Patent Application
20180050331
This relates to the field of catalysis and, more particularly, to recovery of homogeneous catalysts.
Homogeneous catalysts are used to catalyze many different chemical reactions and are invaluable tools in organic synthesis. But a major problem with homogeneous catalysts is that they are soluble in the reaction solution. Because they are soluble, they are difficult to recover from the solution after the reaction is completed. Much research has been devoted to recovering spent homogeneous catalysts, but the conventional catalysts and their associated recovery techniques have their drawbacks.
This disclosure describes homogeneous catalysts that are recoverable from solution by forming a host-guest compound in the solution. The host portion of the host-guest compound binds to the soluble catalyst, allowing the catalyst to be isolated from the solution.
An exemplary method for separating a homogeneous catalyst from a solution includes forming a host-guest compound between a first isomer of the catalyst and inclusion compound in the solution and isolating the host-guest compound from the solution. The catalyst may be released from the inclusion compound by converting the first isomer of the catalyst to a second isomer of the catalyst.
An exemplary method of performing a catalyzed chemical reaction includes catalyzing a chemical reaction in a solution using a homogeneous catalyst and adding an inclusion compound to the solution. The inclusion compound binds a first isomer of the catalyst to form a host-guest compound including the inclusion compound and first isomer of the catalyst. The host-guest compound is isolated from the solution and the catalyst is released from the inclusion compound by converting the first isomer of the catalyst to a second isomer of the catalyst.
These methods may include the following additional features.
The first isomer may be a cis or trans isomer and the second isomer is the other of a cis or trans isomer.
The catalyst may include a transition metal and an N-heterocyclic carbene moiety bonded to an azobenzene functional group.
The inclusion compound may be a cyclodextrin.
The inclusion compound may be a cyclodextrin attached to a surface of a substrate.
Converting the first isomer of the catalyst to a second isomer of the catalyst may include applying electromagnetic radiation.
The solution may be an olefin metathesis reaction solution.
An example of a homogeneous catalyst that may be used in the methods includes a transition metal complex having an N-heterocyclic carbene ligand with an azobenzene functional group thereon, the azobenzene functional group is effective to undergo cis-trans isomerization. The composition may also include a cyclodextrin moiety bound to the azobenzene functional group. A silica substrate may be attached to the cyclodextrin moiety.
A homogeneous catalyst is a catalyst that is in the same phase as the reactants. Thus, in a reaction solution the homogeneous catalyst is dissolved. In contrast, a heterogeneous catalyst is a catalyst that is in a different phase than the reactants. In a reaction solution, the heterogeneous catalyst is often a solid. This disclosure relates to homogeneous catalysts and their recovery from the reaction solution.
A host-guest compound is used in the catalyst recovery process. In general, a host-guest compound includes two or more molecules held together by non-covalent intermolecular forces. The host-guest compound includes an inclusion compound that acts as the host. The inclusion compound has a cavity that receives the catalyst (the guest). The catalyst is held within the cavity by intermolecular forces to form the host-guest compound.
In an example method employing this concept a homogeneous catalyst is separated from a solution by first forming a host-guest compound between a first isomer of the catalyst and inclusion compound in the solution. The host-guest compound is then isolated from the solution. The catalyst is subsequently released from the inclusion compound by converting the first isomer of the catalyst to a second isomer of the catalyst.
Certain organic functional groups undergo isomerization changes when external energy is applied. Examples of sources of external energy include, but are not limited to, electromagnetic radiation, heat, electricity, and the like.
For example, azobenzene moieties typically convert from the cis-isomer to the trans-isomer when visible electromagnetic radiation is applied and convert back to the cis-isomer when ultraviolet electromagnetic radiation is applied.
The method takes advantage of the fact that different isomers of a compound have different binding affinity for inclusion compounds. The trans-isomer of azobenzene, for example, forms a host-guest compound with Beta-cyclodextrin (BCD), whereas the cis-isomer does not. This different binding affinity permits the catalyst to bind to the inclusion compound for removal from solution, and then be released from the inclusion compound for reuse.
