The present invention, relates to hollow polymer particles and a method tor producing the same.
Polymer particles having voids inside thereof are being developed as functional members, such as light, diffusing agents, matting agents, heat insulating agents, and lightening agents, by making use of she voids.
PTL 1 discloses an invention relating to hollow porous resin particles comprising a mesoporous structure and an outer shell formed on the surface of the mesoporous structure. The hollow porous resin particles axe described as being obtained by allowing an oil-soluble polymerisation initiator and a water-soluble polymerisation initiator to simultaneously act when a polymerisable monomer is subjected to suspension polymerisation in a water system.
However, since the surface layer of the hollow porous resin particles is extremely thin and brittle, there is a high risk that the particles are destroyed due to the application of an external force to expose the inside.
On the other hand, PTL 2 discloses porous resin particles comprising a methacrylic resin, wherein the particles are porous inside and are provided on their surface with a non-porous surface layer. The porous resin particles are described as being obtained by swelling slightly crosslinked (0.15%) particles with an alcohol solvent, then, dropping them into an aqueous system fox precipitation, and removing the alcohol.
However, even such porous resin particles do not have a sufficient crosslinked structure, and the strength of the particles is insufficient. For this reason, the particles may be deformed by an external force, and their internal pores may be crashed. In addition, the solvent resistance is insufficient, and it is difficult to use them with media other than aqueous media.
As described above, conventional hollow porous particles did not have sufficient mechanical strength and were easily deformed and broken due to the application of an external force, and it was difficult to maintain their shape under conditions where an external force was applied. Even if such hollow porous particles having insufficient mechanical strength are used as a light diffusing agent or a matting agent to produce optical films, paints, etc., coating films formed from the resulting optical films and paints are vulnerable to scratches.
PTL 1: JP2017-82152A
PTL 2: JP2015-67503A
In view of the above circumstances, an object of the present invention is to provide hollow polymer particles having high, mechanical strength.
As a result of extensive studies to achieve the above object, the present inventor found that hollow particles comprising a polymer containing specific monomer units and having a specific volume average particle diameter have high, mechanical strength. The present inventor has completed the present invention upon further studies based on the above finding.
Specifically, the present invention provides the following hollow polymer particles.
Item 1.
hollow polymer particles comprising a polymer containing a vinylic monomer unit and a phosphate ester monomer unit, the hollow polymer particles having a volume average particle diameter of 0.5 to 1000 μm.
Item 2.
The hollow polymer particles according to Item 1, wherein the phosphate ester monomer unit has an ethylenically unsaturated group.
Item 3.
The hollow polymer particles according to Item 1 or 2, wherein the phosphate ester monomer unit is represented by the following formula (1):
wherein R1 is a (meth)acrylic group or an allyl group, R2 is a linear or branched, alkylene group, m is an integer of 1 to 30, n is 0 or 1, v is an integer of 1 to 10, and x is 1 or 2.
Item 4.
Hollow polymer particles comprising a polymer containing a vinylic monomer unit,
the hollow polymer particles having a phosphorus element content of 2 to 200 mg/kg and an alkaline earth metal element content of 1 to 100 mg/kg, wherein the phosphorus element content is larger than the alkaline earth metal element content, and
the hollow polymer particles having a volume average particle diameter of 0.5 to 1000 μm.
Item 5.
The hollow polymer particles according to any one of Items 1 to 4, which have a specific surface area of 1 to 30 m2/g and a bulk specific gravity of 0.1 to 0.4 g/cm3,
Item 6.
The hollow polymer particles according to any one of Items 1 to 4, wherein the particles each have a porous structure inside thereof.
Item 7.
The hollow polymer particles according to any one of Items 1 to 4, wherein the particles each have only one pore inside thereof.
Item 8.
A resin composition comprising the hollow polymer particles according to any one of Items 1 to 7.
Item 9.
A coating composition comprising the hollow polymer particles according to any one of Items 1 to 7.
Item 10.
A cosmetic comprising the hollow polymer particles according to any one of Items 1 to 7.
Item 11.
A light diffusion film comprising the hollow polymer particles according to any one of Items 1 to 7.
Item 12.
A method for producing hollow polymer particles, the method comprising subjecting a monomer mixture containing 0.01 to 1 part by mass of a phosphate ester monomer unit based on 100 parts by mass of a vinylic monomer unit to suspension polymerisation in the presence of a non-polymerizable organic compound and a dispersant.
Item 13.
The method for producing hollow polymer particles according to Item 12, wherein the dispersant is a phosphate of an alkaline earth metal.
The hollow polymer particles of the present invention have high, mechanical strength.
