratio (V.sub.F /d.sub.F) of ferrite volume fraction (V.sub.F) to ferrite grain size (d.sub.F) of not less than 20, and a volume fraction of retained austenite having a grain size of not more than 2 .mu.m being not less than 5%, at an end temperature of not less than Ar.sub.3 -50.degree. C. at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table down to a temperature T.sub.1 in a range of not more than Ar.sub.3 to more than Ar.sub.1 at a rate of not less than 30.degree. C./second, and from T.sub.1 downwards to a temperature T.sub.2 in a range of not more than T.sub.1 to more than Ar.sub.1 at a rate of less than 30.degree. C./second, and furthermore from T.sub.2 downwards at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
7. A process for producing a high yield ratio, hot rolled high strength steel sheet having an excellent formability and also a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.1, and a uniform elongation of not less than 10%, which comprises conducting a finish-rolling of a slab prepared by casting a steel consisting essentially of 0.15 to less than 0.30% by weight of C, 2.0 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 2.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, the balance consisting essentially of Fe, being composed of three phases of ferrite, bainite and retained austenite as microstructure, and having a ferrite grain size (d.sub.F) of not more than 5 .mu.m, a ratio (V.sub.F /d.sub.F) of ferrite volume fraction (V.sub.F) to ferrite grain size (d.sub.F) of not less than 7, and a volume fraction of retained austenite having a grain size of not more than 2 .mu.m being not less than 5%, at an end temperature range of Ar.sub.3 .+-.50.degree. C. at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
8. A process for producing a high yield ratio, hot rolled high strength steel sheet having an excellent formability and also a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.1, and a uniform elongation of not less than 10%, which comprises conducting a finish-rolling of a slab prepared by casting a steel consisting essentially of 0.15 to less than 0.30% by weight of C, 2.0 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 2.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, and 0.0005 to 0.01% by weight of Ca or 0.005 to 0.05% by weight of REM, the balance being Fe and inevitable elements, being composed of three phases of ferrite, bainite and retained austenite as microstructure, and having a ferrite grain size (d.sub.F) of not more than 5 .mu.m, a ratio (V.sub.F /d.sub.F) of ferrite volume fraction (V.sub.F) to ferrite grain size (d.sub.F) of not less than 7, and a volume fraction of retained austenite having a grain size of not more than 2 .mu.m being not less than 5%, at an end temperature range of Ar.sub.3 .+-.50.degree. C. at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
9. A process for producing a high yield ratio, hot rolled high strength steel sheet having an excellent formability and also a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.1, and a uniform elongation of not less than 10%, which comprises conducting a finish-rolling of a slab prepared by casting a steel consisting essentially of 0.15 to less than 0.30% by weight of C, 2.0 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 2.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, the balance consisting essentially of Fe, being composed of three phases of ferrite, bainite and retained austenite as microstructure, and having a ferrite grain size (d.sub.F) of not more than 5 .mu.m, a ratio (V.sub.F /d.sub.F) of ferrite volume fraction (V.sub.F) to ferrite grain size (d.sub.F) of not less than 7, and a volume fraction of retained austenite having a grain size of not more than 2 .mu.m being not less than 5%, at an end temperature of not less than Ar.sub.3 -50.degree. C., at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table down to a temperature T.sub.1 in a range of not more than Ar.sub.3 to more than Ar.sub.1 at a rate of less than 30.degree. C./second, and from T.sub.1 downwards at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
10. A process for producing a high yield ratio, hot rolled high strength steel sheet having an excellent formability and also a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.1, and a uniform elongation of not less than 10%, which comprises conducting a finish-rolling of a slab prepared by casting a steel consisting essentially of 0.15 to less than 0.30% by weight of C, 2.0 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 2.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, and 0.0005 to 0.01% by weight of Ca or 0.005 to 0.05% by weight of REM, the balance being Fe and inevitable elements, being composed of three phases of ferrite, bainite and retained austenite as microstructure, and having a ferrite grain size (d.sub.F) of not more than 5 .mu.m, a ratio (V.sub.F /d.sub.F) of ferrite volume fraction (V.sub.F) to ferrite grain size (d.sub.F) of not less than 7, and a volume fraction of retained austenite having a grain size of not more than 2 .mu.m being not less than 5%, at an end temperature of not less than Ar.sub.3 -50.degree. C., at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table down to a temperature T.sub.1 in a range of not more than Ar.sub.3 to more than Ar.sub. 1, at a rate of less than 30.degree. C./second and from T.sub.1 downwards at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
