The present disclosure relates to the field of polymerization, mainly the homopolymerization of terpenoids containing an alcohol group via a free radical polymerization mechanism.
In the scientific and patent literature there is a need for new renewable polymers and polymeric materials. Terpenes and terpenoids are a large class of biological compounds with one or more isoprene units that have generated significant interest as monomers for polymerization. Terpenes and terpenoids have many desirable properties including antimicrobial1, anticancer2, and antioxidant3 activity. However, they are often volatile or water insoluble which can make them less useful for some applications.2 Polymerization of these compounds is one possible route to improving their physical properties while retaining their desirable chemical properties, because larger molecules are less volatile and various functional groups can be incorporated into polymers to alter other physical properties such as solubility. Polymers and co-polymers of terpenes have found numerous uses in coatings (U.S. Pat. No. 7,776,959 B2), therapeutic agents (US20120213727 A1), pharmaceuticals,2,4 green plastics5 and pesticides.6
The polymerization of these monomers has involved different chemical strategies. As reviewed reviewed by Wilbon et al.5 Terpenes and terpenoids have been both homo and copolymerized for a variety of applications. However, the polymerization of terpenoids is difficult.
It has been proposed to be impossible to homopolymerize acyclic monoterpenoids via a free radical polymerization mechanism, based on the previous reports in the literature.7-11
Accordingly there is a need to develop techniques for homopolymerizing terpenoids, which are chemically different from terpenes due to the inclusion of one or more oxygen containing functional group(s). These materials have been considered extremely difficult to homopolymerize via a free radical mechanism to yield useful functional materials as significant chemical modification of the monomer is usually required prior to polymerization5.
The present disclosure relates to the homopolymerization of terpenoids containing at least one alcohol group using free radical polymerization. Terpenoids with alcohol containing groups, in particular acyclic monoterpenoids, have been considered by the scientific literature to be impossible to homopolymerize via free radical chemistry without significant chemical modification of the monomers.
These terpenoids are natural, plant based compounds with numerous uses including therapeutic, antimicrobial, scent, flavor, and insecticidal. However, they are often volatile which can reduce their utility in some applications. Polymerization offers a method to improve their use by reducing volatility and modifying the physical properties of the material to be more desirable from an applications perspective. Polymerization can also potentially enhance the therapeutic, antimicrobial and other desirable properties of these materials. Such polymers would also contain multiple functional groups (polyols etc.) that can then be used as renewable prepolymers for urethane and other chemistry.
In one embodiment of the disclosure, there is included a terpenoid homopolymer having the general representative structure (I) or (II)
wherein the broken lines represent either a carbon-carbon single or double bond, with at least one carbon double bond being present in the structure,
n is an integer between 1 and 10,000;
R1 to R14 are independently or simultaneously H, halo, (C1-C24)-alkyl, (C2-C24)-alkenyl, (C2-C24)-alkynyl, (C6-C14)-aryl or (C5-C14)-heteroaryl, wherein the latter 5 groups are optionally substituted and wherein the optional substituents are chosen from one or more of halogen, —OH, (C1-C6)-alkyl, (C1-C6)-alkoxy, thionyl, nitro, amino (—NH2), (C6-C14)-aryl, (C5-C14)-heteroaryl, phosphate (—PO4), and phosphoryl (—PO3),
wherein at least one of R1-R14 contains at least one —OH group;
and wherein R1-R14 can also optionally comprise one or more isoprene subunits according to the general structure
In one embodiment of the disclosure, there is included a terpenoid homopolymer having the general representative structure (I) or (II)
In one embodiment, the homopolymer is comprised of covalently joined terpenoid monomers having the general structures
wherein R1-R14 and the dashed lines are as defined above.
