Patent Application
20110132037
The present invention relates to a hole diameter measuring method and device for a holey optical fiber in which a plurality of holes are formed in silica glass that constitutes an optical fiber, and to a manufacturing method and device for a holey optical fiber that uses this method and device.
In a holey optical fiber, a plurality of holes are formed along the lengthwise direction of the optical fiber in silica glass that constitutes an optical fiber. Such an optical fiber is called a photonic crystal fiber (PCF). This holey optical fiber has optical characteristics that cannot be realized in a conventional optical fiber due to the existence of holes. For example, in this holey optical fiber, the light confining effect of the optical fiber is heightened, and the bending loss is reduced by the existence of the holes.
The holey optical fiber can be manufactured by drawing an optical fiber base material (preform) in which holes are formed. Methods of forming holes in an optical fiber base material include for example a drill method that pierces the optical fiber base material using a drill.
When drawing an optical fiber base material in which holes are formed, pressurizing is performed on the holes on one side of this optical fiber base material. By controlling the pressure that pressurizes these holes, adjustment of the hole diameter in the holey optical fiber bare wire after drawing is possible. That is, a holey optical fiber that has the desired hole diameter is obtained by control of the pressure.
In the holey optical fiber bare wire 22 shown in
Among these parameters, the position p of the hole 22a is mostly determined in the hole opening process that forms holes in the optical fiber base material. Accordingly, the position p of the hole 22a, that is, the diameter of a circle which pass centers of the holes 22a, can be made constant in an optical fiber bare wire that is manufactured if the hole forming process is performed in the accurate location when opening holes in the optical fiber base material.
In contrast to this, the hole diameter d in the drawing process fluctuates due to various causes, such as the hole internal pressure, the furnace temperature, the drawing speed, and the like. Therefore, in order to stably manufacture the holey optical fiber bare wire 22 having the desired hole diameter d, measuring the hole diameter d in-line during the manufacturing process is desired.
For example, if it is possible to measure the hole diameter in-line and adjust the hole internal pressure of the optical fiber base material by a feedback control according to the measurement results, the holey optical fiber bare wire 22 having the desired hole diameter d is obtained over the lengthwise direction of the holey optical fiber.
As a technique to measure the hole diameter in-line in the holey optical fiber manufacturing process, there is a method that is disclosed for example in Patent Document 1. This method consists of irradiating the side of an optical fiber with light from a laser diode (LD), and then measuring the hole diameter based on the interference pattern of the forward scattering light produced by this light irradiation.
Patent Document 2 discloses a technique of making light incident on an optical fiber in-line from one end and imparting a bend to this optical fiber, and measuring the hole diameter based on changes in the rearward scattering light produced by the bend.
Generally, a holey optical fiber has four or more holes 22a as shown in
In the method disclosed in Patent Document 2, since a bend is imparted to the optical fiber, it is necessary to prevent the optical fiber from being damaged by this bend. Also, since it is necessary to impart a bend, the productivity of the optical fiber drops. Furthermore, there is also a problem of this method only being applicable to a holey optical fiber in which the dependency of the bending loss on the hole diameter is large.
The present invention was achieved in view of the above circumstances, and has an object to provide a hole diameter measuring method and device for a holey optical fiber that can measure the hole diameter of an optical fiber while increasing the productivity of the optical fiber without causing damage to the optical fiber, and a manufacturing method and device for a holey optical fiber that uses these.
(1) A hole diameter measuring method for a holey optical fiber according to the present invention is a hole diameter measuring method for a holey optical fiber, the method including: continuously irradiating a side of a holey optical fiber bare wire with parallel light rays, the holey optical fiber bare wire obtained by drawing an optical fiber base material; continuously detecting, with a detecting portion, forward scattering light that is generated by the irradiation of the holey optical fiber bare wire with the parallel light rays; and calculating a diameter of at least one hole in the holey optical fiber bare wire using a correlation relationship between a scattering intensity pattern of the detected forward scattering light and the diameter of the at least one hole.
(2) In the hole diameter measuring method for a holey optical fiber according to (1) above, a covering may not be formed on the holey optical fiber bare wire which is irradiated with the parallel light rays.
(3) In the hole diameter measuring method for a holey optical fiber according to (1) above, it may further include: generating forward scattering light by irradiating a side of a hole-less optical fiber bare wire with parallel light rays and obtaining a scattering intensity pattern of the forward scattering light; and finding a difference spectrum between the scattering intensity pattern that is obtained from the hole-less optical fiber bare wire and the scattering intensity pattern that is obtained from the holey optical fiber bare wire; the calculating the diameter of the at least one hole further includes using a correlation relationship between the difference spectrum and the diameter of the at least one hole.