The hollow polymer particles of the present invention comprise a polymer containing a vinylic monomer unit and a phosphate ester monomer unit, and have a volume average particle diameter of 0.5 to 1000 μm.
The hollow polymer particles of the present invention may have a form with one hollow structure inside the particles, or may have a porous structure inside the particles. Further, the shape of the particles is preferably spherical in consideration of the mechanical strength of the particles.
The volume average particle diameter of the hollow polymer particles is 0.5 μm or more, and preferably 2 μm or more. If the volume average particle diameter of the hollow polymer particles is less than 0.5 μm, when the hollow polymer particles are mined in a coating film or the like, it is necessary to mix them in a large amount in order to obtain the desired optical characteristics, which is uneconomical. In contrast, the volume average particle diameter of the hollow polymer particles is 1000 μm or less, preferably 100 μm or leas, and more preferably 50 μm or less. If the volute average particle diameter of the hollow polymer particles exceeds 1000 μm, the hollow polymer particles are removed from the coating film.
In the present specification, the volume average particle diameter of the hollow polymer particles can be determined by the Coulter method. The volume overage particle diameter of the hollow polymer particles is measured with a Coulter Mnltisiser™ 3 (analyser produced by Beckman Coulter). More specifically, the measurement is carried out using an aperture calibrated according to the Multisizer™ 3 user's manual, published by Beckman Coulter. The aperture used for measurement is suitably selected depending on the site of the hollow polymer particles to be measured. The current (aperture current) and gain are suitably set depending on the size of the selected aperture. For example, when an aperture with a size of 50 μm is selected, the current (aperture current) is set to be −800, and the gain is set to be 4. The measurement sample used is a dispersion obtained by dispersing 0.1 g of hollow polymer particles in 10 ml of a 0.1 wt % nonionic surfactant aqueous solution using a touch mixer (Touch Mixer MT-31, produced by Yamaha Scientific Co., Ltd.) and an ultrasonic cleaner (Ultrasonic Cleaner VS-150, produced by Velvo-Clear Co.). During measurement, gentle stirring is performed to an extent in which bubbles are not formed in the beaker. The measurement is ended when the measurement of 100000 hollow polymer particles is completed. The volume average particle diameter of the hollow polymer particles is the arithmetic mean in the particle size distribution on a volume basis of 100000 particles.
While the hollow polymer particles preferably have a hollow structure or porous structure inside thereof, the surface of the hollow polymer particles is preferably non-porous. More specifically, the specific surface area of the hollow polymer particles is preferably 1 m2/g or more, and more preferably 1.5 m2/g or more. High light diffusivity can be obtained by adopting such a configuration. On the other hand, the specific surface area of the hollow polymer particles is preferably 30 m2/g or less, and more preferably 23 m3/g or less, because there are less shrinkage and cracking on the particle surface. In the present specification, the specific surface area of the hollow polymer particles is defined as being measured according to the BET method (nitrogen adsorption method) described in ISO 3277, 1st edition, JIS Z 8830:2001.
Moreover, the bulk specific gravity of the hollow polymer particles is preferably 0.1 g/cm3 or more, and more preferably 0.15 g/cm3 or more, because of high strength. On the other hand, the bulk specific gravity of the hollow polymer particles is preferably 0.4 g/cm5 or less, and more preferably 0.35 g/cm3 or less, because the weight is light and light diffusivity can be obtained by adding a small amount of the hollow polymer particles. In the present specification, the bulk specific gravity of the hollow polymer particles is defined as being measured according to JIS K5101-12-1 (Test methods for pigments—Part 12: Apparent density or apparent specific volume—Section 1: Loose packing method).
The hollow polymer particles are configured to comprise a polymer containing a vinylic monomer unit and a phosphate ester monomer unit.
The vinylic monomer unit used is not particularly limited, and known vinylic monomer units can be widely used. Specifically, examples of a monofunctional vinylic monomer unit having one ethylenically unsaturated group include (meth)acrylic acid, (meth)alkyl acrylate monomer unit, 2-hydrohyethyl methacrylate, 2-methoxyethyl methacrylate, glycidyl methacrylate, tetrahydrofurfuryl methacrylate, diethylaminoethyl methacrylate, trifluoroethyl methacrylate, heptadecafluorodecyl methacrylate, styrenic monomer unit, vinyl acetate, and the like. The alkyl group contained in the (meth)alkyl acrylate monomer unit may be linear or branched. Examples of the (meth)alkyl acrylate monomer include alkyl acrylates, such as methyl acrylate, ethyl acrylate, n-butyl acrylate, isobutyl acrylate, and 2-ethylhexyl acrylate; alkyl methacrylates, such as n-butyl methacrylate, 2-ethylhexyl methacrylate, methyl methacrylate, ethyl methacrylate, isobutyl methacrylate, cyclohexyl methacrylate, benzyl methacrylate, and isobornyl methacrylate; and the like. The alkyl group contained in the (meth)alkyl acrylate monomer is preferably a C1-8 alkyl group, and more preferably a C1-4 alkyl group. When the alkyl group contained in the (meth)alkyl acrylate monomer has 1 to 8 carbon atoms, the stability of the dispersion is excellent during suspension polymerization. As a result, hollow polymer particles with high mechanical strength can be easily obtained.
