Claims
- 1. A method of making a hose construction comprising the steps of forming a tubular construction having a reference axis and at least one uncured layer portion made primarily of an elastomeric matrix material having randomly distributed elongated fibers embedded therein in substantially parallel relation with said fibers extending in a helical pattern about said axis at an angle relative thereto, disposing said tubular construction on a curved mandrel which extends in a curved path so that said reference axis also extends substantially along said curved path, curing said tubular construction while it is disposed in said curved mandrel to form a hose construction wherein said reference axis and hose construction extend in a curved path defined by the curved path of said curved mandrel.
- 2. A method as set forth in claim 1 in which said forming step comprises forming said tubular construction having another uncured layer portion provided against the first-named layer portion, said other layer portion also being made primarily of an uncured elastomeric matrix material having randomly distributed elongated fibers embedded therein in substantially parallel relation, said fibers of said other layer portion extending in a helical pattern about said axis at an angle relative thereto in a direction opposite from the helical pattern of the fibers of said first-named layer portion, said curing step resulting in said layer portions being bonded together as a unitary homogenous mass with said fibers serving as the main reinforcement means for said hose construction.
- 3. A method as set forth in claim 2 in which said forming step comprises forming said tubular construction having said one and other layer portions using a pair of elongated ribbons to define said layer portions.
- 4. A method as set forth in claim 2 in which said forming step comprises forming said tubular construction having said one and other layer portions using a pair of bias cut sheets to define said layer portions.
- 5. A method as set forth in claim 2 in which said forming step comprises using one bias cut sheet of uncured fiber-loaded elastomeric material which has a longitudinal overlapped area at one circumferential position along the length of the tubular construction to define said one layer portion and using another bias cut sheet of uncured fiber-loaded elastomeric material which has a longitudinal overlapped area at a diametrically opposite circumferential position along the length of the tubular construction to define said other layer portion.
- 6. A method of making a hose construction comprising the steps of forming a tubular construction having a reference axis and having at least one layer portion made primarily of uncured elastomeric matrix material having randomly distributed elongated fibers embedded therein in substantially parallel relation, said matrix material having a tensile modulus in the direction of fiber orientation higher than the tensile modulus in a direction transverse to said fiber orientation, by winding a layer of said matrix material about a mandrel having a right circular cylindrical outside surface with said fibers extending in a helical pattern about said axis at an angle relative thereto, and curing said tubular construction to define said hose construction having said fibers serving as reinforcement means for said hose construction.
- 7. A method as set forth in claim 6 in which said forming step comprises forming said tubular construction having another layer portion provided against the first-named layer portion by winding another layer of said matrix material about said first-named layer portion, said fibers of said other layer portion also extending in a helical pattern about said axis in a direction opposite from the helical pattern of the fibers of the first-named layer portion, said curing step resulting in said layer portions being bonded together as a unitary homogenous mass with said fibers serving as the main reinforcement means for said hose construction.
- 8. A method of making a hose construction comprising the steps of forming an elongated tubular construction having a reference axis and at least one layer made primarily of an uncured elastomeric matrix material which has randomly distributed elongated fibers embedded therein in substantially parallel relation with the fibers extending in a helical pattern about the axis at an angle relative thereto, partially curing the tubular construction, placing the partially-cured tubular construction in a mold device having axially spaced corrugations comprising its wall means, and final forming and curing the partially cured tubular construction by urging it against the wall means while subjecting such tubular construction to a controlled environment to form a fiber reinforced hose construction having axially spaced corrugations defined by alternating crests and troughs of substantially uniform wall thickness.
- 9. A method as set forth in claim 8 in which said forming step comprises forming said tubular construction having another layer portion provided against the first-named layer portion with said other layer portion also being made primarily of an uncured elastomeric matrix material having randomly distributed elongated fibers embedded therein in substantially parallel relation, said fibers of said other layer portion extending in a helical pattern about said axis in a direction opposite from the helical pattern of the fibers of said first-named layer portion, and said partially curing step preceeding said final forming and curing step making possible said substantially uniform wall thickness as well as making possible said final forming with elastomeric material remaining confined in said mold device due to said partially cured tubular construction being less likely to flow during the final forming and curing.
- 10. A method as set forth in claim 9 in which said forming step comprises forming said elongated tubular construction using a ribbon of fiber-loaded uncured elastomeric matrix material to define each of said layers.
- 11. A method as set forth in claim 9 in which said forming step comprises forming said elongated tubular construction using a bias-cut sheet of fiber-loaded uncured elastomeric matrix material to define each of said layers.
- 12. A method as set forth in claim 9 in which said forming step comprises forming said elongated tubular construction by extrusion process with the fibers of each layer being disposed in their correct helical pattern simultaneously with the formation of their associated layer.
- 13. A method as set forth in claim 9 in which said step of partially curing results in partially curing said tubular construction from 10 to 90% of final cure.
- 14. A method as set forth in claim 13 in which said step of final forming and curing is achieved using steam.
- 15. The method of claim 6 wherein said layer portion is formed from an elongated ribbon of said matrix material.
- 16. The method of claim 6 wherein said layer portion is formed from a sheet of said matrix material.
CROSS-REFERENCE TO RELATED APPLICATION
This is a division of application Ser. No. 633,060, filed Nov. 18, 1975, now U.S. Pat. No. 4,013,101 which in turn is a continuation-in-part of application Ser. No. 452,471, filed Mar. 18, 1974, now U.S. Pat. No. 3,921,674.
US Referenced Citations (7)
Divisions (1)
|
Number |
Date |
Country |
Parent |
633060 |
Nov 1975 |
|
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
452471 |
Mar 1974 |
|