The process of forming the host-guest compound between the first isomer of the catalyst occurs in the solution. The kinetics of the formation reaction will vary based on the chemical nature of the inclusion compound and catalyst chosen. Accordingly, an external stimulus such as heat, stirring, ultrasound, or the like may increase the rate of formation of the host-guest compound. If necessary, external energy may be applied to the solution to ensure the catalyst is in its first isomer form.
Once formed, the host-guest compound may be insoluble in the solution, which causes it to precipitate. The precipitate may be separated from the solution using conventional solid-liquid separation technique such as filtration, centrifugation, or the like.
The catalyst may be released from the inclusion compound by converting the catalyst to a second isomer that does not have a binding affinity for the inclusion compound. When the catalyst converts to the second isomer, the intermolecular host-guest interaction diminishes and the catalyst and inclusion compound can be separated. The catalyst may be converted to the second isomer by applying external energy to the catalyst sufficient to cause the isomerization change.
The catalyst may be used to catalyze a chemical reaction, and then separated from the chemical reaction solution. In such a case, the catalyst is combined with the reactant(s) in the solution and the reaction is allowed to proceed. At the desired time after the reaction proceeds, the inclusion compound is added to the solution. The inclusion compound and catalyst form the host-guest compound. The host-guest compound is then isolated from the solution and the catalyst is released from the inclusion compound as discussed above.
The catalyst is particularly useful for catalyzing metathesis reactions, Suzuki-Miyaura Coupling, Buchwald-Hartwig Aminations, Negishi Reactions, Hiyama Coupling, Kumada Coupling, Sonogashira Coupling, Heck Reaction, Hydrosilylation, Allene Formation, 1,4-Reduction, Conjugate Addition, Hydrothiolation, Hydroalkoxylation, Hydroamination, Carboxylation & Carbonylation (via Boronic Acids and CH Activation), CO2 Insertion, [3+2] Cycloaddition Reaction (Formation of Triazole), Allylic Substitution, other organo-catalytic reactions, among many others. Accordingly, the chemical reaction solution contains the reactant(s) associated with the reaction being catalyzed and, after the reaction proceeds, the chemical reaction solution will contain the reaction product(s).
The catalyst may be an organic or organometallic compound having an N-heterocyclic carbene moiety and an azobenzene moiety. The azobenzene moiety is capable of undergoing cis-trans isomerization in response to a stimulus having sufficient energy to cause the cis-trans isomerization.
The azobenzene moiety may be azobenzene itself or a functionalized azobenzene. A functionalized azobenzene includes an azobenzene backbone, but relative to azobenzene, the phenyl groups include one or more appended functional groups, such as, for example, alkanes, alkenes, alkynes, aldehydes, ketones, ethers, esters, alkoxys, and/or carboxylic acids.
The organometallic compound has a transition metal bonded to the N-heterocyclic carbene moiety and azobenzene moiety. The transition metal may be a transition metal that functions as a catalyst. Examples of such transition metals include Ru, Pd, Ni, Cu, Fe, Ag, Au, Rh, Ir, Ni, Pd, and Cu among others.
A particular example of the catalyst has the formula shown below.
In this formula, R represents the position of the azobenzene functional group. Compound 4 shown in
The inclusion compound may be any conventional inclusion compound used in host-guest chemistry, such as, for example, cyclodextrins, porphyrins, calixarenes, cucurbiturils, and crown ethers among others.
In certain examples a cyclodextrin is used as the inclusion compound and with catalyst having azobenzene-based functional groups. When the azobenzene-based functional groups are in the cis-isomer configuration, the catalyst does not interact with the inclusion compound sufficiently enough to hold the catalyst within the cavity. However, when the azobenzene-based functional groups are in the trans-isomer configuration, the inclusion compound holds the catalyst within the cavity, forming the host-guest compound. The external energy stimulus can be used to cause the azobenzene-based functional groups to convert between the cis- and trans-isomers, which modulates the catalyst's interaction with the cyclodextrin inclusion compound.
Cyclodextrins are oligosaccharides including a plurality of sugar molecules linked together to form a ring. Examples include, but are not limited to alpha-cyclodextrin, beta-cyclodextrin, and gamma-cyclodextrin. The cyclodextrin backbone may be functionalized as desired to modify its properties. For example, it may be modified with functional groups that modify the interaction with a particular catalyst.