In one embodiment, R1 to R14 are independently or simultaneously H, halo, (C1-C10)-alkyl, (C2-C10)-alkenyl, (C2-C10)-alkynyl, (C6-C10)-aryl or (C5-C10)-heteroaryl. In another embodiment, R1 to R14 are independently or simultaneously H, halo, (C1-C6)-alkyl, (C2-C6)-alkenyl, (C2-C6)-alkynyl, (C6)-aryl or (C5-C6)-heteroaryl. In another embodiment, R1 to R14 are independently or simultaneously H or (C1-C6)-alkyl,
In one embodiment, the terpenoid monomer is optionally a cyclic terpenoid, a poly-cyclic terpenoid, an acyclic terpenoid, or a terpenoid consisting of between 1 to 8 linked isoprene subunits.
In one embodiment, the terpenoid monomer is an acyclic monoterpenoid.
In one embodiment, the acyclic monoterpenoid monomer is chosen from the group consisting of geraniol, citronellol, linalool, nerol, rhodinol, lasiol, trans and cis nerolidol having the following structures
In one embodiment, the cyclic terpenoid is chosen from terpineol and its isomers.
In one embodiment, n is an integer between about 5 and about 1,000.
In one embodiment, n is an integer between about 5 and about 15.
In one embodiment, the terpenoid homopolymer is a functional polyol pre-polymer.
In one embodiment, the terpenoid homopolymer is a functional pre-polymer for urethane chemistry.
In one embodiment, the terpenoid homopolymer has therapeutic, antimicrobial or insecticidal properties.
In one embodiment, the terpenoid homopolymer has preservative properties.
In one embodiment, the terpenoid homopolymer is incorporated as an organoleptic agent in a cosmetic formulation
In one embodiment, the terpenoid homopolymer is incorporated into a finished consumer product or packaging materials to impart antimicrobial or organoleptic properties to the material.
In one embodiment, the terpenoid homopolymer forms a liquid antimicrobial coating by non-covalently bonding to the desired surface or substrate.
In one embodiment, the antimicrobial terpenoid homopolymer is incorporated into bandages, shrink coatings, polymeric and other composite materials for medicinal, protective coatings and packaging applications.
In one embodiment, the terpenoid homopolymer is applied as a film or surface coating by chemical functionalization or reactions of the hydroxyl group with the surface.
In one embodiment, the terpenoid homopolymer is a feedstock for renewable plastic materials.
There is also included a method of synthesizing a terpenoid homopolymer as defined in claim 1, comprising homopolymerizing a terpenoid monomer comprising at least one double bond, conjugated double bond or aromatic double bond and at least one hydroxyl functional group by free radical polymerization, the method comprising
i. Reacting the monomer with a free radical initiator without deprotonation or without protecting groups;
ii. Optionally deprotonating or protecting the hydroxyl functionality of the monomer prior to polymerization.
In one embodiment, the free radical initiator is selected from hydrogen peroxide, an azo initiator, a halogen initiator, an organic peroxide initiator, an inorganic peroxide initiator, a hydroxyperoxy initiator, a photosensitizer, a photo initiator and a transition metal catalyst capable of generating radicals for polymerization.
In one embodiment, the polymerization is initiated thermally or photoinitiated.
In one embodiment, the reaction is conducted in a solvent.
The present disclosure relates to the homopolyers of terpenoids containing at least one alcohol group and carbon-carbon double bond, polymerized using free radical polymerization. Detailed examples of the homopolymerization using the above technique on terpenoid monomers are presented below. Representative structures of the terpenoid homopolymers are shown below
wherein the broken lines represent either a carbon-carbon single or double bond, with at least one carbon double bond being present in the monomer, which during polymerization is incorporated into the polymer backbone, R1 to R14 are independently or simultaneously H, halo, (C1-C24)-alkyl, (C2-C24)-alkenyl, (C2-C24)-alkynyl, (C6-C14)-aryl or (C5-C14)-heteroaryl, wherein the latter five groups are optionally substituted and the optional substituents are chosen from one or more of halogen, —OH, (C1-C6)-alkyl, (C1-C6)-alkoxy, thionyl, nitro, amino (—NH2), (C6-C14)-aryl, (C5-C14)-heteroaryl, phosphate (—PO4), phosphoryl (—PO3), and at least one of R1-R14 contains at least one —OH groups, and n is an integer between 1 and about 10,000.