11. A process for producing a high yield ratio, hot rolled high strength steel sheet having an excellent formability and also a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.1, and a uniform elongation of not less than 10%, which comprises conducting a finish-rolling of a slab prepared by casting a steel consisting essentially of 0.15 to less than 0.30% by weight of C, 2.0 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 2.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, the balance consisting essentially of Fe, being composed of three phases of ferrite, bainite and retained austenite as microstructure and having a ferrite grain size (d.sub.F) of not more than 5 .mu.m, a ratio (V.sub.F /d.sub.F) of ferrite volume fraction (V.sub.F) to ferrite grain size (d.sub.F) of not less than 7, and a volume fraction of retained austenite having a grain size of not more than 2 .mu.m being not less than 5%, at an end temperature of not less than Ar.sub.3 -50.degree. C., at an entire draft of not less than 80% and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table down to a temperature T.sub.1 in a range of not more than Ar.sub.3 to more than Ar.sub.1 at a rate of not less than 30.degree. C./second, from T.sub.1 downwards to a temperature T.sub.2 in a range of not more than T.sub.1 to more than Ar.sub.1 at a rate of less than 30.degree. C./second, and furthermore from T.sub.2 downwards at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
12. A process for producing a high yield ratio, hot rolled high strength steel sheet having an excellent formability and also a yield ratio (YR) of not less than 60%, a strength-ductility balance (tensile strength.times.total elongation) of not less than 2,000 (kgf/mm.sup.2.%), an enlargement ratio (d/d.sub.o) of not less than 1.1, and a uniform elongation of not less than 10%, which comprises conducting a finish-rolling of a slab prepared by casting a steel consisting essentially of 0.15 to less than 0.30% by weight of C, 2.0 to 3.0% by weight of Si, 0.5 to 3.0% by weight of Mn, more than 2.5 to 6.0% by weight of Si and Mn in total, not more than 0.02% by weight of P, not more than 0.01% by weight of S, and 0.005 to 0.10% by weight of Al, and 0.0005 to 0.01% by weight of Ca or 0.005 to 0.05% by weight of REM, the balance being Fe and inevitable elements, being composed of three phases of ferrite, bainite and retained austenite as microstructure, and having a ferrite grain size (d.sub.F) of not more than 5 .mu.m, a ratio (V.sub.F /d.sub.F) of ferrite volume fraction (V.sub.F) to ferrite grain size (d.sub.F) of not less than 7, and a volume fraction of retained austenite having a grain size of not more than 2 .mu.m being not less than 5%, at an end temperature of not less than Ar.sub.3 -50.degree. C. at an entire draft of not less than 80%, and an ultimate pass strain speed of not less than 30/second, conducting cooling at a hot run table down to a temperature T.sub.1 in a range of not more than Ar.sub.3 to more than Ar.sub.1 at a rate of not less than 30.degree. C./second, from T.sub.1 downwards to a temperature T.sub.2 in a range of not more than T.sub.1 to more than Ar.sub.1 at a rate of less than 30.degree. C./second, and furthermore from T.sub.2 downwards at a rate of not less than 30.degree. C./second, and conducting coiling at a temperature of more than 350.degree. C. to 500.degree. C.
13. A process for producing a high yield ratio, hot rolled high strength steel sheet excellent in both formability and spot weldability according to any one of claims (1) to (6), wherein the hot finish-rolling initiation temperature of the steel is not more than Ar.sub.3 +100.degree. C.
14. A process for producing a high yield ratio, hot rolled high strength steel sheet excellent in both formability and spot weldability according to any one of claims (1) to (6), wherein after the coiling the steel sheet is cooled to 200.degree. C. or less at a cooling speed of not less than 30.degree. C./hour.
15. A process for producing a high yield ratio, hot rolled high strength steel sheet excellent in formability according to any one of claims (7) to (12), wherein the hot finish-rolling initiation temperature of the steel is not more than Ar.sub.3 +100.degree. C.
16. A process for producing a high yield ratio, hot rolled high strength steel sheet excellent in formability according to any one of claims (7) to (12), wherein after the coiling the steel sheet is cooled to 200.degree. C. or less at a cooling speed of not less than 30.degree. C./hour.

Priority Claims (2)

Number	Date	Country	Kind
3-153795	May 1991	JPX
4-121085	Apr 1992	JPX

PCT Information

Filing Document	Filing Date	Country	Kind	102e Date	371c Date
PCT/JP92/00698	5/28/1992			8/27/1993	8/27/1993

Publishing Document	Publishing Date	Country	Kind
WO92/21784	12/10/1992

US Referenced Citations (1)

Number	Name	Date	Kind
5017248	Kawano et al.	May 1991

Foreign Referenced Citations (11)

Number	Date	Country
0295500	Dec 1988	EPX
58-11734	Jan 1983	JPX
60-43425	Mar 1985	JPX
60-165320	Aug 1985	JPX
60-184664	Sep 1985	JPX
62-164828	Jul 1987	JPX
62-202048	Sep 1987	JPX
63-241120	Oct 1988	JPX
64-79345	Mar 1989	JPX
1-184226	Jul 1989	JPX
1168819	Jul 1989	JPX

High yield ratio-type, hot rolled high strength steel sheet excellent in formability or in both of formability and spot weldability, and production thereof

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US