The inclusion compound may be functionalized in such a way that it binds to a solid substrate surface such as a metal surface, a magnetic surface, a silica surface or the like. By attaching the inclusion compound to a surface, the inclusion compound becomes immobilized, which may make removing the inclusion compound from solution easier.
In a particular example, the substrate is silica such as activated silica. The surface of the silica may be functionalized with an isothiocyanate. The isothiocyanate portion acts as a bonding point for amines. Accordingly, if the inclusion compound is functionalized with a terminal amine group, it can be attached to the silica via the isothiocyanate group.
Silica is a porous material and may be used in particle form. Examples of sizes of silica particles include 50 to 300 mesh, 60 to 270 mesh, or 70 to 230 mesh. Examples of pore sizes include 10 to 200 Å, 30 to 150 Å, 20 to 80 Å, or about 60 Å.
This section discusses particular examples of the composition and methods for illustrative purposes. The scope of the claims is not limited to the details discussed in this section.
Substitution under high-temperature conditions with 2,4,6-trimethylaniline, followed by workup, resulted in a diamine (Compound 8). The treatment of the resulting diamine with triethyl orthoformate and ammonium tetrafluoroborate resulted in the precipitation of the cyclized NHC precursor salt (Compound 9).
An indirect route toward the catalyst was ultimately successful involving the formation of an intermediate chloroform adduct (Compound 10) under basic conditions. Thermolysis of the chloroform adduct in the presence of the Hoveyda-Grubbs' first generation catalyst (Compound 1) resulted in the formation of Compound 4, which was isolated as a green/yellow band on a silica gel column.
Additional details of these steps follow.
Synthesis of Compound 6.
A 100 mL round-bottom flask was charged with 4-phenylazophenol (2 g, 10.1 mmol, 1 equiv.) and potassium tert-butoxide (1.19 g, 10.6 mmol, 1.05 equiv.). These reagents were stirred together mechanically for 15 minutes prior to dissolution in anhydrous DMF (24 mL, 0.42 M). Once the solids had been dissolved, the reaction vessel was charged with 5-bromo-1-pentene (1.26 mL, 10.6 mmol, 1.05 equiv.) and the deep red reaction mixture was heated to 120° C. for 1 hour.
Upon completion of the reaction by TLC, the orange reaction mixture was diluted with water and extracted with hexanes several times. The combined organic layers were washed with water and brine, then dried over MgSO4 and concentrated under reduced pressure. The resulting residue was adsorbed to silica gel and purified by column chromatography (100% hexanes to 9:1 hexanes:EtOAc) to yield 1.08 grams of the desired material as a bright orange solid. (4.05 mmol, 81% yield)
Synthesis of Compound 7.
Compound 6 (1.5 g, 5.6 mmol, 1 equiv.) and DMSO (480 μL, 6.8 mmol, 1.2 equiv.) were charged to a 100 mL round-bottom flask and dissolved in ethyl acetate (23 mL, 0.25 M), with no special precautions taken toward air or moisture. Once heated to 60° C., the reaction vessel was charged with 48% aq. HBr (1.52 mL, 13.5 mmol, 2.4 equiv.) in one portion. The reaction was stirred at 60° C. for 30 minutes before being cooled to room temperature and concentrated under reduced pressure.
The resulting solid was redissolved in DCM and adsorbed to silica gel by gentle rotary evaporation, then purified by column chromatography (100% hexanes to 9:1 hexanes:EtOAc) to yield 2.17 grams of the desired product as a bright orange solid. (5.09 mmol, 94% yield).
Synthesis of Compound 8.
A 100 mL round-bottom flask was charged with Compound 7 (9 g, 21.2 mmol, 1 equiv.) and freshly-distilled 2,4,6-trimethylanilne (30 mL, 211 mmol, 10 equiv.). The reaction vessel was fitted with a Vigreux column and stirred at 120° C. for 48 hours. The crude reaction mixture was then charged with 2 M NaOH (50 mL) and DCM (50 mL) and stirred for 30 minutes. The reaction was then extracted with DCM several times, and the combined organic layers were washed with water and brine, then dried over MgSO4 and concentrated under reduced pressure.
