Patent Grant
9174100
1. Field of the Invention
The present invention relates to a hollow golf club head.
2. Description of the Related Art
As wood golf club heads such as driver and fairway wood golf club heads, hollow metallic golf club heads are well known. In general, a hollow wood golf club head has a face portion for hitting a golf ball, a crown portion which forms the upper surface portion of the golf club head, a sole portion which forms the bottom surface portion of the golf club head, a side portion which forms the toe-, back-, and heel-side side surface portions of the golf club head, and a hosel portion. A shaft is inserted into the hosel portion, and fixed by, for example, an adhesive.
Although an aluminum alloy, stainless steel, or a titanium alloy is often used as a material which constitutes the hollow golf club head, titanium alloy in particular is extensively used these days.
Japanese Patent Laid-Open No. 2009-153802 describes a golf club head having a thin portion at the central portion of the crown portion, and a thick portion surrounding it. The thin portion is formed by casting and chemical milling. In this golf club head, portions other than the face portion are integrally molded by casting, and a bulged portion is formed in the crown portion to bulge outwards. After casting, the protrusion of the bulged portion is removed by chemical milling to form a thin portion.
In Japanese Patent Laid-Open No. 2009-153802 mentioned above, only thin and thick portions are formed in the crown portion. With such a structure, a step between the thin and thick portions is large, so stress is likely to concentrate at the boundary portion between the thin and thick portions upon striking a golf ball.
To solve this problem, a medium thick portion can be formed between the thin and thick portions, and a cavity-shaped mold for casting, which has a step portion for forming the medium thick portion, is used in this case. It is thus necessary to use a mold with another shape every time the width and thickness of the medium thick portion are changed, thus increasing the cost of the molds.
As in Japanese Patent Laid-Open No. 2009-153802 mentioned above, when the protrusion of the bulged portion is removed to form a thin portion, a trace of removal of the protrusion of the bulged portion remains in the crown portion. Hence, the boundary between the removed bulged portion and the unremoved portion surrounding it becomes conspicuous, and degrades the aesthetic appearance.
It is the first object of the present invention to make it possible to easily manufacture a golf club head having a metal plate portion with thin, thick, and medium thick portions at a low cost.
It is the second object of the present invention to provide a golf club head which has a metal plate portion with thin and thick portions, and exhibits a good aesthetic appearance.
In order to achieve the first object, according to the present invention, there is provided a hollow golf club head including a metal plate portion provided with a thin portion and a thick portion, wherein a medium thick portion having an intermediate thickness between a thickness of the thin portion and a thickness of the thick portion is formed at a boundary portion between the thin portion and the thick portion, and the thin portion and the medium thick portion are formed by the steps of pressing the metal plate portion to form a recess in one surface of the metal plate portion and a projection on the other surface thereof, performing chemical milling of the recess and a portion surrounding the recess, and removing the projection by grinding. A method of manufacturing the same is also provided.
In order to achieve the second object, according to the present invention, there is provided a hollow golf club head including a metal plate portion provided with a thin portion and a thick portion, wherein the thin portion is formed by the steps of forming a recess in a head inner surface of the metal plate portion and a projection on a head outer surface thereof, and removing the projection by grinding, and a low-reflection coating is applied onto the outer surface of the metal plate portion. A method of manufacturing the same is also provided.
Further features of the present invention will become apparent from the following description of exemplary embodiments with reference to the attached drawings.
<First Embodiment>
An embodiment will be described below with reference to
A golf club head 1 is a hollow driver head, and has a face portion 2, crown portion 3, sole portion 4, side portion 5, and hosel portion 6. The golf club head 1 is made of a titanium alloy.
The golf club head 1 is manufactured by, for example, forming a crown portion and the remaining portions (head body) as separate portions, and integrating these portions by welding such as laser welding or plasma welding. Note that the crown portion and face portion may be integrated with each other, and welded to the remaining portions to serve as the head body. The crown portion and face portion may be formed as separate portions, and welded to the remaining portions to serve as the head body.
The head body is a cast product, which can be easily manufactured even when a complex shape is formed. However, the head body may be a forged product.