In one embodiment, n is an integer between about 5 and about 1,000.
In one embodiment, n is an integer between about 5 and about 15.
In another embodiment, the polymers have the structure
Terpenoids, or isoprenoids comprise a large class of organic chemicals similar to terpenes but with added oxygen functional group(s), consisting of 5 carbon isoprenene units, assembled and modified in numerous ways. The terpenoids of this disclosure include but are not restricted to acylic, and cyclic terpenoids, poly-cyclic terpenoids, terpenoids consisting of between 1 to 8 linked isoprene subunits and their derivatives provided they contain at least one alkene functionality and at least one hydroxyl (OH) functionality.
In one embodiment, the terpenoid monomers of the present disclosure are acyclic terpenoids of general structure
wherein the broken lines represent either a carbon-carbon single or double bond, with at least one carbon double bond being present in the structure, R1 to R14 are independently or simultaneously H, halo, (C1-C24)-alkyl, (C2-C24)-alkenyl, (C2-C24)-alkynyl, (C6-C14)-aryl or (C5-C14)-heteroaryl, wherein the optional substituents are chosen from one or more of halogen, —OH, (C1-C6)-alkyl, (C1-C6)-alkoxy, thionyl, nitro, amino (—NH2), (C6-C14)-aryl, (C5-C14)-heteroaryl, phosphate (—PO4), phosphoryl (—PO3), and at least one of R1-R14 contains at least one —OH groups
In another embodiment the terpenoid monomers of the present disclosure are cyclic terpenoids of the general structure
wherein the broken lines represent either a carbon-carbon single or double bond, with at least one carbon double bond being present in the structure, R1 to R14 are independently or simultaneously H, halo, (C1-C24)-alkyl, (C2-C24)-alkenyl, (C2-C24)-alkynyl, (C6-C14)-aryl or (C5-C14)-heteroaryl, wherein the latter five groups are optionally substituted and the optional substituents are chosen from one or more of halogen, —OH, (C1-C6)-alkyl, (C1-C6)-alkoxy, thionyl, nitro, amino (—NH2), (C6-C14)-aryl, (C5-C14)-heteroaryl, phosphate (—PO4), phosphoryl (—PO3), and at least one of R1-R14 contains at least one —OH groups.
In one embodiment, R1 to R14 are independently or simultaneously H, halo, (C1-C10)-alkyl, (C2-C10)-alkenyl, (C2-C10)-alkynyl, (C6-C10)-aryl or (C5-C10)-heteroaryl. In another embodiment, R1 to R14 are independently or simultaneously H, halo, (C1-C6)-alkyl, (C2-C6)-alkenyl, (C2-C6)-alkynyl, (C6)-aryl or (C5-C6)-heteroaryl. In another embodiment, R1 to R14 are independently or simultaneously H or (C1-C6)-alkyl,
In another embodiment the terpenoid monomer of the present disclosure is geraniol, citronellol, linalool, nerol, rhodinol, lasiol, trans nerolidol, cis nerolidol, having the structures
In another embodiment the terpenoid monomer of the present disclosure is terpineol and its isomers.
In another embodiment of the present disclosure the free radical initiator is hydrogen peroxide, an azo initiator, a halogen initiator, an organic peroxide initiator, an inorganic peroxide initiator, a hydroxyperoxy initiator, or a transition metal catalyst capable of generating radicals for polymerization.
In another embodiment of the present disclosure the polymerization is initiated thermally. In another embodiment polymerization is photoinitiated.
In another embodiment of the disclosure the polymerization reaction is conducted in a solvent. In another embodiment the polymerization reaction is conducted without the use of solvents.
In one embodiment of the current disclosure the terpenoid homopolymer of citronellol is synthesized. In another embodiment the terpenoid homopolymer of linalool is synthesized. In another embodiment the terpenoid homopolymer of geraniol is synthesized.