(4) In the hole diameter measuring method for a holey optical fiber according to (1) above, the continuously irradiating may include irradiating the holey optical fiber bare wire with parallel light rays from at least two directions.
(5) In the hole diameter measuring method for a holey optical fiber according to (1) above, the method may further include: measuring a distance between the holey optical fiber bare wire and the detecting portion, and adjusting a position of the detecting portion based on the measured distance, thus maintaining a constant a distance between the holey optical fiber bare wire and the detecting portion, while performing the detecting of the forward scattering light.
(6) A hole diameter measuring device, for a holey optical fiber according to the present invention is a hole diameter measuring device, for a holey optical fiber, having: an irradiating device that continuously irradiates a side of a holey optical fiber bare wire with parallel light rays; a detecting portion that continuously detects forward scattering light that is generated by the irradiation of the holey optical fiber bare wire with the parallel light rays; and a computing portion that computes a diameter of at least one hole in the holey optical fiber bare wire using a correlation relationship between a scattering intensity pattern of the detected forward scattering light and the diameter of the at least one hole.
(7) The hole diameter measuring device for a holey optical fiber according to (6) above may have a plurality of the irradiating devices and a plurality of the detecting portions.
(8) The hole diameter measuring device for a holey optical fiber according to (6) above may further include an optical fiber position detector that measures a distance between the detecting portion and the holey optical fiber bare wire.
(9) A manufacturing method for manufacturing a holey optical fiber according to the present invention is a manufacturing method for manufacturing a holey optical fiber by heating and melting a holey optical fiber base material and drawing it, having: continuously irradiating a side of a holey optical fiber bare wire with parallel light rays; continuously detecting, with a detecting portion, forward scattering light that is generated by the irradiation of the holey optical fiber bare wire with the parallel light rays; calculating a diameter of at least one hole in the holey optical fiber bare wire using a correlation relationship between a scattering intensity pattern of the detected forward scattering light and the diameter of the at least one hole; and adjusting a pressure in the at least one hole by controlling a flow rate of a gas that is supplied to at least one hole of the holey optical fiber base material in accordance with the calculated hole diameter.
(10) The manufacturing method according to (9) above may further include generating forward scattering light by irradiating a side of a hole-less optical fiber bare wire with parallel light rays and obtaining a scattering intensity pattern of the forward scattering light; finding a difference spectrum between the scattering intensity pattern that is obtained from the hole-less optical fiber bare wire and the scattering intensity pattern that is obtained from the holey optical fiber bare wire; and the calculating the diameter of the hole further includes using a correlation relationship between the difference spectrum and the diameter of the at least one hole.
(11) In the manufacturing method according to (9) above, the continuously irradiating may include irradiating the holey optical fiber bare wire with parallel light rays from at least two directions.
(12) The manufacturing method according to (9) above may further include measuring a distance between the holey optical fiber bare wire and the detecting portion, and continuously detecting the forward scattering light while adjusting the position of the detecting portion based on the measured distance, thus maintaining a constant distance between the holey optical fiber bare wire and the detecting portion.
(13) A holey optical fiber manufacturing device according to the present invention has a melting furnace that heats a holey optical fiber base material; a hole diameter measuring portion that measures a diameter of at least one hole in a holey optical fiber bare wire, the holey base wire obtained by drawing the holey optical fiber base material; and a pressure controlling portion that adjusts a pressure in at least one hole of the optical fiber base material based on a measurement value of the diameter of the at least one hole in the holey optical fiber; the hole diameter measuring portion includes an irradiating device that continuously irradiates a side of the holey optical fiber bare wire with parallel light rays; a detecting portion that detects a scattering intensity pattern of a forward scattering light that is generated by the irradiation; and a computing portion that calculates a diameter of the at least one hole in the holey optical fiber bare wire using a correlation relationship between the scattering intensity pattern and the diameter of the at least one hole; and the pressure controlling portion, based on the diameter of the at least one hole that is calculated by the computing portion, adjusts the pressure in the at least one hole of the optical fiber base material by controlling a flow rate of a gas that is supplied to the at least one hole of the optical fiber base material.
(14) In the holey optical fiber manufacturing device according to (13) above, the hole diameter measuring portion may include a plurality of the irradiating devices and a plurality of the detecting portions.
(15) The holey optical fiber manufacturing device according to (13) above may further include an optical fiber position detector that measures a distance between the detecting portion and the holey optical fiber bare wire.