Examples of the styrenic monomer include styrene, p-methylstyrene, α-methylstyrene, and the like. Further, examples of a polyfunctional vinylic monomer unit haring two or more ethylenically unsaturated groups include a polyfunctional (meth)acrylate monomer unit, an aromatic divinylic monomer unit, and the like.
Examples of the polyfunctional (meth)acrylate monomer include ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, nonaethylene glycol di(meth)acrylate, tetradecaethylene glycol di(meth)acrylate, decamethylene glycol, di(meth)acrylate, pentadecaethylene glycol di(meth)acrylate, 1,3-butylene glycol di(meth)acrylate, 1,4-butanediol di(meth)acrylate, 1,6-hexanediol di(meth)acrylate, glycerol di(meth)acrylate, trimethylolpropane tri(meth)acrylate, pentaerythritol tetra(meth)acrylate, diethylene glycol di(meth)phthalate, caprolactone-modified dipentaerythritol hexa(meth)acrylate, caprolactone-modified hydroxypivalate neopentyl glycol diacrylate, polyester acrylate, urethane-acrylate, and the like.
Examples of the aromatic divinylic monomer include divinyl benzene, divinyl naphthalene, and derivatives thereof.
It is preferable that the vinylic monomer unit contains a polyfunctional vinylic monomer unit, such us ethylene glycol dimethacrylate, trimethylolpropane trimethacrylate, or divinyl benzene, because the resulting hollow polymer particles have excellent solvent resistance in addition to high mechanical strength.
The polyfunctional vinylic monomer unit is preferably contained in an amount of 5 mass % or more, and more preferably 10 mass % or more, in 100 mass % of the entire vinylic monomer units. Since the polyfunctional vinylic monomer unit is contained in an amount of 5 mass % or more, a hollow structure can be easily formed. On the other hand, the amount of the polyfunctional vinylic monomer unit is preferably 50 mass % or leas, and more preferably 48 mass % or less, in 100 mass % of the entire vinylic monomer unite. Since the amount of the polyfunctional vinylic monomer unit is 50 mass % or less, the shrinkage of the surface of the obtained hollow polymer particles is small, and the strength is increased.
The phosphate ester monomer unit is preferably an acidic phosphate ester monomer unit, because it easily orients on the droplet surface and acts with the inorganic dispersant to increase the hardness near the particle surface during suspension polymerisation.
The acidic phosphate ester monomer unit is preferably an acidic phosphate ester monomer having an ethylenically unsafe rated group, because the particle hardness can be increased toy copolymerization with the vinylic monomer near the droplet surface during suspension polymerisation.
More specific examples of the acidic phosphate ester monomer having an ethylenically unsaturated group include one having a structural formula represented by the following formula (1):
therein R1 is a (meth)acrylic group or an allyl group, R2 is a linear or branched alkylene group, m is an integer of 1 to 30, n is 0 or 1, v is an integer of 1 to 10, and x is 1 or 2.
Even more specific examples include caprolactone EO-modified dimethacrylate phosphate represented by the following formula (2) (product name: KAYAMER PM-21, produced by Nippon Kayaku Co., Ltd.), polyoxypropylene allyl ether phosphate ester represented, by the following formula (3) (product name: Adekaria Soap PP-70, produced by ADEKA Corporation), and 2-methacryloyloxyethyl acid phosphate,
wherein a and b satisfy a=1 and b=2, or a=2 and b=1.
wherein p is ah integer of 1 to 30, and q is 1 or 2.
The amount of the phosphate ester monomer unit is preferably 0.01 parts by mass or mere, and more preferably 0.05 parts by mass or more, based on 100 parts by mass of the vinylic monomer unit. When the monomer unit having a phosphate ester moiety as a main skeleton is contained in an amount of 0.01 parts by mass or more based on 100 parts by mass of the vinylic monomer unit, there is an advantage that a hollow structure can be formed. On the other hand, the amount of the phosphate ester monomer unit is preferably 1 part by mass or less, and more preferably 0.8 parts by mass or less, based on 100 parts by mass of the vinylic monomer unit. When the amount of the phosphate ester monomer unit is 1 part by mass or less based on 100 parts by mass of the vinylic monomer unit, there is an advantage that the resulting hollow polymer particles can easily maintain a substantially spherical shape. It is preferable that the phosphate ester monomer unit is copolymerized with the vinylic monomer unit, because high-strength hollow polymer particles can be obtained.