The central portion of the crown portion 3 constitutes a thin portion 3a, its surrounding portion constitutes a medium thick portion 3b, and its surrounding portion constitutes a thick portion 3c. The area of the thin portion 3a is preferably 30% to 90%, and more particularly about 60% to 80% of that of the crown portion 3. The width of the medium thick portion 3b (the average width in the direction from the thin portion 3a to the thick portion 3c) is preferably 5 to 25 mm, and more particularly about 10 to 15 mm.
The thickness of the thick portion 3c is preferably 0.6 to 1.2 mm, and more particularly about 0.7 to 0.9 mm. The thickness of the thin portion 3a is preferably 30% to 70%, and more preferably about 40% to 60% of that of the thick portion 3c, and the thickness of the medium thick portion 3b is preferably 50% to 90% and more preferably about 60% to 80% of that of the thick portion 3c.
To manufacture the crown portion 3, a plate made of titanium or a titanium alloy is pressed to form a blank plate 3A, as shown in
Since the golf club head 1 configured as mentioned above has a thin portion at the central portion of the crown portion 3, it easily flexes upon hitting a golf ball, increases the launch angle of the golf ball, and improves the repulsive force to increase the flight distance.
The golf club head 1 is provided with the medium thick portion 3b between the thin portion 3a and the thick portion 3c, so stress is dispersed upon hitting a golf ball. This makes it possible to improve the durability of the golf club head 1. It is also possible to improve an impact feel and an impact sound.
As shown in
As described above, a golf club head according to this embodiment has a metal plate portion with thick and thin portions, and a medium thick portion at their boundary. Hence, stress is dispersed upon hitting a golf ball more widely in this golf club head than in a golf club head having only thick and thin portions.
Because the medium thick portion is formed by chemical milling, the press die need not have a step portion for forming the medium thick portion. This makes it possible to form metal plate portions having medium thick portions with various shapes using one press die, and, in turn, to reduce the manufacturing cost of a golf club head.
<Second Embodiment>
A golf club head 1′ according to another embodiment will be described with reference to
In the golf club head 1′, a plurality of thin portions 3d are formed in a crown portion 3′ to extend in the front-to-back direction. The thin portions 3d are aligned in the toe-to-heel direction with gaps between them. Medium thick portions 3e are formed on the two sides (toe and heel sides) of each thin portion 3d. Other constituent components are the same as in the golf club head 1, and the same reference numerals denote the same parts.
The crown portion 3′ of the golf club head 1′ is also manufactured by pressing a titanium or titanium alloy plate to form a blank plate having a recess and projection, performing a chemical milling process on the blank plate, and removing the projection by grinding.
Although the thin portions 3d and medium thick portions 3e extend in the front-to-back direction in the golf club head 1′ shown in
Although all of thin, medium thick, and thick portions are formed in the crown portion in the above-mentioned embodiment, they may be formed in the side, heel, face or sole portion using a similar method.
<Third Embodiment>
The crown portion 3 of the golf club head 1 according to the above-mentioned first embodiment, or the crown portion 3′ of the golf club head 1′ according to the above-mentioned second embodiment may be coated with a low-reflection coating. By applying a low-reflection coating to the crown portion 3 or 3′, the boundary between a trace of grinding removal of the projection 3t and the unremoved region surrounding it becomes inconspicuous and excellent in aesthetic appearance. Note that a low-reflection coating may be applied to portions other than the crown portion. The low-reflection coating preferably has a gloss value of 40 to 70 and more preferably 40 to 60.
Although a medium thick portion is formed in the above-mentioned first and second embodiments, a low-reflection coating is also applicable to a golf club head provided with only thin and thick portions formed by pressing or grinding while omitting a medium thick portion.
A matte coating suitable as a low-reflection coating will be described next. As a base coating resin for a matte coating, various base coating resins for golf club heads, such as polyester resin, epoxy resin, acrylic resin, silicone resin, and fluorocarbon resin, can be used. A matte coating is prepared by blending a silica powder with the base resin. The average particle size of a silica powder is preferably about 0.1 to 20 μm. The gloss value of a coating is preferably 40 to 70 and more preferably about 40 to 60 in determining the amount of blending of a silica powder.