The present disclosure also includes uses of the terpenoid homopolymers, for example, the terpenoid homopolymers of the current disclosure are functional polyol pre-polymers, with applications including urethane polymerization. In another embodiment the terpenoid homopolymers are anti-microbial. In another embodiment, the terpenoid homopolymers are preservative materials. In another embodiment, the terpenoid homopolymers of the present disclosure are insecticide and pest control materials.
In another embodiment, the terpenoid homopolymers are therapeutic agents. In another embodiment the terpenoid homopolymers are organoleptic agents, and can be incorporated into cosmetic and consumer formulations. In another embodiment, the terpenoid homopolymers are incorporated into a finished consumer product or packaging material to impart antimicrobial or organoleptic properties to material. In another embodiment the terpenoid homopolymer forms a liquid antimicrobial coating by non-covalently bonding to the desired surface. In another embodiment, the terpenoid homopolymer is used as a film or surface coating material by chemical functionalization or reactions of the hydroxyl group with the surface. In another embodiment, the terpenoid homopolymers of present disclosure can act as renewable plastic materials.
The polymers of this disclosure have many uses. For example, linalool and citronellol are known pest control agents and the polymers of the disclosure can be applied or sprayed as a diluted solution to control pests indoors.
In one embodiment, the terpenoid monomers are often used as scents in cosmetic formulations. As the polymers of the present disclosure are antimicrobial and retain the characteristic odors of the monomers, they can act as antimicrobial and scent additives to cosmetic formulations. For example, a lotion containing a 1% cross-linked viscosity modifier, 81% water, 5% cetearyl alcohol, 4% coconut oil, 1.5% linalool homopolymer, and 3% almond oil was made as a proof of concept demonstrating the ability to incorporate the polymers of this disclosure into consumer products.
In one embodiment, the terpenoid homopolymers of the present disclosure are liquid polyols, and can thus act as green, renewable based liquid pre-polymers for the synthesis of polyurethanes and urethane chemistry.
In one embodiment, the terpenoid monomers of the present disclosure are derived from food based sources and polymerized by hydrogen peroxide and can act as a natural organoleptic agent.
In one embodiment, the anti-microbial homopolymers of the present disclosure can also be added to packaging materials, and incorporated into various articles to impart anti-microbial activity to the finished product.
Other features and advantages of the present disclosure will become apparent from the following detailed description. It should be understood, however, that the detailed description and the specific examples while indicating preferred embodiments of the disclosure are given by way of illustration only, since various changes and modifications within the spirit and scope of the disclosure will become apparent to those skilled in the art from this detailed description.
Linalool (Sigma-Aldrich, 10.000 mL, 56.40 mmol) was heated to 110° C. under magnetic stirring in a reaction vessel, at which point hydrogen peroxide (Sigma-Aldrich, 10.00 mL of 30% weight in water) was added. The heat was left on for 80 minutes while the clear solution boiled and began to turn yellow then darken to orange/red. A viscous orange/red liquid polymer was collected. The polymers were then characterized by FTIR, NMR, viscosity computational methods and mass spectrometry. Where indicative of monomer presence in the product by NMR, the polymers were purified by vacuum distillation.
In other example synthesis of homopolymers of linalool, the ratio of initiator to monomer as expressed as a weight percent of the pure initiator to monomer was varied from a few weight percent to 50 weight percent. The resulting homopolymers possessed different viscosities and molecular weights.
Geraniol (Sigma-Aldrich, 10.000 mL, 56.40 mmol) was heated to 110° C. under magnetic stirring in a reaction vessel, at which point hydrogen peroxide (Sigma-Aldrich, 10.00 mL of 30% weight in water) was added. The heat was left on for 80 minutes while the clear solution boiled and began to turn yellow then darken to orange/red. The maximum temperature in the reaction vessel reached 204 Celsius during the course of the reaction. A viscous orange/red liquid polymer was collected. The polymers were then characterized by FTIR, NMR, viscosity and mass spectrometry. Where indicative of monomer presence in the product by NMR, the polymers were purified by vacuum distillation.