In addition, the hollow polymer particles may suitably contain, if necessary, one or more of various components, such as pigments, antioxidants, flavoring agents, ultraviolet protective agents, surfactants, preservatives, and medicinal ingredients.
Further, the present invention includes an invention, relating to hollow polymer particles comprising a polymer containing a vinylic monomer unit, the hollow polymer particles having a phosphorus element content of 2 to 200 mg/kg and an alkaline earth metal element content of 1 to 100 mg/kg, wherein the phosphorus element content is larger than, the alkaline earth metal element content, and the hollow polymer particles having a volume average particle diameter of 0.5 to 1000 μm.
The site and shape of the hollow polymer particles of the second invention ere the sense as those described in the first invention. Further, the vinylic monomer unit is also the sere as that described in the first invention.
In the hollow polymer particles of the second invention, the phosphorus element content is larger than the alkaline earth metal content. The contents of these elements can be measured by any elemental analysis. For example, the contents can be measured by high-frequency inductively coupled plasma emission spectroscopy (ICP emission spectroscopy).
The phosphorus element content of the hollow polymer particles is 2 mg/kg or more, and preferably 5 mg/kg or more. It the phosphorus element content is less than 2 mg/kg, a hollow structure is less likely to be formed in the hollow polymer particles. On the other hand, the phosphorus element content, of the hollow polymer particles is 200 mg/kg or less, and preferably 100 mg/kg or less. If the phosphorus element content exceeds 200 mg/kg, the mechanical strength of the hollow polymer particles becomes insufficient.
The alkaline earth metal element content of the hollow polymer particles is 1 mg/kg or more, and preferably 3 mg/kg or more. In the second invention, the interaction between the phosphorus element and the alkaline earth metal, element forms a dense coating on the surface layer of the hollow polymer particles, and significantly improves the mechanical strength of the hollow polymer particles. Therefore, if the alkaline earth metal element content of the hollow polymer particles is less than 1 mg/kg, such a coating is not sufficiently ferried, and the mechanical strength of the hollow polymer particles becomes insufficient. On the other hand, the alkaline earth metal element, content of the hollow polymer particles is 100 mg/kg or less, and preferably 80 mg/kg or leas. If the alkaline earth metal element content exceeds 100 mg/kg, the dispersion stability of the hollow polymer particles in a coating film deteriorates when the coating film is formed, and the scratch resistance of a film deteriorates when the film is formed,
The type of alkaline earth metal element contained in the hollow polymer particles is not particularly limited. However, magnesium or calcium is preferable.
The hollow polymer particles may contain a phosphate ester monomer unit. For example, it is preferable that the hollow polymer particles comprise a polymer containing a vinylic monomer unit and a phosphate ester monomer unit described above. Examples of the phosphate ester monomer unit include those described in the first invention.
The specific surface area and bulk specific gravity of the hollow polymer particles are the same as those of the first invention.
As in the first invention, the hollow polymer particles may suitably contain, if necessary, one or more of various components, such as pigments, antioxidants, flavoring agents, ultraviolet protective agents, surfactants, preservatives, and medicinal ingredients.
The hollow polymer particles of the first and second inventions have excellent mechanical strength, and can be preferably used for resin compositions, coating compositions, cosmetics, light diffusion films, and the like. Resins formed from resin compositions obtained by using the hollow polymer particles of the present invention, coating films formed from coating compositions obtained by using the hollow polymer particles of the present invention, and light diffusion flirts obtained by using the hollow polymer particles of the present invention have a remarkable effect of being excellent in scratch resistance.
In addition, the present invention includes an invention relating to a method for producing hollow polymer particles. The method for producing hollow polymer particles of the present invention is characterized in that the method comprises subjecting a mixture of a non-polymerizable organic compound and a polymerisable monomer to suspension polymerization, and that the polymerizable monomer contains a polymerisable monomer unit having a phosphate ester moiety in an amount of 0.01 to 1 part by mass based on 100 parts by mass of a vinylic monomer unit.
The vinylic monomer unit and the monomer unit having a phosphate ester moiety as a main skeleton can be: the same as those described above.
The mixture of a vinylic monomer unit and a polymerizable monomer unit having a phosphate ester moiety is subjected, to suspension polymerisation in the presence of a non-polymerizable organic compound.