The resulting black, tar-like material was vacuum distilled to remove excess 2,4,6-trimethylaniline (90° C. at 0.35 Torr) from the reaction mixture into the distillation flask. The crude product, without 2,4,6-trimethylaniline, was collected from the original flask and purified by column chromatography (20:1 to 9:1 Hexanes:EtOAc) to yield 8.6 grams of the desired material as a red oil. (16.1 mmol, 76% yield).
Synthesis of Compound 9.
A 250 mL round-bottom flask was charged with Compound 8 (5.2 g, 9.7 mmol, 1 equiv.), ammonium tetrafluoroborate (1.22 g, 11.7 mmol, 1.2 equiv.) and triethyl orthoformate (54 mL, 0.18 M). The reaction vessel was fitted with a Vigreux column and placed in an oil bath so that only the very bottom of the flask came into contact with the oil (allowing for recrystallization of the product during formation). The reaction was then stirred with heating to 120° C. The formation of orange solid after 1 hour is indicative of a successful reaction, and the reaction mixture was stirred for a further 3 hours at 120° C.
After cooling to room temperature the reaction was diluted with an excess of diethyl ether and the heterogeneous slurry was vacuum filtered to give 4.39 grams of the desired product as an orange/yellow solid. (6.94 mmol, 78% yield).
Synthesis of Compound 10.
A 250 mL Schlenk flask was charged with sodium hydroxide (2.53 g, 63.2 mmol, 40 equiv.) that had been ground to a fine powder via mortar and pestle immediately before addition. This was suspended in dry and degassed toluene (79 mL, 0.02 M) and stirred vigorously for 5 minutes before the reaction vessel was charged with dry chloroform (510 μL, 6.32 mmol, 4 equiv.). This suspension was stirred for 10 minutes before adding Compound 9 (1 g, 1.58 mmol, 1 equiv.) in one portion. The reaction was stirred vigorously at room temperature for 75 minutes.
The reaction was filtered to remove excess salts, and the orange solution was concentrated under reduced pressure to remove toluene. The resulting residue was purified by flash chromatography (9:1 Hexanes:EtOAc, dried prior to use) to yield 743 mg of the desired product as a yellow/orange solid after drying. (1.12 mmol, 71% yield) The product was found to be stable as a dry solid on the benchtop for several days.
Synthesis of Compound 4.
A 25 mL Schlenk flask under light nitrogen flow was charged with NHC—CHCl3 Compound 10 (442 mg, 0.67 mmol, 2 equiv.), Hoveyda-Grubbs 1st generation catalyst (200 mg, 0.299 mmol, 1 equiv.), and anhydrous toluene which had been degassed under nitrogen flow for 15 minutes (17 mL, 0.02M). This reaction mixture was heated with stirring to 80° C. for 75 minutes, after which time it was cooled to room temperature and the solvent was removed under reduced pressure.
The crude product was purified by silica gel chromatography, no special precautions were required regarding silica gel or solvent purity (9:1 to 7:3 hexanes:EtOAc, desired product appears as a dark green band following yellow and brown bands). The collected fractions were concentrated to yield 168 mg of the desired product as a dark yellow-green solid (0.194 mmol, 65% yield).
Reductive amination of this compound resulted in a monoamino-BCD compound that was insoluble in common metathesis solvents, requiring a different method to be adopted. To this end, Compound 14 was permethylated (PM) to yield the monoazido-PM-BCD Compound 14 in good yield after purification by column chromatography.
A Staudinger reaction with Compound 14 yielded a monoamino-PM-BCD (Compound 15). The treatment of Compound 15 with activated silica that had been previously functionalized with isothiocyano groups resulted in the desired host complex (Compound 18), joining cyclodextrin to the silica support via a thiourea linkage.
Additional details of these steps follow.
Synthesis of 1-(p-Toluenesulfonyl)imidazole.