In other example synthesis of homopolymers of geraniol, the ratio of initiator to monomer as expressed as a weight percent of the pure initiator to monomer was varied from a few weight percent to 50 weight percent. The resulting homopolymers possessed different viscosities and molecular weights.
Geraniol was also polymerized through the reversible deprotonation of the hydroxyl group followed by free radical polymerization across the carbon double bond. In this method, Potassium hydroxide (0.29 g, 5.17 mmol) was dissolved in distilled water (0.500 mL) to which geraniol (1.000 mL, 5.64 mmol) was added. The solution was heated and stirred. When the temperature reached 80° C., 2,2′-Azobis(2-methylpropionitrile) (0.10 g, 10% weight) was added to the yellow solution. The heat was left on and the solution darkens to orange then dark red/orange. After 26 minutes the heat is turned off (maximum temperature reached is 160° C.). The resulting final product is a brown solid, and can be re-protonated by reacting it with an acid.
Similarly, other reactants well known in the literature can be used to deprotonate the hydroxyl group prior to polymerization. Likewise the hydroxyl group can also be protected by reacting it with silyl ethers, or other well-known protecting groups prior to polymerization.
Finally, to examine the reactivity of geraniol with the base a second control sample containing potassium hydroxide (0.29 g, 5.17 mmol) was dissolved in distilled water (0.500 mL) to which geraniol (1.000 mL, 5.64 mmol) was added. The solution was heated and stirred. With the heat the solution turns yellow then orange and continues to darken to a final blood red/orange solution and the heat is turned off (maximum temperature reached is 180° C.). The final product is a light brown liquid.
The polymerized geraniol, as well as the de-protonated control was analyzed by FTIR, and NMR spectroscopy to demonstrate polymerization of the sample.
Citronellol (2.000 mL, 10.94 mmol) was heated under magnetic stirring in a reaction vessel to 110° C. at which point hydrogen peroxide (0.667 mL 30% weight, 10% weight) was added. The solution is heated over 34 minutes with no visible changes and reaches a temperature height of 160° C. At this point more hydrogen peroxide was added (1.000 mL 30% weight). Heat was left on for another 28 minutes as the solution turns yellow and the temperature reaches a maximum of 175° C. At his point the heat was turned off and the viscous yellow solution was collected and analysed.
Citronellol was also polymerized through the reversible deprotonation of the hydroxyl group followed by free radical polymerization across the carbon double bond. In this method, Potassium hydroxide (0.3 g, 5.17 mmol) was dissolved in distilled water (0.500 mL) to which citronellol (1.000 mL, 5.48 mmol) was added. The solution was heated and stirred. When the temperature reached 80° C., 2,2′-Azobis(2-methylpropionitrile) (0.10 g, 10% weight) was added to the yellow solution. The heat was left on and the solution darkens to yellow/orange then dark orange/brown color. After 26 minutes the heat is turned off (maximum temperature reached is 130° C.). The resulting final product can be re-protonated by reacting it with an acid.
Similarly, other reactants well known in the literature can be used to deprotonate the hydroxyl group prior to polymerization. Likewise the hydroxyl group can also be protected by reacting it with silyl ethers, or other well-known protecting groups prior to polymerization.
Finally, to examine the reactivity of citronellol with the base a second control sample containing potassium hydroxide (0.3 g, 5.17 mmol) was dissolved in distilled water (0.500 mL) to which citronellol (1.000 mL, 5.48 mmol) was added. The solution was heated and stirred. With the heat the solution turns yellow then orange and the heat is turned off (maximum temperature reached is 180° C.). The final product is a dark orange liquid.