The non-polymerizable organic compound functions as a so-called solvent and also contributes to the formation of a hollow structure or porous structure inside the hollow polymer particles.
As such a non-polymerizable organic compound, it is preferable to use an organic solvent having a boiling point of 30° C. or higher and 200° C. or lower because it exists as a liquid in the temperature range in which the polymerization step is carried out. More specific usable examples include one or more members selected from the group consisting of saturated aliphatic hydrocarbons, such as n-pentane, isopentane, n-hexane, cyclohexane, and n-heptane; aromatic compounds, such as toluene and benzene; acetate compounds, such as ethyl acetate and butyl acetate; and fluorine compounds, such as hydrofluoroether and hydrofluorocarbon.
The amount of the non-polymerizable organic compound used is preferably 10 to 250 parts by mass based on 100 parts by mass of the mixture of a vinylic monomer unit and a polymerisable monomer unit having a phosphate ester moiety. When the amount of the non-polymerizable organic compound is 10 parts by mass or more, a hollow structure or a porous structure can be more reliably formed inside the hollow polymer particles. On the other hand, when the amount of the non-polymerisable organic compound is 250 parts by mass ox less, sufficient strength of the obtained hollow polymer particles can be ensured.
It is also preferable to use a radical polymerisation initiator to accelerate the polymerisation reaction of the monomer units used. The radical, polymerisation initiator is not particularly limited, and known radical polymerisation initiators can be widely used.
More specific examples of the radical polymerisation initiator include oil-soluble azo compounds, such as 2,2′-azobis 2,4-dimethylvaleronitrile and 2,2′-azobisisobutyronitrile; and oil-soluble peroxides, snob as benzoyl peroxide, lauroyl peroxide, octanoyl peroxide, methyl ethyl ketone peroxide, propyl peroxydicarbonate, cumene hydroperoxide, and t-butyl hydroperoxide.
these polymerization initiators can be used singly or in combination of two or more. The amount of the radical polymerisation initiator added is preferably 0.01 to 10 parts by mess, and store preferably 0.01 to 5 parts by mass, baaed on 100 parts by mass of the polymerisable monomer, because the polymerization of the polymerization monomer can be smoothly initiated.
In addition, it is also preferable to add, to the suspension, one or more members selected from the group consisting of dispersants, dispersion aids, surfactants, pH adjusters, water-soluble polymerisation inhibitors, and antioxidants, if necessary.
The dispersant is not particularly limited, and known dispersants can foe widely used. However, it is preferable to use an inorganic dispersant because high-strength hollow polymer particles can be obtained. More specific usable examples include water-insoluble salts, such as magnesium pyrophosphate, calcium carbonate, tricalcium phosphate, and barium carbonate; inorganic dispersants, such as silica and zirconium oxide; inorganic polymer substances, such as talc, bentonite, silicic acid, diatomaceous earth, and clay; and the like. These can foe used singly or in combination of two or more.
Among the above, when using a pyrophosphate or phosphate of an alkaline earth metal as the dispersant, the metal ions internet with the phosphate ester moiety in the phosphate ester monomer to form a dense coating on the surface layer. As a result, high-strength hollow polymer particles can be obtained. Further, magnesium or calcium car: be preferably adopted as the alkaline earth metal.
The amount of the dispersant added is preferably 0.1 to 5 mass %, and rote preferably 0.5 to 3 mass %, in 100 mass % of the total amount of the polymerisable monomer because the stability of the oil droplets of the polymerisable monomer solution is ensured, and hollow polymer particles with a uniform particle diameter can foe obtained.
Moreover, in order to obtain hollow polymer particles with a lucre uniform particle diameter, suspension polymerization may be performed by dispersing the droplets, for example, using a high-pressure disperser, such as a microfluidizer or a nanomizer, which utilizes the collision between the droplets or the collision force with the machine wall.
The polymerization temperature is preferably in the range of 50 to 105° C. The time for maintaining this polymerisation temperature is preferably in the range of 0.1 to 20 hours, fitter completion, of the polymerization, a suspension containing hollow polymer particles containing a non-polymerizable organic compound therein are obtained. This suspension is distilled to remove the non-polymerisable organic compound. Further, after the dispersion stabilizer in the suspension is dissolved with an acid, or the like and removed, the hollow polymer particles are preferably separated by filtration to remove the aqueous medium, washed with water of a solvent, and then dried to isolate the hollow polymer particles. Alternatively, after completion of the polymerization, the non-polymerizable organic compound can be removed, without distilling the suspension, by removing the dispersion stabilizer, followed by washing and then drying, thereby isolating the hollow polymer particles. Since the thus-obtained, hollow polymer particles of the present invention have high mechanical strength, they can be suitably used as particles for light diffusing agents for optical films, optical sheets, and lighting covers, matting agents for paints, inks, etc., heat insulating agents for paints and sheets, and lightening agents for resins and bolded products.