A 1 L, 3-necked round-bottom flask was fitted with a nitrogen inlet adapter, a pressure-equalizing addition funnel, a thermometer, and a stir bar. This flask was charged with imidazole (65 g, 954.7 mmol, 2.2 equiv.) in 250 mL dry dichloromethane and cooled to 0° C. The addition funnel was charged with a solution of p-toluenesulfonyl chloride (80 g, 419.6 mmol, 1 equiv.) in another 250 mL dry dichloromethane (0.84 M in total DCM). This solution was added dropwise at 0° C. over 1.5 hours, then warmed to room temperature and stirred for a further 2.5 hours.
The reaction was filtered through a pad of silica with 500 mL of a 1:1 hexanes:EtOAc solution. The filtrate was concentrated under reduced pressure to give an off-white solid which was dissolved in 50 mL of ethyl acetate then crashed out into 500 mL of hexanes. The desired product was collected by filtration as a white, crystalline solid. (79 g, 0.3556 mol, 85% yield).
Synthesis of Compound 12.
A 1 L round-bottom flask, with no special precaution against air or moisture, was charged with 13-cyclodextrin (20 g, 17.6 mmol, 1 equiv.) and 450 mL deionized water. The mixture was heated at 60° C. with vigorous stirring until the solution became clear, then cooled to room temperature. 1-(p-Toluenesulfonyl)imidazole (15.7 g, 70.5 mmol, 4 equiv.) was ground to a fine powder by mortar and pestle before adding to the clear reaction solution all at once. The reaction was stirred for 2.5 hours at room temperature.
After the required time, the reaction mixture was charged with a solution of sodium hydroxide (9 g in 25 mL water, cooled completely to room temperature before addition) over 10 minutes via addition funnel. This reaction mixture was stirred for no more than 15 minutes after addition of base before being filtered through a glass frit to remove unreacted imidazole reagent. The filtrate was quenched by the addition of 24.1 g of ammonium chloride, which was allowed to completely dissolve before continuing.
The reaction mixture was concentrated by blowing a gentle stream of air over the flask overnight. The desired product began to precipitate almost immediately. The following morning, the reaction volume had been reduced by half and the solid product was collected by vacuum filtration and washed twice with 100 mL ice-cold water, and once with 200 mL acetone.
The collected product contained a large amount of hydrolyzed impurity which was inseparable from the desired product and therefore carried on into the next reaction where it could be easily removed. Yield is approximately 45%. Characterization data match previously-reported data.
Synthesis of Compound 13.
Sodium azide (2.81 g, 43.2 mmol, 5 equiv.) was added to a solution of Compound 12 (mono-(6-p-toluenesulfonyl-6-deoxy)-13-cyclodextrin) (11.1 g, 8.64 mmol, 1 equiv.) in 108 mL (0.08 M) of deionized water in a 250 mL round-bottom flask, with no special precautions taken against air. This reaction mixture was stirred for 12 hours at 80° C.
The reaction mixture was then filtered through a fritted funnel while hot to remove hydrolyzed material from the previous reaction (insoluble in water), and the clear filtrate was added to 300 mL of acetone, causing a white solid to crash out of solution. This solid was collected by vacuum filtration and washed twice with 100 mL portions of acetone to yield 8.09 g of the desired product as a white powder. (6.97 mmol, 40% yield over 2 steps from Compound 11).
Synthesis of Compound 14.
A 500 mL round-bottom flask with stir bar was charged with sodium hydride (9.50 g, 238 mmol of a 60% dispersion in mineral oil, 30 equiv.) and 156 mL dry DMF. Compound 13 (Mono-(6-azido-6-deoxy)-I3-cyclodextrin) (9.22 g, 7.9 mmol, 1 equiv.) in 100 mL dry DMF was charged to the reaction vessel dropwise at 0° C. via an addition funnel. The suspension was stirred for 1 hour while warming to room temperature. The reaction was cooled back down to 0° C. and charged with methyl iodide (12.8 mL, 207 mmol, 26 equiv.) dropwise. After addition was complete, the reaction was warmed to room temperature and stirred for 16 hours.
The reaction was then quenched by the dropwise addition of methanol, and then diluted with 100 mL water. The aqueous phase was extracted with five 50 mL portions of dichloromethane. The combined organic layers were washed with brine, then dried over magnesium sulfate, filtered, and concentrated under reduced pressure. The resulting crude product was purified by column chromatography (100% DCM to 9:1 DCM:MeOH) to yield 11 g of the desired product as a yellow oil (7.64 mmol, 96% yield).