Nuclear Magnetic Resonance (NMR) Spectroscopy. 1H-NMR and 13C-NMR were recorded by JEOL ECS-400 MHz NMR Spectrometer at ambient temperature with deuterated chloroform purchased from Sigma-Aldrich and used as received. Data processing was performed using Delta NMR Processing and Control Software Software v5.0.4.
i. Linalool Homopolymers
The 1H-NMR and 13C-NMR of linalool is presented in
It was determined through 1H and 13C NMR as well as computational modelling of the reaction with the hydroxyl radical (
Linalool has four alkene hydrogens, HA, HA′, HB and HG. In the 1H NMR of the monomer, these signals appear as three doublets of doublets at 5.88 ppm (HB), 5.18 ppm (HA) and 5.03 ppm (HA′) and a triplet at 5.09 ppm (HG). The polymer 1H NMR shows the presence of signals for HA, HA′ and HB at essentially the same chemical shifts, however the HG signal is no longer present in the alkene region, further indicating that polymerization has occurred between C7 and C8. The relative integration between the sp2 protons and the sp3 is approximately 3:67, however if polymerization had only occurred between C7 and C8 then it should be 3:15. Therefore, on many of the linalool molecules, both double bonds have participated in polymerization. Because all of the bonds between C7 and C8 have been polymerized, it can be concluded that polymerization occurs more favourably between C7 and C8. We hypothesize that it is because polymerization at this location results in the formation of a more stable tertiary free radical.
The addition of hydroxyl radicals to linalool was also studied computationally to yield further information on the mechanism of polymerization. All reactants and products were optimized at using UB3LYP and a 6-31Gd,p basis set to determine which reaction is the most thermodynamically favorable. It was determined that the addition of a hydroxyl radical to C7 (
ii. Geraniol Homopolymers
The 1H and 13C NMR of geraniol (
From the NMR's (
iii. Citronellol Homopolymers
The 1H and 13C NMR of citronellol (
From the NMR's (
The FTIR spectrum was recorded by Thermo Nicolet iS5 FT-Infrared Spectrometer with iD5 ATR Diamond accessory.
i. Linalool Homopolymers
The FTIR spectrum of the linalool polymer is shown in
The IR spectra of the polymer (
ii. Geraniol Homopolymers
The FTIR spectrum of the geraniol and KOH reaction product is presented in
iii. Citronellol Homopolymers
The FTIR spectrum of citronellol is presented in
Viscosity measurements were performed on a Brookfield Synchro-Lectric LVF Viscometer.
i. Linalool Homopolymers
The viscosities of the homopolymer as well as the linalool monomer were both measured. The viscosity of the polymer in example 1 was determined to be 5760±20 mPa·s while the viscosity of linalool was measured to be only 9.8±0.3 mPa·s, both measured at the 95% confidence level. The more than 500 fold increase in viscosity adds further evidence that polymerization of linalool has been successful, as increasing viscosity of the monomer solution is an indication of polymerization as well as polymer molecular weight.
Furthermore, using the mark-houwink parameters of polyethylene glycol in ethanol as published by Dohmen and coworkers13, K (0.17) and alfa (0.45) the viscosity average molecular weight of the linalool homopolymer synthesized using hydrogen peroxide was calculated as 1549 g/mol relative to polyethylene glycol. The intrinsic viscosity of the homopolymer in ethanol was determined using the viscosity at polymer concentrations of 2, 1.5, 1.25 and 1 g/ml in ethanol to be 4.6339.
ii. Geraniol Homopolymers
The viscosities of the homopolymer and monomer of geraniol was measured. The viscosity of one of the polymers in example 2 (hydrogen peroxide synthesis) was determined to be 5930±72 mPa·s while the viscosity of geraniol was 14±0.75 mPa·s, both measured at the 95% confidence level. The more than 400 fold increase in viscosity adds further evidence that polymerization of geraniol has been successful, as increasing viscosity of the monomer solution is an indication of polymerization as well as polymer molecular weight.
Furthermore, using the mark-houwink parameters of polyethylene glycol in ethanol as published by Dohmen and coworkers13, K (0.17) and alfa (0.45) the viscosity average molecular weight of the geraniol homopolymer synthesized using hydrogen peroxide was calculated as 1373 g/mol relative to polyethylene glycol. The intrinsic viscosity of the homopolymer in ethanol was determined using the viscosity at polymer concentrations of 2, 1.5, 1 and 0.5 g/ml in ethanol to be 4.3894.
iii. Citronellol Homopolymers
The viscosities of the homopolymer and monomer of citronellol was measured. The viscosity of the polymer in example 3 was determined to be 3005±11 mPa·s while the viscosity of citronellol was 24.75±0.53 mPa·s, both measured at the 95% confidence level. The more than 100 fold increase in viscosity of pure compounds adds further evidence that polymerization of geraniol has been successful, as increasing viscosity of the monomer solution is an indication of polymerization as well as polymer molecular weight.