The coating may contain, for example, a pigment, curing catalyst, plasticizer, polymerization inhibitor, anti-settling agent, solvent, antifoaming agent, deposition aid, thickener, dispersant, germicide, and ultraviolet absorber.
To apply a coating, first, the head is undercoated. Examples of this undercoating process are priming and ion plating. As a coating method, various methods such as brush coating, spray coating, and electrostatic coating can be used. Note that the head may be coated twice or more, and a matte coating is applied to at least the top layer in this case. The coating thickness (the total thickness when two or more layers are applied) is preferably 10 to 80 μm and more preferably about 40 to 60 μm.
With this arrangement, the golf club head according to this embodiment has a metal plate portion with a thick portion, and a thin portion formed by grinding removal of a projection, and its outer surface is coated with a low-reflection coating, so the boundary between a trace of grinding removal of the projection 3t and the unremoved region surrounding it becomes inconspicuous and excellent in aesthetic appearance.
While the present invention has been described with reference to exemplary embodiments, it is to be understood that the invention is not limited to the disclosed exemplary embodiments. The scope of the following claims is to be accorded the broadest interpretation so as to encompass all such modifications and equivalent structures and functions.
This application claims the benefit of Japanese Patent Applications No. 2012-141166, filed Jun. 22, 2012, and No. 2012-141167, filed Jun. 22, 2012, which are hereby incorporated by reference herein in their entirety.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2012-141166 | Jun 2012 | JP | national |
| 2012-141167 | Jun 2012 | JP | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4139196 | Riley | Feb 1979 | A |
| 4214754 | Zebelean | Jul 1980 | A |
| 5921872 | Kobayashi | Jul 1999 | A |
| 6381828 | Boyce et al. | May 2002 | B1 |
| 6604568 | Bliss et al. | Aug 2003 | B2 |
| 6623376 | Poynor | Sep 2003 | B2 |
| 6645087 | Yabu | Nov 2003 | B2 |
| 7108614 | Lo | Sep 2006 | B2 |
| 7134972 | Hsu et al. | Nov 2006 | B2 |
| 7250007 | Lu | Jul 2007 | B2 |
| 7377861 | Tateno et al. | May 2008 | B2 |
| 7431668 | Tateno et al. | Oct 2008 | B2 |
| 7435191 | Tateno et al. | Oct 2008 | B2 |
| 7455597 | Matsunaga | Nov 2008 | B2 |
| 7575525 | Matsunaga et al. | Aug 2009 | B2 |
| 7785213 | Matsunaga et al. | Aug 2010 | B2 |
| 7819758 | Matsunaga et al. | Oct 2010 | B2 |
| 7846039 | Gilbert et al. | Dec 2010 | B2 |
| 7942759 | Matsunaga et al. | May 2011 | B2 |
| 8133135 | Stites et al. | Mar 2012 | B2 |
| 8172697 | Cackett et al. | May 2012 | B2 |
| 8216089 | Matsunaga et al. | Jul 2012 | B2 |
| 8221260 | Stites et al. | Jul 2012 | B2 |
| 8308582 | Tanimoto | Nov 2012 | B2 |
| 8540590 | Tsukada et al. | Sep 2013 | B2 |
| 8771095 | Beach et al. | Jul 2014 | B2 |
| 8790196 | Solheim et al. | Jul 2014 | B2 |
| 20050034834 | Huang | Feb 2005 | A1 |
| 20130310192 | Wahl et al. | Nov 2013 | A1 |
| 20140155193 | Takechi | Jun 2014 | A1 |
| 20150045147 | Abe | Feb 2015 | A1 |
| Number | Date | Country |
|---|---|---|
| 3056395 | Jun 2000 | JP |
| 2001-346920 | Dec 2001 | JP |
| 2003-10366 | Jan 2003 | JP |
| 4021727 | Dec 2007 | JP |
| 2008-119445 | May 2008 | JP |
| 2008-154624 | Jul 2008 | JP |
| 4545178 | Sep 2008 | JP |
| 2009-153802 | Jul 2009 | JP |
| 2010-530783 | Sep 2010 | JP |
| 5102084 | Dec 2012 | JP |
| 5135783 | Feb 2013 | JP |
| 2008157691 | Dec 2008 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20130344987 A1 | Dec 2013 | US |