In the hole diameter measuring method for a holey optical fiber according to (1) above, parallel light rays are continuously irradiated from a side of the holey optical fiber bare wire, and the hole diameter is calculated based on the light amount of the forward scattering light that is generated by this irradiation. For this reason, it is possible to measure the hole diameter of a holey optical fiber without adding bending or the like to the optical fiber. As a result, there is no risk of causing damage to the optical fiber, and productivity is not adversely affected. Also, in the hole diameter measuring method for a holey optical fiber according to (1) above, the hole diameter is computed using a correlation relationship of a scattering intensity pattern of the forward scattering light and the hole diameter. For that reason, it is possible to accurately measure the hole diameter even in the case of a plurality of holes existing. In particular, in the hole diameter measuring method for a holey optical fiber according to (1) above, it is possible to measure the hole diameter in-line. For that reason, it is possible to reduce variations in the hole diameter, and possible to ensure the optical characteristics over the entire length of the manufactured optical fiber.
Hereinbelow, a hole diameter measuring device for a holey optical fiber and a holey optical fiber manufacturing device according to the first embodiment of the present invention shall be described in detail referring to the drawings.
This optical fiber manufacturing device 1 is provided with a melting furnace 2 that heats and melts an optical fiber base material 21 that has a hole 21; the hole diameter measuring device 30 that computes the hole diameter of a holey optical fiber bare wire 22 that is obtained by drawing of the optical fiber base material 21; an outer diameter measuring portion 4 that measures the outer diameter of the holey optical fiber bare wire 22; a pressure controlling portion 6 that controls the flow rate of gas that is supplied to the hole 21a of the optical fiber base material 21 in accordance with the hole diameter that is calculated; a first covering coating portion 7 that forms a first covering layer on the optical fiber bare wire 22; a first covering hardening portion 8 that hardens the first covering layer; a second covering coating portion 9 that forms a second covering layer on the first covering layer; a second covering hardening portion 10 that hardens the second covering layer; and a wind-up portion 11 that winds up the holey optical fiber 25 on which the first covering layer and the second covering layer are formed.
The hole diameter measuring device 30 continuously irradiates parallel light rays on the holey optical fiber bare wire 22 that has been drawn from the side thereof, and computes the hole diameter from the scattering intensity pattern of forward scattering light generated thereby. Details relating to the hole diameter measuring device 30 shall be given below.
The outer diameter measuring portion 4 has a light source (LED, LD or the like) that irradiates light from the side of the holey optical fiber bare wire 22; and a detector that is installed facing this light source. The detector receives the forward scattering light of the light emitted from the light source to the optical fiber bare wire 22a, and analyzes the pattern or intensity thereof. Thereby, the outer diameter of the optical fiber bare wire 22 is measured. It is preferred for the outer diameter measuring portion 4 to be able to irradiate light from a plurality of directions.
The pressure controlling portion 6 controls the flow rate of gas that is sent to the optical fiber base material 21 by a valve or the like based on the hole diameter computed by the hole diameter measuring device 30. This gas is sent from a supply source not shown through a gas supply path 6a to the optical fiber base material 21. Thereby, the pressure in the hole 21a of the optical fiber base material 21 is adjusted.
Next, the hole diameter measuring device 30 shall be described in detail. As shown in
The irradiation device 31 has a light source (for example, and LED or LD) of the parallel light rays 37, and for example a collimating lens that makes the light rays emitted from the light source parallel light rays. This irradiation device 31 is arranged so that the parallel rays 37 are irradiated from a side of the holey optical fiber bare wire 22 and perpendicular to the direction of travel of the holey optical fiber bare wire 22.
The detecting portion 32 continuously detects the forward scattering light 38 that is produced by the parallel light rays 37 being irradiated onto the holey optical fiber bare wire 22, and converts it to an electrical signal. An example of this detecting portion 32 includes a CCD line sensor and the like. The detecting portion 32 has sufficient width to detect the forward scattering light 38 that is produced when the parallel rays 37 are irradiated onto the holey optical fiber bare wire 22. The detecting portion 32 is arranged in an appropriate position to detect the forward scattering light 38.
In the optical fiber manufacturing device 1 of the present embodiment, it is determined whether or not the hole diameter of the holey optical fiber bare wire 22 is the desired hole diameter by the hole diameter measuring device 30A by the method described below. In the case of the hole diameter differing from the desired value, feedback control of the pressure controlling portion 6 is carried out based on the signal from the computing portion 34, and the pressure in the hole 21a of the optical fiber base material 21 is adjusted. Thereby, in the optical fiber manufacturing device 1 of this embodiment, the holey optical fiber bare wire 22 that has the desired hole diameter is obtained.