Furthermore, using the mark-houwink parameters of polyethylene glycol in ethanol as published by Dohmen and coworkers13, K (0.17) and alfa (0.45) the viscosity average molecular weight of the citronellol homopolymer synthesized using hydrogen peroxide was calculated as 2005 g/mol relative to polyethylene glycol. The intrinsic viscosity of the homopolymer in ethanol was determined using the viscosity at polymer concentrations of 2, 1.5, 1.25 and 1 g/ml in ethanol to be 5.2044.
A mass spectrum of the linalool polymer was acquired using ESI, with sodium ions. The spectrum is presented in
The polymer samples were characterized using differential scanning calorimetry using a TA instruments Q200 DSC instrument. The DSC plots for the citronellol homopolymer, geraniol homopolymer, and linalool homopolymer are presented in
Disk inhibition studies were performed for all the synthesized homopolymers to demonstrate their retention of their useful monomeric properties (therapeutic, functionality etc.), and possible impact of polymerization on such properties. The procedure used to conduct the testing is outlined below, with the results of the anti-microbial testing presented in table 1.
In general it is observed that there is an improvement in anti-microbial activity for the linalool homopolymer as compared to the monomer, while the citronellol and geraniol homopolymer show similar to slightly increased activity as compared to their monomers.
Preparation of Bacterial Broth.
Tubes of Tryptic Soy Broth (10 mL/tube,) were prepared according to manufacturer directions (Difco) using aseptic techniques. Bacterial broth of Escherichia coli, Staphylococcus aureus, Pseudomonas aeruginosa, Proteus hauseri, and Bacillus cereus were prepared in a tissue culture hood by transferring frozen stock culture (−70° C. freezer, prepared from ATCC bacterial quality control strains) of the given bacteria to the broth tube. The E. coli, S. aureus, P. aeruginosa, and P. hauseri culture tubes were then incubated for 24 hours at 37° C. and the B. cereus culture tubes were incubated at 30° C. for 24 hours.
Preparation of Fungal Broth.
Plates of Sabourad Dextrose Agar (Difco) and tubes of Malt Extract Broth (20 mL/tube) were prepared according to manufacturer direction using aseptic techniques. Fungal broths of Saccharomyces cerevisiae and Candida albicans were prepared in a tissue culture hood by transferring frozen stock culture (−70° C. freezer, prepared from ATCC bought strains) of the given fungi to the broth tube. The S. cerevisiae culture tubes were incubated for 48 hours at 30° C. and the C. albicans culture tubes were incubated for 48 hours at 37° C.
Fungal broths of Aspergillus fumigatus and Aspergillus niger were prepared in a tissue culture hood by transferring the frozen stock culture (−70° C. freezer) of the given fungi to a plate of Sabourad Dextrose Agar. The A. fumigatus culture plates were incubated for 48 hours at 37° C. and the A. niger culture plates were incubated for 72 hours at 25° C. The fungal broth was prepared by using a cork borer to add 2-3 circular pieces of agar containing active fungal growth to distilled water (4.0 mL). A tissue homogenizer was then used to grind the agar and create a suspension of fungal spores.
Preparation of Sample Disks.
Each sample (˜15 mg) was dissolved in a solvent (3.000 mL of tetrahydrofuran or 3.000 mL distilled water) depending on the sample's solubility. The sample (20 μL of sample solution or 100 μg of sample was then transferred to a sterile filter paper disk. The disk was then allowed to dry so that all solvent was evaporated and 100 μg of sample remained on the disk.
Preparation of Bacterial Agar Plates.