Although, the embodiments of the present invention are described above, the present, invention is not limited to these examples, heedless to say, the present invention can be implemented in various forms without departing from the gist of the present invention.
The embodiments of the present invention are described in more detail below based on Examples; however, the present invention is not limited thereto.
The hollow polymer particles were measured by the Coulter method as described below.
The volume average particle diameter of the hollow polymer particles is measured with a Coulter Multisizer™ 3 (analyser produced by Beckman. Coulter). The measurement is carried out using an aperture calibrated according to the Multisizer™ 3 user's manual, published by Beckman Coulter.
The aperture used for measurement is suitably selected depending on the size of the hollow polymer particles to be measured. The current (aperture current) and gain are suitably set depending on the size of the selected aperture, her example, when an aperture having a size of 50 μm is selected, the current (aperture current) is set to be −800, and the gain is set to be 4. The measurement sample used is a dispersion obtained by dispersion 0.1 g of hollow polymer particles in 10 ml of a 0.1 wt % nonionic surfactant aqueous solution using a touch mixer (Touch Mixer MT-31, produced by Yamato Scientific Co., Ltd.) and an ultrasonic cleaner (Ultrasonic Cleaner VS-150, produced by Velvo-Clear Co.). During measurement, gentle stirring is performed to an extent in which bubbles are not formed in the beaker. The measurement is ended when the measurement of 100000 hollow polymer particles is completed. The volume average particle diameter of the hollow polymer particles is the arithmetic mean in the particle site distribution on a volume basis of 100000 particles.
The specific surface area of the hollow polymer particles was measured according to the BET method (nitrogen adsorption method) described in ISO 9277, 1st edition, JIS Z 8830:2001. For the target hollow polymer particles, the BET nitrogen adsorption isotherm was measured using an automated surface area end porosity analyser (TriStar XT, produced by Shimadzu Corporation). The specific surface area was calculated from the amount of nitrogen adsorbed using the BET multipoint method.
After pretreatment by heating gas purging, nitrogen, was used as an adsorbate, and the measurement was carried out using the constant volume method under conditions in which the cross-sectional area of the adsorbate was 0.162 nm2. Specifically, the pretreatment was carried out by performing a nitrogen purge for 20 minutes while heating a container containing resin particles at 65° C., allowing the container to cool at room temperature, and then performing vacuum degassing until the pressure inside the container was 0.05 mmHg or less while heating the container at 65° C.
The bulk specific gravity of the hollow polymer particles was measured according to JIS K5101-12-1 (Test methods for pigments—Part 12: Apparent density or apparent specific volume—Section 1: Loose packing method).
105 parts by mass of methyl methacrylate, 45 parts by mass of trimethylolpropane trimethacrylate, 0.3 parts by mass KAYMER™ PM-21. (produced by Nippon Kayaku Co., Ltd.) as a polymerizable monomer having an acidic phosphate ester group, 0.45 parts by mass of AVN (produced by Japan Finechem Company, Inc.) as a polymerisation initiator, and 75 parts by mass of ethyl acetate and 75 parts by mass of cyclohexane as non-polymerizable organic compounds were mixed to prepare an oil phase. Further, 900 parts by mass of deionised water as an aqueous medium, and 23 parts by mass of magnesium pyrophosphate produced fey the metathesis method as a dispersant were mixed to prepare an aqueous phase.
Next, the oil phase was dispersed in the aqueous phase using a TK homomixer (produced by RRIMIX Corporation) at 8000 rpm for 5 minutes to obtain a dispersion (about 8 μm). Then, the dispersion was placed in a polymerizes equipped with a stirrer and a thermometer, the internal temperature of the polymerizer was raised to 55%, and the suspension was continuously stirred for 5 hours. Thereafter, the infernal temperature of the polymerizer was raised to 70° C. (secondary temperature rise), and the suspension was stirred at 70% for 2 hours. Thus, the suspension polymerization reaction was completed.
After cooling the suspension, the dispersant (magnesium pyrophosphate) contained in the suspension was decomposed with hydrochloric acid. Then, the suspension was dehydrated by filtration to separate solids, and the solids were washed with sufficient water. Thereafter, the non-polymerizable organic compounds were removed by vacuum-drying at 70% for 24 hours, thereby obtaining spherical polymer particles. The average particle diameter of the obtained polymer particles was 8.0 μm. According to SEM observation, the obtained polymer particles had a porous shape inside. The bulk specific gravity was 0.33 g/ml. Further, the specific surface area of the obtained particles measured before and after treatment with a jet mill at a pressure of 0.4 MPa was 8.2 m2/g and 23.2 m2/g, respectively.