Next, the hole diameter measuring method for a holey optical fiber according to the first embodiment of a present invention (hereinbelow referred to simply as the hole diameter measuring method) shall be described. The hole diameter measuring method of the present embodiment is performed using the hole diameter measuring device 30A of the aforementioned first embodiment.
First, the principles of the computation method required for computing the hole diameter from the scattering intensity pattern shall be described with reference to
In the hole diameter measuring method of the present embodiment, it is possible to measure a hole diameter by irradiating parallel light rays 37 on the optical fiber bare wire 22, detecting the forward scattering light 38 that is produced by this irradiation, and analyzing the scattering intensity pattern. First, in order to understand the relationship between the parallel light rays 37 and the scattering intensity pattern, a scattering intensity pattern 41 in the case of irradiating the parallel light rays 37 on an optical fiber bare wire 22n that has no holes shall be described.
Since the parallel light rays 37 are directly incident on the central portion of the detecting portion 32 as described above, there is a risk of the sensor (for example, a CCD line sensor) of the detecting portion 32 charging up. In order to prevent this charge up, a mask 32a that consists of a light shielding board is centrally provided in front portion of the detecting portion 32 as shown in
Next, the scattering intensity pattern 43 in the holey optical fiber bare wire 22 shall be described.
In the case of the holey optical fiber bare wire 22, the scattering intensity pattern of the forward scattering light 38 that is obtained by the device configuration as shown in
The phenomenon of the width W of the central dark portion widening when the parallel light rays 37 are being irradiated onto the holey optical fiber bare wire 22 shall be described using
In the case of light rays that do not pass through the region where the hole 22a exists, in the manner of the light ray 37a and light ray 37b, refraction and reflection of the light rays 37a and 37b occur only at an outer diameter boundary 22b of the optical fiber 22, and forward scattering lights 38a and 38b are produced and detected by the detecting portion 32. That is, the light ray 37a and the light ray 37b trace the same path in the case of the optical fiber bare wire 22 that has no holes. The light ray 37b passes through the cladding 24 so as to be tangent with the hole circumcircle 22c that is tangent to the outer side of the plurality of holes 22a (so as to be tangent with the boundary between the holes 22a and the cladding 24). Accordingly, a light rays that is incident to the inside of this light ray 37b (the center side of the optical fiber) passes within the region of the hole circumcircle 22c (passes through the inside of at least one of the holes 22).
As for the light ray 37c that passes through the region where the hole 22a exists (inside of the hole circumcircle 22c), refraction and reflection occur not only at the outer diameter boundary 22b of the optical fiber 22, but also at the boundary between the holes 22a and the cladding 24. For that reason, a forward scattering light 38c that is produced by this light ray 37c becomes light that greatly deviates from the measuring region of the measuring portion 32. As a result, among the forward scattering lights 38 that are detected by the detecting portion 32, the intensity of the forward scattering light 38c that has passed through the inside of the hole 22a becomes extremely small. For this reason, the forward scattering lights that are obtained from the parallel light rays that are irradiated more to the center side of the optical fiber than the light ray 37b are mostly not detected. Note that in the case of the light ray 37c being irradiated on the optical fiber bare wire 22n that has no holes, the forward scattering light thereof is also light that is incident more on the central side of the detecting portion 32 than the light denoted by reference numeral 38b. Accordingly, for these reasons, the width W of the central dark portion of the scattering intensity pattern 43 is wider compared to the width W of the central dark portion of the scattering intensity pattern 42 of the optical fiber bare wire 22n having no holes.
From the above, as the diameter of the hole circumcircle 22c increases, the width W of the central dark portion of the scattering intensity pattern 43 also widens. That is, the width W of the central dark portion has a correlative relationship with the diameter of the hole circumcircle 22c that is the region in which the holes 22a exist (hereinbelow referred to as a hole circumcircle diameter 2r). Here, the width and installation position of the mask 32a need to be set so as not to interfere with the width W of the central dark portion that has widened due to the existence of the holes 22a.
The hole diameter d can be calculated by Equation (1) shown below, with the position p and the hole circumcircle diameter 2r of the hole 22a.
d=(2r−p) (1)
As stated above, the position p of the hole 22a is determined in the stage of forming the holes 21a in the optical fiber base material 21, and is hardly influenced by the drawing conditions. Accordingly, a correlative relationship comes into effect between the hole circumcircle diameter 2r and the width W of central dark portion as mentioned above, that is, it the hole diameter d and the width W of the central dark portion come to have a correlative relationship.