Plates of Mueller Hinton II Agar (Difco) were prepared according to manufacturer directions using aseptic techniques. The bacterial agar plates were prepared using the bacterial culture broth of E. coli, S. aureus, P. aeruginosa, P. hauseri, or B. cereus as prepared above after the incubation period. In a tissue culture hood, the given bacterial culture broth solution (300 μL) was transferred to each Mueller Hinton Agar II plate and spread evenly over the agar and allowed to dry for a minimum of 20 minutes. Four sample disks (as prepared above) or control antibiotic disks (pre-made disks) were then places onto each agar plate, one in the center of each quadrant of the plate. The pre-made antimicrobial disks were of Penicillin (10 μg), Tetracycline (30 μg), Chloramphenicol (30 μg) and Ampicillin (10 μg).
The E. coli, S. aureus, P. aeruginosa, and P. hauseri, plates were incubated for 24 hours at 37° C. and the B. cereus plates were incubated for 24 hours at 30° C. The plates were then observed for zones of bacterial growth inhibition. Where a zone of growth inhibition was observed, the diameter of the ring was measured to the closest 0.1 mm using a caliper. An incomplete ring or absence of inhibition zone was ruled a failed test and the compound was ruled inactive against that particular organism. The absence of a uniform bacterial lawn was ruled a failed test and in this case the test would need to be repeated in order to achieve meaningful results.
Preparation of the Fungal Agar Plates.
Plates of Sabourad Dextrose Agar (Difco) were prepared according to manufacture directions using aseptic techniques. The fungal agar plates were prepared using the culture broth of S. cerevisiae, C. albicans, A. fumigatus or A. niger as prepared above after the incubation period. In a tissue culture hood, the fungal culture broth solution (200 μL) was transferred to each Sabourad Dextrose Agar plate and spread evenly over the agar and allowed to dry for a minimum of 20 minutes. Four sample disks or control antifungal disks were then places onto each agar plate, one in the center of each quadrant of the plate. The sample disks were prepared as described above and the antifungal disks were pre-made disks of 20 μg of amphotericin B.
The C. albicans and A. fumigfatus plates were incubated for 24 hours at 37° C., the A. niger plates were incubated for 48 hours at 25° C. and the S. cerevisiae plates were incubated for 24 hours at 30° C. The plates were then observed for zones of fungal growth inhibition. Where a zone of growth inhibition was observed, the diameter of the ring was measured to the closest 0.1 mm using a caliper. An incomplete ring or absence of inhibition zone was ruled a failed test and the compound was ruled inactive against that particular organism. The absence of a uniform fungal lawn was ruled a failed test and in this case the test would need to be repeated in order to achieve meaningful results.
Linalool homopolymers were incorporated into bandages, by mixing the homopolymer with cotton bandage squares and vinyl acetate monomer for 24 hrs, after which the monomer was polymerized by free radical polymerization using AIBN.
The resulting composite material (2×2 inch square) was stretched under heat using a heat gun and clamps to an average length of 3.6 inches over 3 samples. The composite was allowed to cool down to room temperature, and the clamps around the material removed. The material was then exposed again to heat from the heat gun, and allowed to shrink towards its original length. When the material stopped visibly shrinking, the heat gun was removed and the material allowed to cool down. Thereafter the final length of the sample was measured to have shrunk to an average length of 2.83 inches, or approx. 21% of its length.
As the cotton and polyvinyl acetate are known to be biocompatible, and the homopolymer antimicrobial, incorporation of antimicrobial terpenoid homopolymer are used to create antimicrobial bandages, and heat shrinkable materials, coatings, and composites for therapeutic, and industrial applications.
E.
S.
P.
P.
B.
A.
S.
C.
A.
Coli
Aureus
Aeriginosa
Hauseri
Cereus
Niger
Cerevisiae
Albicans
Fumigratus
The present application claims the benefit of provisional patent application No. 62/139,129, filed Mar. 27, 2015, the contents of which is herein incorporated by reference.
| Number | Date | Country | |
|---|---|---|---|
| 62139129 | Mar 2015 | US |