Polymer particles were obtained in the same manner as in Example 1, except that 54 parts by mass of styrene, 36 parts by mass of ethylene glycol dimethacrylate, 105 parts by mass of cyclohexane, and 105 parts by mass of ethyl acetate were used.
Polymer particles were obtained in the same manner as in Example 1, except that 135 parts by mass or methyl methacrylate and 15 parts by mass of trimethylolpropane trimethacrylate were used.
Polymer particles were obtained in the same manner as in Example 1, except that 105 parts by mass of isobutyl methacrylate and 45 parts by mass of ethylene glycol dimethacrylate were used.
Polymer particles were obtained in the same manner as in Example 1, except that 105 parts by mass of styrene, 45 parts by mass of trimethylolpropane trimethacrylate, and 0.8 parts by mass of Adekaria Soap PP-70 (produced by ADERA Corporation) as a polymerizable monomer having an acidic phosphate ester group were used.
Polymer particles were obtained in the same manner as in Example 1, except that 150 parts by mass of cyclohexane was used as a non-polymerizable organic compound. The obtained particles had only one pore inside.
When the prepared oil phase was dispersed in the aqueous phase in Example 1, the rotation speed of the TK homomixer was changed to 2500 rpm, and a dispersion (about 35 μm) was obtained. The subsequent polymerisation step and ether steps were performed in the same manner as in Example 1, thereby obtaining polymer particles.
65 parts by mass of methyl methacrylate, 05 parts by mass of ethylene glycol dimethacrylate, 0-3 parts by mass of KAYAMER™ PM-21 as a polymerisable monomer having an acidic, phosphate ester group, 0.75 parts by mass of AVN as a polymerisation initiator, and 75 parts by mass of ethyl acetate and 75 parts by mass of cyclohexane as non-polymerizable organic compounds were mixed to prepare an oil phase, further, 900 parts by mass of deionised water as an aqueous medium, and 30 parts by mass or tricalcium phosphate as a dispersant were mixed to prepare an aqueous phase.
Polymer particles were obtained in the same manner as in Example 1, except for the above. The average particle diameter of the obtained polymer particles was 3-0 μm. According to SEM observation, the obtained polymer particles had a porous shape inside. The fault specific gravity was 0.32 g/ml. Further, the specific surface area of the obtained particles measured before and after treatment with a jet mill at a pressure of 0.4 MPa was 7.2 m2/g and 10.2 m2/g, respectively.
Polymer particles were obtained in the same manner as in Example 1, except that KAYMER PM-21 was not used as a polymerizable monomer having an acidic phosphate ester group. The obtained particles were porous particles.
105 parts by mass of styrene, 15 parts by mass of trimethylolpropane trimethacrylate, 1.5 parts by mass of AVN (produced by Japan Finechem Company, Inc.) as an oil-soluble polymerization initiator, and 150 parts by mass of cyclohexane as a non-polymerizable organic compound were mixed to prepare an oil phase. Further, 500 parts by mass of deionized water as an aqueous medium, 1 part by mass of sodium lauryl sulfate as a surfactant, and 2.3 parts by mass of VA-057 (produced by Wake Pure Chemical Industries, Ltd.) as a water-soluble polymerization initiator were raised to prepare an aqueous phase.
Hunt, the oil phase was dispersed in the aqueous phase using a TK homomixer (produced by PRIMIX Corporation) at 8000 rpm for 5 minutes to obtain a dispersion (about 8 μm). Then, the dispersion was placed in a polymerizable equipped with a stirrer and a thermometer, the internal temperature of the polymerizer was raised to 60° C., and the suspension was continuously stirred for 5 hours. Thereafter, the internal temperature of the polymerizer was raised to 70° C. (secondary temperature rise), and IQ the suspension was stirred at 70% for 2 hours. Thus, the suspension polymerization reaction was completed.
After cooling the suspension, the suspension was dehydrated by filtration to separate solids, and the solids were washed with sufficient water. Then, the non-polymerizable organic compound was removed by vacuum-drying at 70% for 24 hours, thereby obtaining polymer particles. The average particle diameter of the obtained polymer particles was 8.0 μm. According to SEM observation, the obtained polymer particles had a porous shape inside.
The obtained hollow polymer particles of the Examples and Comparative Examples were passed through a jet mill (Current Jet CJ-10, produced by Nisshin Engineering Inc.) at a pressure of 0.4 MPa with a feeding rate of 5 g/min.