From the above, it is evident that the width W of the central dark portion and the hole diameter d have a correlative relationship.
Accordingly, if the correlative relationship between the width W of the central dark portion and the hole diameter d is found in advance, calculation of the hole diameter d is possible based on the width W of the central dark portion that has been measured.
After the coverings (first covering and second covering) are formed on the optical fiber bare wire 22, it is possible to measure the hole diameter d. However, when the parallel light rays are irradiated after the coverings have been formed, refraction and reflection of the light rays occur at the boundary between of the coverings and the cladding, and the boundary between the first covering and the second covering. That is, effect of the coverings occur at the scattering intensity pattern of the forward scattering light that is obtained. In this case, even for optical fibers in which the cladding outer diameter, the hole position p, and the hole diameter d are the same, if the thickness and material of the coverings differ from each other, it will become impossible to find the hole diameter d using the same correlation equation. Therefore, the need arises to find the correlation equation corresponding to the thickness and material of each covering in advance, which take time and effort. In contrast, in the hole diameter measuring method of the present embodiment, measurement of the hole diameter is performed prior to the coverings (first covering and second covering) being formed on the optical fiber bare wire 22. Accordingly, measurement can be easily performed compared to the case of measuring the hole diameter after the coverings are formed. Moreover, since there is no effect of the coverings on the forward scattering light that is obtained, more accurate measurement of the hole diameter d is possible.
Next, a manufacturing method for the holey optical fiber 25 relating to the first embodiment of the present invention shall be described.
First, a correlation equation of the width W of the central dark portion and the hole diameter d is found in a preparatory step of manufacture.
For optical fibers in which the hole position p is the same, the correlative relationship of the hole diameter d and the width W of the central dark portion is also the same for these optical fibers. Therefore, the hole diameter d of a number of the holey optical fiber bare wires 22 in which the hole diameter d is known is measuring using an optical microscope, and in addition the correlation equation with the width W of the central dark portion that has been measured is obtained. By performing the calculation using this correlation equation, it is possible to calculate the hole diameter d with the measurement value of the width W of the central dark portion.
Next, the hole diameter D of the holes 21a that are formed in the optical fiber base material 21 and the hole circumcircle diameter 2R are determined, and the hole processing is performed in the optical fiber base material 21. Hereinbelow, that procedure shall be described.
In the case of manufacturing the holey optical fiber bare wire 22 by drawing the holey optical fiber base material 21, assuming the application of pressure to the holes 21a of the optical fiber base material 21 and the draw speed of the optical fiber base material 21 are appropriate, and letting the diameter of the optical fiber base material 21 be A, the hole diameter of the optical fiber base material 21 be D, the diameter of the optical fiber bare wire 22 after drawing be a, and the hole diameter be d, the relationship of the following Equation (2) is maintained.
A:D=a:d (2)
Similarly, letting the diameter of the optical fiber base material 21 be A, the hole circumcircle diameter of the optical fiber base material 21 be 2R, the diameter of the optical fiber bare wire 22 after drawing be a, and the hole circumcircle diameter be 2r, the relationship of the following Equation (3) is maintained.
A:2R=a:2r (3)
Therefore, in the manufacture of the holey optical fiber bare wire 22, when the desired hole diameter is determined to be d, and the desired hole circumcircle diameter is determined to be 2r, it is possible to find the hole diameter D of the holey optical fiber base material 21 and the hole circumcircle diameter 2R with Equations (4) and (5), respectively.
D=d×A÷a (4)
2R=2r×A÷a (5)
Using the hole diameter D and the hole circumcircle diameter 2R that are found by the aforementioned Equations (4) and (5), holes are opened in the optical fiber perform, and the holey optical fiber base material 21 is obtained.
Next, while pressurizing the holes 21a of the holey optical fiber base material 21, this holey optical fiber base material 21 is drawn. Thereby, the holey optical fiber bare wire 22 is fabricated.
When drawing the holey optical fiber base material 21, if the pressurization pressure during the drawing is suitable, the hole diameter and hole circumcircle diameter of the holey optical fiber bare wire 22 that is fabricated has the hole diameter d and the hole circumcircle diameter 2r has designed. However, if the pressurization pressure is not suitable, the hole diameter d within the design range is not obtained. Also, due to the fluctuation in the pressurization pressure over time and the fluctuation in the drawing temperature, the hole diameter d is not stable in the lengthwise direction of the optical fiber.