Synthesis of Compound 15.
A 100 mL round-bottom flask was charged with Compound 14 mono-(6-azido-6-deoxy)-permethyl-13-cyclodextrin (11.4 g, 7.91 mmol, 1 equiv.), triphenylphosphine (2.29 g, 8.71 mmol, 1.1 equiv.), and acetone (20 mL, 0.4 M) and stirred at room temperature for 3 hours. Water (2 mL, 4 M) was added and the reaction heated to reflux for 1 hour.
The reaction was cooled to room temperature and acetone removed under reduced pressure. The resulting residue was taken into water, and the precipitated triphenylphosphine oxide was removed via filtration. The filtrate was extracted with DCM several times. The combined organic phases were dried over magnesium sulfate and concentrated under reduced pressure. The resulting crude product was purified by column chromatography (100% DCM to 9:1 DCM:MeOH) to yield 9.72 g of the desired product as an off-white oil which recrystallized upon standing (6.88 mmol, 87% yield).
Synthesis of Compound 16.
A 250 mL round-bottom flask was charged with 3-aminopropyltriethoxysilane (7 mL, 30 mmol, 1 equiv.) and 20 mL anhydrous THF and cooled to 0° C. in an ice-water bath. Carbon disulfide (2.7 mL, 44.8 mmol, 1.5 equiv.) was added dropwise over 20 minutes via syringe pump, and the reaction was stirred at 0° C. for 3 hours before warming to room temperature. Dicyandiamide (3.8 g, 44.8 mmol, 1.5 equiv.) was then added in one portion, along with an additional 20 mL anhydrous THF (0.75 M total) and 3 drops of triethylamine.
This mixture was heated at 40° C. for 3 hours before the volatiles were removed in vacuo. The resulting residue was extracted with diethyl ether several times, the combined organic layers were washed twice with a small amount of water, then dried and concentrated. The resulting crude product was purified by Kügelrohr distillation (120° at 1.5 Torr) to yield 3.86 g of the desired compound as a clear yellow liquid (14.7 mmol, 49% yield).
Synthesis of Compound 17.
Silica gel (70-230 mesh, 60 Å pore size, 550 m2/g) was activated by stirring in 50:50 HNO3 (70%):H2O at reflux for 24 hours. The newly activated silica was collected by vacuum filtration and washed several times with water, then methanol. The silica was then collected and dried in a vacuum oven at 100° C. overnight, and stored in an air-free environment prior to use.
Activated silica (5 g) was dispersed in toluene (50 mL) with vigorous stirring for 5 minutes before being charged with Compound 16 (3 grams, 11.4 mmol). This mixture was heated at reflux for 24 hours with gentle stirring before being cooled to room temperature. The cooled mixture was collected by filtration and washed several times with toluene before being dried in a vacuum oven at 60° C. for 16 hours. This product was carried on immediately without further purification.
Synthesis of Compound 18.
Isothiocyanate-grafted silica (17, 500 mg) was added to a solution of Compound 15 (1 g) and pyridine (minimum to dissolve, ˜2 mL). This suspension was stirred at room temperature for 48 hours.
The silica compound was collected by vacuum filtration and washed several times with water, then methanol, then finally with diethyl ether. The recovered host compound was dried in a vacuum oven at 60° C. for 16 hours, and then stored in a moisture-free environment before being subjected to FT-IR and TGA characterization methods, as detailed in the manuscript.
Characterization of Compound 18.
Referring to
The sharper peaks at 2950 cm−1 are the C—H stretching frequencies of PM-BCD. Additionally, the strong and broad peaks at approximately 1075 cm−1 in the spectra of Compound 18 and silica are assigned to Si—O stretching vibrations.
Referring to
Compound 18 showed water loss at about 3.4% before dropping in weight between 220 and 600° C. This drop in weight is due to the thermal decomposition of PM-BCD moieties. This provides direct evidence of the grafting of PM-BCD units onto the silica gel, with a concentration of 1.43×10−4 mmol PM-BCD mg−1.