The phosphorus element content and the alkaline earth metal element content were measured with a multitype ICP emission spectrometer (ICPE-9000, produced by Shimadzu Corporation). 1.0 g of hollow polymer particles was accurately weighed and heated at 450° C. for 3 hours with an electric furnace (STR-15K muffle furnace, produced by Isuzu) to be ashed. The ashed hollow polymer particles were dissolved in 2 ml of concentrated hydrochloric acid, and distilled water was added to take a total volume of 50 ml, thereby obtaining a measurement sample. Then, the measurement sample was measured with the multitype ICF emission spectrometer under the following measurement conditions to obtain peak intensities at wavelengths of elements (Na, Ca, Mg, Fe, Cr, and P). Subsequently, the concentrations (μg/ml) of the elements (Na, Ca, Mg, Fe, Cr, and P) in the measurement sample were calculated from the obtained peak intensities at the wavelengths of the elements (Na, Ca, Ca, Mg, Fe, Cr, and P) based on a calibration curve for quantification prepared by the method for preparing a calibration curve described below. The concentration Tc (μg/ml) of each element (Na, Ca, Mg, Fe, Cr, and P) and the weight W (g) of the weighed hollow polymer particles were substituted into the following equation to calculate the element content in the hollow polymer particles.
Element content=(Tc(μg/ml)/W(g))×50 (ml)
Measurement wavelength: Na (589.592 m), Ca (317.933 nm), Mg (285.213 nm), Fe (238.204 ran), Cr (205.552 nm), P (177.499 nm)
Viewing direction: axial direction
Radio frequency output: 1.20 kW
Carrier flow rate: 0.7 L/min
Plasma flow rate: 10.0 L/min
Auxiliary flow rate: 0.6 L/min
Exposure time: 30 seconds
A standard solution for a calibration curve (XSTC-13 (general-purpose mined standard, solution, mixture of 31 elements (base: 5% HNO3) each in an amount of about 10 mg/l) produced by SPEW, USA) was serially diluted with distilled water to prepare standard solutions at concentrations of 0 ppm (blank), 0.2 ppm, 1 ppm, 2.5 ppm, and 5 ppm. The standard solution at each concentration was measured with the multitype ICP emission spectrometer under the measurement conditions described above to obtain peak intensities at wavelengths of elements (Na, Ca, Mg, Fe, and Cr). The concentrations and peak intensities of the elements (Na, Ca, Mg, Fe, and Cr) were plotted to determine an approximate line (straight line or quadratic curve) by the least-squares method, and the approximate line was used as a calibration curve for quantification.
As shown in the following Table 1, the hollow polymer particles of the Comparative Examples were collapsed due to the jet mill treatment to expose the internal porous structure, and the specific surface area significantly increased compared to before the jet mill treatment. In contrast, it was confirmed that, the increase in the specific surface area of the hollow polymer particles of the Examples after the jet mill treatment tended to be suppressed.
indicates data missing or illegible when filed
7.5 parts by mass of the hollow polymer particles obtained in Example 2, 30 parts by mass of acrylic resin (product name: Acrydic A811, produced by DIO Corporation), 10 parts by mass of a cross-linking, agent (product: name: VM-D, produced by DIG Corporation), and 50 parts by mass of butyl acetate as a solvent were mined for 3 minutes using a stirring and defoaming device/and defoamed for 1 minute, thereby obtaining a light diffusion resin composition.
The resulting light diffusion resin composition was applied to a PET film with a thickness of 125 μm using a coating device with a blade with a clearance of 50 pit, followed by drying at 70° C. for 10 minutes, thereby obtaining a light diffusion film A.
A light diffusion film B was obtained in the same manner as in Example 9, except that, the hollow polymer particles obtained in Comparative Example 2 were used.
The coated surface of the obtained light diffusion films was reciprocally polished with a cloth 20 times using a friction fastness tester, and the degree of scratches in the light diffusion films after polishing was visually observed. One without line scratches or peeling of the coating film was evaluated as ◯, and one with line scratches and peeling of the coating film was evaluated as x.
The total light transmittance of the light diffusion films was measured according to JIS K7361-1, and the hare was measured according to JIS K7136. Specifically, the total light transmittance and hate of the light diffusion films were measured using a base meter (NDH2000) commercially available from Nippon Denshoku Industries Co., Ltd.
An shown in the following Table 2, the film of Comparative Example 3 did not give favorable results in the evaluation of scratch resistance. On the other hand, the film of Example 9 gave a good evaluation result of scratch resistance,
| Number | Date | Country | Kind |
|---|---|---|---|
| 2018-172144 | Sep 2018 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2019/035960 | 9/9/2019 | WO | 00 |