As mentioned above, regardless of the flow rate of gas that is supplied to the base material hole 21a of the holey optical fiber base material 21, the hole position p of the holey optical fiber bare wire 22 after drawing is the same. From this, in the case of the hole circumcircle diameter 2r of the holey optical fiber 22 shifting from the desired value, the hole diameter d indicates that it has not become the desired value, and if the hole circumcircle diameter 2r of the holey optical fiber 22 has become the desired value, the hole diameter d also indicates that it has become the desired value.
In the holey optical fiber manufacturing device 1 of this embodiment, computation of the hole diameter d based on the correlation equation that was found above from the width W of the central dark portion of the obtained scattering intensity pattern is performed by the computing portion 34 at any time. When the hole diameter d shifts from the desired value as described above, the computing portion 34 performs feedback control of the pressure controlling portion 6 to control the flow rate of gas that is sent to the optical fiber base material 21. Accordingly, in the holey optical fiber bare wire 22 obtained by drawing of the optical fiber base material 21, the holey optical fiber bare wire 22 is obtained in which the hole diameter d is stable over the lengthwise direction of the optical fiber without the hole diameter d departing from the allowable range of the designed value.
In the aforementioned method, the hole diameter d was calculated from the width W of the central dark portion, and the pressure control was performed based on the calculated hole diameter d. However, if the desired hole circumcircle diameter 2r is known from the outset, it is possible to compute the width W of the central dark portion of an appropriate scattering intensity pattern from this hole circumcircle diameter 2r. Therefore, it is possible to perform pressure control so that the width W of the central dark portion directly becomes the width W of an appropriate central dark portion without calculating the hole diameter d.
Next, the outer diameter of the holey optical fiber bare wire 22 that has the appropriate hole diameter d is measured by the outer diameter measuring portion 4. Here, it is also possible to control the drawing speed and the like according to the outer diameter of the holey optical fiber bare wire 22 that was measured.
Subsequently, a first covering layer and a second covering layer are administered to the holey optical fiber bare wire 22 by the first covering coating portion 7 and the first covering hardening portion 8, and the second covering coating portion 9 and the second covering hardening portion 10, respectively. Thereby, the holey optical fiber 25 is obtained. The holey optical fiber 25 is rolled up by a rolling-up portion.
The hole diameter measuring method of the present embodiment differs from the hole diameter measuring method of the first embodiment on the point of finding the width W of the central dark portion using the difference spectrum of the scattering intensity pattern that is obtained with a holey optical fiber and the scattering intensity pattern that is obtained with an optical fiber having no holes.
Note that when manufacturing a holey optical fiber, it is the same as that of the above-mentioned first embodiment besides finding the width W of the central dark portion using a difference spectrum. At this time, in the computing portion 34 in the hole diameter measuring device 30, it is programmed so that the width W of central dark portion is found using the difference spectrum. The other constitutions of the hole diameter measuring device 30 and the holey optical fiber manufacturing device are the same as the first embodiment.
In a holey optical fiber, for example, when there are many holes formed, or when the diameter of the holes is comparatively large, judging the intensity peaks of forward scattering light may be difficult. This is due to the following reason. When there are many holes, or when the diameter of a hole is comparatively large, the length of the periphery of the entire hole becomes long, and the boundary portion of air and silica glass increases. When parallel rays are irradiated to such a holey optical fiber, interference easily occurs in the forward scattering light that is obtained because the boundary portion between the air and silica glass has increased. Due to this interference, judging of the intensity peak of the forward scattering light becomes difficult.
In the hole diameter measuring method of the present embodiment, first the scattering intensity pattern of the forward scattering light of a hole-less optical fiber in which holes are not imparted beforehand is obtained. Subsequently, the scattering intensity pattern of the forward scattering light of a holey optical fiber is obtained. The scattering intensity pattern of the forward scattering light of the hole-less optical fiber and the scattering intensity pattern of the forward scattering light of the holey optical fiber are shown in
The scattering intensity pattern of the forward scattering light of a hole-less optical fiber is measurable with the hole diameter measuring device 30A of the first embodiment. Immediately after the start of spinning of a holey optical fiber, an optical fiber bare wire is produced in the state of the hole being blocked. If a scattering intensity pattern of forward scattering light is obtained by irradiating parallel light rays on the optical fiber bare wire in the state of the hole being blocked, the hole diameter measuring method of the present embodiment can be performed with the same manufacturing process, manufacturing apparatus, and conditions of manufacture as a holey optical fiber.