Referring to
A vial containing 1 mg of Compound 4 in 1 mL of dry and degassed toluene was stirred with 2 equiv. of host Compound 18 attached to the silica substrate, based on the surface coverage of the PM-BCD calculated above. After 15 min of stirring, the contents were allowed to settle. The silica-supported host-guest complex settled out as a dark solid, leaving the previously golden-brown solution a much lighter yellow. Filtering this solution through a filter paper yielded a dark solid, distinct from both the white host compound and the dark yellow-green catalyst, confirming that Compound 4 forms a host-guest complex with silica-attached Compound 18.
Adding the azobenzene moiety did not significantly affect the catalyst's activity. Two benchmark ring-closing metathesis (RCM) substrates were chosen. They are Compound 19 and Compound 21 in
The RCM reactions were carried out in dichloromethane (DCM) at 40° C. under typical metathesis concentrations, and the reactions were monitored by gas chromatography (GC) using mesitylene as an internal standard. In the reaction of diethyl diallylmalonate (Compound 19), Compound 4 performed comparably to Compound 3, reaching >90% conversion in 30 min.
The evaluation of the catalytic efficiency of Compound 4 was extended to the more hindered diene (Compound 21). The reaction was slower for both catalysts. Compound 3 required 30 min to achieve greater than 90% conversion, with full conversion taking 3 hours. Compound 4 achieved 80% conversion after 30 min and 86% conversion after 5 hours.
Even more hindered substrates, such as diethyl di(2-methylallyl)malonate (Compound 23), showed a very low conversion for both catalysts even after 5 h, indicating that Compound 4 compares well with other commercially available metathesis catalysts.
Recovery of Compound 4 after Catalyzing a Reaction
The catalyst (Compound 4) is recoverable from a chemical reaction solution after catalyzing a reaction. The metathesis substrates shown in
Catalyst recovery was examined by varying the amount of host (Compound 18) and number of recovery cycles performed. After the ring closing metathesis (RCM) reaction of Compound 19, Compound 18 was added in one portion and stirred at room temperature for 15 min. During this time, the reaction vessel was irradiated with visible light for 30 seconds with a 500 W halogen work lamp to ensure that trans isomer form of the azobenzene functional group on Compound 4 was present in solution. This caused the host-guest compound to form.
The contents of the reaction vessel were filtered with the host-guest complex (Compound 18:Compound 4) separated from the solution onto a filter paper. The residual ruthenium content of the reaction solution was evaluated by ICP-MS analysis and displayed in parts per million, defined as micrograms of ruthenium per gram of product.
Treating the crude reaction mixture twice using 2 equiv of Compound 18 (2×2 equiv) was more effective than treating it only once with 6 equiv of Compound 18 (1×6 equiv), with residual ruthenium contents of 136 and 420 ppm, respectively. Extensive treatment with Compound 18, a 6×2 equiv method, resulted in only 57 ppm remaining ruthenium, although this additional recovery may not justify the amount of time and the host compound consumed in the process.
It was found that increasing the stirring time from 15 to 60 min upon addition of 18 (2×2 equiv) did not increase the amount of ruthenium recovered from solution, with both experiments yielding 136 ppm ruthenium, indicating that complexation occurs rapidly.
After these initial experiments were performed with Compound 19, the other substrates and a blank sample were treated with 2×2 equiv host compound 18. The results are displayed in
The amount of residual ruthenium after recovery by the host compound varied from 752 ppm to as low as 52 ppm, although all examples were greatly reduced from the starting ruthenium concentration, calculated to be 4772 ppm. The blank sample showed essentially 0 ppm ruthenium. These results were gained by a vacuum filtration of the crude reaction mixture. Centrifugation and other advanced separation techniques did not improve the result.
This disclosure describes certain exemplary embodiments, but not all possible embodiments of the composition and methods. Where a particular feature is disclosed in the context of a particular embodiment, that feature can also be used, to the extent possible, in combination with and/or in the context of other embodiments. The composition and methods may be embodied in many different forms. The claims should not be construed as being limited only to the embodiments described here.
This claims priority from provisional Application No. 62/377,777, filed Aug. 22, 2016, which is incorporated by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 62377777 | Aug 2016 | US |