In the hole diameter measuring method of the aforementioned first embodiment (the hole diameter measuring device 30A), the width W of the central dark portion of the scattering intensity pattern 43 may end up changing due to the direction in which the parallel light rays 37 are irradiated.
In contrast to this, in the hole diameter measuring method of the present embodiment, as shown in
In the hole diameter measuring method and the hole diameter measuring device 30B of the present embodiment, the case was shown of obtaining a scattering intensity pattern by irradiating the parallel light rays 37a and 37b from two directions. However, even in the case of irradiating the parallel light rays 37 from one direction, an appropriate width W of the central dark portion is obtained similarly to the present embodiment by adding a rotation movement of at least 90 degrees to the optical fiber bare wire 22 itself.
Even in the present embodiment, the width W of the central dark portion may be determined by finding the difference spectrum between the scattering intensity pattern of the forward scattering light that is obtained with a holey optical fiber and the scattering intensity pattern of the forward scattering light that is obtained with a hole-less optical fiber, similarly to the afore-described second embodiment. Similarly to the above-mentioned case, measurement of the hole diameter becomes possible even for a holey optical fiber that has many holes and a holey optical fiber with a large hole diameter.
The width W of the central dark portion of the scattering intensity pattern changes in accordance with the relative positions of the optical fiber bare wire 22 and the detecting element 32 even for holey optical fibers that have the same hole circumcircle diameter. Causes of a change in the relative position of the optical fiber bare wire 22 and the detecting element 32 include for example changes of the pass line of the optical fiber during spinning and in each spinning operation. As shown in
In the hole diameter measuring method of the present embodiment, the position of the optical fiber bare wire 22 is always detected by providing the optical fiber position detector 39 in a perpendicular direction with the detecting portion 32 as shown in
In this way, according to the hole diameter measuring method of the present embodiment, hole diameter measurement can be performed in the state of the positions of the optical fiber bare wire 22 and the detecting portion 32 being constantly maintained. For this reason, it is possible to calculate the hole diameter d from the width W of the central dark portion of the scattering intensity pattern with greater accuracy and free of error. If a holey optical fiber is manufactured while controlling the pressure of the gas that is supplied to the hole 21a of the optical fiber base material 21 based on the hole diameter d that is calculated by the hole diameter measuring method of the present embodiment, the holey optical fiber 25 is obtained in which the hole diameter d is more stable along the lengthwise direction of the optical fiber. In this case, the holey optical fiber manufacturing device is the same as the holey optical fiber manufacturing device 1 shown in the aforementioned first embodiment, except for the hole diameter measuring device 30 being the constitution shown in
Changes in the relative position of the optical fiber bare wire 22 and the detecting portion 32 also occur due to differences between manufacturing devices of holey optical fibers. In this case, the detecting portion 32 should be arranged so that the relative position of the optical fiber bare wire 22 and the detecting portion 32 becomes an appropriate position.
The optical fiber position detector 39 is not particularly limited provided it is capable of always detecting the distance between the optical fiber bare wire 22 and the detecting portion 32. In the event of the position from the optical fiber bare wire 22 to the detecting portion 32 having changed, this optical fiber position detector 39 preferably can transmit a signal in accordance with this change amount to the aforementioned moving mechanism.
Even in the present embodiment, the width W of the central dark portion may be determined by finding the difference spectrum between the scattering intensity pattern of the forward scattering light that is obtained with a holey optical fiber and the scattering intensity pattern of the forward scattering light that is obtained with a hole-less optical fiber in the same manner as the afore-described second embodiment. Similarly to the above-mentioned case, measurement of the hole diameter becomes possible even for a holey optical fiber that has many holes and a holey optical fiber with a large hole diameter.
Also, the width W of the central dark portion may be measured from a plurality of directions of the optical fiber bare wire 22 by a plurality of irradiating devices 31 (31A, 31B) and detecting portions 32 (32A and 32B) which are provided in the hole diameter measuring device 30C, similarly to the afore-described third embodiment. Similarly to the aforementioned case, it is possible to obtain an appropriate width W of the central dark portion, and measurement of the hole diameter can be performed with good accuracy. In this case, it is possible to impart the functions of the irradiating device 31 and the optical fiber position detector 39 to the same device. In this case, a reduction in size of the hole diameter measuring device is achieved.
The holey optical fiber 25 shown in
The holey optical fiber 25 has eight holes 22a that are arranged at regular intervals along the circumferential direction in the cladding 24 that is near the core glass layer 23. These holes 22a are formed along the lengthwise direction of the optical fiber 25. The hole diameters d of these eight holes are all the same. A covering layer 26 that consists of a first covering layer and a second covering layer are disposed around the cladding 24.
Two LEDs are provided as irradiating devices 31 in the hole diameter measuring device 30B. These irradiating devices 31 (31A and 31B) are arranged so that the parallel light rays 37 that are irradiated from the respective LEDs are perpendicular. CCD line sensors are respectively provided as the detecting portions 32 (32A and 32B) at positions sandwiching the optical fiber bare wire 22 and facing each irradiating device 31 (31A and 31B). A mask 32a that is set in advance so as not to interfere with the hole existence region is installed directly before the middle of the detecting portion 32.
In the signal processing portion 33, a setting is made so as to adopt the larger value of the widths W of the central dark portions of the two scattering intensity patterns 43 that are obtained by the two detecting portions 32A and 32B as the width of the central dark portion. Then, this value is used in the computing process of the hole circumcircle diameter 2r and/or the hole diameter d.
The outer diameter of the optical fiber bare wire 22 is set to 125.0 μm. The hole position p is set to 19.5 μm.
In the present test example, measurement was carried out on three types of samples (test examples 1 to 3) in which the hole diameter d differs. Also, measurement was conducted on an optical fiber bare wire in which holes 22a are not formed.
The width W of the central dark portion shown in
As shown in
The above result showed that a correlation relationship was seen between the width W of the central dark portion obtained from the scattering intensity pattern of the forward scattering light 38 and the actual hole diameter d, for the same hole position p. From this, it was confirmed that the hole diameter d was computable by measuring the width W of the central dark portion of the forward scattering light 38.
The holey optical fibers of the test examples 4 to 16 with different hole diameters were manufactured with the same device as the test examples 1 to 3. The test examples 4 to 16 are the same as the test examples 1 to 3 except for having a larger hole diameter than the test examples 1 to 3. In these test examples 4 to 16, the width W of the central dark portion was found using the difference spectrum between the scattering intensity pattern of the forward scattering light of a holey optical fiber and the scattering intensity pattern of the forward scattering light of a hole-less optical fiber, as shown in the aforementioned second embodiment.
As shown in
The above result showed that a correlation relationship was seen between the width W of the central dark portion obtained from the difference spectrum of the scattering intensity pattern of the forward scattering light 38 and the actual hole diameter d, for the same hole position p. From this, it could be confirmed that the hole diameter d can be computed by measuring the width W of the central dark portion of the forward scattering light 38 using the difference spectrum. Moreover, it could be confirmed that the hole diameter can be accurately measured by adopting the hole diameter measuring method of the aforementioned second embodiment even for a holey optical fiber with a large hole diameter or many holes.
The holey optical fiber 25 shown in
The bending loss was measured by the method in accordance with IEC60793-1-47. The measurement wavelength was 1550 nm, and the bending diameter was 10 mm.
The holey optical fiber 25 was manufactured similarly to the embodiment, except for not performing calculation of the hole diameter (measurement) and feedback control of the gas flow rate by the pressure controlling portion 6 based on this measurement in-line. Also, the hole diameter d and the bending loss were measured in the same manner as the embodiment. The results are shown in Table 2. The sample number of the comparative example was 22, and the average values and the like are shown as measurement results.
From Table 2, the hole of the optical fiber that is obtained in the example has a stable hole diameter over the entire length. For that reason, it is evident that an optical fiber with low bending loss is obtained.
According to the holey optical fiber measuring method of the present invention, it is possible to measure the hole diameter of a holey optical fiber without adding bending or the like to the optical fiber. As a result, there is no risk of causing damage to the optical fiber, and productivity is not adversely affected. Also, the hole diameter is computed using the correlation relationship between the scattering intensity pattern of the forward scattering light and the hole diameter. For that reason, even in the case of a plurality of holes existing, it is possible to accurately measure the hole diameter. In particular, since the hole diameter can be measured in-line, it is possible to reduce variations in the hole diameter in the lengthwise direction of an optical fiber, and possible to ensure the optical characteristics of the manufactured optical fiber over the entire length thereof.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2009-094851 | Apr 2009 | JP | national |
This is a Continuation Application of International Application No. PCT/JP2010/002608, filed on Apr. 9, 2010, which claims priority to Japanese Patent Application No. 2009-094851, filed on Apr. 9, 2009. The contents of the aforementioned applications are incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/JP2010/002608 | Apr 2010 | US |
| Child | 13029628 | US |